Abstract
The success of oxide electronics depends on the ability to design functional properties such as ferroelectricity with atomic accuracy. However, despite tremendous advances in ferroelectric heterostructures, the development towards multilevel architectures with precise layer-by-layer command over the polarization is impeded by the lack of continuous control over the balance of electrostatics, strain, chemistry and film thickness during growth. Moreover, the polarization in the deeper layers becomes inaccessible when these are buried by the ongoing deposition. Taking ferroelectric BaTiO3 and multiferroic BiFeO3 as model systems, we observe and engineer the emergence, orientation and interaction of ferroelectric polarization in ultrathin heterostructures with monolayer accuracy. We achieve this by optical second harmonic generation which tracks the evolution of spontaneous polarization in real time throughout the deposition process. Such direct and in situ access to the polarization during growth leads us to heterostructures with user-defined polarization sequences—towards a new class of functional ferroic materials.
Similar content being viewed by others
Introduction
In epitaxial films, control of ferroelectricity now spans from determination of the critical thickness in the ultrathin regime1, 2 to engineering of ferroelectric properties and domain architectures using epitaxial strain3,4,5, surface termination6, or oxygen partial pressure7. Their potential is greatly enhanced by making the step from single films to advanced multilayer architectures8,9,10,11,12. Here, the interaction between the individual layers adds to the functionality. In particular, fascinating phenomena happen at or across the interfaces between adjacent constituents8. Examples are stabilization of the spontaneous polarization at ultra-low thickness13, 14, global enhancement of ferroelectricity15, but also improper ferroelectricity16, formation of polar vortices9, and negative capacitance10, 11. Implementing the desired degrees of freedom into the multilayer systems remains challenging, however, because of the intricate nature of the interactions among the ferroelectric layers and also between the ferroelectric layers and the paraelectric or metallic spacer layers. In order to achieve deterministic control of the polar state in ferroelectric heterostructures, direct feedback-like access to the polarization of each layer at the unit-cell scale is required. For example, synchrotron X-ray based techniques constitute an advanced approach to in situ investigation of ultrathin ferroelectricity1, 12, but their application is restricted to highly periodic patterns of ferroelectric domains.
Here we show full access in observation and engineering of the amplitude and orientation of polarization in ferroelectric multilayers for two prominent ferroelectrics, BaTiO3 and BiFeO3, using in situ optical second harmonic generation (ISHG) for tracking the evolving polar state. Starting with ultrathin single-layers, the critical thickness and subsequent evolution of the polarization in both compounds are resolved layer by layer. Next, in ferroelectric/metal-spacer multilayers with designed surface termination, we manipulate the relative polarization orientation of adjacent ferroelectric layers. Parallel and opposite orientation of polarization in neighboring layers is initiated and tracked in situ. This level of control opens an avenue towards multilayers with user-defined polarization sequence.
Results
Probing the emergence of ferroelectric polarization in situ using SHG
SHG denotes doubling of the frequency of a light wave in a material. This nonlinear optical technique is sensitive to, in principle, any type of symmetry-breaking long-range order. It has been used to characterize a large variety of ferroic states ex situ17,18,19,20. It is a non-destructive technique with large working distance. Therefore, it is ideal for in situ probing by connecting a laser and an optical detector to the deposition chamber. In fact, such ISHG has been already discussed as a diagnostic tool, e.g., for the surface chemistry of semiconductors21, 22. This is far from the physical electronic functionalities targeted with our work, however. In relation to oxide electronics, ISHG has been suggested as a possible methodical concept, yet without performing any ISHG experiments23.
In ferroelectrics, the efficiency of the frequency doubling, i.e., the SHG susceptibility, is proportional to P s, the spontaneous polarization17, 18. The sign change resulting from a reversal of P s corresponds to a 180° shift in the phase of the SHG light wave24 so that SHG can even distinguish between different directions of polarization in an interference experiment17, an aspect that will be crucial for the design of polarization-engineered multilayer heterostructures later on. A schematic of our ISHG setup is depicted in Fig. 1a as inset.
In the first step, we need to understand the emergence of polarization in a single film during the growth process with layer-by-layer resolution. We begin with BaTiO3 films that we grow epitaxially on SrRuO3-buffered (001)-oriented SrTiO3 (BTO|SRO||STO, see Methods section for details). Reflection high energy electron diffraction (RHEED) is performed simultaneously to ISHG for calibrating the ISHG yield to the thickness of the BTO film with unit-cell accuracy (Fig. 1b).
At zero coverage, Fig. 1a merely yields a surface-induced background ISHG contribution on the order of 1% of the maximum net ISHG signal. It is deconvoluted from the data (Methods section) before calculating the unit-cell polarization in Fig. 1c. The onset of a macroscopic polarization in BTO, indicated by the steady increase of the ISHG signal, occurs around 4 unit cells. This critical thickness is in agreement with previous reports1, 25, but here we observe the emergence in a single, continuous experimental run. According to Fig. 1c, the unit-cell polarization of our film saturates around 16 unit cells.
Note that complementary cooling runs on a BTO film of 3 unit cells yielded no polarization-related ISHG signal down to room temperature (Supplementary Fig. 1), we do not observe a temperature dependence in the critical thickness for the onset of ferroelectricity26. Figure 1 thus tells us that room temperature ferroelectricity in heterostructures with BTO layers of <4 unit cells cannot be intrinsic, but must involve some interlayer coupling12, 13, 27. Our measurement also shows that tetragonal ferroelectric thin films like BTO can be grown right in the ferroelectric state, in agreement with synchrotron studies28, 29. With a growth temperature of 650 °C, \(T_{\mathrm{C}}^{{\mathrm{film}}}\) must be substantially higher than \(T_{\mathrm{C}}^{{\mathrm{bulk}}}\) = 120 °C. Such enhancement is associated with effects like compressive epitaxial strain28 or strain-induced defect dipoles supporting increased tetragonality30. Finally, Fig. 1 points to single-domain growth of the BTO since in a multi-domain film interference of SHG contributions from oppositely polarized domains would lead to cancellation of the ISHG yield24. The depolarization fields from surface charges that would promote such nanodomain generation are screened by the metallic SRO buffer layer31, 32. The suspected single-domain state is further confirmed by the piezoresponse force microscopy (PFM) measurement in the inset of Fig. 1d. The outer, unpoled region shows the same brightness as the innermost quadratic box that was tip-voltage-poled into a single-domain state.
For scrutinizing the influence of domain formation on the emergence of polarization, we then tested BiFeO3 films grown epitaxially on SrRuO3-buffered (110)-oriented DyScO3 (BFO|SRO||DSO, see Methods section for details). The ISHG data in Fig. 2a, c show that ferroelectricity in the multi-domain films emerges at 4 unit cells. The polarization analysis of the ISHG signal in Fig. 2a, performed as described elsewhere19, and complementary PFM scans, included as Supplementary Fig. 2, reveal that films develop a ferroelectric stripe-domain pattern33. The unit-cell polarization in our BFO|SRO||DSO films saturates at 10 unit cells. We verified that, in contrast, saturation in single-domain (111)-oriented BFO|SRO||STO ferroelectric films grown in parallel is not even reached at 20 unit cells. Most likely, the multi-domain structure of our BFO sample with stripe domains influences the depolarizing field such that bulk polarization in such BFO films is reached at much lower thickness than in the (111)-oriented single-domain specimens. We thus see that information on the domain structure in the ultrathin regime during growth, which would be inaccessible without ISHG, is essential for understanding the early stages in the formation of a spontaneous polarization.
Monitoring polar states in heterostructures with user-defined polarization sequences
We now turn towards evolution and control of the spontaneous polarization ±P s in complex heterostructure architectures. We use the relation between chemical termination and polarization orientation known for BFO single layers6 and investigate, if this relation remains valid in BFO multilayer heterostructures, or if interlayer coupling effects interfere with or even dominate the influence of termination. For this purpose, we first grew sequences of BFO|SRO bilayers as shown in Fig. 3a. Here, SrO self-termination of the SRO buffer layer should force P s in all BFO layers into the down direction (Fig. 3a). As the growth of this structure progresses, the ISHG signal in Fig. 3c adds up layer by layer. (The signal decrease during SRO deposition is caused by transmission and reflection of the fundamental and ISHG waves on the SRO.) This reveals constructive interference of the SHG contributions from each layer and confirms uniform orientation of P s. According to the inset of Fig. 3c, the onset of ISHG occurs around 4 unit cells in all BFO layers. Thus, the BFO layers behave in an independent way, without noticeable coupling between them. In agreement with this, switching of the polarization of the buried layers due to the change of the electrostatic environment with the subsequently deposited BFO layers, which would manifest as a drop of the ISHG yield, is not observed. Despite the complexity of polarization screening processes at polar oxide interfaces34, this behavior points towards the metallic nature and an efficient screening provided by the 10-unit-cell SRO interlayers35. Note that the ISHG approach allows us to probe the buried polarization without the irreversible invasion of our sample that we would have with transmission electron microscopy.
The negligible coupling of the BFO layers across the SRO35, 36 gives us the possibility to set the direction of P s in each BFO layer independently and thus construct user-defined up–down polarization sequences. P s is set via the interfacial termination which controls the growth of the BFO from the A-perovskite or B-perovskite ABO3 site6. As mentioned, SrO self-termination of the SRO induces B-site BFO growth with down polarization. TiO2-terminated surfaces, on the other hand, lead to A-site BFO growth with up polarization. Here we pursue the latter in two ways (Fig. 4b): by depositing a single layer of TiO2 on the SrO-self-terminated SRO interlayer, or by replacing the SRO interlayer by MnO2-terminated La0.7Sr0.3MnO3-buffered TiO2-terminated STO37. Scanning-probe images in Fig. 4c, d confirm for single-BFO layers that the polarization direction engineering works as expected. This gives us the possibility to orient the polarization independent of the explicit constituents and interface chemistry in a ferroelectric multilayer architecture.
Figure 4e shows the ISHG intensity during growth of a heterostructure with anticipated up and down polarization, respectively, in the first two BFO layers. For the first BFO layer, we observe the onset of ISHG and, thus, polarization around 4 unit cells, followed by further ISHG increase with increasing BFO film thickness. Subsequently, absorption in the SRO layer attenuates the ISHG intensity as explained above. The second BFO layer, like the first BFO layer, yields an onset of polarization after 4 unit cells, but most strikingly the ISHG signal now decreases with increasing BFO thickness until it finally reaches zero. This clearly points to an opposite direction of P s in the two BFO layers. The associated 180° phase shift between the ±P s-related ISHG waves leads to their destructive interference as depicted in Fig. 4a until finally complete cancellation is achieved. Up-polarized and down-polarized ferroelectric layers may, therefore, be stacked at will by using termination control in the metal/ferroelectric multilayers. In particular, there is no reorientation of P s in the first BFO layer when the SRO or the second BFO layer is grown. Note that only continuous real time observation during growth allows us to conclude that the zero net ISHG signal in Fig. 4e is not caused by an absence of ferroelectricity but by cancellation of opposite ferroelectric polarization contributions in the multilayer stack. This is elaborated further in Supplementary Fig. 3.
Discussion
In conclusion, we demonstrated how to tailor ferroelectric heterostructures with user-defined polarization sequence. First, we resolved the thickness-dependent evolution of polarization in ferroelectric ultrathin films, using ISHG as non-invasive real time probe of the polarization throughout the entire growth process. We thus observed the emergence, build-up and bulk-like saturation of the unit-cell polarization in two important ferroelectrics, single-domain BaTiO3 and multiferroic multi-domain BiFeO3. The saturation in the single-domain sample is acquired at higher thickness than in the multi-domain sample. By combining electrostatics, strain and surface chemistry we then show how ferroelectric multilayers with an, in principle, arbitrary sequence of up-polarized and down-polarized ferroelectric layers can be grown.
The unprecedented degree of freedom in tracking and controlling polarization is only one possible route towards a novel class of oxide-electronic devices. Going beyond the ferroelectric properties, ISHG may be employed to track electronic states38, magnetic-ordering phenomena17, magnetoelectric-coupling effects39, 40, and many other functional oxide-heterostructure correlations.
Methods
Sample preparation
The thin films and heterostructures were grown by pulsed laser deposition (PLD). The DyScO3 substrates (Crystec GmbH) were kept at 700 °C during the SrRuO3 deposition and at 710 °C for the BiFeO3 growth. The La0.7Sr0.3MnO3 layer was grown at 700 °C. Oxygen partial pressure was 0.1 mbar in all cases. On TiO2-terminated SrTiO3 substrates (Crystec GmbH), the BaTiO3 growth with SRO as buffer layer was done at 650 °C with oxygen partial pressure 0.15 mbar. The KrF excimer laser intensity was set to 0.9 J cm−2. Complementary topography and PFM scans of the BFO films and heterostructures are shown in Supplementary Figs. 2–4.
In situ second harmonic generation
SHG is a nonlinear optical process denoting the emission of light at frequency 2ω from a crystal irradiated with light at frequency ω. This is expressed by the equation P i (2ω) = ε 0 Σ j,k \(\chi _{ijk}^{\left( 2 \right)}\) E j (ω) E k (ω), where E j,k (ω) and P i (2ω) are the electric-field components of the incident light and of the frequency-doubled polarization, respectively, with the latter acting as the source of the SHG wave. The nonlinear susceptibility \(\chi _{ijk}^{\left( 2 \right)}\) characterizes the ferroelectric state18. The fundamental light pulses at ω were emitted at 1 kHz from an amplified Ti:sapphire laser system with an optical parametric amplifier. The light pulses possessed a photon energy of 0.95 eV and a pulse length of 120 fs. To monitor the PLD growth process in real time, we used a custom-designed growth chamber (TSST B.V.) into which we guided the probe light for the ISHG process in a reflection configuration. The incident ω-wave and the emitted 2ω-wave were polarized parallel to the reflection plane (p-in/p-out configuration). Laser pulses of about 20 µJ were focused onto a target area with a diameter of 250 µm. The ISHG measurements are performed in real time and without interrupting the growth process. The ISHG acquisition rate was 1 data point per second (1000 laser pulses). Details of the optical setup and the polarization selection rules for SHG on BFO and BTO are given elsewhere19. The surface-related ISHG background signal on the order of 1% of the maximum net ISHG yield was deconvoluted from the polarization-induced ISHG signal by describing the measured total ISHG signal as interference between a thickness-dependent polarization-related and a thickness-independent background ISHG wave. The background contribution stems mainly from interface and surface contributions and may possess a phase shift to the polarization-related contribution. Fit parameters were the relative amplitude and phase of the background contribution.
Data availability
The data that support the findings of this study are available from the corresponding author upon request.
References
Junquera, J. & Ghosez, P. Critical thickness for ferroelectricity in perovskite ultrathin films. Nature 422, 506–509 (2003).
Fong, D. D. et al. Ferroelectricity in ultrathin perovskite films. Science 304, 1650–1653 (2004).
Schlom, D. G. et al. Strain tuning of ferroelectric thin films. Annu. Rev. Mater. Res. 37, 589–626 (2007).
Kornev, I. A. et al. Ferroelectricity of perovskites under pressure. Phys. Rev. Lett. 95, 196804 (2005).
Biegalski, M. D., Dörr, K., Kim, D. H. & Christen, H. M. Applying uniform reversible strain to epitaxial oxide films. Appl. Phys. Lett. 96, 151905 (2010).
Yu, P. et al. Interface control of bulk ferroelectric polarization. Proc. Natl. Acad. Sci. USA 109, 9710–9715 (2012).
Highland, M. J. et al. Equilibrium polarization of ultrathin PbTiO3 with surface compensation controlled by oxygen partial pressure. Phys. Rev. Lett. 107, 187602 (2011).
Hwang, H. Y. et al. Emergent phenomena at oxide interfaces. Nat. Mater. 11, 103–113 (2012).
Yadav, A. K. et al. Observation of polar vortices in oxide superlattices. Nature 530, 198–201 (2016).
Khan, A. I. et al. Negative capacitance in a ferroelectric capacitor. Nat. Mater. 14, 182–186 (2015).
Zubko, P. et al. Negative capacitance in multi-domain ferroelectric superlattices. Nature 534, 524–528 (2016).
Bein, B. et al. In situ X-ray diffraction and the evolution of polarization during the growth of ferroelectric superlattices. Nat. Commun. 6, 10136 (2015).
Tenne, D. A. et al. Probing nanoscale ferroelectricity by ultraviolet Raman spectroscopy. Science 313, 1614–1616 (2006).
Dawber, M. et al. Tailoring the properties of artificially layered ferroelectric superlattices. Adv. Mater. 19, 4153–4159 (2007).
Lee, H. N., Christen, H. M., Chisholm, M. F., Rouleau, C. M. & Lowndes, D. H. Strong polarization enhancement in asymmetric three-component ferroelectric superlattices. Nature 433, 395–399 (2005).
Bousquet, E. et al. Improper ferroelectricity in perovskite oxide artificial superlattices. Nature 452, 732–736 (2008).
Fiebig, M., Pavlov, V. V. & Pisarev, R. V. Second-harmonic generation as a tool for studying electronic and magnetic structures of crystals. J. Opt. Soc. Am. B 22, 96–118 (2005).
Denev, S. A., Lummen, T. T. A., Barnes, E., Kumar, A. & Gopalan, V. Probing ferroelectrics using optical second harmonic generation. J. Am. Ceram. Soc. 94, 2699–2727 (2011).
Trassin, M., De Luca, G., Manz, S. & Fiebig, M. Probing ferroelectric domain engineering in BiFeO3 thin films by second harmonic generation. Adv. Mater. 27, 4871–4876 (2015).
De Luca, G. et al. Domain wall architecture in tetragonal ferroelectric thin films. Adv. Mater. 29, 1605145 (2017).
Hu, X. F. et al. In situ optical second harmonic monitoring of hydrogen adsorption and desorption kinetics during epitaxial growth on Si [001]. Appl. Phys. Lett. 71, 1376–1378 (1997).
Yamada, C. & Kimura, T. In-situ surface second-harmonic generation study of epitaxial growth of GaAs. Jpn. J. Appl. Phys. 34, 1102–1105 (1995).
Rubano, A. et al. Optical second harmonic imaging as a diagnostic tool for monitoring epitaxial oxide thin-film growth. Appl. Surf. Sci. 327, 413–417 (2015).
Kaneshiro, J., Uesu, Y. & Fukui, T. Visibility of inverted domain structures using the second harmonic generation microscope: comparison of interference and non-interference cases. J. Opt. Soc. Am. B 27, 888–894 (2010).
Junquera, J. & Ghosez, P. First-principles study of ferroelectric oxide epitaxial thin films and superlattices: role of the mechanical and electrical boundary conditions. J. Comput. Theor. Nanosci. 5, 2071–2088 (2008).
Tenne, D. A. et al. Ferroelectricity in ultrathin BaTiO3 films: probing the size effect by ultraviolet Raman spectroscopy. Phys. Rev. Lett. 103, 177601 (2009).
Khestanova, E. et al. Untangling electrostatic and strain effects on the polarization of ferroelectric superlattices. Adv. Funct. Mater. 26, 6446–6453 (2016).
Choi, K. J. et al. Enhancement of ferroelectricity in strained BaTiO3 thin films. Science 306, 1005–1009 (2004).
Sinsheimer, J. et al. In-situ X-ray diffraction study of the growth of highly strained epitaxial BaTiO3 thin films. Appl. Phys. Lett. 103, 3–6 (2013).
Damodaran, A. R., Breckenfeld, E., Chen, Z., Lee, S. & Martin, L. W. Enhancement of ferroelectric curie temperature in BaTiO3 films via strain-induced defect dipole alignment. Adv. Mater. 26, 6341–6347 (2014).
Lichtensteiger, C., Triscone, J. M., Junquera, J. & Ghosez, P. Ferroelectricity and tetragonality in ultrathin PbTiO3 films. Phys. Rev. Lett. 94, 047603 (2005).
Fong, D. D. et al. Stabilization of monodomain polarization in ultrathin PbTiO3 films. Phys. Rev. Lett. 96, 127601 (2006).
Trassin, M. et al. Interfacial coupling in multiferroic/ferromagnet heterostructures. Phys. Rev. B 87, 134426 (2013).
Hong, S., Nakhmanson, S. M. & Fong, D. D. Screening mechanisms at polar oxide heterointerfaces. Rep. Prog. Phys. 79, 076501 (2016).
Toyota, D. et al. Ferromagnetism stabilization of ultrathin SrRuO3 films: thickness-dependent physical properties. J. Appl. Phys. 99, 08N505 (2006).
Stengel, M., Vanderbilt, D. & Spaldin, N. A. Enhancement of ferroelectricity at metal–oxide interfaces. Nat. Mater. 8, 392–397 (2009).
Sanchez, S., Ocla, C. & Fontcuberta, J. Tailored surfaces of perovskite oxide substrates for conducted growth of thin films. Chem. Soc. Rev. 43, 2272–2285 (2014).
Rubano, A. et al. Spectral and spatial distribution of polarization at the LaAlO3/SrTiO3 interface. Phys. Rev. B 83, 155405 (2011).
Trassin, M. Low energy consumption spintronics using multiferroic heterostructures. J. Phys. Condens. Matter 28, 033001 (2016).
Fiebig, M., Lottermoser, T., Meier, D. & Trassin, M. The evolution of multiferroics. Nat. Rev. Mater. 1, 16046 (2016).
Acknowledgements
We thank D. Meier for fruitful discussions and J. Nordlander and C. Becher for experimental assistance. We acknowledge funding through the SNSF R’Equip Program (Grant No. 206021-144988). This research was supported by the EU European Research Council (Advanced Grant 694955—INSEETO).
Author information
Authors and Affiliations
Contributions
M.T. and M.F. initiated this work and supervised the research project. G.D.L., N.S. and S.M. performed the ISHG measurements. M.T. performed the thin film growth with G.D.L. and N.S., C.B. conducted the scanning transmission electron microscopy. All authors discussed the results.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
De Luca, G., Strkalj, N., Manz, S. et al. Nanoscale design of polarization in ultrathin ferroelectric heterostructures. Nat Commun 8, 1419 (2017). https://doi.org/10.1038/s41467-017-01620-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-01620-2
This article is cited by
-
Defeating depolarizing fields with artificial flux closure in ultrathin ferroelectrics
Nature Materials (2023)
-
Bowing to ferroelectric artificial flux closure
Nature Materials (2023)
-
Bringing some bulk into ferroelectric devices
Nature Materials (2022)
-
Signatures of enhanced out-of-plane polarization in asymmetric BaTiO3 superlattices integrated on silicon
Nature Communications (2022)
-
Multilevel polarization switching in ferroelectric thin films
Nature Communications (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.