Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Heuristic solution for achieving long-term cycle stability for Ni-rich layered cathodes at full depth of discharge

An Author Correction to this article was published on 09 December 2020

This article has been updated


The demand for energy sources with high energy densities continues to push the limits of Ni-rich layered oxides, which are currently the most promising cathode materials in automobile batteries. Although most current research is focused on extending battery life using Ni-rich layered cathodes, long-term cycling stability using a full cell is yet to be demonstrated. Here, we introduce Li[Ni0.90Co0.09Ta0.01]O2, which exhibits 90% capacity retention after 2,000 cycles at full depth of discharge (DOD) and a cathode energy density >850 Wh kg−1. In contrast, the currently most sought-after Li[Ni0.90Co0.09Al0.01]O2 cathode loses ~40% of its initial capacity within 500 cycles at full DOD. Cycling stability is achieved by radially aligned primary particles with [003] crystallographic texture that effectively dissipate the internal strain occurring in the deeply charged state, while the substitution of Ni3+ with higher valence ions induces ordered occupation of Ni ions in the Li slab and stabilizes the delithiated structure.

Your institute does not have access to this article

Relevant articles

Open Access articles citing this article.

Access options

Buy article

Get time limited or full article access on ReadCube.


All prices are NET prices.

Fig. 1: Correlation between primary particle morphology and electrochemical performance.
Fig. 2: Morphology and orientation of primary particles as a function of the dopant and calcination temperature.
Fig. 3: Li/TM ordered structure observed in the NCTa90 cathode lithiated at 730 °C.
Fig. 4: Twin defect structure observed in the NCTa90 cathode lithiated at 730 °C.
Fig. 5: Electrochemical performances of NCA90 and NCTa90 cathodes lithiated at different temperatures.
Fig. 6: Structural and mechanical stability of NCTa90 cathode verified by structure characterization.
Fig. 7: Mechanisms that enable superior cycling stability of NCTa90 cathode in comparison with other metal-doped NC cathodes.

Data availability

All the data generated or analysed during this study are included in this published article and its Supplementary Information files. The data that support the plots within this paper and other findings of this study are available from the corresponding author upon reasonable request.

Change history

  • 09 December 2020

    An amendment to this paper has been published and can be accessed via a link at the top of the paper.


  1. Naceur, K. B Tracking Clean Energy Progress (International Energy Agency, 2016).

  2. 2017 Annual Merit Review, Vehicle Technologies Office (US Department of Energy, 2017);

  3. Schmuch, R., Wagner, R., Hörpel, G., Placke, T. & Winter, M. Performance and cost of materials for lithium-based rechargeable automotive batteries. Nat. Energy 3, 267–278 (2018).

    Article  Google Scholar 

  4. Andre, D. et al. Future generations of cathode materials: an automotive industry perspective. J. Mater. Chem. A 3, 6709–6732 (2015).

    Article  Google Scholar 

  5. Liu, Z., Yu, A. & Lee, J. Y. Synthesis and characterization of LiNi1−xyCoxMnyO2 as the cathode materials of secondary lithium batteries. J. Power Sources 81–82, 416–419 (1999).

    Article  Google Scholar 

  6. Noh, H.-J., Youn, S., Yoon, C. S. & Sun, Y.-K. Comparison of the structural and electrochemical properties of layered Li[NixCoyMnz]O2 (x = 1/3, 0.5, 0.6, 0.7, 0.8, and 0.85) cathode material for lithium-ion batteries. J. Power Sources 233, 121–130 (2013).

    Article  Google Scholar 

  7. Zhou, P. et al. Stable layered Ni-rich LiNi0.9Co0.07Al0.03O2 microspheres assembled with nanoparticles as high-performance cathode materials for lithium-ion batteries. J. Mater. Chem. A 5, 2724–2731 (2017).

    Article  Google Scholar 

  8. Nam, G. W. et al. Capacity fading of Ni-rich NCA cathodes: effect of microcracking extent. ACS Energy Lett. 4, 2995–3001 (2019).

    Article  Google Scholar 

  9. Wang, X., Ding, Y.-L., Deng, Y.-P. & Chen, Z. Ni-rich/Co-poor layered cathode for automotive Li-ion batteries: promises and challenges. Adv. Energy Mater. 10, 1903864 (2020).

    Article  Google Scholar 

  10. Liu, D. et al. Revealing the effect of Ti doping on significantly enhancing cyclic performance at a high cutoff voltage for Ni-rich LiNi0.8Co0.15Al0.05O2 cathode. ACS Sustain. Chem. Eng. 7, 10661–10669 (2019).

    Article  Google Scholar 

  11. Kim, U.-H., Kuo, L.-Y., Kaghazchi, P., Yoon, C. S. & Sun, Y.-K. Quaternary layered Ni-rich NCMA cathode for lithium-ion batteries. ACS Energy Lett. 4, 576–582 (2019).

    Article  Google Scholar 

  12. Han, S.-H. et al. Improvement of structural stability during high-voltage cycling in high-nickel cathode materials with B2O3 addition. J. Electrochem. Soc. 163, A748–A750 (2016).

    Article  Google Scholar 

  13. Xin, F. et al. Li-Nb-O coating/substitution enhances the electrochemical performance of the LiNi0.8Mn0.1Co0.1O2 (NMC 811) cathode. ACS Appl. Mater. Interfaces 11, 34889–34894 (2019).

    Article  Google Scholar 

  14. Schipper, F. et al. From surface ZrO2 coating to bulk Zr doping by high temperature annealing of nickel-rich lithiated oxides and their enhanced electrochemical performance in lithium ion batteries. Adv. Energy Mater. 8, 1701682 (2018).

    Article  Google Scholar 

  15. Weigel, T. et al. Structural and electrochemical aspects of LiNi0.8Co0.1Mn0.1O2 cathode materials doped by various cations. ACS Energy Lett. 4, 508–516 (2019).

    Article  Google Scholar 

  16. Kim, U.-H. et al. Pushing the limit of layered transition metal oxide cathodes for high-energy density rechargeable Li ion batteries. Energy Environ. Sci. 11, 1271–1279 (2018).

    Article  Google Scholar 

  17. Cho, J., Kim, Y. J. & Park, B. Novel LiCoO2 cathode materials with Al2O3 coating for a Li ion cell. Chem. Mater. 12, 3788–3791 (2000).

    Article  Google Scholar 

  18. Woo, S.-U., Yoon, C. S., Amine, K., Belharouak, I. & Sun, Y.-K. Significant improvement of electrochemical performance of AlF3-coated Li[Ni0.8Co0.1Mn0.1]O2 cathode materials. J. Electrochem. Soc. 154, A1005–A1009 (2007).

    Article  Google Scholar 

  19. Yan, P. et al. Tailoring grain boundary structures and chemistry of Ni-rich layered cathodes for enhanced cycle stability of lithium-ion batteries. Nat. Energy 3, 600–605 (2018).

    Article  Google Scholar 

  20. Watanabe, S., Kinoshita, M., Hosokawa, T., Morigaki, K. & Nakura, K. Capacity fading of LiAlyNi1−xyCoxO2 cathode for lithium-ion batteries during accelerated calendar and cycle life tests (effect of depth of discharge in charge–discharge cycling on the suppression of the micro-crack generation of LiAlyNi1−xyCoxO2 particle). J. Power Sources 260, 50–56 (2014).

    Article  Google Scholar 

  21. Ryu, H.-H., Park, K.-J., Yoon, C. S. & Sun, Y.-K. Capacity fading of Ni-rich Li[NixCoyMn1−xy]O2 (0.6 ≤ x ≤ 0.95) cathodes for high-energy-density lithium-ion batteries: bulk or surface degradation? Chem. Mater. 30, 1155–1163 (2018).

    Article  Google Scholar 

  22. Yang, P. et al. Intragranular cracking as a critical barrier for high-voltage usage of layer-structured cathode for lithium-ion batteries. Nat. Commun. 8, 14101 (2017).

    Article  Google Scholar 

  23. Park, K.-J. et al. Degradation mechanism of Ni-enriched NCA cathode for lithium batteries: are microcracks really critical? ACS Energy Lett. 4, 1394–1400 (2019).

    Article  Google Scholar 

  24. Sun, Y.-K. et al. Nanostructured high-energy cathode materials for advanced lithium batteries. Nat. Mater. 11, 942–947 (2012).

    Article  Google Scholar 

  25. Kim, U.-H. et al. Microstructure‐controlled Ni‐rich cathode material by microscale compositional partition for next‐generation electric vehicles. Adv. Energy Mater. 9, 1803902 (2019).

    Article  Google Scholar 

  26. Park, K.-J. et al. Improved cycling stability of Li[Ni0.90Co0.05Mn0.05]O2 through microstructure modification by boron doping for Li-ion batteries. Adv. Energy Mater. 8, 1801202 (2018).

    Article  Google Scholar 

  27. Ryu, H.-H. et al. Li[Ni0.9Co0.09W0.01]O2: a new type of layered oxide cathode with high cycling stability. Adv. Energy Mater. 9, 1902698 (2019).

    Article  Google Scholar 

  28. Ryu, H.-H. et al. A highly stabilized Ni-rich NCA cathode for high-energy lithium-ion batteries. Mater. Today 36, 73–82 (2020).

    Article  Google Scholar 

  29. Yoon, C. S. et al. Cation ordering of Zr-doped LiNiO2 cathode for lithium-ion batteries. Chem. Mater. 30, 1808–1814 (2018).

    Article  Google Scholar 

  30. Kim, U.-H. et al. Compositionally and structurally redesigned high-energy Ni-rich layered cathode for next-generation lithium batteries. Mater. Today 23, 26–36 (2019).

    Article  Google Scholar 

  31. Meng, Y. S. et al. Cationordering in layered O3 Li[NixLi1/3−2x/3Mn2/3−x/3]O2(0≤ x ≤1/2) compounds. Chem. Mater. 17, 2386–2394 (2005).

    Article  Google Scholar 

Download references


This work was supported by a National Research Foundation of Korea (NRF) grant funded by the Korea government Ministry of Education and Science Technology (MEST) (no. NRF-2018R1A2B3008794). Additionally, this work was also supported by the Human Resources Development program (no. 20184010201720) of the Korea Institute of Energy Technology Evaluation and Planning funded by the Ministry of Trade, Industry and Energy of the Korean government. J.L. thanks the University of Washington for supporting his effort on this manuscript.

Author information

Authors and Affiliations



U.-H.K. and Y.-K.S. conceived and designed the research. U.-H.K., G.-T.P., B.-K.S. and G.W.N. performed the experiments and characterization of materials. U.-H.K., C.S.Y. and Y.-K.S. analysed the data. L.-Y.K. and P.K. performed the theoretical calculations. U.-H.K., C.S.Y., J.L. and Y.-K.S. contributed to the discussion of the results. C.S.Y. and Y.-K.S. wrote the manuscript. All the authors commented on and revised the manuscript.

Corresponding authors

Correspondence to Chong S. Yoon or Yang-Kook Sun.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Supplementary Note 1, refs. 1–4, Figs. 1–14 and Tables 1–3.

Rights and permissions

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Kim, UH., Park, GT., Son, BK. et al. Heuristic solution for achieving long-term cycle stability for Ni-rich layered cathodes at full depth of discharge. Nat Energy 5, 860–869 (2020).

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI:

Further reading


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing