The local coordination environment around catalytically active sites plays a vital role in tuning the activity of electrocatalysts made of carbon-supported metal nanoparticles. However, the rational design of electrocatalysts with improved performance by controlling this environment is hampered by synthetic limitations and insufficient mechanistic understanding of how the catalytic phase forms. Here we show that introducing F atoms into Pd/N–C catalysts modifies the environment around the Pd and improves both activity and durability for the ethanol oxidation reaction and the oxygen reduction reaction. Our data suggest that F atom introduction creates a more N-rich Pd surface, which is favourable for catalysis. Durability is enhanced by inhibition of Pd migration and decreased carbon corrosion. A direct ethanol fuel cell that uses the Pd/N–C catalyst with F atoms introduced for both the ethanol oxidation reaction and oxygen reduction reaction achieves a maximum power density of 0.57 W cm−2 and more than 5,900 hours of operation. Pd/C catalysts containing other heteroatoms (P, S, B) can also be improved through the addition of F atoms.
This is a preview of subscription content, access via your institution
Open Access articles citing this article.
Nature Communications Open Access 16 November 2023
Electrochemical Energy Reviews Open Access 24 August 2023
Nature Communications Open Access 11 March 2023
Access Nature and 54 other Nature Portfolio journals
Get Nature+, our best-value online-access subscription
$29.99 / 30 days
cancel any time
Subscribe to this journal
Receive 12 digital issues and online access to articles
$119.00 per year
only $9.92 per issue
Rent or buy this article
Prices vary by article type
Prices may be subject to local taxes which are calculated during checkout
Li, X., Rong, H., Zhang, J., Wang, D. & Li, Y. Modulating the local coordination environment of single-atom catalysts for enhanced catalytic performance. Nano Res. 13, 1842–1855 (2020).
Zhang, J. et al. Tuning the coordination environment in single-atom catalysts to achieve highly efficient oxygen reduction reactions. J. Am. Chem. Soc. 141, 20118–20126 (2019).
Bianchini, C. & Shen, P. K. Palladium-based electrocatalysts for alcohol oxidation in half cells and in direct alcohol fuel cells. Chem. Rev. 109, 4183–4206 (2009).
Ramaswamy, N. & Mukerjee, S. Alkaline anion-exchange membrane fuel cells: challenges in electrocatalysis and interfacial charge transfer. Chem. Rev. 119, 11945–11979 (2019).
Wang, G., Chang, J., Koul, S., Kushima, A. & Yang, Y. CO2 bubble-assisted Pt exposure in PtFeNi porous film for high-performance zinc-air battery. J. Am. Chem. Soc. 143, 11595–11601 (2021).
Li, Z. et al. Stabilizing atomic Pt with trapped interstitial F in alloyed PtCo nanosheets for high-performance zinc-air batteries. Energy Environ. Sci. 13, 884–895 (2020).
Wang, G., Yang, Z., Du, Y. & Yang, Y. Programmable exposure of Pt active facets for efficient oxygen reduction. Angew. Chem. Int. Ed. 58, 15848–15854 (2019).
Niu, W. et al. Surface-modified porous carbon nitride composites as highly efficient electrocatalyst for Zn-air batteries. Adv. Energy Mater. 8, 1701642 (2018).
Wu, G., More, K. L., Johnston, C. M. & Zelenay, P. High-performance electrocatalysts for oxygen reduction derived from polyaniline, iron, and cobalt. Science 332, 443–447 (2011).
Sun, T. et al. Design of local atomic environments in single-atom electrocatalysts for renewable energy conversions. Adv. Mater. 33, 2003075 (2021).
Yuan, K. et al. Boosting oxygen reduction of single iron active sites via geometric and electronic engineering: nitrogen and phosphorus dual coordination. J. Am. Chem. Soc. 142, 2404–2412 (2020).
Zhang, J. & Dai, L. Nitrogen, phosphorus, and fluorine tri-doped graphene as a multifunctional catalyst for self-powered electrochemical water splitting. Angew. Chem. Int. Ed. 55, 13296–13300 (2016).
Wang, Y. et al. Advanced electrocatalysts with single-metal-atom active sites. Chem. Rev. 120, 12217–12314 (2020).
Kowal, A. et al. Ternary Pt/Rh/SnO2 electrocatalysts for oxidizing ethanol to CO2. Nat. Mater. 8, 325–330 (2009).
Liang, Z. et al. Direct 12-electron oxidation of ethanol on a ternary Au(core)-PtIr(shell) electrocatalyst. J. Am. Chem. Soc. 141, 9629–9636 (2019).
Kim, I. et al. Catalytic reactions in direct ethanol fuel cells. Angew. Chem. Int. Ed. 50, 2270–2274 (2011).
Kavanagh, R., Cao, X. M., Lin, W. F., Hardacre, C. & Hu, P. Origin of low CO2 selectivity on platinum in the direct ethanol fuel cell. Angew. Chem. Int. Ed. 51, 1572–1575 (2012).
Wang, X. X., Swihart, M. T. & Wu, G. Achievements, challenges and perspectives on cathode catalysts in proton exchange membrane fuel cells for transportation. Nat. Catal. 2, 578–589 (2019).
Shao, Y., Dodelet, J. P., Wu, G. & Zelenay, P. PGM-free cathode catalysts for PEM fuel cells: a mini-review on stability challenges. Adv. Mater. 31, 1807615 (2019).
Zhou, Y. et al. A universal method to produce low–work function electrodes for organic electronics. Science 336, 327–332 (2012).
Vayenas, C. G., Bebelis, S. & Ladas, S. Dependence of catalytic rates on catalyst work function. Nature 343, 625–627 (1990).
Tian, N., Zhou, Z. Y., Sun, S. G., Ding, Y. & Wang, Z. L. Synthesis of tetrahexahedral platinum nanocrystals with high-index facets and high electro-oxidation activity. Science 316, 732–735 (2007).
Chong, L. et al. Ultralow-loading platinum-cobalt fuel cell catalysts derived from imidazolate frameworks. Science 362, 1276–1281 (2018).
Luo, M. et al. PdMo bimetallene for oxygen reduction catalysis. Nature 574, 81–85 (2019).
Lim, B. et al. Pd-Pt bimetallic nanodendrites with high activity for oxygen reduction. Science 324, 1302–1305 (2009).
Wang, M., Árnadóttir, L., Xu, Z. J. & Feng, Z. In situ X-ray absorption spectroscopy studies of nanoscale electrocatalysts. Nano Micro Lett. 11, 47 (2019).
Wang, Y., Sun, D., Wang, M., Feng, Z. & Hall, A. S. Oxygen reduction electrocatalysis on ordered intermetallic Pd–Bi electrodes is enhanced by a low coverage of spectator species. J. Phys. Chem. C 124, 5220–5224 (2020).
Liao, H. et al. A multisite strategy for enhancing the hydrogen evolution reaction on a nano-Pd surface in alkaline media. Adv. Energy Mater. 7, 1701129 (2017).
Funke, H., Scheinost, A. C. & Chukalina, M. Wavelet analysis of extended X-ray absorption fine structure data. Phys. Rev. B 71, 094110 (2005).
Funke, H., Chukalina, M. & Scheinost, A. C. A new FEFF-based wavelet for EXAFS data analysis. J. Synchrotron Radiat. 14, 426–432 (2007).
Liu, Y. et al. A highly efficient metal-free electrocatalyst of F-doped porous carbon toward N2 electroreduction. Adv. Mater. 32, 1907690 (2020).
Li, M. et al. Single-atom tailoring of platinum nanocatalysts for high-performance multifunctional electrocatalysis. Nat. Catal. 2, 495–503 (2019).
Jin, H. et al. Improved electrocatalytic activity for ethanol oxidation by Pd@N-doped carbon from biomass. Chem. Commun. 50, 12637–12640 (2014).
Tian, X. et al. Engineering bunched Pt-Ni alloy nanocages for efficient oxygen reduction in practical fuel cells. Science 366, 850–856 (2019).
Chang, J., Feng, L., Liu, C., Xing, W. & Hu, X. Ni2P enhances the activity and durability of the Pt anode catalyst in direct methanol fuel cells. Energy Environ. Sci. 7, 1628–1632 (2014).
von Weber, A. et al. Size-dependent electronic structure controls activity for ethanol electro-oxidation at Ptn/indium tin oxide (n = 1 to 14). Phys. Chem. Chem. Phys. 17, 17601–17610 (2015).
Li, Z. et al. Iridium single-atom catalyst on nitrogen-doped carbon for formic acid oxidation synthesized using a general host–guest strategy. Nat. Chem. 12, 764–772 (2020).
Brushett, F. R., Naughton, M. S., Ng, J. W. D., Yin, L. & Kenis, P. J. A. Analysis of Pt/C electrode performance in a flowing-electrolyte alkaline fuel cell. Int. J. Hydrog. Energy 37, 2559–2570 (2012).
Kaserer, S., Rakousky, C., Melke, J. & Roth, C. Design of a reference electrode for high-temperature PEM fuel cells. J. Appl. Electrochem. 43, 1069–1078 (2013).
Chung, H. T. et al. Direct atomic-level insight into the active sites of a high-performance PGM-free ORR catalyst. Science 357, 479–484 (2017).
Chang, J., Wang, G. & Yang, Y. Recent advances in electrode design for rechargeable zinc–air batteries. Small Science 1, 2100044 (2021).
Greeley, J. et al. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 1, 552–556 (2009).
Guo, Y. et al. Potential-dependent mechanistic study of ethanol electro-oxidation on palladium. ACS Appl. Mater. Interfaces 13, 16602–16610 (2021).
Cheng, Y., Tian, Y., Fan, X., Liu, J. & Yan, C. Boron doped multi-walled carbon nanotubes as catalysts for oxygen reduction reaction and oxygen evolution reaction in alkaline media. Electrochim. Acta 143, 291–296 (2014).
Chang, J., Feng, L., Liu, C., Xing, W. & Hu, X. An effective Pd-Ni2P/C anode catalyst for direct formic acid fuel cells. Angew. Chem. Int. Ed. 53, 122–126 (2014).
Hohenberg, P. & Kohn, W. Inhomogeneous electron gas. Phys. Rev. B 136, B864–B871 (1964).
Kohn, W. & Sham, L. J. Self-consistent equations including exchange and correlation effects. Phys. Rev. 140, A1133–A1138 (1965).
Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Blochl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
This work was supported by a start-up grant from the University of Central Florida. J.C. acknowledges financial support from the Preeminent Postdoctoral Program (P3) at the University of Central Florida. The XPS test was supported by the US National Science Foundation (Division of Electrical, Communications and Cyber Systems, no. 1726636), hosted in the Materials Characterization Facility and Advanced Materials Processing and Analysis Center, Department of Materials Science and Engineering, College of Engineering and Computer Science, University of Central Florida. Z.F. acknowledges support from the US National Science Foundation (National Nanotechnology Coordinated Infrastructure, no. 2025489). Guofeng Wang and B.L. acknowledge support from the US National Science Foundation (Division of Chemical, Bioengineering, Environmental and Transport Systems, no. 1804534). Computational resources were provided by the University of Pittsburgh Center for Research Computing as well as the Extreme Science and Engineering Discovery Environment, which is supported by National Science Foundation grant no. ACI-1053575. The use of the Advanced Photon Source at Argonne National Laboratory for XAS measurements at beamlines 5-BM and 12-BM was supported by the US Department of Energy under contract no. DE-AC02-06CH11357. DuPont-Northwestern-Dow Collaborative Access Team (DND-CAT) is supported through E. I. duPont de Nemours and Company, Northwestern University and the Dow Chemical Company. M.G. acknowledges support from the Guangdong Innovative and Entrepreneurial Research Team Program (grant no. 2019ZT08C044) and the Peacook Team Program supported by the Science, Technology and Innovation Commission of Shenzhen Municipality (KQTD20190929173815000).
The fluorinated fuel cell catalysts disclosed in this work have been filed as US Provisional Patent Application (Serial No. 63/260,768) with Y.Y. and J.C. as inventors. The status of the patent application is pending.
Peer review information Nature Energy thanks Wenzhen Li and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Chang, J., Wang, G., Wang, M. et al. Improving Pd–N–C fuel cell electrocatalysts through fluorination-driven rearrangements of local coordination environment. Nat Energy 6, 1144–1153 (2021). https://doi.org/10.1038/s41560-021-00940-4
This article is cited by
Nature Communications (2023)
Nature Communications (2023)
Titanium Carbide/Carbon-Supported Platinum Nanoparticles Boost Oxygen Reduction Reaction for Fuel Cells
Journal of Electronic Materials (2023)
Electrochemical Energy Reviews (2023)
Nano Research (2023)