Oxygen vacancies (VO) effects on magnetic ordering in Eu0.5Ba0.5TiO3−δ (EBTO3−δ) thin films have been investigated using a combination of experimental measurements and first-principles density-functional calculations. Two kinds of EBTO3−δ thin films with different oxygen deficiency have been fabricated. A nuclear resonance backscattering spectrometry technique has been used to quantitatively measure contents of the VO. Eu0.5Ba0.5TiO3 ceramics have been known to exhibit ferroelectric (FE) and G-type antiferromagnetic (AFM) properties. While, a ferromagnetic (FM) behavior with a Curie temperature of 1.85 K has been found in the EBTO3−δ thin films. Spin-polarized Ti3+ ions, which originated from the VO, has been proven to mediate a FM coupling between the local Eu 4f spins and were believed to be responsible for the great change of the magnetic ordering. Considering the easy formation of VO, our work opens up a new avenue for achieving co-existence of FM and FE orders in oxide materials.
Multiferroics, or materials that simultaneously possess two or more ferroic orders [ferroelectric, (anti-) ferromagnetic, and ferroelastic], have recently returned to the forefront of materials research due to their rich physical properties and potential applications in data storage, sensors, and spintronics1,2. From an application point of view, multiferroics with ferromagnetic-ferroelectric (FM-FE) orders are more attractive and highly desired3. However, very few exist in nature due to the intrinsic contradiction in existence between the FM and FE ordering within a single phase4. On the other hand, antiferromagnetic-ferroelectric (AFM-FE) materials are more commonly found, such as rare-earth manganites (RMnO3) and the well known BiFeO35,6,7,8,9,10,11. It is fundamentally interesting and technologically important to develop FM-FE materials by changing magnetic ordering of the AFM-FE materials. An additional driving force and a deep understanding of physical phenomenon underlying the transformation are needed to realize this purpose.
In oxides, oxygen vacancies (VO) have been approved to be intrinsic defects and are believed to have a critical impact on their properties12. Coey et al reported that VO play a key role in obtaining room temperature FM in HfO2, ZnO, TiO2, and other non-magnetic oxide systems13,14,15,16. It has also been proven that VO are useful in increasing Curie temperature and enhancing magnetic moment of EuO thin films17,18,19,20. Furthermore, VO are known to induce a room temperature ferroelectricity in SrTiO3 thin films21,22,23. Despite the fact that the VO are effective to manipulating the magnetic and ferroelectric properties of oxides, little attention has been focused upon the VO effects on multiferroicity in single-phase materials. A natural question to ask is: are the VO able to change the magnetic ordering from AFM to FM in multiferroic materials?
The beginning of the present work is to choose a suitable material to verify the above idea. In recent years, divalent europium oxidation materials showed attractive functionalities, rendering them subjects of intensive studies. Compared to the 0.05 μB/Fe in BiFeO324, rare-earth Eu2+ ion has seven unpaired and localized 4f electrons, which resulted in a large magnetization of 7 μB/Eu and sometimes is coupled with electrical properties. For example, Rushchanskii et al confirmed that Eu0.5Ba0.5TiO3 (EBTO) ceramics exhibit FE (Curie temperature TC ~ 213 K) and G-type AFM (Néer temperature TN ~ 1.9 K) properties25. And coupling between magnetism and dielectric properties was predicted in Eu1−xBaxTiO3 materials26. Furthermore, as we discussed earlier, the VO have been proven to be useful in manipulating the magnetic orders of divalent Eu ions in EuO thin films. Therefore, EBTO is a potential material for the present study, based on the nature of a large magnetization of 7 μB/Eu and the AFM-FE orders. In addition, if we can alter magnetism of EBTO thin films by doping VO and at the same time still preserve good ferroelectricity, it will certainly make EBTO itself appealing in fundamental research and practical applications. In the present work, we experimentally confirmed that the magnetic ordering in oxygen-deficient Eu0.5Ba0.5TiO3−δ (EBTO3−δ) thin films has been transformed from AFM to FM. First-principle calculations indicated that spin-polarized Ti3+ ions, which originated from the VO, mediated a FM coupling between the local Eu 4f spins. Considering the easy formation of VO, our work presented an effective technique to achieve co-existence of FM and FE orders in oxide materials.
The EBTO3−δ thin films were fabricated on (001) oriented SrTiO3 (STO) and Nb-doped SrTiO3 (Nb-STO) substrates by pulsed laser deposition (PLD). Following the deposition, parts of the thin films were post-annealed under a reducing atmosphere to increase amount of the VO. Typical X-ray diffraction (XRD) θ–2θ scans confirmed that the EBTO3−δ is preferentially oriented along the c axis (not shown). In order to reveal the microstructure of the EBTO3−δ thin films, cross-sectional transmission electron microcopy (TEM) measurements were conducted. A low magnification bright-field TEM image (Fig. 1a) shows that the interface is clean without any obvious interface reaction or intermixing. In the view area, the film is continuous without any obvious grain boundaries, confirming the 2D growth of the film. The corresponding selected area diffraction (SAD) image taken from the interface area is shown as inset of Fig. 1a. The distinguished diffraction dots from the film and substrate indicate the high quality epitaxial growth. The out-of-plane and in-plane orientation relationships have been determined to be (001)EBTO|| (001)STO and EBTO||STO, respectively. A high resolution TEM (HRTEM) image (Fig. 1b) confirmed the excellent heteroepitaxial relation with an atomically sharp interface. Similarly no obvious misfit dislocations have been found along the interface, which is consistent with the SAD observation.
To quantitatively analyze stoichiometry and oxygen concentration of the EBTO3−δ thin films, a nuclear resonance backscattering spectrometry (NRBS) technique was used. The advantage of NRBS over traditional Rutherford backscattering spectrometry (RBS) is its sensitivity to selectively measure oxygen in the EBTO3−δ film on an oxygen-rich substrate, such as STO in our experiment27,28. The NRBS was performed using a 3.043 MeV 4He+ analyzing beam and the backscattering particles were detected by a surface barrier silicon detector located at 167° from the beam direction. At such a beam energy, the He scattering from the heavier elements (Eu, Ba, and Ti) in the film is still Rutherford, therefore the Eu:Ba:Ti ratios can be determined reasonably well by fitting the experimental spectra data with the commercial Rutherford Universal Manipulation Program (RUMP) software29. Within the uncertainty of the measurements (~5%), we determined that our EBTO3−δ thin films do have an Eu:Ba:Ti ratio of 1:1:2.
After the atomic ratios of cations were determined, a nuclear scattering and reaction simulation package (SIMNRA) was used to fit the nuclear resonant oxygen scattering spectra (not shown)30. To minimize uncertainties related to the nuclear scattering cross section and the incident beam energy, a bare STO substrate as a standard reference was measured and analyzed all together along with our EBTO3−δ thin films. Table 1 shows the measured concentration of europium and oxygen in the as-deposited and annealed EBTO3−δ thin films. From the Eu concentration, the ideal oxygen concentration in the stoichiometric Eu0.5Ba0.5TiO3 thin films is estimated to be 5.22 × 1017 and 5.88 × 1017 at./cm2 for as-deposited and annealed thin films respectively. By comparing the measured and the ideal oxygen concentration, we have calculated that there are 4.0% oxygen deficiency (δ ≈ 0.120) in the as-deposited film and 5.1% oxygen deficiency (δ ≈ 0.153) in the annealed film. In other words, the VO were introduced into the EBTO3−δ thin films and the content of the VO were increased by post-annealing under a reducing atmosphere.
Because of the charge compensation, the existence of VO should induce changes in the valance states of cations. To quantify these changes, we investigated the valance states of the EBTO3−δ thin films by using X-ray photoemission spectroscopy (XPS). We found that the valence states of Eu and Ba ions are remained in divalent (not shown), while those of Ti ions have been changed. Because VO act as n-type dopants, the Ti3+ and Ti4+ formal valences should coexist in the EBTO3−δ thin films. Figure 2 shows Ti 2p core-level photoemission spectrum of (a) the as-deposited and (b) the annealed EBTO3−δ thin films with peak fittings. Compared with previous results, the peaks at a binding energy around 459.42 eV and 465.45 eV can be assigned as Ti4+, with peaks around 457.81 eV and 463.53 eV corresponding to Ti3+ 31,32. By comparing the peak area, the content of Ti3+ was calculated to be 27.1% and 33.4% in the as-deposited and annealed thin films respectively. On the other hand, by assuming two free carries for each VO33, the ratio between the content of Ti3+ and that of VO (δ) will be 2:1. Therefore, the ideal content of Ti3+ for the as-deposited and annealed thin films should be 24.0% and 30.6% respectively (see table 1). These results are well fitted with the calculated values and further confirmed that VO were doped into the thin films. In addition, the fact that the change of the valence states only occurred in Ti cations has been verified by first-principles density-functional calculations and will be discussed in more details later.
To investigate VO effects on magnetic properties of the EBTO3−δ thin films, temperature and magnetic-field dependences of magnetization were investigated using a superconducting quantum interface device magnetometer (SQUID). Figure 3 shows the temperature dependent magnetization curves. The measurements were performed under zero-field-cooled (ZFC) and field-cooled (FC) conditions with an external magnetic field of 100 Oe applied parallel to the films surface. The EBTO ceramics antiferromagnetically ordered at 1.9 K25. However, the magnetization on both ZFC and FC curves increased monotonically with decreasing temperature until 0.9 K and tend to be saturated at the lowest temperature, which is a typical FM behavior. The derivative of the magnetization and the reciprocal susceptibility as a function of temperature are shown as insets of Fig. 3a and 3b. It has been found that the derivative of the magnetization shows a sharp valley, in other words the magnetizations increase quickly, at around 1.85 K. In addition, the Curie-Weiss law fitting of the reciprocal susceptibilities at high temperatures intersects the temperature axis at 1.85 K. Both of these results then confirmed the FM ordering in the EBTO3−δ thin films with a Curie temperature of 1.85 K34. Figure 4 shows the field dependent magnetization curves at 1, 1.5, and 5 K. It has been found that, at 1 and 1.5 K, the magnetization increased sharply at low fields and then approached saturation quickly. The large susceptibility at low fields (shown as insets of Fig. 4a and 4b) is also an evidence for the FM ordering below 1.85 K. The saturation magnetizations, measured for the as-deposited and annealed thin films at 1 K, are around 6.75 μB/Eu and 6.85 μB/Eu respectively. These values are close to the ideal magnetic moment of the Eu2+ ions (7 μB/Eu). It should be noticed that the susceptibility at low fields and the value of the magnetization in the annealed thin films are larger than those in the as-deposited thin films, which obviously originates from the enhanced content of VO. In order to further prove the FM ordering of the EBTO3−δ thin films below 1.85 K, magnetic hysteresis loops were measured at 0.5 K (Supplementary Figure S1). Hysteretic behavior is observed with a coercivity of 30 Oe. The combination of these results proved that the EBTO3−δ thin films become a ferromagnet with a Curie temperature of 1.85 K, which is different from bulk EBTO – G-type antiferromagnet25.
Many theoretical studies of vacancy-induced magnetism in non-magnetic SrTiO3 have been performed using ab initio calculations35,36. To investigate the fundamental physics underlying the origin of the FM ordering in the EBTO3−δ thin films, we calculated total energies of EBTO3−1/8 with both FM and AFM orderings from first-principles density-functional theory. FM ordering is found to be 13.1 meV/Eu favorable. Figure 5 shows the spin-density and local density of states (DOS) in the EBTO3−1/8: (a) and (c) for FM ground state; (b) and (d) for AFM state. As shown in DOS of local Ti ions, the occupancy of 3d orbital indicates the appearance of Ti3+, in good agreement with the XPS measurements. Furthermore, the existence of VO does not change the valence state of Eu, since almost fully occupied 4f 7 states are found, which is similar to the pristine EuTiO3 and confirmed by the SQUID and XPS measurements37. On the other hand, as shown in Fig. 5 (a) and (c), the development of large local spin moment at Ti sites makes the FM ground state differ significantly from the AFM state. The local magnetic moment at Ti3+ ions right above or under VO is around 0.24 μB and the dz2 dominates. While for other Ti3+ ions, the local orbital is either dxy or dxz/dyz. Magnetic moment at Eu site does not change from the pristine case with a local magnetic moment of around 7 μB. Judging from Fig. 5, it is the appearance of spin-polarized Ti3+ that mediates the FM coupling between the localized Eu 4f spins. It should be noticed that with increase of the content of VO, e.g. Eu0.5Ba0.5TiO3−1/4, the FM ordering is still found to be energetically favorable than the AFM orderings (see Table 2). These results verified that the EBTO3−δ thin films do show FM ordering, which originated from the ordering of the spin of Eu 4f electrons mediated by the spin-polarized Ti3+ ions.
This article is mainly concerned about the magnetic ordering, but we also investigated the FE properties of the annealed EBTO3−δ thin films by measuring dielectric constant as a function of temperature and room-temperature hysteresis loop using piezoresponse force microscopy (PFM). It's surprised to find out that a peak in dielectric constant versus temperature curves (shown as Fig. 6) is clearly seen above room temperature. Moreover, a room-temperature hysteresis loop measured by PFM was shown as inset of Fig. 6. These results suggest that the FE Curie temperature of the annealed EBTO3−δ thin films is above room temperature, which is significantly higher than that of bulk EBTO (~213 K). The investigation on mechanism of the enhancement on the FE Curie temperature is presently in progress.
In summary, two kinds of EBTO3−δ thin films with different content of VO were fabricated. By using NRBS, SQUID, and first-principles calculations, we demonstrated that the magnetic ordering of oxygen-deficient EBTO3−δ thin films has been changed from AFM to FM. The transformation originated from the VO induced Ti 3d electrons, which mediated the FM coupling between the local Eu 4f spins. The results are significant as they proved that VO are effective to manipulating magnetic ordering in multiferroic materials. Considering the easy formation of VO, the present work presents a methodology to enhance multiferroicity in the EBTO3−δ thin films and this method holds great promise for other oxide materials.
The EBTO3−δ thin films were fabricated on (001) oriented SrTiO3 (STO) and Nb-doped SrTiO3 (Nb-STO) substrates by pulsed laser deposition (PLD) using a pulsed excimer laser (Lambda Physik, 248 nm, 3 Hz, 2 J/cm2). A high-density EBTO ceramic pellet was used as the target. The details of the preparation of EBTO ceramics can be found in elsewhere25. Deposition temperature was 700°C and oxygen pressure was 1 × 10−4 Pa with the purpose of doping VO. Following the deposition, parts of the thin films were annealed at 1000°C under a flowing gas of 95 vol% Ar + 5 vol% H2 for 10 hours to increase amount of the VO. The film thickness, revealed by cross-sectional transmission electron microcopy (TEM), was 100–150 nm.
The crystal structures were characterized by X-ray diffraction (XRD, Rigaku K/Max) and TEM (FEI Tecnai F20 analytical microscope). Nuclear resonance backscattering spectrometry (NRBS) was performed on Los Alamos National Laboratory. A He+ beam energy of 3.043 MeV was used to quantitatively analyze stoichiometry and oxygen concentration in the EBTO3−δ thin films. The valence states were investigated by X-ray photoemission spectroscopy (XPS) at PHI5000 VersaProbe.
Magnetic measurements were performed on EBTO3−δ/STO thin films using a superconducting quantum interface device magnetometer (SQUID) equipped with a He3 insert (Quantum Design, MPMS-XL). The electrical properties were measured using a Pt/EBTO3−δ/Nb-STO heterostructure. The dielectric constants were investigated using an Agilent 4294A Impedence Analyzer. The measurements were performed at selected temperatures in a Linkam Scientific Instruments HFS600E-PB4 system. Room-temperature piezoresponse force microscopy (PFM) was measured using PFM mode of Asylum Research MFP-3D-SA atomic force microcopy.
Our ab initio calculations are performed using the accurate full-potential projector-augmented wave (PAW) method, as implemented in the Vienna ab initio simulation package (VASP)38,39. They are based on density-functional theory with the generalized gradient approximation (GGA) in the form proposed by Perdew, Burke, and Ernzerhof (PBE)40. The on-site Coulomb interaction is included in the GGA + U approach with effective U = 4 eV for Eu 4f orbitals41. A plane-wave cutoff of 600 eV is used throughout and the convergence criteria for energy is 10−6 eV. PAW potentials are used to describe the electron-ion interaction with 17 valence electrons for Eu (4f75s25p66s2), 10 for Ba (5s25p66s2), 10 for Ti (3p63d24s2), and 6 for O (2s22p4). In our calculations, ions are relaxed toward equilibrium positions until the Hellman-Feynman forces are less than 1 meV/A. In addition, lattice constants are optimized until the stress is less than 0.001 Pa. The fully optimized lattice constant of Eu0.5Ba0.5TiO3 stems from an initial cubic lattice, from which the atoms shift a little from their high symmetric positions. Total energies are calculated and compared between different magnetic and A-site atomic arrangements.
The authors acknowledge the support of the National Natural Science Foundation of China (Grant No. 11004145, 11274237, 11134012, 11104193, 51228201, and 51202153), the Natural Science Foundation of Jiangsu Province under Grant No. SBK201021263, the Scientific Research Foundation for the Returned Overseas Chinese Scholars (State Education Ministry of China), and the Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD). Partial support for thin film characterization was also provided by the Center for Integrated Nanotechnologies, a DOE nanoscience user facility, jointly operated by Los Alamos and Sandia National Laboratories. The TEM work at Texas A&M University is funded by the US National Science Foundation (NSF-0846504).