Abstract
Skyrmions are vortex-like spin textures that form strings in magnetic crystals. Due to the analogy to elastic strings, skyrmion strings are naturally expected to braid and form complex three-dimensional patterns, but this phenomenon has not been explored yet. We found that skyrmion strings can form braids in cubic crystals of chiral magnets. This finding is confirmed by direct observations of skyrmion braids in B20-type FeGe using transmission electron microscopy. The theoretical analysis predicts that the discovered phenomenon is general for a wide family of chiral magnets. These findings have important implications for skyrmionics and propose a solid-state framework for applications of the mathematical theory of braids.
Similar content being viewed by others
Introduction
Filamentary textures can take the form of braided, rope-like superstructures in nonlinear media such as plasmas and superfluids1,2,3. The formation of similar superstructures in solids has been predicted, for example, from flux lines in superconductors4. However, their observation has proved challenging5,6.
Here, we provide unambiguous experimental evidence for braids of skyrmion strings in cubic crystals of chiral magnets.
Magnetic skyrmions7,8,9,10 have been observed over a wide range of temperatures and applied magnetic fields in Ge-based and Si-based alloys with B20-type crystal structures, such as FeGe11,12,13,14, MnSi15, Fe1−xCoxSi16,17 and others18. These skyrmions are topologically nontrivial textures of the magnetization unit vector field m(r), whose filamentary structures resemble vortex-like strings or tubes, with typical diameters of tens of nanometers. The length of such a string is assumed to be limited only by the shape and size of the sample19, with direct observations confirming the formation of micrometer-long skyrmion strings20,21. Previous studies have suggested that magnetic skyrmion strings are (nearly) straight19,20,21,22,23,24,25. In contrast, here we show that skyrmion strings are able to twist around one another to form superstructures that we refer to as skyrmion braids (Fig. 1).
We begin with a theoretical description, which is based on a micromagnetic approach and a standard model of cubic helimagnets (chiral magnets), such as FeGe (see Methods). Static equilibrium in such a system results from a delicate balance between Heisenberg exchange, Zeeman interaction, chiral Dzyaloshinskii–Moriya interaction26,27 (DMI), and dipole–dipole interaction. The equilibrium state is typically a conical spin spiral, whose modulation axis is parallel to the applied field Bext (inset to Fig. 1a). The period of such a spiral LD is nearly constant for each material, taking a value of ~70 nm for FeGe28. The conical phase can be regarded as a natural “vacuum” (background), in which clusters and isolated strings of skyrmions are embedded23,24.
Results
Micromagnetic simulations
We use energy minimization (see Methods) to show that interacting skyrmion strings can lower their total energy by twisting into braids. A representative example of such a skyrmion braid is shown in Fig. 1 for an energetically favorable configuration of five skyrmion strings, which wind around a sixth straight string at their center. Such a winding braid forms spontaneously from an initial configuration of six straight skyrmion strings (see Methods and Supplementary Movie 1). A skyrmion braid has one energetically preferable chirality, which depends on the sign of the DMI constant D. Without loss of generality, we assume below that D > 0. The chirality of the twist is opposite to that of the magnetization of the surrounding cone phase, as indicated using blue and red arrows, respectively, in Fig. 1a. Although this behavior may appear to be counterintuitive, along any line parallel to the z axis, the spins have the same sense of rotation about \({\hat{{{{{{{{\bf{e}}}}}}}}}}_{{{{{{{{\rm{z}}}}}}}}}\) as for the conical spiral. The twisting or untwisting of a skyrmion braid by an external magnetic field, as illustrated in Fig. 1a–d, is fully reversible (see Supplementary Movie 1).
In order to quantify the degree of twist, we trace the position of each skyrmion by its center, where the magnetization is antiparallel to Bext. We define the twist angle φi(z) for the ith skyrmion in each z plane as the angle between the x axis and the line connecting the central and ith skyrmion (Fig. 1c). The φi(z) curves shown in Fig. 1e are almost linear and have identical slopes, with small deviations close to the free surfaces due to the chiral surface twist22. A linear fit to each plot of φi(z) can be used to estimate the total twist angle Δφi, by which the strings rotate from the lower to the upper surface.
Figure 1f shows the dependence of the average twist angle \(\langle {{\Delta }}\varphi \rangle =\frac{1}{5}{\sum }_{i}{{\Delta }}{\varphi }_{i}\) on the applied magnetic field, both with and without consideration of demagnetizing fields, to illustrate the role of dipole–dipole interactions. The twist angle is reduced by a factor of ~2 when demagnetizing fields are neglected. This difference decreases with increasing Bext. The applied magnetic field is shown in reduced units relative to the critical field Bc in Fig. 1f, in order to facilitate a comparison between the results obtained with and without demagnetizing fields. In both cases, Bc is the phase-transition field between conical and saturated ferromagnetic states (see Methods). Figure 1g shows the dependence of the twist angle 〈Δφ〉 on sample thickness t at fixed Bext. Although dipole–dipole interactions increase the degree of twist significantly, they are not necessary for the stability of skyrmion braids.
The quasilinear dependence of φi(z) on z in Fig. 1e and the monotonic dependence of 〈Δφ〉(t) on t in Fig. 1g suggest that the volume and the free surfaces both play important roles in the formation of skyrmion braids.
Calculations performed for a bulk sample with periodic boundary conditions show that, for example, in Fig. 2a, a six-string skyrmion braid is energetically more favorable than a cluster of straight strings in fields below B* ≈ 0.61Bc (see the vertical dashed line in Fig. 2b). Figure 2c illustrates the details of the energy redistribution for an arbitrarily chosen value of Bext below B*. In a thin plate, however, the same braid is stable above B* (Fig. 1f), suggesting that surface effects may additionally enhance braid stability. The mechanism of skyrmion braid stability therefore results from a sophisticated interplay of multiple energy terms and depends on the geometry of the system. The dipole–dipole interaction does not play a fundamental role in the energy stability of a braid, but contributes to it. Instead, the stability of a braid results primarily from the energies of exchange-type interactions associated with texture distortions.
Experimental observations
The dependence of the average twist angle 〈Δφ〉 on plate thickness shown in Fig. 1g suggests that the helical twist of skyrmion strings should be observable in a thin sample, for which t ~ LD. This criterion is important for observations using transmission electron microscopy (TEM), for which an electron-transparent sample is required. For Fe0.5Co0.5Si, with LD ~ 90 nm, the thickness below which a sample is electron-transparent at an accelerating voltage of 300 kV is ~3.3 LD, corresponding to ~300 nm17. This value is assumed to be approximately the same for FeGe.
We studied three high-quality electron-transparent FeGe lamellae with thicknesses of ~180 nm (~2.6 LD), which is large enough for the formation of skyrmion braids but small enough for magnetic imaging in the TEM. The lateral dimensions of the samples were 1 × 1 μm (S1), 800 × 540 nm (S2), 6 × 7 μm (S3). We observed skyrmion braids in all three samples. Below, we provide representative results from samples S1 and S2. Other results are included in Supplementary Figs. 2–9 and Movies 3–6.
For experimental observations of skyrmion braids, we designed the following protocol. First, we performed magnetization-reversal cycles until a desired number of skyrmion strings had nucleated in the sample. Multiple cycles were required due to the probabilistic character of skyrmion nucleation. In order to avoid the interaction of skyrmions with the edges of the sample, the strength of the external magnetic field was increased to move the skyrmions toward the center of the sample. We then gradually decreased the applied magnetic field until the contrast of the straight skyrmion strings changed to those expected for braids. (see Supplementary Movie 5). Although this is not a unique protocol for nucleating skyrmion braids (see, e.g., Supplementary Fig. 3), it results in high reproducibility of the results. (See Supplementary Movies 4 and 6). We did not observe skyrmion braids during in-field cooling of the samples.
Figure 3 shows experimental Lorentz TEM images (a–c) and theoretical results (d–g) for short skyrmion braids. Here, we compare only the Lorentz TEM images. See Supplementary Fig. 10 for different defocus values and Supplementary Fig. 11 for the case of opposite chirality of the material. Representative experimental phase-shift images for sample S1 recorded using off-axis electron holography are provided in Supplementary Fig. 2. Good agreement is obtained between the experimental and simulated images. The key feature of these magnetic images of skyrmion braids is the appearance of a ring-like pattern and a significant reduction in contrast in comparison with straight skyrmions, as shown in the lower row in Fig. 3a–c. The correlation between the magnetic images and average in-plane magnetization components \({\langle {{{{{{{{\bf{m}}}}}}}}}_{{{{{{{{\rm{xy}}}}}}}}}\rangle }_{{{{{{{{\rm{z}}}}}}}}}={t}^{-1}\int {{{{{{{{\bf{m}}}}}}}}}_{{{{{{{{\rm{xy}}}}}}}}}dz\) in Fig. 3d–g arises because, to a first approximation, the magnetic field follows the m vector. It should be noted that the electron beam is perpendicular to the plate and only sensitive to xy component of the magnetic field within and around the sample. In sample S1 (and similarly in sample S3—see Supplementary Fig. 9), the typical applied fields that were found to stabilize braids were different from theoretical values. This discrepancy can be attributed to minor damage from the fabrication process29, including the formation of thin amorphous magnetic surface layers30,31,32. In contrast, excellent agreement with theory was achieved for sample S2, which was also used in Ref. 33.
Figure 4 shows experimental and theoretical images for sample S2 (see also Supplementary Fig. 4). Figure 4a shows a three-string skyrmion braid. Figure 4b shows a skyrmion braid comprising six strings in a pentagonal pattern, similar to those shown in Fig. 3c, g. As a result of its smaller size, electron phase-shift images could be recorded from this sample using off-axis electron holography (see Methods). Excellent agreement is obtained between experiment and theory for both underfocus and overfocus Lorentz TEM images and electron phase-shift images, providing confidence in the interpretation of the experimental data. The skyrmion braids can be stabilized over a wide temperature range, as shown in the form of representative magnetic images in Supplementary Fig. 8 for sample S1 at 120 K and Supplementary Fig. 6 for sample S2 at 170 K.
Discussion
Because of the magnetization inhomogeneities along the skyrmion braids, their electromagnetic properties are expected to differ from those of straight skyrmion strings. Electrons passing along the braids accumulate a Berry phase and experience emergent electric and magnetic fields that are modulated with the thickness of the sample and quantized by the number of skyrmion strings in the braid. This, in turn, gives rise to magnetoresistive and transport phenomena that would not be observed for straight skyrmion strings. A promising system for demonstrating these effects is a magnetic nanowire34,35, in which a skyrmion braid can occupy the entire volume. In larger samples, skyrmion braids are expected to differ in structure and close-packing form36,37. See additional examples of superstructures of braided skyrmions in Supplementary Figs. 12 and 13.
In contrast to magnetic hopfions38,39,40, skyrmion braids cannot be localized completely in three dimensions without singularities. In other words, skyrmion strings start on one surface of a sample and end on the other surface. A skyrmion braid represents a geometric braid41 when the ends of the skyrmion strings are fixed on the sample surface due to pinning or surface engineering. It is then topologically protected and cannot be unwound. The latter behavior is guaranteed by the robustness of skyrmion strings, resembling strides42 of a geometric braid. Such skyrmion braids can be described in terms of an Artin braid group43 \({{{{{{{{\mathcal{B}}}}}}}}}_{N}\). In this sense, skyrmion braids are three-dimensional analogs of anyons44 in (2 + 1)-dimensional space-time.
In summary, we have discovered novel magnetic superstructures, which we term skyrmion braids, using electron microscopy and micromagnetic calculations. The generality of our theoretical approach suggests that superstructures of skyrmion strings that wind around one another can be formed in all noncentrosymmetric cubic magnets, offering new perspectives for studies and applications of the anomalous (topological) Hall effect34,45,46, magnetic resonance, spin waves on skyrmion strings47,48, and magnetization dynamics driven by currents34.
Methods
Micromagnetic calculations
For a theoretical description of skyrmion braids, we follow the micromagnetic approach. In the most general case, when the demagnetizing field is taken into account, the state of a system is described in terms of two coupled vector fields: the magnetization field M(r), which is defined only inside the volume of the magnet Vm, and the magnetic field B(r), which is defined in all space. The field B(r) is typically the sum of a homogeneous applied magnetic field Bext and the demagnetizing field produced by the magnetic sample itself. It can be expressed in the form
where Ad(r) is the component of magnetic vector potential due to the presence of the magnetization field M(r). The total energy of the system (up to an additive constant) is the sum of the exchange energy, the DMI energy, the Zeeman energy, and the self-energy of the demagnetizing field:
where m(r) = M(r)/Ms is a unit vector field that defines the direction of the magnetization, Ms = ∣M(r)∣ is the saturation magnetization, \({{{{{{{\mathcal{A}}}}}}}}\) is the exchange-stiffness constant, \({{{{{{{\mathcal{D}}}}}}}}\) is the constant of isotropic bulk DMI, and μ0 is the vacuum permeability (μ0 ≈ 1.256 × 10−6 N A−2). The notation \(| \nabla {{{{{{{\bf{m}}}}}}}}{| }^{2}\equiv \sum\nolimits_{i=x,y,z}| \nabla {m}_{i}{| }^{2}\) denotes the Euclidean norm of gradients of m. In our simulations, we used the following material parameters for FeGe33: \({{{{{{{\mathcal{A}}}}}}}}=4.75\) pJm−1, \({{{{{{{\mathcal{D}}}}}}}}=0.853\) mJm−2, and Ms = 384 kAm−1.
Static equilibrium solutions discussed in the main text were obtained by numerical minimization of (2) for the pair of fields m and Ad. Such an approach for the solution of magnetostatic problems is well known49,50,51, but has rarely been used in practice due to the complexity of its implementation and an ambiguity associated with gauge freedom. In order to eliminate the gauge freedom and to increase the robustness of the numerical scheme, we used the replacement ∣∇ × Ad∣2 → ∣∇Ad∣2 in the last integral in (2) (see Ref. 52 for details). A well-known consequence of the fact that the vector potential is a continuous field that is noncompact is the Ehrenberg–Siday–Aharonov–Bohm effect. As a result of the noncompactness of Ad, the last integral in (2) is taken over the entirety of three-dimensional space.
We split our implementation into two regions: the interior region—the sample and a relatively small (with respect to the size of the sample) vacuum layer around it, and the exterior region—the rest of the space. The interior was discretized on a regular mesh with spacing 3 nm and the corresponding equations were approximated by a finite-difference method. In the case of periodic boundary conditions in the xy plane, the in-plane mesh size was 256 × 256. In the exterior, the field Ad was approximated by a linear combination of the vector fields a1, a2, ... an. The vector fields ai(r) were selected to be linearly-independent solutions of the Laplace equation, with regular behavior at infinity. The total number of the ai vector field n was chosen to achieve a balance between accuracy and performance. By using toy problems (e.g., uniformly magnetized cuboids), as well as the method of optimal grids53,54, it was concluded that the most significant factor that limited the overall accuracy of the calculation was the grid spacing in the interior.
For the calculations of the bulk (Fig. 2), we omitted dipole–dipole interactions. When using periodic boundary conditions, we increased the accuracy of the calculations by means of an 8th-order finite-difference scheme, which is a generalization of the approach suggested by Donahue and McMichael55. In this case, the mesh spacing was set to 0.05 LD (3.5 nm).
Minimization was carried out using a nonlinear conjugate-gradient method. All of the calculations, including simulations of Lorentz TEM images and phase-shift images, were performed using the high performance GPU-accelerated software Excalibur. (see Ref. 56 for more details). For additional verification, a double-check was performed by reproducing some of the solutions for m(r) using the publicly available software MuMax357.
Derivation of critical fields
The Hamiltonian in Eq. (2) has an exact solution for a film of finite thickness t (thin bulk) in the presence of a perpendicular applied magnetic field \({{{{{{{{\bf{B}}}}}}}}}_{{{{{{{{\rm{ext}}}}}}}}}| | {\hat{{{{{{{{\bf{e}}}}}}}}}}_{{{{{{{{\rm{z}}}}}}}}}\):
where the cone angle
the amplitude of the vector potential
the auxiliary function
the wave number \(k = \frac{{{{{{{{\mathcal{D}}}}}}}}}{2{{{{{{{\mathcal{A}}}}}}}}}\), and \({B}_{{{\mbox{D}}}} = \frac{{{{{{{{{\mathcal{D}}}}}}}}}^{2}}{2{M}_{{{\mbox{s}}}}{{{{{{{\mathcal{A}}}}}}}}}\) is the critical value of the magnetic field in the limit of neglecting demagnetization (this limit corresponds to the case μ0 → 0).
In accordance with Eq. (5), we define the critical field Bc to be equal to BD for a model approach that neglects magnetostatics, while Bc = BD + μ0Ms for a full model based on Eq. (2). For the above material parameters for FeGe, BD = 0.199 T and BD + μ0Ms = 0.682 T.
Initial guesses for calculations
We set the initial guess for the magnetization (the initial magnetization state), representing a vacuum for embedded localized states, to be a perfect conical phase (3). We then use a vortex-like ansatz7 to embed straight skyrmion strings into this conical background. In some cases, the skyrmion strings in the initial guess are twisted arbitrarily, in order to identify other possible stable states that have different morphologies or twist angles from the spontaneous one. The initial guess for the vector potential field Ad is always set to be zero.
The positions of the textures in the experimental images were reproduced by adjusting the orientation of Bext and using a technique for crafting magnetic textures that is described in Ref. 56 and Supplementary Movie 2. In the simulations, the maximum tilt angle of Bext relative to the normal \({\hat{{{{{{{{\bf{e}}}}}}}}}}_{z}\) was 1∘, which does not exceed the corresponding tolerance of such an angle in the experimental setup.
Simulation of electron optical-phase shift
Since our approach for the solution of the micromagnetic problem recovers the magnetic vector potential Ad, simulation of the electron optical-phase shift is straightforward. When the incident electron beam direction is along the negative z axis, the phase shift can be calculated using the following integral58:
where e is an elementary (positive) charge (~1.6 × 10−19 C) and h is Planck’s constant (~6.63 × 10−34 m2 kg s−1).
Simulation of Lorentz TEM images
In the phase-object approximation, the wave function of an electron beam58 transmitted through a sample in the xy plane can be written in the form
where φ(x, y) is the phase shift defined in Eq. (6). In the Fresnel mode of Lorentz TEM, neglecting aberrations other than defocus, aperture functions, and sources of incoherence and blurring, the wave function at the detector can be written in the form
where the kernel
the relativistic electron wavelength
Δz is the defocus of the imaging lens, c is the speed of light (~2.99 × 108 m s−1), U is the microscope accelerating voltage, and me is the electron rest mass (~9.11 × 10−31 kg).
The integrals in Eq. (8) were calculated using the convolution theorem. The Fourier transform of (7) is straightforward for the case of periodic boundary conditions in the xy plane. For open-boundary conditions in all dimensions, the wave function in Eq. (7) is nonperiodic, and we use a windowed Fourier transform59. As a window, we took a rectangular function that is more than an order of magnitude larger than the sample, in order to ensure sufficient accuracy of the Fourier transform. The image intensity was then calculated using the expression
TEM sample preparation
TEM samples with well-defined geometries were prepared from a single crystal of B20-type FeGe using a focused ion beam workstation and a lift-out method60.
Magnetic imaging in the TEM
Fresnel defocus imaging and off-axis electron holography were performed in an FEI Titan 60-300 TEM, which was operated at U = 300 kV and is equipped with an electron biprism. The microscope was operated in aberration-corrected Lorentz mode with the sample in magnetic-field-free conditions. The conventional microscope objective lens was used to apply the chosen vertical (out-of-plane) magnetic fields to the sample of between −0.15 and +1.5 T, which were precalibrated using a Hall probe. A liquid-nitrogen-cooled specimen holder (Gatan model 636) was used to vary the specimen temperature between 95 and 380 K. Fresnel defocus images and off-axis electron holograms were recorded using a 4k × 4k Gatan K2 IS direct electron counting detector. The defocus distance was ∣Δz∣ = 400 μm for all images presented in the text.
Multiple off-axis electron holograms, with a 6-s exposure time for each hologram, were recorded to improve the signal-to-noise ratio. The off-axis electron holograms were analyzed using a standard fast Fourier transform algorithm in Holoworks software (Gatan). In order to remove the mean inner potential (MIP) contribution from the total recorded phase shift, phase images were recorded both at low temperature and at room temperature, aligned, and subtracted from each other on the assumption that the MIP contribution is the same and that there are no significant changes in electron-beam-induced specimen charging and dynamical diffraction.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
Parker, E. N. Magnetic neutral sheets in evolving fields. I – General theory. Astrophys. J. 264, 635 (1983).
Cirtain, J. W. et al. Energy release in the solar corona from spatially resolved magnetic braids. Nature 493, 501 (2013).
Eltsov, V. B. et al. Twisted vortex state. Phys. Rev. Lett. 96, 215302 (2006).
Nelson, D. R. Vortex entanglement in high-Tc superconductors. Phys. Rev. Lett. 60, 1973 (1988).
Reichhardt, O. C. J. & Hastings, M. B. Do vortices entangle? Phys. Rev. Lett. 92, 157002 (2004).
Reichhardt, C. Vortices wiggled and dragged. Nat. Phys. 5, 15 (2009).
Bogdanov, A. N. & Yablonskii, D. A. Thermodynamically stable "vortices” in magnetically ordered crystals. The mixed state of magnets. Sov. Phys. JETP 68, 101 (1989).
Back, C. et al. The 2020 skyrmionics roadmap. J. Phys. D Appl. Phys. 53, 363001 (2020).
Bogdanov, A. N. & Panagopoulos, C. Physical foundations and basic properties of magnetic skyrmions. Nat. Rev. Phys. 2, 492 (2020).
Tokura, Y. & Kanazawa, N. Magnetic skyrmion materials. Chem. Rev. 121, 2857 (2021).
Yu, X. Z. et al. Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. Nat. Mater. 10, 106 (2011).
Kovács, A. et al. Mapping the magnetization fine structure of a lattice of Bloch-type skyrmions in an FeGe thin film. Appl. Phys. Lett. 111, 192410 (2017).
Du, H. et al. Interaction of individual skyrmions in a nanostructured cubic chiral magnet. Phys. Rev. Lett. 120, 197203 (2018).
Yu, X. Z. et al. Aggregation and collapse dynamics of skyrmions in a non-equilibrium state. Nat. Phys. 14, 832 (2018).
Yu, X. Z. et al. Variation of skyrmion forms and their stability in MnSi thin plates. Phys. Rev. B 91, 054411 (2015).
Yu, X. Z. et al. Real space observation of a two-dimensional skyrmion crystal. Nature 465, 901 (2010).
Park, H. S. et al. Observation of the magnetic flux and three-dimensional structure of skyrmion lattices by electron holography. Nat. Nanotech. 9, 337 (2014).
Shibata, K. et al. Towards control of the size and helicity of skyrmions in helimagnetic alloys by spin-orbit coupling. Nat. Nanotech. 8, 723 (2013).
Milde, P. et al. Unwinding of a skyrmion lattice by magnetic monopoles. Science 340, 1076 (2013).
Birch, M. T. et al. Real-space imaging of confined magnetic skyrmion tubes. Nat. Commun. 11, 1726 (2020).
Yu, X. Z. et al. Real-space observation of topological defects in extended skyrmion-strings. Nano Lett. 20, 7313 (2020).
Rybakov, F. N., Borisov, A. B. & Bogdanov, A. N. Three-dimensional skyrmion states in thin films of cubic helimagnets. Phys. Rev. B 87, 094424 (2013).
Rybakov, F. N., Borisov, A. B., Blügel, S. & Kiselev, N. S. New type of particlelike state in chiral magnets. Phys. Rev. Lett. 115, 117201 (2015).
Leonov, A., Monchesky, T., Loudon, J. & Bogdanov, A. Three-dimensional chiral skyrmions with attractive interparticle interactions. J. Phys. Condens. Matter 28, 35LT01 (2016).
Hayley, R. O. et al. Real-space observation of skyrmion clusters with mutually orthogonal skyrmion tubes. Phys. Rev. B 100, 104401 (2019).
Dzyaloshinsky, I. A thermodynamic theory of "weak” ferromagnetism of antiferromagnetics. J. Phys. Chem. Solids 4, 241 (1958).
Moriya, T. Anisotropic superexchange interaction and weak ferromagnetism. Phys. Rev. 120, 91 (1960).
Lebech, B., Bernhard, J. & Freltoft, T. Magnetic structures of cubic FeGe studied by small-angle neutron scattering. J. Phys. Condens. Matter 35, 6105 (1989).
Kato, N. I. Reducing focused ion beam damage to transmission electron microscopy images. J. Electron Microsc 53, 451–458 (2004).
Suran, G., Daver, H. & Bruyere, J. C. Magnetic properties of amorphous Fe-Ge films. AIP Conf. Proc. 29, 162 (1976).
Suran, G., Daver, H. & Sztern, J. Spin waves in amorphous FexGe1−x thin films. AIP Conf. Proc. 34, 310 (1976).
Mangin, P., Piecuch, M., Marchal, G. & Janot, C. About the magnetic behaviour of FexMe1−x (Me = Si, Ge, Sn) amorphous alloys. J. Phys. F Met. Phys. 8, 2085 (1978).
Zheng, F. et al. Experimental observation of chiral magnetic bobbers in B20-type FeGe. Nat. Nanotech. 13, 451 (2018).
Liang, D., DeGrave, J. P., Stolt, M. J., Tokura, Y. & Song, J. Current-driven dynamics of skyrmions stabilized in MnSi nanowires revealed by topological Hall effect. Nat. Commun. 6, 8217 (2015).
Stolt, M. J. et al. Selective chemical vapor deposition growth of cubic FeGe nanowires that support stabilized magnetic skyrmions. Nano Lett. 17, 508 (2017).
Olsen, K. & Bohr, J. The generic geometry of helices and their close-packed structures. Theor. Chem. Acc. 125, 207 (2010).
Bohr, J. & Olsen, K. The close-packed triple helix as a possible new structural motif for collagen. Theor. Chem. Acc. 130, 1095 (2011).
Liu, Y., Lake, R. K. & Zang, J. Binding a hopfion in a chiral magnet nanodisk. Phys. Rev. B 98, 174437 (2018).
Voinescu, R., Tai, J.-S. B. & Smalyukh, I. I. Hopf solitons in helical and conical backgrounds of chiral magnetic solids. Phys. Rev. Lett. 125, 057201 (2020).
Kent, N. et al. Creation and observation of Hopfions in magnetic multilayer systems. Nat. Commun. 12, 1562 (2021).
Kassel, C. & Turaev, V. Braid Groups, Graduate Texts in Mathematics (Springer New York, 2008).
Murasugi, K. & Kurpita, B. I. A study of braids (Springer Science, 1999).
Artin, E. Theory of braids. Ann. Math. 48, 101 (1947).
Nayak, C., Simon, S. H., Stern, A., Freedman, M. & Das Sarma, S. Non-Abelian anyons and topological quantum computation. Rev. Mod. Phys. 80, 1083 (2008).
Ye, J. et al. Berry phase theory of the anomalous Hall effect: application to colossal magnetoresistance manganites. Phys. Rev. Lett. 83, 3737 (1999).
Nagaosa, N., Sinova, J., Onoda, S., MacDonald, A. H. & Ong, N. P. Anomalous Hall effect. Rev. Mod. Phys. 82, 1539 (2010).
Seki, S. et al. Propagation dynamics of spin excitations along skyrmion strings. Nat. Commun. 11, 256 (2020).
Xing, X., Zhou, Y. & Braun, H. B. Magnetic skyrmion tubes as nonplanar magnonic waveguides. Phys. Rev. Appl. 13, 034051 (2020).
Asselin, P. & Thiele, A. On the field Lagrangians in micromagnetics. IEEE Trans. Magn. 22, 1876 (1986).
Fredkin, D. & Koehler, T. Numerical micromagnetics by the finite element method. IEEE Trans. Magn. 23, 3385 (1987).
Schrefl, T., Fischer, R., Fidler, J. & Kronmüller, H. Two and three–dimensional calculation of remanence enhancement of rare earth based composite magnets. J. Appl. Phys. 76, 7053 (1994).
Di Fratta, G., Muratov, C. B., Rybakov, F. N. & Slastikov, V. V. Variational principles of micromagnetics revisited. SIAM J. Math. Anal. 52, 3580 (2020).
Druskin, V. Spectrally optimal finite-difference grids in unbounded domains. Schlumberger-Doll Research, Research Note, EMG-002-97-22 (1997).
Muratov, C. B. & Osipov, V. V. Optimal grid-based methods for thin film micromagnetics simulations. J. Comput. Phys. 216, 637 (2006).
Donahue, M. & McMichael, R. Exchange energy representations in computational micromagnetics. Phys. B: Condens. Matter 233, 272–278 (1997).
Rybakov, F. N. & Babaev, E. Excalibur software. http://quantumandclassical.com/excalibur/.
Vansteenkiste, A. et al. The design and verification of MuMax3. AIP Adv. 4, 107133 (2014).
De Graef, M. 2. Lorentz microscopy: theoretical basis and image simulations. Exp. Methods Phys. Sci. 36, 27 (2001).
Kaiser, G. Windowed Fourier Transforms. In: A Friendly Guide to Wavelets. (Birkhäuser Boston, 2011).
Du, H. et al. Edge-mediated skyrmion chain and its collective dynamics in a confined geometry. Nat. Commun. 6, 8504 (2015).
Acknowledgements
The authors are grateful to S. Wang, R. Jiang, and T. Denneulin for asistance with TEM sample preparation, and for funding to the European Research Council under the European Union’s Horizon 2020 Research and Innovation Programme (Grant No. 856538—project “3D MAGiC”; Grant No. 823717—project “ESTEEM3”; Grant No. 766970—project “Q-SORT”), to the Deutsche Forschungsgemeinschaft (Project-ID 405553726-TRR 270; Priority Programme SPP 2137; Project No. 403502830), and to the DARPA TEE program through grant MIPR# HR0011831554. F.N.R. was supported by Swedish Research Council Grants 642-2013-7837, 2016-06122, and 2018-03659, and by the Göran Gustafsson Foundation for Research in Natural Sciences. N.S.K. acknowledges financial support from the Deutsche Forschungsgemeinschaft through SPP 2137 “Skyrmionics” Grant No. KI 2078/1-1.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
F.Z., F.N.R. and N.S.K. conceived the project, and contributed equally to the work. F.Z. and N.S.K. performed TEM experiments and data analysis. F.N.R. performed simulations, with assistance from N.S.K.. All of the authors discussed the results and contributed to the final paper.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Shinichiro Seki and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zheng, F., Rybakov, F.N., Kiselev, N.S. et al. Magnetic skyrmion braids. Nat Commun 12, 5316 (2021). https://doi.org/10.1038/s41467-021-25389-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-021-25389-7
This article is cited by
-
Spacetime magnetic hopfions from internal excitations and braiding of skyrmions
Communications Physics (2024)
-
Spin-wave-driven tornado-like dynamics of three-dimensional topological magnetic textures
Communications Physics (2024)
-
Bending skyrmion strings under two-dimensional thermal gradients
Nature Communications (2024)
-
Distinct skyrmion phases at room temperature in two-dimensional ferromagnet Fe3GaTe2
Nature Communications (2024)
-
Spin disorder control of topological spin texture
Nature Communications (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.