Abstract
Dielectric capacitors with high energy storage density (Wrec) and efficiency (η) are in great demand for high/pulsed power electronic systems, but the state-of-the-art lead-free dielectric materials are facing the challenge of increasing one parameter at the cost of the other. Herein, we report that high Wrec of 6.3 J cm-3 with η of 90% can be simultaneously achieved by constructing a room temperature M2–M3 phase boundary in (1-x)AgNbO3-xAgTaO3 solid solution system. The designed material exhibits high energy storage stability over a wide temperature range of 20–150 °C and excellent cycling reliability up to 106 cycles. All these merits achieved in the studied solid solution are attributed to the unique relaxor antiferroelectric features relevant to the local structure heterogeneity and antiferroelectric ordering, being confirmed by scanning transmission electron microscopy and synchrotron X-ray diffraction. This work provides a good paradigm for developing new lead-free dielectrics for high-power energy storage applications.
Similar content being viewed by others
Introduction
Dielectric capacitors are widely utilized in numerous advanced high/pulsed power electronic systems, due to their distinctive features of high power density, ultrafast charge/discharge capability, long storage lifetime, robust, and excellent thermal stability1,2,3,4. However, they possess inferior energy density in comparison with other electrochemical energy storage systems such as batteries. Therefore, extensive efforts have been made to improve their energy densities to meet the demands of integration, compactness, and miniaturization of electronic devices5,6. In addition, from practical application viewpoint, high energy efficiency (η) is desired since the energy dissipation will greatly degrade the thermal breakdown strength thus impact the reliability and performance of the energy storage capacitors. However, previous investigations have shown that the energy density and efficiency can be enhanced only at the expense of each other for most dielectric materials.
Dielectric materials developed for energy storage capacitors include linear dielectrics (LD), ferroelectrics (FEs), antiferroelectrics (AFEs), and relaxor ferroelectrics (RFEs)5. Among them, AFEs have been attracted extensive attention for energy storage application because of their unique double hysteresis loop originating from the electric field induced antiferroelectric-ferroelectric (AFE–FE) phase transition and zero remnant polarization (Pr) in pristine AFE phase. These advantages have been fully reflected in PbZrO3-based AFE ceramics, in which large energy storage densities ranging from 6.4 to 11.2 J cm−3 were reported7,8,9. However, the disadvantage of AFE is high energy loss due to large hysteresis associated with the first-order AFE–FE phase transition, being confirmed by its polarization vs. electric field (P–E) loop10. It is thus a challenge to achieve high energy storage density and efficiency simultaneously in antiferroelectric materials.
On the other hand, RFEs exhibit hysteresis-free polarization response owing to the existence of local structure heterogeneity, thus leading to a high energy efficiency11,12,13,14. Analogous to RFEs, it is expected that relaxor antiferroelectrics (RAFEs) might be a good choice to address the hysteresis, which inevitably exists in AFE, where disruption of the long-range ordered AFE domains will smear the AFE–FE phase transition due to the weakly intercoupled nanodomains15,16. Based on this concept, a paraelectric or relaxor ferroelectric end member was judiciously introduced to AFEs to break the long-range AFE order into nanodomains. The introduction of (Sr0.7Bi0.2)TiO3 relaxor end member into (Na0.5Bi0.5)TiO3 forms a new RAFEs solid solution with high energy efficiency of 95% and energy storage density of 2.5 J cm−316. In addition, an ultrahigh energy storage density of 12.2 J cm−3 was achieved in (Bi0.5Na0.5)TiO3-NaNbO3 ceramics, where the relaxor component (Bi0.5Na0.5)TiO3 was added into NaNbO3, with the purpose to stabilize the room temperature antiferroelectric phase in NaNbO3 and introduce relaxor feature17, but with less success in energy efficiency being below 70% due to the inferior AFE stability.
To achieve both high energy storage density and efficiency simultaneously, we propose to design material system with a highly stabilized antiferroelectricity with relaxor feature. AgNbO3 (AN) has been actively studied for dielectric energy storage application, due to its unique antiferroelectric feature. It undergoes a series of phase transitions with increasing temperature, possessing a ferrielectric (FIE) M1 phase and two disordered AFE phases (M2 and M3) below Curie temperature18,19, as shown in Fig. 1a. At room temperature (RT), the M1 phase exhibits metastable AFE feature under applied electric field, leading to a large Pr and hysteresis in the P–E loops, as shown in Fig. 1b. Nevertheless, a relatively high Wrec of 1.5–2.0 J cm−3 was obtained in AN, with an efficiency only around 38%20,21. Numerous attempts have been made on A-site22,23,24, B-site25,26, and A/B-site27,28 chemical modifications with the idea to shift the highly stable AFE M2 phase to RT, where P–E loop with small Pr and reduced hysteresis have been achieved (Fig. 1c), exhibiting good energy storage densities varying in the range of 2.5–4.5 J cm−3 and efficiency of 55–69%. A more attractive energy storage density of 5.2 J cm−3 was reported in Ag0.91Sm0.03NbO3 ceramics but with yet low efficiency of 68.5%29. It should be noted that the disorder feature can be induced by aliovalent ion dopant in AN system, which can be confirmed by the obvious frequency dispersion over M1–M2 phase transition and high diffuseness parameter30. This may be associated with the downward shifting of M2–M3 phase transition temperature with diffused dielectric maximum31, being generally ascribed to the different degrees of displacement orders in M2 and M3 phases32. Therefore, relaxor characteristic with slim P–E loop is expected if M2–M3 phase transition temperature (TM2-M3) shifts downward to RT, which can be represented by the minimized Pr and hysteresis as given in Fig. 1d, leading to high energy storage density and efficiency simultaneously.
Analogous to AN, the AgTaO3 (AT) material possesses numerous phase transitions as a function of temperature, with room temperature rhombohedral phase18,33. Of particular significance is that AN and AT have the infinite miscibility thus (1-x)AgNbO3-xAgTaO3 (ANTx) solid solution can be formed with the addition of AgTaO3 in AgNbO3, leading to successive physical property transformations, such as phase transition sequence and dielectric permittivity depending on solid solution composition34. It is expected that the M1–M2 and M2–M3 phase transition temperatures of AN can be tailored over a wide temperature range downward to below RT with addition of AT, which provides a feasible way for tuning the physical properties of the solid solution.
In this work, we designed the ANTx solid solutions, where the M2–M3 phase boundary was built at RT with significantly stabilized antiferroelectric phase, meanwhile possessing relaxor features. As expected, high energy storage density of 6.3 J cm−3 and efficiency of 90% were achieved simultaneously. In addition, the local structure heterogeneity and antiferroelectric ordering of M2–M3 phase boundary were confirmed on the atomic scale, giving a solid proof on the long-term confusion about the broad dielectric anomaly of TM2–M3.
Results
Dielectric property of ANTx
Figure 2a gives the temperature-dependent dielectric permittivity and loss for the representative ANTx compositions. Typical dielectric anomalies associated with various phase transitions are observed in AN, consistent with the results reported previously20. Similar phase transition behaviours are observed for ANTx solid solutions. As expected, the phase transition temperatures TM1–M2 and TM2–M3 are found to shift significantly downward. Of particular importance is that the TM2–M3 of ANT55 composition decreases to around RT, as represented in the schematic phase diagram of Fig. 2b. In addition, the phase transition of TM1–M2 is found to become smeared and diffused with clear frequency dispersion over a broad temperature range, as shown in Fig. 2c, indicating a typical relaxor feature35. To further analyze the relaxor behaviour of ANTx ceramics, the frequency dispersion is calculated based on △T = TM1–M2 (100 kHz) − TM1–M2 (100 Hz), where the TM1–M2 (100 kHz) and TM1–M2 (100 Hz) are determined by the dielectric anomalies. The △T is found to increase with increasing Ta content, indicating the addition of Ta component in AN will induce a strong relaxor characteristics, which will greatly benefit the energy storage density and efficiency.
Energy storage performance of ANTx
To evaluate the energy storage performance of the as-designed ceramics, P–E loops are measured prior to their corresponding breakdown strengths at a frequency of 1 Hz, as shown in Fig. 3a. The P–E loops conform to the typical feature of AFEs, where the AFE–FE phase transition is shifted to higher electric fields with the addition of Ta. Of particular importance is that the remnant polarization monotonically decreases with the increase of Ta content, reaching the value of zero at x = 65 mol%, while the hysteresis of P–E loops reduces obviously with nearly hysteresis-free feature at compositions with x above 50 mol%. The obvious evolutions of AFE–FE phase transition electric field and remnant polarization, together with the less electric field dependent dielectric permittivity with increasing Ta concentration (Supplementary Fig. 1), give solid proof of high stability of antiferroelectricity in ANT system. It should be noted here that the relaxor characteristic would smear the P–E loops, which also increases AFE–FE phase transition electric field and decreases remnant polarization. As a consequence, the energy storage efficiency η is remarkably increased with addition of Ta, reaching above 90% for ANTx with x > 55% (Fig. 3b). Of particular significance is that ultrahigh energy storage density up to 6.3 J cm−3 is achieved for ANT55, showing a pronounced enhancement of ~330% comparing to 1.9 J cm−3 for the pure AN counterpart. The ultrahigh energy storage density is closely associated with a high breakdown strength (Eb). Figure 3c gives the Eb values based on the Weibull distribution, in which good linear relationship between X and Y axes can be observed for all compositions. The Eb increases substantially after the addition of Ta, demonstrating ultrahigh values of 470 and 550 kV cm−1 for ANT55 and ANT65 (Fig. 3d), respectively. To understand the underlying mechanisms responsible for the significantly improved Eb in ANTx solid solution, the micro-morphology and grain size, the band gap, as well as the polarizations at high electric fields are studied. All ANTx ceramics show highly compacted grains with nearly pore-free microstructure (insets of Fig. 3d), leading to high relative bulk density of >96%. The average grain size decreases obviously with the increase of Ta content (6.8 µm for AN vs. 1.3 µm for ANT65), as represented in Fig. 3d, due to the refractory nature of Ta2O536. More detailed composition-dependent micro-morphology and average grain size distribution can be found in Supplementary Figs. 2 and 3, respectively. The high relative bulk density and reduced grain size will greatly benefit the enhanced breakdown strength37. Furthermore, improved band gap (Eg) is observed with the increase of Ta content, with values ranging from ~2.8 eV (AN) to ~3.0 eV (ANT65), obtained from the UV–vis absorption spectra (Fig. 3e). The wider band gap will make the electrons in the valence band more difficult to jump into the conduction band, which contributes to a higher intrinsic breakdown strength38. Finally, the polarization is clearly decreased after Ta addition, as shown in Fig. 3f, which is associated with the smeared AFE–FE phase transition and relaxor behaviour. The decreased polarization results in much lower dielectric permittivity (dP/dE) maxima upon AFE–FE phase transition, as shown in the inset of Fig. 3f. A moderate increase in polarization and/or dielectric permittivity as a function of applied electric field will impede the dramatic enhancement in electric energy density, thus leading to improved breakdown strength39. All the above-mentioned factors are responsible for the significantly increased breakdown strength for ANTx ceramics.
To verify the antiferroelectric characteristics of ANT55, the electric field dependent P–E loops and current vs. voltage (I–V) curves were measured, as given in Fig. 4a, b, respectively. Linear P–E loops with very low polarization are observed at low electric field, similar to those observed in antiferroelectric materials. With the increase of electric field, the P–E loops gradually bend upward with remarkable enhancement of polarization, being associated with the AFE–FE phase transition, beyond which, the P–E loops gradually bend downward, due to the saturated polarization in FE phase. The P–E loops remain slim in shape with minimal hysteresis over the entire measuring electric field range, ascribing to the relaxor characteristics of ANT55. The AFE feature is further confirmed by the unipolar I–V curves in Fig. 4b, in which two peaks are observed with the increase of electric field. These peaks are associated with the AFE-to-FE (EF, ~330 kV cm−1) and FE-to-AFE (EA, ~270 kV cm−1) phase transitions, respectively. The energy storage density also exhibits strong electric field dependent behavior, which increases significantly around phase transition (Fig. 4c), as generally observed in antiferroelectrics. The energy storage efficiency maintains high level of >90% over the measuring electric field. It should be noted that the breakdown strength is sample dimension dependent, where a higher breakdown strength of 530 kV cm−1 with the maximum polarization of 32 μC cm−2 is achieved in sample with thickness of ~80 μm and electrode diameter of 2 mm. This leads to improved energy storage density up to 7.5 J cm−3, meanwhile with yet high energy storage efficiency of 86% (Supplementary Fig. 4). Compared with state-of-the-art lead-free bulk ceramics17,20,24,25,29,40,41,42,43,44,45,46,47,48,49, the ANT55 exhibits more attractive energy storage performance with both high energy storage density and efficiency, as shown in Fig. 4d.
From application viewpoint, the temperature stability and cycling reliability of energy storage properties are important16,50. The temperature-dependent energy storage property of ANT55 is evaluated at 400 kV cm−1 to guarantee the safety in practical application, the corresponding results are given in Fig. 4e. The ANT55 exhibits very good temperature stability over temperature range of 25–150 °C, with minimal variations of <5 and <2% for energy storage density and efficiency respectively. Figure 4f gives the cycling reliability of ANT55. Both energy storage density and efficiency maintain the same values at 400 kV cm−1 after 106 cycles, indicating the ANT55 has outstanding cycling reliability. In general, the large volume strain accompanied with AFE–FE phase transition in classic antiferroelectrics might accelerate the mechanical failure due to the electromechanical breakdown51, while the strong relaxor feature in ANT55 smears the phase transition, leading to the highly improved cycling reliability16.
In addition to the stability and reliability, the charge–discharge of dielectric capacitor is also important for high-power energy storage application. The charge–discharge performance of ANT55 is measured at RT using a resistance–capacitance (RC) circuit. The discharge energy density (Wdis) is calculated according to \(W_{{\mathrm{dis}}} = R\smallint i(t)^2dt/V\)52, where V is the sample volume and R is the load resistor (13 kΩ). The time dependence of Wdis under various electric fields is displayed in Fig. 4g. The Wdis is measured to be 6.1 J cm−3 at 470 kV cm−1, comparable to that calculated from P–E loops. The small variation in values between two methods may be associated with the loss of discharged energy in the equivalent series resistor (ESR), domain walls movement and measurement frequency16,53. Moreover, the discharge time (t0.9, 90% of all stored energy is released) is less than 15 μs, revealing a high discharge speed.
Antiferroelectric ordering and local structure heterogeneity analysis
The excellent energy storage properties in ANTx solid solution are believed to be associated with its microstructure, i.e., the existence of AFE phase and relaxor component. In order to understand the relationship between the microstructure and energy storage properties, the synchrotron X-ray diffraction (SXRD), Raman spectra and annular dark-field scanning transmission electron microscopy (ADF-STEM) imaging were performed on the ANTx samples. Figure 5a shows the SXRD of ANTx ceramic powders, where pure perovskite structure can be observed for all ANTx solid solutions. The (220) and (008) reflections appear as a single peak at x > 50 mol%. The corresponding Rietveld refinements of SXRD profiles based on Pbcm space group are given in Supplementary Fig. 5. The low reliability factor values indicate the structural model is valid and the refinement results fit well with the experimental data. The Rietveld parameters are given in Fig. 5b–d, all of which exhibit strong composition-dependent behavior. The reduced cell volume might be attributed to the lower effective electronegativity of Ta5+ (1.5) compared to that of Nb5+ (1.6) since their ionic radii and valence are the same54,55. The displacements for Ag1 (located in 4d site in the Pbcm structure, see Supplementary Fig. 6a) and B-site (Nb/Ta) cations are calculated and found to decrease with increasing Ta content (Fig. 5c), indicating a weaker ordering of local displacements55. The [Nb/TaO6] octahedral tilting angles θ and Φ (the θ and Φ are tilting angles along b and c axes, respectively) also decrease with increase of Ta content (Fig. 5d), due to the smaller size of [TaO6] octahedra. The decreased cell volumes, cation displacements and octahedral tilting angles are thought to reflect an improved stability of AFE phase32,55. Of particular significance is that the parameters exhibit different trends as function of Ta level over the range of 50 mol to 60 mol% (guided by the blue shaded area in Fig. 5). Similar phenomenon is also observed for the lattice parameters, (220)/(008) d-spacing and |B-O | distance (Supplementary Fig. 6b–d). The abnormal variations in parameters might be attributed to M2–M3 phase transition, as generally observed in pure AN counterpart around M2–M3 phase transition temperature32, demonstrating that the x = 50–60 mol% compositions possess room temperature M2–M3 phase boundary. Figure 5e gives the Raman spectra of ANTx solid solution, where the incorporation of Ta is found to shift Raman wavenumbers to lower values, due to the higher atomic mass of Ta comparing to that of Nb. All Raman peaks become weaker in intensity and broader in shape with the increase of Ta content, being related to the improved disorder or relaxor feature. The peaks around 83, 205, and 632 cm−1, which are associated with the M1–M2 (FIE–AFE) phase transition, disappear at x = 20 mol%, being consistent with the dielectric measurement. The peaks with wavenumber at 500–650 cm−1 were fitted by using Gaussian function. Of particular interest is that the three fitted peaks in AN are merged into two peaks with Ta content over 40 mol% (Fig. 5f), revealing a possible M2–M3 phase transition above this composition, in agreement with the above dielectric and SXRD analysis regardless of the small deviation in composition.
The simultaneous integrated differential phase contrast (iDPC) and annular dark-field scanning transmission electron microscopy (ADF-STEM) imaging are performed on samples with x = 0 mol and 55 mol%, in order to investigate the local heterogeneity after Ta incorporation. While ADF imaging affords mass contrast imaging, the phase contrast of iDPC imaging is sensitive to light elements, allowing for the observation of oxygen56. Supplementary Fig. 7 shows atomic resolution iDPC images for AN and ANT55 samples on grains oriented along the [100]pc and [011]pc zone axes. Structural models generated from SXRD measurements are overlaid on the respective images illustrating the effect of octahedral distortion on the shape of the oxygen columns. Observations made directly from iDPC images are in agreement with SXRD measurements showing decreased octahedral distortion in ANT55 in comparison with AN. Figure 6a, b illustrates the oxygen–oxygen distances measured directly from iDPC images acquired for AN and ANT55 samples on grains oriented along the pseudocubic [011]pc zone axis, respectively. Obviously, the overall distortion on the oxygen sublattice decreases with mean oxygen–oxygen distances, which is 394.2 pm for AN and 393.1 pm for ANT55. It is important to note that while these mean values do not change significantly, the standard deviation of the distances decrease from 40 pm for AN to 25 pm for ANT55, in agreement with the expected decrease in octahedral tilting. The difference in cation–cation distances can also be determined for each sample. Cation–cation distances for the A sublattice (Ag) along the [110]pc direction are plotted in Fig. 6c, d for AN and ANT55 samples, respectively. Similar to O–O distances, the A–A distances are determined to decrease with Ta content, falling from 276.8 pm for AN to 276.2 pm for ANT55 samples. Conversely, while the A–A distances tend to decrease with Ta incorporation, the standard deviation of these distances increases from 2.9 to 4.5 pm between AN and ANT55, suggesting the increased local structural heterogeneity in ANT55 samples, induced by the mixing of Nb/Ta on the B sublattices, which is consistent with observations made in other relaxor systems57. To further demonstrate local structural heterogeneity, B sublattice (with respect to the A sublattice) displacements are plotted for the [100]pc zone axis as shown in Supplementary Fig. 8. For AN sample, a regular cation displacement pattern consistent with long-range antiferroelectricity is evident. For comparison, cation displacements for ANT55 vary significantly and lack long-range cooperation, being consistent with the scenario in a relaxor58. These observations provide strong evidence that Ta incorporation increases local structure heterogeneity in cation structure of ANT55. The existence of local structure heterogeneity in a fully stabilized AFE leads to relaxor AFEs and thus effectively impede the formation of macroscopic domain and smear the AFE–FE phase transition process. This is responsible for the nearly hysteresis-free P–E loops and the excellent energy storage properties in the designed ANT55 ceramics.
In summary, high energy storage density (6.3 J cm−3) and efficiency (90%) are achieved simultaneously in 0.45AgNbO3–0.55AgTaO3 bulk ceramics, by judiciously constructing the diffused M2–M3 phase boundary. The material exhibits broad usage temperature range up to 150 °C, with minimal variations less than 5 and 2% for energy storage density and efficiency, respectively. Meanwhile the minimal variations in storage density and efficiency as function of cycling number up to 106 reveal excellent cycling reliability. All the merits demonstrate that 0.45AgNbO3–0.55AgTaO3 ceramic is a promising candidate for high-power energy storage applications. It should be noticed that the energy storage density would be further improved in ANTx multilayer ceramics and film capacitors, due to the significantly increased breakdown strength. In addition, the unfolding of RAFE characteristic of M2–M3 phase boundary on atomic scale in AN-based solid solution gives a solid evidence to the long-term confusion of the broad dielectric anomaly over M2–M3 phase transition temperature, which opens a broad range of applications where relaxor feature is desired, such as electrocaloric solid-state cooling devices59,60 and hysteresis-free actuators61,62.
Methods
Ceramic fabrication
The (1-x)AgNbO3–xAgTaO3 (x is 0, 10, 20, 30, 40, 45, 50, 55, 60, and 65 mol%, abbreviated as ANTx: ANT0-65) ceramics were synthesized by a conventional solid-state reaction method. The raw materials Ag2O (99.7%), Nb2O5 (99.5%), and Ta2O5 (99.99%) were carefully weighed and ball milled for 24 h in a nylon jar with alcohol using yttrium stabilized zirconia balls as milling media. The mixed powders were dried and then calcined at 900 °C for 6 h in oxygen atmosphere, followed by a second ball milling. The granulated powers were pressed into pellets with a diameter of 8 mm and thickness of ~1 mm, followed by cold isostatic pressing under 200 MPa to improve the green density. The pellets were then sintered at 1070–1180 °C based on the compositions for 6 h in oxygen atmosphere. For electrical properties measurement, the ceramics were polished down to a thickness of ~0.15 mm and then two parallel surfaces were coated with silver paste (~3 mm in diameter), and finally fired at 560 °C for 30 min as electrodes.
Dielectric measurements
The temperature dependence of dielectric permittivity and loss was measured using an LCR analyzer (Model 4294 A, Hewlett-Packard Co., Palo Alto, CA, USA) over the temperature range from −180 to 440 °C. The electric field dependence of normalized dielectric permittivity (dielectric tunability) was measured using an TF Analyzer 2000 (aixACCT, Aachen, Germany) with a maximum bias field of 80 kV cm−1.
Ferroelectric measurements
P–E loops and I–V curves were measured under a triangular field at 1 Hz by using the ferroelectric testing system (Precision Multiferroic, Radiant Technologies Inc., Albuquerque, NM) connected to a homemade heating system.
Charge–discharge measurements
The discharge speed and discharge energy density were measured using a capacitor charge–discharge test system (PK‐CPR1701, PolyK Technologies, PA, USA).
Dielectric breakdown test
The Eb was measured using a voltage breakdown tester (RK2671AM, Shenzhen Meiruike electronic technology Co. Ltd, Shenzhen, China) on the sample with thickness of ~0.15 mm and diameter of 3 mm. The value of Eb was evaluated by using the following Weibull distribution functions:21,49
where n is the total number of samples, Ei is the breakdown electric field for the ith specimen arranging in ascending order, and Ni the probability of dielectric breakdown. Xi and Yi should have a linear relationship.
Band gap tests
Ultraviolet and visible (UV–vis) absorption spectra was obtained using a UV–vis spectrometer (UV3600, Shimadzu, Kyoto, Japan), fitted with BaSO4 as the standard material in the wavelength region of 200–800 nm.
Characterization of phase and microstructure
The microstructure of the polished and thermally etched samples was observed using a scanning electron microscope (Phenom Pro X, Phenom-World, Eindhoven, Netherlands). The crystal structure was characterized using synchrotron X‐ray diffractions (SXRD) in a capillary mode. The high-resolution data were collected at TPS 09 A (Taiwan Photon Source) of the National Synchrotron Radiation Research Center. The 15 keV X-ray source (wavelength 0.826569 Å) is delivered from an in-vacuum undulator (IU22), and the powder diffraction patterns were recorded by a position-sensitive detector, MYTHEN 24 K, covering a 2θ range of 120°. The full XRD data were analyzed by the Rietveld refinement using TOPAS 4.2 software (Bruker AXS GmbH, Germany). The Raman spectra was carried out using a laser confocal Raman microspectroscopy (LabRAM HR800, Horiba JobinYvo) with excitation at 532 nm and 50 mW. Atomic resolution scanning transmission electron microscope (STEM) was performed on an image and probe corrected FEI Themis Z 60–300k kV S/TEM (ThermoFisher Scientific, Eindhoven, Netherlands) equipped with an X-FEG source and operated at an accelerating voltage of 300 kV. A beam current of 15 pA and a semi-angle of convergence of 17.9 mrad was utilized. ADF images were collected with a detector semi-angle range of 28–180 mrad while iDPC images were collected with a detector semi-angle range of 7–28 mrad. Distortion corrected images were produced via post processing two (1024 × 1024 pixel, 10 µs/pixel dwell time) images acquired at orthogonal scan directions63. Atom column locations were determined via Atomap64 with analysis being performed with custom MATLAB and Python scripts.
Data availability
The data that support the plots within this paper and other findings of this study are either provided in the Article and its Supplementary information or available from the corresponding author upon request.
References
Chu, B. et al. A dielectric polymer with high electric energy density and fast discharge speed. Science 313, 334–336 (2006).
Li, Q. et al. Flexible high-temperature dielectric materials from polymer nanocomposites. Nature 523, 576–579 (2015).
Yao, Z. et al. Homogeneous/inhomogeneous-structured dielectrics and their energy-storage performances. Adv. Mater. 29, 1601727–1601741 (2017).
Li, Q. et al. Solution-processed ferroelectric terpolymer nanocomposites with high breakdown strength and energy density utilizing boron nitride nanosheets. Energy Environ. Sci. 8, 922–931 (2015).
Hao, X. A review on the dielectric materials for high energy-storage application. J. Adv. Dielect. 3, 1330001 (2013).
Yang, L. et al. Perovskite lead-free dielectrics for energy storage applications. Prog. Mater. Sci. 102, 72–108 (2019).
Wang, H., Liu, Y., Yang, T. & Zhang, S. Ultrahigh energy-storage density in antiferroelectric ceramics with field-induced multiphase transitions. Adv. Funct. Mater. 29, 1807321 (2019).
Zhang, L., Jiang, S., Fan, B. & Zhang, G. Enhanced energy storage performance in (Pb0.858Ba0.1La0.02Y0.008)(Zr0.65Sn0.3Ti0.05)O3–(Pb0.97La0.02)(Zr0.9Sn0.05Ti0.05)O3 anti-ferroelectric composite ceramics by spark plasma sinterin. J. Alloy. Compd. 622, 162–165 (2015).
Liu, X., Li, Y. & Hao, X. Ultra-high energy-storage density and fast discharge speed of (Pb0.98−xLa0.02Srx)(Zr0.9Sn0.1)0.995O3 antiferroelectric ceramics prepared via the tape-casting method. J. Mater. Chem. A 7, 11858–11866 (2019).
Kittel, C. Theory of antiferroelectric crystals. Phys. Rev. 82, 729–732 (1951).
Cowley, R., Gvasaliya, S., Lushnikov, S., Roessli, B. & Rotaru, G. Relaxing with relaxors: a review of relaxor ferroelectrics. Adv. Phys. 60, 229–327 (2011).
Li, F., Zhang, S., Damjanovic, D., Chen, L. Q. & Shrout, T. R. Local structural heterogeneity and electromechanical responses of ferroelectrics: learning from relaxor ferroelectrics. Adv. Funct. Mater. 28, 1801504 (2018).
Pan, H. et al. Giant energy density and high efficiency achieved in bismuth ferrite-based film capacitors via domain engineering. Nat. Commun. 9, 1813 (2018).
Venkateshwarlu, S., Nayak, S., Marlton, F. P., Weyland, F. & Pramanick, A. Relaxor behavior and electrothermal properties of Sn- and Nb-modified (Ba,Ca)TiO3 Pb-free ferroelectri. J. Mater. Res. 35, 1017–1027 (2020).
Cao, W. et al. Large electrocaloric response and high energy-storage properties over a broad temperature range in lead-free NBT-ST ceramics. J. Eur. Ceram. Soc. 36, 593–600 (2016).
Li, J., Li, F., Xu, Z. & Zhang, S. Multilayer lead-free ceramic capacitors with ultrahigh energy density and efficiency. Adv. Mater. 30, e1802155 (2018).
Qi, H. et al. Ultrahigh energy-storage density in nanbo3-based lead-free relaxor antiferroelectric ceramics with nanoscale domains. Adv. Funct. Mater. 29, 1903877 (2019).
Łukaszewski, M., Pawełczyk, M., Haňderek, J. & Kania, A. On the phase transitions in silver niobate AgNbO3. Phase transitions: a multinational. Journal 3, 247–257 (1983).
Sciau, P., Kania, A., Dkhil, B., Suard, E. & Ratuszna, A. structural investigation of AgNbO3 phases using X-ray and neutron diffraction. J. Phys. Condens. Matter 16, 2795 (2004).
Tian, Y. et al. High energy density in silver niobate ceramics. J. Mater. Chem. A 4, 17279–17287 (2016).
Zhao, L., Liu, Q., Zhang, S. & Li, J.-F. Lead-free AgNbO3 anti-ferroelectric ceramics with an enhanced energy storage performance using MnO2 modification. J. Mater. Chem. C. 4, 8380–8384 (2016).
Tian, Y. et al. Phase transitions in bismuth-modified silver niobate ceramics for high power energy storage. J. Mater. Chem. A 5, 17525–17531 (2017).
Luo, N. et al. Lead free Ag1−3xLaxNbO3 antiferroelectric ceramics with high energy storage density and efficiency. J. Am. Ceram. Soc. 102, 4640–4647 (2019).
Luo, N. et al. Design for high energy storage density and temperature insensitive lead-free antiferroelectric ceramics. J. Mater. Chem. C. 7, 4999 (2019).
Zhao, L., Liu, Q., Gao, J., Zhang, S. & Li, J. F. Lead-Free antiferroelectric silver niobate tantalate with high energy storage performance. Adv. Mater. 29, 1701824–1701830 (2017).
Zhao, L., Gao, J., Liu, Q., Zhang, S. & Li, J.-F. Silver niobate lead-free antiferroelectric ceramics: enhancing energy storage density by B-site doping. ACS Appl. Mater. Interfaces 10, 819–826 (2018).
Yan, Z. et al. Silver niobate based lead-free ceramics with high energy storage density. J. Mater. Chem. A 7, 10702–10711 (2019).
Han, K. et al. Ultrahigh energy-storage density in A-/B-site co-doped AgNbO3 lead-free antiferroelectric ceramics: insight into the origin of antiferroelectricity. J. Mater. Chem. A 7, 26293–26301 (2019).
Luo, N. et al. Aliovalent A-site engineered AgNbO3 lead-free antiferroelectric ceramics toward superior energy storage density. J. Mater. Chem. A 7, 14118–14128 (2019).
Han, K. et al. Realizing high low-electric-field energy storage performance in AgNbO3 ceramics by introducing relaxor behaviour. J. Materiomics 5, 597–605 (2019).
Valant, M., Axelsson, A.-K. & Alford, N. Review of Ag (Nb, Ta)O3 as a functional material. J. Eur. Ceram. Soc. 27, 2549–2560 (2007).
Levin, I. et al. Structural changes underlying the diffuse dielectric response in AgNbO3. Phy. Rev. B 79, 104113 (2009).
Farid, U., Khan, H. U., Avdeev, M., Injac, S. & Kennedy, B. J. Structural studies of the high temperature phases of AgTaO3. J. Solid State Chem. 258, 859–864 (2018).
Pawełczyk, M. Phase transitions in AgTaxNb1−xO3 solid solutions. Phase Transit 8, 273–292 (1987).
Cross, L. E. Relaxor ferroelectrics. Ferroelectrics 76, 241–267 (1987).
Khan, H., Alam, K., Mateenullah, M., Blaschke, T. & Haq, B. Synthesis and characterization of solid solution Ag(NbxTa1−x)O3 (x = 0, 0.25, 0.5, 0.75, 1.0). J. Eur. Ceram. Soc. 35, 2775–2789 (2015).
Tunkasiri, T. & Rujijanagul, G. Dielectric strength of fine grained barium titanate ceramics. J. Mater. Sci. Lett. 15, 1767–1769 (1996).
Kim, C., Pilania, G. & Ramprasad, R. Machine learning assisted predictions of intrinsic dielectric breakdown strength of ABX3 perovskites. J. Phy. Chem. C. 120, 14575–14580 (2016).
Shen, Z.-H. et al. Phase-field modeling and machine learning of electric-thermal-mechanical breakdown of polymer-based dielectrics. Nat. Commun. 10, 1843 (2019).
Wang, Y. et al. Optimization of energy storage density and efficiency in BaxSr1−xTiO3 (x ≤ 0.4) paraelectric ceramics. Ceram. Int. 41, 8252–8256 (2015).
Yuan, Q., Yao, F., Wang, Y., Ma, R. & Wang, H. Relaxor ferroelectric 0.9BaTiO3–0.1Bi (Zn0.5Zr0.5)O3 ceramic capacitors with high energy density and temperature stable energy storage properties. J. Mater. Chem. C. 5, 9552–9558 (2017).
Li, W.-B., Zhou, D., Pang, L.-X., Xu, R. & Guo, H.-H. Novel barium titanate based capacitors with high energy density and fast discharge performance. J. Mater. Chem. A 5, 19607–19612 (2017).
Li, F. et al. Influence of structural evolution on energy storage properties in Bi0.5Na0.5TiO3-SrTiO3-NaNbO3 lead-free ferroelectric ceramics. J. Appl. Phys. 121, 054103 (2017).
Yang, H., Yan, F., Lin, Y., Wang, T. & Wang, F. High energy storage density over a broad temperature range in sodium bismuth titanate-based lead-free ceramics. Sci. Rep. 7, 1–12 (2017).
Shao, T. et al. Potassium–sodium niobate based lead-free ceramics: novel electrical energy storage materials. J. Mater. Chem. A 5, 554–563 (2017).
Yang, Z. et al. Significantly enhanced recoverable energy storage density in potassium–sodium niobate-based lead free ceramics. J. Mater. Chem. A 4, 13778–13785 (2016).
Qu, B., Du, H. & Yang, Z. Lead-free relaxor ferroelectric ceramics with high optical transparency and energy storage ability. J. Mater. Chem. C. 4, 1795–1803 (2016).
Zhou, M., Liang, R., Zhou, Z., Yan, S. & Dong, X. Novel sodium niobate-based lead-free ceramics as new environment-friendly energy storage materials with high energy density, high power density, and excellent stability. ACS Sustain. Chem. Eng. 6, 12755–12765 (2018).
Zhou, M., Liang, R., Zhou, Z. & Dong, X. Superior energy storage properties and excellent stability of novel NaNbO3-based lead-free ceramics with A-site vacancy obtained via a Bi2O3 substitution strategy. J. Mater. Chem. A 6, 17896–17904 (2018).
Maurya, D., Sun, F. C., Pamir Alpay, S. & Priya, S. A new method for achieving enhanced dielectric response over a wide temperature range. Sci. Rep. 5, 15144 (2015).
Pan, W., Zhang, Q., Bhalla, A. & Cross, L. E. Field-forced antiferroelectric-to-ferroelectric switching in modified lead zirconate titanate stannate ceramics. J. Am. Ceram. Soc. 72, 571–578 (1989).
Li, F., Zhou, M., Zhai, J., Shen, B. & Zeng, H. Novel barium titanate based ferroelectric relaxor ceramics with superior charge-discharge performance. J. Eur. Ceram. Soc. 38, 4646–4652 (2018).
Xu, R. et al. Polarization of antiferroelectric ceramics for pulse capacitors under transient electric field. J. Appl. Phys. 119, 224103 (2016).
Eng, H. W., Barnes, P. W., Auer, B. M. & Woodward, P. M. Investigations of the electronic structure of d0 transition metal oxides belonging to the perovskite family. J. Solid State Chem. 175, 94–109 (2003).
Levin, I. et al. Displacive ordering transitions in perovskite-like AgNb1/2Ta1/2O3. Chem. Mater. 22, 4987–4995 (2010).
Lazić, I., Bosch, E. G. & Lazar, S. Phase contrast STEM for thin samples: Integrated differential phase contrast. Ultramicroscopy 160, 265–280 (2016).
Kumar, A. et al. Decoding the complexities of lead-based relaxor ferroelectrics. Preprint at http://arXiv:1911.05853 (2019).
Pan, H. et al. Ultrahigh–energy density lead-free dielectric films via polymorphic nanodomain design. Science 365, 578–582 (2019).
Nair, B. et al. Large electrocaloric effects in oxide multilayer capacitors over a wide temperature range. Nature 575, 468–472 (2019).
Pirc, R., Kutnjak, Z., Blinc, R. & Zhang, Q. M. Electrocaloric effect in relaxor ferroelectrics. J. Appl. Phys. 110, 074113 (2011).
Yin, J., Zhao, C., Zhang, Y. & Wu, J. Ultrahigh strain in site engineering-independent Bi0.5Na0.5TiO3-based relaxor-ferroelectrics. Acta Mater. 147, 70–77 (2018).
Li, T. et al. High electrostrictive strain in lead-free relaxors near the morphotropic phase boundary. Acta Mater. 182, 39–46 (2020).
Ophus, C., Ciston, J. & Nelson, C. T. Correcting nonlinear drift distortion of scanning probe and scanning transmission electron microscopies from image pairs with orthogonal scan directions. Ultramicroscopy 162, 1–9 (2016).
Nord, M., Vullum, P. E., MacLaren, I., Tybell, T. & Holmestad, R. Atomap: a new software tool for the automated analysis of atomic resolution images using two-dimensional Gaussian fitting. Adv. Struct. Chem. Imag. 3, 9 (2017).
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China (Grant No. 11864004), the Natural Science Foundation of Guangxi Province (Grant No. 2017GXNSFBA198132), the Science and Technology Major Project of Guangxi Province (Grant No. AA17204100). S.Z. acknowledges the support of the Australian Research Council (Grant No. FT140100698). M.J.C. and X.L. acknowledge the support of the Australian Research Council (Grant No. DP190101155). J.L. acknowledges the support of the Basic Science Center Program of the National Natural Science Foundation of China (Grant No. 51788104). We are grateful for the scientific and technical support from the Australian Centre for Microscopy and Microanalysis as well as the Microscopy Australia node the University of Sydney. We also acknowledge the support team (Dr. H.S. Sheu, Dr. Y.C. Chuang, Dr. Y.C. Lai, and Mr. C.K. Chang) for assistance at TPS 09 A in NSRRC.
Author information
Authors and Affiliations
Contributions
N.L. conceived the initial concept. N.L., H.K., X.C., and Q.F. prepared the sample and processed the experimental data. N.L., M.J.C., S.Z., Y.W., and J. L. interpreted the theoretical and experimental results. M.J.C. and X.L. conducted the TEM observations. C.L. measured the SXRD. G.Z. conducted the charge–discharge measurement. N.L., M.J.C., and S.Z. wrote the paper, all authors discussed and edited the paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Luo, N., Han, K., Cabral, M.J. et al. Constructing phase boundary in AgNbO3 antiferroelectrics: pathway simultaneously achieving high energy density and efficiency. Nat Commun 11, 4824 (2020). https://doi.org/10.1038/s41467-020-18665-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-18665-5
This article is cited by
-
Design strategies of high-performance lead-free electroceramics for energy storage applications
Rare Metals (2024)
-
Moderate Fields, Maximum Potential: Achieving High Records with Temperature-Stable Energy Storage in Lead-Free BNT-Based Ceramics
Nano-Micro Letters (2024)
-
Well-defined double hysteresis loop in NaNbO3 antiferroelectrics
Nature Communications (2023)
-
Heterovalent-doping-enabled atom-displacement fluctuation leads to ultrahigh energy-storage density in AgNbO3-based multilayer capacitors
Nature Communications (2023)
-
Tailoring high-energy storage NaNbO3-based materials from antiferroelectric to relaxor states
Nature Communications (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.