Resonantly enhanced multiple exciton generation through below-band-gap multi-photon absorption in perovskite nanocrystals

Nature Communicationsvolume 9, Article number: 1518 (2018) | Download Citation


Multi-photon absorption and multiple exciton generation represent two separate strategies for enhancing the conversion efficiency of light into usable electric power. Targeting below-band-gap and above-band-gap energies, respectively, to date these processes have only been demonstrated independently. Here we report the combined interaction of both nonlinear processes in CsPbBr3 perovskite nanocrystals. We demonstrate nonlinear absorption over a wide range of below-band-gap excitation energies (0.5–0.8 Eg). Interestingly, we discover high-order absorption processes, deviating from the typical two-photon absorption, at specific energetic positions. These energies are associated with a strong enhancement of the photoluminescence intensity by up to 105. The analysis of the corresponding energy levels reveals that the observed phenomena can be ascribed to the resonant creation of multiple excitons via the absorption of multiple below-band-gap photons. This effect may open new pathways for the efficient conversion of optical energy, potentially also in other semiconducting materials.


Semiconductors are nowadays the most prominent materials for applications in optoelectronic devices. Harvesting the energy of light and converting it into usable electric energy with the lowest amount of losses is one of the main goals to achieve high efficiency in photovoltaic devices. The two main loss sources are (i) the absorption cutoff for photons with energies below the semiconductor band gap (Eg) and (ii) the wasted excess energy of photons with energies above the band gap. Below-band-gap photons normally pass the respective semiconductor without being absorbed. Multiple photon excitation (MPE) processes, however, represent a route to access such low-energy photons leading to the generation of one exciton via the simultaneous absorption of a number (≥2) of below-band-gap photons whose combined energy is greater than the band-gap energy1. On the other side, highly energetic photons do not contribute effectively to the total usable energy in semiconducting devices because their excess energy is typically lost as heat. A possible approach to address this limitation is to generate multiple excitons from one photon, a process known as multiple exciton generation (MEG) or carrier multiplication2,3,4,5. This process typically requires photons with energies several times that of the band gap and has been shown to work efficiently only in nanocrystals exhibiting strong quantum confinement6,7,8,9,10,11,12.

Here we investigate the combined action of MPE and MEG on the light-emitting properties of non-quantum-confined metal halide perovskite nanocrystals, a semiconducting material that in recent years has shown its high potential for photovoltaic13,14 as well as for light-emitting applications15. Although these mechanisms have been studied independently in perovskite nanocrystals16,17,18,19,20,21,22,23,24,25, here we analyze the possibility to combine them together to further enhance their efficiencies under specific resonant conditions. We find interband photoluminescence (PL) of CsPbBr3 nanocubes (NCs) under MPE for a wide spectral range below the band gap. Strikingly, we observe distinct resonances of the PL intensity for specific excitation wavelengths in the MPE-PL spectra. These correspond to specific energies of the excitation source and can be ascribed to the resonant creation of multiple excitons through MPE, as illustrated in Fig. 1.

Fig. 1
Fig. 1

Schematic of the combined MPE-MEG mechanism. Multiple photon excitation with below-band-gap photons of energies 4 and 3 resonantly matching the energy levels 3|x> and 2|x> associated to multiple exciton generation


Synthesis and optical characterization

The CsPbBr3 NCs were synthesized using a one-step process based on direct tip sonication of precursor mixtures, according to our previously published work26. The purified dispersion of NCs exhibits an absorption spectrum characterized by a sharp absorption onset and a distinct excitonic peak at 500 nm (see Fig. 2a). The PL spectrum of the NCs deposited on a glass substrate shows a single PL emission peak centered around λx = 523 nm, corresponding to an energy Ex = x = 2.37 eV. A spectrometer with an integrating sphere detector was used to measure the absorbance of the NCs deposited on a substrate (Supplementary Fig. 1). The absorbance of the NCs distributed on a glass substrate resembles the absorbance in solution, indicating almost no absorption of the nanocrystals for excitation below the band-gap. The average size of the cubes was determined from transmission electron microscopy (TEM) images to be in the range of 10–15 nm (Fig. 2b). These sizes along with the absorption and PL spectra clearly show that these NCs do not show quantum confinement, but have already bulk-like properties27,28. Moreover, from the TEM and the scanning electron microscopy (SEM) analysis (Fig. 2c), we observe that the NCs are mostly ordered on the substrate leading to a superlattice-like arrangement.

Fig. 2
Fig. 2

Optical and morphological characterization of the CsPbBr3 nanocubes. a Absorbance (left axis) spectra of CsPbBr3 nanocubes in hexane and normalized photoluminescence (right axis) of CsPbBr3 nanocubes on substrates, excitation wavelength 480 nm. The arrows indicate, respectively, the position of the photoluminescence emission λx, and the excitation wavelengths λ4, λ3 and λ2 associated to the observed resonances. b TEM image of CsPbBr3 nanocubes, scale bar 50 nm. c SEM image of a CsPbBr3 nanocube film showing the superlattice-like arrangement, scale bar 200 nm

Below-band-gap optical excitation

By studying the emitting properties of the nanocrystals using an excitation source with below-band-gap energy photons, we observe that the CsPbBr3 NCs show PL emission for a wide range of excitation wavelengths (see inset in Fig. 3a). The excitation was provided by a focused supercontinuum laser (repetition rate 78 MHz) with 15 ps pulses tunable from 680 to 1080 nm. For each excitation energy we observe PL centered around 523 nm, indicating almost no shift with respect to the PL measured using above-band-gap excitation. Since the linear absorption of the NCs is negligible in this wavelength range, the absorption processes must be of nonlinear origin.

Fig. 3
Fig. 3

Nonlinear absorption-induced PL in perovskite NCs. a Photoluminescence intensity of CsPbBr3 NCs as a function of the below-band-gap excitation wavelength. The PL intensity is normalized by the laser fluence (see Supplementary Fig. 2). The dashed line is a guide to the eye. The inset shows the normalized photoluminescence spectrum for excitation wavelengths varying from 870 to 700 nm (specifically: 870, 850, 820, 800, 790, 770, 750, 720 and 700 nm). b Integrated photoluminescence intensity as a function of the laser excitation intensity for excitation wavelengths λ4 (700 nm), λ3 (790 nm) and λ2 (1030 nm). The solid lines represent the respective fit with power functions, from which we can deduce the order of the process: 4 for λ4 excitation, 3 for λ3 excitation and 2 for λ2 excitation. c Order of the absorption processes as a function of the below-band-gap excitation wavelength

While the spectral shape of the PL emission does not change with wavelength, the PL intensity depends strongly on the excitation wavelength (see Fig. 3a). There is a clear onset of the PL intensity for an excitation wavelength around λ2 = 1030 nm (photon energy 2 = 1.20 eV  0.50 Eg), with the intensity generally increasing as the excitation wavelength is decreased. This onset can be associated to the minimum excitation energy required for two photons to overcome the band gap via MPE. A local maximum is reached at 680 nm, after which the PL intensity sharply drops to nearly zero. Even more interestingly, the MPE-PL spectrum does not increase monotonically, but rather exhibits two distinct peaks located at excitation wavelengths of λ3 = 790 nm and λ4 = 700 nm (photon energies 3 = 1.57 eV  0.66 Eg and 4 = 1.77 eV  0.75 Eg, respectively). These peaks are associated with a PL intensity which is several orders of magnitude higher (103 and 105, respectively) than the signal detected in the vicinity of λ2. For clarity, the positions of the observed peaks in the MPE-PL spectrum are also marked with black arrows in the absorbance spectrum in Fig. 2.

Interestingly, these particular energies perfectly match the energy of multiples of the exciton energy x, suggesting the possible connection between multiple photon absorption and the resonant generation of multiple excitons. In fact, three photons of energy corresponding to the excitation wavelength λ3 have the exact energy required to generate two excitons in the NCs. In the same way, four photons of energy associated to the the excitation wavelength λ4 correspond to the energy necessary to generate three excitons. Analogously, two photons of energy related to the excitation wavelength λ2 exactly equal the exciton energy Ex. No multiple exciton generation is therefore expected in correspondence to λ2, explaining the absence of an associated peak in the MPE-PL spectrum.

To exclude the possibility that the observed resonances are due to an effect only observable in CsPbBr3 NCs, we have performed analogous measurements on CsPbI3 NCs (Supplementary Fig. 3 and 4). These were fabricated through an ion exchange step from the originally synthesized CsPbBr3 NCs, preserving their size and geometry (see Supplementary Fig. 3 for more details). In these NCs, we again observe clear resonances in the PLE spectra. Their spectral positions again align with multiples of the exciton energy (Ex = 1.81 eV), i.e., they are red-shifted with respect to those observed in the CsPbBr3 system. These results support the notion that the proposed mechanism is not a specific property of CsPbBr3 NCs.

Order of the absorption processes

For an absorption process involving p photons, the intensity of the PL, IPL, is proportional to the excitation intensity to the power of p, \((I_{{\mathrm{exc}}})^p\), with p being the order of the process. For p = 1 this accounts to the regular linear absorption, while for p > 1 the process corresponds to a multiple photon absorption process via p−1 virtual states. Thus, by measuring the PL intensity in dependence of the excitation intensity and applying a power law fit, one can obtain the order of the process and thus determine the nature of the absorption.

In Fig. 3b the integrated PL intensities at the respective excitation wavelengths λ4, λ3 and λ2 are plotted in dependence of the laser excitation intensity. Fitting power law functions to the data, we find that at λ4 absorption takes place via a fourth-order process, while at λ3 the process is of third order and at λ2 of second order. This is in complete accordance with our interpretation of an MPE process.

Analysis of the energy levels

With the knowledge that 4 and 3 photons are involved in the absorption processes associated to the excitation wavelengths λ4 and λ3 respectively, we can determine the energy levels reached by the MPE process and correlate them with the energy necessary to generate multiple excitons. A schematic representation of the combined MPE and MEG processes in the analyzed system is shown in Fig. 4. When λ4 is used as the excitation wavelength, the system undergoes 4-photon absorption and reaches the energy level 7.08 eV, that is resonant with 3Ex = 7.10 eV. Similarly, when photons with wavelength λ3 are used, a 3-photon absorption process is observed and the photogenerated electrons have an energy of 4.71 eV, resonant with 2Ex = 4.73 eV. Therefore, the energy matching between the energy level reached through MPE and the level associated to multiples of the exciton energy Ex allows the combined interplay of MEG and MPE. The combination of these processes produces the observed maxima in the PL efficiency for specific values of the excitation energy, which is in agreement with the efficient creation of multiple excitons.

Fig. 4
Fig. 4

Energy diagram of the resonances between MPE and MEG in CsPbBr3 NCs. Photo-excitation at 3Ex (a) and 2Ex (b) and subsequent generation three (a) and two (b) excitons via multiple photon excitation processes with photons of energies 4 and 3, respectively


The observation of resonances given by MEG in the MPE-PL of CsPbBr3 is realized when the following relation is fulfilled:

$$p \times h\nu = N \times E_{\mathrm{x}}$$

where p is the number of photons involved in the MPE, N is the number of excitons created through MEG and Ex is the energy of a single exciton. In order to confirm this theory, we look at MPE at excitation wavelengths away from the observed resonances and focus on the order of the excitation process (Fig. 3c). The PL intensity drops off steeply for excitation wavelengths longer than 1030 nm, corresponding to twice the band-gap energy of the CsPbBr3 NCs. For slightly shorter wavelengths, the PL intensity scales proportionally to (Iexc)2, while for slightly longer wavelengths the PL intensity clearly scales with (Iexc)3 (Supplementary Fig. 5). These values confirm that the drop off region marks the onset of two-photon absorption (2PA), while PL emission for excitation at longer wavelengths requires three photon absorption (3PA). For shorter wavelengths the order of the absorption process remains around 2 or slightly below this value (see Supplementary Fig. 6). Close to the resonance at λ3 the order jumps up to a value of 3 again, and at λ4, the order increases to 4. In between these resonances, the order decreases rapidly to 2. This suggests that the specific resonances are indeed necessary to promote the higher order MPE. Notably, the PL decreases abruptly to almost zero for excitation wavelengths shorter than 680 nm. At these wavelengths, four photon absorption leads to energies in excess of 7 eV, which could possibly induce ionization of the NCs, opening a new non-radiative decay channel.

Upon closer inspection, the peaks in the PL spectrum corresponding to excitation wavelengths in the vicinity of resonances have a characteristic non-symmetrical shape (Fig. 3a). Surprisingly, when photons with energies slightly higher than the resonance energy are used for excitation, the efficiency of the emission drops. This is an indication that the combined MPE-MEG process is particularly favorable when no additional excess energy is involved in the excitation process.

Another striking result is that the resonant MPE-MEG process is absent for such nanocubes under comparable laser excitation intensities when they are dispersed in solution. This suggests that the observed PL enhancement in correspondence with the MEG resonances relies on the close-packed arrangement of the CsPbBr3 NCs on the substrate. As reported by Trinh et al., MEG in adjacent silicon nanocrystals results in a suppression of the non-radiative Auger recombination and in the creation of long-living multiple excitons29. The initial optical excitation possesses a large energy and the related wavefunctions can overlap spatially with those of adjacent nanocrystals, if they are close enough. The highly energetic excitation can then create multiple excitons in different adjacent nanocrystals. The spatial extent of these wavefunctions is much smaller, consequently Auger recombination becomes less likely and in turn radiative recombination is enhanced. This model thus offers an explanation for the radiative character of MEG in our system.

To substantiate our proposed model, we have also measured a highly diluted dispersion of CsPbBr3 NCs on substrate (see Supplementary Fig. 7). While we could measure linearly excited PL from these NCs, we did not observe the MPE-MEG resonances observed for a dense array of NCs. This further supports the idea that a dense arrangement of the NCs is crucial for observing this phenomenon and for suppressing non-radiative Auger recombination. Further validity is obtained by repeating the investigations on larger CsPbBr3 nanocubes with edge sizes on the order of 100 nm (Supplementary Fig. 8). While we observe an enhanced PL near the expected resonance positions, the resonances themselves—if present—are significantly weaker and strongly broadened. This is to be expected, as Auger recombination will not be similarly suppressed as in the case of the smaller close-packed NCs.

In conclusion, we have shown that perovskite NCs exhibit interband PL emission when excited with photons with below-band-gap energies over a wide range of energies. Our findings show that multiple excitons can be generated in non-quantum-confined perovskite NCs by the excitation with multiple photons and that the system exhibits resonances for specific values of the excitation wavelength. These resonances occur when the total energy of a number of exciting photons is equal to the energy necessary to create multiple excitons. Owing to the presence of resonances, the photogeneration together with the radiative recombination of excitons are highly enhanced, while the non-radiative Auger recombination is suppressed due to the spatial arrangement of the NCs on substrate. Therefore, high-order MPE can be used as an efficient pathway for the creation of multiple excitons in non-quantum-confined perovskite nanocrystals. Moreover, having observed the presence of MEG-MPE resonances in different perovskite NCs, we can envision this process also occurring in other semiconducting nanocrystals even with sizes greater than the quantum dot restriction. This could open new pathways for various energy conversion systems exploiting high light intensities.



The synthesis of CsPbBr3 NCs was carried out by ultrasonication of precursors in octadecene solvent mixed with oleylamine and oleic acid ligands, as reported previously by our group26. A detailed description of the synthesis techniques can be found in the Supplementary Note 1.

Experimental setup

The excitation for the MPE-PL measurements was provided by a SuperK EXTREME supercontinuum white light laser focused by a 100× magnification to the specimen. More information about the experimental setup is in the Supplementary Note 2. All the measurements were conducted in normal atmosphere and at room temperature.

Feasibility studies

An estimation of the efficiency of the proposed mechanism for solar applications can be found in the Supplementary Note 3.

Data availability

The data that support the findings of this study are available from the corresponding authors on reasonable request.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.


  1. 1.

    He, G. S., Tan, L. S., Zheng, Q. & Prasad, P. N. Multiphoton absorbing materials: Molecular designs, characterizations, and applications. Chem. Rev. 1080, 1245–1330 (2008).

  2. 2.

    Trupke, T., Green, M. A. & Würfel, P. Improving solar cell efficiencies by down-conversion of high-energy photons. J. Appl. Phys. 920, 1668–1674 (2002).

  3. 3.

    Schaller, R. D., Agranovich, V. M. & Klimov., V. I. High-efficiency carrier multiplication through direct photogeneration of multi-excitons via virtual single-exciton states. Nat. Phys. 10, 189–194 (2005).

  4. 4.

    Klimov, V. I. Mechanisms for photogeneration and recombination of multiexcitons in semiconductor nanocrystals: Implications for lasing and solar energy conversion. J. Phys. Chem. B 1100, 16827–16845 (2006).

  5. 5.

    Kamat, P. V. Quantum dot solar cells. Semiconductor nanocrystals as light harvesters. J. Phys. Chem. C 1120, 18737–18753 (2008).

  6. 6.

    Schaller, R. D. & Klimov, V. I. High efficiency carrier multiplication in PbSe nanocrystals: Implications for solar energy conversion. Phys. Rev. Lett. 920, 186601–186601 (2004).

  7. 7.

    Ellingson, R. J. et al. Highly efficient multiple excition generation in colloidal PbSe and PbS quantum dots. Nano Lett. 5, 865–871 (2005).

  8. 8.

    Beard, M. C. et al. Multiple exciton generation in colloidal silicon nanocrystals. Nano Lett. 70, 2506–2512 (2007).

  9. 9.

    Pijpers, J. J. H. et al. Carrier multiplication and its reduction by photodoping in colloidal inas quantum dots carrier multiplication and its reduction by photodoping in colloidal InAs quantum dots. J. Phys. Chem. 111, 4146–4152 (2007).

  10. 10.

    Nozik, A. J. Multiple exciton generation in semiconductor quantum dots. J. Phys. Chem. Lett. 457, 3–11 (2008).

  11. 11.

    Beard, M. C. Multiple exciton generation in semiconductor quantum dots. J. Phys. Chem. Lett. 20, 1282–1288 (2011).

  12. 12.

    Kumar, M. et al. Hot exciton cooling and multiple exciton generation in PbSe quantum dots. Phys. Chem. Chem. Phys. 18, 31107–31114 (2016).

  13. 13.

    Swarnkar, A., et al. Quantum dot-induced phase stabilization of α-CsPbI3 perovskite for high-efficiency photovoltaics. Science 354, 92–95 (2016).

  14. 14.

    Akkerman, Q. A. et al. Strongly emissive perovskite nanocrystal inks for high-voltage solar cells. Nat. Energy 2, 1–7 (2016).

  15. 15.

    Protesescu, L. et al. Nanocrystals of cesium lead halide perovskites (CsPbX3, X = Cl, Br, and I): novel optoelectronic materials showing bright emission with wide color gamut. Nano Lett. 15, 3692–3696 (2015).

  16. 16.

    Walters, G. et al. Two-photon absorption in organometallic bromide perovskites. ACS Nano 90, 9340–9346 (2015).

  17. 17.

    Wang, Y. et al. Nonlinear absorption and low-threshold multiphoton pumped stimulated emission from all-inorganic perovskite nanocrystals. Nano Lett. 160, 448–453 (2016).

  18. 18.

    Wei, K. et al. Temperature-dependent excitonic photoluminescence excited by two-photon absorption in perovskite CsPbBr3 quantum dots. Opt. Lett. 410, 16–19 (2016).

  19. 19.

    Zhang, R. et al. Nonlinear optical response of organic-inorganic halide perovskites. ACS Photonics 3, 371–377 (2016).

  20. 20.

    Lu, W. G. et al. Nonlinear optical properties of colloidal CH3NH3PbBr3 and CsPbBr3 quantum dots: a comparison study using Z-scan technique. Adv. Opt. Mater. 40, 1732–1737 (2016).

  21. 21.

    Gu, Z. et al. Two-photon pumped CH3NH3PbBr3 perovskite microwire lasers. Adv. Opt. Mater. 40, 472–479 (2016).

  22. 22.

    Li, J. et al. Two-photon absorption and emission in CsPb(Br/I)3 cesium lead halide perovskite quantum dots. CrystEngComm 180, 7945–7949 (2016).

  23. 23.

    Makarov, N. S. et al. Spectral and dynamical properties of single excitons, biexcitons, and trions in cesium-lead-halide perovskite quantum dots. Nano Lett. 160, 2349–2362 (2016).

  24. 24.

    de Jong, E. M. L. D. et al. Multiexciton lifetime in all-inorganic CsPbBr3 perovskite nanocrystals. J. Phys. Chem. C. 121, 1941–1947 (2016).

  25. 25.

    Aneesh, J. et al. Ultrafast exciton dynamics in colloidal CsPbBr3 perovskite nanocrystals: bi-exciton effect and auger recombination. J. Phys. Chem. C. 121, 4737–4739 (2017).

  26. 26.

    Tong, Y. et al. Highly luminescent cesium lead halide perovskite nanocrystals with tunable composition and thickness by ultrasonication. Angew. Chem. Int. Ed. 550, 13887–13892 (2016).

  27. 27.

    Sichert, J. A. et al. Quantum size effect in organometal halide perovskite nanoplatelets. Nano Lett. 150, 6521–6527 (2015).

  28. 28.

    Kim, Y.-h et al. Highly efficient light-emitting diodes of colloidal metal-halide perovskite nanocrystals beyond quantum size. ACS Nano 11, 6586–6593 (2017).

  29. 29.

    Trinh, M. T. et al. Direct generation of multiple excitons in adjacent silicon nanocrystals revealed by induced absorption. Nat. Photon. 60, 316–321 (2012).

Download references


This work was supported by the Bavarian State Ministry of Science, Research, and Arts through the grant “Solar Technologies go Hybrid (SolTech)”, the DFG-project "LMUexcellent", the EU-project "COMPASS" and the China Scholarship Council (Y.T.).

Author information


  1. Chair for Photonics and Optoelectronics, Department of Physics and Center for NanoScience (CeNS), Ludwig-Maximilians-Universität, Amalienstr. 54, 80799, Munich, Germany

    • Aurora Manzi
    • , Yu Tong
    • , Julius Feucht
    • , En-Ping Yao
    • , Lakshminarayana Polavarapu
    • , Alexander S. Urban
    •  & Jochen Feldmann
  2. Nanosystems Initiative Munich (NIM), Schellingstr. 4, 80799, Munich, Germany

    • Aurora Manzi
    • , Yu Tong
    • , Julius Feucht
    • , En-Ping Yao
    • , Lakshminarayana Polavarapu
    • , Alexander S. Urban
    •  & Jochen Feldmann


  1. Search for Aurora Manzi in:

  2. Search for Yu Tong in:

  3. Search for Julius Feucht in:

  4. Search for En-Ping Yao in:

  5. Search for Lakshminarayana Polavarapu in:

  6. Search for Alexander S. Urban in:

  7. Search for Jochen Feldmann in:


J.F. and L.P. suggested below-band-gap experiments on perovskite NCs. A.M. performed most of the optical measurements and the analytical work. Y.T. and L.P. synthesized and characterized the perovskite nanocubes. Ju.F. and E-P.Y. contributed to the optical measurements on CsPbI3 NCs. A.M. wrote the manuscript with inputs from J.F. and A.S.U. All the authors contributed to the discussion.

Competing interests

The authors declare no competing interests.

Corresponding authors

Correspondence to Aurora Manzi or Jochen Feldmann.

Electronic supplementary material

About this article

Publication history






By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.