## Abstract

Recently, the layered semimetal WTe_{2} has attracted renewed interest owing to the observation of a non-saturating and giant positive magnetoresistance (~10^{5}%), which can be useful for magnetic memory and spintronic devices. However, the underlying mechanisms of the giant magnetoresistance are still under hot debate. Herein, we grew the stoichiometric and non-stoichiometric WTe_{2} crystals to test the robustness of giant magnetoresistance. The stoichiometric WTe_{2} crystals have magnetoresistance as large as 3100% at 2 K and 9-Tesla magnetic field. However, only 71% and 13% magnetoresistance in the most non-stoichiometry (WTe_{1.80}) and the highest Mo isovalent substitution samples (W_{0.7}Mo_{0.3}Te_{2}) are observed, respectively. Analysis of the magnetic-field dependent magnetoresistance of non-stoichiometric WTe_{2} crystals substantiates that both the large electron-hole concentration asymmetry and decreased carrier mobility, induced by non-stoichiometry, synergistically lead to the decreased magnetoresistance. This work sheds more light on the origin of giant magnetoresistance observed in WTe_{2}.

## Introduction

Magnetoresistance (MR) is the change of electrical resistance under the application of a magnetic field. The materials with large MR can generate great potential applications in magnetic sensors^{1}, magnetic information storage^{2}, and so on. Recently, giant (~1.5 × 10^{5}% at 2 K and 9 Tesla magnetic field) and non-saturated MR is observed in two-dimensional (2D) layered transition-metal dichalcogenides WTe_{2}^{3}. It leads to a series of works to study the novel physical properties of WTe_{2}, such as superconductivity with *T*_{c} as high as 7 K under external mechanical pressure^{4}, and possible quantum spin Hall effect in monolayer WTe_{2} with bulk electronic energy band-gap as large as 100.0 meV^{5}. Certainly, the origin of extremely large MR is not only an important physical problem, but also valuable to device application of WTe_{2}. As it was proposed, the main physical origin of giant MR is attributed to the nearly perfect compensation of electron and hole pockets^{3}. This opinion is supported by subsequent Fermi surface determination by angle-resolved photoemission spectroscopy (ARPES)^{6}, as well as suppressed MR under external mechanical pressure^{7}.

However, recent work based on detailed ARPES claims that there are more subtle details in electronic band structure and abstract Fermi surface morphology in WTe_{2}^{8}. Quantum oscillation of MR (Shubnikov-de-Haas oscillation) substantiates that there are multiple fermion pockets^{9}. Some studies find evidences for spin-orbit split bands in WTe_{2}. Spin-orbit split bands suppress the inter- and intra-band backscattering^{10}. In addition, a latest study implies that the large MR in WTe_{2} also may be related to the crystal quality or carrier mobility^{11}, and the more apparent decreased effect of MR to aliovalent doping (Re and Ta) over simple isovalent substitution (Mo-doping) and the different growth method also support it^{12}. The physical origin of extremely large MR observed in WTe_{2} therefore is still an open question.

In this work, considering the above-mentioned confusion, we intentionally introduce the non-stoichiometry and isovalent doping Mo in WTe_{2} to investigate the dependence among electron-hole asymmetry, carrier mobility and MR. Our systematic MR and Hall effect measurements substantiate the extremely large MR in stoichiometric WTe_{2}. But large MR is disappeared in non-stoichiometric and isovalent Mo substitution WTe_{2} crystals. Based on analysis of magnetic-field dependent MR, both enlarged electron-hole concentration asymmetry and decreased mobility synergistically lead to the decreased MR in doped WTe_{2}. From the viewpoint of real application, our result suggests that significant MR is strongly dependent on the stoichiometry of WTe_{2}.

## Results

The optical micrograph of the synthesized crystals is shown in Fig. 1(a). The crystals show metallic luster and sheet-shape morphology. And the largest sample can be reached to 9 × 5 × 0.5 mm^{3}. The XRD patterns of single crystal W_{1−x}Mo_{x}Te_{2−y} samples are depicted in Fig. 1(b). Only the (00*l*) reflections are observed in these curves. It suggests that the exposed surface of crystals (see Fig. 1(a)) belongs to *ab*-plane and the thinnest dimension is along the *c*-axis. To show the effect of Mo substituted and non-stoichiometric on the lattice constant clearly, we plot the *c*-axis lattice parameter *d*_{c} for all W_{1−x}Mo_{x}Te_{2−y} samples in Fig. 1(c). It displays that the *c*-axis lattice parameter *d*_{c} decreases monotonically with increasing *y* or *x*. As a result, we suggest that the Mo^{4+} ions enter into W-sites, due to the ionic radius of Mo^{4+} ions (0.65 Å) being smaller than that of W^{4+} (0.66 Å), which gives rise to the decrease in the lattice parameter *d*_{c}^{13}. By the same mechanism, the lack of Te element also can lead to the decrease of the lattice parameters (see the black line of Fig. 1(c)). Figure 1(d) plots the EDS spectra of three representative samples of WTe_{2}, WTe_{1.80} and W_{0.7}Mo_{0.3}Te_{2} crystals. These results prove that the samples with varied chemical composition are obtained.

Figure 2(a) depicts the typical temperature-dependent *ab*-plane resistivity *ρ*_{xx}, measured from 2 K to 300 K, for the stoichiometric and non-stoichiometric WTe_{2} crystals. They all show the metallic behavior but with different residual resistance. Quantitatively, the residual resistance of WTe_{2}, WTe_{1.90}, WTe_{1.85} and WTe_{1.80} are 8.0 × 10^{−6}, 5.4 × 10^{−5}, 5.9 × 10^{−5} and 7.4 × 10^{−5} Ω·cm, respectively. One can see that stoichiometric WTe_{2} sample has the minimum residual resistance. It infers that non-stoichiometry does induce the high density of defects/impurities, which in turn increases the residual resistance in non-stoichiometric WTe_{2} crystals^{14}. The temperature-dependent resistances of stoichiometric and Mo substituted WTe_{2} crystals are presented in Fig. 2(b). As the same as the non-stoichiometric WTe_{2−y}, they also demonstrate the metallic behavior and raising the Mo-substituting concentration increases the residual resistance of W_{1−x}Mo_{x}Te_{2} samples too. The relationship between the residual resistance *ρ*_{res}, as well as the residual resistivity ratio (RRR) and Mo-substituting concentration *x* and non-stoichiometric concentration *y* are presented in Fig. 2(c). It substantiates that upon raising the Te deficiency and the Mo concentration, the density of defects/impurities in non-stoichiometric WTe_{2} samples gradually increases.

In order to study the influence of the chemical composition changes on the MR property of WTe_{2}, the transport properties of stoichiometric WTe_{2} crystals were investigated firstly. Figure 3(a) shows the curves of MR *vs* external magnetic field for WTe_{2} crystals under variable temperatures. The MR is defined as

where *ρ*_{xx} and B are longitudinal resistance and magnetic field, respectively. One can see that curves of the MR are parabola-like up to 9 T. And the most impressive feature is that the MR of stoichiometric WTe_{2} reaches around 3100% at 2 K and 9 T. Though this value is smaller than that in the first paper reporting the giant MR (~10^{5}%) in WTe_{2}^{3}, it is quite comparable to results in other reports^{4,15,16}. As can be seen in Fig. 3(a), distinct Shubnikov-de-Haas oscillations are observed in MR-magnetic field curve measured at 2 K, which is related to the quantum behavior of the electrons or holes. And it is inferred that there is high enough carrier mobility in this crystal to observe the quantum oscillation^{17}. After subtracting the smooth background of the MR measured at 2 K, the fast Fourier transform (FFT) analysis was carried out on the Shubnikov-de-Haas oscillations^{18}. As shown in Fig. 3(b), we have identified four peaks: F_{1} ≈ 86.4 T, F_{2} ≈ 129.6 T, F_{3} ≈ 146.2 T, and F_{4} ≈ 159.6 T, which are consistent with the previous results^{9}. In accordance with previous analysis, the oscillations of F_{1} and F_{4} come from hole, while the left two oscillations do electrons^{9}. The observed peaks of 247.9 T and 274.6 T can be attributed to sum frequencies F_{1} + F_{4} and F_{2} + F_{3}, respectively. Accordingly, by assuming isotropic parabolic dispersion, the electron and hole’s concentrations can be extracted as 3.2 × 10^{19} cm^{−3} and 3.7 × 10^{19} cm^{−3}, respectively. To quantify the degree of the mismatch of electron and hole concentrations, we define the electron-hole concentration asymmetry factor *k* as

where *n*_{e} and *n*_{h} represent the electron and hole concentration, respectively. The small dimensionless value of asymmetry factor *k* represents the small mismatch between the electron and hole concentrations. The value of *k* in as-grown stoichiometric WTe_{2} can be calculated as 0.0725.

To further support above discussion, magnetic-field dependent Hall resistivity (*ρ*_{xy}) is presented in Fig. 3(c) at variable temperatures. The negative and linear magnetic-field-dependent *ρ*_{xy} at high temperature (above 50 K) reveals that the dominant carrier is electron. According to the formula *R*_{H} = B/*ne* (where *R*_{H}, *n*, and *e* represent the Hall resistivity^{14}, carrier concentration and electron charge, respectively), the electron carrier concentration of WTe_{2} at 300 K is 3.0 × 10^{20} cm^{−3}. But with the temperature decreasing, the dependence of *ρ*_{xy} on magnetic field obviously deviates from the linear relationship (below around 50 K). This suggests that hole and electron carriers contribute together for the electrical transport in WTe_{2} crystal. This is consistent to the result of the Shubnikov-de-Haas oscillation. So a classical two-band model was used to fit the non-linear relationship between Hall resistivity and magnetic field at 2 K (Fig. 3(d)). In two-band model, the Hall resistivity is described as^{14}:

where *μ*_{e} and *μ*_{h} are the carrier mobility of electron and hole, respectively. Here, with the best fitting shown in Fig. 3(d), the values of electron and hole mobility are 4.0 × 10^{3} cm^{2}V^{−1}s^{−1} and 5.2 × 10^{3} cm^{2}V^{−1}s^{−1}, respectively. In the fitting, the electron and hole concentrations extracted from Shubnikov-de-Haas oscillation are used. It should be noted that below around 50 K, the Hall curves deviate from the linear relationship gradually. Simultaneously, the MR is increased gradually up to 3100% at 2 K. It strongly suggests that extremely large MR is coincident to high carrier mobility and comparable concentration of electron and hole at low temperatures.

The non-stoichiometric and Mo substituted WTe_{2} samples provide a platform to adjust the Fermi level and enhanced impurity scattering. It in turn affects the mismatch degrees of the electron and hole concentrations, as well as carrier mobility^{14}. Compared with the stoichiometric WTe_{2} single crystals, the MR of non-stoichiometric WTe_{2−y} (*y* = 0.10, 0.15, 0.20) and Mo substituted WTe_{2} W_{1−x}Mo_{x}Te_{2} (*x* = 0.05, 0.10, 0.15, 0.30) single crystals is smaller (Fig. 4). Quantitatively, the MR of WTe_{2−y} (*y* = 0.10, 0.15, 0.20) and W_{1−x}Mo_{x}Te_{2} (*x* = 0.05, 0.10, 0.15, 0.30) measured at 2 K and 9 T magnetic field are 640%, 86%, 71%, 210%, 33%, 31% and 13%, respectively.

Here we analyze the physical origin of MR evolution in stoichiometric and non-stoichiometric WTe_{2} crystals. According to the two-band model with electrons and holes, the MR can be written as^{14}:

The meanings of symbols are the same as those described above. For simplifying this complex equation, we assume that electron and hole have same carrier mobility, so *μ*_{e} = *μ*_{h} = *μ* (*μ* is the mean mobility). This approximation is often used to describe the MR in the semimetals^{19}. Thus, Eq. (4) can be simplified as

So we firstly used this formula to fit all the curves at various temperatures and get the value of asymmetry factor *k* and the mean mobility *μ* for stoichiometric WTe_{2} (shown in Fig. 3(a)), summarized in Fig. 5(a). One can see that the mobility *μ* remains fairly steady below 10 K but gradually decreases with increasing the temperature above 20 K. On the contrary, the asymmetry factor *k* has a reverse trend. With the decrease of *μ* and the enlarging of *k*, the MR of stoichiometric WTe_{2} gradually decreases. Thus we speculate the large MR effect in WTe_{2} material may be related to both electron-hole concentration asymmetry and the carrier mobility. In order to verify the assumption, we further used the equation (5) to fit all the curves at 2 K and get the value of asymmetry factor *k* and the mean mobility *μ* for each composition W_{1−x}Mo_{x}Te_{2−y} (shown in Fig. 4). As depicted in Fig. 5(b), upon raising the lack of Te element or increasing Mo-substituting concentration, the electron-hole concentration asymmetry enlarges and carrier mobility decreases. Both these two factors lead to the decreased MR in non-stoichiometric and Mo substituted WTe_{2}. Figure 5(c) shows the asymmetry factor *k* and the mean mobility *μ* dependent MR colored picture, which is calculated from the equation (5). As shown in Fig. 5(c), one can find that the highest MR is observed at the bottom-right region with the equal electron-hole concentration and the largest mobility. In the real material systems, the colored discrete points of each composition distributes along the dash line in Fig. 5(c). Thus, one can conclude that electron-hole concentration asymmetry, induced by both non-stoichiometric and Mo-substituting, leads to the dramatically depressed MR in WTe_{2} system. Furthermore, the new lesson we learned here is that decreased carrier mobility also can lead to the depressed MR. Quantitatively, there is only 13% MR in W_{0.7}Mo_{0.3}Te_{2}. In this case, the corresponding electron-hole concentration asymmetry (*k*) and mobility (*μ*) are 0.68, 5.7 × 10^{2} cm^{2}V^{−1}s^{−1}, respectively. Compared with stoichiometric WTe_{2} crystal, *μ* of W_{0.7}Mo_{0.3}Te_{2} is much smaller than stoichiometric one. Thus it suggests that both electron-hole concentration and carrier mobility play the crucial role on the MR in WTe_{2} material.

Here we’d like to compare aforementioned work to current available similar works. Flynn, *et al*. also found that the significant MR in 1% Mo, Re or Ta doped WTe_{2} is nearly lost, which is attributed to the large electron-hole asymmetry induced by Re or Ta-doping^{12}. But it can be seen that the specimens in this work are ceramic ones. We suspect that the low carrier mobility in ceramic samples also contributes the decreased MR therein. Ali, *et al*. compared the MR of WTe_{2} synthesized by both chemical vapor transport and self-flux methods^{11}. It claimed that WTe_{2} synthesized by self-flux method has larger mobility than one by chemical vapor transport, which leads to larger MR in WTe_{2} synthesized by flux method. Compared these works to current one, it is obvious that based on our systematic single crystals W_{1−x}Mo_{x}Te_{2−y} samples, the relationship among MR, electron-hole asymmetry and carrier mobility is clearly revealed.

## Conclusions

In summary, we intentionally synthesized the non-stoichiometric and Mo substituted WTe_{2} single crystals to study the effect of electron-hole concentration asymmetry on the MR of WTe_{2}. It is substantiated that no matter in non-stoichiometric or in Mo substituted WTe_{2} single crystals, there is dramatically decreased magnetoresistance. The quantitative magnetoresistance fitting substantiates that non-stoichiometric and Mo-substituting not only induces the electron-hole concentration asymmetry, but also generates the decreased mobility. These two factors *synergistically* lead to the dramatically decreased magnetoresistance in non-stoichiometric WTe_{2} crystals. Thus, it is crucial to obtain high purity single samples to realize the equal amount of electrons and holes, as well as high carrier mobility. Our work will provide an important clue for the exploring of such large MR materials.

## Methods

Single crystals of W_{1−x}Mo_{x}Te_{2−y} were grown by a chemical vapor transport method using Br_{2} as the transport agent. All polycrystalline samples of W_{1−x}Mo_{x}Te_{2−y} were synthesized from high purity elemental powders W (99.99%), Mo (99.99%) and Te (99.999%) by solid state reaction in evacuated quartz tubes. It is worthwhile to mention that *in nominal stoichiometric WTe*_{2} *sample described below, the mole ratio of W and Te in raw materials is set as 1:2*. Afterwards, mixtures of as-prepared polycrystalline W_{1−x}Mo_{x}Te_{2−y} and Br_{2} (about 5 mg/L) were loaded into the sealed evacuated quartz tube, and then placed at a double zone furnace with a temperature gradient between hot end 850 °C and cold end 750 °C to grow crystals for 10 days. Then all the crystals samples were characterized by X-ray diffraction (XRD) measurement in an X-ray diffractometer (Ultima III Rigaku) using Cu-*K*α radiation with 2θ scanned from 10° to 70°. The detailed elemental compositions of the as-grown crystals were determined by a scanning electron microscope (SEM, FEI-Quanta) equipped with an energy-dispersive spectroscopy (EDS) spectrometer. Standard six-probe method was used for the electrical resistivity, MR, and Hall resistance measurements. These characterizations were performed in a 9 T physical properties measurement system (PPMS, Quantum Design). The magnetic field was perpendicular to the *ab*-plane in our magneto-transport measurements.

## Additional Information

**How to cite this article**: Lv, Y.-Y. *et al*. Dramatically decreased magnetoresistance in non-stoichiometric WTe_{2} crystals. *Sci. Rep*. **6**, 26903; doi: 10.1038/srep26903 (2016).

## References

- 1.
Daughton, J.

*et al.*Magnetic Field Sensors Using GMR Multilayer.*IEEE Trans. Magn.***30**, 4608–4610 (1994). - 2.
Prinz, G. A. Magnetoelectronics.

*Science***282**, 1660–1663 (1998). - 3.
Ali, M. N.

*et al.*Large, non-saturating magnetoresistance in WTe_{2}.*Nature***514**, 205–208 (2014). - 4.
Pan, X. C.

*et al.*Pressure-driven dome-shaped superconductivity and electronic structural evolution in tungsten ditelluride.*Nat. Commun.***6**, 7805 (2015). - 5.
Qian, X. F., Liu, J. W., Fu, L. & Li, J. Quantum spin Hall effect in two-dimensional transition metal dichalcogenides.

*Science***346**, 1344–1347 (2014). - 6.
Pletikosić, I., Ali, M. N., Fedorov, A. V., Cava, R. J. & Valla, T. Electronic Structure Basis for the Extraordinary Magnetoresistance in WTe

_{2}.*Phys. Rev. Lett.***113**, 216601 (2014). - 7.
Cai, P. L.

*et al.*Drastic Pressure Effect on the Extremely Large Magnetoresistance in WTe_{2}: Quantum Oscillation Study.*Phys. Rev. Lett.***115**, 057202 (2015). - 8.
Jiang, J.

*et al.*Signature of Strong Spin-Orbital Coupling in the Large Non-saturating Magnetoresistance Material WTe_{2}.*Phys. Rev. Lett.***115**, 166601 (2015). - 9.
Zhu, Z. W.

*et al.*Quantum Oscillations, Thermoelectric Coefficients, and the Fermi Surface of Semimetallic WTe_{2}.*Phys. Rev. Lett.***114**, 176601 (2015). - 10.
Rhodes, D.

*et al.*Role of spin-orbit coupling and evolution of the electronic structure of WTe_{2}under an external magnetic field.*Phys. Rev. B.***92**, 125152 (2015). - 11.
Ali, M. N.

*et al.*Correlation of crystal quality and extreme magnetoresistance of WTe_{2}.*EPL*,**110**, 67002 (2015). - 12.
Flynn, S., Ali, M. & Cava, R. J. The Effect of Dopants on the Magnetoresistance of WTe

_{2}. arXiv:1506.07069 (2015). - 13.
Shannon, R. D. Revised Effective Ionic Radii and Systematic Studies of Interatomic Distances in Halides and Chalcogenides.

*Acta Cryst.***A32**, 751–767 (1976). - 14.
Ziman, J. M.

*Electrons and phonons-the theory of transport phenomena in solids*pp. 490–495 (Oxford University Press, 1960). - 15.
Kong, W. D.

*et al.*Raman scattering investigation of large positive magnetoresistance material WTe_{2}.*Appl. Phys. Lett.***106**, 081906 (2015). - 16.
Xiang, F. X., Veldhorst, M., Dou, S. X. & Wang, X. L. Multiple Fermi pockets revealed by Shubnikov-de Haas oscillations in WTe

_{2}.*EPL*,**112**, 37009 (2015). - 17.
Xiang, F. X., Wang, X. L., Veldhorst, M., Dou, S. X. & Fuhrer, M. S. Observation of topological transition of Fermi surface from a spindle torus to a torus in bulk Rashba spin-split BiTeCl.

*Phys. Rev. B.***92**, 035123 (2015). - 18.
Singleton, J.

*Band theory and electronic properties of solids*pp. 91–97 (Oxford University Press, 2001). - 19.
Zhang, L. Y.

*et al.*Tunable semimetallic state in compressive-strained SrIrO_{3}films revealed by transport behavior.*Phys. Rev. B.***91**, 035110 (2015).

## Acknowledgements

We’d like to acknowledge the financial support from the National Natural Science Foundation of China (51032003, 51472112, 11374149, and 10974083), the Major State Basic Research Development Program of China (973 Program) (2015CB921203), and the Program for New Century Excellent Talents in University (NCET-09-0451). Y.-Y. Lv acknowledges the financial support from the Graduate Innovation Fund of Nanjing University (2015CL11). We acknowledge very helpful discussions with Hongtao Yuan.

## Author information

## Author notes

- Yang-Yang Lv
- & Bin-Bin Zhang

These authors contributed equally to this work.

## Affiliations

### National Laboratory of Solid State Microstructures and Department of Materials Science and Engineering, Nanjing University, Nanjing 210093, China

- Yang-Yang Lv
- , Bin-Bin Zhang
- , Xiao Li
- , Bin Pang
- , Fan Zhang
- , Da-Jun Lin
- , Jian Zhou
- , Shu-Hua Yao
- , Shan-Tao Zhang
- , Minghui Lu
- & Yan-Feng Chen

### National Laboratory of Solid State Microstructure and Department of Physics, Nanjing University, Nanjing 210093, China

- Y. B. Chen

### School of Physical Science and Technology, ShanghaiTech University, Shanghai 200031, China

- Zhongkai Liu
- & Yulin Chen

### State Key Laboratory of Low Dimensional Quantum Physics, Collaborative Innovation Center of Quantum Matter and Department of Physics, Tsinghua University, Beijing 100084, China

- Yulin Chen

### Collaborative Innovation Center of Advanced Microstructures, Nanjing University, Nanjing 210093, China

- Yan-Feng Chen

## Authors

### Search for Yang-Yang Lv in:

### Search for Bin-Bin Zhang in:

### Search for Xiao Li in:

### Search for Bin Pang in:

### Search for Fan Zhang in:

### Search for Da-Jun Lin in:

### Search for Jian Zhou in:

### Search for Shu-Hua Yao in:

### Search for Y. B. Chen in:

### Search for Shan-Tao Zhang in:

### Search for Minghui Lu in:

### Search for Zhongkai Liu in:

### Search for Yulin Chen in:

### Search for Yan-Feng Chen in:

### Contributions

S.-H.Y. and Y.-Y.L. performed the crystal growth in assist of D.-J.L., Y.-Y.L. and F.Z. determined the structure content and the elemental composition of the crystals. B.-B.Z. and Y.-Y.L. conducted the transport measurements. Y.-B.C., B.-B.Z. and Y.-Y.L. analyzed the data and refined the measurements. J.Z., Y.-F.C. and Y.L.C. contributed to the result analysis. Y.-B.C., B.-B.Z. and Y.-Y.L. co-wrote the manuscript. S.-H.Y., S.-T.Z., M.H.L. and Z.K.L. revised the manuscript. B.P. and X.L. did some additional experiments in reviewing manuscripts. All authors discussed the results and commented on the manuscript.

### Competing interests

The authors declare no competing financial interests.

## Corresponding authors

Correspondence to Shu-Hua Yao or Y. B. Chen.

## Rights and permissions

To obtain permission to re-use content from this article visit RightsLink.

## Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/