Abstract
We report a series of ionically modified ferrocene compounds for hybrid lithium-organic non-aqueous redox flow batteries, based on the ferrocene/ferrocenium redox couple as the active catholyte material. Tetraalkylammonium ionic moieties were incorporated into the ferrocene structure, in order to enhance the solubility of the otherwise relatively insoluble ferrocene. The effect of various counter anions of the tetraalkylammonium ionized species appended to the ferrocene, such as bis(trifluoromethanesulfonyl)imide, hexafluorophosphate, perchlorate, tetrafluoroborate and dicyanamide on the solubility of the ferrocene was investigated. The solution chemistry of the ferrocene species was studied, in order to understand the mechanism of solubility enhancement. Finally, the electrochemical performance of these ionized ferrocene species was evaluated and shown to have excellent cell efficiency and superior cycling stability.
Similar content being viewed by others
Introduction
Redox flow batteries (RFBs) are rechargeable electrochemical energy storage devices that utilize the redox chemistry of at least one soluble redox couple for energy conversion between electrical energy and chemical energy1,2,3. The positive and negative electrolytes are stored in two separate reservoirs and pumped through the cell compartments where energy is converted. The cell architecture provides RFBs with a unique virtue of decoupled energy capacity and power output, which gives RFBs tremendous design flexibility to meet the different requirements for energy–driven or power–oriented applications. The excellent modularity and scalability makes RFBs especially suitable for large-scale stationary applications such as grid stabilization and renewable integration. Although great progress has been made in the past years, conventional aqueous RFB systems are generally limited by the water electrolysis on cell voltage and by the low solubility of electro-active materials, resulting in generally low energy density systems (less than 25 Wh L−1 in practical applications)4,5. In contrast, non-aqueous electrolytes offer a wider electrochemical window. The main advantage of adopting non-aqueous electrolytes in flow batteries is to achieve higher cell voltage aiming at high energy density storage. Organic compounds are considered as electroactive materials due to the tremendous diversity of the active species and redox mechanisms and the possibility of incorporating multiple electron transfers via functionality control in the molecular design. In addition, the structure can be synthetically tailored to improve the solubility which in turn results in a higher system energy density6,7. Therefore, non-aqueous RFBs have attracted considerable attention recently and a number of redox chemistries have been proposed and investigated1,8.
Among these efforts, we implemented a novel concept: a hybrid lithium-organic non-aqueous RFB (LORFB) that used the Li metal as the anode and an organic electroactive material as the cathode9,10,11. In a synergistic form of RFB and Li-ion battery, this cell design takes advantage of the high energy density of the Li metal and the extremely low redox potential of the Li/Li+ couple to harvest a high cell voltage. This LORFB concept was first illustrated by using a structurally tailored anthraquinone (AQ) catholyte, which produced an energy efficiency of 82% and a discharge energy density of ~25 Wh L−1 using a static cell12. However, although improved from almost zero to 0.25 M in the electrolyte, the solubility of the modified AQ was still low, limiting the energy density that could be harvested from the system. Also, many other reported nonaqueous RFBs were characterized at the electroactive material concentrations of no more than 0.1 M13,14,15,16,17. Such low concentrations generally result in low energy density RFB systems that cannot fully compete with the aqueous RFB counterparts. Therefore, there is a compelling need to search for organic electroactive candidates having higher redox potentials and solubilities.
Here we report a new LORFB based on the ferrocene/ferrocenium (i.e. Fc/Fc+) redox couple as the catholyte material hence abbreviated as the Li|Fc system. Ferrocene-containing compounds, mostly polymers, have been extensively investigated in solid-state Li-ion batteries due to the relatively high redox potential of the ferrocene (~3.4 V versus Li/Li+) and stable redox characteristics6,7. Yu et al. published two reports showing impressive performance from ferrocene–based Li batteries, in a different architecture, though in one case, it is not clear whether the ferrocene is functionalized or not18,19. However, the use of the pristine ferrocene as an active species in flow battery is limited by its low solubility in the supporting electrolytes (e.g. a saturation concentration of 0.04 M in the electrolyte of 1.2 M LiTFSI in an organic solvent mixture). Therefore, a polar tetraalkylammonium ionic moiety was incorporated into the ferrocene structure (i.e. ionized Fc compounds) in an attempt to improve the solubility of the chromophore in polar supporting electrolytes. We investigate the effect of a series of counter anions (A−) affixed to the tetraalkylammonium group on properties such as solubility, melting point, bond energies and cell performance. The counterion containing analogs synthesized and studied include bis(trifluoromethanesulfonyl)imide (TFSI−), hexafluorophosphate (PF6−), perchlorate (ClO4−), tetrafluoroborate (BF4−) and dicyanamide (N(CN)2−). The solution chemistry of these ionized Fc electrolytes was studied using nuclear magnetic resonance (NMR) analysis and density functional theory (DFT) to understand the mechanism of solubility enhancement. Finally, the electrochemical performance of these ionic-Fc compounds in their corresponding Li|Fc flow battery was evaluated to demonstrate excellent cell efficiency and superior cycling stability.
Results and Discussion
Synthesis of Ionic-Fc analogs
According to Fig. 1, all the ionic ferrocene compounds were synthesized from a common bromide salt intermediate (Fc1N112-Br) that was synthesized from commercially available N,N-dimethyl(aminomethyl)ferrocene (Fc1N11) via nucleophilic substitution with bromoethane in acetonitrile. The subsequent ionic Fcs were prepared in decent yields via an ion exchange reaction of the bromide intermediate with the lithium or sodium salt of the desired counter anions including TFSI−, ClO4−, BF4−, N(CN)2− and PF6−. The ion exchange reactions were performed in an organic, polar, anhydrous solvent, with the exception of the TFSI− and N(CN)2− analogs which were performed in de-ionized water. Due to the stability of LiTFSI in water, the ease of removing the LiBr salt byproduct and ease of isolation of the final product in near quantitative yield, water was the perfect solvent for this synthesis. In the case of the dicyanamide analog, the sodium dicyanamide salt was too insoluble in a suitable organic solvent, therefore the reaction was performed in water, followed by extraction with dichloromethane. The other ion exchange reactions were performed in anhydrous organic solvents such as acetonitrile, methanol or acetone because the starting lithium or sodium salts were too hygroscopic and/or prone to hydrolysis and decomposition in water (for BF4− and PF6−).
Solubility study
The catholyte used in the Li|Fc system contains an ionic-Fc and the corresponding lithium salt (LiA where A is the counter anion) in a carbonate mixture solvent of ethylene carbonate (EC)/propylene carbonate (PC)/ethyl methyl carbonate (EMC) at a weight ratio of 4:1:5. The solubility of the ionic-Fc analogs was evaluated first in the EC/PC/EMC solvent system, followed by the more relevant 1.2 M LiA supporting electrolytes in EC/PC/EMC as they were the actual medium in the Li|Ionic-Fc cells. The results are summarized in Table 1.
The pristine ferrocene has a low solubility in both solvent and electrolyte, reaching saturation at 0.2 M in EC/PC/EMC and at only 0.04 M in 1.2 M LiTFSI in EC/PC/EMC. It is obvious that incorporation of the ionic pendants resulted in a significant increase in the solubility of all the Fc chromophores, although they exhibited quite different solubility values. In EC/PC/EMC, the Fc1N112-N(CN)2 had the highest solubility of 2.08 M, followed by 1.73 M for Fc1N112-TFSI, 1.71 M for Fc1N112-PF6, 0.63 M for Fc1N112-ClO4 and 0.40 M for Fc1N112-BF4, respectively. The solubilities of all ionic-Fcs in the corresponding supporting electrolytes (1.2 M LiA in EC/PC/EMC) were reduced compared with those in the solvent: 0.85 M for Fc1N112-TFSI, 0.65 M for Fc1N112-PF6, 0.38 M for Fc1N112-ClO4 and 0.38 M for Fc1N112-BF4, respectively. The solubility of Fc1N112-N(CN)2 in the electrolyte of Li N(CN)2 in EC/PC/EMC was not measured due to the lack of a commercial source of Li N(CN)2. As previously stated, the solubility of the electroactive materials in the electrolyte is critically important for a RFB system to achieve high energy density delivery. The solubility improvement will result in a significant increase in the system energy density of the Li|Ionic-Fc flow battery.
The goal of this work is not only to determine the most soluble candidate of the Ionic-Fc series for non-aqueous RFB application, but also to understand the solvation mechanism and factors that lead to the solubility increase of the Ionic-Fc molecules. In a simplified model, the solvation phenomenon can occur in two different ways: (1) the cation and anion fragments of the Ionic-Fc are separated by the solvent molecules; or (2) the Ionic-Fc molecule as a whole is surrounded by the solvent molecules such that the entire pair is solvated. One study by Fox et al.20 suggests that the ionic liquid is not strongly interacting with the solvent (acetonitrile or PC), but rather stays closely associated in solution. Similar work by the same group shows a strong aggregation behavior of ionic liquids dependent on the solvent used21. Therefore, in depth studies of density functional theory (DFT) calculations and solution NMR characterizations were performed in order to gain a comprehensive understanding of the solvation mechanism.
DFT Study
The solubility of an ionic salt critically depends on two competing interactions namely the ion–solvent and cation–anion (i.e. ion pair) interactions which transpires as solvation phenomena. The solubility of the Fc1N112+ - anion salt in EC/PC/EMC solvent mixture clearly showed an explicit counter anion dependent behavior, indicating varying degree of cation-anion interaction strengths (i.e. affinity between specific anion and Fc quaternary ammonium cation). To verify this hypothesis, the characteristics of the Fc1N112 cation-anion bonds in terms of affinity (i.e. electronic binding energy ΔE) and ion-pair distance (i.e. shortest distance between Fc1N112+ and anion) was analyzed using DFT calculations. The geometry of the Fc1N112+ cation-anion pairs was optimized under open-shell electron configuration using the hybrid B3LYP function with a slater type TZ2P all electron basis set implemented in the ADF 2013 package. Although such a single pair gas phase calculation excluded the highly correlated ion- solvent mixture interactions and temperature effects, it qualitatively captures the relative affinity between specific anion and Fc quaternary ammonium cation.
Figure 2 shows the fully optimized geometry of the Fc1N112-PF6 molecule. To extract the correct bond distance between these complex molecules, the electron density profile was calculated on the optimized structure. For the unsymmetrical Fc1N112+ cation the positive charge density is mainly concentrated on the nitrogen atom, while for the PF6− anion the negative charge density is nearly equally distributed among the fluorine atoms. Therefore, the typical cation-anion bond distance should be the shortest distance between the cation nitrogen atom and the anion in the molecule. This was verified by the good agreement between the calculated bond distance of 4.08 Å and the single crystal structure experimental value of 4.20 Å (Supplemental Information) of the Fc1N112-TFSI molecule. Then, the cation-anion affinity (i.e. electronic energy differences ΔE) was calculated by the difference between the electronic bonding energy of the ion pair and the isolated cation/anion, i.e. ΔE = (ion − pair)BE − (cation)BE − (anion)BE.
Figure 3 shows the single pair electronic energy differences ΔE and ion-pair distance between the Fc1N112+ cation and various anions. The BF4− and ClO4− based ion pair molecules show large bonding energies along with shorter bonding distances, indicating a lower propensity for solvation. On the other hand, the TFSI− and PF6− anions show relatively lower affinity and positions at relatively longer distances with the Fc1N112+ cation, suggesting anions more likely to be solvated. The N(CN)2− anion has an intermediate affinity and ion-pair distance which lies between the above two groups of anions. In general, the trend of the calculated affinities and ion-pair distances of these Ionic-Fcs matches well with that of their solubility data, which provides a potential qualitative explanation of the solubility difference among the various Ionic-Fcs. However, the Fc1N112-N(CN)2 exhibits an extremely high solubility in the carbonate solvent mixture although it has intermediate bonding energy and bonding distance. The reasons for this anomalous behavior need to be studied further. Based on this study, we confirm that the high solubility of Fc1N112-TFSI and Fc1N112-PF6 could be a consequence of the relatively weaker affinity between the TFSI− or PF6− anion with the Fc1N112+ cation, which allows for the solvent insertion between the ion pair. Our DFT calculations suggest a solvation mechanism where the ion-pair retention in solution is less likely and the ions are surrounded by solvent molecules and subsequently experience higher solubility. The DFT calculations do not take into account the ion-solvent mixture interactions as the system would become very complex (our solvent has three components) and results difficult to interpret, however, we do not exclude the possibility of this solvation mechanism.
NMR studies
The NMR studies aim to explore solvent-ion interactions in a 0.2 M solution of EC/PC/EMC with a weight ratio of 4:1:5. In order to decouple the potential interaction of TMS with the concentrated ferrocene-based analogs solutions, we conducted co-axial 1H NMR with an external tetramethylsilane (TMS) reference. At this concentration, we followed the response of the solvent peaks to the different ionic-Fc environments.
The substrates were dissolved in EC/PC/EMC (4:1:5) at concentrations of 0.2 M with an external TMS reference (co-axial tube) in a neat solvent system and the mixtures were subjected to 1H NMR tests. The proton shifts of the solvent remain the same for EC, PC and EMC regardless of the ionic-Fc present, which indicates that in the context of NMR scale (i.e., milliseconds to seconds) and at a relatively low concentration (0.2 M) the chemical environment of the solvent molecules does not change. Although a higher concentration would have been beneficial to gain more conclusive insights, we chose the concentration of 0.2 M because it was the highest concentration at which all analogs were soluble. This experiment suggests that no fixed molecular bond or interaction between any of the solvent molecules and the ionized molecules occurs at this concentration. Furthermore, this indicates that the solvation mechanism at low concentrations is one in which the entire Ionic-Fc is surrounded by the solvent molecules and there is no preferential interaction with any part of the Ionic-Fc. If there are long range interactions between the solvent and the ionic pair, it is not detectable by NMR. Although all counter ions have different degrees of polarizability, the interactions may be too small to be detected by NMR. This supports the hypothesis that the Ionic-Fc remains generally bound, not allowing preferential solvent interactions with the cation or anion. The extent of bonding between the anion and the cation of each analog differs with the nature of the respective anion and its polarizability and it is reflected in the low concentration 1H NMR in deuterated chloroform, Fig. 4. Slight shifts and change in splitting patterns are observed in each cation, as a response to the different environments of various counter anions.
Another explanation of the different solvation lies in the shape and size of the overall ionic pair and how the different counter anions affect the crystal lattice. This can be easily probed by comparing melting points of all the analogs. Indeed, the melting point trend (see Table 1) in all analogs but PF6−, which was not measured, follows the same trend observed in the solubility of the respective species: DCA− has the lowest melting point at 81.5 °C, followed closely by TFSI− at 85 °C, followed by BF4− at 148.5 °C then closely by ClO4− at 153 °C.
In conclusion the solvation behavior appears to be a complex phenomenon and several factors and mechanisms may play in concert. DFT calculations show an energy and ion-pair distance trend that agrees with experimental solvation data; however, they do not take into account the various solvents surrounding the molecule. Melting point data suggests that the energy of the crystal lattice plays a role in the solvation of the Ionic-Fcs and this data is also in agreement with the solubility data. Co-axial 1H NMR however, given the 0.2 M concentration limitation and the inherent inability of detect long-range molecular interactions, suggests that solvents do not preferentially interact with any of the Ionic-Fcs.
Electrochemical performance
The electrochemical behavior of the four Ionic-Fcs was studied as the catholyte materials in the hybrid Li|Ionic-Fc batteries (the N(CN)2-analog was not evaluated due to the unavailability of LiN(CN)2). Figure 5 shows the cyclic voltammetry (CV) curves of the four Ionic-Fcs and the pristine Fc in 1.2 M corresponding LiA electrolytes in EC/PC/EMC (4:1:5, by wt.), where the LiTFSI salt was used for the unmodified Fc.
The pristine Fc exhibited the oxidation and reduction peaks at 3.38 V and 3.15 V versus Li/Li+, respectively, yielding an average redox potential of 3.26 V. Incorporation of the ionic pendants shifts the Fc species to higher redox potentials by ~0.2 V, which is considered to be closely associated with the electron withdrawing effect of the quaternary ammonium functionality. The counter anions in the ionic arms have a relatively minor effect on the electrochemical properties of the ionic-Fc analogues, resulting in similar electrochemical reversibility and redox potentials. The redox reactions of Fc1N112-ClO4 and Fc1N112-PF6 are slightly more reversible than the other two. The four ionic-Fcs, exhibit an average redox potential of 3.49 V for Fc1N112-BF4, 3.47 V for Fc1N112-TFSI, 3.45 V for Fc1N112-ClO4 and 3.44 V for Fc1N112-PF6, versus Li/Li+ as listed in Table 1. The positive shift of the redox potential and the improved solubility function in synergy to increase the energy density of the Li|Ionic-Fc cells. For example, the Li|Ionic-Fc employing the Fc1N112-TFSI as the catholyte has a theoretical energy density of 79 Wh L−1 that is twice as high as that of the aqueous mixed-acid VRB system22.
The cell performance of the Li|Ionic-Fc batteries was investigated in static cell configurations with the Ionic-Fc concentrations at their nominal solubilities in 1.2 M LiA in EC/PC/EMC. The coin cells were galvanostatically cycled in the constant current mode at a current density of 1.5 mAcm−2 between 3 and 4 V. Reliable protection of the solid electrolyte interphase (SEI) on the Li surface is crucial for lithium metal-based rechargeable batteries, because continuous dendrite growth during repeated charge/discharge cycles may cause internal short of the cell which is one of the major battery safety hazards23,24. Fluoroethylene carbonate (FEC) has been recognized as an effective electrolyte additive for Li, carbon and Si anodes to form good quality SEI layers and then enhance battery performance25. Therefore, a 5 wt% of FEC was used in each of the Ionic-Fc catholytes.
Among the four Ionic-Fc analogs, the static cells of Li|Fc1N112-TFSI and Li|Fc1N112-ClO4 systems produced excellent long-term performance over extended cycling. Figure 6a,b show the cycling efficiency and the specific volumetric capacity of the Li|Fc1N112-TFSI and the Li|Fc1N112-ClO4 static cells, respectively. Both Li|Fc1N112-TFSI and Li|Fc1N112-ClO4 static cells exhibited remarkably stable performance and high cell efficiencies which were maintained over 500 cycles. The Li|Fc1N112-TFSI cell produced 95% Coulombic efficiency (CE), 92% voltaic efficiency (VE) and 88% energy efficiency (EE), while the Li|Fc1N112-ClO4 cell produced even higher efficiencies with 98% CE, 95% VE and 93% EE. These cell efficiencies are significantly higher than those reported in most non-aqueous redox chemistries26,27,28. The Li|Fc1N112-TFSI cell delivered an energy density of ~28 Wh L−1 that is comparable to practical mixed-acid VRB systems22. The initial discharge energy density of the Li|Fc1N112-ClO4 cell was ~13 Wh L−1 due to the relatively low concentration of the Fc1N112-ClO4 in its electrolyte, but it is still comparable to the aqueous iron-vanadium system. The lower CE of the Li|Fc1N112-TFSI cell was due to the higher cycling capacity (~8 vs ~3.7 Ah L−1) leading to longer per cycle time and more self-discharge reactions when tested at the same current density. Excellent capacity retention was achieved for both systems and an average capacity loss of 0.04% and 0.02% per cycle was observed for the Li|Fc1N112-TFSI and Li|Fc1N112-ClO4 cells, respectively, throughout the 500 cycles. Such a performance exceeds many other reported non-aqueous RFB systems which suffer from serious degradation15,16,29. The excellent cyclability is attributed to the stabilized SEI layer contributing to the effective suppression of the self-discharge reactions between the charged species at the anode and cathode compartments.
In contrast, the Fc1N112-PF6 and the Fc1N112-BF4 produced poor cyclability and the coin cells using these two compounds failed after only a few cycles. The failure mechanism is speculated to be due to the poor solubility of the charged species, i.e., the Ionic-ferrocenium salts, or more specifically PF6−-Fc+1N+112-PF6− and BF4−-Fc+1N+112-BF4−, in the electrolytes. In an effort to prove this hypothesis, all of the coin cells were disassembled and examined after cycling. Solid precipitation was observed in the Li|Fc1N112-PF6 and Li|Fc1N112-BF4 cells but not in the Li|Fc1N112-TFSI and Li|Fc1N112-ClO4 cells. Further research is warranted to identify the source of the precipitation and elucidate the battery failure mechanism.
Conclusions
The transition from aqueous to non-aqueous battery systems provides great benefits but it is not without challenges. Appropriate active materials can achieve higher energy and power densities and efficiencies. The use of organic electroactive species offers both opportunities and challenges for the design and synthesis of novel materials with tunable solubilities, redox potentials and activities. Our present work was focused on understanding the effect of the counter anion on the solubility and performance of a series of ferrocene containing ionic species. The data demonstrates a wide range of solubility for the various anions studied N(CN)2− > TFSI− > PF6− > ClO4− > BF4− from 2.08 M to 0.40 M in EC:PC:EMC (4:1:5), while the electrochemical performance shows a different trend. Both Li|Fc1N112-TFSI and Li|Fc1N112-ClO4 static cells exhibited remarkably stable performance and high cell efficiencies which were maintained over 500 cycles. The Li|Fc1N112-TFSI cell produced 95% CE, 92% VE and 88% EE, while the Li|Fc1N112-ClO4 cell produced even higher efficiencies with 98% CE, 95% VE and 93% EE. In contrast, the Fc1N112-PF6 and the Fc1N112-BF4 produced poor cyclability and the coin cells using these two compounds failed after only a few cycles. In conclusion, a high solubility of the active species is required but not sufficient in assessing battery performance. The solubility and stability of the charged species formed as a result of redox chemistry will need to also be assessed. Although the electrochemical performance of several ferrocene ionic species is quite remarkable, there is still a need for better understanding of long-term stability of organic species in their charged and neutral states to optimize performance.
Methods
Synthesis
All reagents and starting materials were purchased from Sigma-Aldrich and used as received unless noted otherwise. All reactions were run in an inert atmosphere in oven dried glassware. Experimental details can be found in the Supporting Information. Mass spectrometry: A one milligram of sample was dissolved into 2 mL of methanol. The sample was electrosprayed at 3 microliters per minute into a LTQ-Orbitrap (Thermo Fischer Scientific. The electrospray emitter (150 micrometers OD and 20 micrometers ID at tip) was custom made using the protocol described by Kelly et al.30. Data acquisition was an average of 100 scans with a FT mass resolution setting of 30000. X-Ray: Single crystals of Fc1N112-TFSI were grown by slow solvent evaporation of a saturated solution of methylene chloride. A suitable crystal was selected and mounted on a nylon loop with Paraton-n oil on a Bruker APEX-II CCD diffractometer. The crystal was kept at 120 K during data collection. Using Olex231, the structure was solved with the olex2.solve structure solution program using Charge Flipping and refined with the ShelXL32 refinement package using Least Squares minimization. The structure is shown in Figure S7 while crystal data, bond distances and angles are shown in Tables S1-S2 in the SI.
NMR measurements
1H and 13C NMR were performed on a Varian 500 MHz NMR spectrometer equipped with a Z axis-gradient 5 mm HCN probe. 1H NMR co-axial experiments of concentrated samples (0.2 M) were externally referenced to tetramethylsilane (TMS) to avoid TMS interaction with ferrocene, while regular low concentration 1H NMR spectra were referenced to internal TMS.
DFT calculations
Quantum chemistry calculations were carried out using the Amsterdam Density Functional (ADF-2013) program. The hybrid-GGA based Becke, three-parameter, Lee-Yang-Parr DFT function (B3LYP) with Grimme dispersion correction (D3) and TZ2P (triple Z, 2 polarization functions, all electron) basis set function is used. All basis sets and preceding calculations were done with the Slater type functional implemented in the ADF program for both geometry optimization and bonding energy calculation.
CV tests
Lithium salts (LiTFSI, LiPF6, LiBF4, LiClO4), carbonate solvents (EC, PC, EMC) and the FEC additive in battery grade were ordered from BASF Battery Materials (Independence, OH) and used as received. The solvent mixtures and electrolytes were prepared inside an argon-filled MBraun glove box (Stratham, NH) with H2O and O2 levels both less than 1 ppm. The CV curves were run between 2.5 and 4 V on a CHI760D Potentiostat (CH Instruments, Austin, TX) at a scan rate of 50 mV s−1 with a 2-mm diameter Pt working electrode, a Li metal counter electrode and a Li metal reference electrode. The three-electrode cells for the CV tests were placed inside the MBraun glove box.
Static cell tests
The performance of Li|Ionic-Fc batteries was tested in 2325-type coin cells. The cell configuration employed a Li foil (99.9%, Alfa Aesar) as the anode, a 2.5-mm-thick graphite felt (SGL Carbon Group, Germany) as the cathode substrate and a polyethylene-based microporous separator in between. The active area of the coin cell was 1.6 cm2. The graphite felt was saturated with an Ionic-Fc catholyte solution (~0.2 mL) with the concentration at its nominal solubility in a 1.2 M LiA supporting electrolyte in EC/PC/EMC (4:1:5, by wt.). The catholyte contained a 5 wt% FEC to protect the SEI on the Li surface. The galvanostatic charging/discharging cycling of the coin cells was performed on an Arbin BT-2000 battery tester (Arbin Instruments, College Station, TX) at 1.5 mA cm−2 in a voltage range of 3–4 V.
Additional Information
How to cite this article: Cosimbescu, L. et al. Anion-Tunable Properties and Electrochemical Performance of Functionalized Ferrocene Compounds. Sci. Rep. 5, 14117; doi: 10.1038/srep14117 (2015).
References
Wang, W. et al. Recent Progress in Redox Flow Battery Research and Development. Adv. Funct. Mater. 23, 970–986, 10.1002/adfm.201200694 (2013).
Yang, Z. G. et al. Electrochemical Energy Storage for Green Grid. Chem. Rev. 111, 3577–3613, 10.1021/Cr100290v (2011).
Dunn, B., Kamath, H. & Tarascon, J. M. Electrical Energy Storage for the Grid: A Battery of Choices. Science 334, 928–935, 10.1126/science.1212741 (2011).
Leung, P. et al. Progress in redox flow batteries, remaining challenges and their applications in energy storage. RSC Adv. 2, 10125–10156, 10.1039/C2ra21342g (2012).
Skyllas-Kazacos, M., Chakrabarti, M. H., Hajimolana, S. A., Mjalli, F. S. & Saleem, M. Progress in Flow Battery Research and Development. J. Electrochem. Soc. 158, R55–R79, 10.1149/1.3599565 (2011).
Liang, Y. L., Tao, Z. L. & Chen, J. Organic Electrode Materials for Rechargeable Lithium Batteries. Adv. Energy Mater. 2, 742–769, 10.1002/aenm.201100795 (2012).
Song, Z. P. & Zhou, H. S. Towards sustainable and versatile energy storage devices: an overview of organic electrode materials. Energy Environ. Sci. 6, 2280–2301, 10.1039/C3ee40709h (2013).
Sung-Hee, Shin, Yun, S.-H. & Moon, S.-H. A review of current developments in non-aqueous redox flow batteries: characterization of their membranes for design perspective. RSC Adv. 3, 9095–9116, 10.1039/C3RA00115F (2013).
Wang, W., Xu, W., Li, L. & Yang, Z. Hybrid Energy Storage Systems Utilizing Redox Active Organic Compounds. US Pat. US20130266836 A1 (2012).
Wei, X. L. et al. TEMPO-Based Catholyte for High-Energy Density Nonaqueous Redox Flow Batteries. Adv. Mater. 26, 7649–7653, 10.1002/adma.201403746 (2014).
Wei, X. L. et al. Towards High-Performance Nonaqueous Redox Flow Electrolyte Via Ionic Modification of Active Species. Adv. Energy Mater. 5, 10.1002/Aenm.201400678 (2015).
Wang, W. et al. Anthraquinone with tailored structure for a nonaqueous metal-organic redox flow battery. Chem. Commun. 48, 6669–6671, 10.1039/C2cc32466k (2012).
Wang, Y. R., Wang, Y. G. & Zhou, H. S. A Li-Liquid Cathode Battery Based on a Hybrid Electrolyte. Chem Sus Chem 4, 1087–1090, 10.1002/cssc.201100201 (2011).
Lu, Y. H. & Goodenough, J. B. Rechargeable alkali-ion cathode-flow battery. J. Mater. Chem. 21, 10113–10117, 10.1039/C0jm04222f (2011).
Brushett, F. R., Vaughey, J. T. & Jansen, A. N. An All-Organic Non-aqueous Lithium-Ion Redox Flow Battery. Adv. Energy Mater. 2, 1390–1396, 10.1002/aenm.201200322 (2012).
Li, Z. et al. Electrochemical Properties of an All-Organic Redox Flow Battery Using 2,2,6,6-Tetramethyl-1-Piperidinyloxy and N-Methylphthalimide. Electrochem. Solid-State Lett. 14, A171–A173, 10.1149/2.012112esl (2011).
Liu, Q. H. et al. Non-aqueous chromium acetylacetonate electrolyte for redox flow batteries. Electrochem. Commun. 12, 1634–1637, 10.1016/j.elecom.2010.09.013 (2010).
Zhao, Y. et al. Sustainable Electrical Energy Storage through the Ferrocene/Ferrocenium Redox Reaction in Aprotic Electrolyte. Angew. Chem. Int. Ed. 53, 11036–11040, 10.1002/anie.201406135 (2014).
Ding, Y., Zhao, Y. & Yu, G. A membrane-free ferrocene-based high-rate semiliquid battery. Nano Lett. 15, 4108–4113, 10.1021/acs.nanolett.5b01224 (2015).
Fox, E. T., Paillard, E., Borodin, O. & Henderson, W. A. Physicochemical Properties of Binary Ionic Liquid-Aprotic Solvent Electrolyte Mixtures. J. Phys. Chem. C 117, 78–84, 10.1021/Jp3089403 (2013).
Borodin, O. et al. Influence of Solvent on Ion Aggregation and Transport in PY15TFSI Ionic Liquid–Aprotic Solvent Mixtures. J. Phys. Chem. B 117, 10581–10588, 10.1021/jp406541e (2013).
Li, L. Y. et al. A Stable Vanadium Redox-Flow Battery with High Energy Density for Large-Scale Energy Storage. Adv. Energy Mater. 1, 394–400, 10.1002/aenm.201100008 (2011).
Aurbach, D., Zinigrad, E., Cohen, Y. & Teller, H. A short review of failure mechanisms of lithium metal and lithiated graphite anodes in liquid electrolyte solutions. Solid State Ionics 148, 405–416, 10.1016/S0167-2738(02)00080-2 (2002).
Bruce, P. G., Freunberger, S. A., Hardwick, L. J. & Tarascon, J. M. Li-O-2 and Li-S batteries with high energy storage. Nat. Mater. 11, 19–29, 10.1038/Nmat3191 (2012).
Zhang, S. S. A review on electrolyte additives for lithium-ion batteries. J. Power Sources 162, 1379–1394, 10.1016/j.jpowsour.2006.07.074 (2006).
Hamelet, S., Larcher, D., Dupont, L. & Tarascon, J. M. Silicon-Based Non Aqueous Anolyte for Li Redox-Flow Batteries. J. Electrochem. Soc. 160, A516–A520, 10.1149/2.002304jes (2013).
Mun, J. et al. Non-Aqueous Redox Flow Batteries with Nickel and Iron Tris(2,2′-bipyridine) Complex Electrolyte. Electrochem. Solid-State Lett. 15, A80–A82, 10.1149/2.033206esl (2012).
Duduta, M. et al. Semi-Solid Lithium Rechargeable Flow Battery. Adv. Energy Mater. 1, 511–516, 10.1002/aenm.201100152 (2011).
Shinkle, A. A., Sleightholme, A. E. S., Griffith, L. D., Thompson, L. T. & Monroe, C. W. Degradation mechanisms in the non-aqueous vanadium acetylacetonate redox flow battery. J. Power Sources 206, 490–496, 10.1016/j.jpowsour.2010.12.096 (2012).
Kelly, R. T. et al. Chemically etched open tubular and monolithic emitters for nanoelectrospray ionization mass spectrometry. Anal. Chem. 78, 7796–7801, 10.1021/Ac061133r (2006).
Dolomanov, O. V., Bourhis, L. J., Gildea, R. J., Howard, J. A. K. & Puschmann, H. OLEX2: a complete structure solution, refinement and analysis program. J. Appl. Crystallogr. 42, 339–341, 10.1107/S0021889808042726 (2009).
Sheldrick, G. M. & Thorn, A. Restrained anisotropic refinement with SHELXL. Acta Cryst. A64, 112–122 (2008).
Acknowledgements
The authors would like to acknowledge financial support primarily from the U.S. Department of Energy’s (DOE’s) Office of Electricity Delivery and Energy Reliability (OE) (under Contract No. 57558) and support from the Laboratory-Directed Research and Development Program (LDRD) of the Pacific Northwest National Laboratory (PNNL). PNNL is a multi-program national laboratory operated by Battelle for DOE under Contract DE-AC05-76RL01830. Funding Sources: U.S. Department of Energy’s (DOE’s) Office of Electricity Delivery and Energy Reliability (OE) (under Contract No. 57558) and the Laboratory-Directed Research and Development Program (LDRD) of the Pacific Northwest National Laboratory (PNNL) under Contract DE-AC05-76RL01830 provided financial support for this work.
Author information
Authors and Affiliations
Contributions
The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Cosimbescu, L., Wei, X., Vijayakumar, M. et al. Anion-Tunable Properties and Electrochemical Performance of Functionalized Ferrocene Compounds. Sci Rep 5, 14117 (2015). https://doi.org/10.1038/srep14117
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep14117
This article is cited by
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.