Abstract
Main drives, cutterheads and other critical components of tunnel shield machines require welding with thick plates that leave roots over 5 mm. Full penetration welds cannot be achieved by conventional Pulsed MAG welding methods. This article introduces Super Spray MAG Welding technology and investigates its penetrating regularities and mechanisms through high-speed camera images, finite element simulation, and microstructural analysis. An optimal welding procedure was generated using a combination of Genetic Algorithm and Back Propagation Neural Network. The data show that Super Spray MAG arc exhibits greater concentration and stability than traditional MAG arc, marking its strong qualities in emitting high-energy beams. The morphological solidification pattern of the molten pool closely matches the FEM simulation results of the composite Gaussian surface heat source model and peak linear attenuation Gaussian cylinder heat source. The welding current mainly affects the penetration of the weld, followed by the extension of the wire, and lastly the welding speed. Increasing the welding current can transition droplet transfer from globular to spray, as well as alter microstructure development and mechanical characteristics. Suggested parameters for penetrating the 5 mm root were put forward. The BPNN-GA model established can effectively predict weld formation, and points out the optimal welding parameters.
Similar content being viewed by others
Introduction
As tunnel construction technology advances, the size of tunnel boring machines (TBMs) continues to grow and the demand for greater load capacity increases. Key bearing components such as main drives and cutterheads bear large vibration loads during operation1,2,3. To ensure product dependability, T-joints are typically constructed using thick plates measuring at least 40 mm for both horizontal and vertical welding. In addition, more than 40% of full-penetration welds undergo initial-class ultrasonic testing. Compared to alternative methods such as TIG welding and submerged arc welding, MAG welding is frequently used in the production of TBM components because of its stable process, controllability, simple equipment, versatility, dependable joint quality, and high welding efficiency. Conventional MAG welding, due to its low welding current and arc pressure, faces difficulties in achieving full penetration of thick plates with root height exceeding 5 mm, and may lead to weld cracks, poor formation, and root defects. As a result, the rate of detection of qualified defects is low. Several techniques for optimizing the MAG welding process have been suggested, including raising the welding current, employing double-layer gas shielding, enhancing ultrasonic support, changing the properties of the joint shape, and so on4,5,6,7,8,9,10, but the arc energy is still low. Through a lot of industrial experiments, it has been found that MAG welding transitions into spray transfer when the welding current reaches about 400 A to properly penetrate the root height of 5 mm. As the temperature rises, the affected area expands, resulting in a more coarse grain structure and reduced mechanical properties11,12,13. Various post-weld heat treatments have been suggested to enhance penetration by transforming the microstructure14, 15. However, these treatments may affect local areas such as grain boundary precipitates, which can stabilize the microstructure and alleviate welding stress rather than promote rapid penetration. Several methods for optimizing the heat source, such as hybrid TIG/MAG welding and hybrid multi-wire MAG welding, have been proposed to improve droplet deposition rates16,17,18. However, these methods do not significantly increase the energy density at the welding site or enhance penetration depth. Conversely, the adaptability to grooves is reduced due to larger welding gun heads. Furthermore, high-energy beams like lasers and plasma are proposed as potential enhancements for increasing energy density19,20,21,22,23. But laser welding and plasma welding require highly precise assembly precision, have low energy efficiency, low cladding efficiency, and high equipment costs, making them unsuitable for producing large structural components.
This paper introduces a new Super Spray MAG welding technology. The welding arc is digitally controlled to produce a strong, focused, consistent beam. With removing the use of pulses, Super Spray MAG welding achieves a consistent and dependable arc to enhance droplet transfer frequency. However, it requires strict welding arc control to limit welding heat input. If the heat input is insufficient, it is difficult to penetrate the root. If the heat input is too large, it is easy to cause problems such as coarse grains, root defects, decline of mechanical properties, etc.24, 25. This paper presents an analysis of the heat flow distribution in Super Spray MAG Welding using FEM simulation. A combined heat source model is also proposed. The deep penetration phenomenon was investigated by analyzing spray arcs, melted droplets, microstructure, and joint properties. In addition, the combination of Back Propagation Neural Network and Genetic Algorithm was used to predict weld penetration and optimize process parameters. The research on Super Spray MAG Welding has provided valuable insights into heat source analysis, penetration regularities, and mechanisms. The stable and deep penetrating weld parameters obtained from this study can be used as a guide for welding thick plates in construction machinery.
Experimental work
Welding materials
Q355 steel plates were used as welding workpieces. The “V” groove weld joints with a 1 mm gap as shown in Fig. 1 were prepared with ER50-6 filler wires (DIN SG2). The filler wires were 1.2 mm in diameter. 1.2 mm. The chemical composition of the welded workpieces and filler wire is given in Table 1. Shielding gas was a mixture of 80% Ar + 20% CO2 with a flow rate of 15 L min−1.
Welding tests
All tests use robotic welding to ensure stability. The welding heat source was Qineo Pulse 600 Inverter. For each test, the groove shall be welded in one pass and free cooling down. The welding gun is located on the center line of the corner bisection of the joints and moves evenly perpendicular to the intersection line of the two vertical plates. The welding parameters are shown in Tables 2, 3. This experiment set up a group of orthogonal experiments to compare parameters, and a group of random experiments for BPNN prediction of weld microstructure and performance.
As shown in Table 2, the orthogonal test is set L25 (35), i.e. three factors, five levels and a total of 25 trials, to compare and evaluate the impact of different factors. The corresponding sample number is shown in Table 3. Comparative parameters for Sample 26 were inherited from conventional MAG welding practices for steel plates below 40 mm. In addition, a groups of random experiments as shown in Table 4 were supplied to meet the sample size requirement of BPNN calculation. The extension of the wire sticking out of the nozzle is almost equal to the distance between the contact tip to work at the beginning. And it is set by trimming the length of the welding wire before arcing. Due to static characteristics of welding arc26, welding voltage is almost linearly determined by the current which can expressed as U = 0.04I + 20 ± 2 (V).
Characterization
To analyze heat source properties, a finite element method was applied to simulate the heat flow distribution of welding arc. Meanwhile, a high-speed image acquisition system was established to capture images of welding procedures as shown in Fig. 2. The acquisition system included a computer, a Photron Limited SA1.1 high-speed camera and composite filter lenses. The filter lenses were composed of a high transparency UV lens, 800 nm narrow-band filter and a ND dimmer. The arc shape and droplet transfer process were captured by 8000 frames per-second and a shutter speed of 1/20,000 s.
To observe the microstructure of welds, optical microscopy (OM) was adopted. Before observation, the specimen was polished and viewed 100× under an optical microscope. No discernible scratches were identified. Use degreased cotton dipped in 4% nitric acid alcohol solution to wipe and corrode for 10–20 s.
To assess weld quality, Brinell hardness was estimated for each part of the joints. To verify optimal parameters, mechanical tests and ultrasonic flaw detection were performed after the groove had been filled by conventional MAG welding. According to EN ISO 15614 Specification and qualification of welding procedures for metallic materials—Welding procedure test, mechanical tests should contain tensile, impact, and bending tests. The tensile test was performed at room temperature using the MTS-810 electrohydraulic servo material test system. The tensile strength of the joints must exceed that of the base metal. Impact test was performed using the CEAST9350 microcomputer controlled metal pendulum impact test machine. The minimum impact absorption energy of three standard specimens in each region of welded steel joints shall be above 20 J. It is acceptable for a specimen to have a slightly lower energy value, not falling below 70% of the specified minimum. The MTS-810 electrohydraulic servo material testing machine was also used for bending test. The center diameter for bending was d = 3a (with “a” being the thickness of the samples) and the bending angle was 180°. There should be no visible defects exceeding 3 mm in any direction. Ultrasonic testing was used to assess the integrity of welded joints in accordance with EN ISO 17640 and EN ISO 11666.
Results and discussion
Penetration simulation and heat source analysis
During the welding process, the filler wire is heated until it melts into tiny droplets. These droplets then transfer to the base metal, forming a molten pool that cools down to create a weld seam. Thus, the configuration and energy dispersion of the welding arc dictate the droplet transfer mode and the ultimate microstructure and mechanical properties of joints. The section above the melting point is separated and analyzed against the real weld to examine the appropriateness of various heat source models. The finite element model for butt joints in welding has dimensions of 100 mm × 100 mm × 12 mm, as illustrated in Fig. 3A. The central weld area has C3D8 cell grids measuring 1 mm × 1 mm × 1 mm. The welding heat source moves in the positive Z direction and the model’s six degrees of freedom are restricted at its four corners. The predefined temperature field of the model is 20 ℃. The cross-sectional data of the butt joint weld for Sample 11 with a well-formed weld were collected, as depicted in Fig. 3B, indicating a weld width of 14.35 mm and a penetration depth of 8.63 mm. The welding parameters are as follows: welding current of 310A, welding speed of 30 cm min−1, wire extension of 14 mm, and a heat efficiency of 0.827.
Table 5 shows the varying physical parameters of base steel at different temperatures. Through the linear interpolation method, thermophysical parameters are segmented into piecewise linear forms and used in CAE calculation.
Gaussian double ellipsoid heat resource model shown in Fig. 4, is applied to describe the heat distribution of conventional MAG welding27,28,29,30. Set the half-axis parameters of the double ellipsoid to be \((a,b,c_{1} ,c_{2} )\), and the proportions of heat input in the front and back hemispheres are \(f_{f}\) and \(f_{r}\) respectively. \(Q\) is the total heat input power.
The heat flow distribution of can be expressed by Formula (1, 2) as following31.
Taking the fusion width as the end point of the iterative calculation, the fusion line is multiplied until \(a = 14.35\), \(b = 8.63\), \(c_{1} = 6.3\), \(c_{2} = 17.5\), \(f_{f} = 0.4\), \(f_{{\text{r}}} = 0.6\). Figure 5 illustrates the welding temperature distribution on the cross section of the workpiece, which was calculated using the double ellipsoid heat source model. The actual weld pool fusion line and upper surface boundary enclose an area of 54.42 mm2. However, the simulated fusion line and upper surface boundary enclose an area of 63.47 mm2, exhibiting a significant error of 16.63%. Moreover, the simulated contour morphology does not correspond to the actual shape of the flat upper and narrow lower surfaces.
Due to the significant difference between the high and low ends of Super Spray MAG joints, a combined heat source is being considered. To simulate the surface profile of the molten pool, a Gaussian heat source is utilized as the surface heat source. Additionally, a peak linear attenuation Gaussian cylinder heat source is used to simulate the penetration of the molten pool. The energy distribution coefficients are \(\chi_{1}\), \(\chi_{2}\) respectively.
Gauss surface heat source is used for the surface part of the workpiece, and the heat flux formula32, 33is
where \(r_{TOP}\) is the effective action radius of surface Gaussian heat source. In order to reflect the energy distributing concentration of welding heat source. Define \(r_{m}\) as the action radius when the welding heat source is not divergent (taking the inner diameter of the nozzle as the reference value), and \(k\) is the ratio of the effective action radius \(r_{TOP}\) and \(r_{m}\),
where, replace Formula (3) with Formula (4) to obtain the final heat flux formula on the workpiece surface as following
where, \(\alpha\) is the heat flow concentration coefficient and defined as below
The rest of the workpiece adopts cylinder heat source, described by following formula34,
where, \(r_{0}\) is the effective radius of the heat source, \(H\) is the heat affected height, and \(m\) is the heat flow attenuation factor.
Taking the fusion width as the end point of iterative calculation35, the fusion line is multiply fitted until \(r_{m}\) = 6.5, \(\alpha\) = 1.65, H = 8.63, m = 0.2, \(r_{0}\) = 1.95, \(\chi_{1} = 0.3\), \(\chi_{2} = 0.7\). The welding temperature field of workpiece cross section calculated by Combined heat source model is shown in Fig. 6. The area enclosed by the simulated fusion line and the upper surface boundary is 55.44 mm2, with a little error of 1.87%. The calculation accuracy is greatly improved, and the curve shape is in good agreement with the reality.
The overall evaluation of Super Spray MAG arc energy concentration can be carried out as following. The total effective radius is \(r_{TOP} = kr_{m} = \sqrt \alpha r_{m} = 8.35\;\;{\text{mm}}\), and 70% energy is concentrated within the effective action radius of cylinder heat source \(r_{0} = 1.95\;\;{\text{mm}}\). The current density in this range is 77 times greater than the average current density, and the arc energy is efficiently compressed, exhibiting high-energy beam characteristics similar to those of lasers. Dynamic arc observations also verify and support this combined effect and high-energy beam characteristics. As shown in Fig. 7, in contrast to conventional MAG welding, the majority of the heat flux of Super Spray MAG arc is centered, indicating a reduced cylindrical heat source effect. However, there is still a certain level of conical divergence in arc compression, showing the Gaussian surface heat source effect36. Under different forms of heat source, the energy obtained from welding arc varies greatly. The droplet transfer in Super Spray MAG welding is primarily in the form of spray transfer, while conventional MAG welding typically employs globular transfer.
Further observation of welding arc and droplets was conducted by using high speed camera. The arc shape can directly reflect the degree of compression of the arc. As illustrated in Fig. 8A, B, at a welding current of 280 A and a wire extension of 16 mm, droplets are transferred in a globular shape and are wider than half the diameter of the welding wire. The arc exhibits divergence, instability, and oscillation, transitioning from an energy-dense cone to an energy-dispersive bell shape. Meanwhile, the droplet flow is intermittent and uneven. When the current is raised to 310 A and the wire extension is held at 16 mm, as depicted in Fig. 8C, D, droplets flow in a manner similar to a gurgling stream consisting of stream-like liquid beads. The arc has a tighter concentration with a smaller distribution angle and maintains its conical shape without noticeable changes. The droplets transfer streamly, uniformly and steadily, with a diameter of about half of the weld wire. When the welding current is increased to 340 A with a wire extension of 16 mm, there is a noticeable arc jump observed in Fig. 8E, F. However, the conical shape of the upper tip and lower flat remain intact, and the droplet spray stream becomes more uniform and coarse. Notably, when the wire extension was raised to 18 mm, as illustrated in Fig. 8G, H, the spray stream became unstable, resulting in breakage and splashing.
Regularities of weld penetration
For thick plates, narrow and deep cooled weld pools are expected. To analyze the regularities of arc control parameters on penetration, the depth and width of weld pools, i.e. heat source depth and heat source width, were inferred by intercepting the cross section as shown in Fig. 9. The depth-width ratio can characterize the penetration effectiveness of welding arcs.
The welding test procedure parameters and the weld cross section morphological data are shown in Tables 6, 7 and 8. According to the range analysis in the Heat source depth column of Table 8, the Range R values for welding current, wire extension, and welding speed were 4.48, 1.65, and 0.72, respectively. It can be concluded that the welding current mainly affects penetration, followed by wire extension. The welding speed has little effect on penetration. Increasing welding current within a certain range and reducing wire extension can effectively improve weld penetration and hardness. But after reaching a peak, weld penetration decreases with the increase of welding current. In contrast, on weld width, welding speed has the greatest influence, followed by wire extension, and welding current has no influence.
Microstructure evolution
Analysis of grains and phases can assess how the microstructure evolves and whether the structure is reliable. It refers to Refs.26, 38, 39 to observe morphology. The microstructure morphology of some typical experimental weld joints is shown in Fig. 10. Each joint is divided into weld zone, fusion zone, heat affected zone and base metal zone. As mentioned in the literature, the weld zone is mainly composed of initial austenite grains and net pre-eutectic ferrites precipitated between grains. The fusion zone has the deepest color and forms an obvious fusion line with the weld zone, where cracks are most likely initiated. The heat affected zone is lighter than the fusion zone and darker than the base metal. The base metal shows typical rolling flow lines, with grain flattened and elongated and black pearlites scattered between the flow lines.
In typical MAG welding joints, depicted in Fig. 10A–C, the central area displays fine equiaxed grains, with more well-formed columnar crystals in the branching direction. The heat affected zones exhibit strip martensites with slight variations in orientation. But for Super Spray MAG welding, as shown in Fig. 10D–L, apical dominance of heat conduction is more evident. The austenite grains are radially distributed symmetrically from the center like veins on a leaf. This suggests that heat conduction from the center of the heat source is most efficient, spreading along the trunk and then outwards along the lateral branches during welding. With the change of arc control parameters, the weld penetration of all samples changes greatly and the precipitated structure is similar. But its distribution and morphology, especially on both sides of the fusion line, are very different. Based on the microstructure morphology of the welded zone and surrounding regions, it can be observed that, under low current of 280 A, the initial austenite grains in the weld zone appear to be coarse. Additionally, the pre-eutectoid ferrite grids display uneven patterns with wide boundaries. There are few granular pearlites and granular ferrites precipitated in the crystal. In the fusion zone, strip martensites precipitated between pearlites and ferrites. As the welding current increases, the austenite grains in the weld zone become more refined, and the pre-eutectoid ferrite grids become shorter and slender. The precipitation of pearlites and ferrites occurs more appropriately in crystals, and martensites in the fusion zone gradually change from a regular strip shape to a more interlaced flake or pine needle shape. Of all samples, Sample 14 was fully penetrated with the most developed trunk and shortest branches. There is a tendency for initial austenite crystals to become equiaxed at the ends of branches where pre-eutectoid ferrites are present in lower amounts and pearlites are precipitated more frequently. Therefore, the heat transfer in the penetration direction is faster and further than that in the width direction.
Optimization of welding process parameters
Back Propagation Neural Network (BPNN) model for Super Spray MAG Welding were specified in Fig. 11. The input layer had 3 nodes, i.e. welding current, welding speed and wire extension. The output layer also had 3 nodes, weld penetration, weld width and weld hardness. Using the data in Tables 6 and 7, 70% were selected for training, 15% for verification, and 15% for simulation. Through repeated tests, 12 were selected as the number of hidden layer nodes under the condition that the network error is as small as possible.
The transfer function between the input layer and the hidden layer was set to function tansig, the transfer function between the hidden layer and the output layer was function purelin, and the network training function is function trainlm. Due to the large difference in the range of factors, function mapminmax was used to normalize the input parameters, and the output parameters were anti-normalized. The max-epoch for the training network was 8000, and the mean square deviation was below 0.0003. The MATLAB program code for building neural networks was as follows:
After 8 iterations, the target accuracy requirements were met as shown in Fig. 12A. Although the BP neural network had been formed and the corresponding parameters of each layer had been obtained, model verification was required. The accuracy and generalization of the model were fully verified with the remaining 8 groups of experimental data. Figure 12B shows the audit results. It can be seen that the confidence levels of the training, verification and test samples were all above 85%.
Then, based on BPNN, Genetic Algorithm (GA) was performed for optimization, as shown in Fig. 13. BPNN prediction data were imported into the GA model for fitness calculation, and individuals with lower fitness values were selected as breeding parents. Then, the propagated sub-individuals were converted into new prediction data, simulated by neural networks and calculated fitness. This cycle continued until the optimal individual was finally obtained.
The weld penetration was calculated by using the neural network constructed by calling the fitness function, and the fitness value was obtained by comparing the weld penetration with the target value of 12 mm. The construction program code is as follows:
Call function Genetic Algorithm in MATLAB for multi-objective optimization, take the number of variables nvars = 3, the lower limit of variables lb = [280 30 10], the upper limit ub = [370 50 18]. The MATLAB function program code is as follows:
Through calculation, the optimal solution is 316.0877, 42.5068, 12.1823. The rounding parameters are: welding current 316 A, welding speed 42 mm/min, and wire extension 12 mm.
Verification
The optimum parameters are substituted in the BPNN model for simulation verification, and the weld penetration is 12 mm, the weld width is 9.34 mm, the Brinell hardness of the weld is 224.23 HB, and the error is less than 5%. The precise control of welding formation and mechanical properties is realized, and the accuracy of genetic algorithm optimization is verified.
Moreover, the results of tensile, bending and impact tests are shown in Table 9, indicating that tensile strength of all joints is greater than that of the base metal. The fracture position of the tensile sample is not at the weld seam but in the base metal zones, which can meet the design requirements. There are no defects on the surface of the four bending samples, and the plasticity of the welded joint is perfect. The impact energy of weld and heat affected zone at – 20 ℃ is higher than that of the base metal. Ultrasonic flaw detection was carried out to detect internal defects. The Grade I qualification rate for ultrasonic flaw detection of the preferred combination is over 90%.
Application
Deep penetration technology, using Super Spray MAG welding, has been successfully applied to weld TBM main drives, cutterheads, and various structural components, as depicted in Fig. 14. Moreover, the initial pass rate for Grade I ultrasonic flaw detection of welded joints exceeds 99%, enabling complete welding automation for critical TBM components. Furthermore, under the requirements of equal strength, as shown in Fig. 15, Super Spray MAG welding could reduce the volume of groove cutting and require less filler metal, saving energy and material. Generally, the amount of welding wire used and the energy consumption of Super Spray MAG Welding can be reduced by 25%, respectively, and the direct cost can be reduced by 30% compared to conventional MAG welding. It not only greatly improves weld quality and welding efficiency, but also becomes more green and environmentally friendly.
Conclusion
The heat source properties, penetration mechanism, and valuable processing parameters for Super Spray MAG welding were investigated. Compared to traditional GMAW welding, eliminating pulses and achieving a consistent and dependable spray welding process can greatly enhance welding efficiency and achieve full penetration.
-
The heat flux of Super Spray MAG welding can be described by the combined model of Gaussian surface heat source and peak linear attenuation Gaussian cylinder heat source. The simulation results are highly consistent with the actual shape of the molten pool.
-
Weld penetration is very sensitive to changes in welding current and wire extension. Increasing welding current within a certain range and reducing wire extension can effectively improve weld penetration, strength, hardness and qualification rate for defect detection. But after reaching a peak, weld penetration and joint performance decline as welding current increases.
-
Super Spray MAG arc has a high energy concentrated heat flux, resulting in higher pool temperature, stronger diffusion and faster nucleation than conventional MAG welding. In a certain range, welding current can improve pearlite precipitation and refinement of pre-eutectoid ferrites in the weld zone, and promote martensite refinement.
-
The BPNN-GA model is capable of accurately predicting weld formation and facilitating progress optimization. For achieving a 5 mm penetration with Super Spray MAG welding, recommended parameters include a welding current of around 316 A, a welding speed of 42 cm/min, and a wire extension of 12 mm.
At present, the Super Spray MAG welding equipment still has a heavy and complex structure, and needs simplification to improve the accessibility of all positions. This will enable the full automation of welding for even more multifaceted structural components.
Data availability
In relation to the availability of raw data I want to inform you that this work is a part of a long research study, and the raw data will not be public at the moment but are available from corresponding author upon the request.
References
Zheng, Y.-L. & He, L. TBM tunneling in extremely hard and abrasive rocks: Problems, solutions and assisting methods. J. Cent. South Univ. 28, 454–480. https://doi.org/10.1007/s11771-021-4615-z (2021).
Yang, M., Xia, Y.-M., Lin, L.-K., Qiao, S. & Ji, Z.-Y. Optimal design for buckets layout based on muck removal analysis of TBM cutterhead. J. Cent. South Univ. 27, 1729–1741. https://doi.org/10.1007/s11771-020-4403-1 (2020).
Huo, J. et al. Dynamic analysis and experimental study of a Tunnel boring Machine testbed under multiple conditions. Eng. Fail. Anal. 127, 105557. https://doi.org/10.1016/j.engfailanal.2021.105557 (2021).
Zong, R., Chen, J. & Wu, C. A comparison of double shielded GMAW-P with conventional GMAW-P in the arc, droplet and bead formation. J. Mater. Process. Tech. 285, 116781. https://doi.org/10.1016/j.jmatprotec.2020.116781 (2020).
Chen, C., Fan, C., Cai, X., Lin, S. & Yang, C. Analysis of droplet transfer, weld formation and microstructure in Al-Cu alloy bead welding joint with pulsed ultrasonic-GMAW method. J. Mater. Process. Tech. 271, 144–151. https://doi.org/10.1016/j.jmatprotec.2019.03.030 (2019).
Cai, X. et al. The effects of double groove type on the backing weld penetration in swing arc vertical-up MAG welding. Weld. World 63, 1133–1143. https://doi.org/10.1007/s40194-019-00737-w (2019).
Dutra, J. C., Gonçalves-Silva, R. H., Riffel, K. C. & Marques, C. High-performance GMAW process for deep penetration applications. Weld. World 64, 999–1009. https://doi.org/10.1007/s40194-020-00889-0 (2020).
Almeida, T., da Mendes, M. & Scotti, K. The effect of switchback parameters on root pass formation of butt welds with variable gap. J. Manufact. Mater. Process. 3, 54. https://doi.org/10.3390/jmmp3030054 (2019).
Zhao, D., Bezgans, Y., Vdonin, N., Radionova, L. & Bykov, V. Modeling and optimization of weld bead profile with varied welding stages for weathering steel A606. Int. J. Adv. Manuf. Tech. 116, 3179–3192. https://doi.org/10.1007/s00170-021-07722-y (2021).
Mathivanan, A., Senthilkumar, A. & Devakumaran, K. Pulsed current and dual pulse gas metal arc welding of grade AISI: 310S austenitic stainless steel. Defence Technol. 11, 269–274. https://doi.org/10.1016/j.dt.2015.05.006 (2015).
Phillips, D. H. Arc Welding Processes in Welding Engineering: An Introduction 4–73 (Wiley, 2016). https://doi.org/10.1002/9781119191407.ch2.
Kah, P. Chapter 1—Gas Metal Arc Welding in Advancements in Intelligent Gas Metal Arc Welding Systems (ed. Paul, K.) 1–103 (Elsevier, 2021). https://doi.org/10.1016/b978-0-12-823905-6.00001-5.
Kah, P. Chapter 4—Control of GMAW in Advancements in Intelligent Gas Metal Arc Welding Systems (ed. Paul, K.) 165–279 (Elsevier, 2021). https://doi.org/10.1016/b978-0-12-823905-6.00004-0.
Abioye, T. E., Omotehinse, I. S., Oladele, I. O., Olugbade, T. O. & Ogedengbe, T. I. Effects of post-weld heat treatments on the microstructure, mechanical and corrosion properties of gas metal arc welded 304 stainless steel. World J. Eng. 17, 87–96. https://doi.org/10.1108/wje-11-2019-0323 (2020).
John, M., Kumar, P. A. & Bhat, K. U. AHSS welding using undermatching filler wires and process advantages with P-GMAW. Mater. Today-Proc. 49, 1312–1318 (2022).
Wu, K., Cao, X., Yin, T., Zeng, M. & Liang, Z. Metal transfer process and properties of double-wire double pulsed gas metal arc welding. J. Manuf. Process. 44, 367–375. https://doi.org/10.1016/j.jmapro.2019.06.019 (2019).
Wu, K., Yin, T., Ding, N., Zeng, M. & Liang, Z. Effect of phase on the behavior of metal transfer in double-wire pulsed GMAW. Int. J. Adv. Manuf. Tech. 97, 3777–3789. https://doi.org/10.1007/s00170-018-2140-5 (2018).
Hamed Zargari, H. et al. Metallurgical characterization of penetration shape change in workpiece vibration-assisted tandem-pulsed gas metal arc welding. Mater. Basel 13, 3096. https://doi.org/10.3390/ma13143096 (2020).
Gao, X., Wang, L., Chen, Z., Zhang, Y. & You, D. Process stability analysis and weld formation evaluation during disk laser–mag hybrid welding. Opt. Laser Eng. 124, 281–293. https://doi.org/10.1016/j.optlaseng.2019.105835 (2020).
Wang, X., Luo, Z., Liu, Y. & Fu, L. Fatigue properties of advanced high strength steel plate welded by hybrid plasma arc welding. Procedia Struct. Integr. 22, 59–63. https://doi.org/10.1016/j.prostr.2020.01.008 (2019).
Bunaziv, I., Frostevarg, J., Akselsen, O. M. & Kaplan, A. F. H. Process stability during fiber laser-arc hybrid welding of thick steel plates. Opt. Laser Eng. 102, 34–44. https://doi.org/10.1016/j.optlaseng.2017.10.020 (2018).
Üstündağ, Ö., Gook, S., Gumenyuk, A. & Rethmeier, M. Hybrid laser arc welding of thick high-strength pipeline steels of grade X120 with adapted heat input. J. Mater. Process Tech. 275, 116358. https://doi.org/10.1016/j.jmatprotec.2019.116358 (2020).
Sun, Z., Han, Y., Du, M., Tong, J. & Hong, H. An improved simulation of temperature field in VPPA–GMAW of Al–Cu–Mg alloy. J. Mater. Process Tech. 263, 366–373. https://doi.org/10.1016/j.jmatprotec.2018.08.017 (2019).
Zhai, P. et al. Effects of arc length adjustment on weld bead formation and droplet transfer in pulsed GMAW based on datum current time. Metals-Basel 10, 665. https://doi.org/10.3390/met10050665 (2020).
Yang, K. et al. Prediction of HAZ microstructure and hardness for Q960E joints welded by triple-wire GMAW based on thermal and numerical simulation. Mater. (Basel) 14, 17. https://doi.org/10.3390/ma14174898 (2021).
Chen, Z. Chapter 2—Welding Metallurgy Physics in Dictionary of Welding Engineers (ed Lv, D.) 103–210(China Machine Press, 2009).
Azar, A. S., Ås, S. K. & Akselsen, O. M. Determination of welding heat source parameters from actual bead shape. Comput. Mater. Sci. 54, 176–182. https://doi.org/10.1016/j.commatsci.2011.10.025 (2012).
Mondal, A. K., Kumar, B., Bag, S., Nirsanametla, Y. & Biswas, P. Development of avocado shape heat source model for finite element based heat transfer analysis of high-velocity arc welding process. Int. J. Therm. Sci. 166, 107005. https://doi.org/10.1016/j.ijthermalsci.2021.107005 (2021).
Devaraj, J., Ziout, A. & Abu Qudeiri, J. E. Dissimilar non-ferrous metal welding: An insight on experimental and numerical analysis. Metals-Basel 11, 31. https://doi.org/10.3390/met11091486 (2021).
Piekarska, W. & Kubiak, M. Theoretical investigations into heat transfer in laser-welded steel sheets. J. Therm. Anal. Calorim. 110, 159–166. https://doi.org/10.1007/s10973-012-2486-0 (2012).
Zhang, T., Wu, C. S., Qin, G. L., Wang, X. Y. & Lin, S. Y. Thermomechanical analysis for Laser plus GMAW-P hybrid welding process. Comput. Mater. Sci. 47, 848–856. https://doi.org/10.1016/j.commatsci.2009.11.013 (2010).
Gui, X. Y., Gao, X. D., Zhang, Y. X. & Wu, J. K. Investigation of welding parameters effects on temperature field and structure field during laser-arc hybrid welding. Mod. Phys. Lett. B 36, 12. https://doi.org/10.1142/s0217984921504674 (2022).
Chen, Z., Wu, Z., Lu, S., Zhang, G. & Yan, H. A new laser welding method of two transparent plastic parts based on reflector assisted method. J. Market. Res. 24, 5309–5320. https://doi.org/10.1016/j.jmrt.2023.04.108 (2023).
Podder, D., Mandal, N. R. & Das, S. Heat source modeling and analysis of submerged arc welding. Weld. J. 93, 183S-192S (2014).
Cheon, J. & Na, S.-J. Influence of simulation methods of temperature distribution on thermal and metallurgical characteristics in GMA welding. Mater. Des. 108, 183–194. https://doi.org/10.1016/j.matdes.2016.06.090 (2016).
Cheon, J., Kiran, D. V. & Na, S.-J. CFD based visualization of the finger shaped evolution in the gas metal arc welding process. Int. J. Heat Mass Transf. 97, 1–14. https://doi.org/10.1016/j.ijheatmasstransfer.2016.01.067 (2016).
Chen, C., Lv, N. & Chen, S. B. Weld penetration monitoring for pulsed GTAW using visual sensor based on AAM and random forests. J. Manuf. Process. 63, 152–162. https://doi.org/10.1016/j.jmapro.2020.04.005 (2021).
Kou, S. Weld Metal Solidification II: Microstructure Within Grains in Welding Metallurgy 199–215 (Wiley, 2002). https://doi.org/10.1002/0471434027.ch8.
Phillips, D. H. Welding Metallurgy of Carbon Steels in Welding Engineering 187–202 (Wiley, 2016). https://doi.org/10.1002/9781119191407.ch10.
Acknowledgements
Test platforms and application conditions in this paper are provided by China Railway Construction Heavy Industry Group Co., Ltd.
Funding
This paper is supported by the Special Project of Construction of Innovative Provinces in Hunan, China (Granted no. 2019GK1010) and the Fundamental Research Funds for the Central Universities of Central South University (Granted no. 2018zzts020).
Author information
Authors and Affiliations
Contributions
L.Z.L. designed the study, performed the research, analysed data and wrote the paper. Y.M.X. revised the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, Z., Xia, Y. Heat source modeling, penetration analysis and parametric optimization of super spray MAG welding. Sci Rep 13, 9435 (2023). https://doi.org/10.1038/s41598-023-36505-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-36505-6