Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Substrate strain tunes operando geometric distortion and oxygen reduction activity of CuN2C2 single-atom sites


Single-atom catalysts are becoming increasingly significant to numerous energy conversion reactions. However, their rational design and construction remain quite challenging due to the poorly understood structure–function relationship. Here we demonstrate the dynamic behavior of CuN2C2 site during operando oxygen reduction reaction, revealing a substrate-strain tuned geometry distortion of active sites and its correlation with the activity. Our best CuN2C2 site, on carbon nanotube with 8 nm diameter, delivers a sixfold activity promotion relative to graphene. Density functional theory and X-ray absorption spectroscopy reveal that reasonable substrate strain allows the optimized distortion, where Cu bonds strongly with the oxygen species while maintaining intimate coordination with C/N atoms. The optimized distortion facilitates the electron transfer from Cu to the adsorbed O, greatly boosting the oxygen reduction activity. This work uncovers the structure–function relationship of single-atom catalysts in terms of carbon substrate, and provides guidance to their future design and activity promotion.


Single-atom catalysts (SACs) dispersed on conductive carbon substrates are granted rich redox and coordination chemistry of metal centers, and present unique built-in catalytic activity and selectivity in numerous energy conversion reactions such as oxygen reduction1,2,3, oxygen evolution4,5,6, and carbon dioxide reduction7,8,9. Accordingly, the single-atom catalysis has become the most active frontier in energy conversion catalysis in the past decade10,11,12,13. Despite tremendous efforts, the general try-and-error methodology of constructing single-atom sites lacks the efficiency in tuning the activity and selectivity of SACs. Comprehensively understanding the catalytic behavior and structure–function relationship of single-atom active sites is a prerequisite for the rational design and construction of highly efficient SACs. This understanding, however, remains a great challenge because of the complicated active site structures and the complex reaction conditions of SACs.

As the latest development of understanding the catalytic behavior of SACs, the dynamic evolution of active sites in operando processes has recently been probed using advanced characterization techniques, especially X-ray absorption spectroscopy (XAS)14,15,16. For instance, the Fe center in Fe–N–C SACs is found to undergo Fe2+/Fe3+ transition, and the ferrous state is the real active site during the oxygen reduction reaction (ORR)17,18. For the RuN4 SACs catalyzing the oxygen evolution reaction, the adsorption of extra O is observed to induce the in situ reconstruction of active site, and the formed O-RuN4 moiety highly enhances the activity5. These dynamic catalytic behaviors provide valuable information on the determination of active sites and the comprehension of reaction mechanism. However, the detailed structure–function relationship underneath diverse catalytic behaviors is still unclear. In particular, the correlation between the carbon substrate structure and the operando catalytic behavior has not yet been paid much attention, although previous studies have proven that carbon substrates have strong effects on the properties of SACs19,20,21,22.

Graphene and carbon nanotube (CNT) have definite and uniform sp2-hybridized carbon framework structures, providing ideal model substrates to investigate the structure–function relationship of SACs. Compared with graphene, CNT possesses more sp3-like C atoms and strained C–C bonds due to the geometric bending23,24,25. The bended carbon substrates possibly lead to distinctive dynamic evolution of active sites and thus manipulate the catalytic processes of SACs26,27. In this work, we try to correlate the operando structure evolution of SACs to their catalytic properties, and demonstrate the substrate-induced activity enhancement of CuN2C2 SACs embedded within sp2-hybridized carbon frameworks. Both theoretical computation and operando XAS indicate that the CuN2C2 active site is geometrically distorted during the ORR as a response to the newly coordinated O-containing species, and the active site on the highly curved CNT substrates undergoes more severe distortion to release strain. Taking advantage of the strain of CNT substrate, we are able to manipulate the geometric distortion of CuN2C2 active site (Fig. 1). This distortion artfully balances the two contrary effects of strengthening the new Cu–O bonding and weakening the original Cu–N/Cu–C bonding to tune the electron transfer to the adsorbent. As a result, the CuN2C2 active site on the reasonable CNT substrate presents the optimized geometric distortion for achieving the most electrons transferred to the adsorbed O2 molecules, thus enhancing the ORR activity of up to sixfold. Our work reveals the strain-induced geometric distortion and the substrate structure–activity relationship of CuN2C2 active site, paving a new pathway to the future rational design and further activity promotion of SACs.

Fig. 1: Illustration of structural distortion of CuN2C2 active site with adsorbed O2 on different sp2-hybridized carbon frameworks.
figure 1

The distortion becomes more severe as the curvature-induced strain increases in the substrate from graphene (left) to CNT with small diameter (right).


Fabrication and ORR performance

The CuN2C2 single-atom active site on the sp2-hybridized carbon substrates was fabricated using a confined self-initiated dispersing protocol as described in our previous work28. These single-atom Cu moieties are in situ formed during the high temperature pyrolysis, and have a quasi-planar coordination geometry, corresponding to an embedded structure within the carbon framework29. Graphene and two representative sizes of CNT with the diameter of 8 and 4 nm were utilized as the substrates, and the corresponding SACs are denoted as Cu/G, Cu/CNT-8, and Cu/CNT-4, respectively.

The catalytic activity of these Cu-SACs toward ORR was evaluated in O2-saturated 0.1 M KOH solution in a standard three-electrode quartz cell with catalyst-coated glassy carbon (GC) rotating-disk electrode, Hg/HgO electrode and Pt foil as the working, reference and counter electrodes, respectively (see details in Methods). Among the three catalysts, Cu/CNT-8 presents the most positive ORR polarization curve (Fig. 2a). To quantitatively assess the ORR activity, kinetic current density (ik) was calculated based on the K–L plots30 (Supplementary Fig. 1) and is shown in Fig. 2b. In the whole kinetics control and mixed kinetics-diffusion control regions from ~0.92 to ~0.8 V, ik of Cu/CNT-8 is apparently higher than that of the other two samples. Specifically, ik at 0.85 V for Cu/CNT-8 reaches 9.24 mA cm−2, which is more than 2.5 times that for Cu/G (3.62 mA cm−2).

Fig. 2: Oxygen reduction activity of Cu/G and two Cu/CNT samples.
figure 2

a ORR polarization curves, b kinetic current density curves, and c E1/2, Eonset, MA, and TOF at 0.85 V.

The onset potential (Eonset) and half-wave potential (E1/2) are compared in Fig. 2c. Eonset (0.933 V) and E1/2 (0.863 V) of Cu/CNT-8 surpass Cu/G by 13 and 12 mV, respectively, confirming that Cu/CNT-8 is the most active towards the ORR and even comparable to some reported Fe- and Co-based SACs (Supplementary Table 1). Moreover, to normalize the ORR activity by the amount of Cu single atoms, mass activity (MA), and turnover frequency (TOF) were calculated based on the inductively coupled plasma optical emission spectroscopy (ICP-OES) results (Supplementary Table 2), and are further compared in Fig. 2c31. Cu/CNT-8 exhibits the highest MA of 1.08 A mg−1 and TOF of 0.72 e·s−1·site−1 at 0.85 V, which are more than 6 times those of Cu/G (0.17 A mg−1 and 0.11 e site−1 s−1, respectively), outperforming most of the Cu-based active moieties in SACs (Supplementary Table 1). Noteworthy is that a much lower ORR activity is observed for Cu/CNT-4 in terms of onset potential, half-wave potential, MA and TOF even though it also employs CNT as the substrate, and similar compromise on ORR performance can also be seen on larger-sized CNT sample (Supplementary Fig. 2).

In addition to activity, the ORR selectivity is also evaluated by the electron transfer number and peroxide yield (Supplementary Fig. 3), which were obtained based on the rotating ring-disk electrode (RRDE) method32. It can be observed that although the majority of oxygen on Cu/G is reduced to hydroxide via the 4-electron pathway, the amount of peroxide is fairly noticeable at the relatively low potential region. On Cu/CNT-8, however, a remarkable selectivity to hydroxide is presented with the peroxide yield <5%. In comparison, Cu/CNT-4 shows a rather different selectivity, whose peroxide yield is even higher than that of Cu/G in the whole region.

These results clearly demonstrate the importance of carbon substrate nature in designing the SACs. Modulating the carbon substrate from graphene to a proper CNT can tremendously enhance the activity and selectivity to hydroxide of CuN2C2 SACs towards the ORR, while the CNT substrate with too small or too large diameter worsens the catalytic properties, despite their similar sp2 hybridized structure. At the same time, Cu/CNT-8 has a high durability in both potentiostatic and potentiodynamic conditions (Supplementary Fig. 4), probably due to its less edge sites than Cu/G and the lower chemical reactivity of substrate than Cu/CNT-433,34.

Characterization of Cu-SACs

In order to identify the real ORR active site and reveal the underlying mechanism of carbon substrate nature in tuning the catalytic properties of SACs, the composition and structure of these CuN2C2 SACs were systematically characterized by experimental characterization and density functional theory (DFT) computation. From the transmission electron-microscopy (TEM) observation (Fig. 3a–c), the Cu/G SAC exhibits a planar sheet-like morphology, while both Cu/CNT samples are the typical cross-stacking nanotube structure. The diameters of Cu/CNT-8 and Cu/CNT-4 SACs measured from the high resolution TEM images (Supplementary Fig. 5) are around 8 and 4 nm, respectively. The bright diffraction rings assigned to graphitic carbon in the selected area electron diffraction (SAED) patterns (insets in Fig. 3a–c) suggest that all the three SACs have the well-defined crystallized sp2-hybridized carbon nature, without any crystalline Cu-containing species29. This observation is verified by their X-ray diffraction (XRD) patterns in Supplementary Fig. 6, where only a strong peak assigned to the C (002) plane can be identified. The atomic dispersion of Cu is evidenced by the sub-nanoscale bright dots observed in the high-angle annular dark-field (HAADF) images from the spherical aberration corrected scanning TEM (AC-STEM) (Fig. 3d–f), and the evenly distributed Cu signals in the energy dispersed X-ray spectroscopy (EDS) results (Supplementary Fig. 7)35.

Fig. 3: Characterization of Cu-SACs.
figure 3

ac TEM images, corresponding SAED patterns (insets in ac) and (df) spherical aberration corrected HAADF-STEM images of Cu/G (a, d), Cu/CNT-8 (b, e) and Cu/CNT-4 (c, f), (g) Cu 2p and Cu LMM Auger XPS spectra of the Cu-SACs, (h) Cu K-edge XANES spectra of the Cu-SACs with Cu, Cu2O, and CuO as references, (i) R-space Cu K-edge EXAFS of the Cu-SACs.

Various elemental analyses were further conducted to gain information on the chemical status of CuN2C2 SACs. Based on the Cu 2p and LMM Auger X-ray photoelectron spectroscopy (XPS) profiles (Fig. 3g), the binding energy difference of Cu 2p and Auger peaks, ΔE, and its derivative Auger parameter, which is rather sensitive to the oxidation states of Cu, can be calculated36. Judging from the similar Auger parameter around 1850 eV, Cu in all the three samples fits common profile of Cu(I)37. This conclusion is confirmed by the synchrotron radiation X-ray absorption fine structure (XAFS) analysis. In the Cu K-edge X-ray absorption near edge structure (XANES) spectra (Fig. 3h), the absorption edge and white line intensity of all the samples are between the Cu2O and CuO references. The enhanced white line intensity for both Cu/CNT SACs, especially Cu/CNT-4, in comparison with Cu/G suggests higher oxidation state of Cu38, which should result from the more electron transfer between Cu and the conjugated π bond in graphene than in CNT (Supplementary Table 3).

In the R-space extended XAFS (EXAFS) spectra (Fig. 3i), all the SACs present only one main peak at ca. 1.5 Å, which is distinctive from the Cu and its oxide references (Supplementary Fig. 8) and rules out their presence. The EXAFS spectra can be well fitted using only Cu–C and Cu–N paths (Supplementary Fig. 9), indicating that the Cu atoms on graphene and CNT substrates are stabilized in the form of CuN2C2 moiety. The fitting parameters summarized in Supplementary Table 4 suggest that the CuN2C2 moieties on CNT and graphene have the similar coordination structure, providing well guidance for further DFT modeling and analysis.

DFT computation

With the information of the composition and structure of CuN2C2 active site, the DFT computation was conducted to look into the detailed electronic and geometric structures of the active site during the operando ORR catalysis. In the modeling process, the graphene moiety and the armchair single-walled CNTs of (59,59) type (diameter ~8 nm) and (29,29) type (diameter ~4 nm) were employed as the full scale substrates, in order to simulate the actual local environment around the CuN2C2 active site. The three models are shown in Supplementary Fig. 10.

The entire ORR process in alkaline media fits the profile of associate pathway with the following five elementary steps according to the DFT calculation (Supplementary Table 5), and illustrated in Fig. 4a39. The proposed reaction mechanism is in accordance with most of the reports on the ORR SACs in aqueous systems2,40,41.

$${}^{\ast }\,+\,{{{{{{\rm{O}}}}}}}_{2}\,\to\, {}^{\ast }{{{{{\rm{O}}}}}}_{2}$$
$${}^{\ast }{{{{{\rm{O}}}}}}_{2}\,+\,{{{{{{\rm{H}}}}}}}_{2}{{{{{\rm{O}}}}}}\,+\,{{{{{{\rm{e}}}}}}}^{-}\,\to\, {}^{\ast }{{{{{\rm{O}}}}}}{{{{{\rm{OH}}}}}}\,+\,{{{{{{\rm{OH}}}}}}}^{-}$$
$${}^{\ast }{{{{{\rm{O}}}}}}{{{{{\rm{OH}}}}}}\,+{{{{{{\rm{e}}}}}}}^{-}\,\to\, {}^{\ast }{{{{{\rm{O}}}}}}\,+\,{{{{{{\rm{OH}}}}}}}^{-}$$
$${}^{\ast }{{{{{\rm{O}}}}}}\,+\,{{{{{{\rm{H}}}}}}}_{2}{{{{{\rm{O}}}}}}\,+\,{{{{{{\rm{e}}}}}}}^{-}\,\to\, {}^{\ast }{{{{{\rm{O}}}}}}{{{{{\rm{H}}}}}}\,+\,{{{{{{\rm{OH}}}}}}}^{-}$$
$${}^{\ast }{{{{{\rm{O}}}}}}{{{{{\rm{H}}}}}}\,+\,{{{{{{\rm{e}}}}}}}^{-}{\,\to\, }^{\ast }\,+\,{{{{{{\rm{OH}}}}}}}^{-}$$

where * represents the active site for the adsorption of intermediates.

Fig. 4: DFT computation results on energy, electron structure, and geometry analysis.
figure 4

a Illustration of ORR process on CuN2C2 active site, (b) ORR free energy diagrams on Cu/CNT-8, Cu/CNT-4 and Cu/G, (c) side view and top view of the charge density difference for three models with O2*, where yellow and blue areas represent higher and lower charge density, respectively, and (d) geometric descriptor θ of CuN2C2 active site at various stages of ORR for the three models (inset: illustration of the model used for geometry analysis).

The Gibbs free energies of all the related oxygen-containing species adsorbed on the active sites were calculated by the CP2K/Quickstep package, and the free energy diagrams of ORR reaction pathways are presented in Fig. 4b. Based on the calculation results, all the O-containing intermediates involved are preferred to adsorb on the Cu center compared with the neighboring C or N atoms (Supplementary Tables 6, 7), whose geometries are illustrated in Supplementary Fig. 11b, supporting that Cu is the real adsorption and catalytic site for the ORR. Visually, the free energy diagrams of all the three models differ substantially from that of Cu (111) (Supplementary Fig. 11a). The trend of Cu/G shares the similarity with that of Cu/CNT-8, but is distinctive from that of Cu/CNT-4. Nevertheless, the potential determining step (i.e., the most endothermic step) is the same for these models, which is the protonation of *O2 to *OOH. The energy difference in the potential determining step for Cu/CNT-8 is the smallest, consistent with its highest ORR activity42.

The charge density difference analysis was performed to evaluate the charge transfer between the active site and the O-containing intermediates on the models, and the results are shown in Fig. 4c and Supplementary Fig. 12, where the yellow and blue areas represent the higher and lower electron densities, respectively. For all the models, electron is transferred from Cu onto the adsorbed O-containing intermediates. The Mulliken charge of *O2, the reactant of potential determining step, was calculated and given in Fig. 4c. It is found that more negative charge is transferred to *O2 on Cu/CNT-8 (−0.041) in comparison with Cu/CNT-4 (−0.023) and Cu/G (−0.037), which results in a more favorable protonation of *O2. Sufficient electron transfer promotes the further reduction of adsorbed species and thus the ORR activity, which is well consistent with our experiment results43. Since the active sites for the three models are exactly the same in composition, the varied electron transfer capability originates from the substrate structure and its induced operando evolution.

We evaluate the geometry structure evolution of different CuN2C2 active sites during the reaction process. In order to quantify the geometric structure distortion, a descriptor, θ, is introduced, which is calculated by the following equation:

$$\theta =\, 360^\circ -\alpha =360^\circ -(\angle {{{{{{\rm{N}}}}}}}_{1}-{{{{{\rm{Cu}}}}}}-{{{{{{\rm{N}}}}}}}_{2}+\angle {{{{{{\rm{N}}}}}}}_{2}-{{{{{\rm{Cu}}}}}}\\ -{{{{{{\rm{C}}}}}}}_{1}+\angle {{{{{{\rm{C}}}}}}}_{1}-{{{{{\rm{Cu}}}}}}-{{{{{{\rm{C}}}}}}}_{2}+\angle {{{{{{\rm{C}}}}}}}_{2}-{{{{{\rm{Cu}}}}}}-{{{{{{\rm{N}}}}}}}_{1})$$

where α is the sum of the bond angles between every two neighboring Cu–N or Cu–C bonds, as illustrated in the inset of Fig. 4d. Ideally, for the CuN2C2 active site embedded in a planar sp2-hybridized carbon framework, θ should be close to 0°. As the coordination asymmetry/substrate curvature varies, or the adsorption species induces, θ deviates from 0. In Fig. 4d, θ of the pristine CuN2C2 active site without adsorbing the O-containing intermediates is almost identical for Cu/G and Cu/CNT-8, and slightly increases for Cu/CNT-4, which is induced by its larger curvature with smaller diameter, in accordance with the conclusion on pure CNT44. However, when O2 is adsorbed on Cu, initiating the ORR, the situation becomes quite different. Cu/CNT-8 undergoes more obvious distortion upon O2 adsorption as evidenced by its θ variation (Δθ) much greater than that of Cu/G (1.59° vs. 0.26°), even though their original geometry structures are almost identical to each other. Moreover, the structural distortion is more apparent on Cu/CNT-4 with greater θ during the whole reaction process.

In addition to the bond angle, the geometry distortion of CuN2C2 active site is also revealed by the bond length. Taking the Cu–N bond as an example, the average Cu–N bond length elongates after the O2 adsorption (Supplementary Table 8). Similar with θ, Cu/CNT-4 presents the largest bond length increment, which is sequentially followed by Cu/CNT-8 and Cu/G. These calculation results clearly demonstrate that the three models present distinctive geometry structure distortion during the ORR catalytic process, despite their similar original structures.

Operando XAFS and mechanism of distortion on ORR

In order to gain the experimental evidence of the geometric structure distortion induced by the O-containing species, we investigate the operando behavior of CuN2C2 active site via the in situ XAFS on Cu/CNT-8. Comparing with the ex situ condition, the operando Cu K-edge XANES (Fig. 5a) clearly shows the positively shifted absorption edge and the enhanced white line intensity, revealing a upshift of Cu oxidation state, which should be ascribed to the thermodynamically favored adsorption of O2 on Cu as revealed by the DFT calculation and the subsequent electron transfer driven by the electronegativity18. The operando R-space EXAFS spectra (Fig. 5b) shows the increment of magnitude and the positive shift of the main peak, which, based on the fitting results, are attributed to the formation of a new Cu–O coordination with the coordination number of 1 (Fig. 5c and Supplementary Fig. 13). It is noteworthy that from the fitting results, the Cu–N coordination distance of Cu/CNT-8 elongates by 0.015 Å in the operando test, well in accordance with the increment of Cu–N bond upon the O2 adsorption from the DFT calculation (Fig. 5d and Supplementary Table 9). The in situ XAFS results provide direct and strong experimental evidence to support Cu is the real active site in the CuN2C2 moiety for ORR, and the original coordination structure distinctively distorts after the O2 adsorption.

Fig. 5: XAFS characterization of Cu/CNT-8.
figure 5

In situ and ex situ Cu K-edge (a) XANES and (b) EXAFS of Cu/CNT-8, (c) fitting of in situ R-space EXAFS spectrum of Cu/CNT-8, and (d) comparison of Cu–N bond lengths obtained from EXAFS fitting and DFT calculation.

The operando geometric structure distortion during the ORR catalysis is directly related to the displacement of metal centers, as a structural response to the adsorption of reaction intermediates. This response depends on the carbon substrate, which is closely correlated to the strain of substrate framework. As the substrate is changed from graphene, the CNT with large diameter, to the CNT with small diameter, curvature increases although they have the same sp2-hybridized carbon composition. The increase in curvature induces the pyramidalization of sp2-hybridized C atoms and the misalignment of p orbitals, enhancing the torsional strain in the carbon frameworks45. The high strain tends to be released, if possible, through distorting the conjugated framework to a lower energy structure. According to the bond angle analysis (Supplementary Fig. 14 and Supplementary Table 10), the geometry distortion by the newly formed axial Cu–O bond induces the relaxation of neighboring bonds to lower the local curvature, which is thermodynamically favored. This analysis can explain the curvature-dependent distortion levels varying from severe Cu/CNT-4 (the highest strain) to mild Cu/G (the lowest strain).

The adsorption-induced distortion of the geometric coordination environment directly triggers the refinement of the ligand field around the metal Cu atoms, which is a prerequisite for achieving the strong interaction with the adsorbed O-containing species. The structure distortion of Cu/G is the mildest among the three models, and the visible lack of electron density changes between the Cu and O atoms (Fig. 4c) indicates the weak Cu–O hybridization, which is not conducive to the charge transfer from the catalyst to *O2. Nevertheless, the too severe distortion in Cu/CNT-4 leads to the over-lengthened Cu–N bond after the *O2 adsorption, which impairs the conjugation of Cu 3d orbitals with C/N pz orbitals, weakening the original Cu–C/Cu–N interaction and thus lowering the electron transfer from N/C atoms to adsorbed *O2 via the shared Cu atom. As a result, to achieve the optimal activity of CuN2C2 SACs, it is vital to modulate the structure distortion to a balanced point, where a strong hybridization of Cu with O can be achieved and meanwhile the original bonds of Cu–N/Cu–C are not excessively undermined. This balance can be reached through rationally tuning the stain of carbon substrates via facilely choosing the different sp2-hybridized carbon frameworks.


In summary, using the single-atom Cu dispersed on different sp2-hybridized carbon substrates as the model, we have demonstrated the operando substrate-related geometry distortion of single-atom CuN2C2 active site and its relationship with the ORR activity. The geometry distortion is revealed to be positively correlated with the torsional strain of carbon substrates reflected by curvature, due to the thermodynamically favored tendency of releasing strain in the curved substrates. Tuning the carbon substrate with a desirable strain is able to reach a delicate balance between achieving the strong Cu–O interaction and maintaining the substantial Cu bonding with the original surrounding atoms. This balance maximizes the charge transferred from Cu atom to O2, thus greatly favoring the ORR activity. Our work discloses the structure–function relationship of SACs in terms of carbon substrates, and provides new insights into the mechanism of carbon substrates on the activity expression of embedded single-atom active sites, which can be potentially extended to other catalytic systems. This finding paves a new pathway to further design and the activity promotion of SACs.


Preparation of grapheme oxide (GO)46

5 g graphite powder (XFNANO, Co., Ltd.) was added into 180 mL concentrated H2SO4, and mechanically stirred for 1 h. 90 mL concentrated HNO3 and 25 g KMnO4 were slowly added into the mixture under ice bath in sequence. The mixture was stirred for 120 h in room temperature. Subsequently, 600 mL ultra-pure water was slowly poured into the mixture and stirred for another 2 h. The slurry turned yellow with bubbling after adding 30 mL H2O2. The mixture was centrifuged and washed with the mixture of 3 L water, 2 mL concentrated HCl and 5 mL H2O2, and then with 3 L ultra-pure water. The orange slurry was finally freeze-dried to obtain GO.

Preparation of oxidized carbon nanotube (OCNT)

CNT (XFNANO, Co., Ltd.) was pretreated in 6 mol L−1 HCl solution for 12 h to remove any impurities. After that, the CNT sample was filtrated, washed with ultra-pure water and freeze-dried. 30 mL concentrated sulfuric acid was added into 200 mg treated CNT in a three-neck round-bottom flask. After stirring for 30 min, 10 mL concentrated HNO3 was added dropwise, and the mixture was refluxed at 70 °C for 2 h and cooled down to room temperature. OCNT was collected by filtration, washing repeatedly with ultra-pure water and freeze-drying.

Preparation Cu/G and Cu/CNT catalysts

Typically, 20 mg GO (for Cu–G) or OCNT (for Cu/CNT) and 240 mg dicyandiamide (DICY) were ultrasonically mixed in 20 mL ultra-pure water. The dispersion was stirred overnight and freeze-dried. 100 mg resultant mixture was added into a quartz boat, which was entirely wrapped using a piece of Cu foil. After pyrolyzing at 600 °C for 2 h and 800 °C for another 1 h in Ar, black powder was collected and washed in 0.5 mol L−1 O2-saturated H2SO4 for 10 h at 80 °C. The product was washed with ultra-pure water, filtrated, and freeze-dried. After that, the final catalyst was obtained by pyrolyzing at 300 °C for 1 h in Ar. The samples with CNT substrates of 8 and 4 nm diameters were denoted as Cu/CNT-8 and Cu/CNT-4.

Electrochemical measurement

The mixture of 520 μL water and isopropanol (3:1: in volume), 30 μL 5 wt. % Nafion and 2.6 mg catalyst powder were sonicated to form a homogenous ink. A certain amount of ink was pipetted onto a GC rotating-disk electrode (RDE, 3 mm in diameter) or a rotating ring-disk electrode (RRDE, 5.61 mm in diameter) connected to PINE 636 rotating-disk electrode system, which was adopted as the working electrode. The catalyst loading was 0.4 mg cm−2 for RDE and 0.1 mg cm−2 for RRDE.

All electrochemical measurements were conducted in a standard three-electrode cell and recorded using CHI 720b electrochemical workstation. Reference and counter electrode were Hg/HgO electrode and Pt foil (1 cm × 1 cm), respectively. All potentials were converted to the reversible hydrogen electrode (RHE) reference scale, and the calibration was conducted by measuring the open circuit potential between Hg/HgO and Pt electrode immersed in H2-saturated 0.1 mol L−1 KOH at 25 °C.

RDE tests were performed in O2 saturated 0.1 mol L−1 KOH solution with a scan rate of 10 mV s−1 between 1 V and 0 V at different rotating rates, and the background current in Ar saturated KOH solution was subtracted to obtain the ORR polarization curves. RRDE tests were conducted at 1600 rpm and the Pt ring was polarized at 1.2 V. The durability of catalysts was evaluated by both potentiostatic and potentiodynamic procedures. Accelerated durability tests (ADTs) were conducted by potential sweeping between 0.6 V and 1.0 V for 10,000 cycles in O2-saturated KOH solution. The negative shift of half-wave potential was obtained based on the ORR polarization curves recorded before and after the ADTs. Potentiostatic i–t tests were measured at 1600 rpm at 0.65 V for 10 h, and the current loss was acquired.

Kinetic current density (ik) was calculated by Koutechy–Levich equation47:

$$\frac{1}{i}\,=\,\frac{1}{{i}_{{{{{{\rm{k}}}}}}}}\,-\,\frac{1}{B{\omega }^{1/2}}$$

where i is the ORR current density, ik is the kinetic current density, and ω is the rotating rate of RDE.

TOF and MA were calculated by the following equations assuming metal atoms as active sites for ORR48:

$${{{{{\rm{TOF}}}}}}\,=\,\frac{i{{{{{\rm{k}}}}}}M{{{{{\rm{metal}}}}}}}{{{{{{\mathcal{C}}}}}}{{{{{\rm{cat}}}}}}.\omega {{{{{\rm{metal}}}}}}F}$$
$${{{{{\rm{MA}}}}}}\,=\,\frac{i{{{{{\rm{k}}}}}}}{{{{{{\mathcal{C}}}}}}{{{{{\rm{cat}}}}}}.\omega {{{{{\rm{metal}}}}}}}$$

where ik is kinetic current density calculated from the K–L equation, Mmetal is molar mass of metal element, ccat. is mass loading of catalyst on electrode, ωmetal is mass ratio of metal in catalysts measured by ICP-OES, and F is Faraday constant.

Electron transfer number (n) and HO2 yield (HO2%) were calculated by the following equations49:

$${{{{{{\rm{HO}}}}}}}_{2}^{-} \% \,=\,200\,\times\, \frac{{I}_{{{{{{\rm{r}}}}}}}/N}{({I}_{{{{{{\rm{r}}}}}}}/N)\,+\,{I}_{{{{{{\rm{d}}}}}}}}$$

where Id is the current recorded on GC disk electrode, Ir is the current recorded on Pt ring electrode, and N is collection efficiency (37%).


TEM and HAADF scanning transmission electron-microscopy (HAADF-STEM) images were taken on samples dispersed onto Mo grids using a JEOL JEM2010 microscope operated at 200 kV, and a probe aberration corrected JEOL JEM-ARM200CF microscope operated at 200 kV, respectively, for the morphology characterization. Energy dispersive spectroscopy (EDS) was performed on NORAN System 7 equipped with TEM. X-ray photoelectron spectroscopy (XPS) was performed on a Physical Electronics PHI model 5700 instrument using Al Kα radiation for surface chemistry investigation. PerkinElmer Optima 5300DV ICP-OES System was used to determine the mass fraction of Cu. The crystal structure was analyzed by XRD using a Rigaku D/max-rB diffractometer with Cu Kα (λ = 1.5406 Å) radiation at step size of 0.026°. The Cu K-edge (8979 eV) XAFS was collected on a piece of carbon cloth (1 cm × 1 cm) coated with catalyst at a loading of 0.4 mg·cm−2 and taped with Kapton film on the back at the 1W1B beamline of Beijing Synchrotron Radiation Facility (BSRF). Ex situ spectra were measured directly in air, and in situ ones were collected by immersing catalyst-coated carbon cloth into O2 saturated 0.1 mol L−1 KOH solution at 1.0 V in a homemade three-cell system.

DFT calculations

The zero-gaped armchair CNTs of (29, 29) and (59, 59) were used as substrate to simulate the real diameters of ~4 and ~8 nm in Cu/CNT-8 and Cu/CNT-4, respectively. Periodic boundary conditions were along the tube axis. Cu atoms were fixed in the double-atom vacancies in CNT or graphene structures, with configuration of CuN2C2, to explore the substrate-dependent electronic and geometric properties. All DFT simulations were carried out using CP2K/Quickstep package50. The 2s, 2p electrons of O, C, and N atoms and the 4s, 3d electrons of Cu atoms were treated as valence electrons. Perdew–Burke–Ernzerhof functional with Grimme’s dispersion correction was adopted for the treatment of the electron–ion interactions51. The core electrons were represented by analytic Goedecker–Teter–Hutter pseudopotentials52. The Gaussian basis sets were double-ζ with one set of polarization functions (DZVP)53. The plane-wave cutoff for the electron density was 400 Ry.

Cu(111) was modeled by a four layer slab of p(4 × 4) super-cell and the size of simulation box is 10.224 × 10.224 × 21.261. In order to avoid spurious self-interactions, neighboring slabs were separated by a vacuum of 15 Å. Monkhorst-Pack k-point meshes of 4 × 4 × 1 were used for periodic models and an energy cutoff of 400 eV was employed for the plane-wave basis set. The convergence threshold for ionic steps in geometry optimization was 1 × 10−4 eV. Geometries were deemed converged when the forces on each atom were below 0.02 eV/Å. A frequency analysis was carried out on the stable states in order to confirm that these represent genuine minima. All of the electronic energies were corrected for zero-point energy (ZPE) contributions.

The change in Gibbs free energy for all intermediates was evaluated using the following relation:

$$\varDelta G\,=\,\varDelta E\,-\,T\varDelta S-neU$$

where E is the total energy obtained from DFT, T is the absolute temperature, S is entropy obtained directly from Atkins’ Physical Chemistry54, n is the number of transferred electrons, and U is the operating electrochemical potential vs. standard hydrogen electrode (SHE). In order to calculate the change in S of the molecules, O2, H2, and H2O molecules were considered to be in gas phase at room temperature and under ambient pressure, and the S of the adsorbed molecules were negligible55,56. The G of H2O (l), O2 (g), and OH were estimated from the following equations:

$${G}_{{{{{{{\rm{OH}}}}}}}^{-}}\,=\,{G}_{{{{{{{\rm{H}}}}}}}_{2}{{{{{\rm{O}}}}}}({{{{{\rm{l}}}}}})}\,-\,{G}_{{{{{{{\rm{H}}}}}}}^{+}}\,=\,{G}_{{{{{{{\rm{H}}}}}}}_{2}{{{{{\rm{O}}}}}}({{{{{\rm{l}}}}}})}\,-\,\frac{1}{2}{G}_{{{{{{{\rm{H}}}}}}}_{2}({{{{{\rm{g}}}}}})}\,+\,{k}_{{{{{{\rm{B}}}}}}}T{{{{{\rm{ln10}}}}}}\,\times\, {{{{{\rm{pH}}}}}}$$

where R is the gas constant, kB is the Boltzmann constant, T = 298.15 K, p = 0.035 bar and p0 = 1 bar. “H+ + e” was assumed to be in equilibrium with 1/2 H2, at pH = 0 and 0 V potential in SHE.

The adsorption energy (ΔEad) of the O-containing intermediates was calculated according to the following equation:

$$\varDelta {E}_{ad}\,=\,{E}_{{{{{{\rm{total}}}}}}}\,-\,{E}_{{{{{{\rm{substrate}}}}}}}\,-\,{E}_{{{{{{\rm{free}}}}}}}$$

where Etotal is the total energy of the adsorbent and the substrate, Esite and Efree are the energy of isolated substrate and free species, respectively.

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.  Source data are provided with this paper.


  1. Zhang, J. et al. Tuning the coordination environment in single-atom catalysts to achieve highly efficient oxygen reduction reactions. J. Am. Chem. Soc. 141, 20118–20126 (2019).

    CAS  PubMed  Article  Google Scholar 

  2. Chen, Y. et al. Enhanced oxygen reduction with single-atomic-site iron catalysts for a zinc-air battery and hydrogen-air fuel cell. Nat. Commun. 9, 5422 (2018).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  3. Jiang, H.-L. et al. From MOFs to single Fe atoms implanted n-doped porous carbons: efficient oxygen reduction in both alkaline and acidic media. Angew. Chem. Int. Ed. 9, 819–830 (2018).

    Google Scholar 

  4. Hou, Y. et al. Atomically dispersed nickel–nitrogen–sulfur species anchored on porous carbon nanosheets for efficient water oxidation. Nat. Commun. 10, 1392 (2019).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  5. Cao, L. et al. Dynamic oxygen adsorption on single-atomic ruthenium catalyst with high performance for acidic oxygen evolution reaction. Nat. Commun. 10, 4849 (2019).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  6. Lei, C. et al. Fe-N4 sites embedded into carbon nanofiber integrated with electrochemically exfoliated graphene for oxygen evolution in acidic medium. Adv. Energy Mater. 8, 1801912 (2018).

    ADS  Article  CAS  Google Scholar 

  7. Ren, W. et al. Isolated diatomic Ni‐Fe metal–nitrogen sites for synergistic electroreduction of CO2. Angew. Chem. Int. Ed. 58, 6972–6976 (2019).

    CAS  Article  Google Scholar 

  8. Cheng, Y. et al. Atomically dispersed transition metals on carbon nanotubes with ultrahigh loading for selective electrochemical carbon dioxide reduction. Adv. Mater. 30, 1706287 (2018).

    Article  CAS  Google Scholar 

  9. Jiang, K. et al. Isolated Ni single atoms in graphene nanosheets for high-performance CO2 reduction. Energy Environ. Sci. 11, 893–903 (2018).

    CAS  Article  Google Scholar 

  10. Sun, Y. et al. Activity-selectivity trends in the electrochemical production of hydrogen peroxide over single-site metal-nitrogen-carbon catalysts. J. Am. Chem. Soc. 141, 12372–12381 (2019).

    CAS  PubMed  Article  Google Scholar 

  11. Li, Z. et al. Iridium single-atom catalyst on nitrogen-doped carbon for formic acid oxidation synthesized using a general host–guest strategy. Nat. Chem. 12, 764–772 (2020).

    PubMed  Article  CAS  Google Scholar 

  12. Zang, W. et al. Copper single atoms anchored in porous nitrogen-doped carbon as efficient pH-universal catalysts for the nitrogen reduction reaction. ACS Catal. 9, 10166–10173 (2019).

    CAS  Article  Google Scholar 

  13. Chen, W. et al. Rational design of single molybdenum atoms anchored on N-doped carbon for effective hydrogen evolution reaction. Angew. Chem. Int. Ed. 56, 16086–16090 (2017).

    CAS  Article  Google Scholar 

  14. Wan, J. et al. In situ phosphatizing of triphenylphosphine encapsulated within metal-organic frameworks to design atomic Co1-P1N3 interfacial structure for promoting catalytic performance. J. Am. Chem. Soc. 142, 8431–8439 (2020).

    CAS  PubMed  Article  Google Scholar 

  15. Gao, J. et al. Enabling Direct H2O2 production in acidic media through rational design of transition metal single atom catalyst. Chem 6, 658–674 (2020).

    CAS  Article  Google Scholar 

  16. Xiao, M. et al. Climbing the apex of the ORR volcano plot via binuclear site construction: electronic and geometric engineering. J. Am. Chem. Soc. 141, 17763–17770 (2019).

    CAS  PubMed  Article  Google Scholar 

  17. Zitolo, A. et al. Identification of catalytic sites in cobalt-nitrogen-carbon materials for the oxygen reduction reaction. Nat. Commun. 8, 957 (2017).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  18. Zhang, N. et al. High-density planar-like Fe2N6 structure catalyzes efficient oxygen reduction. Matter 3, 509–521 (2020).

    Article  Google Scholar 

  19. Mun, Y. et al. Versatile strategy for tuning ORR activity of a single Fe-N4 site by controlling electron-withdrawing/donating properties of a carbon plane. J. Am. Chem. Soc. 141, 6254–6262 (2019).

    CAS  PubMed  Article  Google Scholar 

  20. Wang, H. et al. Impacts of imidazolate ligand on performance of zeolitic-imidazolate framework-derived oxygen reduction catalysts. ACS Energy Lett. 4, 2500–2507 (2019).

    CAS  Article  Google Scholar 

  21. Pan, F. et al. Pore-edge tailoring of single-atom iron–nitrogen sites on graphene for enhanced CO2 reduction. ACS Catal. 10, 10803–10811 (2020).

    CAS  Article  Google Scholar 

  22. Xiong, Y. et al. Single-atom Rh/N-doped carbon electrocatalyst for formic acid oxidation. Nat. Nanotechnol. 15, 390–397 (2020).

    ADS  CAS  PubMed  Article  Google Scholar 

  23. Moreno, J., Aspera, S., David, M. & Kasai, H. A computational study on the effect of local curvature on the adsorption of oxygen on single-walled carbon nanotubes. Carbon N. Y. 94, 936–941 (2015).

    CAS  Article  Google Scholar 

  24. Eckert, V. et al. Investigation of the surface properties of different highly aligned N-MWCNT carpets. Carbon N. Y. 141, 99–106 (2019).

    CAS  Article  Google Scholar 

  25. Chai, G. L. & Guo, Z. X. Highly effective sites and selectivity of nitrogen-doped graphene/CNT catalysts for CO2 electrochemical reduction. Chem. Sci. 7, 1268–1275 (2016).

    CAS  PubMed  Article  Google Scholar 

  26. Chai, G. L., Hou, Z., Shu, D. J., Ikeda, T. & Terakura, K. Active sites and mechanisms for oxygen reduction reaction on nitrogen-doped carbon alloy catalysts: stone-wales defect and curvature effect. J. Am. Chem. Soc. 136, 13629–13640 (2014).

    CAS  PubMed  Article  Google Scholar 

  27. Zhao, L. et al. Density functional study of hydrogen evolution on cobalt-embedded carbon nanotubes: effects of doping and surface curvature. ACS Appl. Nano Mater. 1, 6258–6268 (2018).

    CAS  Article  Google Scholar 

  28. Han, G. et al. High loading single-atom Cu dispersed on graphene for efficient oxygen reduction reaction. Nano Energy 66, 104088 (2019).

    CAS  Article  Google Scholar 

  29. Wang, P. et al. Atomically dispersed cobalt catalyst anchored on nitrogen-doped carbon nanosheets for lithium-oxygen batteries. Nat. Commun. 11, 1576 (2020).

    ADS  CAS  PubMed  PubMed Central  Article  Google Scholar 

  30. Han, X. et al. Atomically dispersed binary Co‐Ni sites in nitrogen‐doped hollow carbon nanocubes for reversible oxygen reduction and evolution. Adv. Mater. 31, 1905622 (2019).

    CAS  Article  Google Scholar 

  31. Xie, W. et al. Single‐atomic‐Co electrocatalysts with self‐supported architecture toward oxygen‐involved reaction. Adv. Funct. Mater. 29, 1906477 (2019).

    CAS  Article  Google Scholar 

  32. Li, J. et al. Thermally driven structure and performance evolution of atomically dispersed FeN4 sites for oxygen reduction. Angew. Chem. Int. Ed. 58, 18971–18980 (2019).

    CAS  Article  Google Scholar 

  33. Gupta, S. et al. Highly active and stable graphene tubes decorated with FeCoNi alloy nanoparticles via a template‐free graphitization for bifunctional oxygen reduction and evolution. Adv. Energy Mater. 6, 1601198 (2016).

    Article  CAS  Google Scholar 

  34. Park, S., Srivastava, D. & Cho, K. Generalized chemical reactivity of curved surfaces: carbon nanotubes. Nano Lett. 3, 1273–1277 (2003).

    ADS  CAS  Article  Google Scholar 

  35. Yang, Z. et al. Boosting oxygen reduction catalysis with Fe–N4 sites decorated porous carbons toward fuel cells. ACS Catal. 9, 2158–2163 (2019).

    CAS  Article  Google Scholar 

  36. Ania, C. O., Seredych, M., Rodriguez-Castellon, E. & Bandosz, T. J. New copper/GO based material as an efficient oxygen reduction catalyst in an alkaline medium: the role of unique Cu/rGO architecture. Appl. Catal. B Environ. 163, 424–435 (2015).

    CAS  Article  Google Scholar 

  37. Jernigan, G. G. & Somorjai, G. A. Carbon monoxide oxidation over three different oxidation states of copper: metallic copper, copper (I) oxide, and copper (II) oxide—a surface science and kinetic study. J. Catal. 147, 567–577 (1994).

    CAS  Article  Google Scholar 

  38. Kim, J. Y., Rodriguez, J. A., Hanson, J. C., Frenkel, A. I. & Lee, P. L. Reduction of CuO and Cu2O with H2: H embedding and kinetic effects in the formation of suboxides. J. Am. Chem. Soc. 125, 10684–10692 (2003).

    CAS  PubMed  Article  Google Scholar 

  39. Shen, H. et al. Atomically FeN2 moieties dispersed on mesoporous carbon: a new atomic catalyst for efficient oxygen reduction catalysis. Nano Energy 35, 9–16 (2017).

    CAS  Article  Google Scholar 

  40. Jiang, R. et al. Edge-site engineering of atomically dispersed Fe–N4 by selective C–N bond cleavage for enhanced oxygen reduction reaction activities. J. Am. Chem. Soc. 140, 11594–11598 (2018).

    CAS  PubMed  Article  Google Scholar 

  41. Ji, D. et al. Atomically transition metals on self‐supported porous carbon flake arrays as binder‐free air cathode for wearable zinc–air batteries. Adv. Mater. 31, 1808267 (2019).

    Article  CAS  Google Scholar 

  42. Jiang, H. et al. Defect-rich and ultrathin N doped carbon nanosheets as advanced trifunctional metal-free electrocatalysts for the ORR, OER and HER. Energy Environ. Sci. 12, 322–333 (2019).

    CAS  Article  Google Scholar 

  43. Tang, C. et al. Coordination tunes selectivity: two-electron oxygen reduction on high-loading molybdenum single-atom catalysts. Angew. Chem.—Int. Ed. 59, 9171–9176 (2020).

    CAS  Article  Google Scholar 

  44. Niyogi, S. et al. Chemistry of single-walled carbon nanotubes. Acc. Chem. Res. 35, 1105–1113 (2002).

    CAS  Article  Google Scholar 

  45. Haddon, R. C. Chemistry of the fullerenes: the manifestation of strain in a class of continuous aromatic molecules. Science 261, 1545–1550 (1993).

    ADS  CAS  PubMed  Article  Google Scholar 

  46. Sun, Y. et al. Boron-doped graphene as promising support for platinum catalyst with superior activity towards the methanol electrooxidation reaction. J. Power Sources 300, 245–253 (2015).

    ADS  CAS  Article  Google Scholar 

  47. Pampel, J. & Fellinger, T.-P. Opening of bottleneck pores for the improvement of nitrogen doped carbon electrocatalysts. Adv. Energy Mater. 6, 1502389 (2016).

    Article  CAS  Google Scholar 

  48. Gong, L. et al. Bridge bonded oxygen ligands between approximated FeN4 sites confer catalysts with high ORR performance. Angew. Chem. Int. Ed. 59, 13923–13928 (2020).

    CAS  Article  Google Scholar 

  49. Ferrero, G. A. et al. Fe-N-doped carbon capsules with outstanding electrochemical performance and stability for the oxygen reduction reaction in both acid and alkaline conditions. ACS Nano 10, 5922–5932 (2016).

    CAS  PubMed  Article  Google Scholar 

  50. VandeVondele, J. et al. Quickstep: fast and accurate density functional calculations using a mixed gaussian and plane waves approach. Comput. Phys. Commun. 167, 103–128 (2005).

    ADS  CAS  Article  Google Scholar 

  51. Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).

    ADS  PubMed  Article  CAS  Google Scholar 

  52. Goedecker, S., Teter, M. & Hutter, J. Separable dual-space gaussian pseudopotentials. Phys. Rev. B 54, 1703–1710 (1996).

    ADS  CAS  Article  Google Scholar 

  53. Seifitokaldani, A. et al. Hydronium-induced switching between CO2 electroreduction pathways. J. Am. Chem. Soc. 140, 3833–3837 (2018).

    CAS  PubMed  Article  Google Scholar 

  54. Atkins, P. W., De Paula, J. & Keeler, J. Atkins’ Phys. Chem. 870–878 (Oxford University Press, 2018).

  55. Shin, D., Sinthika, S., Choi, M., Thapa, R. & Park, N. Ab initio study of thin oxide–metal overlayers as an inverse catalytic system for dioxygen reduction and enhanced CO tolerance. ACS Catal. 4, 4074–4080 (2014).

    CAS  Article  Google Scholar 

  56. Wang, Y., Yuan, H., Li, Y. & Chen, Z. Two-dimensional iron-phthalocyanine (Fe-Pc) monolayer as a promising single-atom-catalyst for oxygen reduction reaction: a computational study. Nanoscale 7, 11633–11641 (2015).

    ADS  CAS  PubMed  Article  Google Scholar 

Download references


This work is supported by the National Natural Science Foundation of China (grant nos. 51634003, 21433003, and 22102208), National Key Research and Development Program of China (no. 2016YFB0101207), and the Heilongjiang Touyan Innovation Team Program (HITTY-20190033).

Author information

Authors and Affiliations



G.H. and C.D. designed the study, contributed to sample synthesis, characterization, and paper organization. X.Z. and J.C. performed DFT computation and helped with the analysis of mechanism. Z.W., W.L., and T.Y. performed XAFS and contributed to the related data fitting as well as analysis. Q.Z. and L.G. contributed to electron-microscopy characterization. Y.G. and G.Y. provided valuable suggestions to the experiment.

Corresponding author

Correspondence to Chunyu Du.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Oyinkansola Romiluyi, Jeng-Han Wang and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Source data

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Han, G., Zhang, X., Liu, W. et al. Substrate strain tunes operando geometric distortion and oxygen reduction activity of CuN2C2 single-atom sites. Nat Commun 12, 6335 (2021).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing