Abstract
Schottky barrier controls the transfer of hot carriers between contacted metal and semiconductor, and decides the performance of plasmonic metal–semiconductor devices in many applications. It is immensely valuable to actively tune the Schottky barrier. In this work, electrical tuning of Schottky barrier in an Au-nanodisk/TiO2-film structure was demonstrated using a simple three-electrode electrochemical cell. Photocurrents excited at different wavelength significantly increase as the applied bias voltage increases. Analyzing and fitting of experimental results indicate that the photocurrent is mainly affected by the bias tuning position of Schottky barrier maximum, which shifts to metal–semiconductor interface as applied voltage increases, and enhances the collection efficiency of the barrier for plasmonic hot electrons. The conduction band curvature of 0.13 eV was simultaneously obtained from the fitting. This work provides a new strategy for facile tuning of Schottky barrier and hot-electron transfer across the barrier.
Similar content being viewed by others
Introduction
Plasmonic nanostructures have greatly strong ability to harvest photon energy by free electrons collective oscillation under light excitation, which is known as localized surface plasmonic resonance (LSPR)1. Its excellent properties such as strong field confinement, largely enhanced light-matter interaction, make LSPR extensively employed for scientific researches and emerging applications of ultrasensing2, nanolasing3, waveguide4, photothermal therapies5, et al. When metal nanostructure is in contact with semiconductor, their different work functions induce a space-charge region with internal electric field, bending semiconductor bands, and give rise to a Schottky barrier on metal–semiconductor interface6. High energy hot carriers excited via surface plasmon non-radiative decay by Landau damping can overcome Schottky barrier and transfer from metallic nanostructures to the contacted semiconductor7. The Schottky barrier significantly inhibits hot-carrier recombination and facilitates hot-carrier separation, which plays a key role in photocatalytic reactions and photovoltaic devices8,9.
In plasmonic metal–semiconductor devices based on hot carriers, the transfer of hot carriers between contacted metal and semiconductor is one of the most important aspect that determines the device performance. Efforts have been made to control the hot-carrier transfer by different means. Shi et al. tuned Au–TiO2 interfacial structure by annealing at different temperatures. The closer contact between Au and TiO2 promoted hot-electron transfer across the interface10. Decorating metal or semiconductor was also investigated to control the hot-carrier transfer. The addition of decorating materials or functional groups provides new hot-carrier transfer pathways across the interface11,12,13. More works aim to control the hot-carrier transfer by tuning the Schottky barrier, which promotes the separation of hot carriers and also resists their directional migration. Diversely means were proposed to tune the Schottky barrier, such as changing carrier density by adjusting doping concentration and oxygen vacancies of metal oxide semiconductors14,15,16, modifying the metal–semiconductor interface by plasma treatment17, molecule capping18 and insertion layer19,20, electrostatic gating and applying strain on two-dimensional semiconductors21,22,23,24, and simply applying external bias voltage or gate light25,26,27,28,29. Among the strategies above, electrical tuning of Schottky barrier is quite promising. It achieves reversible and active tuning, but limited by the requirement of ingenious cell structure and precise operation for connecting nanostructures with electrodes. Facile and reversible methods still need developing.
On the other hand, most works of tuning Schottky barrier mainly focus on the change of Schottky barrier height and corresponding effects. In fact, the Schottky barrier is much more complex than the simple models frequently used6. As Schottky barrier height is tuned, other parameters of Schottky barrier may also change, such as width of depletion region, position of Schottky barrier maximum, height of barrier caused by band curvature, etc.30. These factors may seriously affect the transfer of hot carriers, but they were usually ignored.
In this work, Schottky barrier of an Au-nanodisk/TiO2-film (AT) structure was electrically tuned in a simple three-electrode electrochemical cell. As the increase of reverse bias voltage, photocurrent originated from plasmonic hot-electron transfer from Au nanodisks to TiO2 significantly increases. Based on fitting and analyzing of experimental results, it is found that the increase of photocurrent is mainly induced by electrical tuning of Schottky barrier maximum position, which improves collection efficiency of the barrier, rather than Schottky barrier height.
Results and discussion
To achieve the electrical tuning of Schottky barrier and further control of hot-electron injection from Au to TiO2, an external bias should be effectively applied on the Au–TiO2 Schottky junction. In this sense, the existence of Schottky barrier on Au–TiO2 interface of the investigated structure should be confirmed, while barrier on other interfaces in the structure should be avoided. In Fig. 1a, the current of an In-Ga/TiO2/In-Ga structure is proportional to voltage from − 2 to 2 V, showing an Ohmic characteristic. In-Ga alloy connects TiO2 and electrode with an Ohmic contact, so the contact properties of TiO2 with Au or ITO can be revealed by replacing one of the In-Ga alloy layers. In Au/TiO2/In-Ga structure, the Schottky contact of Au and TiO2 can be corroborated by the nonlinear (current–voltage) I–V curve in right panel of Fig. 1b. The Schottky barrier height calculated from I–V data by Cheung’s method is approximately 0.8 eV31,32. Whereas, for In-Ga/TiO2/ITO structure, the linear I–V plot in Fig. 1c indicates that ITO and TiO2 are also in Ohmic contact. Therefore, in AT structure fabricated on ITO glass, there is Schottky barrier only on the interface of Au and TiO2.
When AT structure was tested as working electrode in an electrochemical cell, voltage drop also occurs at metal-electrolyte interfaces, including those of nanoparticle-electrolyte and counter electrode–electrolyte, because of electric double layer on the interfaces. However, the existence of Au–TiO2 Schottky barrier makes this fraction prone to be small. Besides, the different Fermi levels of TiO2 and electrolyte give rise to a space charge layer at TiO2-electrolyte interface, and further induce another TiO2-electrolyte barrier on the interface. The barrier is parallel with Au–TiO2 Schottky barrier, avoiding short circuiting the latter. Therefore, external bias can be effectively applied on the Schottky junction of Au and TiO2, while a fraction of voltage drop inevitably exists on other interfaces and components of the investigated system. Electrical tuning of the Schottky barrier can be revealed by experiments at different bias voltages.
I–V curve of AT sample in the electrochemical cell was also measured and shown in Fig. 2a. The nonlinear curve and calculated Schottky barrier height of approximately 0.8 eV is in accordance with the analysis above. Figure 2b shows the photocurrents of AT structure with nanodisk diameters of 80 nm (D80) and 100 nm (D100) at different bias voltages. Excited by incident light, hot electrons generated from localized surface plasmon (LSP) decay in Au nanodisks pass through the Schottky barrier to the TiO2 film, and induce positive photocurrents. When 300 mV bias was applied, the photocurrents of both samples significantly increase several times. Considering hot electrons excited at a certain wavelength in nanodisks have almost the same energy distribution, it can be inferred that the enhancement of photocurrent comes from the electrical tuning effect for the Schottky barrier, which affects the hot-electron transfer efficiency from Au nanodisks to TiO2 film.
Bias tunes the Schottky barrier in different aspects as illustrated in Fig. 3. When a reverse bias (\(V_{a} < 0\), positive on the semiconductor side, negative on the metal side) is applied to the Schottky junction, Fermi level of the semiconductor (\(E_{f}\)) decreases at a degree of \(\left| {qV_{a} } \right|\) to \(E_{f}^{^{\prime}}\). And semiconductor conduction band minimum also decreases from \(E_{c}\) to \(E_{c}^{^{\prime}}\), while the potential barrier resulted from conduction band curvature increases from \(qV_{i}\) to \(q\left( {V_{i} - V_{a} } \right)\) 30. Due to the effect of mirror charges induced in the metal by electrons in the semiconductor, the height of Schottky barrier (\(\Phi_{b}\)) is slightly affected by applied voltage and decreases at a degree of
where q, \(N_{d}\) and \(\varepsilon_{s}\) are electron charge, donor carrier concentration of semiconductor and semiconductor permittivity, respectively30. The resulting Schottky barrier height equals \(\Phi_{b} - \Delta \Phi_{b}\). Meanwhile, the Schottky barrier maximum position (\(x_{m}\)) is also affected by mirror charges and varies with applied voltage as30
It can be seen that as the magnitude of applied reverse voltage increases, xm decreases and Schottky barrier shifts close to the metal–semiconductor interface.
Incident light with photon energy higher than Schottky barrier excites hot electrons in the metal and transports them from metal to semiconductor conduction band. This effect is also called internal photoemission and its efficiency (\(\eta\)) is influenced by multiple factors as follows:
where \(A\) is optical absorbance of the metal part, \(F_{e}\) is the fraction of photons generating photoelectrons and contributing to photocurrent, \(P_{E}\) is the probability of photoexcited electrons overcoming Schottky barrier after scattering with cold electrons and boundary surface, \(\eta_{c}\) is collection efficiency of the barrier. Among the above four parameters, \(A\) and \(P_{E}\) are independent on Schottky barrier, while \(F_{e}\) and \(\eta_{c}\) are functions of Schottky barrier height and Schottky barrier maximum position, respectively33.
To reveal how the bias tuning Schottky barrier affects internal photoemission and hot electron harvest, relations between bias and \(F_{e}\), \(\eta_{c}\) are analyzed. Incident photon-to-electron conversion efficiencies (IPCEs) of AT structure (D80) at different bias voltages were measured and calculated according to
where ne, N, h, c, I, e, P and λ are collected photoelectron number, incident photon number, Plank constant, light velocity, photocurrent, electron charge, incident light power, and light wavelength, respectively. As Fig. 4a shows, IPCEs at all bias conditions exhibit a peak around 600 nm for LSPR of the structure. At this condition, the resonance results in an enhancement of plasmonic hot electron generation. Besides, the IPCEs significantly increase with the bias from − 100 to 700 mV, which is coherent with the photocurrents in Fig. 2. The peak IPCE with 700 mV bias is as high as about seven times of that without bias. Estimating from Eq. (2) with common TiO2 parameters, bias (< 1 V) induced Schottky barrier height variation for an Au–TiO2 interface is quite small (tens of milli-electron-volts)29,34. Compared with the total Schottky barrier height near 1 eV, the influence of applied voltage on \(F_{e}\), which is a function of Schottky barrier height, can be neglected, and it cannot support the significant increase of IPCEs with bias.
Then, it comes to the relation between bias and \(\eta_{c}\). The barrier collection efficiency \(\eta_{c}\) indicates the probability of hot electrons migrating from metal interface to Schottky barrier maximum without scattering, and is given by
where \(L_{s}\) is electron scattering length in TiO2 33. Combining Eqs. (2) and (5), it is known
where \(B\) is \(\frac{1}{{4L_{s} }}\sqrt[4]{{\frac{q}{{2\pi^{2} \varepsilon_{s} N_{d} }}}}\), independent of bias and Schottky barrier. In Fig. 4b, data points of IPCE with bias voltage at different excitation wavelength obtained from Fig. 4a were fitted using the relation of \({\text{IPCE}} = ke^{{ - B\left( {V_{i} - V_{a} } \right)^{{ - \frac{1}{4}}} }}\). Fitting parameters were given in Table 1. According to Eq. (3), \(k\) is proportional with \(AF_{e} P_{E}\) and varies with \( A\) at different wavelength. It is clear that the fitted dash curves in the figure match the experimental data well. Moreover, fitting at different wavelength is in good agreement, having the same fitting parameters of \(V_{i} = 130{ }\;{\text{mV}}\) and \(B = 15\). The obtained conduction band curvature \(qV_{i}\) of 0.13 eV here is quite close to the ones in references35, and it further supports the fitting results. Therefore, it can be deduced that the hot-electron harvest efficiency of the plasmonic Au/TiO2 structure is mainly determined by the bias tuning Schottky barrier maximum position \(x_{m}\). Taking \(N_{d} = 2.5 \times 10^{25} {\text{m}}^{ - 3}\), \(\varepsilon_{s} = 8.85 \times 10^{ - 10} \;{\text{F}} \cdot {\text{m}}^{ - 1}\) from a reference with similar samples into Eq. (2), \(x_{m}\) can be estimated to be 0.3 nm36. For \(x_{m}\) is proportional to \(\left( {V_{i} - V_{a} } \right)^{{ - \frac{1}{4}}}\), as the reverse bias increases, the Schottky barrier maximum position shifts to the metal–semiconductor interface and decreases to 63% of the primitive one at 700 mV reverse bias. In fact, \(x_{m}\) can be further electrically tuned to 56% of the primitive value at a reverse bias voltage of 1.2 V, above which the electrolysis of water will happen. The deduced Schottky barrier maximum position significantly enhances the hot-electron collection efficiency of the Schottky barrier, and thus achieves an improved photocurrent.
Conclusion
In conclusion, Schottky barrier of AT structure was electrically tuned in a simple three-electrode electrochemical cell. Appling a reverse bias, photocurrents and IPCEs at different excitation wavelength significantly increase as the applied voltage increases. According to fitting results, the photoelectric response obeys a relation of \({\text{IPCE}} = ke^{{ - B\left( {V_{i} - V_{a} } \right)^{{ - \frac{1}{4}}} }}\). It indicates the photocurrent is mainly controlled by bias tuning Schottky barrier maximum position, rather than Schottky barrier height. Schottky barrier maximum position increases photocurrent via shifting to the interface and enhancing collection efficiency of Schottky barrier for hot electrons. The conduction band curvature of Schottky barrier was also obtained to be 0.13 eV from the fitting. This work suggests a new strategy to facilely and reversely tune the Schottky barrier and hot-carrier transfer across the barrier. It is highly beneficial to improve the performance of plasmonic hot-carrier devices in photocatalysis and photovoltaic systems.
Methods
Sample fabrication
AT structure was fabricated on ITO glass substrate. First, a 2 nm thick Cr adhesion layer was deposited on the substrate, followed by sputtering a 100 nm thick TiO2 film in an O2 (3 sccm) and Ar (50 sccm) plasma at 5 mTorr and 0.8 kW DC. Then, Au nanodisks with average diameter 80 nm or 100 nm, and height 30 nm were fabricated on the TiO2 film using hole-mask colloid lithography (HCL, Fig. 5a) followed by annealing at 350 °C. The structure and SEM image of AT sample are shown in Fig. 5b,c, respectively. Au nanodisks randomly distributed on TiO2 film, and their diameter is relatively uniform. In-Ga/TiO2/In-Ga and Au/TiO2/In-Ga structures were fabricated by coating In-Ga alloy layer, TiO2 film, and In-Ga alloy or Au layer in sequence. In-Ga/TiO2/ITO structure was also fabricated by sequentially coating TiO2 film and In-Ga alloy layer using ITO glass as substrate. Further details of sample fabrication are referred to the literature37.
Photocurrent measurement
Photocurrents of AT structure were measured in a three-electrode system using an Ag/AgCl wire reference electrode, a Pt counter electrode, and standard phosphate buffer saline (PBS) electrolyte (Fig. 5b). Photocurrents were collected at chronoamperometric mode with constant bias voltages against reference electrode. Incident light with different wavelength was filtered out by an acousto-optic tunable filter (AOTF) from a laser driven light source (LDLS, Energetiq). Further detailed description of procedures for photocurrent measurements is referred to the literature37.
References
Zhang, X., Chen, Y. L., Liu, R. S. & Tsai, D. P. Plasmonic photocatalysis. Rep. Prog. Phys. 76, 046401 (2013).
Saha, K., Agasti, S. S., Kim, C., Li, X. & Rotello, V. M. Gold nanoparticles in chemical and biological sensing. Chem. Rev. 112, 2739–2779 (2012).
Oulton, R. F. et al. Plasmon lasers at deep subwavelength scale. Nature 461, 629–632 (2009).
Fang, Y. & Sun, M. Nanoplasmonic waveguides: towards applications in integrated nanophotonic circuits. Light-Sci. Appl. 4, e294 (2015).
Kim, M., Lee, J. H. & Nam, J. M. Plasmonic photothermal nanoparticles for biomedical applications. Adv. Sci. 6, 1900471 (2019).
Tung, R. T. The physics and chemistry of the Schottky barrier height. Appl. Phys. Rev. 1, 011304 (2014).
Shahbazyan, T. V. Landau damping of surface plasmons in metal nanostructures. Phys. Rev. B 94, 235431 (2016).
Zheng, B. Y. et al. Distinguishing between plasmon-induced and photoexcited carriers in a device geometry. Nat. Commun. 6, 7797 (2015).
Clavero, C. Plasmon-induced hot-electron generation at nanoparticle/metal-oxide interfaces for photovoltaic and photocatalytic devices. Nat. Photonics 8, 95 (2014).
Shi, X., Ueno, K., Takabayashi, N. & Misawa, H. Plasmon-enhanced photocurrent generation and water oxidation with a gold nanoisland-loaded titanium dioxide photoelectrode. J. Phys. Chem. C 117, 2494 (2012).
Sun, Z. G. et al. A promising visible-light photocatalyst: H2 plasma-activated amorphous-TiO2-supported Au nanoparticles. J. Catal. 37, 380 (2019).
Tang, L. et al. Controlled synthesis of Au nanocrystals-metal selenide hybrid nanostructures toward plasmon-enhanced photoelectrochemical energy conversion. Nanomaterials 10, 564 (2020).
Lee, C. et al. Enhancement of hot electron flow in plasmonic nanodiodes by incorporating PbS quantum dots. ACS Appl. Mater. Interfaces 10, 5081–5089 (2018).
Guo, D. Y. et al. Oxygen vacancy tuned Ohmic-Schottky conversion for enhanced performance in β-Ga2O3 solar-blind ultraviolet photodetectors. Appl. Phys. Lett. 105, 023507 (2014).
Zheng, Z., Qiu, Z. J., Liu, R., Ostling, M. & Zhang, S. L. Schottky-barrier height tuning by means of ion implantation into preformed silicide films followed by drive-in anneal. IEEE Electr. Device Lett. 28, 565–568 (2007).
Alptekin, E. & Ozturk, M. C. Tuning of the nickel silicide Schottky barrier height on p-type silicon by indium implantation. IEEE Electr. Device Lett. 30, 1272–1274 (2009).
Son, Y., Li, J. & Peterson, R. L. In situ chemical modification of Schottky barrier in solution-processed zinc tin oxide diode. ACS Appl. Mater. Interfaces 8, 23801–23809 (2016).
Li, Y., Lin, S., Liu, Y., Chai, Y. & Lau, S. P. Tunable Schottky barriers in ultrathin blackphosphorus field effect transistors via polymercapping. 2D Mater. 6, 024001 (2019).
Hu, J., Saraswat, K. C. & Wong, H. S. P. Metal/III-V Schottky barrier height tuning for the design of nonalloyed III-V field-effect transistor source/drain contacts. J. Appl. Phys. 107, 063712 (2010).
Coss, B. E. et al. Near band edge Schottky barrier height modulation using high-κ dielectric dipole tuning mechanism. Appl. Phys. Lett. 95, 222105 (2009).
Padilha, J. E., Fazzio, A. & da Silva, A. J. R. Van der Waals heterostructure of phosphorene and graphene: tuning the Schottky barrier and doping by electrostatic gating. Phys. Rev. Lett. 114, 066803 (2015).
Yang, H. et al. Graphene barristor, a triode device with a gate-controlledSchottky barrier. Science 336, 1140–1143 (2012).
Pham, K. D. et al. Layered graphene/GaS van der Waals heterostructure: controlling the electronic properties and Schottky barrier by vertical strain. Appl. Phys. Lett. 113, 171605 (2018).
Liu, B., Wu, L. J., Zhao, Y. Q., Wang, L. Z. & Caii, M. Q. Tuning the Schottky contacts in the phosphorene and graphene heterostructure by applying strain. Phys. Chem. Chem. Phys. 18, 19918–19925 (2016).
Boettcher, S. W. et al. Tunable electronic interfaces between bulk semiconductors and ligand-stabilized nanoparticle assemblies. Nat. Mater. 6, 592–596 (2007).
Ho, Y. L. et al. Plasmonic hot-carriers in channel-coupled nanogap structure for metal−semiconductor barrier modulation and spectral-selective plasmonic monitoring. ACS Photonics 5, 2617–2623 (2018).
Lonergan, M. C. A Tunable diode based on an inorganic semiconductor| conjugated polymer interface. Science 278, 2103–2106 (1997).
Gao, X. D., Fei, G. T., Zhang, Y., Zhang, L. D. & Hu, Z. M. All-optical-input transistors: light-controlled enhancement of plasmon-induced photocurrent. Adv. Funct. Mater. 28, 1802288 (2018).
Jeon, B., Lee, C. & Park, J. Y. Amplifying hot electrons with Schottky barrier lowering by application of an external bias on a metal-semiconductor nanodiode. Abstr. Pap. Am. Chem. Soc. 258, 225 (2019).
Colinge, J. P. & Colinge, C. A. Physics of Semiconductor Devices (Springer, Berlin, 2002).
Cheung, S. K. & Cheung, N. W. Extraction of Schottky diode parameters from forward current–voltage characteristics. Appl. Phys. Lett. 49, 85–87 (1986).
Rawat, G. et al. Effective Richardson constant of sol–gel derived TiO2 films in n-TiO2/p-Si heterojunctions. IEEE Electr. Device Lett. 38, 633–636 (2017).
Casalino, M., Sirleto, L., Moretti, L. & Rendina, I. A silicon compatible resonant cavity enhanced photodetector working at 1.55 μm. Semicond. Sci. Technol. 23, 075001 (2008).
Sellers, M. C. K. & Seebauer, E. G. Measurement method for carrier concentration in TiO2 via the Mott–Schottky approach. Thin Solid Films 519, 2103–2110 (2011).
Fu, Q. & Wagner, T. Interaction of nanostructured metal overlayers with oxide surfaces. Surf. Sci. Rep. 62, 431–498 (2007).
Tang, H., Prasad, K., Sanjinbs, R., Schmid, P. E. & Lévy, F. Ellectrical and optical properties of TiO2 anatase thin films. J. Appl. Phys. 75, 2042–2047 (1994).
Fang, Y. et al. Plasmon enhanced internal photoemission in antenna-spacer-mirror based Au/TiO2 nanostructures. Nano Lett. 15, 4059–4065 (2015).
Acknowledgments
This research was supported by the National Natural Science Foundation of China (Grant No. 12074054, 11704058) and the Fundamental Research Funds for the Central Universities (Grant No. DUT19RC(3)007).
Author information
Authors and Affiliations
Contributions
Z.S. and Y.F. wrote the manuscript text and prepared the figures. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Sun, Z., Fang, Y. Electrical tuning effect for Schottky barrier and hot-electron harvest in a plasmonic Au/TiO2 nanostructure. Sci Rep 11, 338 (2021). https://doi.org/10.1038/s41598-020-79746-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-79746-5
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.