Abstract
Replacing precious and nondurable Pt catalysts with cheap materials is a key issue for commercialization of fuel cells. In the case of oxygen reduction reaction (ORR) catalysts for direct methanol fuel cell (DMFC), the methanol tolerance is also an important concern. Here, we develop AlN nanowires with diameters of about 100–150 nm and the length up to 1 mm through crystal growth method. We find it is electrochemically stable in methanol-contained alkaline electrolyte. This novel material exhibits pronounced electrocatalytic activity with exchange current density of about 6.52 × 10−8 A/cm2. The single cell assembled with AlN nanowire cathodic electrode achieves a power density of 18.9 mW cm−2. After being maintained at 100 mA cm−2 for 48 h, the AlN nanowire-based single cell keeps 92.1% of the initial performance, which is in comparison with 54.5% for that assembled with Pt/C cathode. This discovery reveals a new type of metal nitride ORR catalyst that can be cheaply produced from crystal growth method.
Similar content being viewed by others
Introduction
Direct methanol fuel cell (DMFC) is one of the most attractive power sources for portable and vehicular applications due to the simplicity of the system and the adaptability of the liquid fuel1,2. At present, the commercialization of DMFCs is hindered by several issues, including crossover of methanol from anode to cathode3,4, as well as the dependence on precious Pt catalyst for methanol oxidation and oxygen reduction reactions5,6. Methanol transported through the membrane will be electrochemically oxidized at the cathode, thus reducing the cathodic reactant. And in intermediate reactions during this process, for instance the adsorption of carbon monoxide onto the catalyst surface, the cathode will also be poisoned, which further lowers its performance7,8,9.
Thus, the methanol-tolerant oxygen reduction reaction (ORR) catalysts have attracted much attention in recent years. One of the effective approaches is the nanostructured Pt alloy since Pt is the most effective electrocatalyst for ORR reaction. Pt-Pd Alloy Nanoflowers10, Pt/CoSe2 Nanobelt11, core-Shell Pt decorated PdCo12 and numbers of Pt alloy nanoparticles13,14,15,16 fall into this category. Although great advances have been achieved for the improvement of methanol tolerance, a high usage of Pt metal is still of great concern for further practical applications of DMFCs.
In recent years, some promising non-precious catalysts have been developed towards oxygen reduction reaction, including Co or Fe-based macrocyclic compounds17, transitional metal chalcogenides18, nitrogen-doped carbon nanotubes19, nitrogen-doped ordered mesoporous carbon20 and even nitrogen-doped graphene21,22. The transition metal nitride catalysts also displayed methanol-tolerance for ORR reactions. In comparison with a sharp ORR current decrease of ~80% for commercial Pt/C catalyst after the addition of a 3 M methanol at 90 s in the LSV test, it was reported that a sulfur-nitrogen Co-doped carbon foam catalyst has no noticeable decrease under the same test condition23. The similar behavior was also found for sulfur-nitrogen Co-doped graphene oxide24 and Co-doping carbon blacks with nitrogen- fluorine25.
With the recent advancement in anion-exchange membrane materials, there has been a growing interest in alkaline direct methanol fuel cell. Compared with proton exchange membrane under acidic environment, there are several significant advantages including the improved kinetics for both anodic alcohol oxidation reactions and cathodic oxygen reduction reactions, as well as a wide range of stable catalyst materials in alkaline media26,27,28. Many Pt-free catalysts exhibited excellent performance close to that of Pt in alkaline media, e.g., the maximum power density of alkaline direct methanol fuel cell assembled with fluorine-doped carbon black as the cathode achieved 14.56 mW cm−2 at 60°C, which is superior than a maxima of 9.44 mW cm−2 for commercial Pt/C29. Graphitic carbon nitride exhibited comparable ORR activity, better durability and methanol tolerance ability in comparison to Pt/C30.
Herein, we report an AlN nanowire with fine crystallization as oxygen reduction electrocatalyst in alkaline direct methanol fuel cell. Unlike the doped metal-N structure, the crystallized AlN is chemically stable in both acid and alkaline conditions, which should be helpful to improve the durability of fuel cells. The ORR activities were studied in an alkaline medium using cyclic voltammetry (CV) and rotating disk electrode (RDE) techniques. An alkaline direct methanol fuel cell test was constructed by using the so-formed materials as electrocatalyst in cathode. The performance of this single fuel cell demonstrated that the AlN nanowire catalyst is a promising methanol-tolerant candidate as oxygen reduction electrocatalyst for alkaline direct methanol fuel cell.
Results
The XRD pattern of the as-prepared sample (Figure 1) shows that the sample can be indexed as wurtzite AlN (a = 3.113 Å and c = 4.982 Å), agreeing well with the calculated diffraction pattern (ICDD-PDF No. 25-1133). No impure peaks have been detected within the instrumental resolution, indicating that the sample is wurtzite AlN with high purity. Figure 2a gives an overall view of the sample collected from the crucible lid, revealing that there are large-scale ultralong AlN nanowires with high density. SEM image with higher magnification (Figure 2b) indicates that the flexible nanowires are 100–150 nm in diameter and up to 1 mm in length with smooth surface and good toughness. The flexible structure and smooth surface of the ultralong nanowires are important for applications as catalyst in fuel cells. The typical TEM feature of a single AlN nanowire (Figure 2c) suggests a highly ordered and uninterrupted wire structure for the nanowires, where no segmentation or morphological imperfections, such as branching, are observed. High resolution TEM image (Figure 2d) indicates that an amorphous thin sheathed layer with thickness of 2–3 nm on the nanowire surface and no defects like dislocations and stacking faults are found, indicating the high crystalline nature of the nanowires. The surface area of the AlN nanowire catalyst was determined by using the N2 adsorption technique and the value is 43 m2/g, which is close to the calculated value with diameter of 100 nm.
Figure 3 shows the polarization and power density curves obtained in an alkaline DMFC single cell with PtRu/C electrodes on the anode side and either AlN nanowire catalyst or Pt/C as the cathode electrodes at 60°C. Clearly, the initial cell performance and power density of the single cell equipped with Pt/C are superior to those recorded for AlN nanowire. The open circuit potential (OCP) for both single cells is of ca. 0.89 V. The maximum power densities are of ca. 30.5 and 18.9 mW cm−2 for single cells with Pt/C or AlN nanowire cathode electrodes, respectively. After being maintained at 100 mA cm−2 for 48 h, the situation changes drastically. As shown in Fig. 3b the OCP for both single cells decreases to around 0.8 V, while the maximum power densities decrease to 16.9 and 17.4 mW cm−2 for Pt/C-based single cell and AlN nanowire-based single cell, respectively. Remarkably, the effect of running time on performance of the single cell assembled with AlN nanowire catalyst is less pronounced compared to that on performance of the single cell using Pt/C catalyst. The origin for the superior methanol tolerance of AlN should be ascribed to the inertness of AlN toward methanol oxidation.
Discussion
Electrochemical property of the AlN nanowire catalyst was performed by using cyclic voltammetry(CV) in N2 saturated 1 M KOH aqueous solution electrolyte with a scan rate of 50 mV s−1 (Figure 4). No significant oxidation or reduction current peaks are observed in the CV curve recorded from N2 saturated solution, indicating that the novel catalyst is electrochemically stable over the entire potential range (−0.9–+0.2 V vs. MMO). These results differed from other reports on non-noble ORR catalysts such as Fe–N/C containing instable metal ions that present redox couples within the electrochemical windows18. Furthermore, no significant oxidation or reduction current peak is observed in the curves when methanol was presented in the solution, demonstrating that the AlN nanowire is also chemically stable in methanol.
To assess their ORR activity, the AlN nanowire coated electrodes were also tested in O2 saturated KOH solution. As displayed in Figure 5, the reduction waves near −0.3 V vs. Hg/HgO indicate that the catalyst is active toward the ORR. The pronounced electrocatalytic activity is associated with an ORR onset potential at about −0.12 V vs. Hg/HgO. The cathodic current density achieved a value of −1.3 mA cm−2 at −0.28 V vs Hg/HgO. To examine the ORR kinetics and the corresponding kinetic parameters for the AlN nanowire catalyst, linear sweep voltammograms (LSVs) were recorded at various electrode rotation rates from 400 to 2000 rpm, in an O2 saturated solution with a rotating disk electrode (RDE) (Figure 5a). The current at low-potential range shows a typical increase with rotation rate due to the attenuated diffusion layer. The onset potential of AlN nanowire is more negative than that of the commercial Pt/C catalyst and it presents a slightly lower limiting current density than that of Pt/C, which consists with the results of single cell performance. However, for practical application in DMFC, the methanol crossover effect should also be considered. Thus, the current-time (i-t) chronoamperometric responses of Pt/C and AlN electrodes upon adding 3M methanol were recorded. (Figure. 5b) After the addition of methanol, the AlN electrode shows no noticeable change in its ORR current, indicating its superior methanol tolerance and high catalytic selectivity against methanol. While in contrast, an instantaneous current jump is observed for Pt/C electrode after the addition of methanol, which should be attributed to the initiation of methanol oxidation reaction (MOR). The different responses demonstrate the remarkably superior methanol tolerance of AlN nanowire to commercial Pt/C as the ORR catalyst.
By plotting applied electrode potential (E) as a function of log(id) (id is the disk current density), as shown in Figure 6, the Tafel slope and the intercept can be separately obtained. Thus, two important ORR kinetic parameters (the electron transfer coefficient, α and the exchange current density, i°) can be calculated. The exchange current density (i°) calculated through a Tafel equation is about 6.52 × 10−8 A/cm2, close to the exchange current density obtained for the O2 reduction on the Pt microelectrodes at acidic condition31,32. The number of electrons transferred (n) is calculated to be ~2.45 at −0.1–−0.2 V vs. Hg/HgO from the slopes of the Koutecky-Levich plots19, suggesting that the ORR catalyzed by the AlN nanowires is a mixed process of 2- and 4-electron transfer.
In conclusion, the crystallized AlN nanowires are elelctrochemically stable in alkaline conditions with or without methanol. No significant oxidation or reduction current peak is observed in the CV curve recorded from N2 saturated solution in the investigated potential range. Linear sweep voltammograms (LSVs) demonstrates that the AlN nanowire catalyst has a pronounced electrocatalytic activity with ORR onset potential at about −0.12 V vs. Hg/HgO and a high cathodic current density of −1.3 mA cm−2 at −0.28 V vs Hg/HgO. The exchange current density is about 6.52 × 10−8 A/cm2 and is independent on the methanol addition in the electrolyte. Single cell performance achieves 18.9 mW cm−2 for the DMFC with AlN nanowire cathode electrodes. After being maintained at 100 mA cm−2 for 48 h, the AlN nanowire-based cell keeps 92.1% of the initial performance, in comparison with 54.5% for the cell assembled with Pt/C cathode. The results demonstrated the AlN nanowire catalyst is a promising methanol-tolerant candidate as oxygen reduction electrocatalyst for alkaline direct methanol fuel cells.
Methods
Preparation of the AlN nanowire catalyst
AlN nanowire catalyst was conducted in a RF-heated furnace capable in the temperatures of 1700°C. TaC crucible with 30 mm in diameter and 50 mm in depth was used. AlN source materials sintered at 1500°C for 2 h served as charge. Fiber growth was carried out under a nitrogen (99.999%) pressure of 0.6 atm and a distance of 10 mm between the source and crucible lid. The estimated temperature gradient between the source and crucible lid was 3–7°C/mm. After growing for 2 hours, the AlN nanowire catalyst was collected from the crucible lid.
Structure analysis of the AlN nanowire catalyst
The morphology and micro-structure of the collected products were examined by SEM (Filiphis, XL-30) and HRTEM (Philip CM-200). The fiber orientation was identified by XRD. Here, XRD data were collected on a MACM18XHF diffractometer with Cu Kα radiation. The nitrogen adsorption and desorption isotherms at 77 K were collected by using a Micrometrics ASAP 2020 system. The samples were degassed overnight prior to the test. Brunauer–Emmett–Teller (BET) surface areas were estimated over a relative pressure (P/P0) range from 0.05 to 0.30.
Electrochemical performance of the AlN nanowire catalyst
The electrocatalytic characterization for the ORR on the electrocatalysts was evaluated in a 1 M KOH aqueous solution with or without methanol at 30°C using the Autolab PGSTAT-30 electrochemical system. The electrochemical measurements were made in a classical three-electrode electrochemical cell with a Pt mesh counter electrode and Hg/HgO (MMO) reference electrode. To prepare the working electrode, 10 μL of catalyst ink, consisting of 2 mg AlN nanowire catalyst per mL, was pipetted onto the surface of a GC disk electrode with a geometric area of 0.20 cm2. The catalyst loading was kept at 0.1 mg cm−2. After the coating dried, 5 μL of PBI solution (5wt% in Dimethylacetamide) was dropped onto the catalyst coating to form a catalyst layer.
Cyclic voltammograms and single-scan current-voltage curves were collected in the potential range of −0.9– 0.2 V vs. MMO at 50 mV/s. To evaluate the alcohol crossover tolerance of the electrocatalysts, solutions of 1 M KOH with 2 M methanol were used as the electrolyte Linear sweep voltammograms were conducted at 400, 800, 1200, 1600 and 2000 revolutions per minute (RPM) with a scan rate of 10 mV/s. The current –time (i–t) chronoamperometry was recorded for both Pt/C and AlN nanowire electrodes upon adding 3 M methanol at −0.4 V in O2-saturated 1 M KOH at a rotation rate of 1600 rpm.
Single cell performance of the AlN nanowire catalyst
KOH dope PBI film (100 μm thick) were used as polymer electrolyte membrane as reported33. Prior to fabricating electrodes, a homogeneous suspension composed of PTFE and carbon powder was sprayed onto the carbon paper (TGP-060, Toray Inc.) to form the gas diffusion layer with sublayer34. Catalyst slurry was prepared prior to the MEA fabrication. A commercial PtRu/C (Johnson Matthey, 30 wt%, Pt:Ru 2:1) was used as anode whereas AlN nanowire catalyst or commercial Pt/C (Johnson Matthey, 40 wt%) was used at the cathode side. During the preparation, Pt-Ru/C (1 g), AlN nanowire (1 g)/active carbon (0.3 g) or Pt/C(1 g) were mixed with 13 mL deionized water under vigorous stirring. Then 6.7 mL PBI solution (5wt% in Dimethylacetamide) was added to the mixture, followed by ultrasonic treatment for 30 min and a high-speed homogenizer for 1 h to form catalyst slurry. The catalyst slurry was applied to PTFE thin film by spraying. After dried at 60°C for 10 min followed with at 90°C in N2 atmosphere for 3 min, the catalyst layer was then transferred onto the membrane at 125°C and 10 MPa by the decal method to form the catalyst-coated membrane (CCM)35. The gas diffusion layers were placed on the anode and cathode side of the CCM to form the MEA. The Pt or AlN loading for both the anode and cathode catalyst layer was controlled by weight and the value was 0.8 mg/cm2.
Two flow-field plates made of high-density carbon with carved double-channel serpentine flow paths (1 mm wide and 1 mm deep) were fixed next to the MEA. Finally, the single fuel cell was assembled by two gold-plated copper end plates used as current collectors and assembled next to the flow-field plates. Fuel cells were tested at 60°C under ambient pressure conditions using 2 M methanol in 1 M KOH aqueous solution as fuel into the anode and oxygen as oxidant into the cathode. The flow rates for methanol and oxygen were kept constant with values of 20 and 40 mL/min, respectively. The cell voltage (V) was obtained by varying the current at 5 mA intervals and equilibrated for 7 s between the intervals during the polarization curve measurement using an Autolab PGSTAT-30 electrochemical system.
References
Sundarrajan, S., Allakhverdiev, S. I. & Ramakrishna, S. Progress and perspectives in micro direct methanol fuel cell. Int. J. Hydrogen Energ. 37, 8765–8786 (2012).
Liu, Z. et al. Sulfur-nitrogen co-doped three-dimensional carbon foams with hierarchical pore structures as efficient metal-free electrocatalysts for oxygen reduction reactions. Nanoscale 5, 3283–8 (2013).
Ahmed, M. & Dincer, I. A review on methanol crossover in direct methanol fuel cells: challenges and achievements. Int. J. Energ. Res. 35, 1213–1228 (2011).
Zenith, F. & Krewer, U. Simple and reliable model for estimation of methanol cross-over in direct methanol fuel cells and its application on methanol-concentration control. Energ. Environ. Sci. 4, 519–527 (2011).
Wang, Z. H. et al. Research Progress on Pt-Based Anode Catalysts in the Direct Methanol Fuel Cell. Acta Chim. Sinica 71, 1225–1238 (2013).
Basri, S., Kamarudin, S. K., Daud, W. R. W. & Yaakub, Z. Nanocatalyst for direct methanol fuel cell (DMFC). Int. J. Hydrogen Energ. 35, 7957–7970 (2010).
Du, C. Y., Zhao, T. S. & Yang, W. W. Effect of methanol crossover on the cathode behavior of a DMFC: A half-cell investigation. Electrochim. Acta 52, 5266–5271 (2007).
Liu, P., Yin, G. P. & Cai, K. D. Investigation on cathode degradation of direct methanol fuel cell. Electrochim. Acta 54, 6178–6183 (2009).
Tang, H. L., Pan, M., Jiang, S. P. & Yuan, R. Z. Modification of Nafion (TM) membrane to reduce methanol crossover via self-assembled Pd nanoparticles. Mater. Lett. 59, 3766–3770 (2005).
Fu, G. T. et al. One-Pot Water-Based Synthesis of Pt-Pd Alloy Nanoflowers and Their Superior Electrocatalytic Activity for the Oxygen Reduction Reaction and Remarkable Methanol-Tolerant Ability in Acid Media. J. Phys. Chem. C 117, 9826–9834 (2013).
Gao, M. R. et al. A Methanol-Tolerant Pt/CoSe2 Nanobelt Cathode Catalyst for Direct Methanol Fuel Cells. Angew. Chem. Int. Edit 50, 4905–4908 (2011).
Wang, D. L. et al. Pt-Decorated PdCo@Pd/C Core-Shell Nanoparticles with Enhanced Stability and Electrocatalytic Activity for the Oxygen Reduction Reaction.J. Am. Chem. Soc. 132, 17664–17666 (2010).
Trinh, Q. T., Yang, J. H., Lee, J. Y. & Saeys, M. Computational and experimental study of the Volcano behavior of the oxygen reduction activity of PdM@PdPt/C (M = Pt, Ni, Co, Fe and Cr) core-shell electrocatalysts J.Catal. 291, 26–35 (2012).
Liu, S. H., Zheng, F. S. & Wu, J. R. Preparation of ordered mesoporous carbons containing well-dispersed and highly alloying Pt-Co bimetallic nanoparticles toward methanol-resistant oxygen reduction reaction. Appl. Catal. B-Environ. 108, 81–89 (2011).
Taufany, F. et al. Relating Structural Aspects of Bimetallic Pt3Cr1/C Nanoparticles to Their Electrocatalytic Activity, Stability and Selectivity in the Oxygen Reduction Reaction. Chem.- Eur. J. 17, 10724–10735 (2011).
Yang, J. H., Zhou, W. J., Cheng, C. H., Lee, J. Y. & Liu, Z. L. Pt-Decorated PdFe Nanoparticles as Methanol-Tolerant Oxygen Reduction Electrocatalyst. ACS Appl. Mater. Interfaces 2, 119–126 (2010).
Lefevre, M., Proietti, E., Jaouen, F. & Dodelet, J. P. Iron-Based Catalysts with Improved Oxygen Reduction Activity in Polymer Electrolyte Fuel Cells. Science 324, 71–74 (2009).
Feng, Y. J. & Alonso-Vante, N. Nonprecious metal catalysts for the molecular oxygen-reduction reaction. Phys. Status Solid B 245, 1792–1806 (2008).
Gong, K. P., Du, F., Xia, Z. H., Durstock, M. & Dai, L. M. Nitrogen-Doped Carbon Nanotube Arrays with High Electrocatalytic Activity for Oxygen Reduction. Science 323, 760–764 (2009).
Yang, W., Fellinger, T.-P. & Antonietti, M. Efficient Metal-Free Oxygen Reduction in Alkaline Medium on High-Surface-Area Mesoporous Nitrogen-Doped Carbons Made from Ionic Liquids and Nucleobases. J. Am. Chem. Soc. 133, 206–209 (2010).
Li, Y. et al. An oxygen reduction electrocatalyst based on carbon nanotube-graphene complexes. Nat. nanotechnol. 7, 394–400 (2012).
Wu, Z.-S. et al. 3D Nitrogen-Doped Graphene Aerogel-Supported Fe3O4 Nanoparticles as Efficient Electrocatalysts for the Oxygen Reduction Reaction. J. Am. Chem. Soc. 134, 9082–9085 (2012).
Liu, Z. et al. Sulfur-nitrogen co-doped three-dimensional carbon foams with hierarchical pore structures as efficient metal-free electrocatalysts for oxygen reduction reactions. Nanoscale 5, 3283–3288 (2013).
Xu, J. X., Dong, G. F., Jin, C. H., Huang, M. H. & Guan, L. H. Sulfur and Nitrogen Co-Doped, Few-Layered Graphene Oxide as a Highly Efficient Electrocatalyst for the Oxygen-Reduction Reaction. Chemsuschem 6, 493–499 (2013).
Sun, X. J. et al. A Class of High Performance Metal-Free Oxygen Reduction Electrocatalysts based on Cheap Carbon Blacks. Sci. Rep. 3, (2013).
Goswami, G. K., Nandan, R., Barman, B. K. & Nanda, K. K. Excellent performance of Pt-free cathode in alkaline direct methanol fuel cell at room temperature. J. Mater. Chem. A 1, 3133–3139 (2013).
Ye, Y. S. et al. Alkali doped polyvinyl alcohol/graphene electrolyte for direct methanol alkaline fuel cells. J. Power Sources 239, 424–432 (2013).
Yu, E. H., Krewer, U. & Scott, K. Principles and Materials Aspects of Direct Alkaline Alcohol Fuel Cells. Energies 3, 1499–1528 (2010).
Sun, X. J. et al. Fluorine-Doped Carbon Blacks: Highly Efficient Metal-Free Electrocatalysts for Oxygen Reduction Reaction. ACS Catal. 3, 1726–1729 (2013).
Liu, Q. & Zhang, J. Y. Graphene Supported Co-g-C3N4 as a Novel Metal-Macrocyclic Electrocatalyst for the Oxygen Reduction Reaction in Fuel Cells. Langmuir 29, 3821–3828 (2013).
Parthasarathy, A., Davé, B., Srinivasan, S., Appleby, A. J. & Martin, C. R. The Platinum Microelectrode/Nafion Interface: An Electrochemical Impedance Spectroscopic Analysis of Oxygen Reduction Kinetics and Nafion Characteristics. J. Electrochem. Soc. 139, 1634–1641 (1992).
Xie, Z. & Holdcroft, S. Polarization-dependent mass transport parameters for orr in perfluorosulfonic acid ionomer membranes: an EIS study using microelectrodes. J. Electroanal. Chem. 568, 247–260 (2004).
Xing, B. & Savadogo, O. Hydrogen/oxygen polymer electrolyte membrane fuel cells (PEMFCs) based on alkaline-doped polybenzimidazole (PBI). Electrochem. commun. 2, 697–702 (2000).
Tang, H., Wang, S., Pan, M. & Yuan, R. Porosity-graded micro-porous layers for polymer electrolyte membrane fuel cells. J.Power Sources 166, 41–46 (2007).
Tang, H., Wang, S., Pan, M., Jiang, S. P. & Ruan, Y. Performance of direct methanol fuel cells prepared by hot-pressed MEA and catalyst-coated membrane (CCM). Electrochim. Acta 52, 3714–3718 (2007).
Acknowledgements
This work was financially supported by The National Basic Research Program of China (Grant No. 2013CB932901, 2010CB923200), Program for New Century Excellent Talents in University (NCET-13-0684), Fund of State Key Laboratory of Information Photonics and Optical Communications (Beijing University of Posts and Telecommunications, PR China), National Natural Science Foundation of China (Grant No. 61376018, 51372267, 51102019, 51272031).
Author information
Authors and Affiliations
Contributions
M.L., T.H.L. and W.J.W. conceived the idea, performed the experiments, analyzed and discussed data and wrote the paper; J.R.L. performed the characterization, revised the paper. J.W. and Y.G.W. contributed to the AlN synthesis, TEM and XRD experiments.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-sa/4.0/
About this article
Cite this article
Lei, M., Wang, J., Li, J. et al. Emerging methanol-tolerant AlN nanowire oxygen reduction electrocatalyst for alkaline direct methanol fuel cell. Sci Rep 4, 6013 (2014). https://doi.org/10.1038/srep06013
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep06013
This article is cited by
-
Designing methanol tolerant Pt islands at Pd on carbon promoting electrocatalytic oxygen reduction reaction in acidic media
Ionics (2022)
-
Pt3Ag alloy wavy nanowires as highly effective electrocatalysts for ethanol oxidation reaction
Nano Research (2020)
-
Ultrathin wavy Rh nanowires as highly effective electrocatalysts for methanol oxidation reaction with ultrahigh ECSA
Nano Research (2019)
-
Porous VOxNy nanoribbons supported on CNTs as efficient and stable non-noble electrocatalysts for the oxygen reduction reaction
Scientific Reports (2015)
-
Novel VN/C nanocomposites as methanol-tolerant oxygen reduction electrocatalyst in alkaline electrolyte
Scientific Reports (2015)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.