Abstract
Engineering surface chemistry to precisely control interfacial interactions is crucial for fabricating superior antifouling coatings and separation membranes. Here, we present a hydrophobic chain engineering strategy to regulate membrane surface at a molecular scale. Hydrophilic phytic acid and hydrophobic perfluorocarboxylic acids are sequentially assembled on a graphene oxide membrane to form an amphiphilic surface. The surface energy is reduced by the introduction of the perfluoroalkyl chains while the surface hydration can be tuned by changing the hydrophobic chain length, thus synergistically optimizing both fouling-resistance and fouling-release properties. It is found that the surface hydration capacity changes nonlinearly as the perfluoroalkyl chain length increases from C4 to C10, reaching the highest at C6 as a result of the more uniform water orientation as demonstrated by molecular dynamics simulations. The as-prepared membrane exhibits superior antifouling efficacy (flux decline ratio <10%, flux recovery ratio ~100%) even at high permeance (~620 L m−2 h−1 bar−1) for oil-water separation.
Similar content being viewed by others
Introduction
Massive oily wastewater is continuously being generated with the rapid development of industry, especially in petrochemicals, machining, textile, and food industries1,2. For example, global produced water production is estimated to be around 250 million barrels per day3. Given the discharge standards of most nations for the oil content of effluents (<40 mg/L), there raises a great demand for advanced treatment of oily wastewater4. Membrane technology has unique advantages in dealing with oily wastewater for its high separation efficiency and low energy cost, especially for the disposal of the highly stable oil-water emulsion with a droplet size smaller than 20 μm5,6. The major obstacle for the membrane separation technique to overcome is the fouling issue. The spreadable oil droplets are susceptible to coalesce and spread on membrane surfaces, which results in severe membrane fouling, lower separation efficiency, and higher operational costs7,8. Two-dimensional graphene oxide (GO)-based membranes show great promise in wastewater treatment for their high flux9,10,11,12. However, at high flux, the intensified concentration polarization effect will lead to more oil droplets at the surface and induce stronger interaction of the membrane surface with oil droplets13. Tailoring membrane surfaces to mitigate the severe fouling at high flux is thus a critical challenge for developing membranes for oil-water separation14,15.
Minimizing the interfacial interactions of surface to pollutants is the key to enhancing antifouling property7,16. A recent promising strategy is constructing amphiphilic surfaces that incorporate hydrophobic materials (typically fluorinated) onto hydrophilic surfaces to simultaneously realize fouling resistance and release, which has been demonstrated to be effective in numerous fields, including medical devices, marine antifouling, and membrane separation17,18,19,20,21,22. The steric and energetic barrier of hydration layers induced by the hydrophilic domains resists the spread of pollutants23,24,25,26, while the low surface energy of the hydrophobic domains facilitates the release of pollutants27,28,29. Although the amphiphilic antifouling surfaces have been widely reported, achieving the synergic optimization of fouling-resistance and fouling-release properties is still challenging30. Generally, nonpolar hydrophobic domains used to enhance fouling-release ability usually reduce the surface hydration, which thermodynamically promotes the spread of pollutants and thus deteriorates the fouling-resistance ability31,32. To introduce hydrophobic domains while maintaining the surface hydration capacity, surface chemistry needs to be engineered to elaborately regulate the interfacial interactions between surfaces and pollutants33. Previous work attempted to perform the regulation mostly by adjusting the hydrophobicity, amount, and distribution of hydrophobic domains33,34,35,36. So far, few studies have achieved the optimization of the interfacial interaction by interfering with the surface hydration of the amphiphilic surfaces. Additionally, the underlying molecular-level influence of hydrophobic domains on the hydration capacity of amphiphilic surfaces is still elusive.
Herein, we constructed an amphiphilic GO membrane and proposed a hydrophobic chain engineering strategy to regulate the interfacial interactions of the surface with oil droplets, thus achieving ultralow fouling at high flux. We sequentially assembled hydrophilic phytic acid (PA) and hydrophobic perfluorocarboxylic acids on a GO membrane to form an amphiphilic surface with a continuous hydrophilic domain and discrete hydrophobic domains. For the construction of PA on membrane surfaces, assembly strategies based on hydrogen bonds and coordination are recently proposed37,38,39. Coordination-driven metal-bridging assembly, in our study, is employed to perform the controllable assembly of PA and perfluoroalkyl chains. The surface energy is reduced by introducing the perfluoroalkyl chains, while concomitantly, the surface hydration can be tuned by changing the length of the hydrophobic chains, thus achieving the synergetic enhancement in both fouling-release and fouling-resistance properties. We systematically analyzed the wetting behavior of the proposed membrane to illustrate the effect of the length of perfluoroalkyl chains on interfacial interactions and correlated them with antifouling properties. Further, molecular dynamics simulation, together with experiments, were employed to elucidate the evolution of the hydration structure on the proposed amphiphilic membrane. Finally, we applied the membrane in the filtration of oily wastewater and demonstrated the enhancement in the antifouling capacity during the separation process.
Results
Regulation of the surface chemical structure of the F-hGO membranes
PA possessing six phosphate groups with high hydration energy and perfluorocarboxylic acid with ultralow surface energy were selected as the hydrophilic and hydrophobic components, respectively, and the amphiphilic surfaces were prepared on GO membranes via coordination-driven metal-bridging assembly. We chose perfluorocarboxylic acids with different numbers of carbon atoms, namely, 4, 6, 8, and 10, to adjust the length of the hydrophobic chains and changed the concentration of Fe3+ on the surface to control the density of the perfluorocarboxylic acids, hence achieving the molecular-scale regulation of the surface chemistry. Specifically, as described in Fig. 1, during the fabrication, the Fe3+-PA complexes grew on GO nanosheets via coordination, and a superhydrophilic GO membrane (hGO) was formed by vacuum-assisted self-assembly. The presence of the characteristic peaks of phosphate bond (1001 and 1067 cm−1) in the Fourier transform infrared (FTIR) spectrum of the hGO membrane (Fig. 1b), together with the appearance of the phosphate peaks (132.7 and 133.6 eV) in the X-ray photoelectron spectroscopy (XPS) spectrum of the hGO membrane (Fig. 1c and Supplementary Fig. 3a), illustrates the introduction of Fe3+–PA complex on the GO membrane37,38. Fe3+ acts as bridges and incorporates the hGO membrane surface with the carboxylic acid of the perfluorocarboxylic acids, thus anchoring the perfluorocarboxylic acids and forming the amphiphilic surfaces. The C–F bond can be detected in the XPS spectra (688.2 eV, Fig. 2c and Supplementary Fig. 3b) of the F-hGO membranes, which demonstrates the incorporation of perfluoroalkyl chains on the hGO membrane40.
The variation in the length of perfluorocarboxylic acids is supposed to exert a negligible effect on the coordination process, which can be proved quantitatively by the area ratio of the F peak to the P peak in the XPS spectra of the F-hGO membranes. The peak areas of the P element are almost consistent in the four cases (Supplementary Fig. 3a), suggesting the detection of the P element is not significantly affected by the chain length, which illustrates the validity of the F/P ratio to characterize the F content. As shown in Fig. 1d, the F content continuously ascends with the chain length, and its variation is almost in line with the molar ratio of the F atoms in the introduced perfluorocarboxylic acids, implying the distribution density of the coordinated perfluorocarboxylic acids on the four surfaces is almost similar. Further, we observed the F6-hGO membrane without substrate under transmission electron microscopy. The energy-dispersive X-ray spectroscopy mapping image reveals that the perfluorocarboxylic acids are evenly distributed on the membrane surface (Supplementary Fig. 4).
Wetting behavior
The wetting behavior of the membranes was studied to assess the effect of the length of perfluoroalkyl chains on the interfacial interactions. Generally, a low intermolecular interaction and a small contact area lead to low adhesion and thus help the removal of oil droplets (Fig. 2a)27,41. Modulating the length of perfluoroalkyl chains, we observed that the apparent water contact angle monotonously increases with the chain length (Fig. 2b). The decline in apparent surface energy \(({\gamma }_{SV}^{{\prime} })\) caused by the increased F content accounts for the increase in water contact angle (Fig. 2c). The decreasing \({\gamma }_{SV}^{{\prime} }\), especially the dispersion component\(({\gamma }_{SV}^{{\prime} d})\), indicates that the Van der Waals interaction between the surface and the environment descends with the prolongation of hydrophobic chains. On the other hand, the reduced surface energy thermodynamically promotes the spread of oil droplets on surfaces42. In our case, the underwater oil contact angle reduces, but it still exhibits underwater superoleophobicity (Fig. 2d). It is worth noting that the underwater oil contact angle is not linearly related to the chain length but show an inverted-U tendency. The F6-hGO membrane displays the highest underwater oil contact angle (165.7°) and smallest contact area compared to those of other F-hGO membranes. We further analyzed the relationship between the \({\gamma }_{SV}^{{\prime} }\) and the underwater oil contact angle and calculated the corresponding theoretical values according to Young’s equation in solid–liquid–liquid systems and Wenzel’s equation43,44.
where θOW and θ′OW are the underwater oil contact angles on the smooth and rough surfaces, respectively. \({\gamma }_{{SW}}\), \({\gamma }_{{SO}}\), and \({\gamma }_{{OW}}\), are the interfacial tension of the surface/water, surface/ hexadecane, and hexadecane/water, respectively. r is the roughness factor of the surfaces, which was obtained from the AFM test (Supplementary Fig. 5). The result is presented in Fig. 2e and Supplementary Table 1. We noticed that the experimental values are all higher than the calculated values. This deviation can be observed in many works, which is mainly because surface hydration changes the interfacial interactions of the system45,46. More importantly, we find that the curve shape deviates from the calculated one in which the underwater oil contact angle continuously decreases with the surface energy. The F6-hGO membrane with lower surface energy shows higher underwater oleophobicity compared to that of the F4-hGO membrane. This unexpected result suggests that the surface hydration is sensitive to the chain length, which allows us to control the surface hydration when introducing perfluoroalkyl chains to simultaneously achieve both a low contact angle and a low intermolecular interaction. To illustrate the universality of the phenomenon, we also tested the underwater oil contact angles with tetrachloromethane and n-hexane, and similar results were obtained (Supplementary Fig. 6).
Adhesive force, as shown in Fig. 2f, was further measured by AFM to quantitatively probe the oil-membrane interaction between the amphiphilic membranes and oil droplets. As expected, due to the lower surface energy and the smaller oil contact area, the adhesive force of the F6-hGO membrane (0.54 μN) drops nearly 50% compared with that of the F4-hGO membrane (1.01 μN). When the number of carbon atoms in the perfluoroalkyl chains exceeds 6, extending the perfluoroalkyl chains can further reduce the surface energy, but the excessively increased contact area substantially rises interfacial interactions. For instance, in terms of the F10-hGO membrane, the surface energy decreased by ~15%, while the contact area increased by more than 60% compared with those of the F6-hGO membrane, eventually leading to a 1.20 μN adhesive force.
Hydration capacity
Our experiments presented an unexpected phenomenon that the underwater oil contact angle of the proposed membrane surface shows a nonmonotonic relationship with the length of perfluoroalkyl chains. This endows the amphiphilic membrane with the medium-length perfluoroalkyl chains (C6) with the lowest contact area, thereby obtaining the lowest underwater oil adhesive force. Surface hydration has been proven to be associated with underwater oil-wetting behaviors47. More and more studies pointed out that the side groups or functional groups within the size range of the hydration layers (subnanometer to few nanometers) can control the hydration structure, hence affecting interfacial behavior and antifouling performances24,48. Inspired by these, we suppose that perfluoroalkyl chains with different lengths alter the hydration structure of the surface, hence regulating the distribution density and cohesive strength of the water adsorbed on surfaces.
To confirm our hypothesis, molecular dynamics simulations were performed to elucidate the evolution of the hydration on the proposed amphiphilic surfaces. The perfluoroalkyl chains, due to their nonpolar nature, is not prone to attach to the polar superhydrophilic surfaces in the water49. Therefore, the perfluoroalkyl chains were set as stretching outward to the aqueous phase in our model. Figure 3a–d display the plots of the water density along the direction perpendicular to the surfaces. Due to the coulombic interaction between the superhydrophilic substrate and water molecules50, an interfacial water layer (<~0.6 nm in our case) with a density higher than that of the bulk water is formed on all the surfaces. It can be found that the sharpness of the peak of the interfacial water layer first decreases and then increases with the length of the perfluoroalkyl chain, suggesting the structure of the hydration layer displays a varying tendency of first decreasing and then increasing. The hydration layer induced on the F6-hGO surface possesses wider and more uniform density distribution. Some studies proved that moderately interfering with the hydration layer can increase the amount of interfacial water, thus achieving a stronger hydration capacity51. We also observed a change in the water amount in the hydration layer, that is, the value first increases and then decreases with the perfluoroalkyl chain length (Fig. 3e). The variation in hydration capacity is considered to be related to the interfacial hydration structure induced by the perfluoroalkyl chains with different lengths, which will be discussed in detail later. Further, differential scanning calorimetry was used to monitor the crystallization temperature and crystallization enthalpy of water (~10 mg) on the membrane surfaces to evaluate the amount of interfacial water (Supplementary Figs. 7,8). All the two values follow the order of F4-hGO > F8-hGO > F6-hGO, illustrating the amount of interfacial water in the order of F6-hGO > F8-hGO > F4-hGO, which is well consistent with the simulation results. It is believed that more water pinning on surfaces provides a stronger steric and energetic barrier24. These results explain the unexpected nonlinear relationship between the perfluoroalkyl chain length and the underwater oil contact angle.
We defined α as the angle between \(\vec{{{{{{\bf{u}}}}}}}\) (the opposite vector of the water dipole) and \(\vec{{{{{{\bf{z}}}}}}}\) (the normal vector of the surface) to estimate the spatial orientation of interfacial water to explore the underlying molecular-level details for the variation in the water amount of the hydration layer. We divide the hydration layers into two regions and compare the probability distributions of cosα in the two regions (Fig. 3f). It can be seen that most of the water bears the distributions of cosα centered ~−1, implying water mainly favor orienting with two O–H bonds directed downwards towards the surface in our models. With the presence of perfluoroalkyl chains, the orientation of the water molecules is perturbed due to the electrostatically dominated interactions between the water and the perfluoroalkyl chains52. This electrostatic interaction is sensitive to chain length and position, which was adequately discussed in detail in the previous work52. In our study, the water orientation distribution in regions I and II is more similar in the case of F6-hGO, which implies a more uniform hydration structure on the surface. The uniformity in hydration structure offers more available water interaction sites and thus reaches a larger amount of interfacial water and higher hydration capacity50. This nonlinear dependence of the hydration capacity to the perfluoroalkyl chain length reveals that an appropriate chain length exists for similar amphiphilic surfaces to exhibit the strongest hydration capacity.
Antifouling efficacy
Based on the regulation of interfacial interactions by the length of perfluoroalkyl chains, we tried to explore its effect on the antifouling efficacy. Hexadecane-in-water emulsion (average size = 291.1 nm, Supplementary Fig. 9) was selected as the target separation system to evaluate antifouling performances. All membranes bear high oil repellency (Rejection >98%, Supplementary Fig. 10) at high permeance (~620 L m−2 h−1 bar−1). The oil concentration of the filtrates is less than 20 ppm (Supplementary Fig. 11), which meets the discharge standard of most nations4. The fluxes varying with time during filtration and the corresponding indices are illustrated in Fig. 4a, b. The antifouling capability quantized by DRt first decreases and then increases with the chain length, which is consistent with variation in adhesive force (Fig. 2f). It can be significantly reduced by more than 50% by the hydrophobic chain engineering. Additionally, we investigated the effect of the density of the perfluoroalkyl chains on the antifouling properties to explore the optimal chemical composition of the proposed amphiphilic membrane surface (Supplementary Fig. 12). Our results indicate that the amphiphilic membrane with medium-length perfluoroalkyl chains (C6) prepared at the immersed FeCl3 solution concentration of 0.6 mM possesses the lowest DRt (6.8%) and the highest FRR (99.8%). Its DRt is dramatically reduced by nearly 90 and 80%, respectively, and its FRR is improved by 1.4 and 1.1 times, respectively, relative to those of the GO membrane (DRt = 60.0 %, FRR = 73.3%) and the hGO membrane (DRt = 31.8 %, FRR = 88.6%).
Compared with the currently reported GO-based membranes and polymeric membranes for oil-water separation, the F6-hGO membrane shows superior antifouling performance (Fig. 4c, d and Supplementary Tables 2,3). DRt of our membrane is far lower than that of the reported membranes, with the index generally of 40–60%. More importantly, as shown in Fig. 4d, most membranes achieve ultralow DRt at low initial fluxes. While the F6-hGO membrane can maintain its ultralow fouling tendency even at a relatively high initial flux of ~310 L m−2 h−1. This value exceeds most oil-water separation membranes, which confirms their robustness in resisting oil fouling and their advantage over state-of-the-art membranes. In addition, the membrane exhibits a comparable pure water flux as the initial one after multiple cycles of fouling with oils and cleaning with water (Fig. 4e). For the challenge of scaling, no significant flux decline was observed after operating the gypsum scaling experiment for 6 h (Supplementary Fig. 13). Besides, the F6-hGO membrane shows a promising opportunity in the antifouling treatment of various emulsions with high rejection (>98%, Supplementary Fig. 14) and low DRt (<10%, Fig. 4f).
The introduction and optimization of multiple antifouling mechanisms on the membrane surface account for excellent antifouling properties. The hydration barrier and steric repulsion of the hydrophilic PA coating resist the spread of oil droplets, making the oil contact the membrane surface with a small area53. The perfluoroalkyl chains with low surface energy endow the membrane surface with nonstick properties and fouling-release behavior27. Most importantly, in our case, the interfacial interactions of the proposed amphiphilic surface are regulated by the perfluoroalkyl chain length. There is an optimal chain length, namely C6, to endow the surfaces with the lowest oil adhesion. At this length, the interfacial water is oriented more uniformly, thereby forming a hydration layer with more water. This enables the surface to maintain the hydration capacity when introducing the perfluoroalkyl chains, thereby synergistically optimizing fouling resistance and release properties. Consequently, the proposed F6-hGO membrane harvests ultralow adhesion with oil droplets, allowing oil droplets to easily peel from the membrane surface instead of forming a filter cake layer and thus resulting in enhanced antifouling efficacy.
Discussion
In summary, we constructed an amphiphilic surface by sequentially assembling hydrophilic PA and hydrophobic perfluoroalkyl chains on a graphene oxide membrane and achieved molecular-scale regulation of its chemical structure and interfacial interactions by adjusting the density and length of the perfluoroalkyl chains. Our study demonstrates that the perfluoroalkyl chain length is one of the key factors affecting the antifouling ability, because it can tune the surface hydration structure, thus synergistically optimizing both fouling-resistance and fouling-release properties. We observed that the hydration capacity varies nonlinearly with the perfluoroalkyl chain length and proved that the medium-length perfluoroalkyl chains (C6) is optimal by providing a more uniform orientation of the interfacial water to hydrate more water on the surface. This hydrophobic chain engineering reduces the adhesive force of oil droplets by over 50%, thus achieving superior antifouling capability (DRt: <10%, FRR: ~100%) at even high permeance (~620 L m−2 h−1 bar−1). Our work provides guidance for the regulation of surface interactions. We anticipate that the microscopic understanding of interfacial interaction is also instructive to interfacial engineering in oil recovery, biomedicine, and nanofluidics.
Methods
Materials and chemicals
GO nanosheets were purchased from Nanjing XFNANO Materials Tech Co., Ltd. Polyacrylonitrile (PAN) membranes were provided from Lanjing Membrane Engineering Co. PA, iron chloride hexahydrate (FeCl3·6H2O), sodium dodecyl sulfonate, tetrachloromethane, n-hexane, and hexadecane were supplied from Tianjin heowns Biochemical Technology Co., Ltd. HFBA, PFHA, PFOA, NFDA, and diiodomethane were obtained from Shanghai Macklin Biochemical Co., Ltd. Vacuum pump oil was provided by Special Oil Factory. Corn oil was bought from COFCO Fulinmen Co., Ltd.
Preparation of the hGO membrane
Fe3+–PA complex was grown on GO nanosheets via the metal-organic coordination37. Typically, as described in Fig. 1a, 0.50 mg GO nanosheets and 49.50 mg PA were uniformly dispersed in 25 mL deionized water. After shaking at 150 rpm and 25 °C for 10 min, 5 mL 0.20 mM FeCl3 aqueous solution was added into the mixed solution of GO and PA and then shaken for 10 min to fabricate Fe3+–PA@GO nanosheets. Subsequently, 1800 μL of the above-resulting Fe3+–PA@GO nanosheet solution was ultrasonically dispersed in 100 mL of water. The hGO membrane was prepared via filtrating the Fe3+–PA@GO dispersion onto the PAN membranes.
Preparation of the F-hGO membranes
F-hGO membranes were fabricated by sequentially assembling Fe3+ and perfluorocarboxylic acids on the hGO membrane38. As shown in Fig. 1a, the hGO membrane was first immersed into 30 mL 0.60 mM FeCl3 aqueous solution and shaken for 10 min at 100 rpm and 25 °C, followed by washing with water. Afterward, the resulting membranes were sunk into the 30 mL ethanol solution of perfluorocarboxylic acids and shaken at 100 rpm and 25 °C for 10 min. The F-hGO membranes were obtained after washing with ethanol. The subscript of the membrane name indicates the number of C atoms in the molecular chain of perfluorocarboxylic acids, that is, F4-hGO, F6-hGO, F8-hGO, and F10-hGO represent the membranes assembled by HFBA, PFHA, PFOA, and NFDA, respectively. The concentration of the immersed FeCl3 solution, namely, 0.20, 0.40, 0.60, and 0.80 mM, was adjusted to control the density of the perfluorocarboxylic acids. The concentration of perfluorocarboxylic acids solution was set to an excessive concentration (2.00 mM) to achieve the adequate coordination of perfluorocarboxylic acids with Fe3+, according to the influence of the concentration of perfluorocarboxylic acids on the surface properties quantified by the water contact angle (Supplementary Fig. 1).
Molecular dynamics simulation
Molecular dynamics simulations with a simple model system were used to investigate the interfacial water on F-hGO membranes with perfluoroalkyl chains of different lengths. Supplementary Fig. 2 shows a typical box used in our simulations. There are 1000 water molecules on the substrate. The substrate is made up of a group of randomly arranged atoms with a density of 0.005 nm−3 (i.e., there are 259 substrate atoms in the simulation box). The substrate is negatively charged with the total charges Q = −10 e where e is the charge of an electron (we checked that this type of substrate is superhydrophilic). Na+ ions are added in the system to neutralize the system. 12 perfluorocarboxylic acid chains are anchored on the substrate with the C atom of the –COOH groups fixed at the top of the surface (i.e., at z = 0.5 nm in Supplementary Fig. 2). The perfluorocarboxylic acids are arranged in a hexagonal lattice with the distance between them d = 1 nm. The cases anchored by the perfluorocarboxylic acids of HFBA, PFHA, PFOA, and NFDA are named F4-hGO, F6-hGO, F8-hGO, and F10-hGO, respectively.
The SPC/E model was applied to the water molecules54. The SHAKE algorithm was used to maintain the rigidity of the water. The force field for the perfluoroalkyl chains were generated by LigParGen55. The model for Na+ ions was from ref. 56. The substrate atom was set to be the same as the O atom of H2O (except for the charges). Nonbonding pairwise interaction was given by
where \({\epsilon }_{{ij}}\) and \({\sigma }_{{ij}}\) are the energy and distance parameters, respectively, \({r}_{{ij}}\) is the distance between atoms \(i\) and \(j\), \({q}_{i}\) and \({q}_{j}\) are the atomic charge of atoms \(i\) and \(j\), \({\epsilon }_{0}\) is the vacuum permittivity. The Lennard-Jones (LJ) potentials were cut and shifted at 1.0 nm. The arithmetic mixing rule was applied for LJ potentials between different species. The electrostatic interaction was also cut at \(1.0\,{{{{{\rm{nm}}}}}}\) and the particle−particle particle−mesh (PPPM) with an accuracy of 10−4 was employed to calculate the long-range electrostatic interactions.
All simulations were carried out using the parallel molecular dynamics software package LAMMPS57. Periodic boundary conditions were imposed in all three directions. The velocity-Verlet algorithm with a time step of \(1\,{{{{{\rm{fs}}}}}}\) was used to integrate the equation of motion, and a Nosé–Hoover thermostat with a time constant of \(100\,{{{{{\rm{fs}}}}}}\) was used to maintain the temperature of the fluid at \(T=300\,{{{{{\rm{K}}}}}}\). During all simulations, all atoms of the substrates and the C atom of the –COOH groups were frozen at their initial positions. Each simulation was run for 2 ns for equilibrating and another 10 ns for producing.
Characterization
Characterization used in this work are provided in detail in the Supplementary Methods.
Data availability
All data supporting the findings of this study are available within the article and the Supplementary Information file, or available from the corresponding authors upon request. Source data are provided with this paper.
References
Wang, B., Liang, W., Guo, Z. & Liu, W. Biomimetic super-lyophobic and super-lyophilic materials applied for oil/water separation: a new strategy beyond nature. Chem. Soc. Rev. 44, 336–361 (2015).
Kota, A. K., Kwon, G., Choi, W., Mabry, J. M. & Tuteja, A. Hygro-responsive membranes for effective oil-water separation. Nat. Commun. 3, 1025 (2012).
Fakhru’l-Razi, A. et al. Review of technologies for oil and gas produced water treatment. J. Hazard Mater. 170, 530–551 (2009).
Tanudjaja, H. J., Hejase, C. A., Tarabara, V. V., Fane, A. G. & Chew, J. W. Membrane-based separation for oily wastewater: a practical perspective. Water Res. 156, 347–365 (2019).
Yang, C. et al. Fabrication of a PPS microporous membrane for efficient water-in-oil emulsion separation. Langmuir 34, 10580–10590 (2018).
Tao, M., Xue, L., Liu, F. & Jiang, L. An intelligent superwetting PVDF membrane showing switchable transport performance for oil/water separation. Adv. Mater. 26, 2943–2948 (2014).
Zhang, R. et al. Antifouling membranes for sustainable water purification: strategies and mechanisms. Chem. Soc. Rev. 45, 5888–5924 (2016).
Zhang, S. et al. Cupric phosphate nanosheets-wrapped inorganic membranes with superhydrophilic and outstanding anticrude oil-fouling property for oil/water separation. ACS Nano 12, 795–803 (2018).
He, M. et al. Reduced graphene oxide aerogel membranes fabricated through hydrogen bond mediation for highly efficient oil/water separation. J. Mater. Chem. A 7, 11468–11477 (2019).
Guan, J. et al. Engineering multi-pathway graphene oxide membranes toward ultrafast water purification. J. Membr. Sci. 638, 119706 (2021).
Liu, Y. et al. 2D heterostructure membranes with sunlight-driven self-cleaning ability for highly efficient oil-water separation. Adv. Funct. Mater. 28, 1706545 (2018).
Yang, C. et al. Ultrathin nanofiltration membrane assembled by polyethyleneimine-grafted graphene quantum dots. J. Membr. Sci. 642, 119944 (2022).
Dong, D. et al. Double‐defense design of super‐anti‐fouling membranes for oil/water emulsion separation. Adv. Funct. Mater. 32, 2113247 (2022).
Dhyani, A. et al. Design and applications of surfaces that control the accretion of matter. Science 373, eaba5010 (2021).
Rana, D. & Matsuura, T. Surface modifications for antifouling membranes. Chem. Rev. 110, 2448–2471 (2010).
Callow, J. A. & Callow, M. E. Trends in the development of environmentally friendly fouling-resistant marine coatings. Nat. Commun. 2, 244 (2011).
Han, N. et al. Amphiphilic cellulose for enhancing the antifouling and separation performances of poly (acrylonitrile-co-methyl acrylate) ultrafiltration membrane. J. Membr. Sci. 591, 117276 (2019).
Benda, J. et al. Studying the effect of pre-polymer composition and incorporation of surface-modifying amphiphilic additives on the fouling-release performance of amphiphilic siloxane-polyurethane coatings. ACS Appl Mater. Interfaces 14, 37229–37247 (2022).
Leonardi, A. K. & Ober, C. K. Polymer-based marine antifouling and fouling release surfaces: strategies for synthesis and modification. Annu Rev. Chem. Biomol. Eng. 10, 241–264 (2019).
Guo, H. & Ulbricht, M. Surface modification of polypropylene microfiltration membrane via entrapment of an amphiphilic alkyl oligoethyleneglycolether. J. Membr. Sci. 349, 312–320 (2010).
Kristalyn, C. B. et al. Surface structures of an amphiphilic tri-block copolymer in air and in water probed using sum frequency generation vibrational spectroscopy. Langmuir 26, 11337–11343 (2010).
Calabrese, D. R. et al. Amphiphilic oligopeptides grafted to PDMS-based diblock copolymers for use in antifouling and fouling release coatings. Polym. Adv. Technol. 26, 829–836 (2015).
Chen, S., Li, L., Zhao, C. & Zheng, J. Surface hydration: pPrinciples and applications toward low-fouling/nonfouling biomaterials. Polymer 51, 5283–5293 (2010).
Molino, P. J. et al. Hydration layer structure of biofouling-resistant nanoparticles. ACS Nano 12, 11610–11624 (2018).
Long, M. et al. Electrostatic enhanced surface segregation approach to self-cleaning and antifouling membranes for efficient molecular separation. J. Membr. Sci. 638, 119689 (2021).
Koc, J. et al. Low-fouling thin hydrogel coatings made of photo-cross-linked polyzwitterions. Langmuir 35, 1552–1562 (2019).
Lejars, M., Margaillan, A. & Bressy, C. Fouling release coatings: a nontoxic alternative to biocidal antifouling coatings. Chem. Rev. 112, 4347–4390 (2012).
Galhenage, T. P. et al. Fouling-release performance of silicone oil-modified siloxane-polyurethane coatings. ACS Appl Mater. Interfaces 8, 29025–29036 (2016).
Kumar, M. et al. Preparation and characterization of low fouling novel hybrid ultrafiltration membranes based on the blends of GO−TiO2 nanocomposite and polysulfone for humic acid removal. J. Membr. Sci. 506, 38–49 (2016).
Galli, G. & Martinelli, E. Amphiphilic polymer platforms: surface engineering of films for marine antibiofouling. Macromol. Rapid Comm. 38, 1600704 (2017).
Stammitti-Scarpone, A. & Acosta, E. J. Solid-liquid-liquid wettability and its prediction with surface free energy models. Adv. Colloid Interface Sci. 264, 28–46 (2019).
Jung, Y. C. & Bhushan, B. Wetting behavior of water and oil droplets in three-phase interfaces for hydrophobicity/philicity and oleophobicity/philicity. Langmuir 25, 14165–14173 (2009).
Baxamusa, S. H. & Gleason, K. K. Random copolymer films with molecular-scale compositional heterogeneities that interfere with protein adsorption. Adv. Funct. Mater. 19, 3489–3496 (2009).
Hederos, M., Konradsson, P. & Liedberg, B. Synthesis and self-assembly of galactose-terminated alkanethiols and their ability to resist proteins. Langmuir 21, 2971–2980 (2005).
Gudipati, C. S., Finlay, J. A., Callow, J. A., Callow, M. E. & Wooley, K. L. The antifouling and fouling-release perfomance of hyperbranched fluoropolymer (HBFP)−poly(ethylene glycol) (PEG) composite coatings evaluated by adsorption of biomacromolecules and the green fouling alga ulva. Langmuir 21, 3044–3053 (2005).
Chi, Y., Xu, S., Xu, X., Cao, Y. & Dong, J. Studies of relationship between polymer structure and hydration environment in amphiphilic polytartaramides. J. Polym. Sci. B PolymPhys 55, 138–145 (2017).
You, X. et al. Metal-coordinated sub-10 nm membranes for water purification. Nat. Commun. 10, 4160 (2019).
Yu, Q. et al. Ultrathin fluorinated self-cleaning membranes via coordination-driven metal-bridging assembly for water purification. J. Mater. Chem. A 8, 4505–4514 (2020).
Song, X. et al. A phytic acid induced super-amphiphilic multifunctional 3D graphene-based foam. Angew. Chem. Int. Ed. Engl. 55, 3936–3941 (2016).
Yang, C. et al. Design of a Janus F-TiO2@PPS porous membrane with asymmetric wettability for switchable oil/water separation. ACS Appl Mater. Interfaces 11, 22408–22418 (2019).
Extrand, C. W. Designing for optimum liquid repellency. Langmuir 22, 1711–1714 (2006).
de Gennes, P. G. Wetting: statics and dynamics. Rev. Mod. Phys. 57, 827–863 (1985).
Liu, M., Wang, S., Wei, Z., Song, Y. & Jiang, L. Bioinspired design of a superoleophobic and low adhesive water/solid interface. Adv. Mater. 21, 665–669 (2009).
Wenzel, R. N. Surface roughness and contact angle. J. Phys. Colloid Chem. 53, 1466–1467 (1949).
Trinavee, K., Gunda, N. S. K. & Mitra, S. K. Anomalous wetting of underliquid systems: oil drops in water and water drops in oil. Langmuir 34, 11695–11705 (2018).
Seveno, D., Blake, T. D., Goossens, S. & De Coninck, J. Predicting the wetting dynamics of a two-liquid system. Langmuir 27, 14958–14967 (2011).
Dargaville, B. L. & Hutmacher, D. W. Water as the often neglected medium at the interface between materials and biology. Nat. Commun. 13, 4222 (2022).
Chen, Q. et al. Impact of antifouling PEG layer on the performance of functional peptides in regulating cell behaviors. J. Am. Chem. Soc. 141, 16772–16780 (2019).
Du, Z. et al. Adsorption behavior and mechanism of perfluorinated compounds on various adsorbents–a review. J. Hazard Mater. 274, 443–454 (2014).
Li, C. Y. et al. In situ probing electrified interfacial water structures at atomically flat surfaces. Nat. Mater. 18, 697–701 (2019).
Huang, K. et al. Cation-controlled wetting properties of vermiculite membranes and its promise for fouling resistant oil-water separation. Nat. Commun. 11, 1097 (2020).
Robalo, J. R., Mendes de Oliveira, D., Ben-Amotz, D. & Vila Verde, A. Influence of methylene fluorination and chain length on the hydration shell structure and thermodynamics of linear diols. J. Phys. Chem. B 125, 13552–13564 (2021).
Li, N. et al. Superamphiphilic TiO2 composite surface for protein antifouling. Adv. Mater. 33, 2003559 (2021).
Berendsen, H. J. C., Grigera, J. R. & Straatsma, T. P. The missing term in effective pair potentials. J. Phys. Chem. 91, 6269–6271 (1987).
Dodda, L. S., Cabeza de Vaca, I., Tirado-Rives, J. & Jorgensen, W. L. LigParGen web server: an automatic OPLS-AA parameter generator for organic ligands. Nucleic Acids Res. 45, W331–W336 (2017).
Joung, I. S. & Cheatham, T. E. Determination of alkali and halide monovalent ion parameters for use in explicitly solvated biomolecular simulations. J. Phys. Chem. B 112, 9020–9041 (2008).
Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).
Acknowledgements
This work is financially supported by the National Natural Science Foundation of China, Grant No. 21961142013 (Z.J.), 21878215 (H.W.), Key Research and Development Program of Zhejiang Province, Grant No. 2021C03173 (Z.J.), and the Haihe Laboratory of Sustainable Chemical Transformations for financial supports. The authors also appreciate Dr. Mingrui He from the Harbin Institute of Technology for his help with the AFM test. Y.L. sincerely appreciates Prof. Suojiang Zhang (IPE, CAS) for his careful aca- demic guidance and great support.
Author information
Authors and Affiliations
Contributions
H.W., Z.J., and C.Y. conceived the idea and designed the experiment. C.Y., M.L., S.Z., J.Y., and C.D. performed the experiment. K.Z., Z.Y., and Y.Z. measured the separation performances. R.Z provided constructive suggestions for results and discussion. Y.L. did molecular dynamics simulations. All authors participated in the discussion.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Yusuf Olabode Raji and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Source data
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Yang, C., Long, M., Ding, C. et al. Antifouling graphene oxide membranes for oil-water separation via hydrophobic chain engineering. Nat Commun 13, 7334 (2022). https://doi.org/10.1038/s41467-022-35105-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-35105-8
This article is cited by
-
Recent advances in membrane technologies applied in oil–water separation
Discover Nano (2024)
-
Durable Janus membrane with on-demand mode switching fabricated by femtosecond laser
Nature Communications (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.