Abstract
Gel films of low-molecular-weight polyethylene (LMWPE) were prepared by partial melt under compression. The gel films could be readily stretched up to 20 times at 135°C. The Young’s modulus is in the range 32–34 GPa. This value is slightly higher than that of melt-crystallized ultrahigh-molecular-weight polyethylene (UHMWPE) drawn to 40 times at the same temperature but is much lower than that (>200 GPa) of UHMWPE gel films drawn to 300. This behavior is discussed in terms of the morphology of the gel film as studied by wide-angle X-ray diffraction, small-angle X-ray scattering, and birefringence measurements. It turns out that the Young’s modulus, 32–34 GPa, of the LMWPE gel film is attributed to a suitable degree of chain entanglement to assure effective transmission of the drawing force associated with a significant crystal transformation from a folded to a fibrous type. In spite of the perfect orientation of the c-axes, however, the Young’s modulus of the LMWPE gel film is much lower than that of the UHMWPE gel films with a draw ratio of 300. This is thought to be due to low crystallinity and short length of extended crystal chains.
Similar content being viewed by others
Article PDF
References
C. Sawatari, T. Okumura, and M. Matsuo, Polym. J., 18, 741 (1986).
C. Sawatari, S. Shimogiri, and M. Matsuo, Macromolecules, 20, 1033 (1987).
W. O. Statton and P. H. Geil, J. Appl. Polym. Sci., 3, 357 (1960).
P. A. Irvine and P. Smith, Macromolecules, 19, 240 (1986).
M. Matsuo, K. Inowe, and N. Abumiya, Sen-i Gakkaishi, 40, 275 (1984).
C. Sawatari and M. Matsuo, Colloid Polym. Sci., 263, 783 (1985).
C. Sawatari and M. Matsuo, Polymer, 30, 1603 (1989).
M. Matsuo, K. Hirota, K. Fujita, and H. Kawai, Macromolecules, 11, 1000 (1978).
S. Kojima and R. S. Porter, J. Polym. Sci., Polym. Phys. Ed., 16, 1729 (1978).
W. T. Mead, C. R. Porter, and R. S. Porter, J. Polym. Sci., Polym. Phys. Ed., 17, 859 (1979).
M. Ito, T. Kanamoto, K. Tanaka, and R. S. Porter, Macromolecules, 14, 1779 (1979).
J. M. Andrews and I. M. Ward, J. Mater. Sci., 5, 411 (1970).
J. Clements, G. Capaccio, and I. M. Ward, J. Polym. Sci., Polym. Phys. Ed., 17, 693 (1979).
J. Clements, R. Jakeways, and I. M. Ward, Polymer, 19, 639 (1978).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Ogita, T., Yasuda, H., Suzuki, N. et al. Drawing of Low-Molecular-Weight Polyethylene Gel Films and Ultrahigh-Molecular-Weight Polyethylene Melt Films. Polym J 25, 445–452 (1993). https://doi.org/10.1295/polymj.25.445
Issue Date:
DOI: https://doi.org/10.1295/polymj.25.445