Abstract
Doping usually reduces lattice thermal conductivity because of enhanced phonon-impurity scattering. Here, we report unexpected doping effects on the lattice thermal conductivity of quasi-one-dimensional (quasi-1D) van der Waals (vdW) TiS3 nanoribbons. As the nanoribbon thickness reduces from ~80 to ~19 nm, the concentration of oxygen atoms has a monotonic increase along with a 7.4-fold enhancement in the thermal conductivity at room temperature. Through material characterizations and atomistic modellings, we find oxygen atoms diffuse more readily into thinner nanoribbons and more sulfur atoms are substituted. The doped oxygen atoms induce significant lattice contraction and coupling strength enhancement along the molecular chain direction while have little effect on vdW interactions, different from that doping atoms induce potential and structural distortions along all three-dimensional directions in 3D materials. With the enhancement of coupling strength, Young’s modulus is enhanced while phonon-impurity scattering strength is suppressed, significantly improving the phonon thermal transport.
Similar content being viewed by others
Introduction
Benefited from actively manipulating electron transport in various semiconductor materials, microelectronics has been a driver for innovation in a wide range of applications since the invention of transistors in 1959. It is expected that atomic thin transistors made of low-dimensional materials help extend Moore’s law. In the recent two decades, tremendous efforts have been made to explore two-dimensional (2D) van der Waals (vdW) materials and their potential applications in electronic1,2, optoelectronic3,4,5, bioelectronic6, thermal7,8, and energy storage devices9,10,11. These studies suggest that 2D materials provide atomic flat surfaces free from defects, in which electrons are less prone to be scattered and charges can flow relatively freely. Compared to 2D vdW materials, quasi-1D vdW materials12 are not well explored, which can help extend Moore’s law as well.
Quasi-1D vdW materials are composed of molecular/atomic chains with strong intrachain covalent or ionic bonds assembled through relatively weak interchain vdW interactions. Compared to the restriction of strong covalent bonds on the structure in 3D materials, the presence of the vdW gaps in quasi-1D vdW materials facilitates more freedom of structure manipulation and modification such as disassembly/reassembly12,13, ions intercalation14, and substitution15. For example, quasi-1D Ta2Pt3Se8 and Ta2Pd3Se8 nanowires can be assembled together to form nanoscale heterojunctions13. The physical properties of quasi-1D vdW materials are expected to be different from those of 3D materials because of the weak vdW interactions and the vdW gaps.
An interesting quasi-1D vdW crystal is titanium trisulfide (TiS3)16,17 and it is an n-type semiconductor with a bandgap of ~1 eV18,19. TiS3 nanoribbons manifest higher current-carrying capacity than that of copper via field-effect gating20. Besides tunable electrical properties, excellent photoresponse up to 2910 A/W has also been observed in TiS3 nanoribbon-based field-effect transistors21. The wide-range tunable electron mobility and ultrahigh optical responsivity22 promise TiS3 nanoribbons various applications in electronic and optoelectronic devices23. For device applications, thermal properties are critical for thermal management because device lifetime decays exponentially with temperature24. However, so far, the thermal properties of TiS3 nanoribbons are not well explored25,26,27.
In this work, doping effects on phonon transport in quasi-1D vdW crystal TiS3 nanoribbons are reported, which demonstrates that O atoms can easily diffuse into thin TiS3 nanoribbons and significantly enhance rather than reduce lattice thermal conductivity. The replacement of sulfur atoms with oxygen atoms results in significant lattice contraction and coupling strength enhancement of TiS3 along the molecular chain direction, with little effect on vdW strengths. Compared with the doped atom inducing strain and reducing lattice thermal conductivity in 3D materials, the significant lattice contraction enhances Young’s modulus along the molecular chain direction in thin TiS3 nanoribbons, which results in an enhanced phonon group velocity and suppressed phonon-impurity scattering strength. The combination effects lead to a 7.4-fold enhancement in thermal conductivity at room temperature. This work provides a new method to actively control phonon thermal transport through doping low-dimensional materials with small atoms.
Results
Thermal conductivity of TiS3 nanoribbon
The TiS3 crystal structure is schematically shown in Fig. 1a, b: (i) transition metal Ti atoms form trigonal prismatic coordination with S atoms through Ti-S bond; (ii) these trigonal prisms connect into quasi-1D molecular chains through S-Ti-S bond along the b-axis direction; (iii) stacking of these quasi-1D chains through vdW interactions in the other 2D directions (a- and c-axis) into a quasi-1D vdW structure. Figure 1c shows a TiS3 nanoribbon placed on a microdevice composed of two suspended membranes with integrated heaters and resistance thermometers serving as the heat source and heat sink, respectively. The thermal conductivity is extracted through a microthermal bridge scheme and additional platinum electrodes patterned on the suspended membranes that allow for four-probe measurements of the electrical conductivity. The dimensions of each measured nanoribbon sample are listed in Table 1. High-resolution transmission electron microscopy (HRTEM) images viewed along the [001] (Fig. 1d) and [100] directions (Fig. 1e) indicate that the nanoribbon is grown along the b-axis direction. The inset in Fig. 1d shows a fast Fourier transform pattern of the HRTEM image, from which the lattice constants of all samples are extracted and listed in Table 2.
Figure 2a plots the measured thermal conductivity (κ) along the b-axis direction of 11 TiS3 nanoribbons with different thicknesses (Table 1) in the temperature range from 20 to 300 K, which displays several interesting trends. First, for all samples, κ displays consistent temperature dependence, with its value first increasing with temperature from 20 to ~85 K and then decreasing as the temperature further escalates. Second, κ shows a clear and unexpected thickness dependence for thinner ribbons (<52-nm thick). For example, at room temperature, κ drops from ~15.5 W/m-K for the 19 nm thick ribbon to the bulk value of ~2.1 W/m-K for ribbons of >80-nm thick (Fig. 2b), which is opposite to the expectation based on the classical size effect as reported in a recent first-principles study28. To explore width dependence, we measured three samples with different widths, all of 52-nm thick, and the results show an increasing trend with the sample width, as shown in Supplementary Fig. 2. To explore the length dependence, we measured a 26-nm-thick ribbon with different suspended lengths (see Supplementary Note 4), and Fig. 2c indicates that the room temperature thermal conductivity increases from 7.3 to 9.2 W/m-K as the suspended length increases from 4.6 to 6.6 μm, but only varies marginally (<1.5%) as the length further extends from 6.6 to 8.9 μm. Overall, while the positive correlation with sample width or length agrees with the classical size effect, the negative correlation with sample thickness is counterintuitive.
To understand the thickness dependence of thermal conductivity, we first evaluated the electronic contribution to κ based on the Wiedemann–Franz law, κe = LTσ, where L is the Lorenz number, T is the temperature and σ is the electrical conductivity. The measured σ (Supplementary Fig. 3) corresponds to a rather low κe that contributes <0.02% to κ for all samples, thus phonons dominate κ. According to the kinetic theory, the lattice κ is proportional to Cv2τ, where C is the volumetric heat capacity, v is the speed of sound and τ is the relaxation time. In a recent publication on thermal transport through NbSe3 nanowires29, it has been shown that elastic stiffening leads to a 25-fold increase of κ as the wire hydraulic diameter reduces from 26 to 6.8 nm. It has also been shown that elastic stiffening can enhance the lattice κ of silver nanowires30. As such, we measured Young’s modulus (E) of TiS3 nanoribbons and examined whether elastic stiffening occurs in thin ribbons here.
Young’s modulus of TiS3 nanoribbon
E of TiS3 nanoribbons along the b-axis was measured with a three-point bending scheme (Fig. 2d) using an atomic force microscope (AFM) for nine different samples with thickness spanning from 23 to 218 nm (Supplementary Table 1). A typical force–deflection (F–D) curve is plotted in Fig. 2f, from which E is extracted (Supplementary Note 5). Consistent with the thermal conductivity data, E remains approximately a constant value for ribbons thicker than ~80 nm but escalates rapidly as the ribbon thickness reduces below 50 nm as shown in Fig. 2e. The correspondence between κ and E in terms of both thickness dependence and transition thickness strongly suggests that the unexpected thickness dependence of κ is induced by elastic stiffening with enhanced E for thinner ribbons.
Elastic stiffening in thin nanowires has been observed for a wide variety of different wires. In addition to NbSe3 and Ag nanowires mentioned previously, it has been shown that Au, CuO, Pb and ZnO nanowires also demonstrate elastic stiffening31,32,33,34. The reason for the increased E is usually attributed to surface effects such as surface tension or enhanced surface elastic stiffness35. We note that for all 3D materials, the observed enhancement in E is smaller than two-fold, while for TiS3 nanoribbons, we observed a more than six-fold increase, similar to the case of NbSe3 nanowires, which are also composed of quasi-1D vdW crystal. Therefore, it is likely that the enhancement of E in quasi-1D vdW crystal nanowires could be due to a different mechanism.
Lattice contraction due to atomic substitution
From a microscopic point of view, Young’s modulus can be regarded as the ratio of interatomic spring constant to equilibrium lattice constant. Thus, we measured the thickness dependence of the lattice constant along the a- and b-axis directions from HRTEM images (Fig. 3a–c). The measured data are listed in Table 2, which suggests a significant reduction of lattice constant, i.e., lattice contraction, for thinner ribbons. To quantitatively measure the level of lattice contraction, we define a parameter of lattice contraction rate as (0.169 – a * b) / 0.169, where 0.169 is the product of equilibrium lattice constants a and b for bulk TiS327. Figure 3d plots the thickness-dependent lattice contraction rate, which indicates that significant lattice contraction occurs for ribbons with thickness below 50 nm. The transition thickness agrees with the trend observed for κ and E. We note that the lattice contraction rate can reach up to ~9% for a 19-nm-thick nanoribbon. Since lattice contraction shortens the interatomic interaction distance and significantly strengthens the interactions, Young’s modulus of thin TiS3 nanoribbon has a remarkable enhancement.
To evaluate the effects of lattice contraction, we calculated E by first-principles calculations based on the experimental lattice contraction rates (see Methods). Encouragingly, the calculated values (triangle points) in Fig. 4a agree with the measurement data (rectangle points) in terms of both the trend and level of enhancement. In addition, we also used simple two-body potentials to examine the lattice contraction effects on Young’s modulus (More details in Supplementary Note 9). Results (Supplementary Figs. 6 and 7) show that a 9% lattice contraction rate can induce a drastic enhancement of interatomic interaction strength and Young’s modulus, which corroborates the first-principles calculations and experimental measurements (Fig. 4a). Thus, we conclude that the unexpected thickness dependence of κ is caused by the enhancement in E, which is induced by the lattice contraction. In fact, κ and E show impressive agreement as the lattice contraction rate escalates as shown in Fig. 4a. Naturally, the key question is what leads to the lattice contraction.
Based on Vegard’s law36,37, lattice contraction typically happens when host atoms are substituted by dopant atoms with smaller radii. Considering that materials can be oxidized easily during growth or in the ambient environment, it is likely that O atoms may substitute S atoms in thin TiS3 nanoribbons, which are responsible for the observed lattice contraction. To verify this hypothesis, we measured the O atom concentration in TiS3 nanoribbon samples by energy dispersive spectroscopy (EDS). As shown in Fig. 4b, the O atom concentration increases significantly as the ribbon thickness reduces. We note that although the measured O concentration with EDS may associate with large uncertainties38, the systematic trend and the dramatic percentage increase as the ribbon thickness reduces provide convincing evidence that the O atom concentration increases in thinner ribbons. Moreover, as displayed in the inset of Fig. 4b, the increased peak intensities corresponding to the O atoms in the EDS spectrum also certify the increased O concentration with decreasing thickness. The consistent trends between the thickness-dependent lattice contraction rate and oxygen concentration suggest that the amount of O atoms in the ribbon could play a key role in the observed lattice contraction.
Although the existence of O atoms has been verified in the TiS3 ribbon, it is not clear whether the O atoms are only adsorbed on the surface or they diffuse inside and substitute S atoms in the ribbon. In order to clarify this, we performed first-principles calculations to explore the relation between the lattice contraction rate and oxygen concentration. For the calculation, a portion of S atoms in the unit cell were directly substituted by O atoms and the symmetry constraint was switched off during the structural relaxation process. The calculated lattice contraction rate matches well with the experimental data (Fig. 4c) for different O concentrations. For comparison, E of a lattice with O atoms adsorbed on the surface was calculated and the value is even smaller than that of bulk TiS3 (Supplementary Fig. 8). These results indicate that O atoms substitute S atoms in our samples.
Since defects can also cause lattice contraction in TiS3 samples, we calculated the total energy and lattice contraction rate for TiS3 with S vacancies. The results indeed show a clear lattice contraction with S vacancies; however, the total energy in TiS3 with S vacancies is 7–17% higher than that of pristine TiS3, while the corresponding value in the O substituted TiS3 is 8.4% lower (Supplementary Table 2), indicating that the substitution of S atoms by O atoms is energetically favorable. To further rule out the possibility that our observation is induced by S vacancies, we calculated the phonon dispersion relations of pristine TiS3, TiS3 with S vacancies and TiS3 with O substitution as shown in Supplementary Fig. 10. From these phonon dispersion relations, pristine TiS3 and O substituted TiS3 are stable while TiS3 with one S atom vacancy is not stable because imaginary frequency phonons appear as shown in Supplementary Fig. 10a, b. Although the structure with two S vacancies (Supplementary Fig. 10c) is stable, the calculated thermal conductivity is actually lower than that of pristine TiS3 along the b-axis direction (Supplementary Fig. 11), as a result of phonon-defect scattering. Moreover, the lattice with two S vacancies is quite different from that of TiS3 and this structure is not consistent with our TEM study. Overall, while S vacancies can also cause lattice contraction, it will decrease the thermal conductivity and/or render the structure unstable. Therefore, we believe that the lattice contraction observed in our study is induced by the substitution of S atoms with O atoms. We note that a similar phenomenon was observed by Ning et al.39, in which the volume of unit cell is reduced by 3.4% because of the intercalation of protons into WO3 film.
To further verify the O atoms substitution, we measured the X-ray photoelectron spectroscopy (XPS) of a powder of TiS3 nanoribbons. The atomic fraction of oxygen in the samples derived from the XPS spectrum is around 14%. While the XPS measurements cannot be performed on individual nanoribbons, the study further confirms that the ribbon contains O atoms. Figure 4d shows that the O 1s spectrum is composed of two peaks. The lower binding-energy peak at 531.11 eV is assigned to \({{{\mbox{O}}}}^{x-}\) (\(0\, < \,x\, < \,2\)) and the higher binding-energy peak at 533.25 eV is characterized as \({{{\mbox{O}}}}_{2}^{\delta -}\) (\(\delta \, < \,2\))40,41. These less-negatively charged O species should be associated with a certain chemical bond formation40. The chemical state of Ti4+ ions is further analyzed to confirm that the oxygen atoms substitute into the TiS6 trigonal prisms. Figure 4e exhibits that the Ti 2p peak has been broken down into two components: the lower binding-energy peak (456.28 and 461.75 eV), which may be attributed to titanium atoms with a TiS6 trigonal environment in TiS342, and the higher binding-energy peak (457.27 and 463.31 eV), which has been found in titanium oxysulfide species and may be assigned to the Ti-O bond because the binding energy of the Ti-O bond is higher than that of Ti-S bond43. The S 2p peak containing three components is also investigated as shown in Fig. 4f. The lowest binding energy (161.36 and 162.46 eV) likely belongs to S2– sulfide ions in TiS3 and the moderate binding energy (162.17 and 163.26 eV) could be attributed to \({{{\mbox{S}}}}_{2}^{2-}\) disulfide. In pristine TiS344, the fitted disulfide/sulfide peak intensity ratio of S 2p spectrum is around 2, while our fitting results deviate from this value, indicating that other forms of S atoms exist. The highest binding energy (162.98 and 164.08 eV) is assigned to \(({{{\mbox{SO}}}})^{2-}\) ions in trigonal prisms due to its shorter S-O bond. The detailed bond information is depicted in Supplementary Fig. 12. From the XPS analysis, a portion of S atoms are substituted by O atoms in thin TiS3 nanoribbons.
Comparison of doping effects in 3D and quasi-1D materials
Based on the above-detailed material characterizations and first-principles calculations, we can conclude that once the TiS3 nanoribbon thickness decreases below 50 nm, more S atoms are substituted by O atoms, which leads to lattice contraction and enhanced thermal conductivity. As we know, doping is a widely adopted and effective strategy to reduce thermal conductivity in 3D materials, and the mechanism of the reduced thermal conductivity is attributed to the enhanced phonon-impurity scattering strength. It is curious that doping leads to an increase in the thermal conductivity in the quasi-1D vdW materials here. In order to reveal the underlying mechanism, the thermal conductivity of a bulk Si doped with C (inset of Fig. 5d) was calculated. At a doping level of 25% (Si0.75C0.25), the lattice contraction appears due to the smaller radii of C atoms. However, the thermal conductivity decreases to 34% of the pure Si. Thus, it is unlikely that the increase of thermal conductivity in TiS3 is only because of doping-induced lattice contraction, which should also originate from the quasi-1D vdW structure. The most distinct feature of quasi-1D vdW structure is the weak vdW interactions along the interchain directions and the presence of the vdW gaps. Then, we calculated the coupling strength along both the interchain and intrachain directions at different O doping levels (Fig. 5a). The coupling strength along the interchain directions fluctuates slightly, while the coupling strength along the intrachain direction demonstrates a significant increase with the O doping levels (Fig. 5b). Correspondingly, it is interesting to compare the strain fields induced by doped atoms in bulk silicon and TiS3 nanoribbons. In bulk silicon, the doped C atom introduces lattice contraction along three-dimensional directions due to the strong covalent bonds of C-Si. As a result, the elastic strain induced by the doped C atoms in bulk Si is along all three-dimensional directions, and the strong potential energy and structural distortions are introduced, which significantly enhance phonon scattering and reduce phonon lifetime as demonstrated in Fig. 5d. In contrast, when O atoms substitute S atoms in TiS3 nanoribbons, the vdW gaps provide the freedom and space for structural evolution. As a result, the doped atoms induce the lattice contraction and enhance the coupling strength only along the molecular chain direction (Fig. 5b), which leads to a significant increase in Young’s modulus, phonon group velocity and phonon lifetime (Fig. 5c). Notably, the increased phonon lifetime is caused by the enlarged phonon bandgap due to lattice contraction (Supplementary Fig. 13). Overall, the difference of doping effects in quasi-1D and 3D materials causes the increase of thermal conductivity in O-doped TiS3 and the decrease of thermal conductivity in C-doped Si.
Besides phonon group velocity and phonon lifetime, heat capacity is another factor to affect thermal conductivity. The lattice contraction increases the atom number density that will cause an increase in the heat capacity at room temperature. To prove it, we calculated the heat capacity through the first-principles method. Supplementary Fig. 14 verifies that heat capacity is enhanced at room temperature for the O-doped TiS3 nanoribbon. Overall, Fig. 2e demonstrates that E increases 6.1 times from 28 to 170 GPa, which corresponds to a 5.9-fold increase in the square of the speed of sound (\({v}^{2}\propto E/\rho\)). It is noticed that the mass density ρ increases from 3225.2 to 3317.2 kg/m3 as the thickness of TiS3 nanoribbons reduces from ~80 to ~19 nm as a result of lattice contraction. Meanwhile, the thermal conductivity κ increases by 7.4 times from ~2.1 to ~15.5 W/m-K at room temperature (Fig. 2b). This suggests that the enhancement of the speed of sound plays a key role in the increase of thermal conductivity. The specific heat and phonon lifetime have relatively weak contributions to this unexpected increase.
Discussion
Considering that TiO2 has a higher thermal conductivity than TiS3, one might expect that the formation of a core-shell (TiS3-TiO2/TiOxS3-x) structure can explain the observed enhancement of thermal conductivity. However, detailed calculations exclude the possibility of the core-shell structure, which is clearly described in Supplementary Note 11. In fact, the diffraction pattern of HRTEM displays only one type of lattice structure. If a core-shell structure was formed, two types of lattice structures would be easily discerned because the weak interchain vdW interactions should allow for the TiS3 and TiO2/TiOxS3-x layers retaining their respective lattice structures.
We also note that the O-doping-induced lattice contraction is mainly thickness dependence, but not width and length dependence. This is because the coupling strength along the a-axis direction is 2.5 times higher than that along the c-axis direction as shown in Fig. 5b28. Thus, the sample width is always significantly larger than the thickness. Actually, the minimum width for all measured samples in the current work is >50 nm. As demonstrated in Fig. 4b, the thinner ribbons have a higher doping level because it is easier for O atoms to diffuse and replace S atoms. The O doping level starts to increase quickly as the ribbon thickness is below 50 nm. In contrast, the doping levels (and hence lattice contraction as shown in Supplementary Fig. 15a and Young’s modulus) for all of the measured samples are not sensitive to the width variations because the minimum width is larger than 50 nm. So, the measured thermal conductivity demonstrates strong thickness dependence but relatively weak width dependence. The relatively weak width-dependent thermal conductivity is attributed to the reduced phonon boundary scattering.
Atomic substitution causes mass mismatch and local strain, which inevitably enhances phonon-impurity scattering that tends to decrease thermal conductivity. However, our analysis suggests a longer phonon lifetime when O atoms replace S atoms in TiS3 nanoribbon, which indicates that the reduction in the Umklapp scattering rate is more significant than the enhancement in phonon-impurity scattering rate. In order to further understand the effects of phonon-impurity scattering from O substitution, we applied the Callaway model to fit the temperature-dependent thermal conductivity and extracted the phonon-impurity scattering cross-section Ω and strength A (where phonon-impurity scattering is expressed as \(\tau^{-1}_{d}=A \omega^{4}=\frac{d^{3}\varOmega}{4 \pi \nu^{3}_{g}} \omega^{4}\) based on Abeles’ theory45, and the detailed method was described in Supplementary Note. 7). Notably, the bulk phonon spectrum is employed in the model to fit the thermal conductivity since the thinnest sample (~19 nm) in the current study is larger than 20 atomic layers thick (17.6 nm)28. The fitted profiles are shown in Fig. 6a. The extracted scattering cross-section Ω increases monotonically with the decrease of nanoribbon thickness as listed in Table 3, which is reasonable because Ω describes the effects of mass disorder and local strain on phonon transport39. Interestingly, although the scattering cross-section increases significantly, the scattering strength A in Table 3 has a weak dependence on thickness and even decreases as the thickness becomes smaller than 52 nm. The reason behind the decrease of A is the significant increase in phonon group velocity vg (Supplementary Eq. 16) due to the lattice contraction. A similar decreasing trend of A due to the increase of vg is observed in epitaxial WO3 thin films39. Another possible reason could be that the dopant O atoms are located in the same group of the periodic table as S atoms. Thus, the two elements have the same number of electrons in the outermost electron shell, and subsequently, the phonon-impurity scattering due to O doping is suppressed. In order to verify our hypothesis, F atoms were chosen to substitute S atoms and the first-principles calculations observed much stronger phonon-phonon scattering than pristine TiS3 and the O atom-doped TiS3 (Supplementary Fig. 16). By employing Callaway model to fit the temperature-dependent thermal conductivity of F-doped TiS3 from first-principles calculations (Supplementary Fig. 17), we find that both Ω and A of F-doped TiS3 are much higher than that of pristine TiS3. Thus, two rules should be satisfied in order to increase thermal conductivity by means of doping: (1) dopant atoms should have a smaller radius compared with host atoms; (2) dopant atoms should locate in the same group of the periodic table as host atoms.
Finally, we want to briefly discuss how to intentionally control the oxygen doping level in TiS3 since the doping level in the current study is controlled by nanoribbon thickness, which is not intentional. As discussed above, the atomic modeling indicates that the O atom-doped TiS3 has a lower energy compared to pristine TiS3, indicating that the substitution of S by O atoms is energetically favorable. In order to verify the modeling result, the evolution of O atom concentration with the elapse of time was experimentally measured and the details are shown in Supplementary Fig. 19, which demonstrates that O atoms could adsorb and then replace S atoms in TiS3 samples though the substitution rate is rather slow in ambient conditions as shown in Fig. 6b. Thus, the substitution of S by O atoms is spontaneous in TiS3, which is similar to that the O atoms can replace S atoms in monolayer MoS2 under ambient conditions46. If the sample is put into an oxygen-rich environment, the substitution rate should be high, which may provide an intentional method to control the oxygen doping level.
In this work, we explore thermal transport in quasi-1D vdW crystal TiS3 nanoribbons. The measured thermal conductivity displays an unexpected increase as the ribbon thickness reduces, which is opposite to the expectation based on the classical size effect on phonon transport. Measurements of the corresponding mechanical properties indicate that this thermal behavior is due to elastic stiffening with a drastic increase of the ribbon Young’s modulus of up to six times the bulk value. Detailed structural characterizations and composition analyses show that the unexpected thermal and mechanical properties are induced by lattice contraction as a result of the substitution of a portion of sulfur atoms with oxygen atoms. Due to the presence of the vdW gaps in TiS3, the lattice contraction enhances the bond strength significantly along the molecular chain direction while weakly affects vdW strengths, leading to the enhancement of thermal conductivity. These findings provide new insights into the structural properties of quasi-1D vdW nanostructures and potential approaches of modulating their mechanical and thermal properties.
Methods
TiS3 nanoribbon fabrication
TiS3 nanoribbons were grown in a furnace with titanium and sulfur powders loaded according to the stoichiometric ratio. The reactants were placed in a quartz ampule, evacuated to <1 Pa and flame-sealed. The ampule was then heated to 500 °C within two hours and held at this temperature for 2.5 days in a box furnace for a complete reaction via a chemical vapor transport process. As a result, TiS3 nanoribbons were grown and distributed around the inner wall of the quartz ampule, as reported in the literature47.
Structural characterizations
TEM and high-resolution TEM studies were carried out to measure the lattice constant of TiS3 nanoribbon via using Titan 80-300, FEI microscope. The thickness of samples was measured by AFM (Cypher S, Asylum Research, Oxford Instruments). The width and length of specimens were obtained from scanning electron microscopy (Helios NanoLab 600i, FEI, USA) images. The XPS measurement was performed by Al Kα source that provides monochromatic x-rays at 1486.6 eV. Narrow-scan spectra of concerned regions were recorded to analyze the chemical binding states of corresponding elements. The obtained binding energies were calibrated with the contaminant C1s peak at 284.6 eV. The narrow-scan spectra were fitted through a Gaussian–Lorentzian product function.
Thermal conductivity, electrical conductivity and Young’s modulus measurements
The thermal resistance and electrical conductance of samples were measured using the suspended micro-devices technique following previous reports48,49,50. The suspended micro-thermometry devices as illustrated in Fig. 1c include two adjacent silicon nitride (SiNx) membranes suspended with six SiNx beams severing as heating source and heating sink, respectively. The samples were measured in a cryostat under a high vacuum in order to eliminate the heat transfer through the air. The traditional 4-point I-V measurement approach was implemented to investigate the electrical transport in TiS3 NRs30,51.
To measure Young’s modulus, individual TiS3 NRs were transferred to a 6-μm-wide Si trench using micromanipulator. The Pt powder was deposited at the two ends of the nanoribbon to clamp the ribbon to the substrate. Then we carried out the three-point bending test with AFM. Before bending test, the spring constant of cantilever was extracted via thermal tune process. Figure 2d shows a schematic description of the bending experiment. First, we carefully imaged the devices using the AFM to locate the middle point across the trench and then pushed the middle point of the nanoribbon using the AFM cantilever to implement bending test. The bending tests were repeated three times to guarantee the rigidity of the constraints and the elastic property of the nanoribbons within the measured range.
First-principles calculations of Young’s modulus
To calculate Young’s modulus, a large energy cutoff of 600 eV was chosen with the Perdew–Burke–Ernzerhof of generalized gradient approximation as the exchange-correlation functional52. The Г-centered k-mesh was set as 15 × 25 × 9 to simulate the Brillouin zone in the total energy calculation and structural optimization. To introduce the vdW interactions into the TiS3 nanostructure, we imposed the density functional dispersion correction method of Grimme (DFT-D3)53 in all calculations. The tolerances for geometry optimization were set as the difference in atomic force being within 10–3 eV/Å. In calculating Young’s modulus for O-doped TiS3, lattice constants were adjusted according to experimental lattice contraction rates. The steps to calculate Young’s modulus are (1) the elastic tensor is determined by performing six finite distortions of the lattice; (2) the elastic constants are obtained based on the previous elastic tensor and the strain–stress relationship54; and (3) Young’s modulus of TiS3 were derived from elastic constants metrics through a series of formulas given in ref. 55.
Theoretical calculations of specific heat and phonon lifetime of O-doped TiS3
To investigate the doping effects of O atoms on phonon thermal transport quantitatively, thermal conductivity of TiS3 with different O concentrations was calculated with the first-principles method. In the calculation, energy cutoff of 520 eV was chosen and DFT-D3 method was employed to consider the vdW interactions. The Г-centered k-mesh was set as 15 × 25 × 9 for bulk TiS3 with different O atom concentrations to simulate the Brillouin zone in the total energy calculation and structural optimization. The lattice constants and internal atomic coordinates were optimized until the atomic forces became less than 10–3 eV/Å. To calculate the harmonic interatomic force constants, we chose the 3 × 4 × 2 supercell with Г-centered 3 × 3 × 2 k-mesh. To obtain the anharmonic interatomic force constants, a 3 × 4 × 2 supercell with Г-centered 2 × 2 × 2 k-mesh was chosen and the cutoff distance was set as 0.41 nm. The specific heat and phonon lifetime were calculated in the ShengBTE code56 by iteratively solving the linearized BTE.
Data availability
The data generated in this study have been deposited in Figshare under accession code https://doi.org/10.6084/m9.figshare.24039186.
Code availability
The code that has been used for this work is available from the corresponding author on request.
References
Piatti, E. et al. Charge transport mechanisms in inkjet-printed thin-film transistors based on two-dimensional materials. Nat. Electron. 4, 893–905 (2021).
Thomas, S. An industry view on two-dimensional materials in electronics. Nat. Electron. 4, 856–857 (2021).
Hwangbo, S., Hu, L., Hoang, A. T., Choi, J. Y. & Ahn, J. H. Wafer-scale monolithic integration of full-colour micro-LED display using MoS2 transistor. Nat. Nanotechnol. 17, 500–506 (2022).
Shreiner, R., Hao, K., Butcher, A. & High, A. A. Electrically controllable chirality in a nanophotonic interface with a two-dimensional semiconductor. Nat. Photonics 16, 330–336 (2022).
Dushaq, G., Paredes, B., Villegas, J. E., Tamalampudi, S. R. & Rasras, M. On-chip integration of 2D Van der Waals germanium phosphide (GeP) for active silicon photonics devices. Opt. Express 30, 15986–15997 (2022).
Rohaizad, N., Mayorga-Martinez, C. C., Fojtu, M., Latiff, N. M. & Pumera, M. Two-dimensional materials in biomedical, biosensing and sensing applications. Chem. Soc. Rev. 50, 619–657 (2021).
Balandin, A. A. Thermal properties of graphene and nanostructured carbon materials. Nat. Mater. 10, 569–581 (2011).
Ghosh, S. et al. Dimensional crossover of thermal transport in few-layer graphene. Nat. Mater. 9, 555–558 (2010).
Yun, Q. B. et al. Layered transition metal dichalcogenide-based nanomaterials for electrochemical energy storage. Adv. Mater. 32, 1903826 (2020).
Liao, L. P., Jiang, D. G., Zheng, K., Zhang, M. Z. & Liu, J. Q. Industry-scale and environmentally stable Ti3C2Tx MXene based film for flexible energy storage devices. Adv. Funct. Mater. 31, 2103960 (2021).
Wang, J., Malgras, V., Sugahara, Y. & Yamauchi, Y. Electrochemical energy storage performance of 2D nanoarchitectured hybrid materials. Nat. Commun. 12, 3563 (2021).
Balandin, A. A., Kargar, F., Salguero, T. T. & Lake, R. K. One-dimensional van der Waals quantum materials. Mater. Today 55, 74–91 (2022).
Wang, T., Zhu, Y., Mao, Z. & Xu, Y.-Q. Tunneling effects in crossed Ta2Pt3Se8-Ta2Pd3Se8 nanowire junctions: implications for anisotropic photodetectors. ACS Appl. Nano Mater. 4, 1817–1824 (2021).
Cheon, G. et al. Data mining for new two-and one-dimensional weakly bonded solids and lattice-commensurate heterostructures. Nano Lett. 17, 1915–1923 (2017).
Wu, K. et al. Phase transition across anisotropic NbS3 and direct gap semiconductor TiS3 at nominal titanium alloying limit. Adv. Mater. 32, 2000018 (2020).
Wu, K. et al. Unusual lattice vibration characteristics in whiskers of the pseudo-one-dimensional titanium trisulfide TiS3. Nat. Commun. 7, 12952 (2016).
Lipatov, A. et al. Quasi-1D TiS3 nanoribbons: mechanical exfoliation and thickness-dependent Raman spectroscopy. ACS Nano 12, 12713–12720 (2018).
Island, J. O. et al. Electronics and optoelectronics of quasi-1D layered transition metal trichalcogenides. 2d Mater. 4, 022003 (2017).
Zhang, J. et al. Titanium trisulfide monolayer as a potential thermoelectric material: a first-principles-based Boltzmann transport study. Acs Appl. Mater. Inter. 9, 2509–2515 (2017).
Molina-Mendoza, A. J. et al. High current density electrical breakdown of TiS3 nanoribbon‐based field‐effect transistors. Adv. Funct. Mater. 27, 1605647 (2017).
Island, J. O. et al. Ultrahigh photoresponse of few-layer TiS3 nanoribbon transistors. Adv. Opt. Mater. 2, 641–645 (2014).
Molina-Mendoza, A. J. et al. Electronic bandgap and exciton binding energy of layered semiconductor TiS3. Adv. Electron. Mater. 1, 1500126 (2015).
Tripathi, N. et al. Review of titanium trisulfide (TiS3): a novel material for next generation electronic and optical devices. Mat. Sci. Semicon. Proc. 127, 105699 (2021).
Black, J. R. Electromigration—a brief survey and some recent results. IEEE T. Electron Dev. 16, 338–347 (1969).
Liu, H. et al. Extreme in-plane thermal conductivity anisotropy in titanium trisulfide caused by heat-carrying optical phonons. Nano Lett. 20, 5221–5227 (2020).
Misse, P. R., Berthebaud, D., Lebedev, O. I., Maignan, A. & Guilmeau, E. Synthesis and thermoelectric properties in the 2D Ti1-xNbxS3 trichalcogenides. Materials 8, 2514–2522 (2015).
Guilmeau, E. et al. ZrSe3-type variant of TiS3: structure and thermoelectric properties. Chem. Mater. 26, 5585–5591 (2014).
Liu, C., Lu, P., Li, D., Zhao, Y. & Hao, M. Non-monotonic thickness dependent and anisotropic in-plane thermal transport in layered titanium trisulphide. Mater. Today Nano 17, 100165 (2022).
Yang, L. et al. Observation of superdiffusive phonon transport in aligned atomic chains. Nat. Nanotechnol. 16, 764–768 (2021).
Zhao, Y., Fitzgerald, M. L., Tao, Y., Pan, Z. & Li, D. Electrical and thermal transport through silver nanowires and their contacts – effects of elastic stiffening. Nano Lett. 20, 7389–7396 (2020).
Cuenot, S., Frétigny, C., Demoustier, C. S. & Nysten, B. Surface tension effect on the mechanical properties of nanomaterials measured by atomic force microscopy. Phys. Rev. B 69, 165410 (2004).
Sondors, R. et al. Size distribution, mechanical and electrical properties of CuO nanowires grown by modified thermal oxidation methods. Nanomaterials (Basel) 10, 1051 (2020).
Chen, C. Q., Shi, Y., Zhang, Y. S., Zhu, J. & Yan, Y. J. Size dependence of Young’s modulus in ZnO nanowires. Phys. Rev. Lett. 96, 075505 (2006).
Diao, J., Gall, K. & Dunn, M. L. Atomistic simulation of the structure and elastic properties of gold nanowires. J. Mech. Phys. Solids 52, 1935–1962 (2004).
Zhang, J. Y., Wang, X. Y., Xiao, M., Qu, L. & Peng, X. Lattice contraction in free-standing CdSe nanocrystals. Appl. Phys. Lett. 81, 2076–2078 (2002).
Vegard, L. Z. Die Konstitution Der Mischkristalle Und Die Raumfellung Der Atome. Z. f.ür. Phys. A Hadrons Nucl. 5, 17–26 (1921).
Denton, A. R. & Ashcroft, N. W. Vegard’s law. Phys. Rev. A 43, 3161–3164 (1991).
Dobranszky, J., Szabo, P. J., Berecz, T., Hrotko, V. & Portko, M. Energy-dispersive spectroscopy and electron backscatter diffraction analysis of isothermally aged SAF 2507 type superduplex stainless steel. Spectrochim. Acta B 59, 1781–1788 (2004).
Ning, S., Huberman, S. C., Ding, Z., Nahm, H. & Ross, C. A. Anomalous defect dependence of thermal conductivity in epitaxial WO3 thin films. Adv. Mater. 31, 1903738 (2019).
Ayyoob, M. & Hegde, S. An XPS study of the adsorption of oxygen on silver and platinum surfaces covered with potassium or cerium. Surf. Sci. 133, 516–532 (1983).
Xu, C., Xia, Y., Liu, Z. & Meng, X. Chemical states change at (Ba,Sr)TiO3/Pt interfaces investigated by x-ray photoelectron spectroscopy. J. Phys. D. Appl. Phys. 42, 085302 (2009).
Sun, M. X. et al. Anomalous heavy doping in chemical-vapor-deposited titanium trisulfide nanostructures. Phys. Rev. Mater. 5, 094002 (2021).
Gonbeau, D. et al. XPS study of thin films of titanium oxysulfides. Surf. Sci. 254, 81–89 (1991).
Fleet, M. E., Harmer, S. L., Liu, X. & Nesbitt, H. W. Polarized X-ray absorption spectroscopy and XPS of TiS3: S K- and Ti L-edge XANES and S and Ti 2p XPS. Surf. Sci. 584, 133–145 (2005).
Abeles, B. Lattice thermal conductivity of disordered semiconductor alloys at high temperatures. Phys. Rev. 131, 1906–1911 (1963).
Pető, J. et al. Spontaneous doping of the basal plane of MoS2 single layers through oxygen substitution under ambient conditions. Nat. Chem. 10, 1246–1251 (2018).
Island, J. O. et al. TiS3 transistors with tailored morphology and electrical properties. Adv. Mater. 27, 2595–2601 (2015).
Kim, P., Shi, L., Majumdar, A. & McEuen, P. L. Thermal transport measurements of individual multiwalled nanotubes. Phys. Rev. Lett. 87, 215502 (2001).
Li, D. et al. Thermal conductivity of individual silicon nanowires. Appl. Phys. Lett. 83, 2934–2936 (2003).
Lin et al. Distinct signatures of electron-phonon coupling observed in the lattice thermal conductivity of NbSe3 nanowires. Nano Lett. 19, 415–421 (2018).
Wang, Y., Liu, S., Wu, Z., Liu, G. & Zhu, J. Enhanced thermoelectric performance of van der Waals tellurium via vacancy engineering. Mater. Today Phys. 18, 100379 (2021).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Dingreville, R., Qu, J. & Cherkaoui, M. Surface free energy and its effect on the elastic behavior of nano-sized particles, wires and films. J. Mech. Phys. Solids 53, 1827–1854 (2005).
Wu, Z. J. et al. Crystal structures and elastic properties of superhard IrN2 and IrN3 from first principles. Phys. Rev. B 76, 054115 (2007).
Li, W., Carrete, J., A. Katcho, N. & Mingo, N. ShengBTE: a solver of the Boltzmann transport equation for phonons. Comput. Phys. Commun. 185, 1747–1758 (2014).
Acknowledgements
The authors thank the financial support from the National Natural Science Foundation of China (No. 52127811, 52035003, 52206092) and the Department of Science and Technology of Jiangsu Province (BK20220032). C.L. was funded by the Natural Science Foundation of Jiangsu Province (Grant no. BK20210565), Basic Science (Natural Science) Research Project of Higher Education Institutions of Jiangsu Province (21KJB470009), “Shuangchuang” Doctor program of Jiangsu Province (JSSCBS20210315), and the open research fund of Jiangsu Key Laboratory for Design and Manufacture of Micro-Nano Biomedical Instruments, Southeast University (No. KF202010). The numerical calculation in this research work is supported by the Big Data Computing Center of Southeast University and the Scientific Computing Center of Nanjing Normal University.
Author information
Authors and Affiliations
Contributions
C.L. performed theoretical calculations and wrote the manuscript with the assistance of C.W. X.Y.T. fabricated samples. C.W. performed thermal measurements and sample characterizations. C.L., D.L., and Y.C. analyzed the results. C.W., Y.T., and Y.Z. discussed the results. Y.C., Q.Y., and J.Y. conceived and directed the project.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewer(s) for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, C., Wu, C., Tan, X.Y. et al. Unexpected doping effects on phonon transport in quasi-one-dimensional van der Waals crystal TiS3 nanoribbons. Nat Commun 14, 5597 (2023). https://doi.org/10.1038/s41467-023-41425-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-41425-0
This article is cited by
-
Defect scattering can lead to enhanced phonon transport at nanoscale
Nature Communications (2024)