Abstract
With ever-increasing laser power, the requirements for ultraviolet (UV) coatings increase continuously. The fundamental challenge for UV laser-resistant mirror coatings is to simultaneously exhibit a high reflectivity with a large bandwidth and high laser resistance. These characteristics are traditionally achieved by the deposition of laser-resistant layers on highly reflective layers. We propose a “reflectivity and laser resistance in one” design by using tunable nanolaminate layers that serve as an effective layer with a high refractive index and a large optical bandgap. An Al2O3–HfO2 nanolaminate-based mirror coating for UV laser applications is experimentally demonstrated using e-beam deposition. The bandwidth, over which the reflectance is >99.5%, is more than twice that of a traditional mirror with a comparable overall thickness. The laser-induced damage threshold is increased by a factor of ~1.3 for 7.6 ns pulses at a wavelength of 355 nm. This tunable, nanolaminate-based new design strategy paves the way toward a new generation of UV coatings for high-power laser applications.
The demand for laser-resistant mirror coatings is increasing in inertial confinement fusion (ICF)1, extreme light infrastructure2 and other laser applications3,4,5,6. An ideal ultraviolet (UV) laser mirror (UVLM) coating requires a high reflectivity with a large bandwidth and a high laser-induced damage threshold (LIDT). Unfortunately, these requirements are difficult to satisfy simultaneously, because, for example, a high reflectivity requires materials with a high refractive index (n), while higher n materials tend to have a smaller optical bandgap and therefore a lower LIDT. Traditionally, compromises are made for these seemingly contradictory requirements7,8,9,10. We propose to use nanolaminate coatings for UVLMs. Nanolaminate materials11,12,13,14,15,16 have properties that make them attractive for many applications15,17,18,19,20. Our nanolaminate-based UVLM coatings are deposited using e-beam evaporation, a technique that is particularly favorable for large laser optics10,21,22,23,24. This novel concept results in improved performance parameters and paves the way toward a new generation of UV coatings for high-power laser applications.
In the traditional “reflectivity bottom and LIDT top” combination design (TCD coating) strategy, alternating high-n and low-n layers, such as HfO2 and SiO2, are deposited on the substrate to obtain a high reflectivity, as illustrated in Fig. 1a (the high-n layer is denoted as CHN). Subsequently, pairs of high-n layers (with a relatively larger optical bandgap than CHN, denoted as layer CLB) and low-n layers, such as Al2O3 and SiO2, or LaF3 and AlF3, are deposited to achieve a high LIDT8,9. Our new “reflectivity and laser resistance in one” strategy uses nanolaminate layers with co-evaporated interfaces, which are produced by alternating CLB layers and CHN layers, as shown in Fig. 1b. The CLB-CHN nanolaminate layers can be considered high-n layers, with a tunable refractive index and optical bandgap. As we will show, this arrangement allows for mirror designs with the advantageous combination of a high reflectivity and a high LIDT.
The high-n materials HfO2 and Al2O3 in combination with the low-n material SiO2 are widely used for multilayer coating stacks in the UV region25. The microstructure and optical properties of an e-beam-evaporated Al2O3–HfO2 nanolaminate coating consisting of 18 Al2O3–HfO2 pairs have been compared with those of HfO2 and Al2O3 single-layer coatings. In this study, ~4-nm co-evaporated interfaces are introduced for each alternating interface between two different materials, as shown in Fig. 1. The elemental percentages of an Al2O3–HfO2 pair in the nanolaminate vs. depth are measured by XPS and are shown in Fig. 2a. Due to diffusion, both the Al2O3 and HfO2 contents are observed at each depth. The Al2O3 to HfO2 integrated content ratio in an Al2O3–HfO2 pair is calculated to be ~1.7:1. A sharp diffraction peak is not observed in the X-ray diffraction (XRD) spectra of the Al2O3–HfO2 nanolaminate and Al2O3 single-layer coatings, while multiple sharp diffraction peaks indicative of crystallinity are obtained from the HfO2 single-layer coating (Fig. 2b). The transmittance spectra of the substrate and coatings are measured to determine the refractive indices (Fig. 2c). The optical bandgaps of the Al2O3 and HfO2 single-layer coatings and Al2O3–HfO2 nanolaminate coatings are estimated using the Tauc equation26 to be 6.25 eV, 5.44 eV, and 5.65 eV, respectively. The Al2O3–HfO2 nanolaminate coating acts as an equivalent single-layer coating with a higher refractive index than Al2O3 and a larger optical bandgap than HfO2. The (average) refractive index and optical bandgap can be tuned by adjusting the thickness ratio of the two materials in the nanolaminate layers while keeping the total optical thickness constant. This allows one to develop UVLM coatings with a high reflectivity and a high LIDT.
Using the refractive index and optical bandgap tunability, a nanolaminate-based multilayer coating (NLD coating) consisting of Al2O3–HfO2 nanolaminate layers with an equivalent n of 1.714 at 355 nm is designed. The coating structure is as follows: substrate/4L(0.335A0.165H0.335A0.165HL)20A8.15L/air. Here, A, H, and L represent Al2O3, HfO2, and SiO2 layers with a quarter-wavelength optical thickness (QWOT), respectively. The number represents the optical thickness in units of the QWOT of the respective material. Thus, 0.335A0.165H0.335A0.165H represents a nanolaminate layer with four sublayers (Supplementary Fig. S2). For a given total optical thickness, a nanolaminate layer with a larger number of sublayers has a higher optical bandgap16. Here, four sublayers are used as a compromise between a large bandgap and the overall layer quality. Note that the co-evaporated interfaces have a thickness of ~4 nm. To achieve a high reflectivity at 355 nm for an angle of incidence of 45°, the reference wavelength λ0 is 395 nm. The refractive indices of A, H, and L at 395 nm are 1.616, 1.956, and 1.481, respectively. According to 2 × (nAd0.335A + nHd0.165H) = nLdL = nAdA = λ0/4, the physical thicknesses are d4L = 266.80 nm, d0.335A = 20.47 nm, d0.165H = 8.33 nm, dL = 66.70 nm, dA = 61.11 nm, and d8.15L = 543.61 nm. The designed Al2O3 to HfO2 integrated content ratio in the nanolaminate layers is 2.46:1. A thick SiO2 overcoat layer (8.15L) is used as a protective layer, and the resulting electric (E)-field intensity at the coating-air interface is close to 0.
For a comparison, the aforementioned NLD coating stack and a TCD coating with a substrate/4L(HL)5(AL)15A8.15L/air structure are prepared. Obvious sharp diffraction peaks are not observed in the XRD spectra of either the NLD and TCD coatings. Figure 3a, b shows images from high-resolution transmission electron microscopy (TEM) of both coatings, and the lattice is consistent with the selected-area electron diffraction result (see Supplementary Fig. S4). The elemental percentages vs. depth are shown in Fig. 3c. The Al2O3 to HfO2 integrated content ratio in the nanolaminate layers is ~2.2:1, slightly lower than the designed value. Al2O3 is also observed at the interface between SiO2 and HfO2 in the nanolaminate layers, which is attributed to diffusion and/or preferential sputtering effects. The reflectance spectra of the two coatings are compared in Fig. 3d. The high-reflectivity (Rs ≥ 99.5%) bandwidth of the NLD coating is 38 nm, more than twice that of the TCD coating (17 nm). In addition, the NLD average transmission is higher in the VIS–NIR region and exhibits smaller ripple amplitudes (Fig. 3e). This result indicates that properly designed NLD structures also have potential as harmonic separators, which require a high reflectivity at one wavelength and a high transmittance at other wavelengths.
The laser damage probabilities as a function of fluence of the two coating structures are compared in Fig. 3f. The damage probability curves show a shape that can, for example, be explained by the presence of two types of defects with different LIDTs. The defect parameters can be extracted using the model developed by Krol et al.27. If we assume the existence of two defects with different values of the LIDT Ti and area density Di (integrated over the thickness), we obtain the results shown in Table 1. Overall, the NLD coating shows improved damage resistance compared with the damage resistance of the TCD coating stack.
To investigate the damage mechanism, the stress, absorption, E-field distribution, and damage morphology of the coatings are studied. The stresses of the TCD and NLD coatings are determined to be −160.7 MPa and −171.1 MPa, respectively. The E-field intensity in the NLD coating decays more rapidly with depth than the TCD coating (Fig. 3g). The absorption of the coating stacks is measured using nano-Kelvin calorimetry28. At the wavelength of interest (355 nm), the absorption losses in the NLD coating stack are ~20% smaller than those in the TCD mirror (Fig. 3h). Consequently, the laser-induced temperature increase in the NLD coating will be lower.
Typical damage morphologies of the NLD and TCD structures are shown in Fig. 4 and suggest the existence of two types of defects. One morphological feature is related to nodules, which produce a pit for an illumination fluence just above the LIDT (Fig. 4i). At larger fluences, the top layers are ablated (Fig. 4j). As the laser fluence further increases, a second type of damage morphology can be observed. This morphology consists of many shallow pits (Fig. 4k), which evolve into larger areas of delaminated films for larger laser fluences (Fig. 4l). The defects that initiate damage features of this second type do not involve nodules. The damage morphology of the second type is observed for fluences of 25.9 J/cm2 in the TCD coatings (Fig. 4g), while only the first kind of morphology is observed in the NLD coatings for fluences at 32.7 J/cm2 (Fig. 4b). After laser irradiation with the same fluence above the LIDT, the damaged area in the NLD coating stack is smaller than that in the TCD coating stack.
A finite-element method (FEM) simulation is used to illustrate the effect of nodular defects on the E-field intensity distribution. As an input for the simulation, the nodular defect size is estimated from the FIB cross-sections (Fig. 4). In both the TCD- and NLD-coating stacks, the nodular defects produce an E-field intensification (see Supplementary Fig. S5), especially in the top layers close to air. This result explains why laser damage originates from nodules, and a delamination of top layers occurs as the laser fluence increases. Compared with the TCD coating, the NLD coating exhibits a lower E-field intensification, faster E-field decay with depth and smaller absorption, which are consistent with the observed higher LIDT.
In summary, we have developed and experimentally demonstrated a new class of UVML coatings with an unprecedented combination of properties. The new structure replaces the high-n materials in traditional designs with nanolaminate layers. The proposed method enables UVML coatings with a larger high-reflectivity bandwidth, higher LIDT, and smaller transmission ripples in the VIS–NIR region than traditional designs with a comparable overall thickness. The e-beam-deposited nanolaminate materials can be used for large (meter-scale) UVML coatings. We believe that the described concept opens new avenues for improved UV coatings and can benefit many areas of laser technology that rely on high-quality optical coatings.
Materials and methods
Preparation of coatings
HfO2 and Al2O3 single-layer coatings, Al2O3–HfO2 nanolaminate coatings, and TCD and NLD multilayer coatings are deposited on fused silica substrates using e-beam evaporation. The coating chamber is heated to 473 K and evacuated to a base pressure of 9 × 10–4 Pa before deposition. The deposition rates for the HfO2, Al2O3, and SiO2 layers are 0.1 nm/s, 0.1 nm/s, and 0.2 nm/s, respectively. The oxygen pressure of HfO2 and Al2O3 is 1.3 × 10–2 Pa. Except for the 4L layer (3.0 × 10–3 Pa) in the TCD and NLD coatings, the oxygen pressure of the remaining SiO2 is 5.0 × 10–3 Pa. The co-evaporated interface is obtained by dual e-beam co-evaporation. The details of the co-evaporation system and process are shown in Supplementary Figs. S1 and S2.
Characterization of the coatings
The transmittance spectra in the range of 150–220 nm and 220–1200 nm are measured by a VUV spectrometer (LZH ML 6500) and a UV–visible spectrometer (Perkin Elmer Lambda 1050), respectively. The reflectance spectra in the VIS–NIR region are calculated from the transmission data neglecting absorption. The refractive indices are fitted using commercial thin film software (Essential Macleod). The E-field intensity distributions are obtained from FEM simulations.
The elemental compositions along the depth are determined by X-ray photoelectron spectroscopy (XPS, Thermo Scientific K-Alpha) using a monochromatic Al Kα (1486.6 eV) X-ray source. The spectra are recorded after every 20 s of etching with 1 keV Ar+ ions.
The surface and cross-section morphologies of the laser-induced damaged sites are obtained by a focused ion beam scanning electron microscope (FIB-SEM, Carl Zeiss AURIGA CrossBeam).
The 1-on-1 LIDT is determined according to ISO 21254 using an s-polarized 3ω Nd: YAG laser with a Gaussian TEM00, single-longitudinal mode (355 nm). The pulse shape is Gaussian with a full width at half maximum of 7.6 ns. The test is performed at an angle of incidence of 45°. The effective beam size on the sample surface is ~0.18 mm2, and 15 sites are tested for each energy fluence. The sample surfaces before (substrate) and 15 days after the deposition are inspected by an interferometer (ZYGO Mark III-GPI) at 632.8 nm in an environment with a temperature of 23 ± 1.5 °C and a relative humidity of 45 ± 5%. The coating stress is obtained from Stoney’s formula. The absorption is measured by an optical nano-Kelvin calorimeter28 using a tunable light source with a spectral width of ~6 nm, a step size of 5 nm, and an optical illumination power between 30 and 40 µW.
References
Macilwain, C. Inadequate optics ‘threat to US laser facility’. Nature 403, 120 (2000).
Extreme light. Nat. Mater. 15, 1 (2016).
Fan, Z. W. et al. High beam quality 5 J, 200 Hz Nd:YAG laser system. Light Sci. Appl. 6, e17004 (2017).
Norvig, P. et al. 2020 visions. Nature 463, 26–32 (2010).
Malobabic, S., Jupé, M. & Ristau, D. Spatial separation effects in a guiding procedure in a modified ion-beam-sputtering process. Light.: Sci. Appl. 5, e16044 (2016).
Jauregui, C., Limpert, J. & Tünnermann, A. High-power fibre lasers. Nat. Photonics 7, 861–867 (2013).
Hu, C. Q. et al. New design for highly durable infrared-reflective coatings. Light Sci. Appl. 7, 17175 (2018).
Xing, H. B. et al. Improving laser damage resistance of 355 nm high-reflective coatings by co-evaporated interfaces. Opt. Lett. 41, 1253–1256 (2016).
Xu, L. et al. Improvement of the laser-induced damage threshold of oxide/fluoride double stack high reflective coatings at 355 nm by introducing interlayers. Appl. Surf. Sci. 280, 772–775 (2013).
Tolenis, T. et al. Next generation highly resistant mirrors featuring all-silica layers. Sci. Rep. 7, 10898 (2017).
Hausmann, D. et al. Rapid vapor deposition of highly conformal silica nanolaminates. Science 298, 402–406 (2002).
Zhong, L. J. et al. Nanolaminates of zirconia and silica using atomic layer deposition. Chem. Mater. 16, 1098–1103 (2004).
Peng, Q. et al. Bi-directional kirkendall effect in coaxial microtube nanolaminate assemblies fabricated by atomic layer deposition. ACS Nano 3, 546–554 (2009).
Wickberg, A. et al. Second-harmonic generation from ZnO/Al2O3 nanolaminate optical metamaterials grown by atomic-layer deposition. Adv. Optical Mater. 4, 1203–1208 (2016).
Willemsen, T. et al. Enhancement of the damage resistance of ultra-fast optics by novel design approaches. Opt. Express 25, 31948–31959 (2017).
Willemsen, T. et al. Tunable optical properties of amorphous Tantala layers in a quantizing structure. Opt. Lett. 42, 4502–4505 (2017).
Kim, L. H. et al. Al2O3/TiO2 nanolaminate thin film encapsulation for organic thin film transistors via plasma-enhanced atomic layer deposition. ACS Appl. Mater. Interfaces 6, 6731–6738 (2014).
Heuser, S. et al. 3D 3C-SiC/Graphene hybrid nanolaminate films for high-performance supercapacitors. Small 14, 1801857 (2018).
Kahouli, A. et al. Electrical characteristics and conduction mechanisms of amorphous subnanometric Al2O3-TiO2 laminate dielectrics deposited by atomic layer deposition. Appl. Phys. Lett. 109, 202901 (2016).
Cho, M. H. et al. Dielectric characteristics of Al2O3-HfO2 nanolaminates on Si(100). Appl. Phys. Lett. 81, 1071–1073 (2002).
Cheng, X. B. et al. Waterproof coatings for high-power laser cavities. Light Sci. Appl. 8, 12 (2019).
Xu, N. et al. Laser resistance dependence of interface for high-reflective coatings studied by capacitance-voltage and absorption measurement. Opt. Lett. 43, 4538–4541 (2018).
Chai, Y. J. et al. Laser-resistance sensitivity to substrate pit size of multilayer coatings. Sci. Rep. 6, 27076 (2016).
Cheng, X. B. et al. The effect of an electric field on the thermomechanical damage of nodular defects in dielectric multilayer coatings irradiated by nanosecond laser pulses. Light Sci. Appl. 2, e80 (2013).
Grilli, M. L. et al. Al2O3/SiO2 and HfO2/SiO2 dichroic mirrors for UV solid-state lasers. Thin Solid Films 517, 1731–1735 (2009).
Tauc, J., Grigorovici, R. & Vancu, A. Optical properties and electronic structure of amorphous germanium. Phys. Status Solidi (B) 15, 627–637 (1966).
Krol, H. et al. Investigation of nanoprecursors threshold distribution in laser-damage testing. Opt. Commun. 256, 184–189 (2005).
Roshanzadeh, B., Boyd, S. T. P. & Rudolph, W. (Submitted for consideration).
Acknowledgements
The authors express their appreciation to Yuan’an Zhao and Yun Cui for the LIDT and FIB measurements, respectively. This work is supported by the National Special Support Program for Young Top-notch Talent; National Natural Science Foundation of China (61975215 and 61505227); Youth Innovation Promotion Association of the Chinese Academy of Sciences; and Shanghai Young Top-notch Talent Program.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhu, M., Xu, N., Roshanzadeh, B. et al. Nanolaminate-based design for UV laser mirror coatings. Light Sci Appl 9, 20 (2020). https://doi.org/10.1038/s41377-020-0257-4