Liquid-in-liquid printing of 3D and mechanically tunable conductive hydrogels

Xie, Xinjian; Xu, Zhonggang; Yu, Xin; Jiang, Hong; Li, Hongjiao; Feng, Wenqian

doi:10.1038/s41467-023-40004-7

Download PDF

Article
Open access
Published: 18 July 2023

Liquid-in-liquid printing of 3D and mechanically tunable conductive hydrogels

Nature Communications volume 14, Article number: 4289 (2023) Cite this article

13k Accesses
20 Citations
3 Altmetric
Metrics details

Subjects

Abstract

Conductive hydrogels require tunable mechanical properties, high conductivity and complicated 3D structures for advanced functionality in (bio)applications. Here, we report a straightforward strategy to construct 3D conductive hydrogels by programable printing of aqueous inks rich in poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) inside of oil. In this liquid-in-liquid printing method, assemblies of PEDOT:PSS colloidal particles originating from the aqueous phase and polydimethylsiloxane surfactants from the other form an elastic film at the liquid-liquid interface, allowing trapping of the hydrogel precursor inks in the designed 3D nonequilibrium shapes for subsequent gelation and/or chemical cross-linking. Conductivities up to 301 S m⁻¹ are achieved for a low PEDOT:PSS content of 9 mg mL⁻¹ in two interpenetrating hydrogel networks. The effortless printability enables us to tune the hydrogels’ components and mechanical properties, thus facilitating the use of these conductive hydrogels as electromicrofluidic devices and to customize near-field communication (NFC) implantable biochips in the future.

Shell buckling for programmable metafluids

Article 03 April 2024

Designer peptide–DNA cytoskeletons regulate the function of synthetic cells

Article Open access 23 April 2024

Self-assembly of peptide nanocapsules by a solvent concentration gradient

Article 26 April 2024

Introduction

Electronics, such as brain-computer interfaces, are one of the most important materials for connecting electronic functionality and biological systems^1,2,3,4. In particular, flexible bioelectronics have attracted extensive attention owing to their tremendous potential in disease treatment, such as Parkinson’s or amyotrophic lateral sclerosis^5,6,7,8. Relative to most conventional rigid electronics that are physically and mechanically dissimilar to biological tissues, conductive hydrogel electronics offer both favorable electrical properties and ideal interfaces with the tissues, eliminating immunological responses or the electrochemical instability arising from severe mechanical mismatch^9,10,11. To mimic the mechanical properties of a wide range of biological tissues from ultrasoft to stiff (with elastic modulus values ranging from 0.1–500 kPa)¹², conductive hydrogels are required to form mechanically compliant interfaces without compromising their electronic performance. Additionally, the prevailing fabrication of conducting hydrogels has mostly relied on conventional manufacturing techniques for 2D patterns^13,14,15. To broaden the applications of conductive hydrogels, a transformation of customized hydrogel (bio)electronics from traditional 2D thin films to shape-conformable, integrated 3D structures is in process^{16,17,18,19,20}.

Among the investigated conductive polymers used to make electrically conducting hydrogels, poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) has many advantages owing to its biocompatibility, water solubility, intrinsic electronic conductivity and commercial availability^21,22,23,24. With the aid of 3D printing technology that has emerged in recent years, PEDOT:PSS-based hydrogels with 3D microscale structures have been fabricated²⁵. Reported examples of 3D PEDOT:PSS hydrogels either rely on inkjet extrusion of conducting polymer inks layer by layer^16,26,27 or the employment of light-based 3D printing where lasers or light-emitting diodes (LEDs) initiate spatial photopolymerization in liquid^{28,29,30,31,32,33}. Unfortunately, the inject extrusion method has a specific rheological requirement for the employed polymer inks, which brings difficulties in ink preparation and thus makes it difficult to selectively tune the mechanical properties of the formed gel. In the light-based 3D printing process, the light-induced curing of a prepolymer or monomer mixture first forms an inert hydrogel matrix. Then, the conductive components are introduced in the hydrogel system by blending PEDOT:PSS with hydrogel-forming precursors before curing^30,31 or by in situ polymerization of EDOT within the resulting hydrogel matrix^32,33. Such disconnected aggregates of the conductive polymer network result in a high number of open circuits, making both strategies suffer from low conductivity (0.01–2.2 S m⁻¹), even with a relatively high PEDOT:PSS content³⁴. Additionally, constructing hydrogels with 3D overhanging structures does not accommodate soft objects in the absence of auxiliary support.

Liquid-in-liquid 3D printing is a promising approach that allows for the freeform fabrication of soft materials³⁵. In this technique, the ink phase is extruded into a bath phase while a translation stage moves according to a 3D design, shaping the soft material into complex structures. However, suppressing Rayleigh-Plateau instabilities and minimizing the deformation of the extruded ink in the bath phase remain significant challenges in this process. Unlike embedded extrusion 3D printing, which requires specific support bath phases with shear-thinning or solid-fluid transition capabilities^36,37, another liquid-in-liquid printing technology utilizes self-assembly³⁸, jamming³⁹, and coacervation⁴⁰ to stabilize the filament extruded from the jet nozzle. This approach partly eliminates the need for rheological properties in both ink and support bath phases. Despite these advantages, reports on the use of liquid-in-liquid 3D printing for PEDOT:PSS conductive hydrogels are rare. While some cases of fibrillary gelation of PEDOT:PSS by injection into coagulation baths^40,41,42 have been reported, the printing method still requires strict matching of ink concentration, support bath components, and extrusion rate due to the limited ability to overcome Rayleigh-Plateau instabilities. Although considerable efforts have been devoted to 3D printing conductive polymers, constructing 3D hydrogels with tunable mechanical properties, high conductivity, a broad selection of ink materials, and complicated structures remains challenging.

To address these limitations, we describe a liquid-in-liquid 3D printing process for the production of highly conductive PEDOT-based hydrogels with tunable stiffness and arbitrary structures (Fig. 1). Relying on the interfacial jamming of PEDOT:PSS–PDMS surfactants (PPSs) at the immiscible aqueous and oil-liquid interface, this process provides compelling routes to trap the aqueous inks into a nonequilibrium and 3D programmable shape and physically and/or chemically convert the liquid ink into the hydrogel state inside the defined profile. As such, the mechanical stability of the PEDOT:PSS–surfactant elastic film enables us to implement PEDOT:PSS physical gelation to form a loose gel interpenetrated by a secondary and robust polymer network. Conductivities up to 301 S m⁻¹ are achieved for a low PEDOT:PSS content of 9 mg mL⁻¹. Importantly, the printable PEDOT:PSS inks are highly versatile, covering a broad range of PEDOT:PSS concentrations (in this study, the investigated concentration is 0.1–20 mg mL⁻¹) and viscosity values (the corresponding viscosity of aqueous inks ranges from 6.5–23000 mPa·s, with inks of higher viscosity also being applicable). Therefore, the mechanical properties of the cured hydrogels can be orthogonally controlled by tuning the ink formulation and cross-linking conditions. Given the printed hydrogels’ compatibility with biological systems, such easy printability and designability would allow for the fabrication of stretchable hydrogels without compromising conductivity, multimaterials integrated with 3D hydrogels, electrochemical devices and, notably, conductive hydrogels for implantable chips.

**Fig. 1: Liquid-in-liquid 3D printing of hydrogels with tunable morphology, mechanical properties and conductivity.**

Results

PEDOT:PSS-PDMS surfactants interfacial assembly

The typical conformation of PEDOT:PSS in water is expected to be colloidal particles that consist of a hydrophilic PSS shell surrounding a hydrophobic PEDOT core region⁴³. Although PEDOT:PSS in the aqueous phase alone does not possess significant interfacial activity (Supplementary Fig. 1), the addition of a PDMS surfactant terminated with primary amines (PDMS-NH₂) to an immiscible oil solution leads to the self-assembly of PEDOT:PSS colloidal particles and PDMS-NH₂ surfactants at the water-oil interface, forming a jammed PEDOT:PSS-surfactants (PPSs) composite (Fig. 2a). The rapid interfacial assembly can be assumed to be a result of electrostatic interactions^44,45,46 between the exposed sulfonate groups (R-SO₃⁻) in the PSS-rich shell and protonated amino groups (PDMS-NH₃⁺) from the oil phase at the liquid-liquid interface. Since the two components can only exist in their respective phases, strong electrostatic adsorption causes the jammed assembly to become immobilized at the liquid-liquid interface, arresting further shape changes in the drop and kinetically trapping the drop into a shape even far removed from equilibrium.

**Fig. 2: PPSs interfacial assemblies for printing of a PEDOT:PSS aqueous dispersion in oil.**

To demonstrate that the expected PPSs assembly behavior occurs at the interface, we investigated the co-assembly kinetics of PEDOT:PSS dispersion and PDMS surfactant using pendant drop tensiometry. This technique provides the time evolution of the interfacial tension (IFT) by fitting the axisymmetric profile of the droplet to the Young-Laplace equation³⁵. The pH dependence of the sulfonate-ammonium ion-pairing was firstly investigated by monitoring the IFT of pendant droplets of a diluted commercial PEDOT:PSS dispersion (0.50 mg mL⁻¹) in a toluene phase consisting of bis(3-aminopropyl)-terminated PDMS-NH₂ (M_n 4000 g mol⁻¹, 10 vol%) while varying the pH of the aqueous phase. We found that the rate of interfacial self-assembly of PPSs increases with decreasing pH (Fig. 2b and Supplementary Fig. 2). At higher pH values (>11), PDMS-NH₂ loses its ability to assemble at the interface with PEDOT:PSS particles due to deprotonation. Within the range of pH values from 3.01 to 10.87, the IFT of PEDOT:PSS droplets decreased below 18 mN m⁻¹, and well-defined wrinkles were observed at the interfacial area when extracting the aqueous droplets, revealing the irreversible formation of elastic films at the liquid-liquid interface. With further decreasing the pH until the pKa of PSS (PSS is assumed to have an average pKa of approximately 1.5⁴⁷), PEDOT:PSS tends to exhibit a higher negative charge (Supplementary Fig. 3 and Supplementary Table 1). This results in stronger electrostatic interactions between the PEDOT:PSS particles and surfactants in such pH conditions. For pH values less than 3 or for higher PEDOT:PSS concentrations, the initial adsorption of PEDOT:PSS particles to the interface at pH 2.55 is therefore too rapid to form regular droplet shapes, preventing the measurement of IFT using the shape-fitting method. More specifically, adjusting the pH to 2.07 can lead to a continuous jet without breakup when the flow rate is set to 0.07 mL min⁻¹ (Supplementary Fig. 4). When the pH was further adjusted to 1.21, the PEDOT:PSS droplet became opaque, and parts of the assembly containing PEDOT:PSS were removed from the aqueous phase into the oil phase. This phenomenon may have been caused by the formation of micelles (water in oil (W/O)) at the liquid-liquid interface, which could be attributed to the very low interfacial tension and osmotic pressure at low pH levels^48,49. These results indicate that there is a broad pH range from 2.07 to 10.87 that is compatible with this PEDOT:PSS-surfactant self-assembly system.

The concentrations of PEDOT:PSS in the aqueous phase influence the rate of diffusion to the interface and the areal density of polymers at the interface, which ultimately dictate the IFT and the mechanical strength of the assembled film at the steady state. As shown in Fig. 2c, increasing PEDOT:PSS concentration from 0.17 mg mL⁻¹ to 0.5 mg mL⁻¹ decreased the equilibrium time of IFT from 800 s to 40 s. When increasing the PEDOT:PSS concentration to more than 1 mg mL⁻¹, the system reached its steady state on a time scale of milliseconds, as evidenced by the behavior of instantaneous particle-surfactant self-assembly and maintenance of the droplet’s original shape for at least 12 h (Supplementary Fig. 5). The formation of the PPSs interfacial assembly was ultimately confirmed through the fabrication of a planar layer of PPSs using a mold, as shown in Supplementary Fig. 6. SEM images revealed the densely packed PEDOT:PSS nanoparticles at the assembly layer, thus confirming our proposed interface assembly hypothesis.

Since the jammed assembly has the ability to counteract the compressive force in the system arising from Rayleigh-Plateau instabilities in a timely manner³⁹, it is convenient to use PPSs films to stabilize the aqueous architectures that are generated in the oil phase via direct-write methods (namely, liquid-in-liquid 3D printing). By moving the print head of a commercial extrusion-based 3D printer equipped with a syringe pump, the aqueous PEDOT:PSS dispersion was injected into the surrounding oil phase containing PDMS-NH₂ surfactant along the programmed trajectories, drawing the liquid ink into linear or curved threads (in this study, the term ‘threads’ refers to liquid inks with a thread-like shape and lacking any crosslinked structure). The printing conditions under which stable structures can form in silicone oil (η_e ~ 30000 mPa·s) are summarized in the printability phase diagram (Fig. 2d). When the PEDOT:PSS and PDMS surfactants are beyond their critical concentrations, mechanically stable interfacial assemblies are obtained to prevent the threads from breaking up into droplets. Due to the quick assembly, the oil phase, even with a low viscosity (η_e ~ 10 mPa·s), is also capable of quickly causing the PPSs to form threads from the liquid (Fig. 2e and Supplementary Fig. 7). Thus, the oil phase has minimal requirements, with only water immiscibility and good solubility to PDMS surfactants being necessary. The viscosity and rheological properties of the oil phase have little impact on the PPSs interfacial assembly process. For long-term printing, the density of the oil phase can be adjusted to match that of the aqueous phase to prevent the printed aqueous structures from settling under gravity. Such interfacial assembly is surprisingly solid in that the printed aqueous threads manage to retain their structures for at least 12 h (Supplementary Fig. 5) and can even be pulled out of the oil without rupturing (Fig. 2f and Supplementary Fig. 8). All these features allow extensive manipulation of the aqueous threads within the physical framework and within the experimental timeframe.

Printing PEDOT-based hydrogels with a chemically crosslinked network

In a first demonstration of 3D printing a conductive hydrogel, we mixed the hydrogel precursor, poly(ethylene glycol) diacrylate (M_n 1000 g mol⁻¹, PEG 1000), and blue-light photoinitiator, lithium phenyl-2,4,6-trimethylbenzoylphosphinate, into the pristine PEDOT:PSS dispersion to prepare polymer ink 1 (Table 1). After drawing the liquid ink into threads in the surrounding oil phase, subsequent light irradiation (λ = 395 nm) initiated the radical polymerization of PEG diacrylate to generate the chemically crosslinked network of the PEDOT@PEG hydrogel (Fig. 3a, b). The scanning electron microscopy (SEM) image clearly shows that this PEDOT@PEG hydrogel has a 5 µm-thick, wrinkled skin surrounding a cured PEG core (Fig. 3c), demonstrating that the UV curing occurred throughout the whole thickness. The formation of the skin-core structure can be attributed to the differences in PEDOT:PSS particle density and PEG monomer concentration, which result from the PPSs interfacial assembly (Supplementary Fig. 9). This provides additional evidence for the liquid-liquid interfacial assembly that contributes to the hydrogel formation in desired shapes.

Table 1 Different formulations and processing of PEDOT hydrogels and their corresponding electronic and mechanical properties

Full size table

**Fig. 3: Printed PEDOT hydrogels with a chemically crosslinked network.**

As the UV-induced chemical crosslinking of PEG-diacrylate plays an essential role in the mechanical reinforcement of ink 1 (Fig. 3d), the mechanical strength of the printed hydrogels can be easily tuned by varying the UV curing time, monomer concentration (Supplementary Fig. 10) and the selection of hydrogel-forming precursors. To test the compatibility of this system, five cylindrical PEDOT:PSS hydrogels (diameter: 1.5 mm) were fabricated by printing the inks 1–5 listed in Table 1. In all cases, the interfacial assemblies reached their steady state rapidly for subsequent UV curing. The hydrogels printed with different ink formulations and curing conditions exhibit distinct transitions in mechanical characteristics, transitioning from stiff (Young’s modulus: 3875 kPa) to soft (Young’s modulus: 41.2 kPa) (Fig. 3e). As such, the range of hydrogels that can be generated by this printing technique is rather broad as long as the hydrogel-forming precursors can coexist with PEDOT:PSS microgel particles in dispersion. The ability to control mechanical properties using the cross-linked hydrogel network enables us to take advantage of the stiffness or elasticity of certain hydrogel formulations to impart the designed mechanical strength onto the conductive composite. As a preliminary demonstration, the PEDOT@PAAM/PEG hydrogel (ink 4) is able to keep a light-emitting diode (LED) lit even after being stretched to 800% strain (Fig. 3f).

Next, we quantified the electrical conductivity of these printed hydrogels by measuring the resistance of the gels using a two-point probe method (Table 1). The conductivity of the hydrogels tends to increase as a function of PEDOT:PSS concentration in the hydrogel precursor solution (Supplementary Fig. 11). The increase in PEDOT:PSS concentration over 20 mg mL⁻¹ in PEDOT@PEG gel, however, results in a sharp rise in the apparent viscosity of the polymer inks¹⁶. The tendency for PEDOT:PSS particles to agglomerate in these viscous inks further leads to an increase in printing head-clogging risk, particularly in the cases where small nozzles are used. Thus, to improve the electrical properties of our hydrogels that were printed with low PEDOT:PSS concentrations, we conducted a post-treatment process (i.e., soaking the hydrogels in ethylene glycol and dry annealing at 130 °C) once the printed inks were solidified. The conductivity of hydrogels made from ink 5 (9 mg mL⁻¹ PEDOT:PSS content) was enhanced by 3 orders of magnitude after post-treatment (ink 5*, 61.8 S m⁻¹ in the dry state and over 1.9 S m⁻¹ in the hydrogel state, Supplementary Fig. 12). Besides the known mechanisms of phase separation of PEDOT and PSS during the soaking process to form a denser PEDOT network^50,51 and the recrystallization of PEDOT-rich domains during dry annealing to generate higher conductive pathways^52,53, the water-loss-induced collapse of the conducting PEDOT@PEG network into aggregates during the dry annealing process is another significant factor that contributes to the enhanced conductivity of the printed gels, as revealed by the comparison of different drying treatments on printed hydrogels (Supplementary Fig. 13). The denser PEDOT network of the gels in the dry state also highly improved the modulus of the gels to dissipate more stress from mechanical deformation (Fig. 3e).

Interestingly, we found that the resistance of the post-treated gels made from ink 5* gradually decreased during the stretching-releasing process (Fig. 3g). Reversible stretching of the gel between 0 and 50% strain is likely to encourage a better orientation and more π–π stacking interactions between the PEDOT networks, which contribute to lowering the gel’s resistance by 12% after 30 cycles. Supporting this finding, grazing-incidence wide-angle X-ray scattering (GIWAXS) measurements show that the PEDOT:PSS crystallites in the gel changed from a disordered arrangement to a preferred face-on molecular orientation⁵⁴ relative to the stretching direction during stretching. Furthermore, a red shift of the C_α = C_β vibration peak indicates that the cyclic stretching process leads to a more planar backbone of PEDOT, which contributes to more efficient charge delocalization and a higher packing order^55,56 (Supplementary Fig. 14).

We further investigated the electrical stability of these printed gels. Compared with the chemically cured PEDOT@PEG hydrogel ink 5, cyclic voltammetry (CV) measurements show that the post-treated ink 5* hydrogel has satisfactory electrochemical stability against charging and discharging cycles in a wet environment (10× phosphate-buffered saline) with no obvious shifts in the oxidization and reduction peaks after 1000 CV cycles (Fig. 3h, i). Despite the absence of a covalent bond or strong physical interaction between the PEDOT chain and PEG network, the PEDOT gradually migrates away from the hydrogel network and into the surrounding aqueous environment after a period of more than two months (Supplementary Fig. 15). These elastic and conductive gels with a single chemically crosslinked network are more suitable for practical applications in air.

Highly conductive PEDOT-based hydrogels with two interpenetrating networks

Macroscopically connecting PEDOT:PSS particles as a conductive network to increase the number of charge conduction pathways is regarded as another effective strategy to improve the conductivity of PEDOT:PSS hydrogels^57,58. To generate a sufficient number of physical crosslinks between particles, we first mixed the ionic liquid 1-carboxymethyl-3-methylimidazolium bis(trifluoro-methylsulfonyl)imide (HOOCMIMNTF2) (2 wt%) in printing inks 6 and 7 and extruded the ink into threads suspended in the oil phase with PDMS-NH₂. Since ionic liquids are effective in screening the electrostatic repulsions between particles and thus triggering PEDOT:PSS to form physical crosslinks (Supplementary Fig. 16) through π–π stacking of PEDOT⁵⁹, these liquid inks trapped inside the PEDOT:PSS-surfactant assembly were gradually gelled into the designed 3D shapes (Fig. 4a, b). Rheological measurements (Fig. 4c) show that the physical crosslinking was triggered by the time the solution was mixed with HOOCMIMNTF2. Even though the storage modulus (G’) of the ink exceeded the loss modulus (G”) throughout the entire process, at this ionic liquid concentration, the ink mixture could maintain its flowability in the first 8 min (Supplementary Fig. 17). Since the gelation rate could be tuned by the concentration of the ionic liquid additive, for those processes that require a longer operation time, a lower concentration of HOOCMIMNTF2 could be selected to gel PEDOT:PSS at a slower rate. Although the PEDOT:PSS networks (primary network) behave similarly to solids after 10 min of gelation, they are still highly brittle if manipulated further. An acrylate network (secondary network) was then consequently introduced into the PEDOT:PSS network by UV curing for 2 min (Fig. 4d), resulting in mechanical reinforcement of the resultant polymer matrix (Fig. 4e). The printed PEDOT@PEG hydrogels with two interpenetrating networks could be stretched to 96% elongation (PEG 1000 (ink 6)) and even up to 263% elongation (PEG 20000 (ink 7)) prior to fracture.

**Fig. 4: Printed PEDOT hydrogels with two interpenetrating networks.**

Due to the formation of PEDOT conductive networks with enhanced π–π stacking interactions for electron transfer, both the conductivity (Table 1) and electrical stability (Supplementary Fig. 15) of the printed hydrogels are largely improved. These hydrogels with post-treatments achieve an electrical conductivity as high as 301 S m⁻¹ (ink 6*), 4-fold higher than the value of another printed gel without ionic liquid treatment (ink 5*). Electrical behavior under mechanical deformation shows that the conductivities of the printed hydrogels remained nearly unchanged from their starting values despite large variations in tensile strains (50% strain for ink 6* and 200% strain for ink 7*) (Fig. 4f). In particular, there was no apparent change in the resistance of both ink 6* and ink 7* gels even after being stretched to 25% strain. The robust conductivity can be attributed to the rearrangement of PEDOT domains that stay connected with others during the stress deformation, rather than disrupting or insulating the conductive regimes³⁴. Owing to the strain-independent conductivity of the gels, an LED can be kept lit after stretching ink 7* to 200% elongation. These results indicate that elasticity has been successfully incorporated into our conductive polymeric materials without sacrificing their electrical properties. The ability to orthogonally control the mechanical and electrical properties therefore enables us to impart the required stiffness onto the highly conductive composite.

Conductive hydrogel with 3D structures

Conducting polymer solutions, such as the pristine PEDOT:PSS aqueous dispersion (CLEVIOS™ PH 1000) used in this study, are typically not suitable for direct use in extrusion-based 3D printing or inkjet printing due to their fluidity. A significant advantage of using PEDOT:PSS-surfactant films to stabilize the liquid hydrogel precursor is that this printing technique refrains from restricting the viscosity and yield stress of the printing ink. As shown above (Fig. 2d), PEDOT:PSS inks with concentrations from 0.1 mg mL⁻¹ to 20 mg mL⁻¹ are applicable for printing free-form hydrogels with complex architectures. The sizes of the ink threads can be readily modulated by adjusting the print head speeds and flow rates. For instance, being equipped with a 14-gauge needle (internal diameter = 1.6 mm), the average diameter of the printed hydrogels varies from 2027 ± 64 μm to 94 ± 12 μm (Fig. 5a and Supplementary Fig. 18). The excellent uniformity and high yield of the PEDOT hydrogels (Fig. 5b) allow us to customize the conductive filaments facilely and accurately.

**Fig. 5: Printing Conductive hydrogels with 3D structures.**

With the PEDOT:PSS-surfactant assembly at the liquid-liquid interface, the squeezed liquid threads can be physically isolated and prevented from sticking to or fusing with each other during the whole process. Thereby, we successfully fabricated a 1.1 m-long conductive gel in a 1.8 cm-diameter circle of printing area (Fig. 5c, d, and Supplementary Movie 1). As the viscous oil phase (η_e ~ 30000 mPa∙s) could restrain the ink threads and counteract the effect of gravity, overhung structures that cannot be achieved in extrusion-based 3D printing were finely realized in our print (Fig. 5e, Supplementary Fig. 19 and Supplementary Movie 2). The compatibility with various inks enables this printing technique to integrate multiple materials into 3D hydrogels by programming the ink feed. A helix hydrogel consisting of two heterogeneous components was fabricated by sequential injection of distinct inks as a demonstration (Supplementary Fig. 20).

Apart from two of the existing strategies for 3D tubular structured hydrogels, i.e., the template method⁶⁰ and the digital light processing printing technique⁶¹, our approach provides another solution for tubular hydrogel fabrication when the print head is replaced by a coaxial double needle. Herein, while injecting the aqueous ink into a silicone oil bath (η_e ~ 30000 mPa s, oil phase 1) through the outer ring of the print head, another silicone oil solution of PDMS-NH₂ (η_e ~ 1000 mPa∙s, oil phase 2) was squeezed out from the interior cavity of such a needle at the same time (Fig. 5f). In this way, two concentric PPSs assembly layers were simultaneously formed at both the internal and external interfaces of the aqueous phase and thus shaped the ink into a tubular structure. The resulting hydrogel after chemical curing presents a clearly concentric circle cross-section without any collapse, and both the aqueous and organic liquids could be smoothly pumped through the channel (Fig. 5g, h). These results reveal the ability to facilely control the 3D morphology and composite properties of the printed hydrogels.

Hydrogel-based electrochemical microfluidic devices

To verify the capability of the printed tubular PEDOT:PSS hydrogel in creating an electric field of coaxial cylinders, we investigated the use of the printed 3D tube as an electro-microfluidic device⁶² for conducting electrochemical reactions, such as copper electroplating⁶³. As schematically shown in the working mechanism of the reaction in Fig. 6a, the hydrogel shell was designed to be connected with the positive electrode of a direct current (DC) source as an anode. A Pt wire, the object to be plated, was installed in the center of the hydrogel tube. To prevent the Pt wire from touching the hydrogel shell and produce a short circuit, the Pt wire was pinned through two electrically insulating O-ring gaskets that were placed at the inlet and outlet of the hydrogel channel. The gaskets were sealed tightly with the hydrogel shell to prevent leakage of the electrolyte during flow (Fig. 6b). Once the Pt wire was connected to the DC source to complete the circuit, we pumped a solution of 1 M CuSO₄ through the channel to trigger the electrolytic reaction. The real decomposition voltage in this fluidic electrolytic cell was determined to be 1.36 V by measuring the V-I characteristic curve (Fig. 6c). While pumping the solution under given voltages, the reduction of Cu(II) ions in electrolyte flow resulted in the deposition of the desired elemental Cu(0) on the Pt cathode surface, as demonstrated by the cathode thickness variation and the SEM imaging associated with EDX measurements (Fig. 6d, e and Supplementary Fig. 21). The byproduct O₂ generated from water in the hydrogel shell was emitted out of the channel along with the fluid stream. The uniform copper coating on the surface of the platinum wire confirms the presence of an electric field created by coaxial cylinders.

**Fig. 6: PEDOT conductive hydrogel as an electrochemical microfluidic device.**

Since the ink formulation plays an important role in tuning the conductivity of the printed gels, the rate of the electrolysis process is also affected. The electrolysis in a pure PEG hydrogel tube that was fabricated via the template method was quite slow (Fig. 6f), despite the diffusion of CuSO₄ electrolyte inside the hydrogel improving the conductivity of the tubular shell. In contrast, the printed ink 6* hydrogels could finish the electrolysis reaction within only four minutes, obtaining a 162 ± 41 μm thick copper layer at the Pt cathode. Although the conductivity of PEDOT:PSS tubular gels is inferior to that of metal tubes, their ease of printing and adjustable mechanical properties make them a promising candidate for producing coaxial cylindrical conductors, including customized coaxial cables for implantable patch antennas⁶⁴, in a more efficient and tailored way.

PEDOT-based NFC chip

Near-field communication (NFC) is a short-range and wireless technology that allows simultaneous power and data transmission between devices, offering exciting opportunities for the design of miniature and battery-free sensing systems in health care⁶⁵. Enabled by the effortless 3D printability as well as the combination of elasticity and electrical properties, 3D printing of the conducting polymer ink can offer a promising route for the facile fabrication of conducting polymer-based devices. As a proof-of-concept of the integration of these conductive gels into applicable devices, we fabricated a simple PEDOT-based NFC antenna at room temperature. As shown in Fig. 7a, we used the 3D printing method detailed in Fig. 5c to produce the filament-shaped PEDOT gels (ink 5*, approximately 1 meter long), which were then strung onto a chip holder that possessed a continuous coil groove to prevent contact short circuits between the conductive PEDOT gels (Fig. 7b).

**Fig. 7: Demonstration of PEDOT NFC devices.**

The PEDOT-based NFC antennas show stable accessibility for various NFC-enabled equipment. The wirelessly harvested energy from a smartphone via the PEDOT NFC antenna was able to make the connected LED blink at a cycle of 2 Hz (Fig. 7c and Supplementary Movie 3). The amplitude of the radio frequency signal (13.56 MHz) from the smartphone can also be read and collected through the biological tissue (here, a 3-mm thick pork rind was used), showing that the wireless transfer of power and data through skin is possible. With the increase in the signal transmission distance, the current density in the circuit shows a declining trend (Fig. 7d).

To validate the biocompatibility of our printed PEDOT:PSS-based hydrogels for potential use as implantable materials, we performed experiments to assess their cytocompatibility in vitro and histological analysis in vivo. We found that after 72 h of culture, the tested hydrogel samples (ink 5, ink 5*, ink 6, and ink 6*) demonstrated high cell proliferation with a viability percentage of approximately 95% (Supplementary Fig. 22). Despite the changes in interfacial density of PEDOT:PSS particles and concentration of PEG monomers resulting from the PPSs interfacial assembly process, the printed PEDOT@PEG hydrogels exhibited anti-cell adhesion properties (Supplementary Fig. 23), which are critical for preventing implant materials from failing due to unpredictable protein adsorption and cell interaction. In addition, we observed high biocompatibility of the printed PEDOT@PEG hydrogels (ink 6* with the most components) in immunocompetent mice at a time point of 7 days (Supplementary Fig. 24), with unsacrificed mice remaining alive and healthy without any abnormalities for two months after subcutaneous implantation. Although we failed to implant this unencapsulated PEDOT NFC tag into biological tissue because of the inevitable short circuit in a wet physiological environment, the energy transmission capability suggests the great potential of these PEDOT-based gels to be applied in next-generation, battery-free, wireless sensing and electrical impulse delivery devices, such as artificial cardiac pacemakers⁶⁶ or devices for cranial electrotherapy stimulation⁶⁷. Experiments for creating elastic and conductive gels surrounded with insulative shells for stretched, squeezable, and superficially implantable biomaterials are now underway in our laboratory.

Discussion

This is an effective attempt to facilely construct highly conductive hydrogels with tunable mechanical properties and 3D architecture by using liquid-in-liquid 3D printing technology. Polymer inks based on aqueous PEDOT:PSS capable of simultaneously forming PEDOT:PSS colloidal particles and PDMS surfactants assemblies at the liquid-liquid interface are successfully printed into arbitrary 3D structures without additional templates or supports. Additionally, the mechanically stable interfacial assembly allows these all-liquid architectures to be extensively manipulated, such as through ionic liquid-induced gelation and UV curing. This PEDOT:PSS-based ink exhibits broad applicability for various hydrogel-forming precursors and 3D printability over a wide range of PEDOT:PSS concentrations, solution pH values and, most importantly, apparent viscosities. With this capability, we successfully printed stretchable hydrogels (subjected to >200% strain) without compromising their conductivity, integrating multiple materials into advanced 3D objects and fabricating conductive tubular hydrogels for electrosynthesis. The PEDOT gel-based NFC chips enable wireless power harvesting through biological tissues, offering a possible route for electrical signal transmission while preserving the designed 3D architecture and matched mechanical properties when applied to human tissue engineering. Although there may be a lower resolution at the current stage and the long-term stability of the electrodeposited PEDOT:PSS on bioelectrodes in a wet physiological environment needs to be further improved, the ability to spatially program the electronic conductivity, mechanical properties and material functionality of a hydrogel in three dimensions makes this liquid-in-liquid 3D printing technique highly promising for integrating conductive gels into flexible and implantable bioelectronics, directing both matter and energy across biotic-abiotic interfaces.

Methods

Materials

Aqueous PEDOT:PSS dispersion, CLEVIOS™ PH 1000 (1.0 ~ 1.3 solid content) was purchased from Heraeus and used after adjusting the solid content to 10 mg mL⁻¹. Aminopropyl-terminated polydimethylsiloxane (PDMS-NH₂, M_n 4000 g mol⁻¹) was purchased from Suzhou Siso new material Co.,Ltd. (China) and used as received. The ionic liquid of 1-carboxymethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (HOOCMIMNTF2) was kindly provided by Yu Wang lab in Sichuan University (Purity ≥ 98%). PEG-diacrylates (M_n 6000 g mol⁻¹and M_n 20000 g mol⁻¹) were synthesized according to the literature⁶⁸. Rabbit anti-F4/80 antibody (70076S)、rabbit anti-Ly6G antibody (87048S)、and rabbit anti-CD206 antibody (24595T) were purchased from Cell Signaling Technology, Inc. (CST, USA). All other chemicals were purchased from Aladdin Scientific Ltd. (China) and used without further purification.

Synthesis of poly(ethylene glycol) diacrylate (M _n 6000 g mol⁻¹)

The synthesis was carried out following a literature procedure⁶⁸. In a 100 mL three-neck flask under a nitrogen atmosphere, 20 g of PEG (M_n 6000 g mol⁻¹, 1 eq.), 695 μL of triethylamine (5 eq.), and 40 mL of anhydrous tetrahydrofuran were combined and stirred until a homogeneous mixture was obtained. The flask was then placed in an ice-water bath, and a solution of 10 mL of anhydrous tetrahydrofuran containing 400 μL of acryloyl chloride (5 eq.) was added dropwise under a nitrogen atmosphere. Once the dropwise addition was complete, the reaction mixture was allowed to react overnight at room temperature. The formed salt was removed by filtration, and the filtrate was concentrated under vacuum. The resulting residue was then precipitated in ether, yielding a white solid product with 75% yield. The synthesis of poly(ethylene glycol) diacrylate (M_n 20,000 g mol⁻¹) followed a similar procedure as described above.

Mice

All studies of implantation experiments in vivo were approved with the permission of the Sichuan University Ethics Committee (protocol number 2020361A) and were conducted according to the institution’s guidelines. Female C57 black 6 mice (8 weeks old) were provided by the Dr. Hong Jiang laboratory (Sichuan University) and were used for all experiments in this study. The mice were housed in a controlled environment with a 12h–12h light-dark cycle (light cycle: 8:00 to 20:00), and they had access to food and water ad libitum. The room temperature was maintained within the range of 20–22 °C, while the humidity was kept between 30–70%, with an average daily humidity level of approximately 47%.

3D printing hydrogels

Water-in-oil threads were produced using a commercially available 3D printer (Ender 5 s, Creality, China), with the print heads replaced by a 30-, 25-, or 14-gauge stainless steel needle attached to a syringe pump (Longer Pump, China). To generate liquid threads with more accurate and uniform diameter, a precision dispenser (Prtronic, China) was also applied for injecting inks into liquid threads. Print head trajectories was generated using AutoCAD 2014 software, which was subsequently converted into G-code using open-source software Repetier-Host to monitor the x-y-z motion of the print head. Lateral print head velocities were set from 0.1 to 1.5 m min⁻¹. Aqueous dispersions were injected at 0.05–1.5 mL min⁻¹, depending on the desired thread thickness. All the printing procedures were implemented in the mixed silicone oil phase (viscosity varied from 10 mPa∙s to 30,000 mPa∙s) containing 10 vol% aminopropyl terminated polydimethylsiloxane. Unless specified otherwise, the oil phase utilized for 3D printing is silicone oil (η_e ~ 30,000 mPa∙s) that contains 10 vol% PDMS-NH₂.

For the hydrogels with a single chemically crosslinked network, the liquid ink threads were irradiated under UV_{395 nm} light for various time to ensure the chemical crosslinking after printing. For the hydrogels with two interpenetrating networks, freshly prepared ink containing 2 wt% ionic liquid HOOCMIMNTF2 was charged into a syringe and implemented a similar 3D printing process. Subsequently, the liquid thread was static for 10 min in the silicone oil to ensure sufficient physical gelation. After UV curing, the hydrogels were rinsed thoroughly with hexane.

Post-treatments

Post-treatments were carried out via washing the hydrogels by using ethylene glycol for 1.5 h, and annealing at 130 °C for 10 more minutes. If needed, the dry-annealed polymer gels were further immersed in water for 24 h to convert into the hydrogel state.

Characterization

A Discovery Hybrid Rheometer HR 20-TA instrument (USA) was used to perform tensile testing. Rheological measurements were conducted by using Anton-Paar’s Modular Compact Rheometer 302 (Austria). For the physical crosslinking measurement, a 25 mm parallel plate was used and the measurements were taken at 25 °C at 1 Hz and a strain rate of 0.1%. SEM images of the hydrogels were obtained by lyophilizing the hydrogels, and images were obtained using an Apreo 2 SEM (Thermo Fisher Scientific, USA). Conductivity was calculated by measuring resistance using a Keithley 2400 two-point probe head. Reported values reflect an average over a minimum of three to five measurements obtained for each condition. The brightfield images were taken by using a Leica M205 FCA microscope (Germany) and Leica DMi 8 microscope (Germany), and the data were analyzed with FIJI software. GIWAXS data were obtained at 1W1A Diffuse X-ray Scattering Station, Beijing Synchrotron Radiation Facility (BSRF-1W1A). The monochromatic of the light source was 1.54 Å. The data were recorded by using the two-dimensional image plate detector of Eiger 2 M from Dectris, Switzerland.

Interfacial tension (IFT) measurements

Dynamic surface tension measurements were performed by fitting the profile of a pendant drop of aqueous PEDOT:PSS dispersion, immersed in toluene containing PDMS-NH₂ surfactants, to the Young-Laplace equation. Droplet profiles and fitting were performed using Krüss DSA25 Drop Shape Analyzer, with surface tensions calculated using the DSA Advance software. The evolution of IFT with time was recorded after slowly injecting the highly diluted PEDOT:PSS aqueous droplets with an initial volume of 20 μL into the toluene phase.

Copper electroplating in the conductive hydrogels

The hollow structured hydrogels with different electrical conductivities (ink 1 and ink 6*) were fabricated and soaked in 1 M CuSO₄ solution for 12 h before setting up. The open ends of the hydrogel tubes were sealed tightly by using two identical insulated pipe gaskets, and a clean and bare platinum wire (diameter: 0.28 mm) was implanted into the hollow hydrogels along the central axial of the hydrogel tubes. In a humidity-saturated environment, the hydrogel shell was connected with the positive electrode of a DC source, and the Pt wire was connected to the negative electrode of the DC source to complete the circuit. A steady stream of 1 M CuSO₄ solution was pumped through the inlet at a flow rate of 0.05 mL min⁻¹, and a certain voltage was applied to initiate the electrolytic reaction.

NFC chip fabrication

A small chip holder that possessed a continuous coil groove was obtained via DLP 3D printing of commercial resin (MiiCraft Prime 110). Next, a printed PEDOT filament (ink 5*), 1 m long with a thickness of 200 µm, was strung inside the groove under room temperature. An LED was embedded in the chip to form a close circuit.

Reporting summary

Further information on research design is available in the Nature Portfolio Reporting Summary linked to this article.

Data availability

The data that support the plots within this paper and other finding of this study are presented in the main article and the Supplementary Materials. All other additional data are available from the corresponding author upon request. Source data are provided with this paper.

References

Jiang, Y. et al. Topological supramolecular network enabled high-conductivity, stretchable organic bioelectronics. Science 375, 1411–1417 (2022).
Article ADS CAS PubMed Google Scholar
Benabid, A. L. et al. An exoskeleton controlled by an epidural wireless brain–machine interface in a tetraplegic patient: a proof-of-concept demonstration. Lancet Neurol. 18, 1112–1122 (2019).
Article PubMed Google Scholar
Yang, X. et al. Bioinspired neuron-like electronics. Nat. Mater. 18, 510–517 (2019).
Article ADS CAS PubMed PubMed Central Google Scholar
Daly, J. J. & Wolpaw, J. R. Brain–computer interfaces in neurological rehabilitation. Lancet Neurol. 7, 1032–1043 (2008).
Article PubMed Google Scholar
Song, E., Li, J., Won, S. M., Bai, W. & Rogers, J. A. Materials for flexible bioelectronic systems as chronic neural interfaces. Nat. Mater. 19, 590–603 (2020).
Article ADS CAS PubMed Google Scholar
Oh, J. Y. & Bao, Z. Second Skin Enabled by Advanced Electronics. Adv. Sci. 6, 1900186 (2019).
Article Google Scholar
Chaudhary, U. et al. Spelling interface using intracortical signals in a completely locked-in patient enabled via auditory neurofeedback training. Nat. Commun. 13, 1236 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Ma, Y. et al. Flexible Hybrid Electronics for Digital Healthcare. Adv. Mater. 32, 1902062 (2020).
Article CAS Google Scholar
van de Burgt, Y., Melianas, A., Keene, S. T., Malliaras, G. & Salleo, A. Organic electronics for neuromorphic computing. Nat. Electron. 1, 386–397 (2018).
Article Google Scholar
Mahmood, M. et al. Fully portable and wireless universal brain–machine interfaces enabled by flexible scalp electronics and deep learning algorithm. Nat. Mach. Intell. 1, 412–422 (2019).
Article Google Scholar
Inal, S., Rivnay, J., Suiu, A.-O., Malliaras, G. G. & McCulloch, I. Conjugated Polymers in Bioelectronics. Acc. Chem. Res. 51, 1368–1376 (2018).
Article CAS PubMed Google Scholar
Engler, A. J., Sen, S., Sweeney, H. L. & Discher, D. E. Matrix Elasticity Directs Stem Cell Lineage Specification. Cell 126, 677–689 (2006).
Article CAS PubMed Google Scholar
Lu, B. et al. Pure PEDOT:PSS hydrogels. Nat. Commun. 10, 1043 (2019).
Article ADS PubMed PubMed Central Google Scholar
Zheng, Y.-Q. et al. Monolithic optical microlithography of high-density elastic circuits. Science 373, 88–94 (2021).
Article ADS CAS PubMed Google Scholar
Feig, V. R. et al. An Electrochemical Gelation Method for Patterning Conductive PEDOT:PSS Hydrogels. Adv. Mater. 31, 1902869 (2019).
Article Google Scholar
Yuk, H. et al. 3D printing of conducting polymers. Nat. Commun. 11, 1604 (2020).
Article CAS PubMed PubMed Central Google Scholar
Meng, J., Streitz, T., Gulachek, N., Suma, D. & He, B. Three-Dimensional Brain–Computer Interface Control Through Simultaneous Overt Spatial Attentional and Motor Imagery Tasks. IEEE Trans. Biomed. Eng. 65, 2417–2427 (2018).
Article PubMed PubMed Central Google Scholar
Huang, Z. et al. Three-dimensional integrated stretchable electronics. Nat. Electron. 1, 473–480 (2018).
Article Google Scholar
Lin, P. et al. Three-dimensional memristor circuits as complex neural networks. Nat. Electron. 3, 225–232 (2020).
Article Google Scholar
Zhao, Y. et al. Scalable ultrasmall three-dimensional nanowire transistor probes for intracellular recording. Nat. Nanotechnol. 14, 783–790 (2019).
Article CAS PubMed Google Scholar
Yazdimamaghani, M. et al. Biomineralization and biocompatibility studies of bone conductive scaffolds containing poly(3,4-ethylenedioxythiophene):poly(4-styrene sulfonate) (PEDOT:PSS). J. Mater. Sci.: Mater. Med. 26, 274 (2015).
PubMed Google Scholar
Berggren, M. & Richter-Dahlfors, A. Organic Bioelectronics. Adv. Mater. 19, 3201–3213 (2007).
Article CAS Google Scholar
Kayser, L. V. & Lipomi, D. J. Stretchable Conductive Polymers and Composites Based on PEDOT and PEDOT:PSS. Adv. Mater. 31, 1806133 (2019).
Article Google Scholar
Green, R. Elastic and conductive hydrogel electrodes. Nat. Biomed. Eng. 3, 9–10 (2019).
Article PubMed Google Scholar
Martinelli, A., Nitti, A., Giannotta, G., Po, R. & Pasini, D. 3D printing of conductive organic polymers: challenges and opportunities towards dynamic and electrically responsive materials. Mater. Today Chem. 26, 101135 (2022).
Article CAS Google Scholar
Wei, H. et al. Orthogonal photochemistry-assisted printing of 3D tough and stretchable conductive hydrogels. Nat. Commun. 12, 2082 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Heo, D. N. et al. Development of 3D printable conductive hydrogel with crystallized PEDOT:PSS for neural tissue engineering. Mater. Sci. Eng.: C. 99, 582–590 (2019).
Article CAS Google Scholar
Lopez-Larrea, N. et al. Digital Light 3D Printing of PEDOT-Based Photopolymerizable Inks for Biosensing. ACS Appl. Polym. Mater. 4, 6749–6759 (2022).
Article CAS PubMed PubMed Central Google Scholar
Zhu, H., Hu, X., Liu, B., Chen, Z. & Qu, S. 3D Printing of Conductive Hydrogel–Elastomer Hybrids for Stretchable Electronics. ACS Appl. Mater. Interfaces 13, 59243–59251 (2021).
Article CAS PubMed Google Scholar
Wu, Q. et al. A robust, highly stretchable supramolecular polymer conductive hydrogel with self-healability and thermo-processability. Sci. Rep. 7, 41566 (2017).
Article ADS PubMed PubMed Central Google Scholar
Dai, T., Qing, X., Lu, Y. & Xia, Y. Conducting hydrogels with enhanced mechanical strength. Polymer 50, 5236–5241 (2009).
Article CAS Google Scholar
Goding, J., Gilmour, A., Martens, P., Poole-Warren, L. & Green, R. Interpenetrating Conducting Hydrogel Materials for Neural Interfacing Electrodes. Adv. Healthc. Mater. 6, 1601177 (2017).
Article Google Scholar
He, Y. et al. Continuous and Patterned Conducting Polymer Coatings on Diverse Substrates: Rapid Fabrication by Oxidant-Intermediated Surface Polymerization and Application in Flexible Devices. ACS Appl. Mater. Interfaces 13, 5583–5591 (2021).
Article CAS PubMed Google Scholar
Feig, V. R., Tran, H., Lee, M. & Bao, Z. Mechanically tunable conductive interpenetrating network hydrogels that mimic the elastic moduli of biological tissue. Nat. Commun. 9, 2740 (2018).
Article ADS PubMed PubMed Central Google Scholar
Honaryar, H., Amirfattahi, S. & Niroobakhsh, Z. Associative Liquid-In-Liquid 3D Printing Techniques for Freeform Fabrication of Soft Matter. Small 19, 2206524 (2023).
Article CAS Google Scholar
McCormack, A., Highley, C. B., Leslie, N. R. & Melchels, F. P. W. 3D Printing in Suspension Baths: Keeping the Promises of Bioprinting Afloat. Trends Biotechnol. 38, 584–593 (2020).
Article CAS PubMed Google Scholar
Chen, G. et al. Bioinspired 3D Printing of Functional Materials by Harnessing Enzyme-Induced Biomineralization. Adv. Funct. Mater. 32, 2113262 (2022).
Article MathSciNet CAS Google Scholar
Honaryar, H., LaNasa, J. A., Lloyd, E. C., Hickey, R. J. & Niroobakhsh, Z. Fabricating Robust Constructs with Internal Phase Nanostructures via Liquid-in-Liquid 3D Printing. Macromol. Rapid Commun. 42, 2100445 (2021).
Article CAS Google Scholar
Forth, J. et al. Reconfigurable Printed Liquids. Adv. Mater. 30, 1707603 (2018).
Article Google Scholar
Zheng, Y. et al. Coagulation Bath-Assisted 3D Printing of PEDOT:PSS with High Resolution and Strong Substrate Adhesion for Bioelectronic Devices. Adv. Mater. Technol. 7, 2101514 (2022).
Article CAS Google Scholar
Jo, Y. J. et al. Fibrillary gelation and dedoping of PEDOT:PSS fibers for interdigitated organic electrochemical transistors and circuits. npj Flex. Electron. 6, 31 (2022).
Article CAS Google Scholar
Wang, P. et al. Surface engineering via self-assembly on PEDOT: PSS fibers: Biomimetic fluff-like morphology and sensing application. Chem. Eng. J. 425, 131551 (2021).
Article CAS Google Scholar
Takano, T., Masunaga, H., Fujiwara, A., Okuzaki, H. & Sasaki, T. PEDOT Nanocrystal in Highly Conductive PEDOT:PSS Polymer Films. Macromolecules 45, 3859–3865 (2012).
Article ADS CAS Google Scholar
Cui, M., Emrick, T. & Russell Thomas, P. Stabilizing Liquid Drops in Nonequilibrium Shapes by the Interfacial Jamming of Nanoparticles. Science 342, 460–463 (2013).
Article ADS CAS PubMed Google Scholar
Feng, W. et al. Harnessing liquid-in-liquid printing and micropatterned substrates to fabricate 3-dimensional all-liquid fluidic devices. Nat. Commun. 10, 1095 (2019).
Article ADS PubMed PubMed Central Google Scholar
Liu, X. et al. Reconfigurable ferromagnetic liquid droplets. Science 365, 264–267 (2019).
Article ADS MathSciNet CAS PubMed Google Scholar
Jain, K., Mehandzhiyski, A. Y., Zozoulenko, I. & Wågberg, L. PEDOT:PSS nano-particles in aqueous media: A comparative experimental and molecular dynamics study of particle size, morphology and z-potential. J. Colloid Interface Sci. 584, 57–66 (2021).
Article ADS CAS PubMed Google Scholar
Huang, C. et al. Structured Liquids with pH-Triggered Reconfigurability. Adv. Mater. 28, 6612–6618 (2016).
Article CAS PubMed Google Scholar
Bae, J., Russell, T. P. & Hayward, R. C. Osmotically Driven Formation of Double Emulsions Stabilized by Amphiphilic Block Copolymers. Angew. Chem. Int. Ed. 53, 8240–8245 (2014).
Article CAS Google Scholar
Ouyang, L., Musumeci, C., Jafari, M. J., Ederth, T. & Inganäs, O. Imaging the Phase Separation Between PEDOT and Polyelectrolytes During Processing of Highly Conductive PEDOT:PSS Films. ACS Appl. Mater. Interfaces 7, 19764–19773 (2015).
Article CAS PubMed Google Scholar
Wei, Q., Mukaida, M., Naitoh, Y. & Ishida, T. Morphological Change and Mobility Enhancement in PEDOT:PSS by Adding Co-solvents. Adv. Mater. 25, 2831–2836 (2013).
Article CAS PubMed Google Scholar
Shi, H., Liu, C., Jiang, Q. & Xu, J. Effective Approaches to Improve the Electrical Conductivity of PEDOT:PSS: A Review. Adv. Electron. Mater. 1, 1500017 (2015).
Article Google Scholar
Vitoratos, E. et al. Thermal degradation mechanisms of PEDOT:PSS. Org. Electron. 10, 61–66 (2009).
Article CAS Google Scholar
Palumbiny, C. M. et al. The Crystallization of PEDOT:PSS Polymeric Electrodes Probed In Situ during Printing. Adv. Mater. 27, 3391–3397 (2015).
Article CAS PubMed Google Scholar
Wang, Y. et al. A highly stretchable, transparent, and conductive polymer. Sci. Adv. 3, e1602076 (2017).
Article ADS PubMed PubMed Central Google Scholar
Garreau, S., Louarn, G., Buisson, J. P., Froyer, G. & Lefrant, S. In Situ Spectroelectrochemical Raman Studies of Poly(3,4-ethylenedioxythiophene) (PEDT). Macromolecules 32, 6807–6812 (1999).
Article ADS CAS Google Scholar
Noriega, R. et al. A general relationship between disorder, aggregation and charge transport in conjugated polymers. Nat. Mater. 12, 1038–1044 (2013).
Article ADS CAS PubMed Google Scholar
Zhang, S. et al. Room-Temperature-Formed PEDOT:PSS Hydrogels Enable Injectable, Soft, and Healable Organic Bioelectronics. Adv. Mater. 32, 1904752 (2020).
Article CAS Google Scholar
Leaf, M. A. & Muthukumar, M. Electrostatic Effect on the Solution Structure and Dynamics of PEDOT:PSS. Macromolecules 49, 4286–4294 (2016).
Article ADS CAS Google Scholar
Ma, S. et al. Continuous Surface Polymerization via Fe(II)-Mediated Redox Reaction for Thick Hydrogel Coatings on Versatile Substrates. Adv. Mater. 30, 1803371 (2018).
Article Google Scholar
Levato, R. et al. High-resolution lithographic biofabrication of hydrogels with complex microchannels from low-temperature-soluble gelatin bioresins. Mater. Today Bio 12, 100162 (2021).
Article CAS PubMed PubMed Central Google Scholar
Noël, T., Cao, Y. & Laudadio, G. The Fundamentals Behind the Use of Flow Reactors in Electrochemistry. Acc. Chem. Res. 52, 2858–2869 (2019).
Article PubMed PubMed Central Google Scholar
Lennon, A., Colwell, J. & Rodbell, K. P. Challenges facing copper-plated metallisation for silicon photovoltaics: Insights from integrated circuit technology development. Prog. Photovoltaics: Res. Appl. 27, 67–97 (2019).
Article CAS Google Scholar
Kiourti, A. & Nikita, K. S. A Review of Implantable Patch Antennas for Biomedical Telemetry: Challenges and Solutions. IEEE Antennas Propag. Mag. 54, 210–228 (2012).
Article ADS Google Scholar
Olenik, S., Lee, H. S. & Güder, F. The future of near-field communication-based wireless sensing. Nat. Rev. Mater. 6, 286–288 (2021).
Article ADS CAS PubMed PubMed Central Google Scholar
Ouyang, H. et al. Symbiotic cardiac pacemaker. Nat. Commun. 10, 1821 (2019).
Article ADS PubMed PubMed Central Google Scholar
Li, J. et al. A tissue-like neurotransmitter sensor for the brain and gut. Nature 606, 94–101 (2022).
Article ADS CAS PubMed PubMed Central Google Scholar
Mann, B. K., Gobin, A. S., Tsai, A. T., Schmedlen, R. H. & West, J. L. Smooth muscle cell growth in photopolymerized hydrogels with cell adhesive and proteolytically degradable domains: synthetic ECM analogs for tissue engineering. Biomaterials 22, 3045–3051 (2001).
Article CAS PubMed Google Scholar

Download references

Acknowledgements

The authors thank to Dr. Yu Wang in Sichuan University for help in tensile testing. The authors gratefully acknowledge the cooperation of the beamline scientists at BSRF-1W1A beamline. This work was financially supported by the Science and Technology Project of Sichuan Province (2021YFH0183, 2022ZYD0030 and 2023NSFSC0990).

Author information

Authors and Affiliations

College of Polymer Science and Engineering, Sichuan University, 610065, Chengdu, China
Xinjian Xie, Zhonggang Xu & Wenqian Feng
Department of Pancreatic Surgery, Department of Biotherapy, West China Hospital, Sichuan University, 610065, Chengdu, China
Xin Yu & Hong Jiang
College of Chemical Engineering, Sichuan University, 610065, Chengdu, China
Hongjiao Li
State Key Laboratory of Polymer Materials Engineering, Sichuan University, 610065, Chengdu, China
Wenqian Feng

Authors

Xinjian Xie
View author publications
You can also search for this author in PubMed Google Scholar
Zhonggang Xu
View author publications
You can also search for this author in PubMed Google Scholar
Xin Yu
View author publications
You can also search for this author in PubMed Google Scholar
Hong Jiang
View author publications
You can also search for this author in PubMed Google Scholar
Hongjiao Li
View author publications
You can also search for this author in PubMed Google Scholar
Wenqian Feng
View author publications
You can also search for this author in PubMed Google Scholar

Contributions

X.X., H.L. and W.F. conceived the idea and designed the study. X.X. and Z.X. carried out the printing experiments, mechanical characterizations and electrical conductivity measurements. X.X. performed the electrochemical tests, chip fabrication and cell experiments. X.Y and H.J performed the subcutaneous implantation and histological analysis on the mice. X.X., H.L. and W.F. analyzed and interpreted the results. X.X. and W.F. wrote the manuscript.

Corresponding authors

Correspondence to Hongjiao Li or Wenqian Feng.

Ethics declarations

Competing interests

The authors declare no competing interests.

Peer review

Peer review information

Nature Communications thanks Simon Moulton and the other, anonymous, reviewers for their contribution to the peer review of this work. A peer review file is available.

Additional information

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Supplementary Information

Peer Review File

Description of Additional Supplementary Files

Supplementary Movie 1

Supplementary Movie 2

Supplementary Movie 3

Reporting Summary

Source data

Source Data

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and permissions

About this article

Cite this article

Xie, X., Xu, Z., Yu, X. et al. Liquid-in-liquid printing of 3D and mechanically tunable conductive hydrogels. Nat Commun 14, 4289 (2023). https://doi.org/10.1038/s41467-023-40004-7

Download citation

Received: 15 November 2022
Accepted: 06 July 2023
Published: 18 July 2023
DOI: https://doi.org/10.1038/s41467-023-40004-7

This article is cited by

Engineering redox-active electrochemically mediated carbon dioxide capture systems
- Michael Massen-Hane
- Kyle M. Diederichsen
- T. Alan Hatton
Nature Chemical Engineering (2024)
Recent advances in 3D printable conductive hydrogel inks for neural engineering
- Sung Dong Kim
- Kyoungryong Kim
- Mikyung Shin
Nano Convergence (2023)

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.