We report the results from the first 5D tomographic diffraction imaging experiment of a complex Ni–Pd/CeO2–ZrO2/Al2O3 catalyst used for methane reforming. This five-dimensional (three spatial, one scattering and one dimension to denote time/imposed state) approach enabled us to track the chemical evolution of many particles across the catalyst bed and relate these changes to the gas environment that the particles experience. Rietveld analysis of some 2 × 106 diffraction patterns allowed us to extract heterogeneities in the catalyst from the Å to the nm and to the μm scale (3D maps corresponding to unit cell lattice parameters, crystallite sizes and phase distribution maps respectively) under different chemical environments. We are able to capture the evolution of the Ni-containing species and gain a more complete insight into the multiple roles of the CeO2-ZrO2 promoters and the reasons behind the partial deactivation of the catalyst during partial oxidation of methane.
Heterogeneous functional materials and devices, like catalytic solids, batteries and fuel cells tend to possess complex structures where the 3D spatial distribution of the various components is rarely uniform1,2,3. Such materials are known to change with time under operating conditions, and in order to gain an insight into the structure–function relationships, it is highly desirable to study them in situ with spatially resolved techniques4,5,6,7. Non-destructive X-ray spectroscopic/scattering techniques are typically employed to study such materials, but it is the brilliant X-rays generated at synchrotrons coupled with state-of-the-art detectors and tomographic data collections that now allow the acquisition of spatially resolved signals from within the interiors of intact objects under operating conditions8,9,10,11. Operando chemical imaging in 5D by synchrotron X-ray Diffraction-Computed Tomography (XRD-CT) could emerge as a game-changing technique for the non-destructive investigation of functional materials in space and time under real process conditions12,13,14. This chemical tomographic technique, along with the complementary pair distribution function computed tomography technique, has been employed in several cases to study catalysts and more recently batteries, under in situ/operando conditions15,16,17,18,19,20,21,22,23,24. Such multi-scale chemical imaging tools hold the potential to revolutionise our understanding of the relationships between structure and functionality in complex, real world, catalytic materials (ie, in particular to better differentiate between reactive and spectator species); information that can help us unravel the mechanisms underpinning catalytic reactions and catalyst deactivation and rationally design improved materials.
The catalytic partial oxidation of methane (POX) is considered a very promising alternative to the highly energy-demanding steam reforming of methane (highly endothermic reaction) to produce synthesis gas (CO and H2) at gas-to-liquids (GTL) industrial plants (Fischer–Tropsch synthesis)25,26,27. The POX reaction is only mildly exothermic and it leads to a H2/CO molar ratio of 2, which is suitable for methanol and Fischer–Tropsch synthesis28. Given the promise of the POX reaction to decrease significantly the energy requirements of GTL plants, it is highly desirable to understand the spatio-temporal physico-chemical changes taking place in the real working catalyst. Such information is crucial in order to rationally design improved catalysts as the chemical (ie, gas composition) and temperature gradients in a reactor (both axially and radially) can have a direct impact on the chemical state of the catalyst29,30,31,32,33,34.
Ni/Al2O3-based catalysts have been the most widely studied POX catalysts mainly due to Ni being a cheap material compared to the noble metals (eg, Pd, Pt, Rh and Ru). However, Ni/Al2O3-based catalysts are usually prone to deactivation with time under POX reaction conditions for a variety of reasons; the most often reported in literature being carbon deposition on active Ni sites (metallic Ni being the active catalyst component), sintering of Ni particles and solid-state reactions involving Ni (eg, the formation of NiAl2O4 in Ni/Al2O3 catalysts)35,36. The CeO2–ZrO2 support promoters can offer improved oxygen storage capacity and redox properties, enhanced metal-support interaction (higher dispersion and stability of the Ni species) and increased catalytic performance at lower temperatures, while small amounts of noble metal (Pd, Pt, Rh and Ru) can enhance the reducibility of the Ni species through a hydrogen spillover mechanism37,38,39,40,41. In this work, we employed the XRD-CT technique to investigate the behaviour of a complex 10 wt.% Ni–0.2 wt.% Pd/10 wt.% CeO2–ZrO2/Al2O3 catalyst under different operating conditions.
Until now, the XRD-CT temporal resolution has been considered its main drawback along with problems associated with large datasets and high volume processing. However, in this work, we implemented a new data collection strategy, the concept of which we introduced previously, in principle applicable to all pencil beam tomographic techniques, where both tomographic axes (ie, translation and rotation) are allowed to move simultaneously42. This new data collection strategy, coupled with the brilliant X-rays produced at the ESRF and the state-of-the-art Pilatus2M CdTe area detector allowed us to collect an XRD-CT dataset in <2 min (ie, 117 s); the data collection rate is at least one order of magnitude faster than that previously reported (see also Supplementary notes 1 and 2). Also, we were able to meet the data handling challenge by analysing millions of diffraction patterns.
Multi-length scale physico-chemical imaging
The in situ experiments were performed at beamlines ID31 and ID15A of the ESRF using the same catalyst (Supplementary Figures 1–3). The first experiment was a five-dimensional (5D) tomographic diffraction imaging experiment. Explicitly, here we mean three spatial dimensions, one diffraction dimension (q-space), and one dimension covering imposed chemical environment. Actually, one could consider this experiment covering more than five dimensions (ie, dependencies of multiple parameters such as phase distribution, crystallite size, and so on, over temperature and time too). The behaviour of a Ni–Pd/CeO2–ZrO2/Al2O3 catalyst was investigated during reduction and re-oxidation (redox experiment). In total, four 3D-XRD-CT datasets (each consisting of 30 XRD-CT datasets) were collected at the following operating conditions: ambient (1), 800 °C under He flow (2), 800 °C under 20% H2/He flow (3) and 800 °C under 20% O2/He flow (4). We present the results from the full Rietveld analysis of these datasets; the phase identification and Rietveld approach taken are described in the methods and Supplementary methods sections. The results represent the analysis of ~2 × 106 diffraction patterns, which is an order magnitude larger compared to that previously reported22,24,43,44,45.
The fresh catalyst is shown to contain crystalline NiO, PdO, CeO2, ZrO2 and Al2O3 (Supplementary Figure 4). Figure 1 presents the results from the XRD-CT dataset collected at the middle of the catalyst bed, the top row showing phase distribution maps of all the crystalline phases present in the catalyst particles. Each phase distribution map corresponds to the (normalised) values of the scale factors for each phase. The main catalyst support material, Al2O3, is seen to be homogeneously distributed over the catalyst particles and clearly defines the border and shape of each particle in the bed.
NiO is seen to be present in all catalyst particles as expected, due to the high Ni loading (10 wt.%), but its spatial distribution is not the same in all particles. We note, in the traditional 2D XRD-CT scan, it is not known whether the bottom, middle or top of each catalyst particle is probed, but as can be seen in Fig. 2, this is resolved in the 3D-XRD-CT; specifically, this figure shows the volume rendering of the scale factors of all phases. We see that NiO is found in higher concentration close to the surface of the catalyst particles. Similarly, PdO is also seen to be mainly present at/near the surface of the catalyst particles (this is clearly visible in Figs. 1 and 2), which is a direct outcome of the preparation method (impregnation) and the low Pd loading (0.2 wt.%). However, it can also be seen that there are regions where there is high concentration of PdO (hotspots in Fig. 1) indicating this phase is not well-dispersed over catalyst particles (see also Supplementary Figures 6–9).
The CeO2 and ZrO2 phases are most interesting. As is clear in Fig. 1, the ZrO2 map shows an egg-shell distribution (only present at/close to the surface of the catalyst particles). The same phenomenon is observed in the ZrO2 phase distribution volume shown in Fig. 2. Although one might expect the same distribution for the CeO2 phase (due to co-impregnation method used for the preparation of the CeO2–ZrO2/Al2O3 support), that is not the case. There is a strong signal generated by the CeO2 phase in the regions where ZrO2 is also present, but it does not diminish closer to the centre of the catalyst particles (as the ZrO2 signal does). As shown in Fig. 2, the observations regarding the CeO2/ZrO2 distributions are in full agreement with the rest of the XRD-CT datasets. The maps presented in the middle row of Fig. 1 correspond to values of the average crystallite size of the CeO2, ZrO2 and NiO phases, while the volume rendering of these data are presented in Fig. 2. It should be noted that the axial and radial gradients of these values (ie, spatial variations of the crystallite size values of each phase) provide the important physico-chemical information.
Characteristic examples are the crystallite size maps and volumes of the CeO2 and ZrO2 phases. The range of the ZrO2 crystallite size is generally seen to be very narrow (ca. 8–12 nm), but in the regions where there are hotspots (areas of high concentration) of ZrO2 (top row of Fig. 1), the average crystallite size increases significantly (middle row of Fig. 1). The same conclusion is reached by comparing the ZrO2 volumes shown in Figs. 2 and 3, as the regions of high ZrO2 concentration correspond to higher crystallite sizes. At first glance, one might think that the case of the CeO2 phase is similar (ie, due to the co-impregnation method). For example, the catalyst particle rich in CeO2 shown in Fig. 1 (approximately in the middle of the CeO2 phase distribution map), also corresponds to highly crystalline CeO2 (ie, highly crystalline compared to other regions of the sample). However, the range of CeO2 crystallite sizes is large in the other catalyst particles. In fact, the values of the CeO2 crystallite sizes are shown to follow an egg-yolk distribution. It can be seen in Fig. 1, that in the core of most particles, where there is no ZrO2, the CeO2 crystallite size varies between 8 and 12 nm, while at/close to the catalyst surface, where there is ZrO2 present, the CeO2 crystallite size is less than half that value (ie, between 4 and 6 nm). This phenomenon is more apparent at the CeO2 crystallite size volumes presented in Fig. 2, where it can be readily seen that the CeO2 crystallite size follows an egg-yolk distribution in all catalyst particles.
The NiO crystallite size distribution shows a similar behaviour to that observed for the ZrO2 phase. Explicitly, the NiO concentration is relatively higher close to the surface of the catalyst particles. In these regions, the average NiO crystallite size is also typically higher compared to the inner core of the catalyst particles (Fig. 1). However, it should be noted that there is a peculiar case too. The catalyst particle in the middle of the catalyst bed in Fig. 1 shows the highest values for NiO crystallite size, but the NiO concentration is not higher compared to the other catalyst particles. It seems that the chemistry of this specific particle may differ from the rest as there is also high concentration of CeO2 (high with respect to the other catalyst particles). This may imply that in this particle there is a different chemical interaction between the various components (NiO, CeO2 and Al2O3). It should be noted though, that no other crystalline phases were identified to be present in this particle.
The maps shown in the bottom row of Fig. 2 correspond to the refined values of lattice parameter a of the CeO2 and ZrO2 unit cells. There are two distinct ranges regarding the values of the ZrO2 lattice parameter a. More specifically, as shown in Figs. 1 and 3, in the regions of the sample where there are high concentrations of ZrO2 (hotspots in Fig. 1 and regions of high intensity in Fig. 2), the values of the lattice parameter a are low (<3.6 Å). In all other regions, where CeO2 is present, the ZrO2 lattice parameter a corresponds to higher values (>3.62 Å). This implies that there are actually two different ZrO2 phases present in the sample: (1) a high-purity ZrO2 present in areas of high concentration of ZrO2 and (2) a Zr-rich CexZryO2 phase (Ce incorporation in the ZrO2 unit cell leads to larger unit cell)46,47,48,49. Interestingly though, two distinct CeO2 crystalline species seem to be present in the catalyst particles too. As shown in Figs. 1 and 3, the CeO2 lattice parameter a near the centre of the catalyst particles is notably higher (5.38–5.40 Å) compared to closer to the surface of the catalyst (5.34–5.36 Å), where ZrO2 is present too. This implies that there is incorporation of a Zr4+ substituent onto a Ce4+ site in the CeO2 unit cell in the regions where both CeO2 and ZrO2 are present leading to Ce-rich CexZryO2 phase (smaller unit cell compared to pure CeO2)37,38,39,40. Summarising the CeO2–ZrO2 results derived from the Rietveld analysis of the 3D-XRD-CT data of the fresh catalyst, it can be concluded that there are four distinct crystalline CeO2–ZrO2 species present in the catalyst (see also Supplementary Figure 10):
Small crystallites of a Ce-rich CexZryO2 (x»y) phase near the surface of the catalyst particles;
Larger crystallites of a higher purity CeO2 phase closer to the core of the catalyst particles;
Small crystallites of a Zr-rich CexZryO2 (x«y) phase near the catalyst surface;
Larger crystallites of a higher purity ZrO2 phase where there is high concentration of ZrO2 (near the surface of the catalyst particles—hotspots of this material).
Catalyst activation and re-oxidation
After the 3D-XRD-CT measurement was performed at ambient conditions, the temperature of the system was increased to 800 °C (temperature ramp rate of 20 °C per min) under the flow of He (volumetric flow rate of 100 ml min−1). The catalyst remained at 800 °C under He flow (volumetric flow rate of 100 ml min−1) for 1 h while collecting a 3D-XRD-CT scan. The gas mixture was then switched to a 20% H2/He (total flow rate of 100 ml min−1). Another 3D-XRD-CT measurement was then performed under these reducing conditions in an attempt to capture the state of the activated catalyst. Finally, the gas mixture was switched to 20% O2/He (total flow rate of 100 ml min−1) and a last 3D-XRD-CT scan was performed (catalyst re-oxidation experiment).
The main difference in the state of the catalyst at 800 °C under He flow compared to the room temperature 3D-XRD-CT data is related to the Ni-containing phases. Specifically, we observe the presence of the undesired NiAl2O4 phase (Supplementary Figures 11 and 12). It has been previously reported in literature that crystalline NiAl2O4 can be observed in Ni/Al2O3 catalysts calcined at temperatures above 600 °C50. It is perhaps not surprising then that the NiAl2O4 phase is seen to be present in the catalyst at 800 °C51. This indicates that a reducing chemical environment (eg, H2) is essential in order to avoid the NiO to NiAl2O4 transition and reduce the NiO to the desired, active metallic Ni phase, as the formation and growth of the NiAl2O4 phase is a temperature-driven phenomenon taking place even under inert chemical environment (He flow). However, the phase distribution maps of NiO, NiAl2O4 and CexZryO2 revealed that NiO is mainly present near the surface of the catalyst particles (where the most of the CexZryO2 phases are present) while NiAl2O4 is closer to their core. This provides direct evidence that one of the roles of the CexZryO2 phases is to stabilise the NiO phase and suppress the formation of the undesired NiAl2O4 phase (Supplementary Figure 12).
The results from the Rietveld analysis of the 3D-XRD-CT data collected during reduction (catalyst activation) are presented in Fig. 3. In contrast to the results obtained under He flow, there are significant differences between the 30 XRD-CT ‘slices’ consisting this 3D-XRD-CT dataset. This is clearly shown at the right side of Fig. 4 where the summed diffraction patterns from all 30 XRD-CT datasets collected during the 3D-XRD-CT measurement under reducing conditions are presented. The diffraction peak that appears at ca. Q = 3.04 Å−1 corresponds to the metallic Ni phase (reflection (111)). The crystalline metallic Ni phase is seen to form quickly and is present even in the first XRD-CT data collected under H2 flow (bottom of the sample volume probed—XRD-CT scan 1). However, the continuous growth of the Ni diffraction signal and decrease of the NiO and NiAl2O4 peaks (ca. Q = 3 Å−1 and Q = 2.55–2.65 Å−1, respectively) imply that NiO and NiAl2O4 were still present during the acquisition of this 3D-XRD-CT measurement (ie, in several XRD-CT scans). In order to decouple these phenomena, we performed another diffraction experiment where we show that the NiO/NiAl2O4/Ni concentration gradients shown in Fig. 4 are a purely temporal phenomenon (Supplementary Figures 13–15 and accompanying text). The retardation in the full reduction of the Ni–O and Ni–Al–O species could be due to the formation/presence of water produced from the formation of metallic Ni closer to the reactor inlet19,23.
The phase distribution volumes shown in Fig. 3 clearly demonstrate this Ni concentration gradient along the length of the catalyst bed. Similarly, the decrease of the concentration of the NiO and NiAl2O4 phases along the catalyst bed can also be readily observed. A closer inspection of the results also reveals that the NiAl2O4 phase, which is known to be more difficult to reduce compared to the NiO phase, remains present at positions of the catalyst bed where the NiO diffraction signal has already diminished25,35. Of course, as also shown in the 30 XRD-CT-summed diffraction patterns presented in Fig. 4, only metallic Ni is observed near the top of the catalyst bed.
The CexZryO2 mixed oxides seem to be the predominant phases compared to the respective higher purity CeO2 and ZrO2 phases. This is implied from the CeO2 phase distribution volume shown in Fig. 3 where CeO2 is seen to be mainly present near the surface of the catalyst particles, similar to the ZrO2 (ie, Zr-rich CexZryO2) phase distribution volume (egg-shell distribution). It should be emphasised that the most important result obtained from this 3D-XRD-CT dataset is related to the correlation between the Ni and the CexZryO2 phase distribution maps. Specifically, as shown on the right side of Fig. 4, the metallic Ni phase is first formed in the regions (initially following only an egg-shell distribution before being present everywhere in all catalyst particles) where the CexZryO2 phases are present. This result provides direct evidence that the most important role of the CexZryO2 promoters is to enhance the reducibility of the NiO and the formation of the active catalyst component, the metallic Ni phase.
Finally, it should be mentioned that metallic Pd is observed at the 3D-XRD-CT data collected under reducing conditions. The phase distribution volume of Pd shown in Fig. 3 is very well correlated with the PdO distribution presented previously in Fig. 2. It is also important to note that the metallic Pd peak (reflection (111)) is observed at larger Q values than expected (ca. Q = 2.85 Å−1) corresponding to a smaller unit cell than a pure Pd one (Supplementary Figure 17). This result implies that Ni is incorporated in the Pd unit cell (shift of diffraction peak to larger Q values) and that Pd exists as a NixPdy phase (alloy) rather than a high-purity Pd phase; the formation of NixPdy alloys has been previously reported in other catalytic systems52,53,54,55.
The last 3D-XRD-CT dataset was collected under the flow of 20% O2/He. The re-oxidation process of metallic Ni to NiO is really fast as the metallic Ni peak is absent in all 30 XRD-CT datasets and only the NiO and NiAl2O4 phases can be observed (Supplementary Figure 16). The most important results from this re-oxidation step are presented in Fig. 5 where the maps corresponding to the crystallite size of NiO, as obtained from the Rietveld analysis of the XRD-CT data collected at the bottom, middle and top of the sample under He and under 20% O2/He flow, are shown. It can be readily seen that the re-oxidation step at 800 °C led to a substantial increase in the crystallite size of the NiO phase, implying that sintering of the NiO species took place. In many regions of the sample, the NiO crystallite size more than doubled from ca. 5–15 nm to ca. 20–35 nm. The increase of the NiO crystallite size was not prevented even in the regions where the various CeO2/ZrO2/CexZryO2 promoters are present indicating that careful consideration must be given to the catalyst pre-treatment before switching to real reaction conditions.
The evolution of the Ni-containing crystalline phases during this 5D tomographic diffraction imaging redox experiment is summarised in Fig. 6 where the phase distribution volumes of NiO, NiAl2O4 and Ni under the various operating conditions are displayed (panel a). As discussed previously, NiO is the only observed crystalline phase in the fresh catalyst, while NiAl2O4 is the predominant Ni-containing phase in the 3D-XRD-CT dataset collected at 800 °C under He flow. Under these conditions, the NiO follows mainly an egg-shell distribution, similar to the CexZryO2 phase (where y > x), while the NiAl2O4 phase is mainly present closer to the core of the catalyst particles. This information provides direct evidence that the CexZryO2 suppresses/delays the formation of the undesired NiAl2O4 phase.
As discussed previously, under reducing conditions, a Ni chemical gradient is observed along the length of the bed, which is a time effect (ie, delay in the full reduction of NiO and NiAl2O4). This is also illustrated in panel b where it is shown that first the NiO is reduced and then the NiAl2O4 phase (probing from bottom to top of the bed). A similar time effect is shown during the re-oxidation experiment as the top of the bed (last scan) contains less NiO compared to the bottom of the bed (first scan) indicating that the NiO to NiAl2O4 transition can also be captured.
Partial oxidation of methane
The last experiment was an operando XRD-CT experiment of the same catalyst during the partial oxidation of methane. The same protocol was used for the pre-treatment of the catalyst as in the redox experiment. Specifically, the temperature of the system was increased under the flow of He up to 800 °C (temperature ramp rate of 20 °C per min) and then the catalyst was activated under the flow of 20% H2/He (total flow rate of 100 ml min−1) to form the metallic Ni phase. The catalyst bed was then exposed to a POX reaction mixture (ie, 90 ml min−1 of pure He, 12 ml min−1 of pure CH4 and 3 ml min−1 of pure O2—CH4/O2 molar ratio of 4:1), which was kept constant for the duration of the experiment and seven XRD-CT scans were collected in total.
In Fig. 7, the phase distribution maps of certain crystalline phases of interest, as obtained from the Rietveld analysis of the XRD-CT data collected at 800 °C under POX reaction conditions, are presented. These phase distribution maps correspond to the values of the scale factors for each phase normalised with respect to the maximum values. NiO and NiAl2O4 remain only in traces for the duration of the experiment, while Al2O3 is not changing; for these reasons, these maps are not shown here and emphasis is given on the active catalyst components. More importantly, the crystalline Ni phase is seen to be very stable for the duration of the POX experiment (ca. 3 h). We also note there is no evidence for formation of crystalline Ni carbide phases (eg, Ni3C or NiC)56.
The typical reaction mixture used to test the performance of POX catalysts is a gas mixture where the CH4/O2 molar ratio is 2:1 (stoichiometric ratio for the POX reaction)57,58,59. Here, a higher CH4/O2 molar ratio of 4:1 was used in an attempt to force the catalyst to deactivate faster and capture the corresponding solid-state changes. As it is shown in Fig. 7, the Ni remains in a metallic form for the duration of the experiment (ca. 3 h), which is an interesting result especially when one considers the methane-rich operating conditions. It should also be stated that no other crystalline Ni-containing phases were observed in the XRD-CT data beyond the trace amounts of NiO and NiAl2O4 mentioned previously. However, as is shown in the bottom part of Fig. 7, sintering of metallic Ni is seen to take place as a function of time during the POX experiment.
Figure 7 also tells us that the diffraction signal from both CexZryO2 phases is seen to decrease with time under reaction conditions although one may argue that the decrease is not very significant (ca. 10 % decrease after 3 h). The Pd phase (more precisely, the NixPdy alloy as discussed previously) is also seen to decrease as a function of time under the POX reaction conditions. It should be noted though that no other crystalline Pd-containing species were observed in the XRD-CT data collected during the POX experiment. The mass spectrometry data acquired during the POX experiment are presented in Supplementary Figure 18, serve to prove that the catalyst was captured in its active state during the POX reaction. No apparent deactivation of the catalyst was observed during the experiment, but as it is shown in Fig. 7, upon switching to the POX reaction mixture a new phase formed, which was identified as graphite (Supplementary Figure 17)55. From the phase distribution maps presented in Fig. 7, it can be clearly seen that the Ni and graphite maps are directly correlated. Specifically, the results suggest that the coke deposition initially takes place at the regions rich in Ni, which is the active catalyst component for the POX reaction. This graphite phase is seen to continuously grow during the POX reaction experiment. It is also implied that particles that are rich in CexZr1−xO2 are less prone to graphite formation; in these particles, the CexZr1−xO2 forms a protective layer near the surface of the catalyst particles. As mentioned previously, the POX reaction experiment lasted for ~3 h and it can be seen that the diffraction signal from this phase doubled during this time period (Fig. 7). It is reasonable to expect that the growth of graphite at the catalyst particles will probably influence the long-term performance of the catalyst (ie, by blocking the active Ni/Pd sites). This suggestion seems also to be consistent with laboratory catalytic activity measurements we have performed following the same catalyst pre-treatment and activation protocol (Supplementary Figures 19 and 20). Specifically, the catalyst showed high performance when it was exposed to POX reaction conditions (the CH4/O2 molar ratio of 2:1), leading to 84% CH4 conversion and almost 100% H2 yield. However, exposing the catalyst to the CH4/O2 molar ratio equal to 4:1 for 3 h, partially deactivated the catalyst as it did not regain its initial performance when the reaction mixture was switched back to 2:1. As shown by the in situ XRD-CT data, this is highly likely to be due to the graphite formation (see also Supplementary Figures 21–26).
It is well known that time-resolved in situ or operando X-ray spectroscopic or scattering studies provide information on evolving structure activity relationships in functional materials with researchers in the field of heterogeneous catalytic materials shown historically to be keen to exploit their potential60. In more recent times, traditional single-point measurements have been superseded (in terms of the information they provide) by X-ray chemical imaging studies and these have been shown to yield far greater insight into the structure of single particles or else a handful of particles in a cross-section1,2,5,11,17,20,21. Despite these important advantages, there will always be doubts as to whether a single particle/group of particles are truly representative of their ilk in terms of composition and/or behaviour (ie, in a reactor environment). The biggest challenge in this regard is to be able to follow changes in the catalyst particle structure as a function of their location in a reactor. It is well known that catalyst particles experience variation in reactant/product composition both radially and longitudinally, thereby rendering attempts to correlate structure–function relationships in a reactor difficult and in some cases impossible. The 3D chemical imaging results presented herein obtained in real time and under operando conditions therefore represent significant step in attempting to extract more meaningful correlations between structure and function in catalytic and other functional materials.
Specific to this study, we have shown how the Rietveld analysis of the reconstructed XRD-CT data allowed us to differentiate between four different CexZryO2 crystalline species present in the sample. This information could only be obtained by collecting the 3D-XRD-CT dataset and performing the Rietveld analysis. It should be emphasised that the analysis of the reconstructed data (>2 × 106 diffraction patterns) although very challenging, is now possible on reasonable timescales so as to obtain unprecedented physico-chemical information regarding the state of the catalyst under different operating conditions. We were able to create, for the first time, 3D maps corresponding to phase distributions, crystallite sizes and unit cell lattice parameters, demonstrating the multi-length scale information that can be obtained from performing such an experiment and the corresponding data analysis. As such, we were able to effectively track the evolution of the crystalline Ni-containing species under different chemical environments (He, H2/He, O2/He, CH4/O2). NiO was the only crystalline Ni-containing phase present in the fresh catalyst and it was shown that a reducing environment is necessary in order to avoid the formation of the undesired NiAl2O4 phase at high temperatures. It was shown that the role of the CexZryO2 promoters is to suppress this conversion and enhance the reduction of the Ni oxides to the catalytically active metallic Ni. It should be emphasised that this chemical information could have not been obtained with any conventional technique but only from the spatially resolved diffraction signals present in an XRD-CT dataset.
The reduction process was seen to be significantly slower compared to the re-oxidation. Specifically, significant Ni/NiO/NiAl2O4 concentration gradients were observed along the catalyst bed during reduction but not during re-oxidation. This phenomenon was attributed to the water formation during the reduction of the NiO/NiAl2O4 species to metallic Ni. It was also shown that the re-oxidation of the catalyst at 800 °C under 20% O2/He flow can have a strong impact on the NiO crystallite size. Metallic Ni was seen to be the main crystalline Ni-containing phase of the catalyst under POX reaction conditions, but sintering of the Ni crystallites took place as a function of time under reaction conditions. More importantly though, crystalline graphite was seen to form and continuously grow under POX reaction conditions which, as the laboratory catalytic activity data collected under the same conditions indicate, caused the partial deactivation of the catalyst.
We have shown that it is possible to track the chemical evolution of many particles across a catalyst bed and relate these changes and variations to the non-uniform gas composition the catalyst particles experience. The insights and understanding gained from this in situ study can be used to rationally design improved methane-reforming catalysts. With the advancements in synchrotron brightness, detector performance, sample environment (new reactor cells) and data analysis (Rietveld analysis of XRD-CT data), multi-dimensional chemical imaging techniques are bound to become increasingly easier to perform and one can readily foresee that they will replace conventional in situ XRD and X-ray imaging as the preferred method for characterising functional materials and devices (eg, catalytic reactors, batteries and fuel cells).
The 10 wt.% Ni–0.2 wt.% Pd/10 wt.% CeO2–ZrO2/Al2O3 catalyst was prepared by sequential impregnation method. The CeO2–ZrO2/Al2O3 support was prepared by the co-impregnation method61,62. The microspherical (γ + δ)-Al2O3 with granules size of ~500 μm was used. Approximately 500 µm of (γ + δ)-Al2O3 was impregnated by aqueous solution of salts (cerium nitrate Ce(NO)3 · 6H2O and oxychloride of zirconium ZrOCl · 8H2O) at the required ratio. The CeO2–ZrO2/Al2O3 was dried at 120 °C for 6 h and calcined under air at 850 °C for 6 h with a heating rate of 2 °C per min. The 10 wt.% CeO2–ZrO2/Al2O3 support was impregnated by aqueous solution of nickel nitrate salt Ni(NO3)2 · 6H2O of the appropriate concentration. Then, Ni/CeO2–ZrO2/Al2O3 was dried at 120 °C for 6 h and calcined in air at 500 °C for 4 h with a heating rate of 2 °C per min. The Ni/CeO2–ZrO2/Al2O3 was impregnated by aqueous solution of palladium nitrate Pd(NO3)2 salt of the appropriate concentration. The catalyst were then dried at 120 °C for 6 h and calcined in air at 500 °C for 4 h with a heating rate of 2 °C per min. The catalyst samples used in this study were kindly provided by the Boreskov Institute of Catalysis (BIC).
The three catalytic reactors investigated in this study consisted of 10 wt.%Ni–0.2 wt. Pd/10 wt.% CeO2–ZrO2/Al2O3 catalysts (ie, quartz capillary fixed bed reactors supported by glass wool); the catalyst loading was 35 mg for the operando experiment (4 mm outer diameter quartz capillary for the operando experiment, 2 mm for the 5D tomographic diffraction imaging experiment). In each case, the reactor was mounted into a gas delivery stub, itself mounted to a standard goniometer (to enable alignment). The goniometer was fixed to a rotation stage set upon a translation stage to facilitate the movements required for the CT measurement. At ID31, heating was achieved by virtue of two Cyberstar hot air blowers heating each side of the catalytic reactor while at ID15A a furnace designed for CT experiments was used. Temperature calibration was performed before all experiments using a thermocouple by measuring the temperature at the catalyst bed. During the operando XRD-CT measurements, the outflow gasses were monitored by mass spectrometry using an Ecosys portable mass spectrometer. The mass spec line was inserted inside the capillary from the top. The mass spec capillary is dragging with a constant flow rate of 20 ml min−1.
5D tomographic diffraction imaging measurements at ID31, ESRF
XRD-CT measurements were made at beamline station ID31 of the ESRF using a 70 keV monochromatic X-ray beam focused to have a spot size of 25 × 25 μm. 2D powder diffraction patterns were collected also using the state-of-the-art Pilatus3 X CdTe 2 M hybrid photon counting area detector. The total acquisition time per point was 15 ms (exposure time of 11 ms and readout time of 4 ms). Four 3D-XRD-CT scans of the Ni–Pd/CeO2–ZrO2/Al2O3 catalyst were acquired at different operating conditions: (1) at room temperature, (2) at 800 °C under He flow, (3) at 800 °C under 20% H2/He flow (reduction step) and (4) at 800 °C under 20% O2/He flow (re-oxidation step). Each 3D-XRD-CT scan composed of 30 XRD-CT scans, each one collected at a different vertical position (ie, 25 μm step size along the catalyst bed). Each XRD-CT scan lasted ~2 min. The tomographic measurements were made with 100 translation steps (translation step size of 25 μm) covering 0–180° angular range, in steps of 2.5° (ie, 72 line scans). The detector calibration was performed using a CeO2 NIST standard. Every 2D diffraction image was converted to a 1D powder diffraction pattern after applying an appropriate filter (ie, 1% trimmed mean filter) to remove outliers using in-house developed MATLAB scripts63. The final XRD-CT images (ie, reconstructed data volume) were reconstructed using the filtered back projection algorithm.
In situ XRD mapping and XRD-CT measurements at ID15A, ESRF
XRD mapping and XRD-CT measurements were made at beamline station ID15A of the ESRF using a 91 keV monochromatic X-ray beam focused to have a spot size of 40 × 20 μm (horizontal × vertical). 2D powder diffraction patterns were also collected also using the state-of-the-art Pilatus3 X CdTe 2 M hybrid photon counting area detector. The total acquisition time per point was 10 ms. Initially, an XRD-CT scan was performed at the middle of the catalyst bed at ambient conditions. The XRD-CT scan was made with 151 translation steps (translation step size of 40 μm) covering 0–180° angular range, in steps of 1.44° (ie, 126 line scans). Calibration and processing (5% trimmed mean filter) was carried as described in the previous section (5D imaging measurements at ID31, ESRF) with X-ray detection again using the Pilatus3 X detector. The temperature of the system was increased under the flow of pure He (30 ml min−1) up to 800 °C with a ramp rate of 20 °C per min. An XRD-CT scan was collected and then the inlet gas mixture was switched to 20% H2/He (50 ml min−1). Eight successive XRD maps were collected covering the whole bed (151 translation steps and 12 z positions, each 0.5 mm apart). Each XRD map lasted ~5 min. Finally, a 3D-XRD-CT scan was collected after the XRD maps. The 3D-XRD-CT scan composed of 10 XRD-CT scans, each one collected at a different vertical position (ie, 80 μm step size along the catalyst bed).
Operando XRD-CT measurements at ID31, ESRF
XRD-CT measurements were made at beamline station ID31 of the ESRF using a 70 keV monochromatic X-ray beam focused to have a spot size of 20 × 20 μm. Here, the total acquisition time per point was 20 ms. Tomographic measurements were made with 225 translation steps (translation step size of 20 μm) covering 0–180° angular range, in steps of 1.125° (ie, 160 line scans). Calibration and processing was carried as described in the section above (5D imaging measurements at ID31, ESRF) with X-ray detection again using the Pilatus3 X detector. The temperature of the reactor was then increased to 800 °C with a ramp rate of 20 °C per min under the flow of He (ie, 30 ml min−1). The inlet gas was then switched to a 20% H2/He gas mixture (total flow rate of 100 ml min−1). Finally, the catalyst bed was exposed to a POX reaction mixture (ie, 90 ml min−1 of He, 12 ml min−1 of CH4 and 3 ml min−1 of O2 having a CH4/O2 molar ratio of 4:1), which was kept constant for the duration of the experiment.
Rietveld analysis of the XRD-CT data
Quantitative Rietveld refinement was performed using the reconstructed diffraction patterns using the TOPAS software, on a voxel by voxel basis64. The results from the refinements were imported into MALTAB in order to create the various figures presented in this work (eg, phase distribution maps based on the scale factors or weight percentages, lattice parameters, and so on). Unless stated otherwise, the Rietveld analysis of the XRD-CT data presented in this work was based on the intensity of the scale factors and should be treated as a semi-quantitative analysis. Rietveld analysis was performed using the summed diffraction pattern of each XRD-CT dataset prior to the Rietveld analysis of the XRD-CT data in order to have a good starting model before performing the batch Rietveld analysis.
Copies of raw radially integrated XRD-CT data can be found at http://tiny.cc/NCOMMS18-12413A. All data are available from the corresponding authors on reasonable request.
Beale, A. M., Jacques, S. D. & Weckhuysen, B. M. Chemical imaging of catalytic solids with synchrotron radiation. Chem. Soc. Rev. 39, 4656–4672 (2010).
Grunwaldt, J. D. & Schroer, C. G. Hard and soft X-ray microscopy and tomography in catalysis: bridging the different time and length scales. Chem. Soc. Rev. 39, 4741–4753 (2010).
Nelson Weker, J. & Toney, M. F. Emerging in situ and operando nanoscale X-ray imaging techniques for energy storage materials. Adv. Funct. Mater. 25, 1622–1637 (2015).
Buurmans, I. L. C. & Weckhuysen, B. M. Heterogeneities of individual catalyst particles in space and time as monitored by spectroscopy. Nat. Chem. 4, 873 (2012).
Grunwaldt, J.-D., Wagner, J. B. & Dunin-Borkowski, R. E. Imaging catalysts at work: a hierarchical approach from the macro- to the meso- and nano-scale. ChemCatChem 5, 62–80 (2013).
Grey, C. P. & Tarascon, J. M. Sustainability and in situ monitoring in battery development. Nat. Mater. 16, 45 (2016).
Wang, H. & Wang, F. In situ, operando measurements of rechargeable batteries. Curr. Opin. Chem. Eng. 13, 170–178 (2016).
Saida, T. et al. 4D visualization of a cathode catalyst layer in a polymer electrolyte fuel cell by 3D laminography–XAFS. Angew. Chem. Int. Ed. Engl. 51, 10311–10314 (2012).
Cocco, A. P. et al. Three-dimensional microstructural imaging methods for energy materials. Phys. Chem. Chem. Phys. 15, 16377–16407 (2013).
Harks, P. P. R. M. L., Mulder, F. M. & Notten, P. H. L. In situ methods for Li-ion battery research: a review of recent developments. J. Power Sources 288, 92–105 (2015).
Matsui, H. et al. Operando 3D visualization of migration and degradation of a platinum cathode catalyst in a polymer electrolyte fuel cell. Angew. Chem. Int. Ed. Engl. 56, 9371–9375 (2017).
Harding, G. X-ray diffraction computed tomography. Med. Phys. 14, 515 (1987).
Bleuet, P. et al. Probing the structure of heterogeneous diluted materials by diffraction tomography. Nat. Mater. 7, 468–472 (2008).
Beale, A. M., Jacques, S. D. M., Gibson, E. K. & Di Michiel, M. Progress towards five dimensional diffraction imaging of functional materials under process conditions. Coord. Chem. Rev. 277–278, 208–223 (2014).
O’Brien, M. G. et al. Active phase evolution in single Ni/Al2O3 methanation catalyst bodies studied in real time using combined μ-XRD-CT and μ-absorption-CT. Chem. Sci. 3, 509 (2012).
Jacques, S. D. et al. Pair distribution function computed tomography. Nat. Commun. 4, 2536 (2013).
Price, S. W. T. et al. In situ microfocus chemical computed tomography of the composition of a single catalyst particle during hydrogenation of nitrobenzene in the liquid phase. Angew. Chem. Int. Ed. Engl. 127, 10024–10027 (2015).
Vamvakeros, A. et al. Real time chemical imaging of a working catalytic membrane reactor during oxidative coupling of methane. Chem. Commun. 51, 12752–12755 (2015).
Senecal, P. et al. Real-time scattering-contrast imaging of a supported cobalt-based catalyst body during activation and Fischer–Tropsch synthesis revealing spatial dependence of particle size and phase on catalytic properties. ACS Catal. 7, 2284–2293 (2017).
Sheppard, T. L. et al. In situ multimodal 3D chemical imaging of a hierarchically structured Core@Shell catalyst. J. Am. Chem. Soc. 139, 7855–7863 (2017).
Price, S. W. T. et al. Chemical imaging of Fischer–Tropsch catalysts under operating conditions. Sci. Adv. 3, e1602838 (2017).
Sottmann, J. et al. Chemical structures of specific sodium ion battery components determined by operando pair distribution function and X-ray diffraction computed tomography. Angew. Chem. Int. Ed. Engl. 56, 11385–11389 (2017).
Beale, A. M. et al. X-ray physico-chemical imaging during activation of cobalt-based Fischer–Tropsch synthesis catalysts. Philos. Trans. R. Soc. A 376 (2018).
Matras, D. et al. Real-time operando diffraction imaging of La–Sr/CaO during the oxidative coupling of methane. J. Phys. Chem. C 122, 2221–2230 (2018).
Christian Enger, B., Lødeng, R. & Holmen, A. A review of catalytic partial oxidation of methane to synthesis gas with emphasis on reaction mechanisms over transition metal catalysts. Appl. Catal. A-Gen. 346, 1–27 (2008).
Sousa-Aguiar, E. F., Noronha, F. B. & Faro, J. A. The main catalytic challenges in GTL (gas-to-liquids) processes. Catal. Sci. Technol. 1, 698–713 (2011).
Sengodan, S. et al. Advances in reforming and partial oxidation of hydrocarbons for hydrogen production and fuel cell applications. Renew. Sust. Energ. Rev. 82, 761–780 (2018).
Veser, G. Multiscale process intensification for catalytic partial oxidation of methane: from nanostructured catalysts to integrated reactor concepts. Catal. Today 157, 24–32 (2010).
Horn, R., Williams, K. A., Degenstein, N. J. & Schmidt, L. D. Syngas by catalytic partial oxidation of methane on rhodium: mechanistic conclusions from spatially resolved measurements and numerical simulations. J. Catal. 242, 92–102 (2006).
Kimmerle, B. et al. Visualizing a catalyst at work during the ignition of the catalytic partial oxidation of methane. J. Phys. Chem. C 113, 3037–3040 (2009).
Grunwaldt, J.-D. et al. Catalysts at work: from integral to spatially resolved X-ray absorption spectroscopy. Catal. Today 145, 267–278 (2009).
Korup, O. et al. Catalytic partial oxidation of methane on platinum investigated by spatial reactor profiles, spatially resolved spectroscopy, and microkinetic modeling. J. Catal. 297, 1–16 (2013).
Hettel, M., Diehm, C., Torkashvand, B. & Deutschmann, O. Critical evaluation of in situ probe techniques for catalytic honeycomb monoliths. Catal. Today 216, 2–10 (2013).
Morgan, K. et al. Evolution and enabling capabilities of spatially resolved techniques for the characterization of heterogeneously catalyzed reactions. ACS Catal. 6, 1356–1381 (2016).
Dissanayake, D., Rosynek, M. P., Kharas, K. C. C. & Lunsford, J. H. Partial oxidation of methane to carbon monoxide and hydrogen over a Ni/Al2O3 catalyst. J. Catal. 132, 117–127 (1991).
Nahar, G. & Dupont, V. Hydrogen production from simple alkanes and oxygenated hydrocarbons over ceria–zirconia supported catalysts: review. Renew. Sust. Energ. Rev. 32, 777–796 (2014).
Choudhary, V. R., Prabhakar, B. & Rajput, A. M. Beneficial effects of noble metal addition to Ni/Al2O3 catalyst for oxidative methane-to-syngas conversion. J. Catal. 157, 752–754 (1995).
Dong, W.-S., Jun, K.-W., Roh, H.-S., Liu, Z.-W. & Park, S.-E. Comparative study on partial oxidation of methane over Ni/ZrO2, Ni/CeO2 and Ni/Ce–ZrO2 catalysts. Catal. Lett. 78, 215–222 (2002).
Li, D., Nakagawa, Y. & Tomishige, K. Methane reforming to synthesis gas over Ni catalysts modified with noble metals. Appl. Catal. A-Gen. 408, 1–24 (2011).
De, S., Zhang, J., Luque, R. & Yan, N. Ni-based bimetallic heterogeneous catalysts for energy and environmental applications. Energy Environ. Sci. 9, 3314–3347 (2016).
Montini, T., Melchionna, M., Monai, M. & Fornasiero, P. Fundamentals and catalytic applications of CeO2-based materials. Chem. Rev. 116, 5987–6041 (2016).
Vamvakeros, A. et al. Interlaced X-ray diffraction computed tomography. J. Appl. Crystallogr. 49, 485–496 (2016).
Wragg, D. S., O’Brien, M. G., Di Michiel, M. & Lonstad-Bleken, F. Rietveld analysis of computed tomography and its application to methanol to olefin reactor beds. J. Appl. Crystallogr. 48, 1719–1728 (2015).
Frølich, S. & Birkedal, H. MultiRef: software platform for Rietveld refinement of multiple powder diffractograms from in situ, scanning or diffraction tomography experiments. J. Appl. Crystallogr. 48, 2019–2025 (2015).
Frølich, S. et al. Diffraction tomography and Rietveld refinement of a hydroxyapatite bone phantom. J. Appl. Crystallogr. 49, 103–109 (2016).
Alifanti, M. et al. Characterization of CeO2–ZrO2 mixed oxides. Comparison of the citrate and sol−gel preparation methods. Chem. Mater. 15, 395–403 (2003).
Di Monte, R. & Kašpar, J. Nanostructured CeO2-ZrO2 mixed oxides. J. Mater. Chem. 15, 633–648 (2005).
Zhang, F. et al. Phases in ceria-zirconia binary oxide (1−x)CeO2–xZrO2 nanoparticles: the effect of particle size. J. Am. Ceram. Soc. 89, 1028–1036 (2006).
Fu, Y.-P., Hu, S.-H. & Liu, B.-L. Structure characterization and mechanical properties of CeO2–ZrO2 solid solution system. Ceram. Int. 35, 3005–3011 (2009).
Li, G., Hu, L. & Hill, J. M. Comparison of reducibility and stability of alumina-supported Ni catalysts prepared by impregnation and co-precipitation. Appl. Catal. A-Gen. 301, 16–24 (2006).
Boukha, Z. et al. Synthesis, characterisation and performance evaluation of spinel-derived Ni/Al2O3 catalysts for various methane reforming reactions. Appl. Catal. B-Environ. 158–159, 190–201 (2014).
Mukainakano, Y., Yoshida, K., Okumura, K., Kunimori, K. & Tomishige, K. Catalytic performance and QXAFS analysis of Ni catalysts modified with Pd for oxidative steam reforming of methane. Catal. Today 132, 101–108 (2008).
Feng, L. et al. Pd–Ni alloy nanoparticles as effective catalysts for Miyaura–Heck coupling reactions. J. Phys. Chem. C 119, 11511–11515 (2015).
Martínez de Yuso, A. et al. Facile and rapid one-pot microwave-assisted synthesis of Pd-Ni magnetic nanoalloys confined in mesoporous carbons. J. Nanopart. Res. 18, 380 (2016).
Bayat, N., Rezaei, M. & Meshkani, F. Hydrogen and carbon nanofibers synthesis by methane decomposition over Ni–Pd/Al2O3 catalyst. Int. J. Hydrogen Energy 41, 5494–5503 (2016).
Bayer, B. C. et al. In situ observations of phase transitions in metastable nickel (carbide)/carbon nanocomposites. J. Phys. Chem. C 120, 22571–22584 (2016).
Liu, Z. W., Roh, H. S., Jun, K. W., Park, S. E. & Song, T. Y. Partial oxidation of methane over Ni/Ce-ZrO2/θ-Al2O3. Korean J. Chem. Eng. 19, 742–748 (2002).
Dajiang, M. et al. Catalytic partial oxidation of methane over Ni/CeO2-ZrO2-Al2O3. J. Rare Earth 25, 311–315 (2007).
Zhang, Q., Shen, M., Wen, J., Wang, J. & Fei, Y. Partial oxidation of methane on Ni/CeO2-ZrO2/γ-Al2O3 prepared using different processes. J. Rare Earth 26, 347–351 (2008).
Michel, C. & Jacques, C. V. Characterization of Solid Materials and Heterogeneous Catalysts: From Structure to Surface Reactivity Vol. 1–2 (Wiley-VCH, Weinheim, 2012).
Ismagilov, I. Z. et al. Hydrogen production by autothermal reforming of methane over NiPd catalysts: effect of support composition and preparation mode. Int. J. Hydrogen Energy 39, 20992–21006 (2014).
Ismagilov, I. Z. et al. Effect of support modification on the physicochemical properties of a NiPd/Al2O3 catalyst for the autothermal reforming of methane. Kinet. Catal. 56, 394–402 (2015).
Vamvakeros, A. et al. Removing multiple outliers and single-crystal artefacts from X-ray diffraction computed tomography data. J. Appl. Crystallogr. 48, 1943–1955 (2015).
Coelho A.TOPAS and TOPAS-Academic: an optimization program integrating computer algebra and crystallographic objects written in C++. J. Appl. Crystallogr. 51 ,210–218 (2018).
The development of the catalyst used in this work was funded within the DEMCAMER project as part of the European Union Seventh Framework Programme (FP7/2007–2013) under grant agreement no. NMP3-LA-2011–262840. Note: ‘The present publications reflect only the authors’ views and the Union is not liable for any use that may be made of the information contained therein’. The authors would like to thank the ESRF for beamtime. Antonis Vamvakeros and Dorota Matras (respectfully in full and in part) are supported through funding received from the European Union Horizon 2020 research and innovation programme under grant agreement no. 679933 (MEMERE project). Andrew M. Beale acknowledges EPSRC (grant EP/K007467/1) for an Early Career Fellowship. The authors would like to thank Thomas Buslaps and Denis Duran for their help during the experimental setups at beamline ID15A of the ESRF and Gavin Vaughan for optimising the continuous rotation-translation XRD-CT data acquisition macro.
The authors declare no competing interests.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Vamvakeros, A., Jacques, S.D.M., Di Michiel, M. et al. 5D operando tomographic diffraction imaging of a catalyst bed. Nat Commun 9, 4751 (2018). https://doi.org/10.1038/s41467-018-07046-8
Chemical gradients in automotive Cu-SSZ-13 catalysts for NOx removal revealed by operando X-ray spectrotomography
Nature Catalysis (2021)
A deep convolutional neural network for real-time full profile analysis of big powder diffraction data
npj Computational Materials (2021)
Spatial quantification of dynamic inter and intra particle crystallographic heterogeneities within lithium ion electrodes
Nature Communications (2020)
Reconstruction of 5D cardiac MRI through the blood flow registration: simulation of the fifth dimension and assessment of the left ventricular ejection fraction
Network Modeling Analysis in Health Informatics and Bioinformatics (2020)
Design of next-generation ceramic fuel cells and real-time characterization with synchrotron X-ray diffraction computed tomography
Nature Communications (2019)