High-power Na-ion batteries have tremendous potential in various large-scale applications. However, conventional charge storage through ion intercalation or double-layer formation cannot satisfy the requirements of such applications owing to the slow kinetics of ion intercalation and the small capacitance of the double layer. The present work demonstrates that the pseudocapacitance of the nanosheet compound MXene Ti2C achieves a higher specific capacity relative to double-layer capacitor electrodes and a higher rate capability relative to ion intercalation electrodes. By utilizing the pseudocapacitance as a negative electrode, the prototype Na-ion full cell consisting of an alluaudite Na2Fe2(SO4)3 positive electrode and an MXene Ti2C negative electrode operates at a relatively high voltage of 2.4 V and delivers 90 and 40 mAh g−1 at 1.0 and 5.0 A g−1 (based on the weight of the negative electrode), respectively, which are not attainable by conventional electrochemical energy storage systems.
Electrochemical energy storage capable of more energy at high charge−discharge rates is receiving considerable attention because of the strong industrial demands for their widespread use in the smart grid. High-energy Li-ion batteries consisting of Li+ (de)intercalation electrodes currently power most portable electronics, but the power density is not satisfactory for high-power applications1,2. High-power electrochemical capacitors make up many markets ranging from electronics to transportation and stationary applications, but the low energy density is a serious disadvantage3,4. This trade-off between the power and energy densities of electrochemical energy storage has been well recognized, which intrinsically originates from the charge storage mechanism of the electrodes: ion (de)intercalation in batteries and double-layer formation in electrochemical capacitors. In general, ion (de)intercalation stores charge more slowly than a double layer, whereas a double layer stores less charge than ion (de)intercalation3. Thus, the pseudocapacitance (or redox capacitance) has become an increasingly important mechanism for charge storage5,6,7,8,9,10. Pseudocapacitance occurs through (i) monolayer ion adsorption on the electrode surface with charge transfer, (ii) redox at the electrode surface (RuO2·xH2O, ref. 5) or (iii) ultrafast ion intercalation into the bulk (T-Nb2O5, ref. 6), whereby charge storage is partially liberated from the trade-off.
At present, urgent concerns over lithium resources have focused recent attention on Na-ion batteries owing to the abundance and low cost of sodium. The present set of negative-electrode materials for Na-ion batteries mainly consists of Na-ion intercalation, alloying or conversion materials such as hard carbon, expanded graphite, TiO2, Na2Ti3O7, phosphorus, Sb2S3, Sn4+xP3, SnS2 and P2-Na0.66[Li0.22Ti0.78]O2 (refs 11, 12, 13, 14, 15, 16, 17, 18, 19). However, their energy and power densities severely suffer from the trade-off, and the large volume change accompanied by the reaction with the large Na ion generally results in poor cycle stability, both of which have spurred us to develop new negative electrodes based on pseudocapacitive charge storage for advanced Na-ion systems.
We have targeted MXenes as pseudocapacitor electrodes in this study. MXenes have been developed as a novel family of nanosheet compounds by Gogotsi, Barsoum and colleagues20,21,22,23,24,25 MXenes are chemically derived from layered Mn+1AXn or MAX phases, where M is an early transition metal, A is an A-group element and X is C and/or N26. For example, a hydrofluoric-acid treatment of Ti3AlC2 selectively extracts the aluminum layer, resulting in an exfoliated nanosheet compound, the MXene Ti3C2 (Ti3C2Tx where Tx denotes surface function groups), which has a surface terminated with OH, F and O. Importantly, the MXene has both a high electrical conductivity and large surface area; therefore, its application to pseudocapacitor electrodes holds great promise. Indeed, the pseudocapacitance of Ti3C2Tx, Ti2CTx, V2CTx and Nb2CTx in nonaqueous Li-ion electrolytes delivers a specific capacity >100 mAh g−1 below 2 V versus Li/Li+ (refs 22, 27, 28, 29, 30, 31, 32).
Here, we report on Ti2CTx as a negative electrode material for Na-ion hybrid capacitors. The pseudocapacitance of Ti2CTx allows Na-ion hybrid capacitors to be liberated from the trade-off between high energy and high power.
Electrochemical properties of Ti2CT x
Ti2CTx was synthesized by treating the MAX phase Ti2AlC with a 10% HF aqueous solution. Powder X-ray diffraction (XRD) shows the expansion of the interlayer distance by the hydrofluoric acid (HF) treatment, suggesting successful removal of the Al layers by the HF treatment (Supplementary Fig. 1). The significant decrease in the amount of Al according to energy dispersive X-ray spectroscopy (EDX) supports the selective extraction of Al. A delamination process such as sonication was not conducted22; therefore, Ti2CTx in this work is a multilayered MXene, as imaged by scanning electron microscopy (Supplementary Fig. 2).
The Ti2CTx electrode in a nonaqueous Na+ electrolyte behaves differently than in an aqueous Na+ electrolyte or a nonaqueous Li+ electrolyte. Figure 1a shows the cyclic voltammetry (CV) and corresponding ex situ XRD patterns of the MXene Ti2C in a 1 M NaPF6/ethylene carbonate (EC)−diethyl carbonate (DEC) electrolyte. Lukatskaya et al.23 reported that Ti3C2Tx placed in various aqueous salt (NaOH, KOH, LiOH and so on) solutions exhibits a downshift in the (002) diffraction peak in the XRD pattern, corresponding to spontaneous cation intercalation. In contrast, Ti2CTx immersed in a nonaqueous 1 M NaPF6/EC−DEC electrolyte exhibits no downshift in the (002) diffraction peak by immersion into the electrolyte alone, which indicates that Na+ intercalation does not occur spontaneously. The first cathodic scan exhibits an irreversible current below 1.0 V versus Na/Na+ and an associated downshift in the (002) diffraction peak. As EDX confirms an increase in the Na content in Ti2CTx (Supplementary Table S1), Na+ is definitely intercalated/adsorbed into/onto the MXene sheets electrochemically. On the basis of the shift in the (002) diffraction peak, the expansion of the interlayer distance is estimated as 2.5 Å. The expansion is also confirmed by transmission electron microscopy images (Fig. 1b,c). Because the expansion is consistent with the size of bare Na+, Na+ intercalation occurs after desolvation at the electrode/electrolyte interface during the initial reduction process (Fig. 2, activation).
After initial Na+ intercalation, Ti2CTx exhibits pseudocapacitor behaviour. The subsequent CV cycles after the first cycle exhibit the stable rectangular-shaped CV below ~2.0 V, corresponding to typical capacitor behaviour. In addition, a reversible pair of relatively sharp cathodic/anodic peaks is observed at ~2.3 V in each cycle. Although the (002) diffraction peak does not shift during the cycles, EDX confirms a reversible change in the Na content, and X-ray photoelectron spectroscopy (XPS) detects a reversible spectral change in the Ti 2p XPS spectrum (Supplementary Fig. 3), which is indicative of a charge transfer reaction. Therefore, the current flow from Ti2CTx in the nonaqueous Na+ electrolyte is attributable to the pseudocapacitance without exhibiting shrinkage/expansion of the interlayer distance.
As reported previously, Ti3C2Tx and Ti2CTx in a nonaqueous Li+ electrolyte exhibit shrinkage/expansion of the interlayer distance during the cycle27,28. For example, Ti2CTx in a nonaqueous Li+ electrolyte exhibits a change in the interlayer distance between 18.7 and 18.0 Å (4% change). In contrast, bare Na+ is intercalated between the MXene sheets for Ti2CTx in a nonaqueous Na+ electrolyte to expand the interlayer distance from 7.7 to 10.1 Å during the first cathodic process (Fig. 2, activation). Then, activated Ti2CTx allows reversible Na+ intercalation/deintercalation into the interlayer space as well as reversible Na+ adsorption/desorption onto the surface of each layer/sheet, where the change in the interlayer distance is small within ~0.1 Å (Fig. 2 and Supplementary Table 2). Because EDX detects residual Na+, even at 3.0 V (Supplementary Table 1), residual Na+ may behave as a pillar between the MXene Ti2C layers during the entire charge/discharge process, maintaining the interlayer distance at an almost constant value. Another possible explanation for the constant interlayer distance is that the expansion due to Na+ intercalation is balanced by the Coulombic attraction between the MXene sheets and intercalated Na33.
The CV curves of activated Ti2CTx measured at various scan rates (Supplementary Fig. 4) provide insights into the reaction kinetics. The b-value analysis (i=avb; i: current; v: scan rate; a, b: constants) for the peak current at ~2.3 V gives a b-value of unity for 0.05<v<0.5 mV s−1, which is indicative of a surface-controlled reaction. Presumably, (de)solvation or charge transfer at the interface rather than slow Na+ diffusion in the bulk determines the reaction rate.
Ti2CT x as negative-electrode material
Having confirmed that activated Ti2CTx is a promising candidate as a negative-electrode material for Na-ion hybrid capacitors, galvanostatic charge/discharge experiments were conducted. Here, charging is a cathodic process (Na+ adsorption/intercalation), whereas discharging is an anodic process (Na+ desorption/deintercalation). Figure 3a shows the charge−discharge curves measured between the cut-off voltages of 0.1−3.0 V versus Na/Na+ at 20 mA g−1. The first charge exhibits a voltage plateau at ~0.6 V, delivering a relatively large capacity of 360 mAh g−1. The following first discharge curve has a capacitor-type slope in the range of 0.2−2.5 V but with a much smaller capacity, resulting in a relatively low Coulombic efficiency of 65% for the first cycle. However, after the initial few cycles for activation, Ti2CTx exhibits stable and efficient electrode performance. The charge/discharge profiles exhibit a capacitor-type slope in the range of 0.1−2.3 V (an average operating potential of 1.3 V), delivering a reversible capacity of ~175 mAh g−1 with good cycle stability (Fig. 3b, 12 and 19% losses of the second capacity after 50 and 100 cycles, respectively). The average operating potential of 1.3 V is relatively high when used as the negative electrode but is beneficial for stable operation, retaining the capacity at a high rate and avoiding Na metal plating for safety.
The Na/Ti elemental ratio determined by EDX during the first two cycles allow us to estimate the capacity (Supplementary Fig. 5) for various possible nominal chemical formulae of Ti2CTx (Ti2CO2, Ti2C(OH)2 and Ti2CF2). The first experimental charge capacity (359 mAh g−1) is larger than the estimated ones (308−321 mAh g−1), whereas the first discharge capacity (233 mAh g−1) is close to the estimated ones (224−234 mAh g−1). Thus, the initial irreversible capacity arises from the decomposition of the electrolyte as well as the residual Na+ between the MXene layers (vide supra). The electrolyte decomposition during the initial cycles may form stable solid−electrolyte interface, which inhibits continuous electrolyte decomposition.
Figure 3c shows the charge/discharge profiles of Ti2CTx at various specific currents. The reversible capacity is retained, even at extremely high rates (156, 113 and 63 mAh g−1 at 200, 1,000 and 5,000 mA g−1, respectively). Figure 3d compares the rate capability of Ti2CTx, hard carbon11, expanded graphite12 and P2-Na0.66[Li0.22Ti0.78]O2 (ref. 19). Although the carbon compounds (expanded graphite and hard carbon) deliver a high capacity of ~300 mAh g−1 at a low rate, the capacity retention at high rates is much lower than that of Ti2CTx. P2-Na0.66[Li0.22Ti0.78]O2 is an electrode material without a change in lattice volume during the cycle; therefore, the minimum structural change associated with (de)sodiation enables a high capacity retention at high rates. However, the theoretical capacity of P2-Na0.66[Li0.22Ti0.78]O2 is much smaller than that of Ti2CTx; Ti2CTx delivers much higher capacity at any charge/discharge rate. Therefore, Ti2CTx is a high-performance electrode material with a high capacity, stability, safety and a high power. It should be emphasized that the high rate capability was obtained with a thick electrode (thickness: 50 μm); therefore, its practical application to Na-ion hybrid capacitors is highly realistic.
Full cell with Ti2CTx and Na2Fe2(SO4)3
To further demonstrate the potential of Ti2CTx in Na-ion hybrid capacitors, a prototype full cell (Fig. 4a) was fabricated by utilizing Ti2CTx as a negative electrode and alluaudite Na2Fe2(SO4)3 as a positive electrode. Recently, our group has discovered alluaudite Na2Fe2(SO4)3 as a promising positive-electrode material that exhibits a specific capacity of 100 mAh g−1 at a high operating potential of 3.8 V versus Na/Na+, the highest value among all Fe-based compounds, which enables the Na-ion full cell to achieve both high energy and high power densities34,35. The mass balance between the positive and negative electrodes was fixed to 4:1 to ensure full activation of Ti2CTx during the first charge.
Figure 4b shows the charge/discharge curves for the full cell measured at current densities of 150 and 600 mA g−1 (based on the weight of Ti2CTx). Note that the first cycle was conducted at 20 mA g−1 (based on the weight of Ti2CTx) to activate Ti2CTx. After the first cycle, the cell exhibits a voltage profile that mainly reflects the potential of Ti2CTx because the cell capacity is limited by the Ti2CTx negative electrode (Fig. 3a). The average operating voltage is 2.4 V, and the reversible capacities of the second cycle are 133 and 107 mAh g−1 at 150 and 600 mA g−1 (based on the weight of Ti2CTx), respectively, achieving theoretical energy densities of 320 and 260 Wh kg−1 at specific power densities of 360 and 1,440 W kg−1 (based on the weight of Ti2CTx), respectively.
Both the cycle stability and efficiency of the full cell are extremely high. As demonstrated in Fig. 4c, the loss of the discharge capacity after 100 cycles at 600 mA g−1 is only 4% of the second discharge capacity. Furthermore, the Coulombic efficiency for cycling at 600 mA g−1 reaches ~99.7% after a few initial cycles. The excellent cycle stability and efficiency may be attributed to the pseudocapacitive charge storage mechanism without a large structural change.
Figure 4d plots the charge/discharge profiles of the alluaudite Na2Fe2(SO4)3−Ti2CTx full cell at various current rates, demonstrating the promising high-power performance of the cell (Supplementary Fig. 6). The full cell provides reversible capacities of 90 and 40 mAh g−1, even at extremely high rates of 1,000 and 5,000 mA g−1 (based on the weight of Ti2CTx). Thus, by utilizing the pseudocapacitive negative electrode, the Na-ion hybrid capacitor overcomes the trade-off limit and potentially surpasses state-of-the-art high-power rechargeable batteries. Although the capacity for the total weight of the positive and negative electrode materials in the present prototype cell is limited (26.6 mAh g−1 at a low rate) owing to the excess amount of positive-electrode material, an improvement in the initial Coulombic efficiency could reduce the amount of positive-electrode material, and hence, greatly increase the capacity of the full cell.
Finally, we note a positive perspective for further improvement in the Ti2CTx electrode. The gravimetric capacitance from CV of the Ti2CTx electrode in this work is higher than that of previously reported Ti3C2Tx electrodes because of the light weight of Ti2CTx (Supplementary Fig. 7). However, very recently, Ghidui et al.36 have reported a new method to synthesize Ti3C2Tx (Ti3C2Tx ‘clay’) using a solution of lithium fluoride and hydrochloric acid. The resulting Ti3C2Tx ‘clay’ delivers a high volumetric capacitance of 900 F cm−3 and a gravimetric capacitance of 245 F g−1, which is much higher than those of the previously reported Ti3C2Tx electrodes and the Ti2CTx electrode in this work. According to Ghidui et al.36, the Ti3C2Tx clay provides a much higher capacitance at higher rates owing to the improved accessibility of the interlayer spacing. Therefore, the synthetic procedure applied for the Ti3C2Tx clay, that is, the LiF+HCl treatment, could further improve the performance of Ti2CTx.
In summary, the use of the pseudocapacitance of MXene nanosheets was demonstrated as an effective strategy for developing high-performance Na-ion hybrid capacitors. A pseudocapacitance with no significant structural changes can store more charge at a faster charge–discharge rate relative to the ion intercalation and double-layer mechanisms. In the present case, Ti2CTx operates as a pseudocapacitor electrode material at 1.3 V on average versus Na/Na+ with a reversible capacity of 175 mAh g−1. The alluaudite Na2Fe2(SO4)3−Ti2CTx prototype cell delivers a high specific energy of 260 Wh kg−1 at a high specific power of 1.4 kW kg−1 (based on the weight of Ti2CTx), which overcomes the trade-off limit associated with conventional electrochemical energy storage. By exploiting the compositional and structural versatility of MAX phases and the resulting optimized MXenes, we could further extend the possible sets of electrodes for advanced Na-ion hybrid capacitors.
Synthesis of Ti2CT x
Ti2AlC was prepared by heating a precursor mixture of TiC (>99%, High Purity Chemicals, Japan), Ti (>99%, High Purity Chemicals, Japan) and Al (>99.9%, High Purity Chemicals, Japan) at 1,300 °C for 1 h in an Ar gas environment. Ti2CTx was synthesized by treating 1 g of Ti2AlC powder in 10% HF aqueous solution (Wako) for 12 h at room temperature. The HF-treated powder was dried in vacuum at 60 °C for 24 h.
Powder X-ray diffraction patterns were recorded on a Rigaku RINT-TTR III powder diffractometer with Cu Kα radiation in a step of 0.02° over a 2θ range of 10−80°. Scanning electron microscopy measurements were carried out on a JEOL 6510FA apparatus equipped with an energy dispersive X-ray (EDX) spectrometer for chemical analysis. Transmission electron microscopy was conducted on a JEOL JEM-2100 at 200 kV. X-ray photoelectron spectroscopy (XPS) data were collected using a ULVAC PHI 5000 VersaProbe spectrometer with monochromatized Al Kα radiation (hv=1,486.6 eV). The pressure in the analysis chamber during the measurements was maintained in the 10−7 Pa range. The powder sample was pressed onto conductive carbon, and peaks were recorded with a constant pass energy mode of 117 eV for survey investigation. High-resolution spectra were taken at a pass energy of 23 eV, with a step of 0.1 eV. All binding energies were referenced to that of free carbon at 284.5 eV. The crystal structure was drawn using VESTA37.
For electrochemical studies, the working electrode was fabricated by mixing 80 wt% Ti2CTx, 10 wt% acetylene black and 10 wt% polyvinylidene difluoride binder in a minimal amount of N-methylpyrrolidone (NMP) solvent. This slurry was pasted on an aluminum-foil current collector, and the as-obtained electrode sheet was dried overnight at 120 °C in vacuum. The electrode thickness and mass loading are ~50 μm and ~1 mg cm−2, respectively, for all electrochemical measurements (CV and charge–discharge). CR2032-type coin cells were assembled with Na metal as the counter electrode, a glass fibre filter (GB-100R, ADVANTEC) as the separator and 1 M NaPF6 in ethylene carbonate-diethyl carbonate (EC−DEC, 1:1 v/v%) as the electrolyte. These cells were assembled inside an Ar-filled glove box (Miwa Inc., Japan) (dew point <−100 K). They were galvanostatically (dis)charged in the potential range 0.1–3.0 V. The gravimetric capacitance in farads per gram from CV is given by , where C is the gravimetric capacitance, j is the specific current in amperes per gram, s is the scan rate in volts per second, V is the voltage in volts and ΔV is the voltage window.
Full cell fabrication
For full cell preparation, alluaudite Na2Fe2(SO4)3 was used as a positive electrode material. Alluaudite Na2Fe2(SO4)3 was synthesized according to the procedure described previously34. The full cell was prepared with the alluaudite Na2Fe2(SO4)3 electrode as a positive electrode, the Ti2CTx electrode as a negative electrode, a glass fibrr membrane as a separator, and 1 M NaPF6/EC−DEC as an electrolyte. The cut-off voltages were 3.8 V for charging and 0.1 V for discharging.
How to cite this article: Wang, X. et al. Pseudocapacitance of MXene nanosheets for high-power sodium-ion hybrid capacitors. Nat. Commun. 6:6544 doi: 10.1038/ncomms7544 (2015).
This work was financially supported by the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan under the ‘Elemental Strategy Initiative for Catalysts and Batteries’ (ESICB). M.O. was financially supported by the Murata Science Foundation.
Supplementary Figures 1-7, Supplementary Tables 1-2.
About this article
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/