Iron-nickel (Fe-Ni) alloy nanoribbons were reported for the first time by deoxidizing NiFe2O4 nanoribbons, which were synthesized through a handy route of electrospinning followed by air-annealing at 450 °C, in hydrogen (H2) at different temperatures. It was demonstrated that the phase configurations, microstructures and magnetic properties of the as-deoxidized samples closely depended upon the deoxidization temperature. The spinel NiFe2O4 ferrite of the precursor nanoribbons were firstly deoxidized into the body-centered cubic (bcc) Fe-Ni alloy and then transformed into the face-centered cubic (fcc) Fe-Ni alloy of the deoxidized samples with the temperature increasing. When the deoxidization temperature was in the range of 300 ~ 500 °C, although each sample possessed its respective morphology feature, all of them completely reserved the ribbon-like structures. When it was further increased to 600 °C, the nanoribbons were evolved completely into the fcc Fe-Ni alloy nanochains. Additionally, all samples exhibited typical ferromagnetism. The saturation magnetization (Ms) firstly increased, then decreased, and finally increased with increasing the deoxidization temperature, while the coercivity (Hc) decreased monotonously firstly and then basically stayed unchanged. The largest Ms (~145.7 emu·g−1) and the moderate Hc (~132 Oe) were obtained for the Fe-Ni alloy nanoribbons with a mixed configuration of bcc and fcc phases.
As an important noble-metal-free alloy system, Fe-Ni alloys with limited-dimensional structures have received much attention. It is not only owing to their outstanding soft magnetic properties including high saturation magnetization (Ms), high permeability (μ), high Curie Temperature (Tc) and low coercivity (Hc) and energy loss1,2,3,4,5,6, but also owing to their widely applications in electromagnetic microwave absorption, magnetic refrigeration systems, magnetic recording devices, magnetic resonance imaging and sensors7,8,9. Generally, Fe-Ni alloys are basically classified into two categories based on the mass ratio of Fe: Ni. The Fe-Ni alloys with 50 ~ 80 at% Ni are known as permalloys, that with 30 ~ 40 at% Ni are knows as Invar alloys10,11. On the other hand, Fe-Ni alloys can also be distinguished as body-centered cubic (bcc) and face-centered cubic (fcc) alloys12. Hence it means that the above mentioned magnetic properties (Ms, μ, Tc and Hc) of Fe-Ni alloys are closely related to its composition and phase configuration. As reported in 2008, Vitta et al. showed that the Ms of nanocrystalline Fe100−xNix decreased progressively with Ni content increasing10. In 1986, Chuang et al. pointed out that, for Fe-Ni system below 1200 K, the Tc of the bcc phase monotonously decreased with increasing Ni content and finally vanished at 60 at% Ni, while that of the fcc phase increased at first and then decreased by varying Ni content in the range of 15.1 ~ 100 at% and it reached about 879.5 K at 75 at% Ni12. Furthermore, it is noteworthy that the preparation condition and topographic structure (shape and size) are also significant to the magnetic nanomaterials. By controlling the oxidation kinetics, in 2013, Ucar et al. successfully tuned the Tc of the ball milled γ-Fe70Ni30 and γ-Fe72Ni28 nanoparticles (NPs), and severally calculated their refrigeration capacities to be about 470 and 250 J·kg at 5 T6. Moghimi et al. revealed in 2014 that the maximum magnetization of the Fe63Ni37 concave cubic (CC) NPs (85 emu·g−1) at 0.5 T was higher than that of the cuboctahedron (COh) NPs (40 emu·g−1) while the Hc for the CC NPs (100 Oe) was smaller than that for the COh NPs (188 Oe) although both of them had same composition13. The discrepancy was ascribed to different shapes and phase (fcc, bcc) combinations.
One-dimensional (1D) Fe-Ni alloys (nanowires, nanochains and nanofibers) recently are of particularly scientific and technical interest amongst the numerous magnetic nanostructures. This is surely attributed to their unique natures of effectively conquering the abnormally agglomeration between NPs and exhibiting many useful magnetic properties. For instance, in 2005, Liu et al. found that the Hc of the electrodeposited Fe1-xNix nanowires assisted by AAO templates didn’t monotonically decrease as Ni content increased at 300 K14. In 2012, Jia et al.15 and Lu et al.16 respectively prepared FeNi3 nanochains through a template-free microwave-hydrothermal method and a CTAB mediated aqueous solution method to obtain the enhanced Hc and Ms, respectively compared with that of bulk FeNi3 and monodispersed FeNi3 nanospheres. Lu also revealed that the imaginary permeability of the FeNi3 nanochains showed a broad resonance peak in the frequency range of 150 MHz to 4 GHz16. Thus it is believed that preparing a greater variety of 1D Fe-Ni alloy nanostructures with more satisfactory magnetic properties should be significantly meaningful.
To prepare 1D Fe-Ni alloy nanostructures, electrospinning technique is intensively recommended due to its simplicity, efficiency and versatility17,18,19. Earlier reports have certified that nanofibers20, nanotubes21 and nanoribbons22 could be directly obtained via the electrospinning route combined with a series subsequent treatments, and that all of these 1D nanostructures were tens of micrometers in length and their diameters or width can be flexibly tuned from nanometers to micrometers. To date, however, only Lee et al. prepared the Fe-Ni nanofibers using electrospinning route followed by air-calcination and H2-deoxidization, and studied the electromagnetic wave absorption property in the GHz frequency range23. Unlike nanofibers and nanotubes possessing round cross sections, on the other hand, novel nanoribbons are slightly different due to their rectangular cross sections. Nanoribbons could also be regarded as a development by cutting a finite-width slice from the two-dimensional nanosheets. In recently works, we have demonstrated that the electrospun SrFe12O19 and CoFe2O4 nanoribbons both exhibited deeply impressed magnetic properties22,24. To the best of our knowledge, there is still no public report on Fe-Ni alloy nanoribbons. Furthermore, the worth emphasizing is that this work is an indispensable part in research system of iron-based nanoribbons in the range of ferrite to iron-based alloys. Therefore our main objective in this study is to synthesize Fe-Ni alloy nanoribbons through the electrospinning route followed by air-annealing and H2-deoxidizing successively, and to systematically explore the effect of deoxidization temperature on their morphologies, phase configurations and room temperature magnetic properties.
Synthesis of samples
Chemical agents of polyvinylpyrrolidone (PVP), nickel nitrate hexahydrate (Ni(NO3)2·6 H2O), iron nitrate nonahydrate (Fe(NO3)3·9 H2O) with analytical-grade were used without any purification. The Fe-Ni alloy nanoribbons were synthesized through an electrospinning route followed by air-annealing firstly and then H2-deoxidation successively. The detailed procedure is described as below. Firstly, 0.132 g Ni(NO3)2·6 H2O, 0.368 g Fe(NO3)3·9 H2O and 0.4 g PVP were sufficiently dissolved in a mixed solution of 1.5 g deionized water and 2.4 g C2H5OH under vigorous stirring for overnight to form a steady and viscous spinning solution. Secondly, the obtained solution was placed in a glass syringe equipped with a stainless steel needle (0.4 mm inner diameter). Subsequently, the electrospinning was carried out at a DC high-voltage of 15 kV, a spacing of 20 cm between the needle tip and metal collector, and a flow rate of 0.3 mL·h−1. Several hours later, the PVP/Fe(NO3)3/Ni(NO3)2 precursor nanoribbons were deposited on the collector with a form of an uniform membrane. Thirdly, the as-spun precursor membrane was aged initially at 60 °C in a drying box for a few hours followed by annealing at 450 °C for 2 h in air with a heating rate of 1 °C·min−1. Then the as-annealed products S0 was divided into four groups, which were further deoxidized at 300, 400, 500 and 600 °C in H2 atmosphere with a constant flow for 1 h respectively. Finally, the corresponding Fe-Ni alloy nanoribbons S1-S4 were obtained.
Characterization of samples
The morphologies and microstructures of all samples were observed by field emission scanning electron microscopy (FESEM, Hitachi S4800, Japan) and transmission electron microscopy (TEM, FEI TecnaiTM G2 F30, USA) equipped with an energy dispersive X-ray spectroscopy (EDX, Oxford Instrument, UK). The phase components, elements and corresponding chemical states were detected by powder X-ray diffraction on a X-ray diffractometer (XRD, Philips X’Pert Pro MPD, the Netherlands) with Cu-Kα irradiation (λ = 1.54056 Å), high-resolution transmission electron microscopy (HRTEM), EDX and X-ray photoelectron spectroscopy (XPS, Kratos AXIS UltraDLD, 600 W, UK) with an monochrome Al-Kα probe beam. All the recorded XPS spectra were calibrated using C 1 s peak with the binding energy of 284.8 eV and were analyzed through Gaussian-fitting. A vibrating sample magnetometer (VSM, Lakeshore 7403, USA) was used to investigate the room temperature magnetic properties of the samples.
Results and Discussion
Phase configurations and microstructures of samples
Figure 1 shows the XRD patterns of the H2-deoxidized samples S1-S4 as well as the air-annealed sample S0. For S0, the sample is certified as a single phase material. All the observed diffraction peaks marked by the black diamonds can be unambiguously indexed to the standard spinel NiFe2O4 with a cubic structure (JCPDS card no. 54-0964), and they are corresponded to the (200), (311), (400), (422), (511), (440), (622) and (533) planes, respectively. Neither amorphous materials nor other secondary phases are observed. When the pure NiFe2O4 (S0) is H2-deoxidized at 300 °C, it is clearly found that the diffraction peaks of NiFe2O4 are weakened but some new diffraction peaks emerged in the obtained sample S1. The peaks marked by the red diamonds at about 43.88°, 50.88° and 74.75° can be respectively indexed to (111), (200) and (220) planes of the fcc Fe-Ni alloy (JCPDS card no. 47-1405) and the peaks marked by the blue diamonds at about 44.76°, 65.16° and 82.4° can be respectively indexed to (110), (200) and (211) planes of the bcc Fe-Ni alloy (JCPDS card no. 37-0474). That is, NiFe2O4 in S0 is partially deoxidized to fcc and bcc Fe-Ni alloys in S1. Then sample S1 is a complex of the cubic NiFe2O4, fcc Fe-Ni and bcc Fe-Ni. However, the peak intensities of fcc Fe-Ni is weaker than that of bcc Fe-Ni. When S0 is H2-deoxidized at 400 °C, the peaks of NiFe2O4 phase disappear completely in sample S2, only the peaks of fcc and bcc Fe-Ni phases are observed and the peak intensities of fcc Fe-Ni are strengthened obviously. Thus sample S2 is a pure alloy just with a mixed phase of fcc and bcc Fe-Ni. When the deoxidization temperature is further risen to 500 °C, the peaks of fcc Fe-Ni strengthen further but that of bcc Fe-Ni disappear. Therefore, the as-deoxidized sample S3 is a pure fcc Fe-Ni alloy. Seeing from the phase transformation from S0 to S3, it can be concluded that the cubic NiFe2O4 is deoxidized to bcc Fe-Ni at first and then transformed into fcc Fe-Ni with the deoxidization temperature increasing. For S4 resulted from deoxidizing S0 at 600 °C, its phase is fcc Fe-Ni undoubtedly. Using Debye-Scherrer equation25, the average grain sizes (D) of fcc Fe-Ni alloy in S1, S2, S3 and S4 are estimated to be about 17.2 ± 0.30, 29.8 ± 0.32, 34.1 ± 0.27 and 39.9 ± 0.35 nm respectively. It indicates that the as-deoxidized fcc Fe-Ni alloy grains gradually grow with the increased deoxidization temperature.
The morphology features of all samples S0-S4 with the defined phase configurations are examined by FESEM firstly. As presented in Fig. 2(a–c), a large number of continuously ribbon-like structures with random direction are found for sample S0 (NiFe2O4). The ribbon-width is ranged from 269 nm to 512 nm and the average width is about 348.4 nm. Each of nanoribbon is quite uniform in width along the length direction and is constructed by small nanoparticles (NPs). When the NiFe2O4 nanoribbons are deoxidized at 300 to 600 °C, some changes are also occurred on the microstructures beyond on the phase configurations of the resultant products, which are shown in Fig. 2(d–o). Firstly, in Fig. 2(d–f), when the deoxidization temperature is 300 °C, the obtained composite nanoribbons S1 of NiFe2O4 + fcc Fe-Ni + bcc Fe-Ni well keep the continuous structures of the NiFe2O4 nanoribbons. Secondly, when the temperature is risen up to 400 and 500 °C, the NPs contained within the composite nanoribbons S2 of fcc Fe-Ni + bcc Fe-Ni (Fig. 2(g–i)) and pure nanoribbons S3 of fcc Fe-Ni (Fig. 2(j–l)) increase sharply and fuse together. And the nanoribbons S3 become uneven and bent. Compared to S0, however, the average ribbon-widths of S1, S2 and S3 don’t change much and they are about 347.9, 345.1 and 345.4 nm respectively. Thirdly, when the deoxidization temperature is further increased to 600 °C, basically no nanoribbons except for NP-chain (or nanochains) are found in the final fcc Fe-Ni sample (S4) (Fig. 2(m–o)). Due to the excessive growth and fusion together of their NPs, the nanochains S4 are constructed by the NP-clusters as one-by-one and the average diameter is about 241 nm. Moreover, unlike the nanoribbons of S0-S3, the nanochains of S4 connect with each other by lots of junctions, which were marked by the red circles. Hence the whole sample S4 looks more like a three-dimensional network of the nanochains.
TEM analysis was carried out to further explore the microstructures of S0-S4. Firstly, Fig. 3(a,e,i,m,q) describe the typical high-magnification TEM images of the random individuals of all samples. These closer TEM examinations powerfully certify the ribbon-like structures of S0-S3 and the chain-like structure of S4. Owing to the continued particle growth during the second annealing in H2, NPs of the deoxidized S1-S4 are bigger than that of their precursor nanoribbons S0. For S1-S4, the particle size increase gradually with the deoxidization temperature increasing. Secondly, Fig. 3(b–d,f–h,j–l,n–p,r–t) respectively display the corresponding HRTEM images. In Fig. 3(b–d), the lattice fringes scanned from the selected NPs of S0 are measured to be about 0.209, 0.249 and 0.250 nm, which are indexed well to (400), (311) and (311) planes of NiFe2O4 (JCPDS card no. 54-0964). In Fig. 3(f–h), the measured distances of about 0.177, 0.200 and 0.240 nm of S1 are approximately equivalent to the interlayer distances of (200), (110) and (222) planes of the fcc Fe-Ni alloy, bcc Fe-Ni alloy and spinel NiFe2O4, respectively. Thus it proves that the chemical phase of S0 nanoribbons is pure NiFe2O4 and the S1 nanoribbons are assembled by the fcc Fe-Ni, bcc Fe-Ni and spinel NiFe2O4 NPs. In other words, it further demonstrates that NiFe2O4 of S0 transforms to the complex of fcc Fe-Ni alloys, bcc Fe-Ni alloys and spinel NiFe2O4 ferrite after annealing in H2 at 300 °C for S1. Similarly, from Fig. 3(j–l,n–p,r–t), it also notifies that the nanoribbons S2 are constructed by the fcc and bcc Fe-Ni NPs, the nanoribbons S3 and nanochains S4 are both purely constructed by the fcc Fe-Ni NPs, respectively.
To identify the chemical elements and corresponding surface chemical states of S0-S4, the TEM-EDX and XPS spectra are presented. With the exception of the extra signals of C and Cu elements descended from the carbon-coated copper grid clamping the samples for TEM measurements, as shown in Fig. 4a, the peaks of Fe, Ni and O elements are detected together in the spectra of all samples S0-S4. Of which, the atomic ratio of Fe: Ni (38.6: 19.1) of S0 is basically equivalent to the stoichiometric ratio (n(Fe): n(Ni) = 2: 1) of NiFe2O4. Although S1-S4 are respectively the complex of NiFe2O4 + fcc Fe-Ni + bcc Fe-Ni (S1), the complex of fcc Fe-Ni + bcc Fe-Ni (S2) and the pure fcc Fe-Ni (S3 and S4), their total atomic ratios of Fe: Ni (30.9: 15.6, 50.9: 25.3, 41.5: 20.3 and 49.6: 24.7) are still very close to 2: 1. Differently, however, the O contents are found to have a decrease in S2-S4 compared to S0 and S1. For S0 and S1, O elements are mainly belonged to the NiFe2O4, but the small amounts of O elements detected in S2-S4 are probably ascribed to the self-oxidized surfaces. This assumption will be carefully discussed as below. According to the obtained atomic ratios of Fe: Ni, additionally, the S2-S4 can be roughly expressed as Fe67Ni33. Fig. 4(b,d,f,h,j) and (c,e,g,i,k) reveal the recorded high-resolution XPS spectra of Ni 2p3/2 and Fe 2p3/2, respectively. All the binding energy scales are calibrated using the C 1 s peak with a binding energy of 284.8 eV. For precursor nanoribbons S0, the only peak located at about 854.50 eV in its Ni 2p3/2 spectrum (Fig. 4(b)) is assigned to the Ni2+ of O-Ni bonds26,27. The peak observed in Fe 2p3/2 spectrum (Fig. 4(c)) can be fitted into two peaks located at about 711.81 and 709.91 eV, which are respectively assigned to Fe3+ in tetrahedral-site and Fe3+ in octahedral-site of the inverse spinel NiFe2O428,29. For reduced nanoribbons S1, besides the peak of Ni2+ with a higher binding energy presented in its Ni 2p3/2 spectrum (Fig. 4(d)), another peak with a lower binding energy at about 852.11 eV is also observed and assigned to the metallic Ni26,27,30. By fitting, similarly, its Fe 2p3/2 spectrum (Fig. 4(e)) contains four peaks, which can be fallen into two categories. The first and second peaks located at higher binding energies are surely assigned to Fe3+ of the NiFe2O4, but the third and fourth peaks located at lower binding energies of about 707.24 and 706.03 eV are both assigned to metallic Fe29,31,32. Based on the experiment process and above analysis, the metallic Ni and Fe should be derived from the partial deoxidized NiFe2O4 and they are further compounded to fcc and bcc Fe-Ni alloy NPs. For S2-S4 (Fe-Ni alloys), the peaks of Ni2+ and metallic Ni are also found in their Ni 2p3/2 spectra (Fig. 4(f,h,j)) as well as the peaks of Fe3+ and metallic Fe found in Fe 2p3/2 spectra (Fig. 4(g,i,k)). However, the peak signals of Ni2+ in S2-S4 are much weaker than that of metallic Ni while the peaks of Fe3+ are much stronger than that of metallic Fe. It means that the reduced Fe element is oxidized more easily than Ni element in air. Then Ni element in surfaces of S2-S4 mainly exists in metallic state but Fe element exists in oxide state. Because no any obvious Ni- or Fe-oxides are observed from the XRD patterns and HRTEM images of S2-S4, it suggests that the detected signals of Ni2+ and Fe3+ should be ascribed to the slightly oxidization shells on their surfaces.
Magnetic properties of samples
Figure 5(a) depicts the magnetization (M-H) loops of S0-S4 recorded at room temperature and the inset shows the corresponding enlarged views. It reveals that all samples exhibit typical ferromagnetic behaviors. For NiFe2O4 precursor nanoribbons (S0), the Ms and Hc are respectively about 45.1 emu·g−1 and 212 Oe. The hysteresis loops of the deoxidized S1-S4 closely vary with the deoxidization temperature. The largest Ms about 145.7 emu·g−1 is obtained for S2. For standard crystalline Fe and Ni, their magnetic moments per cell are about 2.2 μB and 0.6 μB13,33, respectively. And the bulk Ms34 of bcc Fe is about 222 emu·g−1. Therefore, the bulk Ms of Fe67Ni33 can be approximately estimated to be about 167 emu·g−1, which is basically in constant with the reported value of 168 emu·g−1 in the literature35,36. In our case, thus, the experimental value is very close to the estimated bulk value. The above investigations of XRD and XPS have indicated that a thin oxide shells present at the surface, in which the magnetic spins are disordered and pinned37,38. This could account for the slight difference of Ms between our result and the calculated bulk value. On the other hand, except for S1, the Hc values of S2-S4 (pure Fe67Ni33) are all lower than 150 Oe. Based on the above results, hence, the Fe-Ni alloy nanoribbon is a considerable soft magnetic nanomaterial. Additionally, the most significant feature of the Fe-Ni alloy nanoribbons is their unique geometry of the ribbon-like structure self-assembled by NPs. Compared with the zero-dimensional alloy materials, Fe-Ni alloy nanoribbons have an amazing advantage is that they can be used in the miniaturizing and high density electronic components such as antennas and stealth devices. Therefore, the high-frequency properties can probably be a major future research content and direction.
To further understand the effect of deoxidization temperature on the magnetic properties of S1-S4, the Ms and Hc values as functions of the deoxidization temperature are shown in Fig. 5(b). It is found that Ms of these Fe-Ni alloy samples firstly increases, then decreases, and finally increases with the deoxidization temperature increasing, but the Hc monotonously decreases firstly and then basically stays unchanged. To understand this, the plausible contributing reasons are clarified. For Ms, firstly, because the deoxidization temperature of 300 °C in H2 for S1 is too low to completely deoxidize NiFe2O4 of S0 into Fe-Ni alloys but that of 400 °C for S2 is big enough to deoxidize NiFe2O4 into Fe-Ni alloys completely, a certain amount of residual NiFe2O4 in S1 certainly pulls down the total Ms. Besides, the grain size of S1 (D1 ≈ 17.2 nm) is much smaller than that of S2 (D2 ≈ 29.8 nm). Hence even if S2 has a mix combination of fcc and bcc Fe-Ni phases, its Ms is still increased considerably compared to that of S1. Secondly, when the deoxidization temperature is risen up to 500 °C for S3, bcc Fe-Ni phase is transformed into fcc Fe-Ni phase and then the obtained S3 is pure fcc Fe-Ni with an increased grain size (D3) of about 34.1 nm. But, the increased grain size does not lead the decrease of Ms. Then the decreased Ms of S3 mainly caused by vanishing of bcc Fe-Ni phase. This phenomenon is similar with Moghimi’s results about Fe63Ni3713. Moghimi and other works have pointed out that the Ms of bcc phase is universally larger than that of fcc phase in Invar Fe-Ni alloys (30 ~ 38 at% Ni)13,39,40, and that if the Fe-Ni alloy is a combination of bcc and fcc phases, its Ms linearly decreases with the fcc phase increasing13. Then S3 has a lower Ms than that of S2. Thirdly, when the temperature is sequentially increased to 600 °C, the composition of obtained S4 is still fcc Fe-Ni. Due to the same composition of Fe67Ni33 and same phase configuration, the different grain size of S4 (D4 ≈ 39.9 nm) and S3 (D3 ≈34.1 nm) is the only striking difference, which finally gives rise to the slight increase of Ms. As same as Ms, on the other hand, the variation of Hc is also related to the composition and grain size. Firstly, S1 is the composite of NiFe2O4 + fcc Fe-Ni + bcc Fe-Ni. Since the magneto-crystalline anisotropy constant (K1) of cubic NiFe2O4 (~105 J·m3) is larger than that of either fcc or bcc Fe-Ni alloys (~103 J·m−3)41,42,43, the exchange interactions between the NiFe2O4 and Fe-Ni NPs contribute to the largest Hc value (364 Oe) of S1 among the four samples. Secondly, both of our prepared Fe-Ni alloy nanoribbons (S2 and S3) and nanochains (S4) are self-assembled by Fe-Ni NPs. For simplicity sake, we can temporarily ignore the anisotropic difference originated from the slightly different shapes of nanoribbons and nanochains donating to Hc. Thus we utilize the Hc of Fe-Ni NPs to approximately illustrate the Hc variation from S2 to S4. The random anisotropy model (RAM) originally proposed by Alben et al. reveals that the Hc of ferromegnetically coupled nanocrystallines is related to the average grain size (D) and ferromagnetic exchange length Lex (Lex = (A/K1)1/2, A and K1 respectively denote the exchange stiffness and the magneto-crystalline anisotropy constant44,45. If D < Lex, the Hc is compatible with D6 dependence. If D > Lex, the Hc is proportional to 1/D. To be emphasized, the RAM law for Hc is well-known for polycrystalline Fe-based alloys46,47,48. In Wen’s work, through a liner fitting of A and K1 values of bcc Fe and fcc Ni, he calculated not only the A and K1 values of Fe70Ni30 alloys but also the Lex value of Fe70Ni30 (~ 14 nm)45. Using the suggested method, similarly, we also respectively estimate the A, K1 and Lex of Fe67Ni33 alloys to be about 6.68 × 10–12 J·m−1, 3.18 × 104 J·m−3 and 14.5 nm. In our case, hence, all of the average grain sizes of Fe67Ni33 NPs of S2-S4 are larger than the Lex. Furthermore, the inset in Fig. 5(b) shows that the variation of Hc with the grain size (D) from S1 to S3 except for S4 generally conforms to the Hc ∝ 1/D situation of the RAM theory. Therefore, the decrease of Hc from S1 to S2 to S3 is caused by the increase of grain size. Although all deoxidized samples are self-assembled by the Fe-Ni NPs, thirdly, the nanochains of S4 are still slightly different from the nanoribbons of S2-S3. On one hand, the nanochains are connected by the big clusters of Fe-Ni NPs. Within these clusters range, Fe-Ni NPs contact with each other tightly. That way, the exchange interactions between Fe-Ni NPs are increased at a certain extent. On the other hand, most of the nanochains of S4 connect with each other through the junctions, being marked by the red circles in Fig. 2m, but the nanoribbons of S2 and S4 are more isolated individuals. So there are still increased exchange interactions between the nanochains in S4 compared to S2 and S3. Hence the above two aspects of increased exchange interactions in S4 effectively compensate the decrease of Hc caused by the increase of grain size, and then the net Hc dose not decrease. Consequently, it is concluded that the deoxidization temperature has a great influence on the microstructures of Fe-Ni samples and then further affects the magnetic properties.
Briefly, Fe-Ni alloy nanoribbons were successfully synthesized through an electrospinning route followed by air-annealing and H2-deoxidizing orderly. The results revealed that the deoxidization temperature had a significant influence on the phase components, morphologies and magnetic properties of the final samples. On the one hand, the air-annealed cubic NiFe2O4 ferrite could be firstly deoxidized into bcc Fe-Ni alloy and then transformed into fcc Fe-Ni alloy in H2 with the deoxidization temperature increasing. When the temperature is in the range of 300~500 °C, all the obtained samples possessed the ribbon-like structures perfectly. While when the temperature was further risen to 600 °C, the Fe-Ni alloys nanoribbons were evolved into the Fe-Ni alloy nanochains. On the other hand, the Fe-Ni alloys nanoribbons and nanochains both performed excellent ferromagnetism. Their Ms first increased, then decreased, and finally increased with the deoxidization temperature increasing, but their Hc monotonously decreased firstly and then basically stayed unchanged. Last but not least is that these results can provide a meaningful reference to related fundamental research and practical application in future.
How to cite this article: Jing, P. et al. Dependence of phase configurations, microstructures and magnetic properties of iron-nickel (Fe-Ni) alloy nanoribbons on deoxidization temperature in hydrogen. Sci. Rep. 6, 37701; doi: 10.1038/srep37701 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Koohkan, R., Sharafi, S., Shokrollahi, H. & Janghorban, K. Preparation of nanocrystalline Fe–Ni powders by mechanical alloying used in soft magnetic composites. J. Magn. Magn. Mater. 320, 1089–1094 (2008).
Shirakata, Y., Hidaka, N., Ishitsuka, M., Teramoto, A. & Ohmi, T. High permeability and low Loss Ni–Fe composite material for high-frequency applications. IEEE T. Magn. 44, 2100–2106 (2008).
Feng, C., Liu, X. G., Sun, Y. P., Jin, C. G. & Lv, Y. H. Enhanced microwave absorption of flower-like FeNi@C nanocomposites by dual dielectric relaxation and multiple magnetic resonance. RSC Adv. 4, 22710–22715 (2014).
Zhen, L., Gong, Y. X., Jiang, J. T. & Shao, W. Z. Electromagnetic properties of FeNi alloy nanoparticles prepared by hydrogen-thermal reduction method. J. Appl. Phys. 104, 034312–034316 (2008).
Kurlyandskaya, G. V. et al. Structure, magnetic and microwave properties of FeNi nanoparticles obtained by electric explosion of wire. J. Alloy. Compd. 615, S231–S235 (2014).
Ucar, H., Ipus, J. J., Laughlin, D. E. & McHenry, M. E. Tuning the Curie temperature in γ-FeNi nanoparticles for magnetocaloric applications by controlling the oxidation kinetics. J. Appl. Phys. 113, 17A918–034320 (2013).
Osaka, T. Recent development of Magnetic recording head core materials by plating method. Electrochem. Acta 44, 3885–3890 (1999).
Yang, H. et al. Monodisperse water-soluble Fe–Ni nanoparticles for magnetic resonance imaging. J. Alloy. Compd. 509, 1217–1221 (2011).
Butta, M., Pipka, P., Janosek, M. & Pribil, M. Electroplated FeNi ring cores for fluxgates with field induced radial anisotropy. J. Appl. Phys. 117, 17A722–17A726 (2015).
Vittaa, S., Khuntiaa, A., Ravikumarb, G. & Bahadura, D. Electrical and magnetic properties of nanocrystalline Fe100 −x Nix alloys. J. Magn. Magn. Mater. 320, 182–189 (2008).
ABD-Elemeguid, M. M. Schleede, B. & Micklitz, H. Pressure-induced antiferromagnetic in fcc Fe-Ni invar alloys. J. Magn. Magn. Mater. 72, 253–257 (1988).
Chuang, Y. Y., Chang, Y. A., Schmid, R. & Lin, J. C. Magnetic contributions to the thermodynamic functions of alloys and the phase equilibria of Fe-Ni system below 1200K. Met. Trans. 17A, 1361–1372 (1986).
Moghimi, N., Rahsepar, F. R., Srivastava, S., Heinig, N. & Tong, K. Leung Shape-dependent magnetism of bimetallic FeNi nanosystems. J. Mater. Chem. C 2, 6370–6375 (2014).
Liu, Q. F., Wang, J. B., Yan, Z. J. & Xue, D. S. Characterization and magnetic properties of Fe1-xNix nanowires arrays. Phys. Rev. B 72, 144412–144417 (2005).
Jia, J. C., Yu, J. C., Wang, Y. X. J. & Chan, K. M. Magnetic nanochains of FeNi3 prepared by a template-free microwave-hydrothermal method. ACS Appl. Mater. Inter. 2, 2579–2584 (2010).
Lu, X. et al. CTAB-mediated synthesis of iron–nickel alloy nanochains and their magnetic properties. Colloid. Surfaces A: Physicochem. Eng. Aspects. 407, 23–28 (2012).
Dong, Z. X., Kennedy, S. J. & Wu, Y. Q. Electrospinning materials for energy-related applications and devices, J. Power Sources 196, 4886–4904 (2011).
Rojas, R. & Nicholas, J. P. Using Electrospinning for the fabrication of rapid sesponse gas sensors based on conducting polymer nanowires. IEEE Sens. J. 8, 591–593 (2008).
Wang, X. F., Ding, B. & Li, B. Y. Biomimetic electrospun nanofibrous structures for tissue engineering. Mater. Today 16, 229–241 (2013).
Zhang, J. L. et al. Nanoscale characterization and magnetic reversal mechanism investigation of electrospun NiFe2O4 multi-particle-chain nanofibres. Nanoscale 4, 2754–2759 (2012).
Fu, J. C. et al. Unique magnetic properties and magnetization reversal process of CoFe2O4 nanotubes fabricated by electrospinning. Nanoscale 4, 3932–3936 (2012).
Jing, P. P. et al. Width-controlled M-type hexagonal strontium ferrite (SrFe12O19) nanoribbons with high saturation magnetization and superior coercivity synthesized by electrospinning. Sci. Rep. 5, 15089–15098 (2015).
Lee, Y. I. & Choa, Y. H. Synthesis and electromagnetic properties of FeNi alloy nanofibers using an electrospinning method. J. Koren Cryst. Growth Cryst. Technol. 22, 218–222 (2012).
Jing, P. P. et al. Improved coercivity and considerable saturation magnetization of cobalt ferrite (CoFe2O4) nanoribbons synthesized by electrospinning. J. Mater. Sci. 51, 885–892 (2016).
Holzwarth, U. & Gibson, N. The Scherrer equation versus the ‘Debye–Scherrer equation’. Nat. Nanotech. 6, 534 (2011).
Uhlenbrock, S., Scharfschwerdt, C., Neumann, M., Illing, G. & Freund, H. J. The influence of defects on the Ni 2p and O 1s XPS of NiO. J. Phys.: Condens. Matter 4, 7973–7978 (1992).
Peck, M. A. & Langell, M. A. Comparison of nanoscaled and bulk NiO structural and environmental characteristics by XRD, XAFS, and XPS. Chem. Mater. 24, 4483−4490 (2012).
Ding, R., Lv, L. L., Qi, L., Jia, M. J. & Wang, H. Y. A facile hard-templating synthesis of mesoporous spinel CoFe2O4 nanostructures as promising electrocatalysts for the H2O2 reduction reaction. RSC Adv. 4, 1754–1760 (2014).
Biesinger, M. C. et al. Resolving surface chemical states in XPS analysis of first row transition metals, oxides and hydroxides: Cr, Mn, Fe, Co and Ni. Appl. Surf. Sci. 57, 2717–2730 (2011).
Nesbitt, H. W., Legrand, D. & Bancroft, G. M. Interpretation of Ni2p XPS spectra of Ni conductors and Ni insulators. Phys. Chem. Minerals 27, 357–366 (2000).
Wang, X. F. et al. Striped domains in soft magnetic FeNiN thin films. J. Phys. D: Appl. Phys. 40, 955–959 (2007).
López, M. C., Ortiz, G. F., Lavela, P., Alcántara, R. & Tirado, J. L. Improved coulombic efficiency in nanocomposite thin film based on electrodeposited-oxidized FeNi-electrodes for lithium-ion batteries. J. Alloy. Compd. 557, 82–90 (2013).
Glaubitz, B., Buschhorn, S., Brussing, F., Abrudan, R. & Zabel, H. Development of magnetic moments in Fe1− xNix alloys. J. Phys.: Condens. Matter 23, 254210–254218 (2011).
Suslick, K. S., Fang, M. M. & Hyeon, T. Sonochemical Synthesis of Iron Colloids. J. Am. Chem. Soc. 118, 11960–11961 (1996).
Wei, X. W., Zhu, G. X., Xia C. J. & Ye, Y. A solution phase fabrication of magnetic nanoparticles encapsulated in carbon. Nanotechnology 17, 4307–4311 (2006).
Panda, R. N. & Gajbhiye, N. S. Magnetic properties of nanocrystalline γ-Fe–Ni–N nitride systems. J. Appl. Phys. 86, 3295–3302 (1999).
Kim, J., Kim, J., Kim, J. & Kim, K. H. Characterization of as-synthesized FeCo magnetic nanoparticles by coprecipitation method. J. Appl. Phys. 113, 17A313–17A315 (2013).
Morales, M. P., Verdaguer, S. V., Montero, M. I. & Serna, C. J. Surface and Internal Spin Canting in γ-Fe2O3 Nanoparticles. Chem. Mater. 11, 3058–3064 (1999).
Crangle, J. & Hallam, G. C. The magnetization of face-centred cubic and body-centred cubic iron+nickel alloys. Proc. Roy. Soc. A 272, 119–132 (1963).
James, P. Calculated magnetic properties of binary alloys between Fe, Co, Ni, and Cu. Phys. Rew. B 59, 419–429 (1999).
Chatterjee, B. K., Ghosh, C. K. & Chattopadhyay K. K. Temperature dependence of magnetization and anisotropy in uniaxial NiFe2O4 nanomagnets: Deviation from the Callen-Callen power law. J. Appl. Phys. 116, 153904–153911 (2014).
Karpova, T. S., Vasil’ev, V. G., Vladimirova, E. V. & Nosov, A. P. Synthesis of Ferrite Spinel NiFe2O4 by Thermal Hydrolysis and Its Magnetic Properties. Inorg. Mater.: Appl. Res. 3, 107–112 (2012).
Kuhrt, C. & Schultz, L. Formation and magnetic properties of nanocrystalline mechanically alloyed FeCo and FeNi. J. Appl. Phys. 17, 6588–6590 (1993).
Herzer, G. Grain size dependence of coercivity and permeability in nanocrystalline ferromagnets. IEEE Trans. Magn. 26, 1397–1402 (1990).
Wen, C. S., Chen, Z., Huang, B. X. & Rong, Y. H. Nanocrystallization and Magnetic Properties of Fe-30 Weight Percent Ni Alloy by Surface Mechanical Attrition Treatment. Metall. Mater. Trans. 37A, 1413–1421 (2006).
Gheisari, K., Oh, J. T. & Javadpour, S. The effect of heat treatment on the structure and magnetic properties of mechanically alloyed Fe-45%Ni nanostructured powders. J. Alloys. Compd. 509, 1020–1024 (2011).
Kuhrt, C. & Schultz, L. Formation and magnetic properties of nanocrystalline mechanically alloyed FeCo. J. Appl. Phy. 71, 1896–1900 (1992).
Kumar, M. S. Temperature dependence of magnetization in Fe-Pd thin films. Mater. Sci. Eng.: B 162, 59–63 (2009).
This work is supported by the National Nature Science Foundation of China (51171075, 51371092, 51372144) and the Key Program of Innovative Research Team of Shaanxi Province (2014KCT-06).
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Jing, P., Liu, M., Pu, Y. et al. Dependence of phase configurations, microstructures and magnetic properties of iron-nickel (Fe-Ni) alloy nanoribbons on deoxidization temperature in hydrogen. Sci Rep 6, 37701 (2016). https://doi.org/10.1038/srep37701
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.