Abstract
Resonant tunnelling is a quantum mechanical process that has long been attracting both scientific and technological attention owing to its intriguing underlying physics and unique applications for high-speed electronics. The materials system exhibiting resonant tunnelling, however, has been largely limited to the conventional semiconductors, partially due to their excellent crystalline quality. Here we show that a deliberately designed transition metal oxide superlattice exhibits a resonant tunnelling behaviour with a clear negative differential resistance. The tunnelling occurred through an atomically thin, lanthanum δ-doped SrTiO3 layer, and the negative differential resistance was realized on top of the bipolar resistance switching typically observed for perovskite oxide junctions. This combined process resulted in an extremely large resistance ratio (∼105) between the high and low-resistance states. The unprecedentedly large control found in atomically thin δ-doped oxide superlattices can open a door to novel oxide-based high-frequency logic devices.
Similar content being viewed by others
Introduction
In quantum well (QW) heterostructures, the probability of quantum mechanical tunnelling depends on the available quantized states at both the originating and the receiving sides of the junction. Therefore, the tunnelling current is usually not a monotonically increasing function with respect to the external bias. In particular, quantized resonant states can form in a QW between the two barriers, and can give rise to an interesting tunnelling behaviour, so called, resonant tunnelling (RT). Here, the energy of the wavefunctions with discrete levels can shift and align by applying an external bias (Fig. 1)1,2. When properly aligned, the tunnelling current peaks, exhibiting a negative differential resistance (NDR) just above the resonant bias (VR). Such an intriguing NDR behaviour can be exploited in various devices such as tunnel diodes and RT transistors. More importantly, the RT phenomena offer unique insight into electrical transport properties of materials, such as localized defect states, collective electronic excitations and QW band structures. Up to date, NDR and accompanying RT behaviours have been studied mostly in Si-based or III–V compound semiconductors1,2,3,4,5. Excellent crystalline quality of the conventional semiconductors and actual realization of two-dimensional (2D) heterostructures with nanometre thick barrier layers enabled the observation of the RT behaviour.
On the basis of recent advances in oxide thin-film synthesis, precision design of complex oxide thin films and heterostructures by pulsed laser epitaxy (PLE) or molecular beam epitaxy at the atomic scale has become available6,7,8. Indeed, many previous studies demonstrated emergent physical phenomena in conjunction with the quantum mechanical tunnelling in transition metal oxide (TMO)-based tunnel junctions, utilizing the exotic properties, including superconductivity9, magnetoresistance10,11, electroresistance12,13 and multiferroicity14. The strong coupling among charge, spin, lattice and orbital degrees of freedom has been investigated in terms of the various tunnelling behaviours, such as Josephson effect and spin-polarized tunnelling. More recently, a large electroresistance was also observed in ferroelectric tunnel junctions12. The tunnelling current across the ferroelectric layer is found to be efficiently controlled by not only the polarization direction, but also, more importantly, the interfacial electronic phase of the electrode layers13. Unfortunately, however, a clear RT behaviour has not been experimentally realized in TMO heterostructures.
Although a clear RT behaviour has not been widely explored with TMOs, the NDR behaviour itself has been reported in various complex oxide junction structures15,16,17,18. In particular, non-volatile resistance switching (RS) in TMO-based heterostructures has attracted scientific attention for developing next-generation memory devices based on memristors19,20,21. In typical RS devices, the electric resistance of a junction can be modulated by applying external bias, and the device can have two (or more) resistance states, that is, a high-resistance state (HRS) and a low-resistance state (LRS). The switching from a LRS to a HRS usually accompanies a NDR behaviour, as the amount of current decreases on increasing the bias above the switching voltage.
In the following, we investigate the junction transport property of a QW superlattice (SL) precisely designed by inserting atomically thin LaTiO3 (LTO) between SrTiO3 (STO) barrier layers. A clear RT behaviour with NDR is observed. Moreover, as oxide heterostructures can reveal RS, we further propose that the combination of RS with NDR is an efficient way to maximize the resistance ratio between the HRS and LRS in oxide QW heterostructures.
Results
Precision design of oxide quantum heterostructures
To realize a TMO QW heterostructure, a La δ-doped STO SL with atomically sharp interfaces was fabricated22. We believe that a sample with an excellent crystalline quality is highly necessary for the observation of the quantum resonant behaviour in TMOs. Therefore, we epitaxially grew a high quality [LTO1/STO6]10 SL with minimized defect states using our atomic scale synthesis capability6,8. Detailed information on the sample growth by PLE and experimental detail, as well as the excellent crystallinity of our SL is demonstrated in the Methods and Supplementary Fig. 1.
A schematic drawing of the SL structure is shown in Fig. 1a. It should be noted that La δ doping creates a 2D electron gas (2DEG) with high-density conducting carriers at the interface (0.5 electrons per unit cell), due to the leakage of the 3d1 electrons in La3+Ti3+O2−3 into the 3d0 states in Sr2+Ti4+O2−3 (refs 8, 23, 24, 25). The partial 3d electrons, or the distribution of the Ti3+ ions are confined around the LTO layer with the QW width of a few (5–6) unit cells23,26. On the other hand, it has been shown that the STO layer remains largely insulating and can serve as a barrier layer if the thickness is larger than three unit cells (u.c.)23,26. Therefore, the 2DEG formed at the interface can be considered as a QW with a thickness of a few nanometres, as shown in Fig. 1b. While many previous studies have focused on the in-plane electronic transport behaviours of such a 2DEG in titanate-based oxide heterostructures25,27,28, little is known about the out-of-plane junction properties29. In addition, unlike typical RT devices composed of tens of nanometres-thick semiconductor QWs, the tunnelling in our devices occurs through only an atomically thin layer, the fundamental lattice unit, providing a promising outlook for an ultrafast transit time.
Nonlinear current–voltage characteristics
Figure 2 shows the junction current–voltage characteristics of the TMO QWs at various temperatures. At room temperature, a weak hysteresis curve, which manifests the typical bipolar RS behaviour, was observed. The two different resistance states could be achieved by switching the polarity of the bias voltage. Indeed, the memory characteristics have been confirmed to show a typical RS behaviour. In general, understanding the switching mechanisms is a major challenge in achieving better non-volatile memory performance. To explain the bipolar RS phenomenon, various electric field polarity-dependent models, including ion migration19, Mott transition30 and formation of Schottky barrier31,32,33, have been suggested. In particular, the Schottky barrier formed at the interface has been identified to trigger the RS behaviour for Nb:STO-based junctions31,33. More specifically, changes in the Schottky barrier by either a charge trap at the defect states or oxygen migration due to applied bias voltage has been frequently attributed for the bipolar RS behaviour31,32,34. Similar mechanism, if not the same, seems to play a major role in our SL as well. As a qualitatively similar bipolar RS behaviour was also observed for a Pt/Nb:STO junction (inset of Fig. 2a), we believe that the RS behaviour originates mainly from the interface between the SL and Nb:STO.
As temperature decreases, the overall current level increases for both voltage polarities, and the RS becomes more distinct with a larger discrepancy between the LRS and HRS. Such temperature-dependent increase of the current level can be attributed to the largely enhanced carrier mobility and dielectric constant of STO at low temperatures25. In particular, similar temperature-dependence of the current level for the Pt/Nb:STO junction (inset of Fig. 2a) suggests that the bottom electrode Nb:STO is largely responsible for the increasing current level with decreasing temperature. At T<∼220 K, an interesting transport behaviour starts to develop at ∼1.2 V while maintaining the overall bipolar RS feature of our SL. A clear and smooth NDR behaviour is then observed by further ramping up the voltage to the positive bias direction. It should be noted that such a smooth peak in I(V) curve is significantly different from the usual abrupt NDR features observed for conventional RS in TMOs. For general RS (for both bipolar and unipolar), the current level drops immediately when the switching occurs from a LRS to a HRS, in stark contrast to what we observe here. Moreover, a further increase in the current above the clear peak feature in I(V) curve was observed, which has never been reported for conventional RS, to the best of our knowledge. These characteristic features signify that the origin of NDR in our QW SLs is fundamentally different from that of the conventional RS often observed in oxide thin films.
It is also important to point out that the NDR behaviour uniquely originates from the TMO QW structure. I(V) curves for a Pt/Nb:STO junction as a function of temperature shown in the inset of Fig. 2a represent only a typical bipolar RS behaviour of Nb:STO junctions. While similar RS behaviours have been observed for various Nb:STO-based junctions as discussed previously32,33, the smooth peak feature and clear NDR behaviour were absent, indicating that the deliberately designed TMO SL with QWs is indeed responsible for the unique feature. Moreover, on differentiating the I(V) curves of the SLs as shown in Fig. 2b, we indeed find two clear zero-crossing points for T<200 K. This result again indicates that the NDR is a consequence of the resonant states formed inside the QWs, rather than associated with the conventional RS. Observation of NDR only at lower temperature possibly due to the reduced phonon scattering further confirms the RT behaviour.
Theoretical calculations on resonant tunnelling
To verify that the NDR behaviour indeed originates from RT, we have performed a theoretical analysis by taking into account the band gap, effective mass and dielectric constant (ɛr) of the TMO heterostructure (see Methods section for detail). Among these parameters, ɛr of an oxide heterostructure with 2DEGs has not been widely studied. However, it is expected that the creation of interfacial charges would drastically reduce the ɛr value of the highly dielectric STO. As this change leads to a significant modification in the dielectric screening of the conducting carriers, we focus here on the effect of ɛr. Figure 3 shows the evolution of energy levels of the quantized states and VR for [LTO1/STO6]10 SL as a function of ɛr. The quantized energy levels show the values in the absence of external electric field. The actual potential wells and wavefunctions within the well with corresponding energy levels are represented in Fig. 1b for ɛr=100. As ɛr increases, the well becomes shallower, weakening the quantum confinement—that is, both the energy difference between the states and the number of confined states are reduced upon the increase of ɛr. For ɛr≤100, the well is deep enough to accommodate three confined states (ground, first and second excited states) within the QW, while only two confined states are possible for ɛr>100 (Fig. 3a). On the basis of the energy level separation and the QW geometry, we can calculate VR as a function of ɛr (Fig. 3b). As ɛr increases, a smaller VR is expected because of the smaller energy difference between the ground and first excited states. For ɛr=100, VR=1.23 V is needed to induce RT between the ground and first excited states in the deliberately designed oxide SL, as shown in Fig. 1c. The theoretical calculation implies that it would be rather difficult to observe a well-defined higher order peak in the tunnelling current. The confinement of the second excited state is only possible for ɛr<100 ideally. Even then, the state becomes easily unbound by applying a small electric field. Practically, the overall high current level makes it impossible to observe clear high-voltage features. Especially, the current substantially increased to a very high level at low temperature and the current compliance set to prevent thermal damage of the oxide QW obscures the peak feature. (We noted some temperature fluctuation near the lowest temperature due to the Joule heating, but the I(V) characteristic was highly stable and reproducible.)
Discussion
It should be noted that the RT behaviour is observed for the positive bias only, which can be attributed to the asymmetric sample geometry and resultant current profile. The current level for the negative bias is too large (for both HRS and LRS), possibly hindering the observation of the NDR behaviour. In addition, the current reaches to the compliance limit much faster, which makes it even more difficult to observe the NDR behaviour for the negative bias. Finally, the I(V) characteristic of our oxide device is remarkably similar to that from a SiO2/Si resonant tunnelling diode,4 strongly supporting that the NDR behaviour is based on RT in our TMO heterostructure.
We note that a few previous studies on TMO junctions claimed an observation of resonant states16,35. These reports indicated that resonant states could be formed with VR on the order of 0.1–1.0 V due to defects or impurity states. The observations are based on the chemical doping, that is, oxygen vacancies in SrTiO3−δ and Mn doping into SrRuO3 (SrRu0.95Mn0.05O3) for Pt/SrTiO3−δ and SrRu0.95Mn0.05O3/Nb:STO interfaces, respectively. On the other hand, our discovery of clear RT is based on a deliberately designed TMO QW SL, which might provide an unprecedented opportunity to develop novel tunnelling oxide electronic devices.
The observation of RT behaviour further provides quantitative information useful for understanding the physics of RT phenomena and insight for technological applications. We note that such a quantitative analysis could not be conducted on TMO QWs, as RT behaviour has never been observed previously. As the RT lifetime (τRT) is important to understand the tunnelling behaviour of electrons through the TMO QW, we have computed τRT using the energy uncertainty condition at the energy corresponding to the RT, that is, τRT=ħ/2ΔE, where ħ=h/2π, h is the Planck’s constant and ΔE is the half width at half maximum of the resonant peak36. Due to the broad feature of the resonance peak (∼1 eV) for our TMO QW, we obtain a rather small τRT value (∼0.7 fs), which is orders of magnitude smaller than that obtained in semiconductor QWs36. This value is also rather small compared with the traverse lifetime across the tunnelling barrier, and therefore, strong coherence is not expected in the complex oxide QWs. In fact, the small τRT in our QW SL is expected as such a heterostructure has a rather small relaxation time (τμ=∼42.4 fs)24 of the charge carriers, which is also orders of magnitude smaller than those obtained from conventional semiconductors, due possibly to strong correlation37. In addition, the peak-to-valley current ratio (PVCR) and the peak current density (PCD) of our TMO-based RT diode are about 1.3 and 120 A cm−2, respectively, at the lowest temperature (4 K). PVCR is rather small compared with that of conventional semiconductor RT diodes where the typical value is >3 at room temperature. On the other hand, PCD of semiconductor RT diodes span seven orders of magnitude from tens of mA cm−2 to hundreds of kA cm−2. Therefore, the PCD value we have measured from our TMO RT device is within the range of the semiconductor-based RT diodes.
The RT behaviour in our oxide QW SL enhances yet another advantageous functionality, which is unique to the TMOs. Indeed, the resistance ratio between the HRS and LRS is observed to be largely enhanced due to the RT feature. Figure 4 shows the junction resistance of the HRS and LRS measured at 0.5 and –0.5 V, respectively, as a function of temperature. The inset shows the resistance plot as a function of applied bias voltage. The difference between the HRS and LRS resistance increased with decreasing temperature. Below 150 K, we observed the ON/OFF ratio to be larger than 105, while it was slightly larger than 10 at room temperature. Typically, the ON/OFF ratio for bipolar RS is about 102, much smaller than that for unipolar RS. The completely different temperature-dependent behaviour of the resistance (HRS shows insulating behaviour while LRS shows metallic temperature-dependent behaviour) mainly due to the RT feature greatly enhances the ON/OFF ratio. Below 120 K, the compliance current played a role, somewhat decreasing the HRS resistance value (empty symbols in red). Nevertheless, we could still observe a large resistance ratio (∼105) with an increasing trend towards the lowest temperature we employed. Undoubtedly, such a large enhancement in the resistance ratio stems from the RT behaviour of the QW SL. The drastically enhanced tunnelling probability near the resonant bias voltage substantially decreased the resistance of the LRS near VR. The dip feature for the resistance value at ∼1 V for the LRS shown in the inset of Fig. 4 clearly signifies the enhanced tunnelling probability.
In summary, we have observed an intriguing NDR feature in a SrTiO3/LaTiO3/SrTiO3 QW superlattice at low temperatures. The NDR behaviour is attributed to a resonant tunnelling occurring through the deliberately designed oxide QWs. In particular, because of the existence of the resonant tunnelling, a largely enhanced ON/OFF ratio has been achieved in the bipolar resistance switching, which occurs at the interface between the heterostructure and metallic substrate. Our study also demonstrates the potential of oxide heterostructures for a quantum mechanical behaviour that has been thought to be possible only in conventional semiconductor heterostructures. Thus, we believe that the discovery of resonant tunnelling through oxide-based QWs can lay down a stepping stone to oxide electronics.
Methods
Sample fabrication
A [(LaTiO3)1/(SrTiO3)6]10 SL sample was fabricated at 700 °C in 10−5 torr of oxygen partial pressure using pulsed laser epitaxy. A KrF excimer laser (λ=248 nm) with a laser fluence of ∼1 J cm−2 was used for ablation of a single crystal STO and a sintered La2Ti2O7 target. An atomically flat TiO2 layer terminated (001) Nb-doped STO (0.05 wt%) single crystal buffered with 10 u.c. of STO was used as a substrate. The 10 u.c. STO buffer layer was used to ensure a good surface and interface quality of the oxide QW. The growth process was monitored using reflection high-energy electron diffraction (RHEED), ensuring the layer-by-layer growth. Supplementary Fig. 1a shows an oscillation of the RHEED specular spot intensity as a function of growth time. Six u.c. layers of STO and one u.c. layer of LTO were consecutively deposited. The in situ RHEED pattern along the [100] direction of the substrate before the SL growth (Supplementary Fig. 1b) is clearly maintained even after the growth (Supplementary Fig. 1c), indicating an optimized 2D layer-by-layer growth. The surface topographic image by atomic force microscopy (the background of Supplementary Fig. 1d) also presents a well-conserved ∼0.4 nm high step-and-terrace structure of the substrate even after the deposition of the SL, indicating atomically well-defined surface and interface. After the growth, the SL sample was in situ post-annealed for 10 min at the growth temperature in a relatively high-oxygen pressure ambience (10−2 torr) and then cooled in the same pressure to fully compensate potential oxygen vacancies. We note that the low-pressure growth and subsequent post-annealing are necessary steps for the growth of the perovskite LaTiO3, as it has a very narrow growth window for oxygen pressure. The growth at higher oxygen pressure results in La2Ti2O7 or impurity phases. X-ray diffraction θ–2θ scan demonstrated that the designed SL structure was realized (Supplementary Fig. 1d). Excellent crystallinity was confirmed from the rocking curve scan as shown in Supplementary Fig. 1e (for example, 006 peak of the SL). The full-width-at-half-maximum value was comparable to that of the Nb-doped substrate. Reciprocal space mapping around the 114 Nb:STO substrate reflection confirms the fully-strained SL sample (Supplementary Fig. 1f).
Electrical characterization
The top electrode Pt (∼300 μm in diameter) was patterned by RF sputtering on top of the sample surface using a shadow mask. External bias was applied to the Nb:STO substrate, which served as the bottom electrode. The temperature-dependent current–voltage (I(V)) curve was measured using a physical property measurement system (Quantum Design Inc.) with a source measure unit (Kethley 236). The current compliance (0.1 A) and the maximum sweep voltage value (−2 to 4 V) were set to prevent the device from damaging.
Theoretical calculation
The shape of electrostatic potential (Fig. 1b) induced by La δ-doping in STO was obtained by solving the Poisson and the Schrödinger equation self-consistently, without any electric field applied. The self-consistent calculations were performed iteratively using Broyden’s second method until the convergence of the electrostatic potential is reached.38 An external electric field was then applied to obtain envelope wavefunctions and energy levels of electrons (Fig. 1c). We examined ɛr values of STO in the range of 10–103, (note, while ɛr of bulk STO at low temperature is known to be very large, ɛr strongly varies with the electric field, temperature and sample geometry) and effective mass of 4.4 (out-of-plane band effective mass of STO) was used for the calculations39.
Additional information
How to cite this article: Choi, W.S. et al. Resonant tunnelling in a quantum oxide superlattice. Nat. Commun. 6:7424 doi: 10.1038/ncomms8424 (2015).
References
Chang, L. L., Esaki, L. & Tsu, R. Resonant tunneling in semiconductor double barriers. Appl. Phys. Lett. 24, 593–595 (1974).
Dingle, R., Wiegmann, W. & Henry, C. H. Quantum states of confined carriers in very thin AlxGa1-xAs-GaAs-AlxGa1-xAs heterostructures. Phys. Rev. Lett. 33, 827–830 (1974).
Jian Ping, S., Haddad, G. I., Mazumder, P. & Schulman, J. N. Resonant tunneling diodes: models and properties. Proc. IEEE 86, 641–660 (1998).
Ikeda, H., Iwasaki, M., Ishikawa, Y. & Tabe, M. Resonant tunneling characteristics in SiO2/Si double-barrier structures in a wide range of applied voltage. Appl. Phys. Lett. 83, 1456–1458 (2003).
Bending, S. J. & Beasley, M. R. Transport processes via localized states in thin a-Si tunnel barriers. Phys. Rev. Lett. 55, 324–327 (1985).
Lee, H. N., Christen, H. M., Chisholm, M. F., Rouleau, C. M. & Lowndes, D. H. Strong polarization enhancement in asymmetric three-component ferroelectric superlattices. Nature 433, 395–399 (2005).
Lee, C.-H. et al. Exploiting dimensionality and defect mitigation to create tunable microwave dielectrics. Nature 502, 532–536 (2013).
Choi, W. S., Lee, S., Cooper, V. R. & Lee, H. N. Fractionally δ-doped oxide superlattices for higher carrier mobilities. Nano Lett. 12, 4590–4594 (2012).
Tanaka, Y. & Kashiwaya, S. Theory of tunneling spectroscopy of d-wave superconductors. Phys. Rev. Lett. 74, 3451–3454 (1995).
Hwang, H. Y., Cheong, S. W., Ong, N. P. & Batlogg, B. Spin-polarized intergrain tunneling in La2/3Sr1/3MnO3 . Phys. Rev. Lett. 77, 2041–2044 (1996).
De Teresa, J. M. et al. Role of metal-oxide interface in determining the spin polarization of magnetic tunnel junctions. Science 286, 507–509 (1999).
Tsymbal, E. Y. & Kohlstedt, H. Tunneling across a ferroelectric. Science 313, 181–183 (2006).
Jiang, L. et al. Tunneling electroresistance induced by interfacial phase transitions in ultrathin oxide heterostructures. Nano Lett. 13, 5837–5843 (2013).
Gajek, M. et al. Tunnel junctions with multiferroic barriers. Nat. Mater. 6, 296–302 (2007).
Keiji, S., Hiroyasu, K., Takeshi, Y. & Manabu, G. Origin of negative differential resistance observed on bipolar resistance switching device with Ti/Pr0.7Ca0.3MnO3/Pt structure. Appl. Phys. Express 1, 055002 (2008).
Hikita, Y. et al. Negative differential resistance induced by Mn substitution at SrRuO3/Nb: SrTiO3 Schottky interfaces. Phys. Rev. B 77, 205330 (2008).
Xiao, Y. S., Zhang, X. P. & Zhao, Y. G. Negative differential resistance in La0.67Ca0.33MnO3−δ/Nb–SrTiO3 p-n junction. Appl. Phys. Lett. 90, 013509 (2007).
Du, Y. et al. Symmetrical negative differential resistance behavior of a resistive switching device. ACS Nano 6, 2517–2523 (2012).
Waser, R. & Aono, M. Nanoionics-based resistive switching memories. Nat. Mater. 6, 833–840 (2007).
Sawa, A. Resistive switching in transition metal oxides. Mater. Today 11, 28–36 (2008).
Yang, J. J., Strukov, D. B. & Stewart, D. R. Memristive devices for computing. Nat. Nanotech. 8, 13–24 (2013).
Choi, W. S. et al. Atomic layer engineering of perovskite oxides for chemically sharp heterointerfaces. Adv. Mater. 24, 6423–6428 (2012).
Ohtomo, A., Muller, D. A., Grazul, J. L. & Hwang, H. Y. Artificial charge-modulation in atomic-scale perovskite titanate superlattices. Nature 419, 378–380 (2002).
Seo, S. S. A. et al. Optical study of the free-carrier response of LaTiO3/SrTiO3 superlattices. Phys. Rev. Lett. 99, 266801 (2007).
Kim, J. S. et al. Nonlinear Hall effect and multichannel conduction in LaTiO3/SrTiO3 superlattices. Phys. Rev. B 82, 201407 (2010).
Cooper, V. R. et al. Transparent conducting oxides: A δ-doped superlattice approach. Sci. Rep. 4, 6021 (2014).
Ohtsuka, R., Matvejeff, M., Nishio, K., Takahashi, R. & Lippmaa, M. Transport properties of LaTiO3/SrTiO3 heterostructures. Appl. Phys. Lett. 96, 192111 (2010).
Biscaras, J. et al. Two-dimensional superconductivity at a Mott insulator/band insulator interface LaTiO3/SrTiO3 . Nat. Commun. 1, 89 (2010).
Singh-Bhalla, G. et al. Built-in and induced polarization across LaAlO3/SrTiO3 heterojunctions. Nat. Phys. 7, 80–86 (2011).
Rozenberg, M. J., Inoue, I. H. & Sánchez, M. J. Nonvolatile memory with multilevel switching: a basic model. Phys. Rev. Lett. 92, 178302 (2004).
Fujii, T. et al. Hysteretic current–voltage characteristics and resistance switching at an epitaxial oxide Schottky junction SrRuO3/SrTi0.99Nb0.01O3 . Appl. Phys. Lett. 86, 012107 (2005).
Chen, X. G. et al. Comprehensive study of the resistance switching in SrTiO3 and Nb-doped SrTiO3 . Appl. Phys. Lett. 98, 122102 (2011).
Park, C., Seo, Y., Jung, J. & Kim, D.-W. Electrode-dependent electrical properties of metal/Nb-doped SrTiO3 junctions. J. Appl. Phys. 103, 054106 (2008).
Fujii, T. et al. Electrical properties and colossal electroresistance of heteroepitaxial SrRuO3/SrTi1-xNbxO3 (0.0002≤x≤0.02) Schottky junctions. Phys. Rev. B 75, 165101 (2007).
Son, J. & Stemmer, S. Resistive switching and resonant tunneling in epitaxial perovskite tunnel barriers. Phys. Rev. B 80, 035105 (2009).
Price, P. J. Theory of resonant tunneling in heterostructures. Phys. Rev. B 38, 1994 (1988).
Sze, S. M. & Ng, K. K. Physics of Semiconductor Devices John Wiley & Sons, Inc. (2007).
Eyert, V. A comparative study on methods for convergence acceleration of iterative vector sequences. J. Comput. Phys. 124, 271–285 (1996).
Wunderlich, W., Ohta, H. & Koumoto, K. Enhanced effective mass in doped SrTiO3 and related perovskites. Physica B: Condens. Matter 404, 2202 (2009).
Acknowledgements
We thank In Rok Hwang, Taekjib Choi, Cheol Seong Hwang and Shinbuhm Lee for valuable discussions. This work was supported by the U.S. Department of Energy, Office of Science, Basic Energy Sciences, Materials Sciences and Engineering Division (W.S.C. and H.N.L.). The work on leakage current analysis was in part supported by Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science, ICT and future Planning (NRF-2014R1A2A2A01006478, W.S.C.) and by the Ministry of Education (NRF-2013R1A1A2057523, S.A.L.). S.L. was supported by KIST Institutional Program (Project No. 2E25440).
Author information
Authors and Affiliations
Contributions
W.S.C. and H.N.L. conceived the experiment, synthesized the sample by PLE, and performed structural characterization. W.S.C., S.A.L. and S.L. carried out the electrical measurements. J.H.Y. performed theoretical calculations. W.S.C. and H.N.L. wrote the manuscript with discussions and improvements from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-3, Supplementary Notes 1-3 and Supplementary References (PDF 350 kb)
Rights and permissions
About this article
Cite this article
Choi, W., Lee, S., You, J. et al. Resonant tunnelling in a quantum oxide superlattice. Nat Commun 6, 7424 (2015). https://doi.org/10.1038/ncomms8424
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms8424
This article is cited by
-
Resonant tunneling driven metal-insulator transition in double quantum-well structures of strongly correlated oxide
Nature Communications (2021)
-
Controllable potential barrier for multiple negative-differential-transconductance and its application to multi-valued logic computing
npj 2D Materials and Applications (2021)
-
Resonant tunnelling diodes based on twisted black phosphorus homostructures
Nature Electronics (2021)
-
ZnO composite nanolayer with mobility edge quantization for multi-value logic transistors
Nature Communications (2019)
-
Tuning the charge flow between Marcus regimes in an organic thin-film device
Nature Communications (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.