Abstract
Cellular solids are instrumental in creating lightweight, strong, and damage-tolerant engineering materials. By extending feature size down to the nanoscale, we simultaneously exploit the architecture and material size effects to substantially enhance structural integrity of architected meta-materials. We discovered that hollow-tube alumina nanolattices with 3D kagome geometry that contained pre-fabricated flaws always failed at the same load as the pristine specimens when the ratio of notch length (a) to sample width (w) is no greater than 1/3, with no correlation between failure occurring at or away from the notch. Samples with (a/w) > 0.3, and notch length-to-unit cell size ratios of (a/l) > 5.2, failed at a lower peak loads because of the higher sample compliance when fewer unit cells span the intact region. Finite element simulations show that the failure is governed by purely tensile loading for (a/w) < 0.3 for the same (a/l); bending begins to play a significant role in failure as (a/w) increases. This experimental and computational work demonstrates that the discrete-continuum duality of architected structural meta-materials may give rise to their damage tolerance and insensitivity of failure to the presence of flaws even when made entirely of intrinsically brittle materials.
Similar content being viewed by others
Introduction
Bulk ceramics are highly sensitive to flaws and fail catastrophically upon applied loads, most commonly at the small internal flaws like cracks, voids, and inclusions1,2,3. Fiber-reinforced ceramic-matrix composites (CMCs) have been developed to reduce their sensitivity to flaws while capitalizing on the high strength of ceramics4,5,6,7. These CMCs utilize deformation of the matrix and/or fibers to delocalize strain near stress concentrators, such as holes or notches, which leads to flaw insensitive behavior4,5,7. Insensitivity to notches has been reported for silicon carbide/calcium aluminosilicate CMCs for ratios of notch to sample size of 0.2 < (a0/b) < 0.8, where a0 is the notch size and 2b is the sample width5,7.
It has also been postulated that reducing sample dimensions of brittle materials can give rise to flaw insensitivity and to attain near-theoretical strength8. Gao et al.’s theoretical work demonstrated that a thin plate with a penny shaped notch exhibits the fracture strength of a perfect crystal when the plate thickness falls below a critical length scale, which is a function of surface energy, elastic modulus, and ideal material strength8. Nano-fracture experiments and computations on brittle nanocrystalline platinum nanopillars, with diameters of 100 nm and a grain size of 6 nm, revealed that their failure strength remained equivalent to the ultimate tensile strength even in the presence of pre-fabricated flaws and that failure location was uncorrelated to the presence of the flaws9. This emergence of flaw insensitivity in nano-structures was attributed to their failure at the “weakest-link,” be it at an internal, microstructural stress concentration like a grain boundary triple junction or at an external flaw, with failure mechanism representing the intrinsic material strength. In the absence of a discrete material microstructure, it has been reported that 75 nm-diameter metallic glass nanopillars containing external notches always failed at those locations at lower peak loads than their un-notched counterparts10.
These examples demonstrate that failure tolerance of some materials to flaws cannot be solely attributed to the length scale; it stems from the complex interplay between the internal microstructural energy landscape within the material and the external sample dimensions and geometry10. Several studies have demonstrated that incorporating architecture in material design enables proliferating lucrative material size effects that emerge at the nano-scale onto macro-scale architected meta-materials; for example smaller is stronger/weaker for metals, smaller is ductile for brittle metallic glasses, and smaller is tougher for ceramics11. The periodic arrangements of small-scale ordered cellular solids, such as nano- or meso-lattices, span length scales ranging from hundreds of microns to tens of nanometers and facilitate the attainment of novel mechanical properties under compression, like recoverability and enhanced specific strength compared to bulk, and these properties arise as a result of structural and material size effects12,13,14. Existing cellular solids theories predict that mechanical behavior is determined by the deformation mechanism of the lattice, which is either by bending or stretching and is a function of the nodal connectivity, and the constituent material properties15,16,17. A bending dominated structure is predicted to have lower strength and stiffness when compared to a stretching-dominated structure15,16,17,18. In the case of architected bulk materials, another aspect of microstructure arises in the dimensions of not only the grains of the constituent material but also in the size of the unit cells. Fracture experiments on macro-scale cellular solids have been explored in literature; tensile properties of nanolattices – with or without pre-fabricated defects - are currently unknown16,19,20,21,22,23,24,25,26.
We explore tensile failure of 3-dimensional hollow alumina kagome nanolattices and demonstrate that they exhibit flaw tolerance in terms of strength and failure location, which we attribute to the presence of a discrete structure at the micron and sub-micron lengths scales within a continuum-like material.
Kagome Tension Sample Fabrication
We performed uniaxial tension experiments on hollow alumina (Al2O3) nanolattices with and without through-thickness notches. Figure 1 shows the CAD design and SEM images of an as-fabricated dog-bone-shaped hollow alumina kagome nanolattice thin plate embedded in an octet-truss lattice head; the kagome lattice had a unit cell size of l = 3.85 ± 0.16 μm, the octet-truss head had a unit cell size of l ~ 4.5 μm, shown in Fig. 1(B,F). The kagome lattice was created by tessellating pairs of stacked tetrahedra in three dimensions in a hexagonal tessellation pattern, which gives rise to an A-B-C stacking pattern. The kagome unit cell shown in Fig. 1(C,G) contains a single complete set of A-B-C stacked tetrahedra. The tension samples were fabricated on a silicon wafer using a polymer scaffold created via two-photon lithography direct laser writing process and were subsequently coated with 50 nm of Al2O3 using atomic layer deposition (ALD) at 150 °C to make a composite Al2O3/polymer structure. The octet-truss head had a width of w = 139.8 ± 1.1 μm, a height of h = 19.2 ± 0.2 μm, and a thickness of t = 24.5 ± 0.3 μm, with the averages representing 5 samples. The Al2O3/polymer kagome test section initially had a width of 12 unit cells, a height of 6 unit cells, and a thickness of 2 unit cells but the width was reduced at a later step in the fabrication process to accommodate the experimental set-up. The samples had an octet-truss lattice at both the top and bottom of the kagome test section, shown in Fig. 1(A,E); a kagome A-B-C unit cell layer was embedded in octet-truss head and ~5 μm of the kagome test section was embedded in the bottom octet-truss lattice at the interface between the sample and the silicon wafer. The kagome lattice was embedded in the octet-truss lattices at the top and bottom of the test sections to avoid delamination at the interfaces between the kagome test section and the octet-truss head/substrate under tensile loading.
Samples were shaped into dog-bone tensile geometries using a focused ion beam (FIB), at a current of 7 nA, to have a curved edge at the kagome/octet-truss interfaces that served to reduce stress concentrations (Fig. 1(B,F)). The plate-like kagome Al2O3/polymer test section had a final width of w = 66.3 ± 5.2 μm, a height of h = 81.9 ± 0.3 μm, and a thickness of t = 15.4 ± 0.5 μm; the width and height averages were calculated using all samples presented in this work (n = 18) and the average thickness was determined by averaging the thickness of 10 representative samples after the deformation. The FIB was also used to pattern the notches (Fig. 1(D,H)). We tested samples with notch lengths, a, ranging from 0 to 0 − 34.94 μm, and (a/w) varying from 0–0.54, where w is the width of the test section; the unit cell size was kept constant for all samples and notch length-to-unit cell size ratio, (a/l), was varied from 0–9.1. Once the samples were shaped into their final geometry, the internal polymer was removed using O2 plasma (16–18 hours at 100 W) and the samples were visually inspected in the scanning electron microscope (SEM) to non-destructively determine the amount of polymer remaining in the sample; the amount of polymer removed was verified to be approximately constant across all samples using this technique (see Supplementary Info). When the Al2O3 kagome nanolattices were fully hollowed out, the octet-truss head remained a composite, containing the Al2O3 layer and the internal polymer. Additional details on the fabrication process can be found in refs 12, 13, 14, 27 and 28.
We chose the 3D kagome geometry because of its high predicted fracture toughness in 2D, which stems from elastic blunting near the crack tip16,24. The hollow kagome nanolattices in this work are designed to have a stiffness of E = 45 MPa and a relative density of , calculated using a Solidworks model of the kagome unit cell, shown in Fig. 1, and the measured sample dimensions from SEM images. We chose the denser Al2O3/polymer octet-truss lattice as the sample head to stiffen this section relative to the hollow kagome test section16,18. The composite Al2O3/polymer head has a 760x higher stiffness of E = 3.90 GPa and a relative density of (see Supplementary Info for details). We find that this difference in stiffnesses was sufficient to perform the tensile loading with minimized deformation of the octet-truss head.
In-Situ Uniaxial Experiments and Simulations
The as-fabricated kagome dog-bone specimens were subjected to displacement rate-controlled uniaxial straining in an in-situ nanomechanical instrument, InSEM (Nanomechanics, Inc.), at a quasi-static strain rate of . Contact with the samples was made via a tension grip at the bottom faces of the octet-truss head on either side of the kagome lattice; the tension grip was milled in the head of a 0.8 mm stainless steel screw using electrical discharge machining (EDM), as shown in Fig. 1E. Load-displacement data, as well as real-time video of the deformation, was captured during each uniaxial tension experiment. The displacement of the gauge section was calculated using the observed length change, Δl, in the deformation video; uniaxial strain was defined as ε = Δl/l, with the original length l measured in SEM prior to the experiment. The stress at failure was defined as σ = F/A, where A is the overall cross-sectional area of the sample and F is the measured force at failure. The slope of the unloading curve is not a reliable measure of the energy release-rate of the Al2O3 kagome nanolattice since the slope is an artifact of the InSEM controller.
Finite Element (FE) simulations of the as-designed notched and un-notched hollow kagome lattices were performed to assess the ability of continuum-based models to predict deformation of architected meta-materials. The samples in FE models were created from the SolidWorks-constructed geometries and accounted for the interface between the octet-truss sample head and the InSEM grips. Three-dimensional 3-noded triangular shell elements with reduced-integration were employed. The material properties of Al2O3 for the FE analyses were obtained from bulge experiments of equivalently deposited thin films of ALD Al2O3, with the modulus, E, ranging from 164–165 GPa and the ultimate tensile strength, σUTS, in the range of 1.57–2.56 GPa; for the simulations in this work, the input modulus and UTS were taken to be 165 GPa and 1.57 GPa, respectively29. A linear post-cracking stress-strain relationship was incorporated in the simulations to represent the brittle behavior of Al2O3. Displacement-controlled boundary conditions were applied to the octet-truss sample head in locations closely resembling the experimental setup. For numerical efficiency, explicit dynamics procedure was adopted to model the quasi-static applied uniaxial tension loading. To ensure a quasi-static response, the energy balance of the modeling system was constantly monitored such that the kinetic energy of the system was negligible compared to its internal energy and external work. Computations were performed within the finite strain setting using the general-purpose finite element program ABAQUS/Explicit Version 6.13.2. To model and reflect a quasi-static solution, the kinetic energy of the deforming kagome lattice was monitored and enforced to not exceed 1% of its internal energy throughout the majority of the quasi-static analysis. The studied (a/w) ratios were: 0, 0.11, 0.23, 0.35, 0.47 and 0.54. A constant wall thickness of 50 nm across all elements was assumed for all simulations. The global stress and strain of the FE kagome test section was calculated using the same methodology as in experiments.
Results
Figure 2 shows SEM images and representative load vs. strain-to-failure data for the as-fabricated and notched geometries and reveals that all samples failed instantaneously and catastrophically, as expected for a brittle ceramic. Three un-notched samples (a/w = 0) had a Fpeak = 2.00 ± 0.19 mN and a strain at failure of εfailure = 0.006 ± 0.001; the results for various notch sizes are tabulated in the Supplementary Information. Figure 3 shows peak-load-at-failure data for samples with notch-to-width ratios, (a/w), spanning from 0 to 0.54. Samples with (a/w) between 0 and 0.32 had a relatively constant peak-load-at-failure of ~ 2 mN, which is equivalent to the peak load for the un-notched samples. The peak load decreased by 32% as (a/w) increased from 0.32–0.54, likely caused by the 4.2x higher compliance in the widest-notched samples when compared to un-notched samples, also shown in Fig. 3. The experimentally obtained peak load remained nearly constant over the (a/w) range of 0–0.32; the simulations show a monotonic reduction in the peak load with increasing (a/w), decreasing by 59% as (a/w) widens from 0–0.35. The simulations also show a 1.5x increase in compliance as (a/w) increases from 0–0.54, slightly lower than that observed experimentally.
The sample compliance was calculated as C = ε/σ, where σ is the applied load divided by the full cross-sectional area of the gauge section, A, for both experiments and simulations. The experimentally measured compliance is the combined compliance of the sample/nanoindenter system and may not serve as a reliable measure of the absolute compliance of the nanolattices; the calculated compliance serves to compare the relative changes in sample compliance with increasing ratios of (a/w).
Discussion
All samples in this work failed catastrophically for all (a/w), with failure always occurring along a plane of nodes between the tetrahedral pairs forming the kagome lattice. FE simulations revealed that the highest local Von Mises stresses occur at the nodes, along the “planes” where the tetrahedra connect; Fig. 4 shows these calculations for representative un-notched and notched (a/w = 0.3) samples and reveals that the nodes serve as the weakest links when the nanolattice is tensed. This is not surprising, as it has been previously demonstrated that the nodes in similarly-made Al2O3 nanolattices were the weakest links and served as failure initiation locations in compression12,14. We discovered that the as-fabricated, un-notched samples have equivalent local stresses in the nodes located in sample-interior and at the edge of the sample and that the notched samples have the highest local stress concentrations at the notch roots, with minimal local stress at the sample edge immediately prior to failure. Failure in each sample initiated at the node(s) that had a missing neighbor, whose detached side was not constrained by the neighboring unit cells in the lattice. Failure in the notched samples always initiated at the notch root where the adjacent unit cell had one constrained and one un-constrained boundary. All samples in this work had one edge containing unit cells that were fully disconnected from their vertical neighbors while the other edge had unit cells with minimal intact vertical connections along the sample edge; this is a result of the lattice unit cell size and the sample width required to fit the tension grips. Failure in all un-notched samples initiated at the edge with completely disconnected unit cells, which is similar to local geometry at the notch edge where the unit cells have are disconnected from the rest of the lattice on one side. After incipient failure in a single edge node, the crack propagates instantaneously and causes catastrophic failure of the entire structure; the applied force required to fail the first node in uniaxial tension corresponds to the peak load at failure for a nanolattice.
While continuum-based classical mechanics theory predicts that the peak load will decrease at higher (a/w); the nanolattices here exhibit a nearly constant peak load of ~2 mN for (a/w) < 0.38, a value equivalent to that of the un-notched material1,2,30,31. In monolithic ceramic materials with the same geometry, the stress concentration at a notch is highest because the external notch is significantly larger than the size of the internal microstructural flaws1,2,3. Our simulations indicate that in a nanolattice, the stress concentrations at the nodes (internal) and at the notch (external) have similar magnitude because they both arise from the discrete nature of the periodic unit cells. These findings are consistent with tension experiments on notched nanocrystalline Pt nano-tension specimens, which show that the internal stress concentrations at triple junctions and at grain boundaries are comparable to the stress concentrations at the external notches9. The constancy of the peak load at failure arises from the global deformation in all samples being governed by single-node failure in uniaxial tension (provided the sample compliances are comparable). As (a/w) increases to above ~ 0.38, the observed peak load decreases, likely because the remaining intact unit cells are less constrained and experience bending moments. Fleck et al. used FE simulations to show that 2D kagome lattices with solid beams exhibit elastic blunting at the crack tip that results from the stretching-periodic bending geometry, where the lattice bars deform by bending and stretching in the vicinity of the crack. It was also predicted that the radius of the crack blunting region can extend to lengths of up to 20 unit cells for lattices with 32. The lateral displacements calculated for each sample here did not reveal any elastic blunting, likely because the kagome nanolattices in this work contain hollow, non-slender tubes while the work of Fleck et al. assumes solid, slender beams32.
All nanolattices with (a/w) ≤ 0.23 failed away from the notch with the peak load remaining constant at Fpeak ~ 2mN; nanolattices with wider notches failed along the plane of the notch, orthogonal to the loading direction, and Fpeak decreased with a concomitant increase in compliance. Figure 5 summarizes the stress at failure as a function of relative notch size and outlines failure location property space. Failure stress was determined by dividing the peak load, Fpeak, by the cross-sectional area, A, which was calculated using two different criteria: (1) the intact area at the plane of failure (black diamonds)4,5 and (2) the total cross-sectional area of the gauge section (red diamonds). Using the first approach, we observed a roughly constant stress at failure of ~3MPa for (a/w) > 0.3, a plateau that is consistent with literature4,5. Using the intact area at the notch plane to calculate the stress at failure results in its increase by a factor of 1.8 when (a/w) increased from 0.23–0.32, which corresponds to a transition in failure location. A lower stress at failure of 2.73 MPa for the widest-spanning notch, (a/w) = 0.54, is likely a result of substantial compliance, 12.8 kPa−1, of this sample. To determine the stress at failure for (a/w) ≥ 0.54, samples with more unit cells across the width must be fabricated; the fabrication method used in this work poses limitations on creating significantly larger, structurally robust samples of the same geometry. When the stress at failure is calculated using the full cross-sectional area, a parameter space that is insensitive to flaws exists for (a/w) < 0.38 where the stress at failure is ~2.14 MPa. A reduction in stress at failure as (a/w) increases from 0.38–0.54, calculated using this method, stems from the higher sample compliance for (a/w) > 0.38, which wouldn’t occur for larger samples with more unit cells spanning the un-notched region. This analysis demonstrates that hollow Al2O3 nanolattices are insensitive to the presence of external flaws for pre-fabricated defects spanning up to 30% of the sample width. We postulate that this flaw insensitivity arises from the discrete nature of the nanolattice at the micron scale such that the failure strength for notched and un-notched samples is governed by the failure strength of individual junctions between the unit cells subjected to uniaxial tension.
Figure 4 shows representative load-strain data for the notched and un-notched samples generated using FE simulations, which predict a 2.5-times lower peak load for the notched sample compared to the un-notched sample. The model predicted the same peak load as experimentally observed for the un-notched samples and severely under-predicted it for the notched sample with (a/w) = 0.32 (Figs 3 and 4). We examined the sample region that contains the notch and the unit cell at the notch root, with the same region in the un-notched sample chosen as a reference for comparison. Figure 6 displays the von Mises stress distributions and associated distortions in the samples with (a/w) = 0, 0.11 and 0.35 at an applied nominal strain of εy = 0.003, which is well within the elastic regime of the deformation. We denote σreference as the von Mises stress at the junction node in the notch root unit cell, pointed to by the arrows in the zoomed view, and σcell as the maximum von Mises stress in the unit cell. Using the un-notched lattice, with (a/w = 0), as a reference, simulations reveal that a short notch (a/w = 0.11) leads to the stress distributions and the associated distortions being comparable to those in the un-notched lattice. When the notch is lengthened to (a/w) = 0.35, the stresses in the unit cells above and below the notch become significantly lower, which generates a large stress concentration at the notch root. For the short notches, the relative change in σreference is 13% and that in σcell is 2%; those for long notches are 94% and 22%, respectively. Figure 6B also shows that for the short-notch case, the distortions are marginal and similar to those in the un-notched samples, which corroborate the observed notch-insensitivity in experiments. For longer notches, the distortions become significant, with a shift in local stresses towards the notch roots. The insets in Fig. 6B display a zoomed-in view of the notch root and show that for samples with a short notch, the node at the notch root experiences close-to-uniaxial tensile loading mode, which is similar to that in the samples without the notch (Fig. 6A). In samples with long notches (Fig. 6C), the node adjacent to the notch is subject to bending in addition to tension. Failure in long-notched samples initiates at the notch root node; the transition in stress state from tensile-only in the un- and short-notched samples to tensile-and-bending in the long-notched ones may cause different failure modes, which define the notch-insensitivity and notch-sensitivity regimes.
The observed discrepancies between the computations and experimental results shown in Fig. 3 can be attributed to several factors. First, the compliance of the experimental setup cannot be accurately accounted for in the numerical simulations, which leads to a lower calculated peak loads. Secondly, the beam wall thickness and diameter, as well as the hollowness of the beams in the gauge section and Al2O3/polymer composite in the sample head, are assumed to be perfectly uniform in the simulations, which is an idealization of the as-fabricated structure. Additional calculations indicate that variations in tube wall thickness lead to a higher predicted peak load because of the greater load-bearing capacity of the trusses (See Supplementary Information). During sample preparation, the internal polymer of the sample head may be partially exposed to oxygen plasma near the kagome/octet interface, which would lead to variations in the stiffness of the sample head if the internal polymer inside is partially etched (See Supplementary Info). Our simulations revealed that the stress state at the notch root node changed from uniaxial tension to a combination of tension and bending with increasing notch length, which may render the maximum tensile stress-based failure criterion invalid. Several strategies are being pursued to improve the current numerical model, which include incorporating an inhomogeneous distribution of beam wall thicknesses by considering a statistical distribution of thicknesses based on experimental measurements, developing a better understanding of constituent material properties, and designing a more suitable failure criterion.
Summary/Conclusion
We fabricated 3-dimensional dog-bone shaped, hollow-beam alumina nanolattices with kagome architecture, with and without through-notches that span up to 30% of the sample width, and performed uniaxial tension experiments on them. These alumina nanolattices exhibit a nearly constant load-at-failure for notch length-to-sample width ratios of (a/w) < 0.38, which suggests insensitivity of failure to the presence of flaws. This is in contrast to failure of monolithic alumina containing a notch of comparable ratio, which would necessarily fail at the notch at a significantly lower peak load compared to that of an un-notched specimen. We observed a reduction in the observed peak load for samples with (a/w) ≥ 0.38 and attribute it to greater compliance of those samples, which stems from the fewer intact unit cells at the notch plane where failure occurs. We discovered that failure in these architected meta-materials is governed by the strength of the nodes, and that incipient failure occurs at the nodes with one un-constrained boundary. Once failure is initiated, the crack propagates instantaneously and catastrophically, as expected for a brittle material, along a plane of nodes orthogonal to the loading direction. These results suggest that nanolattices are insensitive to externally introduced defects because their failure mechanism is governed by the stress concentrations within the nodal geometry and by a transition from pure uniaxial tension to bending failure. These findings have significant implications in developing novel materials, which propels architected meta-materials to be particularly lucrative for applications that require simultaneous lightweight, strength, and damage tolerance.
Additional Information
How to cite this article: Montemayor, L. C. et al. Insensitivity to Flaws Leads to Damage Tolerance in Brittle Architected Meta-Materials. Sci. Rep. 6, 20570; doi: 10.1038/srep20570 (2016).
References
Koller, A. et al. Structure and Properties of Ceramics (Elsevier, 1994).
Gross, D. & Seelig, T. Fracture Mechanics with an Introduction to Micromechanics (Springer, 2011).
Lawn, B. Fracture of Brittle Solids. (Cambridge University Press, 1993).
McNulty, J. C., Zok, F. W., Genin, G. M. & Evans, A. G. Notch-Sensitivity of Fiber-Reinforced Ceramic-Matrix Composites: Effects of Inelastic Straining and Volume-Dependent Strength. J. Am. Ceram. Soc 82, 1217–1245 (1999).
Mackin, T. J., Purcell, T. E., He, M. Y. & Evans, A. G. Notch Sensitivity and Stress Redistribution in Three Ceramic-Matrix Composites. J. Am. Ceram. Soc. 78, 1719–1728 (1995).
Heredia, F. E. et al. Notch effects in carbon matrix composites. J. Am. Ceram. Soc 77, 2817–2927 (1995).
Cady, C., Mackin, T. & Evans, A. Silicon Carbide/Calcium Aluminosilicate: A Notch-Insensitive Ceramic-Matrix Composite. J. Am. Ceram. Soc. 78, 77–82 (1995).
Gao, H., Ji, B., Jager, I. L., Arzt, E. & Fratzl, P. Materials become insensitive to flaws at nanoscale: 100, 5597–5600 (2003).
Gu, X. W., Wu, Z., Zhang, Y.-W., Srolovitz, D. J. & Greer, J. R. Microstructure versus flaw: mechanisms of failure and strength in nanostructures. Nano Lett. 13, 5703–9 (2013).
Gu, X. W. et al. Mechanisms of Failure in Nanoscale Metallic Glass. Nano Lett. (2014). doi: 10.1021/nl5027869.
Greer, J. R. & De Hosson, J. T. M. Plasticity in small-sized metallic systems: Intrinsic versus extrinsic size effect. Prog. Mater. Sci. 56, 654–724 (2011).
Meza, L. R., Das, S. & Greer, J. R. Strong, lightweight, and recoverable three-dimensional ceramic nanolattices. Science (80-.). 345, 1322–1326 (2014).
Jang, D., Meza, L., Greer, F. & Greer, J. Fabrication and deformation of three-dimensional hollow ceramic nanostructures. Nat. Mater. 12, 893–898 (2013).
Montemayor, L. C. & Greer, J. R. Mechanical Response of Hollow Metallic Nanolattices: Combining Structural and Material Size Effects. J. Appl. Mech. 82, (2015).
Gibson, L. J. & Ashby, M. F. Cellular Solids: Structure and Properties. (Cambridge University Press, 1999).
Fleck, N. A., Deshpande, V. S. & Ashby, M. F. Micro-architectured materials: past, present and future. Proc. R. Soc. A Math. Phys. Eng. Sci. 466, 2495–2516 (2010).
Deshpande, V. S., Ashby, M. F. & Fleck, N. A. Foam topology: bending versus stretching dominated architectures. Acta Mater. 49, 1035–1040 (2001).
Deshpande, V. S., Fleck, N. A. & Ashby, M. F. Effective properties of the octet-truss lattice material. J. Mech. Phys. Solids 49, 1747–1769 (2001).
J. S. Huang, L. J. G. Fracture toughness of brittle honeycombs. Acta Metall. Mater. 39, 1617–1626 (1991).
Huang, J. S. & Gibson, L. J. Fracture toughness of brittle foams. Acta Metall. Mater. 39, 1627–1636 (1991).
Brezny, R. & Green, D. J. Fracture Behavior of Open-Cell Ceramics. J. Am. Ceram. Soc. 72, 1145–1152 (1989).
Brezny, R. & Green, D. J. Factors Controlling the Fracture Resistance of Brittle Cellular Materials. J. Am. Ceram. Soc. 74, 1061–1065 (1991).
Choi, S. & Sankar, B. V. A micromechanical method to predict the fracture toughness of cellular materials. Int. J. Solids Struct. 42, 1797–1817 (2005).
Romijn, N. E. R. & Fleck, N. A. The fracture toughness of planar lattices: Imperfection sensitivity. J. Mech. Phys. Solids 55, 2538–2564 (2007).
Quintana-Alonso, I., Mai, S. P., Fleck, N. A., Oakes, D. C. H. & Twigg, M. V. The fracture toughness of a cordierite square lattice. Acta Mater. 58, 201–207 (2010).
Maiti, S. K., Ashby, M. F. & Gibson, L. J. Fracture Toughness of Brittle Cellular Solids. Scr. Mater. 18, 213–217 (1984).
Meza, L. R. & Greer, J. R. Mechanical characterization of hollow ceramic nanolattices. J. Mater. Sci. 49, 2496–2508 (2014).
Montemayor, L. C., Meza, L. R. & Greer, J. R. Design and Fabrication of Hollow Rigid Nanolattices via Two-Photon Lithography. Adv. Eng. Mater. 16, 184–189 (2014).
Berdova, M. et al. Mechanical assessment of suspended ALD thin films by bulge and shaft-loading techniques. Acta Mater. 66, 370–377 (2014).
Wachtman, J. B. Mechanical Properties of Ceramics. (John Wiley & Sons, Inc., 1996).
Griffith, A. A. The Phenomena of Rupture and Flow in Solids. Philos. Trans. R. Soc. London. Ser. A, Contain. Pap. a Math. or Phys. Character 221, 163–198 (1921).
Fleck, N. A. & Qiu, X. The damage tolerance of elastic–brittle, two-dimensional isotropic lattices. J. Mech. Phys. Solids 55, 562–588 (2007).
Acknowledgements
The authors gratefully acknowledge the financial support of L.C.M’s National Science Foundation Graduate Research Fellowship and J.R.G’s Defense Advanced Research Projects Agency grant under the MCMA program (contract no. W91CRB-10-0305) and to the National Science Foundation (CMMI‐1234364), as well as Kavli Nanoscience Institute at Caltech for critical support and infrastructure. W.W.H. and Z.Y.W. gratefully acknowledge the financial support from the Agency for Science, Technology and Research (A*STAR), Singapore and the use of computing resources at the A*STAR Computational Resource Centre, Singapore. The authors would also like to acknowledge Tamar Partamian for graphics contributions to Figure 5, Alexander Lozano for helping design the grip and Lucas Meza for help with the CAD images for simulation. The authors would also like to acknowledge Prof. John Hutchinson, Prof. Norman Fleck, and Prof. Katherine Faber for useful discussions.
Author information
Authors and Affiliations
Contributions
L.C.M. fabricated all samples, conducted all experiments, and compiled all experimental data. W.H.W. performed the finite element simulations. J.R.G. conceived of the research and provided guidance. All authors contributed to the analysis of the data, discussed the findings, and wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Montemayor, L., Wong, W., Zhang, YW. et al. Insensitivity to Flaws Leads to Damage Tolerance in Brittle Architected Meta-Materials. Sci Rep 6, 20570 (2016). https://doi.org/10.1038/srep20570
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep20570
This article is cited by
-
Effect of Topology on Transient Dynamic and Shock Response of Polymeric Lattice Structures
Journal of Dynamic Behavior of Materials (2023)
-
The toughness of mechanical metamaterials
Nature Materials (2022)
-
Centimetre-scale crack-free self-assembly for ultra-high tensile strength metallic nanolattices
Nature Materials (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.