Abstract
Origami crease patterns have inspired the design of reconfigurable materials that can transform their shape and properties through folding. Unfortunately, most designs cannot provide loadbearing capacity, and those that can, do so in certain directions but collapse along the direction of deployment, limiting their use as structural materials. Here, we merge notions of kirigami and origami to introduce a rigidly foldable class of cellular metamaterials that can flatfold and lock into several states that are stiff across multiple directions, including the deployment direction. Our metamaterials rigidly fold with one degree of freedom and can reconfigure into several flatfoldable and spatiallylockable folding paths due to face contact. Locking under compression yields topology and symmetry changes that impart multidirectional stiffness. Additionally, folding paths and mixedmode configurations can be activated in situ to modulate their properties. Their loadbearing capacity, flatfoldability, and reprogrammability can be harnessed for deployable structures, reconfigurable robots, and lowvolume packaging.
Similar content being viewed by others
Introduction
Origami and kirigami, the arts of folding and cutting paper, have inspired the development of a plethora of scaleinvariant reconfigurable materials and structures that can deploy either spatially or inplane^{1,2}. These concepts have been implemented across disciplines, from mechanical memories^{3}, robotic actuators^{4,5,6,7,8}, thermally tunable structures^{9,10}, multistable devices^{11,12,13,14,15}, complex 3D geometries^{16,17}, and programmable surfaces^{18,19,20,21} to flexible electronics^{22,23}. Origami crease and kirigami cut patterns also proffer mechanical metamaterial designs with distinct geometric and mechanical properties, such as reconfigurability^{24,25}, flatfoldability^{25,26,27,28,29,30}, and bistable auxeticity^{13,31} among others.
Of recent interest are in situ reprogrammable folding metamaterials^{32,33,34,35,36,37,38} which harness an inherent coupling between the folding pattern and the geometry of motion. Here, rigidfoldability, flatfoldability, and loadbearing are distinct characteristics that can describe the modality of folding and the realization of certain functional performances. Rigidfoldability indicates that folding is solely controlled by the crease lines acting as rotational hinges, and not the deformation of the rigid panels^{39}. Alternatively, in nonrigidfoldable patterns, both panel compliance and crease lines govern folding. Flatfoldability is a property that imparts a high level of reconfigurability by allowing spatial transformations leading into one or more flat states. Loadbearing in a foldable metamaterial simply denotes the capacity to offer structural resistance to a load applied in any given configuration across multiple directions.
Existing origamiinspired metamaterials offer a certain level of programmability, yet they are unable to attain concurrently rigidfoldability, flatfoldability, and loadbearing capacity along the deployment direction. One reason stems from the kinematics of their unit cell, which controls the way the crease pattern folds. Foldable metamaterials using the Miuraori^{27,28,29}, interleaved^{30}, and tubular^{13,26,40} patterns as well as cylindrical structures based on waterbomb patterns^{35}, and other unit cells, utilize crease geometry that exhibits some but not all of the properties defined above. For example, rigidfoldable material systems with multiple degrees of freedom (DoFs)^{24,25}, are either floppy or require precise control of the folding sequence, a characteristic that severely limits their capacity to withstand multidirectional loads. Alternatively, nonflatfoldable concepts^{32,35} have limited reconfigurability, making their size and volume large, and most existing concepts utilizing structural instability^{1,6,11,34,35} or the Kreseling pattern^{33,41} to achieve reconfigurability are nonrigidfoldable. To fold, they must overcome a large energy barrier that bends and stretches their panels, thus sacrificing loadbearing capacity. On the other hand, foldable patterns that offer some load resistance can do so in certain directions only and mainly loses stiffness in the deployment direction^{13,24,25,26,38,40,42}. This aspect can be problematic in applications where during service the load direction is uncertain, hence potentially reverting a stiff into a floppy configuration.
From the current state of the art, an interesting question arises: Can a crease pattern be conceived to reconcile the conflicting nature of rigidfoldability, flatfoldability, and loadbearing capacity in multiple directions, including that of deployment? This paper presents a framework for designing a topological class of rigidly flatfoldable metamaterials that are reprogrammable in situ to reconfigure along multiple directions, some flatfoldable and others lockable, where the latter is multidirectionally stiff even along the deployment direction. Our basis combines origami and kirigami concepts to introduce a crease pattern that is built cellular in its flat configuration, and subsequently stacked with the minimum number of layers to steer folding along one trajectory. To imbue reconfigurability, excisions are introduced in a crease pattern so as to relax the deformation constraints enacted by the rigidity of the faces of the parent origami, and to enable face contact within their intracellular spaces. Besides loadbearing capacity, our concept offers additional hallmarks including topology and symmetry switching that altogether enlarge the degree of in situ programmability. Finally, a simple yet effective fabrication process that can be easily automated is presented to impart threedimensionality in the flat configuration.
Results
Geometry of reconfigurable unit chain
To generate a rigidlyfoldable unit chain that is flatfoldable and can lock into a stiff state upon face contact, we start from a primitive network of bars connected in a planar loop. The network is a planar Nbar linkage that forms a regular N evensided polygon. Figure 1a shows the generative process exemplified with a network of four bars, each of length a and enclosing a square void. Extruding each bar outward to the length b (red arrow) in the xy plane and at a given angle ϕ \(\in \left[\frac{\pi }{N},\pi \frac{\pi }{N}\right]\) yields four parallelograms, which we connect using isosceles triangles with a vertex angle \(\lambda =\frac{2\pi }{N}\). By prescribing the folding profiles (dash lines) at each boundary between interfacing panels, we obtain a planar assembly of rigid surfaces that spatially fold along their connecting valley (V) and mountain (M) folding lines. The conceptual process can be thought as complementary to the fabrication steps (Supplementary Movie 1), where the void is first excised from a planar sheet of paper (kirigamicuts), and then folded along prescribed dash lines (origami folds), thereby generating a hybrid architecture.
The fold lines of both V and M panels enable the system to act as a kinematic chain, in short, “unit chain”. We define its configurational changes (Fig. 1a) using m independent dihedral angles θ_{1}, θ_{2}, …, \({\theta }_{m}\). Each dihedral angle specifies the convex angle between the triangular panel and its adjacent quad panel (Fig. 1a), and m denotes the mobility or nontrivial (term hereafter dropped) DoFs excluding rigidbody motions. We also assume the mountain and valley fold lines are constrained to remain on two parallel planes during folding. Explained later, this strategy is enforced through unit chain stacking, and it enables folding with a single DoF. In this case, the outofplane rise, h, is expressed as a function of three geometric parameters by:
During folding, \({\theta }_{1}\) decreases and the unit chain can reach a lock state, denoted with the superscript “^{L}”, where contact between panels forbids any further motion (right sketch in Fig. 1a). In a lock state, the acute dihedral angles are given by:
The generative process illustrated in Fig. 1a for a unit chain with a square primitive void can be abstracted to other primitives, i.e., regular N evensided polygons, by merely varying N. This gives rise to a class of planar unit chains that spatially reconfigure within the voids and lock upon panel contact. Figure 1b illustrates five of them, where the first three rows show their initial fully developed state, the partially folded states, and one possible lock configuration. The last two rows depict their most compact inplane tessellation and their outofplane stacking in paperboard specimens, where each layer is mirrored with respect to the xy plane and bonded at the triangular panels of the adjacent layers (above and below).
To investigate the kinematics of our unit chains, we first introduce the dimensionless extrusion factor \(\bar{b}=b/a\) and adopt the notation \({{{{{{\rm{N}}}}}}}_{N}(\bar{b},\phi )\) to discriminate between unit chains. \({{{{{{\rm{N}}}}}}}_{N}\) refers to the generic class of unit chains, where \(\bar{b}\) and \(\phi\) can assume any values. For the demonstrative purpose, we mainly focus on a subset (Fig. 1b), namely the subclass defined by \(\bar{b}=1\) and \(\phi =\pi /3\), i.e., \({{{{{{\rm{N}}}}}}}_{N}(1,\pi /3)\) denoted hereafter as \({\widehat{{{{{{\rm{N}}}}}}}}_{N}\) for simplicity, with N = 4, 6, 8, 10 and 12, and we refer to the more general case \({{{{{{\rm{N}}}}}}}_{N}\) whenever our analysis become independent of the two geometric parameters \(\bar{b}\) and \(\phi\).
Kinematic model
We study the unit chain kinematics (Fig. 1a) through a set of assumptions. First, the panels are considered as infinitely rigid plates and the fold lines as rotational hinges. Second, to ease the formulation of the kinematic constraints, we replace the unit chain with a triangulated network of inextensible elements connected through pin joints (Supplementary Fig. 1). Third, the edges of the triangular panels are modeled as bars, and quad panels are replaced with two triangles satisfying the planarity condition of their interplanar angles over the entire folding process (Supplementary Fig. 1d). By modeling our unit chain as a pinjointed network of inextensible bars, we now examine its DoFs, and types of kinematic motion.
Number of degrees of freedom
The unit chain mobility is formulated through the rigidity matrix R pertinent to its structural assembly. The number of DoFs, m, for a pinjointed triangulated network is given by \(m=3j{n}_{K}r\), where j is the total number of joints, \({n}_{K}\) the number of external kinematic constraints, and r the rank of R (see Supplementary Discussion “Kinematic analysis”). For our unit chain, m also represents the number of independent dihedral angles. For the unit chain \({\widehat{{{{{{\rm{N}}}}}}}}_{4}\) (Fig. 1a), m = 5, i.e., five mechanisms are possible. m can be reduced to 1 if the mountain and valley fold lines are constrained to remain on two parallel planes during folding. The specific values and relationships the dihedral angles assume define distinct types of motion, as described below.
Kinematic paths
There are specific trajectories our unit chain can follow during motion. Defined as kinematic paths, each of them can be uniquely defined by a relation between the independent dihedral angles. For example, the equality of dihedral angles, i.e., θ_{1} = θ_{2}, represents the type of motion shown in Fig. 1a, whereas θ_{1} = \(\pi\)  θ_{2} describes another one.
Unit stacking as a pathway to reduce mobility
If the triangular panels shown in Fig. 1a do not remain parallel during folding, our unit chain is endowed with manifold DoFs, which for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}\) is five. Having too many DoFs can be problematic. The unit chain can act as a multiDoF mechanism with a tendency to be floppy such that folding cannot be easily controlled. One way to prune DoFs is to act along the third direction (z), and stack layers of unit chains one on top of the other. Figure 2a shows this strategy applied to \({\widehat{{{{{{\rm{N}}}}}}}}_{6}\). The mountain facets of the triangular panels of the top unit are bonded to the valley facets of the adjacent unit (below). By stacking and bonding three unit chains, the mountain and valley triangular panels lie in parallel planes. If constructed from a material with sufficiently high elastic modulus, the nonnegligible thickness of the triangular panels restrict the relative rotation range of two connected quad panels. This allows only equal and opposite rotations, which satisfy kinematic compatibility, and avoid encountering the energy barrier of the bending or stretching of the panels (Supplementary Discussion “Additional constraints” and Supplementary Fig. 2).
The strategy above is simple yet effective. Not only does it turn off DoFs, but also provides robust reconfiguration along a single folding path. Having now layers of unit chains, we can denote a generic multilayered N evensided unit chain with n stacking layers by \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\). Through a rigidity analysis of \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\), we assess the role of layer stacking, n, on the DoFs (Supplementary Discussion “Kinematic analysis”). The outcome of this analysis is shown in Fig. 2b, where θ_{i} ≠ \(\pi\)/2 (i = 1, 2, 3… m) is assumed, and θ_{i} = \(\pi\)/2 refers to the kinematic bifurcation. From the plot, we gather that the DoFs of single layer unit chains increase linearly with N through the relation m = 2N – 3 which reduces to m = 1 if multiple layers are stacked, thus enabling reconfigurability along one single path. The minimum number of layers, \(\bar{n}\), necessary to trim m to 1 depends on the unit chain primitive. Figure 2b shows that for unit chains \({{{{{{\rm{N}}}}}}}_{4}\) and \({{{{{{\rm{N}}}}}}}_{6}\), \(\bar{n}\) = 3, whereas for \({{{{{{\rm{N}}}}}}}_{N > 6}\), \(\bar{n}\) = 5. With a focus on multilayered units with a single DoF, denoted by \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\), we now investigate their behavior at the instant of kinematic bifurcation and postbifurcation.
Kinematic bifurcation: emergence of lock and flatfold modes
In the early stage of folding, our \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) chain can travel along one route governed by \(\bar{n}\). However, as soon as it reaches a configuration where all its dihedral angles are \(\pi\)/2, i.e., kinematic bifurcation, the DoFs instantaneously grow, and multiple kinematic paths become active (Fig. 2a, c). We classify the postbifurcation modes into either twodimensional (2D) flatfoldable, or threedimensional (3D) lockable (Fig. 2c). Flatfoldable modes are fully flat patterns that are distinct from the initial state. Lockable modes describe 3D states with contact between adjacent panels that impart compressive stiffness (Supplementary Movies 2 and 3).
We can show (Methods) that our singleDoF multilayered unit chains possess only two types of dihedral angle pairs (Fig. 2a, d), acute \({{{{{\mathscr{A}}}}}}\) and obtuse \({{{{{\mathscr{O}}}}}}\), obeying the relation \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{+}}}}}}{{{{{\mathscr{O}}}}}}=\pi\) during the entire range of motion. A given sequence with angle pairs, e.g., two \({{{{{\mathscr{A}}}}}}\)s and one \({{{{{\mathscr{O}}}}}}\) depicted in Fig. 2d, can be simply denoted by the series of angle pairs, e.g.,\(\,{{{{{\mathscr{A}}}}}}{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), and in compact form with the power indicating the repeated pairs, e.g., \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\). This notation allows discriminating between kinematic modes that emerge at bifurcation. Given the modes defined by a repeating sequence of \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), such as \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}{{{{{\mathscr{\ldots }}}}}}\) (or simply \({\overline{{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}}\)), cannot be tessellated inplane, we denote them as irregular modes as opposed to the regular ones which are tileable inplane (Methods).
With the above, we systematically characterize the regular modes of a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) and determine the total number of possible reconfiguration modes. We use the Pólya enumeration theorem of combinatorics (Supplementary Discussion “Pólya enumeration theorem”) to (i) count the regular modes and then (ii) define their kind. The problem of finding all independent regular modes of a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) unit can be treated as the classical necklace problem. The goal is to reconstruct the colored pattern of a necklace of several beads, each colored either in white or black (\({{{{{\mathscr{A}}}}}}\) or \({{{{{\mathscr{O}}}}}}\)), from the knowledge of a limited set of information (Methods). By using a predictorcorrector type incremental method (Supplementary Discussion “Kinematic analysis”), we can now visualize the postbifurcation kinematic paths of \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{4}\), \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{4}\), \({\widehat{{{{{{\rm{N}}}}}}}}_{8}{{{{{{\rm{n}}}}}}}_{5}\) and \({\widehat{{{{{{\rm{N}}}}}}}}_{10}{{{{{{\rm{n}}}}}}}_{5}\) as shown respectively in Supplementary Movies 4–7.
To understand the relation between the total number of postbifurcation modes and the sides of the unit chain primitive N, Fig. 2e plots the total number of lockable modes c^{L} and flatfoldable modes c^{F} versus N. The best curve fits are included to provide phenomenological closedform relations that characterize folding paths and differentiate lockable modes (\({c}^{L}=0.21{{\exp }}(0.3N)\)) from flatfoldable modes (\({c}^{F}=0.54{{\exp }}(0.16N)\)) as a function of N for a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\). The results show that the number of regular modes grows exponentially, hence providing a rich platform to program lockable paths (Supplementary Table 1).
Symmetry and topology
From a single multilayered unit chain, we now turn to its periodic and multilayered tessellation forming a material system. Multilayered unit chains are connected to follow a tessellation pattern (Supplementary Discussion “Tessellations”) that replicates a crystallographic arrangement of atoms. Figure 3 shows the top view of representative patterns for N = 4, 6, 8, and 10. While several others exist, here we focus on tessellations with the most compact pattern. The goal is to show that upon folding along a given path our material systems undergo switches in symmetry and apparent topology, both hallmarks of in situ programmability.
Notions of crystallography become handy to study changes in symmetry. Each pattern is formed by tessellating inplane a representative unit (red boundaries in Fig. 3) defined by the periodic vectors. Upon reconfiguration, the material system at bifurcation can access a new kinematic path that causes the smooth transition of certain dihedral angle pairs from \({{{{{\mathscr{A}}}}}}\) to \({{{{{\mathscr{O}}}}}}\); the result is a break in symmetry. This phenomenon is visualized by the patterns that followed those in the first column of Fig. 3, each denoted by their crystallographic point group and Schoenflies symbol. A variation in the lattice point groups translates into a change of the elastic constants defining the elastic tensor; the symmetry shift endows the material system with another set of elastic properties. For example, the lattice made of \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) (first row of Fig. 3) is shown in one of its lock modes, \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), in the second column. In this mode, \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) has \({C}_{2h}\) symmetry, i.e., a twofold rotational symmetry, and its elastic compliance matrix contains 13 elastic constants defining a monoclinic behavior. Upon switching to lock mode \({{{{{{\mathscr{A}}}}}}}^{2}\) (third column), its symmetry changes to \({C}_{4h}\), a fourfold rotational symmetry, resulting in an elastic compliance matrix with seven independent constants.
Besides symmetry, another aspect enabling in situ programmability is the apparent change of topology undergone after bifurcation. Here topology is defined by connectivity through Z_{f}, the number of faces that meet at an edge, which is equivalent to a foldline as opposed to a cutedge, and Z_{e}, the number of edges meeting at a vertex. The values of Z_{e} and Z_{f} are calculated for the corresponding spatial lattice upon the assumption that in the lock state coincident edges and vertices form a single edge and a single vertex (values on top of each configuration in Fig. 3). A change in Z_{e} and Z_{f} denotes topology differentiation, whereas topology is invariant to other geometric parameters, such as the length of the primitive void. Results show an increase in connectivity values from the partially folded state to the lock state (see also Supplementary Discussion “Rigidity”). A break in topology impacts the deformation mode of the panels, which transition from bending to stretching^{43}, as shown later. The versatility to impart topological changes by traveling across a kinematic bifurcation can be used not only to tune the mechanical and physical properties in situ (see also Supplementary Discussion “Geometric mechanics of representative unit cell (RUC)”, “Relative density” and “Poisson’s ratio”), but also to switch the mechanism of deformation.
Energy landscape
Prior to bifurcation, our multilayered system \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) folds with one DoF through the application of inplane forces. At the point of kinematic bifurcation, however, multiple kinematic paths become accessible (Supplementary Movie 3). The entry into a specific path depends on the interplay between the components of the compressive forces, applied in its plane at the bifurcation instant. To study their role, we examine a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\) (with \(n\ge \bar{n}\)) biaxially and uniformly compressed and investigate the energy landscape of each kinematic path. The goal is to find the path and pertinent mode with the lowest energy level.
To formulate the total energy of \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\) we assume infinitely rigid panels and frictionless rotational springs (hinges) of uniform stiffness per unit length, k. We consider our unloaded system in mode \({{{{{{\mathscr{O}}}}}}}^{N/2}\), with all dihedral angle pairs being obtuse; this is the zeroenergy state of the system denoted by \({\theta }^{0}\) specifying a configuration that is either flat or partially folded due to the presence of residual stresses induced by manufacturing. \({\theta }^{L}\), on the other hand, is the acute dihedral angle of the lock unit. We assume \({\theta }^{0} \; > \; \frac{\pi }{2}\), a condition implying that upon the application of an outofplane load (zdirection in Fig. 1a), our system can only fold from its zeroenergy state to its fully developed configuration.
Modephase diagram: the role of inplane confinement
We consider a pair of compressive inplane forces, f_{x} and f_{y}, applied uniformly, quasistatically, and oriented along the principal directions x and y (Fig. 1a). We define the biaxiality ratio \({r}_{B}={f}_{y}/{f}_{x}\) with \({f}_{y}\in \left[0,\infty\right)\), \({f}_{x}\in \left(0,\infty \right)\) and \({r}_{B}\in \left[{{{{\mathrm{0,1}}}}}\right]\) to discriminate between the relative magnitude of the applied forces, and derive an expression of the total energy as a function of the applied forces and the dihedral angle, i.e., \(\varPi =\varPi (\theta ,{f}_{x},{f}_{y})\) or \(\varPi =\varPi (\theta ,{f}_{x},{r}_{B})\) (Supplementary Discussion “Energy analysis”).
Two representative systems \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) and \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{n}\) (with \(n\ge \bar{n}\) and geometric parameter \(\bar{b}=\frac{b}{a}=1\)) are examined. Their energy landscapes can be mapped into modephase diagrams (Methods) and their application showcased in demonstrative scenarios defined by families of applied inplane forces. Each family is specified by \((f_{x},r_{B})\) where r_{B} is maintained constant over the entire loading history. We consider two load families. The first is \((f_{x},r_{B}=1/3)\), where \({f}_{x}\) and \({f}_{y}\) can be proportionally scaled to respect the one third ratio; the (dimensionless) total energy landscape of one specific case (\({f}_{x}=1,r_{B}=1/3\)) of that family is shown in Fig. 4a by the blue curve for a system with n = 3 and θ^{0} = \(\pi\). In Fig. 4b, \((f_{x},r_{B}=1/3)\) is shown by the blue loadpath ABCD crossing three domains. In the lightyellow region, an increase of the force magnitudes from A to B is not sufficient to reconfigure our system, which remains flat (θ = \(\pi\)) in its fully developed state. Once the load magnitude reaches the first domain boundary (black dash line), point B, the system starts to fold along the only kinematic path (yellow region) up to bifurcation (black solid line), point C. Immediately after bifurcation, the system can in principle access two modes (\({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) and \({{{{{{\mathscr{A}}}}}}}^{2}\) branches in Fig. 4a), yet it enters \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) due to the lower energy it requires for activation. After entering in mode \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), the system momentarily continues to reconfigure until it locks at point D (Fig. 4a, b). At this stage regardless of the magnitude of f_{x} and f_{y} satisfying \({r}_{B}=1/3\), no further folding is possible as the panels have come into contact, thus imparting stiffness (Supplementary Movies 8,9).
The second family of inplane forces is \(({f}_{x},r_{B}=1)\), shown in Fig. 4b by the green loadpath AEFG. The total energy landscape of one specific load case \(({f}_{x}=1,r_{B}=1)\) for that family is illustrated in Fig. 4a (green). Similar to ABCD, the system remains in its flat configuration for a load increase from A to E. A further increase of the inplane confinement makes the system exit the initial region (black dash line) and gradually deform up to the bifurcation point F (second boundary threshold). Thereafter, it enters the lowest energy branch (\({{{{{{\mathscr{A}}}}}}}^{2}\) in Fig. 4a and light blue region in Fig. 4b) with an energetically stable state that occurs slightly prior to its lock state, point G. An additional load increase makes the system fold until it reaches its lock state (dark blue region in Fig. 4b) (Supplementary Movie 10).
The map in Fig. 4b shows that the only way for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) to access mode \({{{{{{\mathscr{A}}}}}}}^{2}\) is with \({r}_{B}=1\); in contrast, any other values of \({r}_{B}\) would bring the system to lock in mode \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\). This is an outcome that is distinctive to \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\), and does not necessarily translate to other systems. For instance, for \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{n}\), more kinematic paths are available, i.e., multiple ranges of \({r}_{B}\) exist to switch between modes. Figure 4c shows the modephase diagram of \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{n}\). Here, \({r}_{B}=0.74\) (diagonal in the light green region) defines a condition for which the system, initially in \({{{{{{\mathscr{O}}}}}}}^{3}\) mode, enters \({{{{{{\mathscr{A}}}}}}}^{3}\) mode immediately after bifurcation. For \({r}_{B} \; > \; 0.74\), the unit enters its lockable mode \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\) (dark green), whereas for \({r}_{B} \; < \; 0.74\), it accesses its flatfoldable mode \({{{{{{\mathscr{O}}}}}}}^{2}{{{{{\mathscr{A}}}}}}\) (brown region). Once entered in the postbifurcation mode with minimum energy, the system remains in that region until it locks. At this stage, the system is rigid under compression and can no longer reconfigure; no other regions beyond the red boundaries (Fig. 4b, c) are accessible. The modephase diagrams depend on the geometric parameters \(\bar{b}\) and ϕ only, the former being a nonlinear scale factor, and the latter governing the slope of the lines separating moderegions and the loading path (biaxiality ratio r_{B}) of a given mode (Supplementary Discussion “Energy analysis”). They enable the choice of inplane confining forces to attain desired postbifurcation modes. The role of outofplane confinement is examined in the following.
Lock state domains governed by outofplane force
Our goal is to determine the magnitude of an outofplane (z axis in Fig. 1a) compressive force f_{o} necessary to bring and keep the system in its lock state without the need of inplane confining forces.
For the demonstrative purpose, we examine \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) folding in mode \({{{{{{\mathscr{A}}}}}}}^{2}\). Figure 4d schematically shows its energy curves (Eq. (3) in Methods) for three representing values of the outofplane load normalized by the lock load, i.e., \(\bar{f}={f}_{o}/{f}^{L}\) where the lock load \({f}^{L}\) is the minimum outofplane force at the lock state (Methods). The interplay between \({f}_{o}\) and \({f}^{L}\) gives rise to three domains:
Region I (light brown): \(\bar{f} < 1\). Since \({f}_{o}\)<\({f}^{L}\), the system cannot access the lock state from a given configuration.
Region IIa (yellow): \(\bar{f} > 1\), \(\frac{\partial \varPi }{\partial \theta } < 0\) and \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} < 0\) – recall \(\varPi\) is expressed as a function of (\(\pi \theta\)). Partially folded at a given dihedral angle, the system is prone to fold back to its fully developed (flat) state.
Region IIb (blue): \(\bar{f} > 1\), \(\frac{\partial \varPi }{\partial \theta } > 0\), and \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} < 0\). This is the lockable domain (Methods).
If inplane forces lead the system to reach one unstable dihedral angle (blue point in Fig. 4d), a small perturbation prompts the system to naturally abandon it. Once the inplane forces succeed in generating dihedral angles smaller than those described by Eq. (5) in Methods, our system can access the descending path in the lockable domain. Here spontaneous folding towards the lock state occurs, and inplane forces are no longer needed. The magnitude of the outofplane action (\({f}_{o}\)>\({f}^{L}\)) enables lifting the inplane confinement. Once in the lockable domain, e.g., orange point, the system is drawn to fold towards a stable configuration of equilibrium until it arrests due to panel contact (black point).
The analysis above has revealed the interplay between inplane and outofplane confinement. The former can be imparted through the biaxiality ratio to program and steer the reconfiguration mode (either lockable or flatfoldable) during the folding process. The latter, in particular its magnitude (\({f}_{o}\)>\({f}^{L}\)) and the threshold value of the dihedral angle, i.e., the lockable domain boundary, set the conditions for spontaneous folding into the lock state without the need for inplane compression. Once contact is attained, our system becomes a stiff structure (see Methods “Rigidity under compression” and Supplementary Discussion “Rigidity”), and it is ready to sustain compressive loads exerted in all three directions, as described below.
Mechanical performance and programmability
We examine a set of representative proofofconcept specimens made of cellulose paperboard in their lock states under compression. The purpose is to demonstrate their capacity to achieve in situ distinct mechanical properties by uniform and nonuniform application of confining forces. Experimentally investigated are Young’s modulus E^{*} (the tangent of the compressive stressstrain curve in the first loading cycle assessing panel engagement as opposed to initial slippage) and the yield strength σ^{*} (the first peak stress before densification); relative density and Poisson’s ratio are given in the closed form in Supplementary Discussion “Relative density” and “Poisson’s ratio”. We avoid finitesize effects by tessellating inplane \({l}_{{{{{{{\bf{e}}}}}}}_{1}}={l}_{{{{{{{\bf{e}}}}}}}_{2}}=7\) unitcells along the base vectors {e_{1}, e_{2}} and stacking n = 6 layers (see Fig. 5a and Supplementary Discussion “Experiments”). A generic tessellated system is thus denoted by \({\widehat{{{{{{\rm{N}}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}({l}_{{{{{{{\bf{e}}}}}}}_{1}},{l}_{{{{{{{\bf{e}}}}}}}_{2}})\), and below two representative systems, \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) and \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\), are examined.
Loadbearing capacity
Figure 5a shows the top view of \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}\)(7,7) along with an inset of a representative primitive unit cell (yellow) in the lock mode \({{{{{{\mathscr{A}}}}}}}^{2}\). Figure 5b reports its engineering stressstrain curves obtained in two lock configurations \({{{{{{\mathscr{A}}}}}}}^{2}\) and \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), and Fig. 5c the corresponding response of \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) in its two lock configurations \({{{{{{\mathscr{A}}}}}}}^{3}\) and \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\). The shaded domain describes the dispersion of the results obtained from testing three samples for each material system in a given mode. Three regions emerge: (i) An initial nonlinear regime, describing panels not yet engaged under compression, hence unable to establish a proper contact. (ii) A linear material response for both locked states of each system. (iii) The stresspeak and the following regime, both indicative of progressive panel buckling and creasing. For \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) switching from \({{{{{{\mathscr{A}}}}}}}^{2}\) to \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), the Young’s modulus and yield strength reduce approximately by an order of magnitude. For \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) switching from \({{{{{{\mathscr{A}}}}}}}^{3}\) to \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\), the corresponding reductions are approximately three and two times. Minor deviations emerge in regions (i) and (ii), as opposed to large values attained in region (iii) far from the peak. Our measurements are comparable with values reported for kirigamibased concepts made of similar material^{44}.
Scaling laws
Figure 5d shows the normalized Young’s modulus, \(\frac{{E}^{* }}{{E}_{s}}\), and normalized yield strength, \(\frac{{\sigma }^{* }}{{\sigma }_{f}}\), (where \({E}_{s}\) and \({\sigma }_{f}\) are the Young’s modulus and failure stress of the base material in the machine direction, MD) for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) measured at three values of relative density. The results are obtained for samples with geometric parameters a = b = 10 mm, 15 mm, and 20 mm; for each of them, five identical samples were fabricated and tested. The normalized Young’s modulus scales almost linearly with the relative density (\(\frac{{E}^{* }}{{E}_{s}}\propto {\bar{\rho }}^{1.1}\)), where \(\bar{\rho }\propto \left(\frac{t}{a}\right)\) (Supplementary Discussion “Relative density”), hence obeying the classical scaling law of stretching dominated structures. The normalized yield strength, on the other hand, scales almost quadratically with relative density (\(\frac{{\sigma }^{* }}{{\sigma }_{f}}\propto {\bar{\rho }}^{1.9}\)), a scaling law deviating from the buckling or yield failure predictions of stretching dominated 3D platelattices. This can be attributed to the presence of additional failure mechanisms, which are governed by hinge stiffness, panel contact and the presence of geometrical imperfections, a topic of ongoing research.
Cyclic response
Figure 5e, f show the cyclic loadingunloading curves of \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) and \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) under compression. Given their similarity, only the response of \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) is examined. The hysteretic behavior might be attributed to the friction of faces and edges coming to contact, the viscoelasticviscoplastic nature of the base material (cellulose paperboard) as well as the local accumulation of plastic damage, which is also responsible for progressive softening. This is caused by the repeated strain of the weak crease ligaments which amplify their detrimental effect at each cycle until the response stabilizes. This occurs after approximately four cycles. Thereafter, no appreciable softening can be observed at higher strains nor significant variations of the modulus. At the end of the test, a strain of 0.04 is registered, indicating a permanent set not fully recovered even after several hours from the test end. These characteristics are qualitatively comparable with those observed in soft polymeric lattices exhibiting viscoelasticity and localized plasticity under cyclic loading^{45}. Further work is required to quantitatively assess the response we observed and the role of the governing factors.
Multidirectional stiffness
\({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) in the lock configuration \({{{{{{\mathscr{A}}}}}}}^{2}\) is tested under inplane and outofplane compression (Fig. 6a) along two inplane directions (A and B) at 45° and 90° with respect to the xaxis, and along the zdirection. Representative curves of their engineering stressstrain responses in Fig. 6b attest a comparable yet distinct elastic response and loadbearing capacity. The largest strength (A) and stiffness (B) observed during inplane testing are attributed to the presence of doublelayered panels, i.e., quad panels bonded to stack layers, an aspect that confers additional anisotropy and larger strength to bear the compressive load beyond the elastic regime. The difference between the initial inplane responses (more compliant for the unit loaded at 45°) is due to the occurrence of a shear deformation that is dominant at the start of the compression test. Overall, our paperboard \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) specimens with a = b = 15 mm and locked in mode \({{{{{{\mathscr{A}}}}}}}^{2}\) weighs ~ 40 g, and can withstand up to 850 N under compression along the zdirection (Supplementary Movie 11), while up to 1450 N when compressed in the inplane directions. In the lock mode \({{{{{{\mathscr{A}}}}}}}^{3}\), \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) with identical geometric parameters and weight can resist 1000 N under outofplane compression (Supplementary Movie 12).
Mixedmode configurations
Uniformly applied forces at the instant of kinematic bifurcation cause the material system to fold into one of its lock modes, each with its own set of properties (e.g., Fig. 5b, c). Here we examine the outcome of a nonuniform set of forces locally applied in given zones, hence bringing the system into a mixedmode configuration, i.e., a state that is partially folded and encompasses a combination of lockable and flatfoldable modes. Figure 6c depicts seven mixedmode configurations among several others for our \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) specimen with square primitive side a = b = 10 mm. The top row shows the emergence of voids from configurations 4 to 7. In the second row, the distribution of the attainable modes, i.e., \({{{{{{\mathscr{A}}}}}}}^{2}\), \({{{{{{\mathscr{O}}}}}}}^{2}\) and \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), which can concurrently form in a given mixedmode, is highlighted with a given color. Figure 6d reports Young’s modulus normalized with respect to that of the configuration (1), i.e., E^{*(1)}, measured in each mixedmode configuration. Measurements of Young’s modulus E^{*} for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}({{{{\mathrm{7,7}}}}})\) shows only a 1.2fold decrease when the tessellation level (3,3) increases to (7,7) (see Supplementary Fig. 14b). The difference is small compared to the decrease observed for a switch from mode \({{{{{{\mathscr{A}}}}}}}^{2}\) to \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) (Fig. 5b) or \({{{{{{\mathscr{O}}}}}}}^{2}\) (Fig. 6d). This result suggests that the stiffness values of mixedmode configurations are relatively insensitive to finitesize effects. In general, the addition of moderegions \({{{{{{\mathscr{O}}}}}}}^{2}\) and \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) reduces stiffness, e.g., a drop to half is observed when configuration (1) switches to (3). Configuration (4) including all three moderegions shows slightly higher stiffness than configuration (2), a counterintuitive result that might be attributed to the distribution of moderegions with a twofold symmetry, as opposed to configurations (2) and (3), which exhibits reflection symmetry only. In this mode, only a single channel (an outofplane void) is formed as opposed to configurations (1), (2), and (3), which have no open channels or voids. Figure 6e shows the normalized openchannel area \(\frac{{A}_{{ch}}}{{A}_{{ch}}^{(4)}}\) changes upon reconfiguration, where \({A}_{{ch}}\) is the openchannels area in the outofplane direction and \({A}_{{ch}}^{(4)}\) that of configuration (4) with a single channel. The change in the openchannel area can be considered as a descriptor of the system permeability, which scales linearly with the conduit area as in a porous medium. The trends show that the compressive Young’s modulus and permeability are antagonists. While not quantified here, this qualitative result attests the versatility of our systems to tune onthefly flow permeability. Further work is required to quantify this aspect in detail.
Discussion
This work has introduced a class of reprogrammable rigidly flatfoldable metamaterials that are topological and loadbearing in multiple directions including the deployment direction. By merging notions of origamifolding with kirigamicuts, we have created foldable patterns made of chains that are shaped with an N evensided regular polygonal primitives defining the inner void. Cellular excisions relax certain deformation constrains imposed by panel planarity and connectivity of the parent origami. The strategy enables folding within the embedded voids with multiple DoFs, which can be reduced upon stacking. This trait simplifies the fabrication process and eases its automation (Supplementary Discussion “Manufacturability” and Supplementary Movie 1). At the bifurcation instant, however, the DoFs grow, and multiple kinematic paths become temporarily accessible. Some lead to 3D stiff (locked) configurations, and others to 2D flatfolded states; this hallmark extends the level of programmability offered by existing origami concepts. When tessellated, our metamaterials undergo symmetry and topology transformations that are amenable to in situ modulation in uniform and mixedmode configurations, each with its own set of properties.
Our foldable metamaterials offer functionalities that can be used as lightweight deployable and selflocking materials, lowvolume transportable packaging, actuators, and lockable robotic systems that tune stiffness upon actuation. Their rigidfoldability also enables the adoption of stiff materials other than paper^{39}. In addition, the loadbearing capacity in their densest lock configuration is not limited to any specific directions, rather it is offered along their three main directions, paving the way to their use as omnidirectionally structural, yet rigidly flatfoldable mechanical metamaterials. This aspect is distinct from current origami metamaterials featuring a tradeoff between reconfigurability and loadbearing capacity, the latter being limited to certain directions^{13,24,25,26,27,28,29,30,32,34,38,40,42}. These concepts when used to withstand volumetric pressure in their deployed state or another set of multidirectional forces, would collapse as they remain floppy at least in one direction. Volumetric pressure can be either externally or internally applied. Examples of the former include remotely operated vehicles, such as shapechanging vessels and submarines, made of structural components that need to deploy underwater and provide multidirectional stiffness and strength to resist water pressure during operation. Examples of the latter include inflatable systems, such as air tents, inflatable shelters, and buildings, saving boats and vests, which can not only be packed into a flat or other compact flatfolded configurations but also safely maintain their deployed state if punctured. Our metamaterials can thus work as the skeleton of punctureresistant inflatable systems that lock in place after deployment, without collapse or losing their functionality due to unforeseen deflation. Furthermore, the capacity to switch permeability while remaining stiff can find application in the design of adaptive porous media and breathable walls for civil engineering, or as smartvalves for medical implants where fluid flow could be modulated in situ by structure rather than by external occlusions.
Methods
Identification of lockable and flatfoldable modes
We systematically study the relations that define the postbifurcation modes belonging to a given kinematic path for a singleDoF stacked unit chain \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\). As illustrated in Fig. 2a, in the pre and postbifurcation stages, the triangular panels (six in dark green in the middle layer) in each set of mountains and valleys remain parallel as \(\bar{n}\) = 3. Three of them are mountain panels that lay in a mountain plane, and the others rest in a valley plane. The distance between them is h (Fig. 2a) which can be calculated through relation (1). In a given plane, there are six fold lines (two per triangle) which form a total of six dihedral angles. The fold lines that are parallel form a pair of dihedral angles (Fig. 2a). This pair can contain either equal or supplementary angles, a condition that defines the type of postbifurcation mode. Equality of dihedral angles in each pair defines regular modes, which in Fig. 2c belong to paths 1 and 2; this implies that the reconfiguration of the unit chain leads to a folded pattern that is compatible with its original tessellation. In contrast, supplementarity of dihedral angles in all pairs, i.e., the dihedral angles sum up to 180° in each pair, gives rises to irregular modes, and path 3 in Fig. 2c shows an example. Irregular modes can be attained only in a single unit chain but not in a tessellated pattern, as they forego folding congruence between the initial and the final pattern, revealing that the flatfoldable tessellation cannot be unpacked to its initial pattern. Only one irregular mode exists for \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) with N > 4 and N/2 equal to an odd number, e.g., modes of \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{3}\) shown in Fig. 2b.
Given the folding incompatibility of irregular modes, we now focus on the regular counterparts and study the conditions that can be used for a given kinematic path to count the number of existing modes and define the characteristics of each of them. Our goal is to demonstrate the existence of relations between distinct pairs of dihedral angles, which in turn govern the kinematic paths \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) can access postbifurcation. We first introduce some basic notions for our analysis. In the denomination of dihedral angles, we specify acute angles with \({{{{{\mathscr{A}}}}}}\) and obtuse angles with \({{{{{\mathscr{O}}}}}}{{{{{\mathscr{.}}}}}}\) The geometry of the units enforces the condition\(\,{{{{{\mathscr{A}}}}}}{{{{{\mathscr{+}}}}}}{{{{{\mathscr{O}}}}}}{{{{{\mathscr{=}}}}}}\pi\) during their entire range of motion. As an example, three pairs of valley dihedral angles are illustrated in Fig. 2d, two \({{{{{\mathscr{A}}}}}}\)s (violet and blue) and one \({{{{{\mathscr{O}}}}}}\) (yellow) for a total of six valley dihedral angles. Since in \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\), which has 1 DoF, each pair contains equal angles, all \({{{{{\mathscr{A}}}}}}\)s are equal as are all \({{{{{\mathscr{O}}}}}}\)s. A given sequence with angle pairs, e.g., two \({{{{{\mathscr{A}}}}}}\)s and one \({{{{{\mathscr{O}}}}}}\) depicted in Fig. 2d, can be simply denoted by the series of angle pairs, e.g.,\(\,{{{{{\mathscr{A}}}}}}{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\), and in compact form with the power indicating the repeated pairs, e.g., \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\). This notation allows discriminating between kinematic modes that emerge at bifurcation. For example, \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{3}\) (Fig. 2c) can travel along four regular modes: \({{{{{{\mathscr{O}}}}}}}^{3}\) (three obtuse angles are engaged only), \({{{{{{\mathscr{A}}}}}}}^{3}\) (three acute angles are engaged only), \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\) (two acute angles and one obtuse angle), \({{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}^{2}\) (one acute and two obtuse), and one irregular, shown with \({\overline{{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}}\). Modes containing identical pairs of dihedral angles belong to the same kinematic path, and we designate them by swapping \({{{{{\mathscr{A}}}}}}\)s and \({{{{{\mathscr{O}}}}}}\)s, i.e., \({{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}\) and \({{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}^{2}\) belong to path 2, and \({{{{{{\mathscr{A}}}}}}}^{3}\) and \({{{{{{\mathscr{O}}}}}}}^{3}\) to path 1.
With the notions above, we can now systematically characterize the regular modes of a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) and determine the total number of possible reconfiguration modes. The problem of finding all independent regular modes of a generic \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) unit can now be treated as the classical necklace problem. In our case, the equivalent necklace is our unit chain \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) with N/2 colored beads (Fig. 2d), and each color represents a type of dihedral angles, either \({{{{{\mathscr{A}}}}}}\) or \({{{{{\mathscr{O}}}}}}\). By applying the Pólya enumeration theory, we determine all reconfiguration modes our \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) chain can attain from knowledge of N/2 numbers of \({{{{{\mathscr{A}}}}}}\) and \({{{{{\mathscr{O}}}}}}\). We also assume that the beads can be rotated around the necklace and that the necklace can be flipped over. By applying this theory to \({\widehat{{{{{{\rm{N}}}}}}}}_{6}{{{{{{\rm{n}}}}}}}_{3}\), for instance, all the possible modes can be collected in a generating function of the form \({{{{{{\mathscr{A}}}}}}}^{3}+{{{{{{\mathscr{A}}}}}}}^{2}{{{{{\mathscr{O}}}}}}+{{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}^{2}+{{{{{{\mathscr{O}}}}}}}^{3}\), which describes the four regular modes illustrated in Fig. 2, and where the sum of the powers of \({{{{{\mathscr{A}}}}}}\) and \({{{{{\mathscr{O}}}}}}\) in each mode is N/2. Similar results can be obtained for other unit chains, \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) (see Supplementary Discussion “Pólya enumeration theorem” and Supplementary Fig. 3 for more details).
Energy of the inplane confinement and modephase diagram
We start with \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) described by the representative set of parameters: k = 1/3 N, n = 3, θ^{0} = \(\pi\) and a = b = 15 mm. Figure 4a illustrates two typical curves of the dimensionless total energy, each for a given value of \(({f}_{x},r_{B})\). Upon bifurcation, when θ = \(\pi\)/2, the total energy curve splits into two branches, each representing a reconfiguration mode \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) and \({{{{{{\mathscr{A}}}}}}}^{2}\). Between these two, the system chooses the mode which has the lowest energy level. This outcome can be determined by examining (i) the magnitude of the energy of all branches immediately before and after the bifurcation, and (ii) the gradient of the energy of all branches at bifurcation, for example, \({\left.\frac{\partial {\varPi }_{{{{{{{\mathscr{A}}}}}}}^{2}}}{\partial \theta }\right}_{\theta =\pi /2}\) and \({\left.\frac{\partial {\varPi }_{{{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}}}{\partial \theta }\right}_{\theta =\pi /2}\) (see Supplementary Discussion “Energy analysis” for more details). The magnitude and the ratio of the inplane biaxial loads, i.e., \(({f}_{x},r_{B})\), govern the relative energy level of each energy branch, dictating the configuration mode our system would travel after bifurcation. For example, Fig. 4a shows the role of \({r}_{B}\) in entering a given postbifurcation mode. For a load case \(({f}_{x},r_{B})=({{{{\mathrm{1,1}}}}}/3)\), the system at bifurcation chooses the \({{{{{\mathscr{A}}}}}}{{{{{\mathscr{O}}}}}}\) energy branch until reaching the lock state in this mode; in contrast once subjected to \(({f}_{x},r_{B})=(1,1)\), the system follows the \({{{{{{\mathscr{A}}}}}}}^{2}\) energy branch to reach the lock state.
The example above suggests the prospect to generate a modephase diagram that maps the activation of a given mode with respect to the relative magnitude of the inplane confinement forces f_{x} and f_{y}. Figure 4b visualizes such a map for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) with a = b = 15 mm and θ^{0} = \(\pi\). Each color is assigned to a region that describes a given configuration mode. The boundaries separating modes \({{{{{\mathscr{AO}}}}}}\) and \({{{{{{\mathscr{A}}}}}}}^{2}\) are obtained by equating the gradient of the total energy of each branch at bifurcation, \({\left.\left(\frac{\partial {\varPi }_{{{{{{\boldsymbol{{{{{\mathscr{A}}}}}}}}}}}^{2}}}{\partial \theta }=\frac{\partial {\varPi }_{{{{{\boldsymbol{{{{{\mathscr{AO}}}}}}}}}}}}{\partial \theta }\right)\right}_{\theta =\pi /2}\).
Formulation of the energy of the outofplane confinement
We start by expressing the potential energy of the hinges as \(V=V(\theta )={{2nNkb}\left(\theta {\theta }^{0}\right)}^{2}\) and the work of a uniformly applied external force f_{o} as \({W}_{o}={{nf}}_{o}a\,{{\sin }}\,\phi \left({{\sin}}\,{\theta }^{0}{{\sin }}\,\theta \right)\), where we recall n is the number of stacked layers and the other parameters are defined in Fig. 1a. The potential energy due to gravity is neglected since the panels of our system are made of cellulose paperboard, lightweight material with the gravitational potential energy of few orders of magnitude lower than that of the hinges and the work of the external forces. If we introduce \(V^{\prime} =V(\pi \theta )\), and denote a generic mode with \({{{{{{\mathscr{A}}}}}}}^{\xi }{{{{{{\mathscr{O}}}}}}}^{{\xi }^{{\prime} }}\), where \(\xi\) is the total number of valley pairs for the acute dihedral angles (\({{{{{{\mathscr{A}}}}}}}\)) and \({\xi }^{{\prime} }\) counts the total number of valley pairs for the obtuse dihedral angles (\({{{{{{\mathscr{O}}}}}}}\)) with \(\xi +{\xi }^{{\prime} }=\frac{N}{2}\), we can express the total energy \(\varPi =\varPi \left(\theta ,{f}_{o}\right)\) of the \({{{{{{\mathscr{A}}}}}}}^{\xi }{{{{{{\mathscr{O}}}}}}}^{{\xi }^{{\prime} }}\) mode as
The first expression in Eq. (3) describes the total energy of the system in mode \({{{{{{\mathscr{A}}}}}}}^{\xi }{{{{{{\mathscr{O}}}}}}}^{{\xi }^{{\prime} }}\) prior to bifurcation, while the second gives the total energy after bifurcation.
Under an outofplane force, a generic system \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\) is in equilibrium at the lock state when the total energy has a stationary value. Given \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{n}\) has one DoF, and the total energy and its derivative are continuous functions, we can determine the minimum outofplane force \({f}^{L}\) at the lock state by solving \({\left.\frac{\partial \varPi (\theta ,{f}_{o})}{\partial \theta }\right}_{\theta {=\theta }^{L}}=0\) for ξ ≥ 2, which yields:
Equations (3) and (4) can be used to map the total energy landscape of a system under a uniform outofplane compression as a function of the supplementary of the dihedral angle \(\theta\), i.e., \(\pi \theta\) (Fig. 1a). For demonstrative purpose, we examine \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{n}\) folding in mode \({{{{{{\mathscr{A}}}}}}}^{2}\) with θ^{0} = 2π/3. Figure 4d shows its energy curves (Eq. (3)) for three representing values of the outofplane load normalized by the lock load, i.e., \(\bar{f}={f}_{o}/{f}^{L}\). Setting \(\bar{f}=1\) yields the boundary (thick curve) between two energy domains, one (below) satisfying \(\bar{f} < 1\) and the other (above) \(\bar{f} > 1\). The red point, which all curves (three shown) pass through, represents the zeroenergy state, described above as the state of the system immediately after manufacturing, either flat (ideal case) or marginally folded due to residual stress from fabrication.
Subject to uniform outofplane compression, our material system can fold into its lock state under two conditions. First, the magnitude of the uniformly applied force \({f}_{o}\) should be above the minimum outofplane force, \({f}^{L}\), required to lock up the unit. Second, the dihedral angle of our unit should be larger than a threshold value defined by the maximum energy barrier of the system. The interplay between \({f}_{o}\) and \({f}^{L}\) described by these conditions gives rise to three domains:
Region I (light brown): \(\bar{f} < 1\). Here fall configurations are defined by supplementary angles for which our system can reach an equilibrium that is either stable if \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} > 0\), or unstable if \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} < 0\). Since \({f}_{o}\)<\({f}^{L}\), the system cannot access the lock state from a given configuration, e.g., lower orange point, and it tends to fold back to its equilibrium point along the “flatfold” direction towards the zeroenergy point (red).
Region II: \(\bar{f} > 1\). In this domain, our system can potentially reach the lock state, but a difference in the outcome exists as determined by the stability of equilibrium. Region II splits into two subdomains (IIa and IIb), each defined by the slope of the energy curve, i.e., the sign of \(\frac{\partial \varPi }{\partial \theta }\), where—we recall—\(\varPi\) is expressed as a function of (\(\pi \theta\)).
Region IIa (yellow): \(\frac{\partial \varPi }{\partial \theta } < 0\) and \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} < 0\). The condition of equilibrium here is unstable despite the outofplane force being larger than the minimum locking force. In this region, a system partially folded at a given dihedral angle by the applied inplane forces is prone to fold back to its fully developed (flat) state.
Region IIb (blue): \(\frac{\partial \varPi }{\partial \theta } > 0\) and \(\frac{{\partial }^{2}\varPi }{{\partial \theta }^{2}} < 0\). This is the lockable domain, bounded by the locus of points (dot line), which satisfies the condition \(\frac{\partial \varPi }{\partial \theta }=0\) for all \(\bar{f} > 1\). Upon imposing the condition\(\,\frac{\partial \varPi (\theta ,{f}_{o})}{\partial \theta }=0\) in Eq. (3), we can express the dihedral angle θ as a function of the load f_{o} when the energy is maximum, \(\frac{\partial \varPi }{\partial \theta }=0\), from which we obtain
Substituting Eq. (5) into Eq. (3) yields the lockable domain boundary of maximum energy (dot bound in Fig. 4d) given as a function of the dihedral angle (\({\theta }^{L}\le {\theta } \le \frac{\pi }{2}\) and \(\xi = 2\)):
Equation (6) traces points of the dot boundary that are unstable configurations of equilibrium, where the total energy attains maximum values, one of which is shown by the blue point of the representative energy curve \(\bar{f} > 1\).
Rigidity under compression
Once folded into the lock state, our multilayered unit chain \({{{{{{\rm{N}}}}}}}_{N}{{{{{{\rm{n}}}}}}}_{\bar{n}}\) inherits compressive loadbearing capacity as panels reach contact and prevent further motion. We study the loadbearing capacity of our class of foldable material systems in relation to their layer stacking. The condition that guarantees their structural rigidity in one of their lock states can be determined by studying their pinjointed counterpart made of a triangulated network (Supplementary Fig. 1c). We can formulate the general problem that predicts the rigidity of a structure by theoretical analysis (Supplementary Discussion “Kinematic analysis” and the “Kinematic model” section). While the units are subjected to compressive loads, we assume coincident bars as a single bar and multiple coincident joints as a single joint. The results can be expressed for a single unit chain as a function of the number of bars and joints at its lock and partially folded configurations along with the conditions of rigidity (see Supplementary Table 3 in Supplementary Discussion “Rigidity”).
Carried out for the general lock state \({{{{{{\mathscr{A}}}}}}}^{N/2}\), where all dihedral angles are acute, our rigidity analysis reveals that N_{4} becomes rigid with a single layer, whereas at least two layers must be stacked for N_{6} and three layers for N_{N>6}. Knowing the minimum number of stacked layers provides an essential guideline to make our unit chain stiff in a lock state under compression.
Experimental methods
Test samples were built out of cellulose paperboard material (200 g m^{−2} Fabriano Craft paper) with a dry thickness t = 0.21 mm. Each flat sheet was perforated via laser cutting (CM1290 laser cutter, SignCut Inc.) along prescribed patterns, followed by manualfolding and layer bonding (using a commercial Polyvinyl acetate, commonly known as white glue). Fold lines were obtained with cuts of 2 mm length spaced uniformly at 1.4 mm intervals. Experiments were performed with a BOSE ElectroForce3510 tester (Bose Corporation, Framingham, Massachusetts) and a BOSE loadcell with a load capacity of 12.5 kN. Displacementcontrol was used with a quasistatic ramp loading and strain rate of 10^{−3} s^{−1}. Manufacturing and testing were performed at room temperature (22 °C) with a relative humidity of about 30%. To measure the properties, e.g., Young’s modulus, we used both the displacement data obtained from the crosshead displacement readings as well as Digital Image Correlation (CCD camera—PointGrey) for comparative purposes. The largest difference in measurements provided by the two techniques was below 3%. Young’s modulus and yield strength were measured as the initial (linear region) slope (maximum strain at 0.05) and the first peak in the stressstrain curve, respectively, for the first loading cycle (see subset in Fig. 5d). Cyclic loadingunloading experiments were carried out using a displacementcontrol module at the same strain rate. The direction of the load was reversed when the load reached ~75% of the first cycle peak load.
All samples were realized with the following geometric parameters a = b = 15 mm and ϕ = 60° and loaded in the outofplane in compression unless stated otherwise. The relative density is defined by \(\bar{\rho }={\rho }^{* }/{\rho }_{s}\) (density of our reconfigurable cellular material, ρ*, divided by the density of the solid material, ρ_{s}). To vary relative density, three values were used a = b = 10, 15, and 20 mm. Specimens were compressed between two smooth flat platens of Aluminum. Initially, samples were brought to their lock position manually and kept in this configuration by wrapping them up with a rubber band. To assess the role of the rubber band during the experiments, we repeated a few compression tests without a rubber band. In these instances, we started the experiment while the sample was wrapped with a rubber band, and then cut it after applying 2% of the peak load, i.e., ~28 N for \({\widehat{{{{{{\rm{N}}}}}}}}_{4}{{{{{{\rm{n}}}}}}}_{6}\)(7,7). The results attest that the stressstrain curves were almost identical to those obtained on samples confined with a rubber band for the entire duration of the tests. See also Supplementary Discussion “Experiments” for further details about the properties of the paperboard.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
Code availability
The codes that support the findings of this study are available from the corresponding author upon reasonable request.
References
Melancon, D., Gorissen, B., GarcíaMora, C. J., Hoberman, C. & Bertoldi, K. Multistable inflatable origami structures at the metre scale. Nature 592, 545–550 (2021).
Zhang, Y. et al. A mechanically driven form of Kirigami as a route to 3D mesostructures in micro/nanomembranes. Proc. Natl Acad. Sci. USA 112, 11757–11764 (2015).
Yasuda, H., Tachi, T., Lee, M. & Yang, J. Origamibased tunable truss structures for nonvolatile mechanical memory operation. Nat. Commun. 8, 1–7 (2017).
Pagano, A., Yan, T., Chien, B., Wissa, A. & Tawfick, S. A crawling robot driven by multistable origami. Smart Mater. Struct. 26, 094007 (2017).
Rafsanjani, A., Zhang, Y., Liu, B., Rubinstein, S. M., & Bertoldi, K. Kirigami skins make a simple soft actuator crawl. Sci. Robot. 3, eaar7555 (2018).
Novelino, L. S., Ze, Q., Wu, S., Paulino, G. H. & Zhao, R. Untethered control of functional origami microrobots with distributed actuation. Proc. Natl Acad. Sci. USA 117, 24096–24101 (2020).
Rafsanjani, A., Jin, L., Deng, B. & Bertoldi, K. Propagation of pop ups in kirigami shells. Proc. Natl Acad. Sci. USA 116, 8200–8205 (2019).
Wu, S. et al. Stretchable origami robotic arm with omnidirectional bending and twisting. Proc. Natl. Acad. Sci. USA 118, e2110023118 (2021).
Boatti, E., Vasios, N. & Bertoldi, K. Origami metamaterials for tunable thermal expansion. Adv. Mater. 29, 1700360 (2017).
Liu, L., Qiao, C., An, H. & Pasini, D. Encoding kirigami bimaterials to morph on target in response to temperature. Sci. Rep. 9, 1–14 (2019).
IniguezRabago, A., Li, Y. & Overvelde, J. T. Exploring multistability in prismatic metamaterials through local actuation. Nat. Commun. 10, 1–10 (2019).
Silverberg, J. L. et al. Origami structures with a critical transition to bistability arising from hidden degrees of freedom. Nat. Mater. 14, 389–393 (2015).
Yasuda, H. & Yang, J. Reentrant origamibased metamaterials with negative Poisson’s ratio and bistability. Phys. Rev. Lett. 114, 185502 (2015).
Liu, K., Tachi, T. & Paulino, G. H. Invariant and smooth limit of discrete geometry folded from bistable origami leading to multistable metasurfaces. Nat. Commun. 10, 1–10 (2019).
Shang, X., Liu, L., Rafsanjani, A. & Pasini, D. Durable bistable auxetics made of rigid solids. J. Mater. Res. 33, 300–308 (2018).
Castle, T., Sussman, D. M., Tanis, M. & Kamien, R. D. Additive lattice kirigami. Sci. Adv. 2, e1601258 (2016).
Choi, G. P., Dudte, L. H. & Mahadevan, L. Programming shape using kirigami tessellations. Nat. Mater. 18, 999–1004 (2019).
Dudte, L. H., Vouga, E., Tachi, T. & Mahadevan, L. Programming curvature using origami tessellations. Nat. Mater. 15, 583–588 (2016).
Pratapa, P. P., Liu, K. & Paulino, G. H. Geometric mechanics of origami patterns exhibiting Poisson’s ratio switch by breaking mountain and valley assignment. Phys. Rev. Lett. 122, 155501 (2019).
An, N., Domel, A. G., Zhou, J., Rafsanjani, A. & Bertoldi, K. Programmable hierarchical kirigami. Adv. Funct. Mater. 30, 1906711 (2020).
Sussman, D. M. et al. Algorithmic lattice kirigami: a route to pluripotent materials. Proc. Natl Acad. Sci. USA 112, 7449–7453 (2015).
Lamoureux, A., Lee, K., Shlian, M., Forrest, S. R. & Shtein, M. Dynamic kirigami structures for integrated solar tracking. Nat. Commun. 6, 1–6 (2015).
Nauroze, S. A., Novelino, L. S., Tentzeris, M. M. & Paulino, G. H. Continuousrange tunable multilayer frequencyselective surfaces using origami and inkjet printing. Proc. Natl Acad. Sci. USA 115, 13210–13215 (2018).
Overvelde, J. T., Weaver, J. C., Hoberman, C. & Bertoldi, K. Rational design of reconfigurable prismatic architected materials. Nature 541, 347–352 (2017).
Overvelde, J. T. et al. A threedimensional actuated origamiinspired transformable metamaterial with multiple degrees of freedom. Nat. Commun. 7, 1–8 (2016).
Filipov, E. T., Tachi, T. & Paulino, G. H. Origami tubes assembled into stiff, yet reconfigurable structures and metamaterials. Proc. Natl Acad. Sci. USA 112, 12321–12326 (2015).
Schenk, M. & Guest, S. D. Geometry of Miurafolded metamaterials. Proc. Natl Acad. Sci. USA 110, 3276–3281 (2013).
Eidini, M. & Paulino, G. H. Unraveling metamaterial properties in zigzagbase folded sheets. Sci. Adv. 1, e1500224 (2015).
Lv, C., Krishnaraju, D., Konjevod, G., Yu, H. & Jiang, H. Origami based mechanical metamaterials. Sci. Rep. 4, 1–6 (2014).
Cheung, K. C., Tachi, T., Calisch, S. & Miura, K. Origami interleaved tube cellular materials. Smart Mater. Struct. 23, 094012 (2014).
Rafsanjani, A. & Pasini, D. Bistable auxetic mechanical metamaterials inspired by ancient geometric motifs. Extrem. Mech. Lett. 9, 291–296 (2016).
Fang, H., Chu, S. C. A., Xia, Y. & Wang, K. W. Programmable self‐locking origami mechanical metamaterials. Adv. Mater. 30, 1706311 (2018).
Zhai, Z., Wang, Y. & Jiang, H. Origamiinspired, ondemand deployable and collapsible mechanical metamaterials with tunable stiffness. Proc. Natl Acad. Sci. USA 115, 2032–2037 (2018).
Silverberg, J. L. et al. Using origami design principles to fold reprogrammable mechanical metamaterials. Science 345, 647–650 (2014).
Mukhopadhyay, T. et al. Programmable stiffness and shape modulation in origami materials: emergence of a distant actuation feature. Appl. Mater. Today 19, 100537 (2020).
Tang, Y., Li, Y., Hong, Y., Yang, S. & Yin, J. Programmable active kirigami metasheets with more freedom of actuation. Proc. Natl Acad. Sci. USA 116, 26407–26413 (2019).
Zhai, Z., Wang, Y., Lin, K., Wu, L. & Jiang, H. In situ stiffness manipulation using elegant curved origami. Sci. Adv. 6, eabe2000 (2020).
Yasuda, H., Gopalarethinam, B., Kunimine, T., Tachi, T. & Yang, J. Origami‐based cellular structures with in situ transition between collapsible and load‐bearing configurations. Adv. Eng. Mater. 21, 1900562 (2019).
Evans, T. A., Lang, R. J., Magleby, S. P. & Howell, L. L. Rigidly foldable origami gadgets and tessellations. R. Soc. Open Sci. 2, 150067 (2015).
Filipov, E. T., Paulino, G. H. & Tachi, T. Origami tubes with reconfigurable polygonal crosssections. Proc. Math. Phys. Eng. 472, 20150607 (2016).
Nayakanti, N., Tawfick, S. H. & Hart, A. J. Twistcoupled kirigami cells and mechanisms. Extrem. Mech. Lett. 21, 17–24 (2018).
Kamrava, S., Mousanezhad, D., Ebrahimi, H., Ghosh, R. & Vaziri, A. Origamibased cellular metamaterial with auxetic, bistable, and selflocking properties. Sci. Rep. 7, 1–9 (2017).
Wagner, M. A., Lumpe, T. S., Chen, T. & Shea, K. Programmable, active lattice structures: unifying stretchdominated and bendingdominated topologies. Extrem. Mech. Lett. 29, 100461 (2019).
Wang, X., Guest, S. D. & Kamien, R. D. Keeping it together: interleaved kirigami extension assembly. Phys. Rev. X 10, 011013 (2020).
Gavazzoni, M., Foletti, S., & Pasini, D. Cyclic response of 3D printed metamaterials with soft cellular architecture: the interplay between asbuilt defects, material and geometric nonlinearity. J. Mech. Phys. Solids 158, 104688 (2022).
Acknowledgements
D.P. and A.A. acknowledge financial support from the Natural Sciences and Engineering Research Council of Canada and Canada Research Chairs Program, and M.M. and A.J. from McGill University (McGill Engineering Doctoral Award) and Fonds de recherche du Québec—Nature et technologies.
Author information
Authors and Affiliations
Contributions
A.J., M.M., and D.P. designed research; A.J. proposed unit cells N4 and N6 and M.M. generalized them to the whole class; A.J. and M.M. performed research under close supervision of D.P.; M.M. and D.P. wrote the paper; all authors contributed to the interpretation of the results and the editing of the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Jonathan Hopkins and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jamalimehr, A., Mirzajanzadeh, M., Akbarzadeh, A. et al. Rigidly flatfoldable class of lockable origamiinspired metamaterials with topological stiff states. Nat Commun 13, 1816 (2022). https://doi.org/10.1038/s41467022294841
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467022294841
This article is cited by

Rigidfoldable cylindrical origami with tunable mechanical behaviors
Scientific Reports (2024)

Largescale modular and uniformly thick origamiinspired adaptable and loadcarrying structures
Nature Communications (2024)

StiffnessTunable Origami Structures via Multimaterial ThreeDimensional Printing
Acta Mechanica Solida Sinica (2023)

Design of compliant mechanisms for origami metamaterials
Acta Mechanica Sinica (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.