Abstract
The control of the density and type of line defects on two-dimensional (2D) materials enable the development of new methods to tailor their physical and chemical properties. In particular, mirror twin boundaries (MTBs) on transition metal dichacogenides have attracted much interest due to their metallic state with charge density wave transition and spin-charge separation property. In this work, we demonstrate the self-assembly of 2,3-diaminophenazine (DAP) molecule porous structure with alternate L-type and T-type aggregated configurations on the MoSe2 hexagonal wagon-wheel pattern surface. This site-specific molecular self-assembly is attributed to the more chemically reactive metallic MTBs compared to the pristine semiconducting MoSe2 domains. First-principles calculations reveal that the active MTBs couple with amino groups in the DAP molecules facilitating the DAP assembly. Our results demonstrate the site-dependent electronic and chemical properties of MoSe2 monolayers, which can be exploited as a natural template to create ordered nanostructures.
Similar content being viewed by others
Introduction
Two-dimensional (2D) transition metal dichalcogenides (TMDs) have great potential for future device applications due to their novel electronic and optical properties1. These properties are often strongly modified by defects2,3,4,5,6, which are inevitable in the growth process. As one of the most common defects, grain boundaries (GBs), have been widely observed in monolayer TMDs synthesised by bottom-up approaches such as chemical vapour deposition (CVD) and molecular beam epitaxy (MBE)7,8,9,10. Bandgap tunability has been observed in single-layer MoS2 GBs11, and mid-gap states reported at low-angle GBs in single-layer WSe212. Other irregular or regular line defects with metallic properties containing 4-, 5-, and 8-membered rings have also been reported in MoS2, WS2, and WSe2 in contrast to the semiconducting nature of their pristine 2D crystals13. More recently, mirror twin boundaries (MTBs) in atomically thin MoSe2 films have attracted increasing attention due to the direct observation of one-dimensional (1D) charge density waves (CDW) along the MTBs at low temperatures14. Dense MTB networks are observed in MBE-grown MoSe2 or MoTe2 monolayers on graphene (and also graphite) or MoS2 surfaces, and their atomic structures and electronic properties have been investigated by scanning probe microscopy and photoemission spectroscopy15,16. Such metallic line defects are usually unfavourable for carrier/energy transport and optical applications. However, they are often catalytically active due to their large density of states (DOS)17,18,19,20, and may potentially be used as templates for self-assembly of molecules21,22, as site-selective adsorption behaviours have been previously reported in 2D materials with a variety of surface inhomogeneities, including edge sites18, atomic defects23, moiré patterns24,25, intrinsical 1 H/1 T patterns26, and so on.
This work elucidates the atomic structures and electronic properties of MTBs in single-layer (SL) MoSe2 grown on graphite, and investigates their chemical reactivity with organic molecules. Using a combination of ultrahigh vacuum scanning tunnelling microscopy/spectroscopy (STM/STS) and non-contact atomic force microscopy (nc-AFM) techniques, we image the electronic modulations in the (quasi) periodic MTB structures, revealing their metallic nature and lower surface potential (work function). 2,3-diaminophenazine (DAP), an amino derivative of phenazine with promising luminescence, electrochemical and biochemical applications27,28,29,30, is selected for investigating the template effect of the dense MTB network. We observed the formation of a porous structure of DAP molecules that map onto the wagon-wheel patterns of the underlying MoSe2. First-principles calculations further suggest that the active amino groups in the DAP molecules play a critical role in this preferential adsorption behaviour, as charge redistribution occurs mainly close to the amino groups. By comparing the adsorption energies of different adsorption configurations, the configuration with the DAP molecule adsorbed parallel to and on the top of the MTBs is found to be the most stable, in agreement with the experimental results. This study demonstrates that organic molecule self-assembly can be facilitated by domain boundaries in epitaxial 2D TMDs. These defective TMDs and porous organic molecule structures have potential applications in site-selective catalysis, or as molecular sensors or flexible organic optoelectronic devices.
Results
Atomic structure and electronic properties of MBE-grown MoSe2 films on HOPG
Figure 1a shows a typical large-scale STM image of a MoSe2 film grown by MBE on a highly oriented pyrolytic graphite (HOPG) substrate. The whole MoSe2 surface is decorated by triangle patterns. A close-up STM image of these patterns is displayed in Fig. 1c, and the boundary appears as two bright parallel rows at negative sample voltages (occupied states). Hence the single layer MoSe2 film is comprised of a mosaic of triangle single-crystalline domains, where neighbouring domains are separated by inversion domain boundaries (IDBs) or mirror twin boundaries (MTBs). These triangle patterns are non-uniform in size, with sizes varying from several to tens of nanometres (nm). Fig. 1b shows the statistical distribution of the triangle domain size (represented by the side lengths of the MTB equilateral triangles) of more than 300 triangles in the samples studied. It is found that these MoSe2 triangle domains are mostly in the size range of 1.5–4.0 nm, which corresponds to 5–12 lattice constants of MoSe2 (a0 = 3.3 Å as determined by nc-AFM measurements). The smaller triangle domains tend to pack in the centre of the MoSe2 islands while the larger domains are observed closer to the island edges.
The detailed atomic structures of the MTBs are further studied by atomically resolved nc-AFM, which eliminates interference from electron density of states imaged in the STM topological images. The nc-AFM measurements were carried at 77 K with a native tungsten tip without CO functionalization. Figure 1d shows the nc-AFM image of the same area as the STM image in Fig. 1c with high resolution. In this large-scale AFM image (30 × 30 nm2), the triangle MoSe2 domains are uniform in contrast, and the MTBs are easily distinguishable as line defects with darker contrast. In frequency-shift nc-AFM images which are sensitive to the tip-sample separation as well as the local electron densities, positive ∆f is generally a result of short-range Pauli repulsive interactions, while negative ∆f is due to long-range attractive van der Waals interactions and/or electrostatic forces31. Therefore, the observed darker contrast with negative frequency shift in the MTB regions might be due to their relatively lower height and/or rich electron densities in comparison to the MoSe2 triangle domains.
The precise atomic structures are clearly revealed in the high-resolution nc-AFM image of Fig. 1e. The corresponding atomistic model is displayed in Fig. 1f. Based on the nc-AFM working principles and by comparing with reported atomic structures of MoSe2 triangle domains14,32, the hexagonal lattices with bright contrast (orange) are attributed to the top-layer Se atoms, which are closer to the tip and generate repulsive forces. The dark features (blue) are attributed to the lower-lying Mo atoms, which are further from the tip and experience attractive forces. The MTBs consist of a Se atomic row sandwiched by two Mo atomic rows connecting two adjacent inverted MoSe2 triangle domains with Se-edges (red dashed line). The darker contrast in the MTB regions is due to higher density of Mo atoms, where each Se atom is bound to four Mo atoms instead of three, and thus giving rise to stronger attractive forces. The darkest contrast around the intersection of the wagon-wheel patterns is attributed to Mo vacancies. The separation between Se-edges of two neighbouring inversion domains is ~0.59 nm, close to √3aMoSe2, as marked by a white arrow in Fig. 1e. This is consistent with previously reported values from theoretical calculations, transmission electron microscopy results33,34, and nc-AFM studies with CO-functionalized tips14. The atomic structures confirmed by the STM/nc-AFM measurements facilitate a better understanding of the modulation of the electronic structures in the MTBs, which will be discussed below.
Figure 2a shows a highly-resolved STM topological image of the SL-MoSe2 surface, where the MTBs appear as bright protrusions with periodic intensity undulations due to charge density wave (CDW) modulation at low temperature14. From the lateral profile shown in Fig. 2b, the periodicity is determined to be 1.00 ± 0.03 nm, equivalent to ~3 lattice constants of MoSe2, consistent with that reported in the literature14,16,32,34. Typical STS spectra taken on the pristine MoSe2 triangle domain and the MTBs are shown in Fig. 2c. The red curve clearly reveals semiconductor characteristics of the single-layer MoSe2 away from the MTBs, with an electronic bandgap of 2.0 ± 0.1 eV15. In contrast, the blue dI/dV spectrum acquired on the MTB shows distinct electronic states inside the bandgap. In particular, a “V” shaped feature around the Fermi level (0 V) (highlighted by a rectangle in Fig. 2c) is observed, indicating the metallic nature of the MTBs5,9,15,32,35. Thus, the mosaic MoSe2 surface is composed of alternating semiconducting and metallic regions, which might enable unique site-selective behaviour at the nanoscale18,26, e.g., for adsorption, catalysis, and so on.
Another key parameter that determines the surface electronic properties is the local work function or surface potential, which can be measured with high spatial resolution by field emission resonances (FERs) at the STM tip-sample junction36,37. FERs are also known as Gundlach oscillations38 in the Fowler-Nordheim tunnelling regime. When the applied bias is large enough to lift the tip Fermi level above the sample vacuum level, hydrogen-like electronic resonances occur in the vacuum junction between the tip and the sample39,40,41. As thus, the first resonance peak of the FERs measured by STS (e.g. dI/dV and dz/dV) is related to the local work function of the underlying sample. Fig. 2d shows the FER spectra measured at different regions of MoSe2 as well as the clean HOPG substrate for comparison. On the bare HOPG (black dashed curve), the first FER peak appears at 4.35 ± 0.05 eV, in a good agreement with the work function of HOPG in the range of 4.4–4.8 eV42. Interestingly, the triangle MoSe2 domains (red curve) yield their first FER at 4.88 ± 0.05 eV, while the MTB regions (blue curve) first resonate at 4.63 ± 0.05 eV, indicating a shift of ~0.25 eV towards lower energy compared to that of the adjacent pristine triangle domain.
Formation of DAP porous structure on MoSe2 surface
To explore the possible site-specific properties, we deposited an amino derivative of phenazine, 2,3-diaminophenazine (DAP), onto the MoSe2 surface. The molecular structure of DAP is shown in the inset of Figure 3a (Supplementary Fig. 1 in supplementary information).The structure of the DAP molecule is essentially planar with two active amino-groups at one end. Upon deposition of a sub-monolayer of DAP molecules, the supramolecular structure networks formed are obvious and distinguishable, but their sizes and shapes are not uniform as shown in Fig. 3a, b. Fig. 3a suggests that the DAP molecules mainly adsorb on the edges of the second and the centre of the first layer MoSe2 at lower coverage. The adsorbed DAP area expands to fill the whole ML-MoSe2 surface with increasing coverage as shown in Fig. 3b. The porous structure sizes can reach hundred nanometres (Supplementary Fig. 2) and are only limited by the MoSe2 island sizes. Figure 3c displays a typical DAP pore region. The shapes of the pores are slightly distorted from perfect hexagons. Statistical analysis of the pore sizes in Fig. 3d reveals the distribution of pore size is mainly in the range of 1.5–4.0 nm. This coincides with the size distribution of the MoSe2 triangle domains (the red dashed line), although the peak has a small offset due to the offset of MTBs from the centre of the wagon-wheel patterns (most of the two opposite MTBs move several atomic lattices relative to each other, seen Fig. 1e, f). These results suggest that the DAP assembled structures map directly onto the wagon-wheel patterns of the underlying MoSe2 substrate.
Figure 4a shows a high-resolution STM image of the DAP nanoporous structure with a partially uncovered MoSe2 surface. Each DAP molecule appears as a dumbbell-shape feature with slightly asymmetric contrast along the long axis direction. This is understandable due to its asymmetric molecular structure (amino-groups at one end). By a statistical analysis of the orientation distribution of the DAP molecules with respective to the MTBs (Supplementary Fig. 4), it is found that the DAP molecules oriented with their long axes parallel to the MTBs are dominant. The alignment of the molecular orientations with the three high symmetry directions of MoSe2 indicating a significant substrate effect43.
In the porous structure, two typical packing configurations are observable, namely linear configurations (L-type) and triangle trimer configurations in a head-to-tail arrangement (T-type) highlighted by the green circles and red triangles in Fig. 4a, b respectively. We have analysed ~1000 DAP molecules to understand the distributions of the L-type and T-type configurations (the statistical histogram is shown in Supplementary Fig. 5). The percentage of L-type configurations is slightly higher than that of the T-type. The L-type configuration preferentially forms on the MTB regions, while the T-type configuration preferentially forms on the MoSe2 triangle domains. A typical hexagonal DAP porous nanostructure shown in Fig. 4c mimics the features of the MoSe2 wagon-wheel pattern, and the corresponding configuration model is shown in Fig. 4d. The hexagonal DAP porous structure form surrounding the intersection of wagon-wheel patterns by alternatingly absorbing the L-type and T-type configurations. Due to the irregularities in the hexagonal MTB network and the size mismatch between the DAP T-configurations (2.1 ± 0.1 nm) and the MoSe2 triangle domains (1.5–4.0 nm), the size and shape of DAP pores are also non-uniform, and display a small distribution offset from the MoSe2 MTB networks as shown in Fig. 3d.
The porous DAP molecular structure is distinctly formed by a site-specific self-assembly: preferential T-type adsorption on the defect-free MoSe2 domains and L-type on the MTBs, while leaving the MTB intersections empty. With increasing molecular coverage, a close-packed phase will emerge coexisting with the loose-packed porous phase (Supplementary Fig. 6). The evolution of the DAP packing structure with annealing temperature have also been studied. We find that the DAP porous nanostructures do not become more ordered after thermal annealing, but desorb above 90 °C (Supplementary Fig. 7). The close-packed configuration starts to desorb at 140 °C. This porous nanostructure is not observable for the DAP molecules grown on graphite and Au(111) substrates (Supplementary Figs. 8 and 9). Therefore, the formation of the hexagonal DAP porous structures is steered by the underlying MTBs and the relatively weak selective adsorption, and is attributed to the subtle competition between the relatively weak DAP–substrate and DAP–DAP interactions.
The formation mechanism of the DAP porous structure
To gain further insight into the formation mechanism of the DAP porous structure, theoretical calculations based on density functional theory (DFT) were performed to investigate the templating effect of the MTB network. It is noted that the electronic structure of MoSe2 can be tuned by external influences such as strain, defects, or substrates35,44,45,46,47. Here, the presence of MTBs in the MoSe2 single-layer reduces the bonding coordination of Mo atoms from 6 to 4, resulting in modified electronic and chemical properties. First-principles calculations show that the electronic structure in the MTB region (Fig. 5a) is significantly different from the defect-free region far away from the MTB (Fig. 5b), consistent with the STS measurements in Fig. 2. The unoccupied electronic states of Mo d orbitals (mainly dzx) in the MTB spread into the band gap, forming metallic states, as shown in Fig. 5a. These slightly delocalised Mo dzx orbitals enhance the interaction with the adsorbed molecules, rendering the MTB more chemically active. This reactivity guides the DAP self-assembly on the MTBs as observed in the STM experiments.
Indeed, compared with DAP on pristine MoSe2 single-layer, the interaction between DAP and the MTB is enhanced, as evidenced by the shorter interfacial spacing, stronger charge redistribution, and larger adsorption energy. As Fig. 5c shows, the spacing (have) between the DAP benzene ring and MTB with a parallel orientation (P site) is ~2.98 Å, beyond the chemical bonding range. In contrast in Fig. 5e, a larger spacing of 3.22 Å is obtained for DAP on defect-free MoSe2 (D site), indicating a physical adsorption stabilised by van der Waals (vdW) forces. From the side-views of the optimised configurations, it is worth noting that the two amine groups of the DAP molecule absorbed atop the MTB region both bend downwards (hamino ~ 2.33 Å), while those on the defect-free region have one amino group pointing upwards and the other pointing downwards (hamino ~ 2.61 Å) (Supplementary Fig. 11). Furthermore, the visualised charge density difference in Fig. 5d–f show different charge redistributions in the DAP molecule and MoSe2. The charge redistribution is more pronounced at the DAP amino groups, resulting in a slightly tilted DAP molecule with a smaller spacing between amino groups and MoSe2. Calculations also show that the charge transfer at the P site is slightly stronger (~0.07e per molecule) than at the D site (~0.05e per molecule) (Supplementary Fig. 12). As a consequence of the shorter interfacial spacing and the larger charge transfer, the adsorption energy of the DAP molecule adsorbed on the MTB (−1.38 eV) up to 0.16 eV is larger than that on the defect-free MoSe2. These results suggest that the MTB on MoSe2 are chemically active, facilitating the adsorption of DAP. Furthermore, the amino group is more reactive than the benzene ring, and forms the active site that electrostatically interacts with the metallic MTB.
Figure 6 shows the angle-dependence of the DAP adsorption energy on the MTB. As shown in the inset in Fig. 6, angle ɵ defines the orientation between the long axis of the DAP molecule and the MTB axis (a axis). It can be seen that the DAP molecule adsorbed parallel (P site) to the MTB is the most energetically favourable, with the lowest binding energy of −1.38 eV. This is because the electronic overlap between DAP and MoSe2 is the largest in this configuration, leading to stronger adsorption. It explains why the L-type configuration is the more observed pattern on the MTBs (in Fig. 4d). Interestingly, the adsorption energy for DAP perpendicular (ɵ = 90o) to the MTB (or V site, as shown in Supplementary Fig. 11) has the second lowest value (−1.29 eV). The adsorption energy of −1.22 eV at ɵ = 45o is equivalent to the value of the D site. This trend can be explained by the chemical reactivity of the DAP amino-groups. When ɵ is >45o, the amino-groups detach from the MTBs and the DAP adsorption becomes stable again. The relatively small energy difference (<0.16 eV) between the most stable configuration and the others is consistent with the molecular orientation distribution observed in Fig. 4 and Supplementary Fig. 4. It should be noted that the chemical reactivity of MTBs is weaker compared with other defects in the MoSe2 single-layer such as Se vacancies, due to the absence of dangling bonds. This is why the MTBs only weakly affect the orientation of DAP molecules, but the interaction is sufficient to guide DAP assembly to form hexangular nano-pores.
Finally, the formation of the DAP porous structure, particularly the coexistence of T-type and L-type building configurations in Fig. 4, can be understood from a comparison of their formation energies (Ebind). From the optimised models shown in Fig. 4e, f, we can see that both configurations are stabilised by the formation of intermolecular hydrogen bonding. That is, the C–N···H distance between the neighbouring DAP molecules is in the range of 2.5–2.9 Å (Supplementary Fig. 10), indicating weak hydrogen-bonding48. In the absence of a substrate, DFT calculations suggest that DAP molecules in the T-type configuration (Ebind = -0.21 eV) is more stable than that in the L-type configuration (Ebind = -0.12 eV) due to the stronger hydrogen bonding interactions, which is in contrast to the slightly higher distribution of the L-type configurations analysed in Supplementary Fig. 5. Hence, the self-assembly of DAP molecules on the MTB network is determined by a subtle balance of intermolecular interactions in competition with the substrate templating effect. When the DAP molecules absorb on the defect-free regions, the T-type configuration is preferred because of the stronger intermolecular interactions. On the other hand, when the molecules diffuse to the MTBs, they bind parallel to the chemically active boundaries.
In conclusion, we demonstrate the self-assembly of a DAP molecular nano-porous structure on the dense MTB network surface of an MBE-grown MoSe2 film. DAP molecules form a hexagonal pores structure that maintains the same symmetry as the MoSe2 substrate as a result of the electronic and chemical inhomogeneity of the substrate surface. The DAP molecules aggregate into linear configurations at the edge of the hexagonal pores along the MTBs, and trimer triangle configurations form at the corner of the hexagonal pores on the defect-free MoSe2 domains. DFT calculations reveal that the DAP amino groups and the metallic MTB are the main active interaction sites. Thus, the formation of the DAP porous structure is guided by the MoSe2 MTB network together with intermolecular hydrogen interactions. This work offers a novel pathway to atomically precise molecular nano-patterning of 2D TMD surfaces, and provides a platform to explore the local chemical properties of MoSe2.
Methods
MoSe2 film preparation
The MoSe2 samples were prepared by molecular beam epitaxy (MBE) on commercial HOPG substrate in a home-built ultra-high vacuum (UHV) system. The growth chamber has a base pressure of 10−9 mbar. The HOPG substrates were cleaved in air and transferred into the loadlock chamber as quick as possible to minimise contamination, and then outgassed for 3 h at 550 °C before sample growth. Molecular beams of Se (99.99%, Sigma-Aldrich) and Mo (99.99%, Goodfellow) were generated from a standard Knudsen cell (MBE-Komponenten) and a commercially available e-beam cell (Focus), respectively. The source flux was calibrated by a flux monitor (quartz crystal monitor). The flux ratio between Mo and Se was at least 1:10, and the film deposition rate was 1.0 ML per hour. The sample temperature during growth was 400 °C. For subsequently ex situ STM measurements using a separate Scienta-Omicron LT-STM system, an amorphous Se capping layer was deposited on the sample at room temperature before it was taken out of the vacuum. This Se capping layer was then thermally desorbed in the Omicron preparation chamber prior to LT-STM measurements.
DAP molecule depositon
DAP (95%, Sigma-Aldrich) molecules were deposited from a Kundsen effusion cell in the loadlock chamber (base pressure is 10−8 mbar) of the Scienta-Omicron system. A typical deposition rate used was ~0.03 ML/min. Here, one monolayer (ML) refers to one full monolayer DAP in closed packed configuration. The deposition rate of DAP was calibrated by large-scale STM images. During the deposition, the MoSe2 substrates were held at room temperature and the samples were subsequently transferred in situ to the STM chamber for analysis.
STM/ nc-AFM imaging
STM/nc-AFM and STS measurements were performed at 77 K in an Scienta-Omicron UHV system interfaced to a Nanonis controller equipped with and STM/qPlus sensor. Electrochemically etched tungsten tips were used, and bias voltages were applied to the sample. For STM imaging, the constant current mode was adopted and the tunnelling current was in the range of 60–200 pA. For STS measurements, the lock-in technique was used, with a modulation voltage of 30 mV and frequency of 963 Hz. For nc-AFM imaging, the constant-height mode with an oscillation amplitude of 1 nm was used to record the frequency shift (∆f) of the qPlus resonator (sensor frequecy f0 ≈ 24 kHz, Q ≈ 8000). All the STM/STS data were analysed and rendered using WSxM software49.
DFT calculation
The first-principles calculations were performed using density-functional theory (DFT) based Vienna ab initio simulation package (VASP 5.4.4.18), in which Perdew-Burke-Ernzerhof (PBE) exchange-correlation functionals and the projector augmented wave (PAW) potentials were used. The cut-off energy for the plane wave expansion was set to 500 eV. We have calculated pristine MoSe2 monoalayer, MoSe2 single-layer with MTB, DAP molecule, DAP molecule on the perfect MoSe2 surface, and DAP molecule on the surface of MoSe2 with MTB, where the corresponding first Brillouin zone was sampled by using Γ-centred 12 × 12 × 1, 12 × 1 × 1, 1 × 1 × 1, 3 × 3 × 1, and 3 × 1 × 1 k-point meshes, respectively. A vacuum layer >15 Å was applied normal to the surface of MoSe2 single-layer. For the interfaces between DAP molecular and MoSe2, van der Waals (vdW) correction was included by using Grimme’s DFT-D3 method. In all calculations, the criterion for energy and force convergence was set to 1.0 × 10−6 eV and 0.01 eV/Å, respectively. The adsorption energy for DAP molecule on MoSe2 single-layer was estimated by:
where EMoSe2+DAP is the total energy of the hybrid structures for DAP on MoSe2, and EDAP and EMoSe2 are the total energies of isolated DAP molecule and MoSe2, respectively. The charge redistrution of DAP molecular on MoSe2 was estimated by the integration of in-plane averaged charge density difference and Bader charge analysis.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable requests.
References
Manzeli, S., Ovchinnikov, D., Pasquier, D., Yazyev, O. V. & Kis, A. 2D transition metal dichalcogenides. Nat. Rev. Mater. 2, 17033 (2017).
Hu, Z. et al. Two-dimensional transition metal dichalcogenides: interface and defect engineering. Chem. Soc. Rev. 47, 3100–3128 (2018).
Zhou, W. et al. Intrinsic structural defects in monolayer molybdenum disulfide. Nano Lett. 13, 2615–2622 (2013).
Huang, P. Y. et al. Grains and grain boundaries in single-layer graphene atomic patchwork quilts. Nature 469, 389–392 (2011).
Komsa, H.-P. & Krasheninnikov, A. V. Engineering the electronic properties of two-dimensional transition metal dichalcogenides by introducing mirror twin boundaries. Adv. Electron. Mater. 3, 1600468 (2017).
Liu, X., Zhang, Z., Wang, L., Yakobson, B. I. & Hersam, M. C. Intermixing and periodic self-assembly of borophene line defects. Nat. Mater. 17, 783–788 (2018).
van der Zande, A. M. et al. Grains and grain boundaries in highly crystalline monolayer molybdenum disulphide. Nat. Mater. 12, 554–561 (2013).
Najmaei, S. et al. Vapour phase growth and grain boundary structure of molybdenum disulphide atomic layers. Nat. Mater. 12, 754–759 (2013).
Ma, Y. et al. Metallic twin grain boundaries embedded in MoSe2 monolayers grown by molecular beam epitaxy. ACS Nano 11, 5130–5139 (2017).
Diaz, H. C., Ma, Y., Chaghi, R. & Batzill, M. High density of (pseudo) periodic twin-grain boundaries in molecular beam epitaxy-grown van der Waals heterostructure: MoTe2/MoS2. Appl. Phys. Lett. 108, 191606 (2016).
Huang, Y. L. et al. Bandgap tunability at single-layer molybdenum disulphide grain boundaries. Nat. Commun. 6, 6298 (2015).
Huang, Y. L. et al. Gap states at low-angle grain boundaries in monolayer tungsten diselenide. Nano Lett. 16, 3682–3688 (2016).
Lin, Z. et al. Defect engineering of two-dimensional transition metal dichalcogenides. 2D Materials 3, 022002 (2016).
Barja, S. et al. Charge density wave order in 1D mirror twin boundaries of single-layer MoSe2. Nat. Phys. 12, 751–756 (2016).
Liu, H. et al. Dense network of one-dimensional midgap metallic modes in monolayer MoSe2 and their spatial undulations. Phys. Rev. Lett. 113, 066105 (2014).
Ma, Y. et al. Angle resolved photoemission spectroscopy reveals spin charge separation in metallic MoSe2 grain boundary. Nat. Commun. 8, 14231 (2017).
Huang, Y. L. et al. The organic-2D transition metal dichalcogenide heterointerface. Chem. Soc. Rev. 47, 3241–3264 (2018).
Tuxen, A. et al. Size threshold in the dibenzothiophene adsorption on MoS2 nanoclusters. ACS Nano 4, 4677–4682 (2010).
Chhowalla, M. et al. The chemistry of two-dimensional layered transition metal dichalcogenide nanosheets. Nat. Chem. 5, 263–275 (2013).
Eftekhari, A. Molybdenum diselenide (MoSe2) for energy storage, catalysis, and optoelectronics. Appl. Mater. Today 8, 1–17 (2017).
Cui, X., Troadec, C., Wee, A. T. S. & Huang, Y. L. Surface nanostructure formation and atomic-scale templates for nanodevices. ACS Omega 3, 3285–3293 (2018).
Tian, G. et al. Effects of monolayer Bi on the self-assembly of DBBA on Au(111). Surf. Sci. 665, 89–95 (2017).
Park, J. H. et al. Defect passivation of transition metal dichalcogenides via a charge transfer van der Waals interface. Sci. Adv. 3, e1701661 (2017).
Zhang, H. G. et al. Assembly of iron phthalocyanine and pentacene molecules on a graphene monolayer grown on Ru(0001). Phys. Rev. B 84, 245436 (2011).
Zhou, H. et al. Template-directed assembly of pentacene molecules on epitaxial graphene on Ru(0001). Nano Res. 6, 131–137 (2013).
Lin, X. et al. Intrinsically patterned two-dimensional materials for selective adsorption of molecules and nanoclusters. Nat. Mater. 16, 717–721 (2017).
Mekler, V. M. & Bystryak, S. M. Application of o-phenylenediamine as a fluorogenic substrate in peroxidase-mediated enzyme-linked immunosorbent assay. Anal. Chim. Acta 264, 359–363 (1992).
Doyle, R. P., Kruger, P. E., Mackie, P. R. & Nieuwenhuyzen, M. Phenazine-2,3-diamine. Acta Cryst. C57, 104–105 (2000).
Huang, S., Wang, L., Huang, C., Su, W. & Xiao, Q. Amino-functionalized graphene quantum dots based ratiometric fluorescent nanosensor for ultrasensitive and highly selective recognition of horseradish peroxidase. Sens. Actuat B Chem. 234, 255–263 (2016).
Tian, B. et al. Amino group enhanced phenazine derivatives as electrode materials for lithium storage. Chem. Commun. 53, 2914–2917 (2017).
Giessibl, F. J. Advances in atomic force microscopy. Rev. Mod. Phys. 75, 949 (2003).
Lehtinen, O. et al. Atomic scale microstructure and properties of Se-deficient two-dimensional MoSe2. ACS Nano 9, 3274–3283 (2015).
Lin, J., Pantelides, S. T. & Zhou, W. Vacancy induced formation and growth of inversion domains in transition metal dichalcogenide monolayer. ACS Nano 9, 5189–5197 (2015).
Zou, X., Liu, Y. & Yakobson, B. I. Predicting dislocations and grain boundaries in two-dimensional metal-disulfides from the first principles. Nano Lett. 13, 253–258 (2013).
Liu, H. et al. Line and point defects in MoSe2 bilayer studied by scanning tunneling microscopy and spectroscopy. ACS Nano 9, 6619–6625 (2015).
Binnig, G. et al. Tunneling spectroscopy and inverse photoemission: Image and field states. Phys. Rev. Lett. 55, 991–994 (1985).
Becker, R. S., Golovchenko, J. A. & Swartzentruber, B. S. Electron interferometry at crystal surfaces. Phys. Rev. Lett. 55, 987–990 (1985).
Cundlach, K. H. Zur Berechnung des tunnelstroms durch eine trapezformige potentialstufe. Solid State Electron. 9, 947–957 (1966).
Fowler, R. H. & Nordheim, L. Fowler Nordheim electron field emission. Proc. R. Soc. A Math. Phys. Eng. Sci. 119, 173–181 (1928).
Pascual, J. I. et al. Role of the electric field in surface electron dynamics above the vacuum level. Phys. Rev. B 75, 165326 (2007).
Ruffieux, P. et al. Mapping the electronic surface potential of nanostructured surfaces. Phys. Rev. Lett. 102, 086807 (2009).
Axnanda, S. et al. Direct work function measurement by gas phase photoelectron spectroscopy and its application on PbS nanoparticles. Nano Lett. 13, 6176–6182 (2013).
Chen, W. et al. Dianhydride supramolecular chiral networks on Ag (111). J. Am. Chem. Soc. 130, 12285–12289 (2008).
Chang, C.-H., Fan, X., Lin, S.-H. & Kuo, J.-L. Orbital analysis of electronic structure and phonon dispersion in MoS2, MoSe2, WS2, and WSe2 monolayers under strain. Phys. Rev. B 88, 195420 (2013).
Johari, P. & Shenoy, V. Tuning the electronic properties of semiconducting transition metal dichacogenides by applying mechanical strains. ACS Nano 6, 5449–5456 (2012).
Zhang, Q. et al. Bandgap renormalization and work function tuning in MoSe2/hBN/Ru(0001) heterostructures. Nat. Commun. 7, 13843 (2016).
Chai, J. W. et al. Tuning contact barrier height between metals and MoS2 monolayer through interface engineering. Adv. Mater. Interfaces 4, 1700035 (2017).
Calhorda, M. J. Weak hydrogen bonds: theoretical studies. Chem. Commun., 801–809 (2000).
Horcas, I. et al. WSXM: a software for scanning probe microscopy and a tool for nanotechnology. Rev. Sci. Instrum. 78, 013705 (2007).
Acknowledgements
A.T.S.W. acknowledges funding support from MOE Tier 2 grant R-144-000-382-112, Tier 3 grant R-143-000-625-112, and A*STAR Pharos Program Grant No. 1527300025. Y.L.H., M.Y., S.J.W., and D.C. acknowledge the A-STAR SERC grant support for the 2D growth project under the 2D pharos program (SERC 1527000012). X.H. acknowledges a research grant from the National Natural Science Foundation of China (NSFC, Grant Nos.11404073 and 11674366). P.K.J.W. is supported by the Singapore NRF Medium Sized Centre Programme R-723-000-001-281. A. acknowledges a research grant from MOE Tier 3 programmer (MOE2014-T3-1-004).
Author information
Authors and Affiliations
Contributions
X.H., Y.L.H. and A.T.S.W. proposed and designed the research project. X.H. performed the STM experiments and analysed the data. Y.L.H. and D.C. participated in discussion and analysis of the data. Y.M. helped in discussion and performed the first-principle calculations. Z.L., R.C. and P.K.J.W. provided the MBE-grown MoSe2 samples. Arramel participated in the STM measurements. Y.P.F. and W.S.J. supervised the calculations. X.H., Y.L.H., Y.M. and A.T.S.W. wrote the paper, and all authors discussed and revised the final manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer Review Information: Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
He, X., Zhang, L., Chua, R. et al. Selective self-assembly of 2,3-diaminophenazine molecules on MoSe2 mirror twin boundaries. Nat Commun 10, 2847 (2019). https://doi.org/10.1038/s41467-019-10801-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-10801-0
This article is cited by
-
Large-scale 2D heterostructures from hydrogen-bonded organic frameworks and graphene with distinct Dirac and flat bands
Nature Communications (2024)
-
Improving the band alignment at PtSe2 grain boundaries with selective adsorption of TCNQ
Nano Research (2023)
-
Lateral epitaxial growth of two-dimensional heterostructure linked by gold adatoms
Nano Research (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.