Abstract
Twisted heterostructures of two-dimensional crystals offer almost unlimited scope for the design of new metamaterials. Here we demonstrate a room temperature ferroelectric semiconductor that is assembled using mono- or few-layer MoS2. These van der Waals heterostructures feature broken inversion symmetry, which, together with the asymmetry of atomic arrangement at the interface of two 2D crystals, enables ferroelectric domains with alternating out-of-plane polarization arranged into a twist-controlled network. The last can be moved by applying out-of-plane electrical fields, as visualized in situ using channelling contrast electron microscopy. The observed interfacial charge transfer, movement of domain walls and their bending rigidity agree well with theoretical calculations. Furthermore, we demonstrate proof-of-principle field-effect transistors, where the channel resistance exhibits a pronounced hysteresis governed by pinning of ferroelectric domain walls. Our results show a potential avenue towards room temperature electronic and optoelectronic semiconductor devices with built-in ferroelectric memory functions.
Similar content being viewed by others
Main
Ferroelectrics are crystals that feature intrinsic charge polarization with two or more preferred stable directions of the polarization vector, determined by the lattice symmetry. Switching between those stable polarization states can be controlled by an external electric field, allowing various applications including non-volatile memory, microwave devices, transistors and sensors1,2. Of particular interest are ferroelectric semiconductors that would potentially allow field-effect transistors with additional functionality, for example storing information. However, it has proved challenging to find suitable materials that will both remain ferroelectric at room temperature and can be manufactured as the thin films required by the microelectronics industry3. The latter requirement is a severe challenge for traditional oxides due to their poor interface quality, which limits the realistically achievable homogenous ferroelectric layer thicknesses1. An alternative is to use layered crystals that can be cleaved or grown in ultrathin form while retaining surface quality. Only few such materials have been experimentally demonstrated so far, including in-plane ferroelectric SnTe (ref. 4), out-of-plane CuInP2S6 (ref. 5) and both types of ferroelectricity in different phases of In2Se3 (ref. 6,7). Up to now, out-of-plane switchable ferroelectricity at room temperature was achieved only in films thicker than 3 nm (ref. 8).
Recently, a new trend in creating truly two-dimensional (2D) ferroelectrics has emerged, which exploits interfacial charge transfer in stacked heterostructures of 2D materials. Layer-by-layer assembly of van der Waals heterostructures from various 2D crystals has matured into a sophisticated experimental field allowing for ultra-sharp and ultra-clean interfaces9 and control the rotation (that is, twist) angle between adjacent layers with high precision. Introducing twist gives rise to moiré superlattices: a periodic variation of a local atomic registry. For small twist angles (θ < 2°) 2D atomic lattices with similar unit cell sizes often undergo substantial reconstruction due to the energy gain from the preferential stacking domains balancing the cost of the resulting lattice strain10,11. Such commensurate domains have been recently shown to host ferroelectricity in marginally twisted wide band gap insulator, hexagonal boron nitride12,13,14 and in semimetallic WTe2 (ref. 15) with the ability to switch the domain type by application of an external electric field and sliding of atomic planes along the interface. Similar domain evolution has also been achieved by electrostatic gating of non-ferroelectric ABC/ABA trilayer graphene domains16.
Here, we report an observation of robust room temperature ferroelectricity in marginally twisted MoS2. While ferroelectricity in transition metal dichalcogenide (TMD) bilayers with parallel stacking of unit cells has been predicted theoretically17, and layer-polarized electronic band-edge states have been recently observed in electron tunnelling10 and optical properties18, the net charge transfer and, therefore, the steady-state electrical polarization has not been shown experimentally. We use a combination of electron channelling microscopy, Kelvin-probe force microscopy (KPFM) and electron transport measurements to explore ferroelectric domain networks in MoS2 bilayers and their dependence on the interlayer twist angle. We demonstrate that such domains can be switched by an external out-of-plane electric field and also find that domain switching produces a strong a response in the lateral electronic properties of the twisted MoS2 layers. Together with the extraordinary optical properties of TMDs19, our work offers a promising avenue towards designing new devices where both memory effect and optoelectronic functionality can be achieved within a single interface in the ultimate 2D limit.
Electron imaging of domain networks and their response to transverse electric field
In homobilayers of MoS2, the period \(\ell = a/\theta\) of the domain network is much longer than the lateral lattice constant, a, of MoS2 and is determined by the twist angle, θ. If the two MoS2 layers are oriented ‘parallel’, they form a bilayer of bulk 3R polytype when \(\theta = 0^\circ ,\) and a triangular network of 3R commensurate domains when \(0 < \theta < 2^\circ\). Such domains are separated by domain walls that have been identified as partial dislocations in earlier transmission electron microscopy studies10. To investigate the possible presence of ferroelectricity we have assembled bilayers of MoS2 using the tear and stamp technique20 aiming at a zero global misalignment angle. While ideally this could result in a 3R bilayer, small random deformations inflicted by the transfer process21 lead to a gradual variation of the misalignment angle \(\left| \theta \right| < 0.1^\circ\). To visualize the resulting domain structure, we adopt back-scattered electron channelling contrast imaging (BSECCI), previously used for bulk materials22. We find that this technique provides a clear contrast even for twisted bilayers encapsulated under hexagonal boron nitride (hBN) crystals that were several nanometres thick, similar to the recently used channelling-modulated secondary electron imaging23 (for details, see Supplementary Information). An example of BSECCI in Fig. 1a shows triangular domains of varying sizes (from <100 nm to >1 μm), which enables us to establish and quantify the dependence of domain behaviour on their lateral dimensions. The stacking order of the two domain types (seen as regions of dark and light contrast in Fig. 1a) is illustrated schematically in Fig. 1b and denoted as MotSb (StMob) corresponding to the vertical alignment of molybdenum atomic positions in the top layer with sulfur positions in the bottom (and vice versa). As MotSb can be seen as a mirror image of StMob stacking, they feature equal adhesion energies and therefore are expected to occupy similar areas of the sample, in agreement with our observations.
In contrast to TMD bilayers with 2H stacking (antiparallel) that possess both C3 rotational and inversion symmetry, the lattice of 3R bilayers is only C3-symmetric, having neither an inversion centre nor a mirror reflection plane. This asymmetry allows for a steady-state electrical polarization, which has been shown theoretically17 to result from an interlayer charge transfer due to asymmetric hybridization between the conduction band states in one (for example, top) layer and the valence band states in the other (for example, bottom) layer. Charge density transferred between the layers (red for positive and blue for negative charges), computed using density functional theory (implemented in the Quantum Espresso code24) and averaged over the MoS2 unit cell area, is shown in the side panels of Fig. 1b. This analysis indicates that the resulting double layer of charge resides on the inner sulfur sublayers (Fig. 1b), generating an areal density, P = ±3.8 × 10−3 e per nm, for the out-of-plane electric dipole moment pointing up/down in MotSb/StMob domains, respectively. This also agrees with the estimation, \(P = {\it{\epsilon }}_0{\Delta}V^{{\mathrm{FE}}}\) obtained using the DFT-calculated ferroelectric (FE) potential of the stacking-dependent double layer, \({\Delta}V^{{\mathrm{FE}}}\) (\(|{\Delta}V^{{\mathrm{FE}}}| = 63\,{{{\mathrm{mV}}}}\) for 3R stacking), described in the Supplementary Information. Coupling to this electrical polarization with an applied electric field favours—depending on the direction of the external field—either MotSb or StMob stacking, providing a means to modify the domain structure.
To observe this ferroelectricity experimentally we encapsulated twisted MoS2 bilayers in hBN and used graphene on both sides to enable electrostatic gating (see Supplementary Information for further details). This design allowed us to apply a transverse field across the twisted bilayer without introducing any noticeable carrier density. First, we consider the effect of an applied field on a double-gated bilayer region containing elongated stripe domains as shown in Fig. 1c–g. These images show that the domain structure strongly varies with the application and reversal of the out-of-plane electric displacement, \(D = {\it{\epsilon }}_0V{\it{\epsilon }}_r/h\) (where \({\it{\epsilon }}_r = 3.5\) is the relative permittivity of hBN25,26 and h is the total thickness between the graphene gates in nm), achieved by varying gate voltages, V. The domain configuration, prepared by applying \({\it{\epsilon }}_0^{ - 1}D = 2.2\,{{{\mathrm{V}}}}{{{\mathrm{nm}}^{-1}}}\) (the field pointing up), stays the same on removing the gate voltage (D = 0) (Fig. 1c,d). Then, the application of \({\it{\epsilon }}_0^{ - 1}D = - 1.75\) V nm−1 (the field pointing down) gradually expands the area of the lighter contrast domain type at the expense of the darker contrast ones. Again, if the gate voltage is swept back, the domain structure remains the same up to D = 0 and through a small interval of positive voltages, but then it returns to an almost identical configuration as was observed at the beginning of the hysteresis cycle (Fig. 1c,g). This behaviour allows us to assign MotSb domain (polarization vector pointing up) to the darker contrast domains and vice versa. A more detailed study of the domain evolution on sweeping D is shown in Supplementary Fig. 2. Although the ‘darker contrast’ domains in Fig. 1e appear to be ‘squeezed’ to almost unnoticeable width (marked by red arrows), they still remain visible as thin line defects within the expanded light contrast domains. On reversal of the field, these lines serve as precursors for growing domains of opposite polarization (dark contrast in Fig. 1g). This behaviour indicates that a pair of partial dislocations at MotSb/StMob and StMob/MotSb boundaries combines into a topologically protected defect, a perfect dislocation between two domains of the same orientation (barely visible at the spatial resolution of Fig. 1c–g; see also below). Note that some domains change relatively little with gate voltage (see, for example, the bottom-left domain in Fig. 1c–g), which can be attributed to domain wall pinning by structural imperfections (sample edges, hydrocarbon bubbles and so on). Although the BSECCI imaging carries information only about the atomic structure of the observed domains, the hysteretic switching observed in response to an external electric field is a distinctive characteristic of ferroelectric materials1.
A very different behaviour is observed in the areas hosting triangular domain networks on application of an electric field (Fig. 2a–c). Similar to Fig. 1c–g, the positive field favours the darker contrast domains and the negative field favours the lighter contrast ones. However, in these triangular networks, the nodes, where three domain walls intersect, remain fixed for all electric displacements. The domains expand (contract) by concave (convex) curvature of the domain walls, with the degree of curvature changing continuously with the applied electric field. Rounding of the walls starts as soon as the electric field is applied, without a discernible threshold in electric displacement D, and the effect is more pronounced for long domain walls. Characterizing domain walls by the minimum distance between the nodes (length, \(\ell ,\) illustrated schematically Fig. 2h) we find that for relatively large domains (\(\ell\) roughly 400 nm) the walls can be seen to merge (Fig. 2d–f). This begins where the partial dislocations are closest, near the nodes, and causes the triangular domains to shrink to less than 50% of the original size leaving a perfect screw dislocation (PSD) that connects the smaller triangular domain to the three surrounding nodes.
Analytical description of domain wall behaviour
We describe the domain wall bending as a transverse displacement, \(y\left( {0 < x < \ell } \right)\), of a single domain walls segment from a straight line (\(y\left( x \right) = 0\)) connecting two nodes. We analyse the variation of energy per supercell of an ideally periodic network (like in Fig. 2g–i), caused by the application of an out-of-plane electric field,
The first term in the integral part of \({{{\mathcal{E}}}}_\ell\) is related to the elongation of the partial dislocations accounted as \(\sqrt {1 + y^{\prime 2}} - 1 \approx \frac{1}{2}y^{\prime 2}\), and their energy dependence, \(\bar w + \tilde w\sin ^2\phi \approx \bar w + \tilde wy^{\prime 2}\), on the deviation angle, \(\phi = \arctan y\prime \approx y\prime \equiv \frac{{{\mathrm{d}}y}}{{{\mathrm{d}}x}}\), of the domain wall axis from the closest armchair direction. In this parametrization, we can use the earlier-computed27 values of \(\bar w =\)1.05 eV nm−1 for the energy density of a partial dislocation aligned along the armchair direction, and \(\tilde w =\) 0.68 eV nm−1 for its orientation-dependent part. This approximation assumes that \(y^{\prime 2} \ll 1\) (justified in Supplementary Information). The second term in the integral accounts for the energy gain from the redistribution of the domain area, promoted by the displacement field D. Here, the coupling between the external field and the ferroelectric polarization density, P, is described using an effective dielectric screening parameter, χ, which we later estimate on the basis of the comparison with the experimentally observed evolution of domains with various sizes, \(\ell\).
The remaining terms in equation (1) account for the possible merger of two partial dislocations into a PSD. The PSDs will separate two equivalently polarized domains near the network nodes and will be aligned along the MoS2 zigzag directions (at ±30o from the armchair directions, which are also the partial dislocation orientations in the unperturbed domain network). Formation of a PSD requires a sufficiently high displacement field characterized by a threshold value, \( D_ \ast (\ell ) \propto \ell ^{ - 1}\). The PSDs, are characterized27 by energy density, u = 2.24 eV nm−1, and, when projected onto the intervals \(0 < x < \delta\) and \(\ell - \delta < x < \ell\), set boundary conditions for the remaining partial dislocation segment, as \(y(\delta ) = y(\ell - \delta ) = \delta /\sqrt 3\).
For \(D < D_ \ast (\ell )\), the border between StMob and MotSb domains is obtained by the minimization of energy in equation (1) and has a parabolic shape:
By fitting the experimentally observed evolution of domain shapes for various \(\ell\) in Fig. 2a–c with equation (2), we estimate that the screening parameter is \(\chi \approx 1.5\). This value enables us to establish the domain-length-scale dependent threshold,
at which pairs of partial dislocations start merging near the network nodes into more energetically favourable PSDs. The merger occurs when the external electric field drives the partial dislocation in the neighbouring domains to touch each other. For more details, see Supplementary Information. For domains with \(\ell\) roughly equal to 400 nm, this critical regime can be reached within a realistic range of electric fields, as observed experimentally in Fig. 2d–f. Theoretically, we estimate that, for \(D > D_ \ast (\ell )\), the PSD segments grow in length near each node, as \(\frac{\ell }{{\sqrt 3 }}\frac{{D - D_ \ast }}{D}\), whereas shorter partial dislocation segments retain an approximately parabolic shape (for comparison with the exact numerical solution, see Supplementary Fig. 11c). Figure 2g–i illustrates such an evolution, with the analytical results of equations (2) and (3) laid over a polarization map of a domain structure computed using mesoscale lattice relaxation (Supplementary Information).
Surface potential studies using KPFM
Having established the inverted ferroelectric polarization inside MotSb and MobSt domains, we have also measured the potential, ΔV, created at the bilayer interface. To this end, we use two-pass phase-modulated-KPFM (PM-KPFM) on a non-encapsulated marginally twisted bilayer MoS2 (Supplementary Information).
The resulting map of the surface potential acquired is shown in Fig. 3a, where the two types of domain display a clear contrast difference. This difference, measured with a conductive scanning probe several nanometres above the sample’s surface, indicates the presence of a transverse electric field built-in to the domains polarized in the opposite directions for MotSb and MobSt regions, respectively. The potential gained due to such fields with respect to the metallic n-Si back gate, ±ΔV, is measured experimentally as a 2ΔV jump when a boundary between two domains is crossed. A histogram of the local potential, Fig. 3b, displays two major peaks corresponding to the dark and light contrast domains with the separation of 2ΔV = 100 ± 20 mV, in close quantitative agreement with the theoretically predicted17 value, 2ΔV = 126 mV, and the potential map in Fig. 3c. The measured ΔV was found to be reproducible for various locations on the sample and also consistent with the results obtained for another sample placed on graphite substrate (Supplementary Information). On applying a positive back-gate voltage to the sample, we observed that the domain pattern gradually vanishes, as expected due to screening of the ferroelectric field by the free electrons. For electron densities of roughly 1013 cm−2 the pattern becomes barely visible (Fig. 3d,e), however, the domain shape changes very little since the electric field inside the bilayer is substantially screened by the bottom MoS2 layer in the case of one-sided gating. On application of the negative gate voltage no change in contrast is observed (Supplementary Fig. 9) as no mobile holes are induced in our samples. Note that the piezo-charges reported earlier10 could partially compensate for the ferroelectric charge transfer. However, piezoelectricity has little effect on the potential in the middle of large domains, as it is caused by strain localized within several nanometres of the domain walls (see the narrow and bold curves in the inset of Fig. 2c), which is below our lateral resolution.
Ferroelectric response in the conductivity of field-effect devices
For a 2D ferroelectric semiconductor, the potential difference between the oppositely polarized domains should translate into gate-controlled doping and, therefore, electron transport through such ferroelectric field-effect transistor devices should depend on the ferroelectric domain distribution. To observe this, we have prepared and studied several heterostructures consisting of marginally twisted pairs of mono-, bi- and tri-layers (L) of MoS2. Parallel alignment for twisted monolayer-on-monolayer and trilayer-on-trilayer devices produces ferroelectric 3R interfaces between the twisted layers. However, for 2L this alignment leads to predominantly centrosymmetric 2H stacking, which has no electric polarization. These heterostructures were encapsulated in hBN and double gated (the top gate was deposited only above the main channel, whereas the bottom gate (Si wafer) was global). At zero gate voltages, all the devices were found to be insulating, and required an applied electric field of roughly 0.1 V nm−1 (that is, n ≅ 2 × 1012 cm−2) to start inducing mobile carriers. Therefore, to study the conductivity, Gsd, we applied a finite positive bottom gate voltage Vb, which was essential to induce electrical conductance in the contact regions, and then swept the top-gate voltage Vt. Because of the generally low carrier mobility of MoS2 channels at room temperature, only two-probe measurements were possible, with source-drain resistances reaching above MΩ in magnitude. Figure 3f,g shows the hysteresis observed for twisted 1L and 3L MoS2 (\(\theta = 0^\circ\)). For further examples, see the Supplementary Information. Sweeping Vt controls both the carrier concentration and the out-of-plane electric field, which leads to redistribution between domains with opposite polarities, depending on whether positive or negative gate voltage is applied, as observed in our microscopy measurements in Fig. 1. Pinning of ferroelectric domain boundaries for up and down sweeps results in memory effects and hysteresis. As a result, the sample-averaged carrier densities for the same Vt for up and down sweeps differ, leading to the observed difference in conductivities seen in Fig. 3f,g. Our reference devices made from 2L MoS2 with predominant 2H stacking (Fig. 3h) and exfoliated trilayer of 2H-MoS2 (Supplementary Fig. 13b) showed a very similar electrical response to applied gate voltages but no discernible hysteresis, because such devices do not feature switchable ferroelectric interfaces. We also tested few-layer MoS2 devices with 3R stacking. The material is an intrinsic ferroelectric, but no switching or hysteresis was observed for the prepared devices for all accessible gate voltages (Supplementary Fig. 13c). This is attributed to much stronger pinning at the 3R device edges than for movements of domain walls in marginally twisted MoS2.
Conclusions
To summarize, our study shows that switchable ferroelectric behaviour is a generic property of heterostructures assembled from atomically thin TMDs with small twist angles providing a 3R interface. Having demonstrated this by studying field-driven domain evolution in both structural (BSECCI) and electronic (KPFM and transport) properties, we have also quantified the amount of charge transfer in the ferroelectric double layer at the interface and found good agreement with theoretical modelling. These observations demonstrate a way towards atomically thin electronic devices with memory effects and open up possibilities for the design of new (opto)electronic devices. For example, strong light-matter coupling in TMDs28 and the single-photon emission by defects in individual TMD layers29 may offer a switchable single-photon emission capability. However, to realize such functional devices, further progress in van der Waals assembly is required to achieve higher interfacial homogeneity and reproducibility of twist angles. Additionally, materials parameters need to be optimized to achieve weaker domain pinning and faster switching.
Methods
Scanning electron microscopy
Samples were imaged with a Zeiss Merlin scanning electron microscope operated at 1.5 keV and probe current of 1.1 nA. The backscattered electron signal is collected at a 5 mm working distance and using an in-lens EsB detector with a 73° take-off angle and an applied energy selected grid bias of 500 V. The optimal tilt angle was established experimentally to be 20.1° while the azimuthal rotation was optimized for each sample before the measurements. For the optimized angular conditions, different acceleration voltages have been tested in the range of 1 to 6 kV, with optimal results achieved for 1.3–1.7 kV. We have found that domains can be clearly seen in BSECCI images, despite overlay of the multilayer hBN and graphene (see Supplementary Information for more details).
Two-pass PM-KPFM has been performed in high vacuum. First, the sample topography acquired in the tapping mode with the probe grounded. Then, the probe is lifted at a constant height and scanned following the sample’s topography, while an a.c. voltage, Va.c., is applied to the probe to create the oscillating electrostatic force that is further minimized by applying a d.c. voltage. This d.c. voltage is equal to the contact potential difference between the tip and the sample and allows us to extract the local work function of the surface for a known tip material. The KPFM measurements have been optimized against both lift height and Va.c. (Supplementary Information).
Data availability
Additional data related to this paper are available from the corresponding authors on reasonable request.
Code availability
The computer code used for the image filtering is available from the corresponding authors on reasonable request.
References
Martin, L. W. & Rappe, A. M. Thin-film ferroelectric materials and their applications. Nat. Rev. Mater. https://doi.org/10.1038/natrevmats.2016.8 (2016).
Mikolajick, T. et al. Next generation ferroelectric materials for semiconductor process integration and their applications. J. Appl. Phys. 129, 100901 (2021).
Bertolazzi, S. et al. Nonvolatile memories based on graphene and related 2D materials. Adv. Mater. 31, 1806663 (2019).
Chang, K. et al. Discovery of robust in-plane ferroelectricity in atomic-thick SnTe. Science 353, 274–278 (2016).
Belianinov, A. et al. CuInP2S6 room temperature layered ferroelectric. Nano Lett. 15, 3808–3814 (2015).
Zhou, Y. et al. Out-of-plane piezoelectricity and ferroelectricity in layered α-In2Se3 nanoflakes. Nano Lett. 17, 5508–5513 (2017).
Zheng, C. et al. Room temperature in-plane ferroelectricity in van der Waals In2Se3. Sci. Adv. 4, eaar7720 (2018).
Li, Y., Gong, M. & Zeng, H. Atomically thin In2Se3: an emergent two-dimensional room temperature ferroelectric semiconductor. J. Semiconduct. https://doi.org/10.1088/1674-4926/40/6/061002 (2019).
Rooney, A. P. et al. Observing imperfection in atomic interfaces for van der Waals heterostructures. Nano Lett. 17, 5222–5228 (2017).
Weston, A. et al. Atomic reconstruction in twisted bilayers of transition metal dichalcogenides. Nat. Nanotechnol. 15, 592–597 (2020).
Rosenberger, M. R. et al. Twist angle-dependent atomic reconstruction and moiré patterns in transition metal dichalcogenide heterostructures. ACS Nano 14, 4550–4558 (2020).
Woods, C. R. et al. Charge-polarized interfacial superlattices in marginally twisted hexagonal boron nitride. Nat. Commun. 12, 347 (2021).
Yasuda, K., Wang, X., Watanabe, K., Taniguchi, T. & Jarillo-Herrero, P. Stacking-engineered ferroelectricity in bilayer boron nitride. Science 372, eabd3230 (2021).
Vizner Stern, M. et al. Interfacial ferroelectricity by van der Waals sliding. Science 372, eabe8177 (2021).
de la Barrera, S. C. et al. Direct measurement of ferroelectric polarization in a tunable semimetal. Nat. Commun. 12, 5298 (2020).
Li, H. et al. Global control of stacking-order phase transition by doping and electric field in few-layer graphene. Nano Lett. 20, 3106–3112 (2020).
Ferreira, F. et al. Weak ferroelectric charge transfer in layer-asymmetric bilayers of 2D semiconductors. Sci. Rep. 11, 13422– (2021).
Sung, J. et al. Broken mirror symmetry in excitonic response of reconstructed domains in twisted MoSe2/MoSe2 bilayers. Nat. Nanotechnol. https://doi.org/10.1038/s41565-020-0728-z (2020).
Wang, G. et al. Excitons in atomically thin transition metal dichalcogenides. Rev. Mod. Phys. 90, 021001 (2017).
Kim, K. et al. Van der Waals heterostructures with high accuracy rotational alignment. Nano Lett. 16, 1989–1995 (2016).
Uri, A. et al. Mapping the twist-angle disorder and landau levels in magic-angle graphene. Nature 581, 47–52 (2020).
Wilkinson, A. J. & Hirsch, P. B. Electron diffraction based techniques in scanning electron microscopy of bulk materials. Micron 28, 279–308 (1997).
Andersen, T. I. et al. Excitons in a reconstructed moiré potential in twisted WSe2/WSe2 homobilayers. Nat. Mater. 20, 480–487 (2021).
Giannozzi, P. et al. Quantum ESPRESSO toward the exascale. J. Chem. Phys. 152, 154105 (2020).
Ahmed, F. et al. Dielectric dispersion and high field response of multilayer hexagonal boron nitride. Adv. Funct. Mater. 28, 1804235 (2018).
Laturia, A., Van de Put, M. L. & Vandenberghe, W. G. Dielectric properties of hexagonal boron nitride and transition metal dichalcogenides: from monolayer to bulk. NPJ 2D Mater. Appl. 2, 6 (2018).
Enaldiev, V. V., Zólyomi, V., Yelgel, C., Magorrian, S. J. & Fal’ko, V. I. Stacking domains and dislocation networks in marginally twisted bilayers of transition metal dichalcogenides. Phys. Rev. Lett. 124, 206101 (2020).
Britnell, L. et al. Strong light-matter interactions in heterostructures of atomically thin films. Science 340, 1311–1314 (2013).
Koperski, M. et al. Single photon emitters in exfoliated WSe2 structures. Nat. Nanotechnol. 10, 503–506 (2015).
Acknowledgements
We acknowledge support from EPSRC grant nos. EP/V007033/1, EP/P009050/1, EP/S019367/1, EP/S030719/1, EP/V036343/1 and EP/V026496/1 the CDT Graphene-NOWNANO. In addition, we acknowledge support from European Union’s Horizon 2020 Research and Innovation programme: European Graphene Flagship Core3 Project (grant agreement no. 881603), European Quantum Flagship Project 2DSIPC (820378), ERC Synergy grant Hetero2D, ERC Starter grant EvoluTEM (no. 715502), ERC Consolidator grant no. ERC-2020-COG–QTWIST—101001515, the Royal Society and Lloyd’s Register Foundation. We also want to acknowledge the support of the UK government department for Business, Energy and Industrial Strategy through the UK national quantum technologies programme.
Author information
Authors and Affiliations
Contributions
R.G., V.I.F. and A.K.G. conceived the study. A.W. fabricated and characterized experimental samples with help from A.S., W.W., M.H. and H.R. E.G.C., H.C.-L. and O.K. performed KPFM experiments and analysed the data. S.B., S.X., Z.W., Y.G., L.F. and A.K.G. have fabricated devices for electronic transport measurements, conducted the experiments and analysed the data. R.G., T.H., N.C., A.V.K. and S.J.H. conducted BSECCI experiments and analysed the data. V.E., F.F. and V.I.F. provided theoretical modelling. R.G., V.I.F., A.K.G. and A.W. wrote the manuscript. All authors contributed to the discussions and commented on the manuscript. A.W., E.G.C. and V.E. have contributed to this work equally and can claim their leading role for job applications, interviews and talks.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Nanotechnology thanks Yu-Jia Zeng and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Supplementary Information
Supplementary information including several sections describing experimental details and providing supporting data.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Weston, A., Castanon, E.G., Enaldiev, V. et al. Interfacial ferroelectricity in marginally twisted 2D semiconductors. Nat. Nanotechnol. 17, 390–395 (2022). https://doi.org/10.1038/s41565-022-01072-w
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/s41565-022-01072-w
This article is cited by
-
Tunable moiré materials for probing Berry physics and topology
Nature Reviews Materials (2024)
-
Remote epitaxy of single-crystal rhombohedral WS2 bilayers
Nature Communications (2024)
-
Excitonic signatures of ferroelectric order in parallel-stacked MoS2
Nature Communications (2024)
-
Creating chirality in the nearly two dimensions
Nature Materials (2024)
-
Atomic-level polarization reversal in sliding ferroelectric semiconductors
Nature Communications (2024)