## Abstract

Few-layer black phosphorus (BP) with an anisotropic two-dimensional (2D)-layered structure shows potential applications in photoelectric conversion and photocatalysis, but is easily oxidized under ambient condition preferentially at its edge sites. Improving the ambient stability of BP nanosheets has been fulfilled by chemical functionalization, however this functionalization is typically non-selective. Here we show that edge-selective functionalization of BP nanosheets by covalently bonding stable C60 molecules leads to its significant stability improvement. Owing to the high stability of the hydrophobic C60 molecule, C60 functions as a sacrificial shield and effectively protects BP nanosheets from oxidation under ambient condition. C60 bonding leads to a rapid photoinduced electron transfer from BP to C60, affording enhanced photoelectrochemical and photocatalytic activities. The selective passivation of the reactive edge sites of BP nanosheets by sacrificial C60 molecules paves the way toward ambient processing and applications of BP.

## Introduction

Few-layer black phosphorus (BP), a two-dimensional (2D)-layered semiconductor that can be exfoliated from bulk BP, has been attracting increasing interest owing to its unique band structure featuring direct band gap with thickness-dependent gap energy in the range of 0.3–2.0 eV and high charge carrier mobility of 1000 cm2 V−1 s−1, rendering its potential applications in transistors, biomedicine, energy conversion, and storage1,2,3,4,5,6. Realization of such applications of few-layer BP is largely dependent on exfoliated BP nanosheets, which are however easily oxidized under ambient condition because each phosphorus atom has a pair of lone electrons prone to react with oxygen adsorbed on the surface of BP nanosheets7,8,9,10. The oxidation rate of BP nanosheets was found by Favron et al. to depend linearly on oxygen concentration dissolved in adsorbed water and light intensity8. A more recent report by Kuntz et al. revealed that pure oxygen led to oxidation of the van der Waals surface of BP, whereas water oxidized BP at pre-existing defects such as edges or steps10. Thus, improving the ambient stability of BP is a prerequisite for its practical applications11. So far several strategies have been developed to improve the ambient stability of BP nanosheets, which includes, for instance, protective layers coating12,13, heteroatoms doping14, and hybridization with other chemicals15,16,17,18 and chemical functionalization19,20. Among them, chemical functionalization has been implemented as one of the most effective routes to passivate the reactive BP, fulfilled by either covalent functionalization19, coordination20, or noncovalent functionalization via van der Waals (vdW) heterostructure formation or electrostatic interactions21,22,23. Noteworthy, these reported chemical functionalization approaches are typically non-selective, mostly on the surface of BP nanosheets19,20,21,22,23. Although surface functionalization can effectively passivate the phosphorus atoms located on the puckered surface, the involvement of functional groups can result in strong structure perturbation, consequently compromising the unique electronic structures of BP. Such an influence is amplified in few-layer BP nanosheets due to its improved specific surface area. On the other hand, P atoms at the edge sites are found to be more reactive in oxidation than those at the surface of phosphorene10. Thus, selective functionalization of BP, especially at its edges, is highly desired for passivating BP without losing its surface integrity. However, edge-selective functionalization of BP nanosheets has rarely been reported because of the difficulty in selectively activating its edge sites and finding a functional molecule with suitable reactivity which affords reaction with the more reactive edge sites only.

Fullerenes such as C60 as the first member of nanocarbon family are one of the most representative molecular materials, showing high stability against light, oxygen and water due to its hydrophobicity and spherical aromaticity24,25,26,27,28. These features along with its strong electron-accepting ability render the potential applications of fullerenes in versatile fields including energy conversion, catalysis, biomedicines29,30,31. Given that the low ambient stability of BP nanosheets is primarily due to its facile oxidation under the conditions of light, oxygen and water7,8,9,10, an intriguing idea is whether incorporating stable C60 molecules would prevent BP from oxidation. Besides, compared to such small molecules as aryl diazonium which afforded surface functionalization of BP19, the lower reactivity of C60 may benefit edge-selective functionalization of BP nanosheets. Nevertheless, to the best of our knowledge, up to now hybrid of BP and C60 has been scarcely reported primarily due to the difficulty on hybridization owing to their divergence on the dimensions.

Herein, we report the edge-selective bonding of C60 molecules onto BP nanosheets via covalent phosphorus–carbon bonds, accomplished via a facile one-step solid-state mechanochemical route by ball-milling bulk BP and C60 powders without any additive. On the basis of a series of morphological and spectroscopic characterizations, the successful edge-selective bonding of C60 within BP-C60 hybrid was confirmed. The effect of C60 bonding on the stability of BP nanosheets in water is studied. C60 molecules bonding at the edges of BP nanosheets serve as sacrificial shield, resulting in significant stability improvement of BP nanosheets against oxidation as well as obviously enhanced photoelectrochemical and photocatalytic activities of BP. Thus, our strategy on selectively passivating the reactive edge sites of BP nanosheets by sacrificial C60 molecules opens up new avenues for versatile applications of BP.

## Results

### Synthesis and characterization of the BP-C60 hybrid

As an alternative route to the solution-phase chemical functionalization, solid-state mechanochemical method has recently been extensively applied to prepare edge-selectively functionalized graphene nanosheets by attaching different elements, small inorganic molecules or C6032,33,34. Given that BP has a 2D-layered structure analogous to graphene, we are stimulated to employ solid-state mechanochemical method to synthesize BP nanosheets with edge-selectively bonded C60 based on its simplicity and environmental-friendliness (without using any organic solvent). Three hundred milligrams of bulk BP, which was prepared by a phase transformation reaction from red phosphorus35, and 600 mg C60 powder were mixed and ball-milled directly under an Ar atmosphere in a planetary ball-milling machine (Fig. 1a). After ball-milling at 250 rpm for 24 h, the resultant black mixture was collected and Soxhlet-extracted with CS2 for 48 h to remove the unreacted C60. Note that, previously Cui et al. made an attempt to synthesize a BP-C60 composite via mechanochemical ball-milling route as a comparative study with BP-graphite composite synthesized under the same condition. However, in their report carbon materials including graphite and C60 were ball-milled prior to blending with BP, thus a two-step ball-milling process was needed for synthesizing their BP-C60 composite. Besides, whether or not C60 molecules bonded directly with BP remained unclear15. Hence, in our present study, we managed to simplify the process to one-step and unravel clearly how C60 molecules bond with BP.

Scanning electron microscopy (SEM) was carried out to study the morphology of BP-C60 hybrid. Compared to the bulk BP which shows large sheets with sizes of more than 10 μm (Supplementary Fig. 1a), BP-C60 hybrid exhibits aggregated particles with sizes of 1 μm in average (Supplementary Fig. 1b). For comparison, we also prepared two control samples obtained by ball-milling BP with LiOH as additive (abbreviated as BP-BM)6 and ball-milling C60 only (abbreviated as C60-BM) under the same ball-milling condition, and found that BP-BM shows smaller aggregated particles (Supplementary Fig. 1c) compared to that of BP-C60 hybrid. This is understandable since the existence of C60 would dissipate the mechanical energy of ball-milling effective for cleaving BP sheets. The average thickness of BP-C60 hybrid, acquired by atomic force microscopic (AFM) analyses (Supplementary Fig. 2), is ~2.5 nm, which is comparable to that of BP-BM (~2.7 nm) and corresponds to ~4-layer nanosheets based on the interlayer distance of ~0.52 nm (ref. 2). An average C60 molar content of 19 per 1000 P atoms was estimated according to the weight ratio of C60 (~30%) within the BP-C60 hybrid determined by thermogravimetric analysis (TGA) (Supplementary Fig. 3). The X-ray diffraction (XRD) pattern of BP-C60 hybrid shows intensive peaks at 16.8°, 34.2°, and 52.3°, which are indexed as the (020), (040), and (060) planes of BP, respectively (Supplementary Fig. 4), thus the crystal structure of BP is preserved after ball-milling. Besides, the signals of C60 crystals are invisible in the XRD pattern of BP-C60 hybrid, indicating the complete removal of unreacted C60 by Soxhlet-extraction.

The transmission electron microscopy (TEM) image of BP-BM shows flat nanosheets (inset of Fig. 1b, see also Supplementary Fig. 5b for a large-area image). According to the high-resolution TEM (HRTEM) image, the lattice fringes of (111) plane with space distance of 2.5 Å were observed at the edge of BP nanosheets, which is covered with amorphous coating due to the existence of defects resulted from P atom reconstruction at the edges of BP nanosheets during ball-milling process as well as the attachment of the hydroxyl groups at the edges introduced by LiOH additive (Fig. 1b). The amorphous coating may raise from oxidation of BP since the specimen had to be exposed in air for hours before transferred into TEM chamber. In contrast, the TEM image of the BP-C60 hybrid shows lattice fringes of (020) plane at the edges of the BP nanosheets without amorphous coating (Fig. 1c), even though the BP-C60 sample was exposed in air together with BP-BM, indicating that the BP-C60 hybrid has an improved structure stability at ambient condition. Interestingly, along the edges of the BP nanosheets, hollow nanospheres with diameter of 1.0 nm are observed in the high-resolution TEM (HRTEM) image of the BP-C60 hybrid (Fig. 1c), which match well with the morphology of C60 molecules with a van der Waals diameter of 1.0 nm24,25. These results indicate that C60 molecules primarily attach at the edges of BP nanosheets. Moreover, we carried out scanning transmission electron microscopy-energy dispersive X-ray spectroscopic (STEM-EDX) measurements to study the chemical distribution of the BP-C60 hybrid, and found that the P elements distribute homogeneously over the entire nanosheet whereas C elements have a much lower content than P elements (Fig. 1d–g). Thus, C60 bonding onto the surface of BP nanosheets can be excluded otherwise a much higher content of C elements should have been observed.

It is intriguing to determine whether C60 molecules attach onto the edges of BP nanosheets via covalent bonding or physical adsorption. We performed a series of spectroscopic characterizations to address this issue. For comparison, we prepared a physical mixture of BP-BM and C60 (abbreviated as BP/C60 mixture, in which the weight ratio of C60 is ~30%, close to that within BP-C60 hybrid) as a control sample. We first performed Fourier-transform infrared (FTIR) and solid-state 13C and 31P nuclear magnetic resonance (NMR) spectroscopic studies so as to investigate the bonding structure of C60 in the BP-C60 hybrid. The FTIR spectrum of the BP-C60 hybrid (Fig. 2a) shows four characteristic vibrational peaks of C60 at 526, 576, 1182, and 1428 cm−1 without appreciable shift relative to the pristine C60, indicating the existence of C60 moiety in the BP-C60 hybrid (see also Supplementary Fig. 6 for comparison with bulk BP and BP-BM). Besides, several new vibrational peaks at 707, 770, 795, 1510, and 1536 cm−1 appear in the spectrum of the BP-C60 hybrid. Except the vibrational peaks at 1510 and 1536 cm−1 which are also detected in the spectrum of C60-BM, the three new vibrational peaks at 707, 770, and 795 cm−1 are exclusively observed in the spectrum of the BP-C60 hybrid but absent in that of BP/C60 mixture. These results confirm that the BP-C60 hybrid is not a physical mixture of BP-BM, and the new vibrational peaks should originate from the as-formed phosphorus-carbon (P–C) covalent bonds15,36. In the solid-state 13C-NMR spectrum of BP-C60 hybrid, intense signals in the region of 130–160 ppm are detected, which are typical for sp2-carbon of C60, and an additional weak peak at 75.75 ppm is observed, which is absent in the spectra of both BP/C60 mixture and pure C60 (Supplementary Fig. 7), confirming the formation of sp3-carbon on the C60 cage. On the other hand, according to the comparison of the solid-state 31P NMR spectra of the BP-C60 hybrid, bulk BP and BP/C60 mixture, the intense signal at 21.68 ppm observed in bulk BP is obviously broadened with the appearance of several shoulder peaks in the high field in the spectra of both the BP-C60 hybrid and BP/C60 mixture probably due to the decreased crystallinity and the covalent functionalization of BP caused by ball-milling6,37. Interestingly, the signal peak at 21.68 ppm observed in bulk BP shifts to 22.86 ppm in the spectrum of the BP-C60 hybrid (Supplementary Fig. 7), suggesting a deshielding effect with decrease of electron density of the nucleus of P atom. On the contrary, for BP/C60-mixture such a signal peak negatively shifts to 19.62 ppm due to the covalent bonding of the hydroxyl functional groups6. The dramatic difference between the spectra of the BP-C60 hybrid and BP/C60-mixture solidifies the conclusion that the BP-C60 hybrid is not the physical mixture of BP and C60.

Figure 2b compares Raman spectra of the BP-C60 hybrid, bulk BP, pristine C60, and BP/C60 mixture. Bulk BP exhibits three intense Raman signals at 361, 437, and 465 cm−1, which are assigned to $${\mathrm{A}}_{\mathrm{g}}^1,{\hskip2pt}{\mathrm{B2}}_{{\mathrm{g}}}$$ and $${\mathrm{A}}_{\mathrm{g}}^2$$ modes, respectively38. In the Raman spectrum of pristine C60, two intense signals are observed at 495 and 1469 cm−1 corresponding to $${\mathrm{A}}_{\mathrm{g}}^1\,{\mathrm{and}}\,{\mathrm{A}}_{\mathrm{g}}^2$$ mode, respectively39. For the BP/C60 mixture, its Raman spectrum shows a superposition of signals of BP and C60 moieties without any shifts, indicating no strong intermolecular interactions between BP and C60 moieties. Instead, the Raman spectrum of the BP-C60 hybrid is apparently different from that of BP/C60-mixture in terms of the absence of the signal at 495 cm−1 ($${\mathrm{A}}_{\mathrm{g}}^1$$ mode) and the down-shift of the most intense $${\mathrm{A}}_{\mathrm{g}}^2$$ mode (1469 cm−1) of pristine C60 by 8 to 1461 cm−1. Since the latter peak ($${\mathrm{A}}_{\mathrm{g}}^2$$ mode) is sensitive to the charge state of C60, such a down-shift suggests that charge transfer from BP to C60 may take place due to the well-known strong electron-accepting ability of C6024,34. These results indicate that the BP-C60 hybrid is not a physical mixture of BP-BM and C60 otherwise charge transfer from BP to C60 could not have happened, instead C60 molecules attach onto the edges of BP nanosheets via covalent bonding. Besides, the three characteristic Raman peaks of bulk BP show negligible shifts and relative intensity change in the spectrum of the BP-C60 hybrid (see inset of Fig. 2b), confirming that C60 molecules primarily attach at the edges of BP nanosheets otherwise obvious change of their relative intensity would have been visible if surface grafting of C60 molecules onto BP nanosheets occurred19.

To further analyze the bonding structure of BP in the BP-C60 hybrid, we carried out X-ray absorption spectroscopic (XAS) and X-ray photoemission spectroscopic (XPS) studies. P K-edge XAS spectra of the BP-C60 hybrid and bulk BP are compared in Fig. 2c. The XAS spectrum of the BP-C60 hybrid exhibits a more intense peak at 2145.8 eV and a blue-shift by 1 eV of the absorption edge compared to that of bulk BP, indicating the electron transfer from BP to C6040,41. We further collected P L-edge XAS spectra of the BP-C60 hybrid and bulk BP, which provide richer spectral features than the K-edge spectra42. As shown in Fig. 2d, the P L-edge XAS spectrum of bulk BP exhibits near-edge absorption peaks in the region of 129.5–132.5 eV corresponding to the P(2p) → 1e* transition and a broad peak at around 137.0 eV ascribed to transitions from 2p3/2 and 2p1/2 levels43,44. However, in the P L-edge XAS spectrum of the BP-C60 hybrid, a new peak centered at 135.2 eV appears, which can be assigned to the as-formed P–C bonds8,38. Noteworthy, this peak is absent in the P L-edge XAS spectrum of the BP/C60 mixture, confirming further that the BP-C60 hybrid is not a physical mixture of BP-BM and C60.

Figure 2e, f compares the high-resolution P 2p spectra of the BP-C60 hybrid and bulk BP. In the high-resolution P 2p XPS spectrum of bulk BP, two intense peaks centered at 129.6 and 130.5 eV are attributed to 2p3/2 and 2p1/2 of P–P bonds, while a weak broad peak at 133.0 eV is due to the unavoidable oxidation of BP (Fig. 2e)6,8,45,46,47. For the BP-C60 hybrid, although the overall P 2p XPS spectrum looks quite similar (Supplementary Fig. 8), a detailed deconvolution analysis reveals the appearance of a new peak centered at 133.5 eV, which can be assigned to P-C covalent bonds (Fig. 2f)19.

### Formation mechanism of the BP-C60 hybrid

Based on the aforementioned characterizations, we propose a plausible conformation of the BP-C60 hybrid as well as its formation mechanism as illustrated in Supplementary Fig. 9. Similar to the studies of mechanochemical functionalization of graphene extensively reported in the literatures32,33,34, high-energy ball-milling of bulk BP results in its exfoliation to few-layer BP nanosheets along with the generation of the reactive species (radicals and ions) at the edges via a mechanochemical cleavage of P–P bonds. Simultaneously, C60 is activated by high-energy ball-milling33, and consequently attaches onto the activated edges of BP nanosheets via the covalent P-C bonds. In this sense, the attachment of C60 onto the surface of BP nanosheets is less preferable because the average thickness of the BP-C60 hybrid (2.5 ± 0.2 nm) is even slightly smaller than that of BP-BM (2.7 ± 0.2 nm) according to AFM analyses (Supplementary Fig. 2). Thus, bonding of C60 onto BP nanosheets is highly edge-selective. Noteworthy, such an edge-selective bonding of C60 onto BP nanosheets can be accomplished by blending bulk BP and C60 directly without any additive, thus being very facile and eco-friendly. In addition, we also carried out a control experiment with an attempt to improve the yield of the BP-C60 hybrid by ball-milling the mixture of bulk BP and C60 in the existence of LiOH, which was a crucial additive for the formation of graphene-C60 hybrid as reported previously34, but surprisingly found almost no hybrid formation according to Raman spectroscopic analysis (Supplementary Fig. 10).

### Ambient stability of the BP-C60 hybrid

It is well known that BP nanosheets can be easily oxidized under ambient condition, and previous reports reveal that surface functionalization of BP can effectively passivate the P atoms located on the puckered surface and consequently stabilize BP nanosheets19,20. It is thus stimulating to investigate whether the edge-selective functionalization by C60 can stabilize BP nanosheets as well. We monitored the optical absorbances of BP-C60 hybrid and BP-BM which are both dispersed in water under ambient condition20. In the UV-vis absorption spectrum of the BP-C60 hybrid dispersion, a shoulder peak at 340 nm appears (Fig. 3a), which is absent in the spectrum of BP-BM dispersion (Fig. 3b), confirming the existence of C60 moiety within the BP-C60 hybrid (Supplementary Fig. 11). Noteworthy, the UV-vis absorbance of BP-C60 dispersion at 550 nm shows only a slight decrease (by 2%) after standing for 5 h, whereas there is a 38% decrease in the absorbance for BP-BM dispersion. After 7 days, the absorbance of BP-C60 dispersion retains at 86%, which is much larger than that of BP-BM dispersion (36%, Fig. 3c). Therefore, the degradation rate of BP-C60 in water is significantly inhibited by a factor of 4.6 compared to that of BP-BM. The significant improvement of the stability of the BP-C60 hybrid is attributed to the bonding of stable C60 molecules via the covalent P-C bonds as confirmed by the above spectroscopic studies. Since C60 molecules have high stability against light, oxygen, and water24,25,26,27, bonding of C60 onto the edges of BP nanosheets provides a sacrificial shield which effectively prevents BP from attacks of light, oxygen and water (see Supplementary Fig. 9)10. Thus, we demonstrate that edge-selective functionalization by C60 can stabilize BP nanosheets other than surface functionalization.

### Photoelectrochemical and photocatalytic activities

Upon improving the stability of BP nanosheets in water via edge-selective bonding of C60, we next applied the BP-C60 hybrid in photoelectrochemical cell and photocatalytic dye degration. Figure 4a shows a typical photocurrent response curve of a photoelectrochemical cell composed of a BP-C60 hybrid-modified FTO transparent electrode measured at a bias voltage of 0.2 V. Clearly, a photocurrent switching during light on–off cycles is observed, and the net photocurrent induced by the initial light illumination is 1.2 μA cm−2, which attenuates rapidly during the light illumination of 100 s (Fig. 4a). Such a photocurrent overshooting phenomenon upon light illumination has been often reported for photoelectrochemical cells based on semiconducting inorganic nanostructures, and is presumably due to the back electron transfer process48. For comparison, we also measured the photocurrent responses of BP–BM and C60-BM under the identical conditions. BP-BM exhibits a photocurrent response of 0.12 μA cm−2, which is comparable to that of BP nanosheets with comparable thickness reported in ref. 49. The photocurrent of the BP-C60 hybrid is around 10 times of that of BP-BM and also much higher than that of C60-BM (0.20 μA cm−2), indicating that the hybrid conformation is advantageous for enhancing the photoelectric conversion properties of both BP and C60. Compared to BP/C60 mixture for which a photocurrent response of 0.57 μA.cm−2 is obtained, the photocurrent response of the BP-C60 hybrid is around two times higher. This indicates again that BP-C60 hybrid and BP/C60 mixture are quite different, and the covalent bonding of C60 onto BP is crucial for improving the photocurrent response. Since the optical absorption edge of the BP-C60 hybrid is comparable to that of BP-BM (Supplementary Fig. 12a), the enhanced photoelectric conversion property can be attributed to the photoinduced electron transfer from BP to C60 within the BP-C60 hybrid as revealed by steady-state photoluminescence (PL) spectroscopic study (Supplementary Fig. 13a), which takes place in the order of tens to hundreds of picoseconds according to time-resolved photoluminescence (TRPL) spectroscopic result (Supplementary Fig. 13b).

We further evaluated the effect of C60 bonding on the photocatalytic activity of BP for degradation of Rhodamine B (RhB) dye under visible light. Figure 4b compares the photocatalytic activities of the BP-C60 hybrid, BP/C60 mixture, bulk BP, pristine C60, BP-BM, and C60-BM. While bulk BP, pristine C60, BP-BM, C60-BM, and BP/C60 mixture all show low photocatalytic activity, the BP-C60 hybrid exhibits significantly enhanced photocatalytic activity with an apparent reaction rate constant (k) of 6.70 h−1 based on fitting to a pseudo-first-order kinetics (Fig. 4b, c)50. Noteworthy, the photocatalytic activity of BP/C60 mixture is much lower than that of the BP-C60 hybrid, and is even lower than that of BP-BM due mainly to the decrease of the content of BP-BM (~70 wt%). This result reveals the advantage of the BP-C60 hybrid formation in enhancing the photocatalytic activity of BP. To evaluate the stability of the BP-C60 hybrid during photocatalytic degradation reactions, we measured the TEM image and P 2p XPS spectrum of the BP-C60 hybrid after photocatalytic degradation reactions (Supplementary Figs. 14, 15), and found that the BP-C60 hybrid kept the original form of nanosheets with comparable sizes to the original one, and no obvious oxidization occurred. Thus, the high stability of the BP-C60 hybrid against oxidation during the photocatalytic degradation reactions is confirmed.

To unravel the mechanism responsible for the enhanced photocatalytic activity of the BP-C60 hybrid, we measured its conduction band (CB) and valence band (VB) energy levels by synchrotron radiation photoemission spectroscopy (SR-PES), which are −3.27 and −4.64 eV versus vacuum level (−1.23 and 0.14 V vs reversible hydrogen electrode (RHE)), respectively (Supplementary Figs. 16, 17 and Supplementary Table 1). Compared to BP-BM with CB/VB levels of −0.86/0.35 V vs RHE, both of the CB and VB levels of the BP-C60 hybrid shift negatively. In particular, the more negative CB level of the BP-C60 hybrid facilitates the reduction of the dissolved O2 to generate O2(ref. 46.), which then transforms to OH radicals50 and consequently degrade RhB (Fig. 4d). Indeed, the gradual generation of .OH radicals during the photocatalytic process was confirmed by monitoring the formation of hydroxyl radicals over the visible light irradiation period of 40 min by PL spectroscopy (Supplementary Fig. 18).

## Discussion

In summary, we report edge-selective functionalization of BP nanosheets by covalently bonding stable C60 molecules, leading to significant stability improvement of BP owing to the sacrificial C60 shield. The edge-selective bonding of C60 molecules via covalent P–C bonds was accomplished via a one-step ball-milling of the BP and C60 mixture without any additive, thus being very facile and eco-friendly. Owing to the high stability of the hydrophobic C60 molecules against light, oxygen, and water, C60 effectively protects BP nanosheets from oxidation, thus significantly improves the stability of BP nanosheets in water with the degradation rate inhibited by a factor of 4.6. The involvement of C60 leads to the photoinduced electron transfer from BP to C60 within the BP-C60 hybrid, which can inhibit the recombination of charge carriers and consequently enhance not only the photoelectric conversion property but also the photocatalytic activity of BP. Our conceptual breakthrough on selectively passivating the reactive edge sites of BP nanosheets by sacrificial C60 molecules paves the way towards ambient processing and applications of BP.

## Methods

### Preparation of the BP-C60 hybrid

Bulk BP was synthesized by a phase transformation reaction from red phosphorus following a similar method reported in literature35. The BP-C60 hybrid was synthesized in a planetary ball-milling machine. Typically, a mixture of 300 mg bulk BP powder and 600 mg C60 powder was put into a ZrO2 ball-milling jar containing 50 g ZrO2 balls (3 mm diameter). The jar was sealed in a glovebox filled with Ar and finally equipped on the planetary ball-milling machine. The ball-milling process was performed at ambient temperature for total 24 h (with 15 min interval for every 30 min milling time) with the rotation speed of 250 rpm. After ball-milling, the resultant mixture was collected and Soxhlet-extracted with CS2 for 48 h to remove the unreacted C60. Finally, the sample was vacuum dried for 1 day at 40 °C.

The control sample BP-BM was prepared by ball-milling a mixture of 270 mg bulk BP powder and 630 mg anhydrous LiOH powder for 12 h with 50 g ZrO2 (3 mm diameter)6. C60-BM was synthesized by ball-milling pristine 1 g C60 powder for 12 h with 50 g ZrO2 (3 mm diameter), followed by Soxhlet-extraction with CS2 for 48 h to remove the unreacted C60. The BP/C60 mixture was prepared through stirring the BP-BM powders (70 wt%) and C60 powders (30 wt%) in the 10 mL isopropanol solution by 24 h and removing solvent by centrifugation.

### Stability measurements

The BP-C60 and BP-BM powders were dispersed in water and sonicated for 30 min, followed by 20 min centrifugation at 9000 rpm to get dispersed BP-C60 and BP-BM nanosheets aqueous solution. The BP-C60 and BP-BM nanosheet aqueous solutions were kept under ambient condition for different periods, and the optical absorbance at each time point was monitored so as to investigate their stability according to the change of the optical absorbance intensity.

### Photoelectrochemical measurements

The sample (15 mg) was dispersed in ethanol (300 μL), ultrasonicated for 30 min to form a homogenous ink. A volume of 100 μL of the ink was dropped onto the conductive side of FTO slide (1 cm × 2 cm) coating ~1 cm2, followed by vacuum drying. The films on FTO were used as working electrode. The electrochemical experiments were carried out on an electrochemical workstation (CHI 660C, Shanghai ChenHua Instrument Company, China). With a typical three-electrode cell under the ambient condition and a 300 W xenon lamp (Lansheng Electronic Co., China) as light source. The counter electrode and reference electrode were a platinum wire and a silver wire. The electrolyte was 0.1 M KCl aqueous solution.

### Photocatalytic measurements

A 5 mg sample was placed in 50 mL 0.01 mg mL−1 RhB solution in a 50 mL beaker. The solution was magnetically stirred in dark for 60 min to ensure the establishment of an adsorption/desorption equilibrium between the photocatalyst and organic pollutants. Photocatalytic degradation of RhB by the powder samples under visible light irradiation was performed using a 300 W xenon lamp with a UV cutoff filter (λ > 420 nm) as light. Before irradiation, 2 mL solution was collected and tested by using UV-vis-NIR spectrometer to measure the concentration of the solution after adsorption/desorption equilibrium. During irradiation, about 2 mL solution was collected and tested by using UV-vis-NIR spectrometer every 10 min. The concentration of RhB was measured according to the absorbance at 550 nm.

To detect the formation of hydroxyl radicals, 5 mg BP-C60 hybrid powder was placed in 50 mL terephthalic acid solution containing (4 × 10−4 M terephthalic acid and 2 × 10−3 M NaOH). The solution was irradiated by a 300 W halogen lamp (with a 400 nm filter). At every 10 min, 1.5 mL suspensions were collected and centrifuged. The resulted supernatants were subjected to PL measurements to detect the fluorescence spectra of the generated 2-hydroxyterephthalic acid.

### Characterization

FTIR spectra were performed on a TENSOR 27 spectrometer (Bruker, Germany) at room temperature. The Raman spectra were obtained at room temperature with an in Via Raman Microscope equipment (Renishaw, England) with a 532 nm excitation laser. Solid-state 13C nuclear magnetic resonance (NMR) spectra was carried out on a AVANCE AV400 magic angle spinning (MAS) measurements (Bruker, Germany) using a standard Bruker 4 mm MAS probe with spinning speed 14 kHz. SEM images were obtained from a JEOL JSM-6390LA instrument (Rigaku, Japan). The high-resolution transmission electron microscopy (HRTEM) was conducted on a JEOL-2010 (Rigaku, Japan) microscope operating at a voltage of 200 kV. The scanning transmission electron microscopy-energy dispersive X-ray (STEM-EDX) mapping images were obtained on a JEOL-2100F (Rigaku, Japan) microscope operating at a voltage of 200 kV. X-ray photoelectron spectroscopy (XPS) was conducted on a Thermo-VV ESCALAB 250 (Thermo-VV Scientific) machine. Atomic force microscopy (AFM) measurements were carried out on a XE7 scanning probe microscope (Park, Korea). XRD patterns were obtained from a Smart Lab 9 kW X-ray diffraction instrument (Rigaku, Japan). Thermal gravimetric analysis (TGA) analysis was carried out on a Q600 SDT instrument (TA, USA) under N2 atmosphere. UV-vis-NIR diffuse reflection spectroscopy (DRS) was performed on a 3700 UV-vis spectrometer (Shimadzu, Japan). The Carbon K-edge X-ray absorption spectroscopy (XAS) and phosphorus L2,3-edge XAS were collected with a 0.1 eV energy resolution at beamline 12B-α of the National Synchrotron Light Source (Heifei, China) at National Synchrotron Radiation Laboratory. The Phosphorus K-edge XAS were collected at beamline 16A1 of the National Synchrotron Radiation Research Center (Hsinchu, Taiwan, China). Synchrotron radiation photoemission spectroscopy (SR-PES) experiments were performed at the Catalysis and Surface Science endstation in the National Synchrotron Radiation Laboratory (NSRL), Hefei, and measured using synchrotron radiation light as the excitation source with a photon energy of 39.9 eV. A sample bias of −5 V was applied to observe the secondary electron cutoff. The fluorescence spectra were measured on a Hitachi F-4500 fluorescence spectrophotometer with an excitation wavelength of 320 nm. The steady-state photoluminescence (PL) spectra were measured using an fluorescence spectrometer (Jobin Yvon, France) with an excitation wavelength of 450 nm.

## Data availability

All data supporting the findings of this study are available from the corresponding author on request.

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## References

1. 1.

Mannix, A. J., Kiraly, B., Hersam, M. C. & Guisinger, N. P. Synthesis and chemistry of elemental 2D materials. Nat. Rev. Chem. 1, 0014 (2017).

2. 2.

Li, L. et al. Black phosphorus field-effect transistors. Nat. Nanotech. 9, 372–377 (2014).

3. 3.

Xia, F., Wang, H. & Jia, Y. Rediscovering black phosphorus as an anisotropic layered material for optoelectronics and electronics. Nat. Commun. 5, 4458 (2014).

4. 4.

Batmunkh, M., Bat-Erdene, M. & Shapter, J. G. Phosphorene and phosphorene-based materials–prospects for future applications. Adv. Mater. 28, 8586–8617 (2016).

5. 5.

Lin, S. et al. Solution-processable ultrathin black phosphorus as an effective electron transport layer in organic photovoltaics. Adv. Funct. Mater. 26, 864–871 (2016).

6. 6.

Zhu, X. et al. Black phosphorus revisited: a missing metal‐free elemental photocatalyst for visible light hydrogen evolution. Adv. Mater. 29, 1605776 (2017).

7. 7.

Walia, S. et al. Defining the role of humidity in the ambient degradation of few-layer black phosphorus. 2D Mater. 4, 015025–015032 (2016).

8. 8.

Favron, A. et al. Photooxidation and quantum confinement effects in exfoliated black phosphorus. Nat. Mater. 14, 826–832 (2015).

9. 9.

Huang, Y. et al. Interaction of black phosphorus with oxygen and water. Chem. Mater. 28, 8330–8339 (2016).

10. 10.

Kuntz, K. L. et al. Control of surface and edge oxidation on phosphorene. ACS Appl. Mater. Interfaces 9, 9126–9135 (2017).

11. 11.

Liu, H., Du, Y., Deng, Y. & Ye, P. D. Semiconducting black phosphorus: synthesis, transport properties and electronic applications. Chem. Soc. Rev. 44, 2732–2743 (2015).

12. 12.

Kim, J. et al. Long-term stability study of graphene-passivated black phosphorus under air exposure. Curr. Appl. Phys. 16, 165–169 (2016).

13. 13.

Wan, B. et al. Enhanced stability of black phosphorus field-effect transistors with SiO2 passivation. Nanotechnology 26, 435702–435707 (2015).

14. 14.

Yang, B. et al. Te-doped black phosphorus field-effect transistors. Adv. Mater. 28, 9408–9415 (2016).

15. 15.

Sun, J. et al. Formation of stable phosphorus–carbon bond for enhanced performance in black phosphorus nanoparticle–graphite composite battery anodes. Nano Lett. 14, 4573–4580 (2014).

16. 16.

Zhang, Y. et al. An air‐stable densely packed phosphorene–graphene composite toward advanced lithium storage properties. Adv. Energy Mater. 6, 1600453 (2016).

17. 17.

Sun, J. et al. A phosphorene–graphene hybrid material as a high-capacity anode for sodium-ion batteries. Nat. Nanotech. 10, 980–985 (2015).

18. 18.

Lei, W., Liu, G., Zhang, J. & Liu, M. Black phosphorus nanostructures: recent advances in hybridization, doping and functionalization. Chem. Soc. Rev. 46, 3492–3509 (2017).

19. 19.

Ryder, C. R. et al. Covalent functionalization and passivation of exfoliated black phosphorus via aryl diazonium chemistry. Nat. Chem. 8, 597–602 (2016).

20. 20.

Zhao, Y. et al. Surface coordination of black phosphorus for robust air and water stability. Angew. Chem. Int. Ed. 128, 5003–5007 (2016).

21. 21.

Abellán, G. et al. Noncovalent functionalization of black phosphorus. Angew. Chem. Int. Ed. 128, 14777–14782 (2016).

22. 22.

Tao, W. et al. Black phosphorus nanosheets as a robust delivery platform for cancer theranostics. Adv. Mater. 29, 1603276 (2017).

23. 23.

Zhao, Y. et al. Passivation of black phosphorus via self-assembled organic monolayers by van der Waals epitaxy. Adv. Mater. 29, 1603990 (2017).

24. 24.

Kadish, K. M. & Ruoff, R. S. Fullerenes: Chemistry, Physics, and Technology (John Wiley, New York, 2000).

25. 25.

Liu, F. P. & Yang, S. F. Carbon: Fullerene in Encyclopedia of Inorganic and Bioinorganic Chemistry (eds Lukehart, C. M. & Scott, R. A.) (John Wiley & Sons, Chichester, UK, 2014).

26. 26.

Scanlon, J. C., Brown, J. M. & Ebert, L. B. Oxidative stability of fullerenes. J. Phys. Chem. 98, 3921–3923 (1994).

27. 27.

Deguchi, S., Alargova, R. G. & Tsujii, K. Stable dispersions of fullerenes, C60 and C70, in water. Preparation and characterization. Langmuir 17, 6013–6017 (2001).

28. 28.

Bühl, M. & Hirsch, A. Spherical aromaticity of fullerenes. Chem. Rev. 101, 1153–1184 (2001).

29. 29.

Popov, A. A., Yang, S. F. & Dunsch, L. Endohedral fullerenes. Chem. Rev. 113, 5989–6113 (2013).

30. 30.

Cui, C. H., Li, Y. W. & Li, Y. F. Fullerene derivatives for the applications as acceptor and cathode buffer layer materials for organic and perovskite solar cells. Adv. Energy Mater. 7, 1601251 (2016).

31. 31.

Chen, X. et al. A facile mechanochemical route to a covalently bonded graphitic carbon nitride (g-C3N4) and fullerene hybrid toward enhanced visible light photocatalytic hydrogen. Nanoscale 9, 5615–5623 (2017).

32. 32.

Jeon, I.-Y. et al. Large-scale production of edge-selectively functionalized graphene nanoplatelets via ball milling and their use as metal-free electrocatalysts for oxygen reduction reaction. J. Am. Chem. Soc. 135, 1386–1393 (2012).

33. 33.

Zhu, S.-E., Li, F. & Wang, G.-W. Mechanochemistry of fullerenes and related materials. Chem. Soc. Rev. 42, 7535–7570 (2013).

34. 34.

Guan, J. et al. Directly bonded hybrid of graphene nanoplatelets and fullerene: facile solid-state mechanochemical synthesis and application as carbon-based electrocatalyst for oxygen reduction reaction. J. Mater. Chem. A. 3, 4139–4146 (2015).

35. 35.

Nilges, T., Kersting, M. & Pfeifer, T. A fast low-pressure transport route to large black phosphorus single crystals. J. Solid State Chem. 181, 1707–1711 (2008).

36. 36.

Puziy, A. M. et al. Surface chemistry of phosphorus-containing carbons of lignocellulosic origin. Carbon 43, 2857–2868 (2005).

37. 37.

Hu, H. et al. Covalent functionalization of black phosphorus nanoflakes by carbon free radicals for durable air and water stability. Nanoscale 10, 5834–5839 (2018).

38. 38.

Sugai, S., Ueda, T. & Murase, K. Pressure dependence of the lattice vibration in the orthorhombic and rhombohedral structures of black phosphorus. J. Phys. Soc. Jpn. 50, 3356–3361 (1981).

39. 39.

Kuzmany, H., Matus, M., Burger, B. & Winter, J. Raman scattering in C60 fullerenes and fullerides. Adv. Mater. 6, 731–745 (1994).

40. 40.

Rouff, A. A., Rabe, S., Nachtegaal, M. & Vogel, F. X-ray absorption fine structure study of the effect of protonation on disorder and multiple scattering in phosphate solutions and solids. J. Phys. Chem. A 113, 6895–6903 (2009).

41. 41.

Huang, T. et al. Direct self-focusing synthesis of monodisperse [Au8(PPh3)7]2+ nanoclusters. Dalton Trans. 46, 12239–12244 (2017).

42. 42.

Kruse, J. et al. Phosphorus L 2,3 - edge XANES: overview of reference compounds. J. Synchrotron Radiat. 16, 247–259 (2009).

43. 43.

Jürgensen, A. The P (1s) and P (2p) XAFS spectra of elemental phosphorus, theory and experiment. Phys. Scr. T115, 548–551 (2005).

44. 44.

Nicotra, G. et al. Absorption edges of black phosphorus: a comparative analysis. Phys. Status Solidi B 253, 2509–2514 (2016).

45. 45.

Tian, B. et al. Supported black phosphorus nanosheets as hydrogen-evolving photocatalyst achieving 5.4% energy conversion efficiency at 353 K. Nat. Commun. 9, 1397 (2018).

46. 46.

Wang, H. et al. Ultrathin black phosphorus nanosheets for efficient singlet oxygen generation. J. Am. Chem. Soc. 137, 11376–11382 (2015).

47. 47.

Zhang, T. et al. Degradation chemistry and stabilization of exfoliated few-Layer Black phosphorus in water. J. Am. Chem. Soc. 140, 7561-7567 (2018).

48. 48.

Hickey, S. G., Riley, D. J. & Tull, E. J. Photoelectrochemical studies of CdS nanoparticle modified electrodes: absorption and photocurrent investigations. J. Phys. Chem. B 104, 7623–7626 (2000).

49. 49.

Ren, X. et al. Environmentally robust black phosphorus nanosheets in solution: application for self-powered photodetector. Adv. Funct. Mater. 27, 1606834 (2017).

50. 50.

Chai, B., Liao, X., Song, F. & Zhou, H. Fullerene modified C3N4 composites with enhanced photocatalytic activity under visible light irradiation. Dalton Trans. 43, 982–989 (2014).

## Acknowledgements

We are grateful to Dr. Huanxin Ju and Professor Hualing Zeng (University of Science and Technology of China) for technical assistances in SR-PES and TRPL measurements, respectively. We also thank Professor Yi Luo (University of Science and Technology of China) for stimulating discussions. This work was partially supported by the National Key Research and Development Program of China (2017YFA0402800), National Natural Science Foundation of China (Nos. 21371164, 51572254, 51672262, 51772285, and 11435012), the Major/Innovative Program of Development Foundation of Hefei Center for Physical Science and Technology (No. 2016FXZY003), and the Fundamental Research Funds for the Central Universities (WK3430000003, and WK3430000023).

## Author information

### Affiliations

1. #### Hefei National Laboratory for Physical Sciences at Microscale, CAS Key Laboratory of Materials for Energy Conversion, Department of Materials Science and Engineering, Synergetic Innovation Center of Quantum Information & Quantum Physics, University of Science and Technology of China, Hefei, 230026, China

• Xianjun Zhu
• , Mengmeng Zhang
• , Runnan Guan
• , Yajuan Liu
• , Muqing Chen
• , Yalin Lu
•  & Shangfeng Yang
2. #### CAS Key Laboratory of Materials for Energy Conversion, iChEM (Collaborative Innovation Center of Chemistry for Energy Materials), Department of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230026, China

• Taiming Zhang
• , Daochuan Jiang
• , Zijun Sun
• , Hongchang Jin
• , Hengxing Ji
•  & Pingwu Du
3. #### National Synchrotron Radiation Laboratory, University of Science and Technology of China, Hefei, 230029, China

• Hengli Duan
• , Wensheng Yan
•  & Shiqiang Wei

### Contributions

S.Y. conceived and designed this research. X.Z. synthesized the BP-C60 samples, conducted characterizations and photoelectrochemical measurements. T.Z. prepared the bulk BP samples. D.J. and Z.S. helped with photocatalytic measurements. H.D., H.C.J., and W.Y. carried out XAS studies. M.Z., R.G., Y.L., and M.C. helped with the material synthesis and characterizations. H.X.J., P.D., S.W., Y.L., and S.Y. co-wrote the paper, and all the authors commented on it.

### Competing interests

The authors declare no competing interests.