## Abstract

While lots of measurements describe the relaxation dynamics of the liquid state, experimental data of the glass dynamics at high temperatures are much scarcer. We use ultrafast scanning calorimetry to expand the timescales of the glass to much shorter values than previously achieved. Our data show that the relaxation time of glasses follows a super-Arrhenius behaviour in the high-temperature regime above the conventional devitrification temperature heating at 10 K/min. The liquid and glass states can be described by a common VFT-like expression that solely depends on temperature and limiting fictive temperature. We apply this common description to nearly-isotropic glasses of indomethacin, toluene and to recent data on metallic glasses. We also show that the dynamics of indomethacin glasses obey density scaling laws originally derived for the liquid. This work provides a strong connection between the dynamics of the equilibrium supercooled liquid and non-equilibrium glassy states.

## Introduction

One of the biggest challenges in condensed matter physics is the understanding of amorphous systems, which lack the long range order of crystalline materials^{1,2,3,4,5}. In spite of it, glasses are ubiquitous in our day life and many materials with technological significance display disordered atomic or molecular arrangements^{1}. Amorphous solids are usually obtained from the liquid state avoiding crystallisation. The relaxation time of the liquid increases exponentially during cooling, at a pace determined by its fragile or strong nature. In the laboratory time scale, around certain value of the relaxation time, the molecules do not have enough time to explore the complete configurational space and get trapped inside local energy minima, forming a glass^{1,2,3,4,5}. Below this temperature, upon further cooling, the relaxation time of the glass follows a much softer Arrhenius-like expression^{6}. For many years, there has been an increased interest in the time scales of physical processes occurring below the glass transition temperature, T_{g}, due to the importance of understanding and controlling relaxation processes in the glass. On the other hand, the inherent unstable nature of glasses has prevented detailed investigations of their properties during heating at temperatures above the conventional T_{g}, where a glass would irreversibly relax into the equilibrium liquid state.

Several models have been developed to comprehend the supercooled liquid (SCL) dynamics and the glass transition phenomena. Among them, the Adam-Gibbs (AG) formalism has provided a suggestive connection between the dynamics and the thermodynamics of amorphous systems^{7}.This model has been able to describe the relaxation behaviour of deeply supercooled liquids remarkably well, yielding the well-known Vogel-Fulcher-Tamman, VFT, equation^{8}, which is often used to evaluate the dynamics of supercooled liquids,

where τ_{0} is the limiting value of τ at an infinite temperature, D is a material constant related to its fragility and T_{0} is the diverging temperature. Many other theories are invoked to extend the modelling to the behaviour of liquids and glasses, such as the random first-order transition theory (RFOT)^{2}, the potential energy landscape (PEL)^{3}, the mode-coupling theory (MCT)^{9}, or the Coupling Model (CM)^{10}. The relaxation time of glasses has generated certain debate in the glass science community^{6,11}. Much below T_{g}, in the glass state, the configurational entropy of the system remains constant and, therefore, it is generally accepted that the dependence of the glass relaxation time with temperature responds to an Arrhenius expression^{6}. However, due to the intrinsically slow relaxation times of such systems below the glass transition temperature, the access to experimental data requires enormous amounts of time, which makes measurements impractically long^{12}. On the other hand, at higher temperatures, the glass irreversibly transforms into the supercooled liquid in shorter time scales. In this range, the access to relaxation time values requires both ultrafast heating and a rapid dynamic response, accessible through fast scanning nanocalorimetry^{13,14,15,16}. The influence of stability on the relaxation time of the glass is also a relevant topic in the current literature^{17,18}. A new procedure to increase the stability of a glass is to grow it by vapour-deposition at temperatures around 0.85 T_{g}^{19,20}. In optimum conditions, the stability of vapour-deposited glasses can be equivalent to the stability of conventional glasses aged for thousands or millions of years or cooled at rates many orders of magnitude slower than conventional methods allow^{21}. Therefore, by tuning the deposition conditions, vapour-deposited glasses offer a convenient route to explore the influence of stability on the melting of the glass over a much larger range than ever before.

Here, we perform heat capacity measurements in a broad range of heating rates, from 0.167 K/s up to 2 10^{4} K/s, of indomethacin (IMC) and toluene glasses embedded with different kinetic and thermodynamic stabilities. We also fit recent experimental data by Wang *et al*.^{22} on Au-based bulk metallic glasses (BMG) to support our conclusions. With the high heating rates achieved with fast scanning calorimetry, we expand the accessible timescales of the glass to much lower values than currently reported, which permits us to infer the dynamics over a large temperature interval. We propose that the kinetic behaviour of a liquid and all its isotropic glasses respond to the same dependence with the temperature and the thermodynamic stability of the system, evaluated through its enthalpic limiting fictive temperature. We also show that glasses of different stability, and therefore with different density, fulfil density scaling relations^{23,24,25} that were originally derived for the relaxation time of supercooled liquids measured at variable temperatures and pressures. The proposed generalization of the relaxation time could pave the way to a clearer connection between thermodynamic and dynamic parameters of a given system.

## Results

### VFT-like description of the dynamics of liquids and glasses

We use fast scanning calorimetry to determine the heat capacity of glasses of indomethacin and toluene. We infer values of relaxation time at the onset devitrification temperature, T_{on}, by applying the known relationship τ_{1}β_{1} = τ_{2}β_{2}^{26}. A reference value of τ_{1} = 100 s, considered as the relaxation time of the glass at T_{on} when heated at β_{1} = 0.167 K/s^{5,27}, is employed, though we remark that slight variations on this value would yield equivalent conclusions. On the other hand, we also estimate the transformation time of each glass at the maximum of the transformation peak using the expression t_{trans}(T_{max}) = ΔT/β_{m}, where ΔT is the width of the transformation peak and β_{m} the mid value of the heating rate during the transformation. Further details about the calculation of the relaxation and transformation times from heat capacity data can be found in the methods section. As shown in the Supplementary Fig. 3 both quantities yield comparable values. In the following we indistinctly use both measures to gauge the dynamics of the liquid and glassy states. Previous works have already considered this equivalence^{28}. Further support of their likeness can be found in the Supplementary Information.

To quantify the stability of the glass we use the enthalpic limiting fictive temperature, , defined as the temperature at which the glass and the supercooled liquid have the same enthalpy^{29}. At this temperature, the glass does not evolve thermodynamically. We remark that the measured values of limiting fictive temperature are independent of the heating rate of each calorimetric scan^{15,30}. The choice of a convenient heating rate, in the range 0.0167–2 ⋅ 10^{4} K/s, permits us to keep the system trapped in its initial glassy state along a larger temperature range, covering up to 75 K in temperature between the slowest and the fastest heating rates, while measuring the heat capacity during the transformation^{15}. Figure 1 portrays data of both relaxation (open squares) and transformation times (closed squares) for three different glasses: (a) vapour-deposited indomethacin glasses grown at T = 266, 290, 300 and 310 K and a liquid-cooled glass, CG, cooled at −0.0167 K/s; (b) vapour-deposited toluene glasses grown at 111, 113 and 116 K in equilibrium with the liquid state and (c) liquid-cooled Au-based bulk metallic glasses aged to equilibrium at 373 and 383 K (data from ref. 22). The relaxation times of the respective supercooled liquids are represented by triangles. The pink dashed line in Fig. 1a represents Arrhenius behaviour and is included to better visualize the non-Arrhenius description of the high temperature data. A plot of the relaxation times as a function of 1/T is shown as Fig. S4 in the SI.

To search for a common description of the experimental data of Fig. 1 we propose a generalization of Equation (1) aimed at describing the dynamics of supercooled liquids and glasses with different thermal stability:

where all the parameters have an analogous meaning as in Equation (1). In this case, however, D has been substituted by a linear function of the limiting fictive temperature of the glass, . In a supercooled liquid the fictive temperature T_{f} = T at all temperatures, from the definition of T_{f}. We remark that for a given glass-former, IMC, toluene or BMG, the only non-shared parameter in the fittings is . That is, all curves have the same fitting parameters but different values of . The only exception is the limiting fictive temperature of the conventional IMC glass cooled at −0.0167 K/s, which for convenience is set to 315 K^{31}. The resulting values of that yield the simultaneous fitting of all glasses and the SCL are in reasonable agreement with the measured enthalpic limiting fictive temperature of each glass (Supplementary Table 2). Table 1 shows the values of the fitting parameters. The green dashed line in Fig. 1a clearly highlights that in the probed temperature range, our experimental results differ from those predicted by the non-linear Adam-Gibbs-Vogel (AGV) equation^{17} which has been often applied to understand out-of-equilibrium behaviour in a short temperature range around the conventional T_{g}^{17}.

Considering that Equations (1) and (2) should be equivalent for a supercooled liquid, we derive the following equalities (see Supplementary Information):

The calculated values of D and τ_{0} are also shown in Table 1. Parameter D obtained for the supercooled liquid is related to the fragility, m, of the liquid^{32}. Evaluation of m yields m = 54 for the Au-based BMG, considering a T_{g} = 395 K (τ_{α} = 100 s), in fair agreement to the value measured by Wang *et al*., m = 49^{22}. The obtained fragility value for IMC is 89, similar to that measured by Wojnarowska *et al*.^{27} using dielectric spectroscopy, m = 83. In the case of toluene, we obtain a fragility m = 131. Kudlik *et al*.^{33} reported a fragility parameter for toluene of m = 122, while from the VFT expression reported by Hatase *et al*.^{34}, m = 130. We note that, under this framework, the values of D and τ_{0} can be obtained from relaxation data corresponding uniquely to the glassy state. This is in accordance with some previous works claiming that the properties of the supercooled liquid may be embedded in the properties of their glasses^{35,36}.

### Superposition of relaxation times

In the following we analyse the common description of the liquid and glassy state from another perspective. It has been shown that van der Waals’ bonded liquids and polymers obey power-law density scaling^{23,24,25}, which means that the average relaxation time of the liquid is a function of Tv^{γ}, where v(T, P) = 1/ρ is the specific volume and γ is a material constant. The idea behind the scaling of relaxation times arises from the consideration that the local dynamics of liquids are governed by a generalised repulsive potential that scales with γ, under the assumption of spherical symmetry. This assumption is not strictly valid for interactions such as hydrogen bonds, although even in these cases the power-law scaling yields superposition of relaxation times as a function of T and v.^{25} Although the scaling relationships were originally formulated for supercooled liquids, we extend them to glasses with different stabilities by introducing a dependence of the specific volume of the system on the limiting fictive temperature. In Fig. 2a we represent our relaxation data as a function of 1000ρ, where we set γ = 6.53. The detailed derivation of density values is given in the methods section.

Casalini *et al*.^{25} derived the expression considering that the relaxation time is governed by the entropy of the system, S_{c}, as the AG model proposes, but using a generalised equation for S_{c} that takes into account the influence of both temperature and, also, pressure (or, equivalently, changes in specific volume). In particular,

where τ_{0} and ϕ are constants and , with T_{g} the conventional value of glass transition temperature for IMC, 315 K, v_{g} the specific volume of a conventional glass at that temperature and γ is the scaling parameter used in Fig. 2a. As in the case of the scaling relationship, we substitute the effect of pressure on specific volume for that of glass stability and express v as . The experimental data shown in Fig. 2b have been simultaneously fitted using Equation (5), setting free the parameters τ_{0}, ϕ and γ. The values of are derived as indicated in the Methods section. The best fit is obtained with τ_{0} = 2.26 ⋅ 10^{−8} s, ϕ = 3.55 and γ = 6.53. Alternatively, we can also infer the value of γ from the slope of the logT_{g} vs logv_{g} curve, where T_{g} and v_{g} refer to the temperature and the specific volume of the system when the relaxation time equals 100 s, obtaining a value of 7 for the IMC glasses (see Supplementary Fig. 6).

The possibility to infer γ from measurements in the glassy state at ambient pressure, is promising. These findings support the idea that the dynamical behaviour of liquids and glasses can be explained and analysed under the same theoretical framework. Surprisingly, even the most stable glass (T_{dep} = 266 K, where hydrogen bonding between molecules are more abundant^{37}, is also reasonably well fitted by Equation (5). This is compatible with the pressure dependence of the glass transition, dT_{g}/dP, evaluated for IMC by Wojnarowska *et al*.^{27} The high value of lim_{P→0}(dT_{g}/dP) = 254 K/GPa, indicates that IMC could be regarded as a typical Van der Waals liquid.

## Discussion

We first focus on the potential role of the structure of the glass on the analysis of Fig. 1a. It is relatively well established that molecular packing anisotropy is a common characteristic of many vapour-deposited glasses^{20,38,39}. Recent studies on thin film ultrastable glasses have shown that the transformation into the SCL proceeds through a heterogeneous mechanism starting at surfaces/interfaces and that the growth front velocity does not uniquely depend on the enthalpy content of the glass^{15,40}. Our previous study concluded that the heterogeneous transformation of vapour-deposited thin film glasses of IMC could be divided into two families depending on the value of their birefringence, Δn^{40}. Glasses with large birefringence (>|0.02|) exhibit much larger growth front velocities compared to glasses with small birefringence (<|0.02|). It is therefore worth interrogating whether anisotropy or molecular packing plays any role in the homogeneous transformation of the glass into the supercooled liquid. If this was the case, one should question the validity of Equation (2) to simultaneously fit the liquid and glassy state, since this equation is a function of the enthalpy state of the glass, expressed through its limiting fictive temperature. Based on previous data^{39}, the glasses analysed here have Δn ≈ 0 except those grown at 266 K with a low Δn ≈ 0.02. We assume that the dynamics of the system during the bulk transformation is affected by the same parameters that affect the front transformation. Therefore, the simultaneous fit of the various glasses and the liquid state using a function of the enthalpy state of the glass is successful because those glasses behave as nearly isotropic from the point of view of the transformation into the SCL. In fact, attempts to include in Fig. 1a IMC glasses vapour-deposited at lower temperatures (T_{dep} < 250 K) and therefore with larger negative values of birefringence (Δn<−0.02) were not successful. It is important to note that the organic glasses analysed in the present work, those shown in Fig. 1a,b, are of bulk-type in the sense that their thickness is thick enough so they melt through a homogeneous process. In particular, the most stable IMC glasses exhibit homogeneous transformation for thicknesses above 900 nm^{15}, while for less stable glasses, the thickness threshold is lower^{40}.

It is interesting to note that glasses of two very different families, molecular and metallic, could be adjusted using Equation (2). The liquid-cooled Au-based metallic glasses measured in ref. 22 and shown in Fig. 1c were aged for long times and equilibrated at the two temperatures of 373 and 383 K before being scanned up at fast heating rates using a Flash DSC. It is worth pointing out that beta relaxation processes are typically important in metallic glasses^{41}, and, in fact, short time aging of the Au-based glasses produced a simultaneous decrease of both T_{on} and T_{f}, in clear contradiction with the Equation (2). However, at the longer aging times needed for equilibration, the alpha relaxation time dominates over the beta relaxation and a decrease of T_{f} is accompanied by an increase of T_{on}. It is however early to draw more general statements due to the scarcity of data in the high temperature regime. The popularisation of fast scanning methods will allow, in the years to come, to test the validity of VFT-type equations, such as Equation (2), on a much larger number of materials. On the other hand, we are aware that a single fictive temperature value does not provide a unique description of the state of the glass^{42,43,44}. However, our analysis suggests that a single enthalpic offers a reasonable account of the dynamics of the glass in the medium-to-high temperature regime. We assume that the behaviour observed here is specific to glasses with a sufficiently narrow spatial distribution of inhomogeneities to allow for a single description of the glass.

The fact that IMC glasses obey analogous density scaling relations as the supercooled liquid suggests that there are two relevant parameters controlling the dynamics in both the liquid and the glassy state: temperature and density. The scaling parameter obtained for glasses, γ_{glass} = 6.53, is, however, different to that of the supercooled liquid, γ_{SCL} = 3.84, obtained from reported PVT data^{45} (see Supplementary Information for the derivation of this value). A common scaling exponent for all IMC glasses and the supercooled liquid could only be obtained with an unrealistic value of γ = 9.1, very far from the experimental value reported for the SCL. This may seem at odds with the common description of Fig. 1. In the first section of this paper, we have shown that the relaxation data of IMC glasses and the supercooled liquid measured at atmospheric pressure could be simultaneously fitted using the same VFT-type expression, where the only variables were temperature and the limiting fictive temperature. However, the density of glasses and the supercooled liquid is not univocally determined by the fictive temperature of the system. In fact, the isobaric thermal expansion coefficient of IMC supercooled liquid at T = 315 K is α_{p,SCL} = 5.69 10^{−4} K^{−1}, while, in the case of the IMC glass in equilibrium with the liquid at the same temperature is α_{p,SCL} = 1.32 10^{−4} K^{−1}. Therefore, it is not surprising that the relaxation dynamics of glasses and their supercooled liquid can be simultaneously described using an expression with the limiting fictive temperature as variable parameter and not using the density.

The relation between the scaling exponent, γ, obtained from data fitting using Equation 5 and the Grüneisen parameter

is also a subject of intense research^{23,25,46}. While at the origin these two parameters were considered to be equivalent, it was found significant discrepancy between them^{25}. This discrepancy was recently solved by proposing that the energy distribution of the activation barrier for molecular rearrangements depends on the density of the system^{46},

where γ_{EOS} is a constant.

Under this framework, the scaling exponent from Equation 5 is reinterpreted as

where D is the same as in Equation 5. We saw before that γ_{glass} = 6.53 and γ_{SCL} = 3.84, while, from Equation 6, γ_{G,glass} = 0.79 (glass with T_{f} = 279 K) and γ_{G,SCL} = 2.25. These values yield, according to eq. 8, γ_{EOS,glass} = 20.38 and γ_{EOS,SCL} = 7.6, meaning that the energy of the activation barriers is more sensitive to density changes in the case of the non-equilibrium glassy state than in the supercooled liquid.

## Conclusions

In essence, we establish that the temperature dependence of the relaxation time for two organic and one metallic glass exhibit a super-Arrhenius behaviour in a medium-to-high temperature range. More importantly, generalised VFT-type equations that depend on the average limiting fictive temperature of the glass can be used to simultaneously describe the relaxation time of nearly-isotropic glasses with different stabilities and the supercooled liquid. The fact that density scaling in glasses of different stability was successfully applied using an expression originally derived for supercooled liquids reinforce the analogy between the dynamic behaviour of glasses and liquids. We hope this work will help other researchers to establish closer connections between the liquid and glassy states of matter.

## Methods

### Growth and calorimetry measurements

IMC layers with thicknesses ranging from 600 nm to 2 μm were grown by thermal evaporation in a UHV chamber at 3·10^{−8 }mbar, using an effusion cell (CREATEC) held at a constant temperature of around 440 K. IMC crystalline powder (99.9% purity) was acquired from Sigma-Aldrich and used as received. The evaporation rate, set at 0.15 nm/s, was monitored with a quartz microbalance (Sycon) located close to the substrate. Samples with different stabilities were produced by depositing them at different substrate temperatures, from 266 to 310 K. A liquid nitrogen cold trap was used to reduce the vapour pressure of certain contaminants, especially water. Conventional glasses have been produced by heating a deposited layer above their glass transition temperature, 315 K, and cooling them at a constant cooling rate of −10 K/min. The choice of thicknesses ensured that the main mechanism of the transformation into the supercooled liquid was homogeneous through the entire sample and not heterogeneous as occurs in thinner films.

In order to study the transformation kinetics of the deposited glasses along a wide temperature range, different calorimetric techniques and methodologies were applied.

In the high temperature range (τ below 10

^{−2 }s), quasi adiabatic fast-scanning calorimetry is employed^{13,15,16}. Fast heating rates (from 10^{3}to 10^{5 }K/s), raise the glass transition temperature by tenths of degrees. The samples are deposited onto a membrane-based calorimetric cell. A shadow mask placed between the calorimetric cell and the vapour-flux assures that the material is deposited within the sensing area of the device (1 mm^{2}). Prior to the experiments, a 200 nm aluminium film is deposited onto the sensing area of the membrane to improve the temperature distribution. A model^{13}is applied in order to obtain heat capacity data from the raw voltage data obtained from the measurement.To measure the transformation kinetics in the medium-to-high temperature range (τ between 1 and 10

^{−2}s), we apply a non-constant intensity to the same nanocalorimetric cell, increasing its value with time, with the possibility of reaching constant but intermediate heating rates, ranging from 10 to 10^{3 }K/s. At these heating rates, the measurements are not strictly adiabatic and, therefore, thermal losses between the sample and the environment are present. From the apparent heat capacity we extract the onset temperature and the width of the transformation peak.Differential Scanning Calorimetry with a Perkin Elmer DSC7 is used to measure the transformation kinetics in the low temperature range (τ between 10

^{2}and 1 s). We deposit 1.5 μm thick samples onto aluminium foil, which is subsequently folded and introduced into a DSC aluminium pan. The time between the extraction of the sample from the deposition chamber and the placement of the pan into the DSC cell was reduced at maximum to avoid water absorption into the glass.The transformation times at the lowest temperature range (τ above 10

^{2 }s) were determined by isothermal experiments. In the case of samples with intermediate stability (with T_{f}> 280 K),*in-situ*isotherms were performed in order to avoid water absorption during the process. In those measurements 1.5 μm thick layers are deposited onto the calorimetric cell and kept at a given temperature (annealing temperature). After time t, a calorimetric scan at low heating rate is performed to determine the onset temperature of the annealed sample. From the Cp curve we can know whether the sample has been transformed or not. The represented value of transformation time corresponds to the mean between the larger annealing time of the non-transformed samples and the shorter annealing time of a completely transformed sample. In the case of ultrastable glasses (T_{dep}= 266 K), the power output of the DSC was registered during an isotherm at the temperature of interest, following the sample preparation method described previously in point (3).

In all cases except for the isothermal experiments, the deposition temperature was controlled by the device itself, feeding it with a non-variable value of intensity during the deposition, reaching a constant temperature. In the case of the isothermal experiments, the deposition temperature is controlled by means of heating resistances and a Pt100 sensor attached to the socket where the measuring device is placed.

The limiting fictive temperature of glasses grown at different deposition temperatures is measured by integrating the specific heat data obtained from slow heating rates measurements performed in the DSC and from ultra-fast heating rate measurements performed by quasi-adiabatic fast-scanning nanocalorimetry in thin layers. The details of the procedure have been described elsewhere^{15}. In the case of intermediate heating rates, the non-adiabatic conditions of the experiment preclude the proper evaluation of reliable values of limiting fictive temperature.

### Analysis of heat capacity data: Derivation of relaxation and transformation times

Once the heat capacity is derived from the raw data, we perform the following analysis to obtain the values of transformation and relaxation times. In the first case, we employ the expression τ_{1}β_{1} = τ_{2}β_{2} to calculate the relaxation time, τ_{2}, of a glass of a given stability at the onset temperature of the transformation when heated at a given rate, β_{2}, considering as reference value of relaxation time τ_{1} = 100 s when the heating rate is β_{1} = 0.167 K/s (Supplementary Fig. 1a). In the second case, we consider the temperature at the maximum of the transformation peak for each glass measured at each heating rate. The transformation time corresponding to this temperature is calculated as t_{trans} (T_{max}) = ΔT/β_{m}, where ΔT is the peak amplitude at its base and β_{m} is the mid value of heating rate (Supplementary Fig. 1b). The methodology is tested by comparing the transformation times obtained with this approach to those measured through isothermal measurements at specific temperatures, (details given in supplementary information). The width of the transformation peaks evaluated at a given temperature (T_{max}) remains approximately constant for glasses of different stabilities. This fact, together with the observation by Talansky *et al*.^{47} that the distribution of transformation times in a vapour-deposited glass of methyl-m-toluate was around 25%, permits us to infer that the potential variation of this parameter among the different glasses, if any, is below our experimental uncertainty in the evaluation of ΔT and will not affect our conclusions.

### Calculation of density as a function of stability and temperature

The density of the conventional IMC glass at ambient conditions is 1.31 g/cm^{3 }^{48}. The density of indomethacin glasses with different stability is calculated from the density variations reported by Dalal *et al*.^{39}, measured at 293 K (Supplementary Fig. 4). The variation of density with temperature has been calculated from the reported thermal expansion coefficients, , and ^{39}. For intermediate stabilities, a linear interpolation between these values has been performed. The reference density of supercooled IMC has been chosen to be equal to the density of the conventional glass, = 315 K, at T_{ref} = 315 K.

Different values of conventional IMC glass density have been reported^{49}. However, it should be noted that while the choice of a different reference value of density shifts the curves towards lower or higher values of Tv^{γ}, it does not appreciably change the scaling factor.

## Additional Information

**How to cite this article**: Rodríguez-Tinoco, C. *et al*. Relaxation dynamics of glasses along a wide stability and temperature range. *Sci. Rep.* **6**, 35607; doi: 10.1038/srep35607 (2016).

## References

- 1.
Debenedetti, P. G. & Stillinger, F. H. Supercooled liquids and the glass transition.

*Nature***410**, 259–267 (2001). - 2.
Lubchenko, V. & Wolynes, P. G. Theory of structural glasses and supercooled liquids.

*Annu. Rev. Phys. Chem.***58**, 235–266 (2007). - 3.
Raza, Z., Alling, B. & Abrikosov, I. A. Computer simulations of glasses: the potential energy landscape.

*J. Phys. Condens. Matter***27**, 293201 (2015). - 4.
Ediger, M. D., Angell, C. A. & Nagel, S. R. Supercooled Liquids and Glasses.

*J. Phys. Chem.***100**, 13200–13212 (1996). - 5.
Cavagna, A. Supercooled liquids for pedestrians.

*Phys. Rep*.**476**, 51–124 (2009). - 6.
Johari, G. P. & Shanker, R. M. On determining the relaxation time of glass and amorphous pharmaceuticals’ stability from thermodynamic data.

*Thermochim. Acta***511**, 89–95 (2010). - 7.
Adam, G. & Gibbs, J. H. On the Temperature Dependence of Cooperative Relaxation Properties in Glass-Forming Liquids.

*J. Chem. Phys.***43**, 139 (1965). - 8.
Angell, C. A. Entropy and fragility in supercooling liquids.

*J. Res. Natl. Inst. Stand. Technol.***102**, 171 (1997). - 9.
Kob, W.

*The Mode-Coupling Theory of the Glass Transition*.**676**, (American Chemical Society, 1997). - 10.
Ngai, K. L.

*Relaxation and Diffusion in Complex Systems*doi: 10.1007/978-1-4419-7649-9 (Springer-Verlag: New York, , 2011). - 11.
Shamblin, S. & Tang, X. Characterization of the time scales of molecular motion in pharmaceutically important glasses.

*J. Phys. Chem. B***103**, 4113–4121 (1999). - 12.
Welch, R. C.

*et al.*Dynamics of Glass Relaxation at Room Temperature.*Phys. Rev. Lett.***110**, 265901 (2013). - 13.
Efremov, M. Y.

*et al.*Thin-film differential scanning nanocalorimetry: heat capacity analysis.*Thermochim. Acta***412**, 13–23 (2004). - 14.
Lopeandía, A. F., Rodríguez-Viejo, J., Chacón, M., Clavaguera-Mora, M. T. & Muñoz, F. J. Heat transfer in symmetric U-shaped microreactors for thin film calorimetry.

*J. Micromechanics Microengineering***16**, 965–971 (2006). - 15.
Rodríguez-Tinoco, C.

*et al.*Evaluation of growth front velocity in ultrastable glasses of indomethacin over a wide temperature interval.*J. Phys. Chem. B***118**, 10795–10801 (2014). - 16.
León-Gutierrez, E.

*et al.**In situ*nanocalorimetry of thin glassy organic films.*J. Chem. Phys.***129**, 181101 (2008). - 17.
Brian, C. W., Zhu, L. & Yu, L. Effect of bulk aging on surface diffusion of glasses.

*J. Chem. Phys.***140**, 054509 (2014). - 18.
Richert, R., Lunkenheimer, P., Kastner, S. & Loidl, A. On the derivation of equilibrium relaxation times from aging experiments.

*J. Phys. Chem. B***117**, 12689–12694 (2013). - 19.
Swallen, S. F.

*et al.*Organic glasses with exceptional thermodynamic and kinetic stability.*Science***315**, 353–356 (2007). - 20.
Rodríguez-Tinoco, C., Gonzalez-Silveira, M., Ràfols-Ribé, J., Garcia, G. & Rodríguez-Viejo, J. Highly stable glasses of celecoxib: Influence on thermo-kinetic properties, microstructure and response towards crystal growth.

*J. Non. Cryst. Solids***407**, 256–261 (2015). - 21.
Pérez-Castañeda, T., Jiménez-Riobóo, R. J. & Ramos, M. A. Two-Level Systems and Boson Peak Remain Stable in 110-Million-Year-Old Amber Glass.

*Phys. Rev. Lett.***112**, 165901 (2014). - 22.
Wang, J. Q., Shen, Y., Perepezko, J. H. & Ediger, M. D. Increasing the kinetic stability of bulk metallic glasses.

*Acta Mater*.**104**, 25–32 (2016). - 23.
Roland, C. M., Feldman, J. L. & Casalini, R. Scaling of the local dynamics and the intermolecular potential.

*J. Non. Cryst. Solids***352**, 4895–4899 (2006). - 24.
Dyre, J. C. Hidden scale invariance in condensed matter.

*J. Phys. Chem. B***118**, 10007–10024 (2014). - 25.
Casalini, R., Mohanty, U. & Roland, C. M. Thermodynamic interpretation of the scaling of the dynamics of supercooled liquids.

*J. Chem. Phys.***125**, 014505 (2006). - 26.
Johari, G. P. Comment on ‘glass transition in pure and doped amorphous solid water: an ultrafast microcalorimetry study’.

*J. Chem. Phys.***127**, 157101 (2007). - 27.
Wojnarowska, Z.

*et al.*Broadband dielectric relaxation study at ambient and elevated pressure of molecular dynamics of pharmaceutical: indomethacin.*J. Phys. Chem. B***113**, 12536–12545 (2009). - 28.
Busch, R., Bakke, E. & Johnson, W. L. Viscosity of the supercooled liquid and relaxation at the glass transition of the Zr46.75Ti8.25Cu7.5Ni10Be27.5 bulk metallic glass forming alloy.

*Acta Mater*.**46**, 4725–4732 (1998). - 29.
Moynihan, C. T., Easteal, A. J., Bolt, M. A. & Tucker, J. Dependence of the Fictive Temperature of Glass on Cooling Rate.

*J. Am. Ceram. Soc.***59**, 12–16 (1976). - 30.
Gao, S. & Simon, S. L. Measurement of the limiting fictive temperature over five decades of cooling and heating rates.

*Thermochim. Acta***603**, 123–127 (2015). - 31.
Kearns, K. L., Swallen, S. F., Ediger, M. D., Sun, Y. & Yu, L. Calorimetric evidence for two distinct molecular packing arrangements in stable glasses of indomethacin.

*J. Phys. Chem. B***113**, 1579–1586 (2009). - 32.
Böhmer, R., Ngai, K. L., Angell, C. A. & Plazek, D. J. Nonexponential relaxations in strong and fragile glass formers.

*J. Chem. Phys.***99**, 4201 (1993). - 33.
Kudlik, A., Tschirwitz, C., Benkhof, S., Blochowicz, T. & Rössler, E. Slow secondary relaxation process in supercooled liquids.

*Europhys. Lett.***40**, 649–654 (1997). - 34.
Hatase, M., Hanaya, M., Hikima, T. & Oguni, M. Discovery of homogeneous-nucleation-based crystallization in simple glass-forming liquid of toluene below its glass-transition temperature.

*J. Non. Cryst. Solids***307–310**, 257–263 (2002). - 35.
Scopigno, T., Ruocco, G., Sette, F. & Monaco, G. Is the fragility of a liquid embedded in the properties of its glass?

*Science***302**, 849–852 (2003). - 36.
Pogna, E. A. A.

*et al.*Probing equilibrium glass flow up to exapoise viscosities.*Proc. Natl. Acad. Sci. USA***112**, 2331–2336 (2015). - 37.
Dawson, K. J., Kearns, K. L., Ediger, M. D., Sacchetti, M. J. & Zografi, G. D. Highly stable indomethacin glasses resist uptake of water vapor.

*J. Phys. Chem. B***113**, 2422–2427 (2009). - 38.
Yokoyama, D., Sakaguchi, A., Suzuki, M. & Adachi, C. Horizontal molecular orientation in vacuum-deposited organic amorphous films of hole and electron transport materials.

*Appl. Phys. Lett.***93**, 173302 (2008). - 39.
Dalal, S. S., Fakhraai, Z. & Ediger, M. D. High-throughput ellipsometric characterization of vapor-deposited indomethacin glasses.

*J. Phys. Chem. B***117**, 15415–15425 (2013). - 40.
Rodriguez-Tinoco, C., Gonzalez-Silveira, M., Rafols-Ribe, J., Lopeandia, A. F. & Rodriguez-Viejo, J. Transformation kinetics of vapor-deposited thin film organic glasses: the role of stability and molecular packing anisotropy.

*Phys. Chem. Chem. Phys.***17**, 31195–31201 (2015). - 41.
Yu, H. Bin, Wang, W. H., Bai, H. Y. & Samwer, K. The β-relaxation in metallic glasses.

*Natl. Sci. Rev*.**1**, 429–461 (2014). - 42.
Lubchenko, V. & Wolynes, P. G. Theory of aging in structural glasses.

*J. Chem. Phys.***121**, 2852–2865 (2004). - 43.
Mauro, J. C., Loucks, R. J. & Gupta, P. K. Fictive Temperature and the Glassy State.

*J. Am. Ceram. Soc*.**92**, 75–86 (2009). - 44.
Ritland, H. N. Limitations of the Fictive Temperature Concept.

*J. Am. Ceram. Soc.***39**, 403–406 (1956). - 45.
Adrjanowicz, K., Grzybowski, A., Grzybowska, K., Pionteck, J. & Paluch, M. Toward Better Understanding Crystallization of Supercooled Liquids under Compression: Isochronal Crystallization Kinetics Approach.

*Cryst. Growth Des.***13**, 4648–4654 (2013). - 46.
Paluch, M.

*et al.*A Relationship between Intermolecular Potential, Thermodynamics, and Dynamic Scaling for a Supercooled Ionic Liquid.*J. Phys. Chem. Lett.***1**, 987–992 (2010). - 47.
Tylinski, M.

*et al.*Vapor-deposited glasses of methyl-m-toluate: How uniform is stable glass transformation?*J. Chem. Phys.***143**, 244509 (2015). - 48.
Kearns, K. L., Still, T., Fytas, G. & Ediger, M. D. High-modulus organic glasses prepared by physical vapor deposition.

*Adv. Mater.***22**, 39–42 (2010). - 49.
Yoshioka, M., Hancock, B. C. & Zografi, G. Crystallization of indomethacin from the amorphous state below and above its glass transition temperature.

*J. Pharm. Sci.***83**, 1700–1705 (1994).

## Acknowledgements

This research was supported by MINECO through Projects MAT2013-40986-P and MAT2014-57866- REDT. We thank discussions with K. Ngai, M. Ediger and J.L. Tamarit.

## Author information

## Affiliations

### Physics Department, Universitat Autònoma de Barcelona, 08193 Bellaterra, Spain

- C. Rodríguez-Tinoco
- , J. Ràfols-Ribé
- , M. González-Silveira
- & J. Rodríguez-Viejo

## Authors

### Search for C. Rodríguez-Tinoco in:

### Search for J. Ràfols-Ribé in:

### Search for M. González-Silveira in:

### Search for J. Rodríguez-Viejo in:

### Contributions

C.R.-T. and M.G.-S. conceived the idea, C.R.-T. and J.R.-R. performed the experiments, C.R.-T. and M.G.-S. analysed the data, J.R.-V. and M.G.-S. supervised the work, C.R.-T. and J.R.-V., with the help of all authors, wrote the paper. All authors contribute to the discussion of the results.

### Competing interests

The authors declare no competing financial interests.

## Corresponding author

Correspondence to J. Rodríguez-Viejo.

## Supplementary information

## PDF files

## Rights and permissions

To obtain permission to re-use content from this article visit RightsLink.

## Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/