Abstract
Supramolecular and covalent polymers share multiple structural effects such as communication mechanisms among monomer repeating units, which are related to their axial helical structure. Herein, a unique multi-helical material combining information from both metallosupramolecular and covalent helical polymers is presented. In this system, the helical structure described by the poly(acetylene) (PA) backbone (cis-cisoidal, cis-transoidal) guides the pendant groups in a fashion where a tilting degree emerges between a pendant and the adjacent ones. As a result, a multi-chiral material is formed comprising four or five axial motifs when the polyene skeleton adopts either a cis-transoidal or cis-cisoidal configuration: the two coaxial helices—internal and external—and the two or three chiral axial motifs described by the bispyridyldichlorido PtII complex array. These results show that complex multi-chiral materials can be obtained by polymerizing appropriate monomers that combine both point chirality and the ability to generate chiral supramolecular assemblies.
Similar content being viewed by others
Introduction
In recent years, covalent and supramolecular helical polymers have attracted the attention of the scientific community to replicate the structure/function relation found in helical biomacromolecules such as peptides, proteins, DNA or polysaccharides1,2,3,4,5,6,7,8,9,10,11,12. Synthetic helical polymers, including both covalent and supramolecular, are archetypal systems exhibiting unique helical structures with various functionalities that may even exceed those found in nature. As a result, stimuli-responsive materials can be obtained, making possible to control the P (right-handed)/M (left-handed) screw sense and/or elongation in covalent polymers13,14,15,16,17,18 and molecular packing (P/M, J-type, H-type, and so on) by the presence of different external stimuli (e.g., solvent, pH, temperature, metal ions, chiral additives, or light)19,20,21,22,23,24,25,26,27,28,29,30,31,32,33,34,35,36,37,38. In addition, in both supramolecular and covalent helical polymers, structural effects such as Sergeants and Soldiers Effect39,40,41,42,43, Majority Rules44,45,46, Chiral Coalition47, Chiral Accord48, or Chiral Conflict49,50 occur when a chiral and an achiral monomer—or two chiral monomers or building blocks—are copolymerized. This fact indicates that the parameters that govern the communication mechanism between monomers along the supramolecular or covalent helix are the same. This has allowed the development of chiral materials that combine these two structural motifs, where supramolecular arrays of dendronized planar molecules or azo groups are found at the periphery of the covalent helix, leading to its stabilization51,52,53,54,55. Interestingly, in literature there are also other examples where a chiral supramolecular helical array of the pendant groups is produced, although the polymer main chain is not folded into a preferred screw sense helix56,57,58,59,60.
Recently, our group reported a poly[oligo(p-phenyleneethynylene)acetylene] (POPEPA) in which the chiral information of the pendant group is harvested by the polyene backbone (P/M helix) through the P/M axial arrangement of the oligo(p-phenyleneethynylene) (OPE) groups used as spacers61. As a result, a POPEPA can adopt a multi-helical scaffold where four different axial motifs coexist in the helical material: the two coaxial helices—internal (helix 1) and external (helix 2)—and the two helices described by the OPE axial array (helices 3 and 4)61.
Herein, using rational monomer design, we have achieved unique multi-helical materials that exist in up to five helical conformations. To this end, we selected a metal-containing monomer, consisting of an asymmetric bispyridyldichlorido Pt(II) complex, functionalized on one edge with a polymerizable terminal alkyne and with a chiral group on the other edge to induce a screw sense in the helical polymer. The choice of the Pt(II) center is biased by the versatile self-assembly behavior and interesting photophysical properties of metal-based monomers62,63,64,65,66. Particularly, bispyridyldichlorido Pt(II) complexes with an extended aromatic surface are privileged scaffolds to prepare a large variety of supramolecular structures by different aggregation pathways and multiple weak non-covalent interactions67,68,69,70,71,72. Hence, an asymmetric bispyridyldichlorido Pt(II) complex should meet all the requirements to generate a multi-helical scaffold.
Results
To validate our hypothesis, two different pyridine ligands, one containing either a chiral L-valine or an L-alanine methyl ester residue, and another one bearing a 4-alkynyl group were synthesized and complexed with a Pt(MeCN)2Cl2 salt to yield the corresponding unsymmetrical bispyridyldichlorido Pt(II) complexes (mono-(S)-1 and mono-(S)-2 respectively; see the Supplementary Information for synthesis and characterization of the complexes; Supplementary Figs. 1–8 and Supplementary Tables 1–4). The terminal alkyne group enables the further polymerization of mono-(S)-1 and mono-(S)−2 using [Rh(nbd)Cl]2 as catalyst (nbd = 2,5-norbornadiene) to obtain poly-(S)−1 and poly-(S)−2, in good yield and high content of cis-double bonds (Fig. 1).
UV-vis studies of mono-(S)-1 and mono-(S)-2 show spectra with four bands between 350 and 250 nm (vide infra). UV–vis theoretical calculations for mono-(S)-1 (time-dependent density functional theory) (TD-DFT) together with either rCAM-B3LYP and wB97XD density functional and LANL2DZ basis set [TD-DFT(wB97XD)/LANL2DZ), TD-DFT(rCAM-B3LYP)/LANL2DZ)], were performed on the molecular structure obtained after DFT optimization (see Supplementary Figs. 18, 19). Both theoretical calculations show a good match between the experimental and the calculated ECD trace, being slightly better when the functional wB97XD is used. From the TD-DFT (wB97XD)/ LANL2DZ theoretical studies, we identified which fragments of mono-(S)-1 are responsible for these absorption bands. Thus, the UV-band at higher wavelength—ca. 345 nm—corresponds to MLCT involving the core of the bispyridyldichlorido Pt(II) complexes, the band at ca. 305 nm corresponds to the para-ethynylpyridyl moiety, while the band at 280 nm is attributed to the para-pyridylbenzamide of (L)-valine-methyl ester complexed to the Pt(II) ion. Finally, the band at 250 nm is assigned to the benzamide group of the chiral moiety (See Fig. 1c and Supplementary Figs. 18, 19).
Intriguingly, UV-vis studies of poly-(S)-1 and poly-(S)-2 show an interesting phenomenon. Thus, while in moderately polar solvents such as THF or DCM, poly-(S)-1 adopts a stretched helix (cis-transoidal), in more polar solvents such as DMF, the polymer adopts a compressed scaffold (cis-cisoidal). This change in elongation is explained by the hypsochromic shift experienced by the polyene band (from 417 to 380 nm) when comparing a DCM/THF solution to a DMF one. In the case of poly-(S)-2, similar results are obtained in DMF, whereas the experiments in THF or DCM were not possible due to insufficient solubility. The compression of the polyene backbone is accompanied by a color change from yellow to translucent due to the lack of alternating double bond conjugation of the polyene backbone (Fig. 2a). Note that the lack of emission, i.e. MMLCT luminescence, both in DMF and DCM (see Supplementary Fig. 14) indicates the absence of short Pt-Pt interactions in the polymers68,69,70,71.
ECD studies of poly-(S)-1 and poly-(S)-2 in these solvents show again an interesting effect. Thus, poly-(S)-1 shows a complex ECD spectra in THF or DCM, with multiple bands in the 250–350 nm region (Fig. 2b). On the contrary, in polar solvents such as DMF, the ECD spectrum is dominated by a strong bisignate in the 250–350 nm region (Fig. 2c). Careful inspection of the ECD spectrum of poly-(S)-1 in DMF reveals that the first negative Cotton band shows two minima, one centered at 385 nm and the other at 355 nm, which corresponds to the polyene backbone and the core of the Pt(II) complex, respectively (see above). Moreover, a strong positive Cotton band is obtained at 302 nm, and a negative one at 280 nm. More precisely, the band at ca. 302 nm corresponds to the para-ethynylpyridyl moiety, while the band at 280 nm is attributed to the para-pyridylbenzamide of (L)-valine-methyl ester, as previously discussed in the monomer calculations (Fig. 1c). The complexity of the ECD spectrum obtained for poly-(S)-1 in different solvents can be explained by combining the classical ECD spectrum of a poly(phenylacetylene) (PPA), which presents three alternating Cotton bands, in this case −/+/−, with the ECD trace obtained by a chiral supramolecular orientation of the metal containing spacers within the helical scaffold. Thus, while in DMF, poly-(S)-1 adopts a compressed cis-cisoidal structure (ω1 < 90°), in DCM or THF an elongated cis-transoidal structure (ω1 > 90°) is adopted by the polyene backbone. As a result, two different architectures with different structural properties are obtained for poly-(S)-1. The cis-cisoidal helix in PPAs is made by two coaxial helices that rotate in the same direction (Pint/Pext or Mint/Mext), while the cis-transoidal helix rotates in the opposite direction (Pint/Mext or Mint/Pext). Moreover, in the cisoidal scaffold, the helix contains three residues per turn, generating a helix with three crests at the periphery. For the transoidal scaffold, the helix possesses two residues per turn, describing a helix with two crests (Fig. 2d).
Interestingly, looking at the arrangement of the metal-containing spacers on the different crests of the cis-cisoidal and cis-transoidal helices, it is possible to create a unique helical arrangement of these achiral spacers within the helix crest whose sense depends on the helical scaffold. Accordingly, in cis-cisoidal PAs, the orientation of the achiral spacers within the helix crest exhibits the same sense as the internal and external helices. As a result, a multi-helical structure with five structural motifs is generated—internal helix, external helix and three helices described by the arrangement of the metal containing spacers at the helix crest.
From the literature, it is known that PPAs with a P orientation of the polyene backbone show an alternating ECD spectrum with three Cotton bands +/−/+, while those PPAs with an M orientation of the polyene backbone show the opposite orientation of the ECD bands (−/+/−). To determine how the axially chiral orientation of the metal containing monomer affects the spectrum, theoretical ECD studies were carried out in a supramolecular helical arrangement of an asymmetric bispyridyldichlorido Pt(II) complex. To this end, the geometry of supramolecular trimers arranged as left-handed and right-handed helices was optimized using DFT together with the rCAM-B3LYP functional and the LANL2DZ basis set73,74,75,76,77,78,79,80. In this case, the wB97XD functional was not employed considering the resemblance between the theoretical UV-vis obtained for the theoretical studies of (S)-1, and the computation time needed for the wB97XD functional.
Theoretical ECD calculations for both trimers (TD-DFT, rCAM-B3LYP/LANL2DZ) reveal a −/+ bisignate for the M helix and a +/− bisignate for the P helix. Interestingly, these two bands correspond to the core of the bispyridyldichlorido Pt(II) complex (350 nm) and to the para-ethynylpyridyl moiety (302 nm) (Fig. 3a).
Considering this result, if the polymer adopts a cis-transoidal scaffold with a preferred P orientation of the polyene backbone, the external helix and the axial array described by the metal-containing spacer will rotate in opposite direction (M helix). Thus, while the polyene produces a +/−/+ ECD trace, the axial array of the spacers promotes a −/+ ECD with an opposite orientation to that described by the polyene. As a result, depending on the intensity and wavelength absorbance of the first and second ECD bands produced by the polyene backbone and the axial array of the metal-containing spacer, complex ECD spectra are obtained with multiple positive and negative ECD bands as observed in poly-(S)-1 dissolved in DCM or THF (Fig. 2b).
On the contrary, in a cis-cisoidal helix with a P orientation of the internal and the external helices, and a P orientation of the asymmetric Pt(II) complexes used as spacers, the first and second cotton bands of the classical ECD spectrum (+/−/+) experience an additive effect of the (+/−) bands obtained for the axial array of the spacers.
As a result, an ECD spectrum with three alternating Cotton bands is obtained, where the second is very intense.
In the case of a polymer adopting a cis-cisoidal structure with a preferred M screw sense of the polyene backbone, the opposite −/+/− ECD trace must be obtained. This is in fact the ECD pattern that we observed for poly-(S)-1 dissolved in DMF: three alternating Cotton bands (−/+/−), showing the second and third band an abnormally large intensity, confirming the additive effect by ECD theoretical calculations (TD-DFT(CAM-B3LYP)/LANL2DZ). Analogous spectra were obtained for poly-(S)-2 dissolved in DMF (Fig. 3b and Supplementary Information).
VT-ECD studies of poly-(S)-1 in THF and DMF corroborate these structures, showing for poly-(S)-1 in DMF a large thermal stability (above 80 °C) promoted by the three axial arrays of the asymmetric Pt(II) complexes used as spacers. Thermal studies for poly-(S)-1 in THF disclose a lower thermal stability due to the presence of just two axial arrays of the asymmetric bispyridyldichlorido Pt(II) complexes used as spacers within the helical scaffold.
Discussion
In summary, we have achieved through two different examples—poly-(S)-1 and poly-(S)-2—unique multi-helical materials built from a supramolecular helix, made from a bispyridyldichlorido Pt(II) complex and a covalent helical polymer (PA). When poly-(S)-1 is dissolved in solvents of moderate polarity, e.g. THF, the polyene backbone adopts a cis-transoidal helical scaffold with four axial motifs: the internal helix (helix 1) described by the polyene backbone, the external helix (helix 2) described by the pendants and two helices described by the bispyridyldichlorido PtII complexes used as spacers (helices 3 and 4). These four axial motifs are interconnected describing either a M1/P2/P3/P4 or P1/M2/M3/M4 multi-axial chiral system. Interestingly, an additional axial motif emerges when the polymer is dissolved in polar solvents such as DMF. In such case, poly-(S)-1 adopts a cis-cisoidal scaffold that shows five axial motifs: the internal helix (helix 1), the external helix (helix 2), and axial motifs described by the bispyridyldichlorido PtII complexes used as spacers (helices 3 and 4). These structural motifs are interconnected describing either a P1/P2/P3/P4/P5 or M1/M2/M3/M4/M5 multi-axial chiral material. These results indicate that rational molecular design can be exploited to stabilize supramolecular helices in covalent polymers, which paves the way for the design of complex multi-helical materials.
Methods
CD measurements were performed on a Jasco-720 and VT-CD measurements on a Jasco-1500 with a 1 mm quartz cuvette. The amount of polymer used for CD and VT-CD measurements was 0.6 mg/mL.
UV spectra were registered on a Jasco V-750 with a 1 mm quartz cuvette. The amount of polymer used for UV measurements was 0.6 mg/mL.
Optical rotation was measured on a Jasco-P2000.
Mass spectra were obtained on an HP 5988A spectrometer (Hewlett‐Packard, Palo Alto, CA, USA).
Elemental analyses were recorded using a Foss‐Heraeus CHNO‐Rapid analyzer.
NMR experiments were measured on a Varian 300 (1H: 300 MHz) or a Bruker Avance II 400 (1H: 400 MHz; 13 C: 101 MHz; 19 F: 376.4 MHz). Solid NMR experiments were measured on a Bruker NEO 750 using a 1.3 mm rotor.
Raman spectra were performed on a Renishaw confocal Raman spectrometer (Invia Reflex model), equipped with two lasers (diode laser 785 nm and Ar laser 514 nm).
DSC traces were obtained on a DSC Q200 Tzero Technology (TA Instruments, New Castle, UK), equipped with a refrigerated cooling system RCS90 (TA Instruments, New Castle, UK), using a Tzero low-mass aluminum pan.
TGA traces were obtained on a TGA Q5000 (TA Instruments, New Castle, UK) using a platinum pan.
Photoluminescence spectra were obtained on a Horiba Fluoromax-Plus-C fluorimeter using a 10 mm quartz cuvette.
IR spectra were obtained on a JASCO-FTIR-6800. IR spectra in solution were recorded using a CaF2 cell with a path length of 0.1 mm.
Computational studies: 3D structures were done with the software package Spartan´18. The asymmetric bispyridyldichlorido Pt(II) complex was built by using the data obtained from another bispyridyldichlorido Pt(II) complex (CCDC deposit number 2004415). Time-dependent density functional theory (TD-DFT) together with either rCAM-B3LYP and wB97XD density functional and LANL2DZ basis set [TD-DFT(wB97XD)/LANL2DZ), TD-DFT(rCAM-B3LYP)/LANL2DZ)] were carried out with the software package Gaussian 16, rev C.01.
Synthesis of ligands
Methyl isonicotinoyl-L-valinate [Ligand 1]: Isonicotinic acid (441 mg, 1.20 equiv.), 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC, 686 mg, 1.20 equiv.), 1-hydroxybenzotriazole (HOBt, 484 mg, 1.20 equiv.) and 4-dimethylaminopyridine (DMAP, 437 mg, 1.20 equiv.) were dissolved in 30 mL of dry CH2Cl2. After 15 min, time needed to activate the acid, L-valine methyl ester (500 mg, 1.00 equiv.) was added and the mixture was stirred overnight. The organic layer was washed three times with HCl 1 M and a saturated solution of NaHCO3. The combined organic layers were dried over anhydrous Na2SO4, filtered and evaporated at reduced pressure. The crude product was chromatographed on silica gel with pentane/ethyl acetate (70:30) as eluent (388 mg, 55 % of yield).
Methyl isonicotinoyl-L-alaninate [Ligand 2]: Isonicotinic acid (529 mg, 1.20 equiv.), 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide (EDC, 824 mg, 1.20 equiv.), 1-hydroxybenzotriazole (HOBt, 581 mg, 1.20 equiv.) and 4-dimethylaminopyridine (DMAP, 525 mg, 1.20 equiv.) were dissolved in 30 mL of dry CH2Cl2. After 15 min, time needed to activate the acid, L-alanine methyl ester (500 mg, 1.00 equiv.) was added and the mixture was stirred overnight. The organic layer was washed three times with HCl 1 M and a saturated solution of NaHCO3. The combined organic layers were dried over anhydrous Na2SO4, filtered and evaporated at reduced pressure. The crude product was chromatographed on silica gel with pentane/ethyl acetate (70:30) as eluent (395 mg, 53 % of yield).
4-((trimethylsilyl) ethynyl)pyridine [Ligand 3]: 4-Iodopyridine (500 mg, 1.00 equiv.), bis(triphenylphosphine)palladium (II) dichloride (Pd(PPh3)2Cl2, 6.85 mg, 0.04 equiv.), triphenylphosphine (10.2 mg, 0.016 equiv.) and copper iodide (CuI, 11.1 mg, 0.024 equiv.) were dissolved in dry THF (20 mL). Next, triethylamine (Et3N, 10 mL) and ethynyltrimethylsilane (359 mg, 1.5 equiv.) were added and the mixture was stirred for two hours. After removing the solvent, the crude product was chromatographed on silica gel with pentane/ethyl acetate (80:20) as eluent obtaining, after solvent removal, an oil (368 g, 86 % of yield). The synthetic procedure was previously reported in supplementary reference 1.
General protocol for complexation and deprotection of monomers
Ligand 3 (1.7 equiv.), trans-PtCl2(PhCN)2 (1.35 equiv.) and the corresponding ligand 1 or 2 (1 equiv.) were placed in a pressure tube and subjected to five vacuum/Ar cycles. Subsequently, dry and degassed toluene was added and the mixture was heated to 70 °C and stirred at this temperature for one week. After evaporating the solvent, the crude was chromatographed on silica gel with pentane/ethyl acetate (80:20) as eluent.
The corresponding Pt(II) complexes with the protected alkyne were dissolved in a mixture of THF:MeOH (3:1). Next K2CO3 was added (1.20 equiv.) and the reaction was stirred at r.t. for 1 h. The crude was chromatographed on silica gel with pentane/ethyl acetate (60:40) as eluent.
Synthesis of polymers
The reaction flask (sealed ampoule) was dried under vacuum and argon flushed for three times before monomer was added as a solid. Dry THF was added with a syringe. Next, a solution of rhodium norbornadiene chloride dimer, [Rh(nbd)Cl]2, and Et3N in dry THF was added to the reaction under stirring at 30 °C. After 6 h, the resulting polymer was diluted in CH2Cl2 and precipitated in methanol and centrifuged twice. Next, the polymer was reprecipitated in hexane and centrifuged again.
Data availability
All data is available from the corresponding authors upon request.
References
Yashima, E. et al. Supramolecular helical systems: helical assemblies of small molecules, foldamers, and polymers with chiral amplification and their functions. Chem. Rev. 116, 13752–13990 (2016).
Yashima, E., Maeda, K., Lida, H., Furusho, Y. & Nagai, K. Helical polymers: synthesis, structures, and functions. Chem. Rev. 109, 6102–6211 (2009).
Nakano, T. & Okamoto, Y. Synthetic helical polymers: conformation and function. Chem. Rev. 101, 4013–4038 (2001).
Tarrío, J. J., Rodríguez, R., Fernández, B., Quiñoá, E. & Freire, F. Dissymmetric chiral poly (diphenylacetylene) s: secondary structure elucidation and dynamic luminescence. Angew. Chem. Int. Ed. 134, e202115070 (2022).
Percec, V. Merging macromolecular and supramolecular chemistry into bioinspired synthesis of complex systems. Isr. J. Chem. 60, 48–66 (2020).
Yashima, E., Maeda, K. & Furusho, Y. Single-and double-stranded helical polymers: synthesis, structures, and functions. Acc. Chem. Res. 41, 1166–1180 (2008).
Okuda, S. et al. Supramolecular helical assemblies of dirhodium (ii) paddlewheels with 1, 4-diazabicyclo[2.2.2.octane: a remarkable substituent effect on the helical sense preference and amplification of the helical handedness excess of metallo-supramolecular helical polymers. J. Am. Chem. Soc. 144, 2775–2792 (2022).
Brunsveld, L., Folmer, B. J., Meijer, E. W. & Sijbesma, R. P. Supramolecular polymers. Chem. Rev. 101, 4071–4098 (2001).
de Greef, T. F. & Meijer, E. W. Supramolecular polymers. Nature 453, 171–173 (2008).
Percec, V. & Xiao, Q. Helical self-organizations and emerging functions in architectures, biological and synthetic macromolecules. Bull. Chem. Soc. Jpn. 94, 900–928 (2021).
Aida, T. & Meijer, E. W. Supramolecular polymers–we’ve come full circle. Isr. J. Chem. 60, 33–47 (2020).
Fernández, Z., Fernández, B., Quiñoá, E. & Freire, F. The competitive aggregation pathway of an asymmetric chiral oligo(p‐phenyleneethynylene) towards the formation of individual P and M supramolecular helical polymers. Angew. Chem. Int. Ed. 60, 9919–9924 (2021).
Liu, J., Lam, J. W. & Tang, B. Z. Acetylenic polymers: syntheses, structures, and functions. Chem. Rev. 109, 5799–5867 (2009).
Schwartz, E., Koepf, M., Kitto, H. J., Nolte, R. J. & Rowan, A. E. Helical poly(isocyanides): past, present and future. Polym. Chem. 2, 33–47 (2011).
Anger, E. et al. Synthesis and chiral recognition ability of helical polyacetylenes bearing helicene pendants. Polym. Chem. 5, 4909–4914 (2014).
Ikai, T., Kurake, T., Okuda, S., Maeda, K. & Yashima, E. Racemic monomer-based one-handed helical polymer recognizes enantiomers through auto-evolution of its helical handedness excess. Angew. Chem. Int. Ed. 60, 4625–4632 (2021).
Rey-Tarrío, F. et al. Photostability and dynamic helical behavior in chiral poly(phenylacetylene)s with a preferred screw-sense. Angew. Chem. Int. Ed. 61, e202207623 (2022).
Rodríguez, R., Quiñoá, E., Riguera, R. & Freire, F. Architecture of chiral poly(phenylacetylene)s: from compressed/highly dynamic to stretched/quasi-static helices. J. Am. Chem. Soc. 138, 9620–9628 (2016).
Guan, X., Wang, S., Shi, G., Zhang, J. & Wan, X. Thermoswitching of helical inversion of dynamic polyphenylacetylenes through cis-trans isomerization of amide pendants. Macromolecules 54, 4592–4600 (2021).
Leiras, S., Freire, F., Seco, J. M., Quiñoá, E. & Riguera, R. Controlled modulation of the helical sense and the elongation of poly(phenylacetylene)s by polar and donor effects. Chem. Sci. 4, 2735–2743 (2013).
Maeda, K., Mochizuki, H., Watanabe, M. & Yashima, E. Switching of macromolecular helicity of optically active poly(phenylacetylene)s bearing cyclodextrin pendants induced by various external stimuli. J. Am. Chem. Soc. 128, 7639–7650 (2006).
Arias, S., Freire, F., Quiñoá, E. & Riguera, R. The leading role of cation–π interactions in polymer chemistry: the control of the helical sense in solution. Polym. Chem. 6, 4725–4733 (2015).
Ikai, T. et al. Chiral/achiral copolymers of biphenylylacetylenes bearing various substituents: chiral amplification through copolymerization, followed by enhancement/inversion and memory of the macromolecular helicity. Macromolecules 53, 973–981 (2020).
Maeda, K., Kamiya, N. & Yashima, E. Poly(phenylacetylene)s bearing a peptide pendant: Helical conformational changes of the polymer backbone stimulated by the pendant conformational change. Chem. Eur. J. 10, 4000–4010 (2004).
Cobos, K. et al. Polymeric helical structures à la carte by rational design of monomers. Macromolecules 53, 3182–3193 (2020).
van Leeuwen, T., Heideman, G. H., Zhao, D., Wezenberg, S. J. & Feringa, B. L. In situ control of polymer helicity with a non-covalently bound photoresponsive molecular motor dopant. ChemComm 53, 6393–6396 (2017).
Suárez-Picado, E., Quiñoá, E., Riguera, R. & Freire, F. Poly(phenylacetylene) amines: a general route to water-soluble helical polyamines. Chem. Mater. 30, 6908–6914 (2018).
Fukuda, M. et al. Macromolecular helicity control of poly(phenylisocyanate)s with a single stimuli-responsive chiral switch. ChemComm 55, 7906–7909 (2019).
Matern, J., Kartha, K. K., Sánchez, L. & Fernández, G. Consequences of hidden kinetic pathways on supramolecular polymerization. Chem. Sci. 11, 6780–6788 (2020).
Sasaki, N. et al. Supramolecular double-stranded Archimedean spirals and concentric toroids. Nat. Commun. 11, 1–9 (2020).
Ghosh, G. et al. Control over multiple nano‐and secondary structures in peptide self‐assembly. Angew. Chem. Int. Ed. 61, e202113403 (2022).
Rodríguez, R., Quiñoá, E., Riguera, R. & Freire, F. Stimuli‐directed colorimetric interconversion of helical polymers accompanied by a tunable self‐assembly process. Small 15, e1805413 (2019).
Fernández, Z., Fernández, B., Quiñoá, E., Riguera, R. & Freire, F. Chiral information harvesting in helical poly(acetylene) derivatives using oligo(p-phenyleneethynylene)s as spacers. Chem. Sci. 11, 7182–7187 (2020).
Rodríguez, R., Suárez‐Picado, E., Quiñoá, E., Riguera, R. & Freire, F. A stimuli‐responsive macromolecular gear: interlocking dynamic helical polymers with foldamers. Angew. Chem. Int. Ed. 59, 8616–8622 (2020).
Yan, X., Wang, F., Zheng, B. & Huang, F. Stimuli-responsive supramolecular polymeric materials. Chem. Soc. Rev. 41, 6042–6065 (2012).
Ma, X. & Tian, H. Stimuli-responsive supramolecular polymers in aqueous solution. Acc. Chem. Res. 47, 1971–1981 (2014).
Rodríguez, R., Quiñoá, E., Riguera, R. & Freire, F. Multistate chiroptical switch triggered by stimuli-responsive chiral teleinduction. Chem. Mater. 30, 2493–2497 (2018).
Arias, S., Freire, F., Calderón, M. & Bergueiro, J. Unexpected chiro‐thermoresponsive behavior of helical poly(phenylacetylene)s bearing elastin‐based side chains. Angew. Chem. Int. Ed. 56, 11420–11425 (2017).
Arias, S., Bergueiro, J., Freire, F., Quiñoá, E. & Riguera, R. Chiral nanostructures from helical copolymer–metal complexes: Tunable cation–π interactions and sergeants and soldiers effect. Small 12, 238–244 (2016).
Nagata, Y., Nishikawa, T. & Suginome, M. Solvent effect on the sergeants-and-soldiers effect leading to bidirectional induction of single-handed helical sense of poly(quinoxaline-2,3-diyl)s copolymers in aromatic solvents. ACS Macro Lett. 5, 519–522 (2016).
Smulders, M. M. et al. Tuning the extent of chiral amplification by temperature in a dynamic supramolecular polymer. J. Am. Chem. Soc. 132, 611–619 (2010).
Adelizzi, B., Van Zee, N. J., de Windt, L. N., Palmans, A. R. & Meijer, E. W. Future of supramolecular copolymers unveiled by reflecting on covalent copolymerization. J. Am. Chem. Soc. 141, 6110–6121 (2019).
Vantomme, G. et al. Tuning the length of cooperative supramolecular polymers under thermodynamic control. J. Am. Chem. Soc. 141, 18278–18285 (2019).
Ke, Y. Z., Nagata, Y., Yamada, T. & Suginome, M. Majority‐rules‐type helical poly(quinoxaline‐2,3‐diyl)s as highly efficient chirality‐amplification systems for asymmetric catalysis. Angew. Chem., Int. Ed. 54, 9333–9337 (2015).
Smulders, M. M. et al. Probing the limits of the majority-rules principle in a dynamic supramolecular polymer. J. Am. Chem. Soc. 132, 620–626 (2010).
van Gestel, J., Palmans, A. R., Titulaer, B., Vekemans, J. A. & Meijer, E. W. “Majority-rules” operative in chiral columnar stacks of C 3-symmetrical molecules. J. Am. Chem. Soc. 127, 5490–5494 (2005).
Cobos, K., Quiñoá, E., Riguera, R. & Freire, F. Chiral-to-chiral communication in polymers: a unique approach to control both helical sense and chirality at the periphery. J. Am. Chem. Soc. 140, 12239–12246 (2018).
Cobos, K., Rodríguez, R., Quiñoá, E., Riguera, R. & Freire, F. From sergeants and soldiers to chiral conflict effects in helical polymers by acting on the conformational composition of the comonomers. Angew. Chem., Int. Ed. 59, 23724–23730 (2020).
Alzubi, M. et al. Chiral conflict as a method to create stimuli‐responsive materials based on dynamic helical polymers. Angew. Chem., Int. Ed. 58, 13365–13369 (2019).
Tang, K., Green, M. M., Cheon, K. S., Selinger, J. V. & Garetz, B. A. Chiral conflict. The effect of temperature on the helical sense of a polymer controlled by the competition between structurally different enantiomers: from dilute solution to the lyotropic liquid crystal state. J. Am. Chem. Soc. 125, 7313–7323 (2003).
Rudick, J. G. & Percec, V. Induced helical backbone conformations of self-organizable dendronized polymers. Acc. Chem. Res. 41, 1641–1652 (2008).
del Barrio, J., Tejedor, R. M. & Oriol, L. Thermal and light control of the chiral order of azopolymers. Eur. Polym. J. 48, 384–390 (2012).
Wang, L., Yin, L., Zhang, L. Y., Zhu, X. & Fujiki, M. Circularly polarized light with sense and wavelengths to regulate azobenzene supramolecular chirality in optofluidic medium. J. Am. Chem. Soc. 139, 13218–13226 (2017).
Gan, Y. et al. Regulating chiral helical structures in liquid-crystalline block copolymers with chiroptical response by synergistic asymmetric effects. Macromolecules 55, 8556–8565 (2022).
Chen, J. et al. Polymerization-induced self-assembly of conjugated block copoly(phenylacetylene)s. Macromolecules 53, 1638–1644 (2020).
Cheng, X. et al. Controlling the multiple chiroptical inversion in biphasic liquid‐crystalline polymers. Angew. Chem. Int. Ed. 60, 24430 (2021).
Tong, X., Cui, L. & Zhao, Y. Confinement effects on photoalignment, photochemical phase transition, and thermochromic behavior of liquid crystalline azobenzene-containing diblock copolymers. Macromolecules 37, 3101–3112 (2004).
Huang, S., Chen, Y., Ma, S. & Yu, H. Hierarchical self‐assembly in liquid‐crystalline block copolymers enabled by chirality transfer. Angew. Chem. Int. Ed. 57, 12524–12528 (2018).
Cheng, X. et al. In situ controlled construction of a hierarchical supramolecular chiral liquid‐crystalline polymer assembly. Angew. Chem. Int. Ed. 59, 9669–9677 (2020).
Wang, L., Yin, L., Zhang, W., Zhu, X. & Fujiki, M. Circularly polarized light with sense and wavelengths to regulate azobenzene supramolecular chirality in optofluidic medium. J. Am. Chem. Soc. 139, 13218–13226 (2017).
Fernández, Z., Fernández, B., Quiñoá, E. & Freire, F. Merging supramolecular and covalent helical polymers: four helices within a single scaffold. J. Am. Chem. Soc. 143, 20962–20969 (2021).
Bentz, K. C. & Cohen, S. M. Supramolecular metallopolymers: from linear materials to infinite networks. Angew. Chem. Int. Ed. 57, 14992–15001 (2018).
Whittell, G. R., Hager, M. D., Schubert, U. S. & Manners, I. Functional soft materials from metallopolymers and metallosupramolecular polymers. Nat. Mater. 10, 176–188 (2011).
Winter, A. & Schubert, U. S. Synthesis and characterization of metallo-supramolecular polymers. Chem. Soc. Rev. 45, 5311–5357 (2016).
Matern, J., Dorca, Y., Sánchez, L. & Fernandez, G. Revising complex supramolecular polymerization under kinetic and thermodynamic control. Angew. Chem. Int. Ed. 58, 16730–16740 (2019).
Zhu, Y., Zheng, W., Wang, W. & Yang, H. B. When polymerization meets coordination-driven self-assembly: metallo-supramolecular polymers based on supramolecular coordination complexes. Chem. Soc. Rev. 50, 7395–7417 (2021).
Bäumer, N. et al. Exploiting coordination geometry to tune the dimensions and processability of metallosupramolecular polymers. Org. Chem. Front. 8, 4138–4143 (2021).
Matern, J., Maisuls, I., Strassert, C. A. & Fernández, G. Luminescence and length control in nonchelated d8‐metallosupramolecular polymers through metal‐metal interactions. Angew. Chem. Int. Ed. 61, e202208436 (2022).
Bäumer, N., Matern, J. & Fernández, G. Recent progress and future challenges in the supramolecular polymerization of metal-containing monomers. Chem. Sci. 12, 12248–12265 (2021).
Matern, J., Baumer, N. & Fernández, G. Unraveling halogen effects in supramolecular polymerization. J. Am. Chem. Soc. 143, 7164–7175 (2021).
Bäumer, N. et al. Tuning energy landscapes and metal–metal interactions in supramolecular polymers regulated by coordination geometry. Chem. Sci. 12, 5236–5245 (2021).
Allampally, N. K. et al. Control over the self‐assembly modes of PtII complexes by alkyl chain variation: from slipped to parallel π‐Stacks. Chem. Eur. J. 22, 7810–7816 (2016).
Varni, A. J. et al. Photostable helical polyfurans. J. Am. Chem. Soc. 141, 8858–8867 (2019).
Hase, Y. et al. Mechanism of helix induction in poly(4-carboxyphenyl isocyanide) with chiral amines and memory of the macromolecular helicity and its helical structures. J. Am. Chem. Soc. 131, 10719–10732 (2009).
Tang, H. Z., Novak, B. M., He, J. & Polavarapu, P. L. A thermal and solvocontrollable cylindrical nanoshutter based on a single screw-sense helical polyguanidine. Angew. Chem. Int. Ed. 44, 7298–7301 (2005).
Wu, P. et al. Non-uniform self-folding of helical poly(fluorenevinylene) derivatives in the solid state leading to amplified circular dichroism and circularly polarized light emission. Angew. Chem. Int. Ed. 61, e202210556 (2022).
Pietropaolo, A., Wang, Y. & Nakano, T. Predicting the switchable screw sense in fluorene-based polymers. Angew. Chem. Int. Ed. 54, 2688–2692 (2015).
Pietropaolo, A. & Nakano, T. Molecular mechanism of polyacrylate helix sense switching across its free energy landscape. J. Am. Chem. Soc. 135, 5509–5512 (2013).
Fernandez, B. et al. Predicting the helical sense of poly(phenylacetylene)s from their electron circular dichroism spectra. Angew. Chem. Int. Ed. 57, 3666–3670 (2018).
Fernandez, B., Rodríguez, R., Quiñoá, E., Riguera, R. & Freire, F. Decoding the ECD spectra of poly(phenylacetylene)s: structural significance. ACS Omega 4, 5233–5240 (2019).
Acknowledgements
The authors thank Servicio de Microscopía Electrónica (RIAIDT, USC). Financial support from AEI (PID2019−109733GB-I00, E.Q. and F.F.), Xunta de Galicia (ED431C 2018/30, ED431C 2021/40, Centro Singular de Investigación de Galicia acreditación 2019−2022, ED431G 2019/03; E.Q. and F.F.) and the European Regional Development Fund (ERDF) is gratefully acknowledged. F.R.T. thanks Xunta de Galicia for a predoctoral contract.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
F.F. and G.F. conceived the project. F.R.-T. synthesized all materials and performed all the experimental studies as well as the theoretical calculations. F.R.-T., E.Q., F. F. and G.F. discussed the results and wrote the manuscript with input from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the other, anonymous, reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Rey- Tarrío, F., Quiñoá, E., Fernández, G. et al. Multi-chiral materials comprising metallosupramolecular and covalent helical polymers containing five axial motifs within a helix. Nat Commun 14, 3348 (2023). https://doi.org/10.1038/s41467-023-39014-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-39014-2
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.