Nanoparticles suppress fluid instabilities in the thermal drawing of ultralong nanowires

Abstract

Ultra-long metal nanowires and their facile fabrication have been long sought after as they promise to offer substantial improvements of performance in numerous applications. However, ultra-long metal ultrafine/nanowires are beyond the capability of current manufacturing techniques, which impose limitations on their size and aspect ratio. Here we show that the limitations imposed by fluid instabilities with thermally drawn nanowires can be alleviated by adding tungsten carbide nanoparticles to the metal core to arrive at wire lengths more than 30 cm with diameters as low as 170 nm. The nanoparticles support thermal drawing in two ways, by increasing the viscosity of the metal and lowering the interfacial energy between the boron silicate and zinc phase. This mechanism of suppressing fluid instability by nanoparticles not only enables a scalable production of ultralong metal nanowires, but also serves for widespread applications in other fluid-related fields.

Introduction

Ultra-long metal ultrafine/nanowires (10s to 100s of nanometers in diameter) with embedded functionalities and their facile fabrication (e.g., thermal drawing of micro preform) have been long sought after as they promise to offer substantially improved performance in numerous applications such as micro-structured photonic crystal fibers1, optical micro-/nano-fibers2, electronics in fibers3, fiber-based metamaterials4,5, fibers as a novel platform for sensing devices6, studying chemical reactions7, multi-material functional fibers8,9, and more recently fibers as a platform for fabrication of nanowires and nanoparticles10,11,12,13. However, most crystalline metal nanowires with high aspect ratio are beyond the capability of current manufacturing techniques11, due to the fluid instability induced by a low viscosity of molten metals and the large interfacial energy with the cladding, despite that reliable drawing of indefinitely long amorphous semiconductor and polymer nanowires has been achieved14,15.

Metal microwire fabrication by thermal drawing in a glass cladding, known as the Taylor-wire process, has been in practice for decades. As this conventional technique combines with the stack-and-draw approach, the fabrication of fine metal wires becomes possible16. However, little success has been reported to fabricate long wires with a diameter of <1000 nm out of metals, especially those of higher melting temperatures, such as gold (Au), copper (Cu), zinc (Zn), and their alloys. Thermally drawn continuous Cu and Cu alloy microwires of 4 μm in diameter have been demonstrated17,18. Au microwires of 4 μm diameter were fabricated over a length of several centimeters, and this continuous length shrank to 20 μm as their diameter was reduced to 260 nm19. Fabrication of discontinuous copper–phosphor (CuP) wire with a diameter of 500 nm and a length of tens of micrometers has been reported using borosilicate glass cladding20. Fiber drawing via laser-based heat source pulling of short pieces of platinum (Pt) microwires has been used to fabricate quartz-sealed Pt nanowires. The resultant fibers were tapered down to 10 nm in diameter yet with a length of only 5 mm21. Alternatively, a polyol process, which is the synthesis of metal-containing compounds in ethylene glycol, was used to fabricate Ag nanowires with a length up to 230 μm and a diameter of 60–90 nm22,23. Low-melting-temperature metals such as tin (Sn), lead (Pb), bismuth (Bi), indium (In), and their alloys are mostly thermally drawn in polymer cladding. The smallest diameter reported for metal wires that can be reliably drawn into indefinitely long arrays is about 4 μm and is achieved from Sn0.95Ag0.05 alloy with PES cladding11. Droplets, discontinuities, and structural deformation would be observed upon further size reduction. Nevertheless, thermally drawn functional fibers embedding indium wires with a diameter approaching 1 µm have been demonstrated24. While low-melting-temperature Pb–Sn alloys and Bi nanowires with a diameter down to 50 nm were reported, no experimental evidence was provided to support their continuity over the claimed drawn length25.

The fundamental reason that long metal nanowire cannot be fabricated is fluid instability, described by the Tomotika model. Tomotika model expresses the dispersion relation of a long cylinder of viscous fluid jet surrounded by another indefinitely long viscous medium26, where instability was introduced by perturbation-caused equilibrium surface deformation27, also called varicose perturbation. It analytically expresses the surface perturbation of the fluid jet as an amplified wave under ideal conditions. This model also defines the term “associated instability growth time,” which describes the time length when the liquid thread breaks into droplets. Thus it could essentially guide the thermal fiber drawing for the fundamental optimization of drawing parameters for indefinitely long microwires/nanowires. Optimization of experimental settings, such as drawing speed and temperature, could successfully produce ultra-long semiconductors nanowires of 10 nm in diameter by thermal drawing, due to their high viscosity and low interfacial energy with cladding. Research has also shown that a high stretching force could result in a certain degree of instability suppression28.

However, there are still great challenges when the scalable production of metal wires below a few hundreds of nanometers in diameter is needed, because the high interfacial energy between molten metals and glass claddings makes the associated instability growth time too short when the core diameter reaches nanometer scale. An alternative way to realize high-temperature metal nanowires is bottom–up methods, such as chemical synthesis, which is costly, non-scalable, and challenging to apply for industrial manufacturing.

Here we show that the limitations imposed by fluid instabilities with thermally drawn nanowires can be alleviated by adding tungsten carbide (WC) nanoparticles to the metal core to arrive at wire lengths >30 cm with diameters as low as 170 nm. In this study, thermally stable WC nanoparticles were incorporated in zinc to manufacture Zn-WC nanocomposite as the core material in the thermal drawing process. The addition of nanoparticles promoted the fabrication capability of the nanowire by increasing the viscosity and reducing the interfacial energy between borosilicate and Zn29. This new mechanism of suppressing fluid instability by nanoparticles not only enables a scalable production of ultra-long metal nanowires but also serves for widespread applications in other fluid-related fields.

Results

Nanoparticle-enabled control of fluid instability in thermal drawing of metal wires

Tomotika dispersion relation is defined as:

$$\tau ^\prime = \frac{\tau }{{D_{{\mathrm{core}}}}} = \frac{{\mu _{{\mathrm{clad}}}}}{{\gamma \cdot G\left( {x,\frac{{\mu _{{\mathrm{core}}}}}{{\mu _{{\mathrm{clad}}}}}} \right)}},$$
(1)
$$x = \frac{{\pi D_{{\mathrm{core}}}}}{\lambda },$$
(2)
$$G = \max \left[ {\left( {1 - x^2} \right) \cdot {\Phi}\left( {x,\frac{{\mu _{{\mathrm{core}}}}}{{\mu _{{\mathrm{clad}}}}}} \right)} \right],$$
(3)

where τ′ is the associated instability growth time, τ is the instability growth time (inverse of the instability growth rate), Dcore is the diameter of the core, μclad and μcore are the viscosities of the core and cladding, respectively, γ is interfacial energy between the core and cladding, λ is the varicosity wavelength, and Φ is a function related to x and viscosity ratio μcore/μclad, containing modified Bessel functions. τ′ implies the capability of nanowire fabrication, where larger τ′ refers to a higher capability. In general cases, x falls between 0 and 1. In an ideal case without additional boundary constrains, G defines the maximum instability and the varicosity wavelength at a predefined viscosity ratio. Generally, increasing μcore results in reduced G, thus increasing μcore (Supplementary Note 1 and Supplementary Fig. 1).

Figure 1a demonstrates the theoretical calculation of the associated instability growth time concerning the core material viscosity and interfacial energy, according to the Tomotika model, through Matlab. Cladding viscosity for all systems is assumed to be 106 Pa·s, a typical value in thermal drawing. Semiconductors with even lower interfacial energy and higher viscosity, like selenium (Se) and As2Se3, can be fabricated to indefinitely long nanowires with diameters of <100 nm, indicated by yellow dots. Low-melting-temperature metals like tin (Sn), bismuth (Bi), lead (Pb), and indium (In), within polymer claddings, have relatively lower interfacial energy, leading to the manufacturing of indefinitely long wires of 4 µm, indicated by green dots11. Metals with high melting temperatures, like zinc (Zn), copper (Cu), silver (Ag), gold (Au), and platinum (Pt), obtain high interfacial energy in glass claddings, indicated by cyan dots. Thus low associated instability growth time results in little success in the fabrication of ultra-long nanowire. It argues for the viability of nanowire fabrication using thermal fiber drawing for materials with high associated instability growth time.

Fig. 1: Theoretical analysis of fluid instability in thermal drawing in multiple systems.
figure1

a Associated instability growth time vs. core material interfacial energy and viscosity under the condition that the cladding viscosity is 106 Pa·s. Data adapted from the literature are specified in Supplementary Table 2. Zinc-WC/borosilicate has been demonstrated to enhance the associated instability growth time by adding nanoparticles to the core material for interfacial energy reduction and viscosity enhancement, as indicated by the cyan arrow. High-melting-temperature metals (Zn, Cu, Au), low-melting-temperature metals (SnAg5, Sn, Bi, Ge), and semiconductors (Se, As2Se3) have been marked on the graph, indicated by cyan, green, and yellow dots, respectively. b Theoretical associated instability growth time of Zn-WC nanocomposite as the core material in borosilicate glass cladding, concerning temperature and nanoparticle concentration. c The associated instability growth time vs. drawing temperature for Zn-WC/borosilicate system. At a typical drawing temperature of 1080–1100 K, 15 vol.% nanoparticles efficiently enable the fluid instability control.

Zn-10 vol.%WC (Zn-10WC)/borosilicate was used as the model material system to demonstrate the fluid instability control by nanoparticles in thermal fiber drawing. The viscosity of Zn-10WC was measured 118 mPa·s at the melting temperature, compared with pure Zn (6 mPa·s), characterized by the modified capillary method, shown in Supplementary Table 1. The contact angle of Zn-10WC/borosilicate was measured to be about 57°, and the corresponding interfacial energy was thus estimated to be 130.6 mJ/m2, shown in Supplementary Note 2 and Supplementary Fig. 2. A typical viable method to enable fluid stabilization of varicose perturbation is by tuning the drawing temperature, but lowering the drawing temperature can enhance the viscosity of cladding material and prohibits high volume production. By applying Zn-WC nanocomposite as the core in thermal fiber drawing, τ could be significantly increased, due to the increased core viscosity and decreased interfacial energy, shown in Fig. 1a, b. Both core and cladding viscosities are temperature-dependent in this simulation30,31. It stabilizes the liquid perturbation during thermal fiber drawing without compromising drawability, as shown in Fig. 1c. At a typical drawing temperature of 1080 K, 15 vol.% WC nanoparticle could theoretically enhance the associated instability growth time to >20 times.

Nanowire fabrication by thermal drawing

Zn-10 vol.% WC microwires/nanowires were obtained by thermal fiber drawing (Supplementary Fig. 3) with optimized experimental settings (Supplementary Table 3) for three times, while the drawn fiber was inserted into another borosilicate capillary glass tube for the next drawing. Drawn fibers were characterized by optical microscopy and scanning electron microscopy (SEM) for thickness measurement and continuity verification. The diameter of nanocomposite microwires/nanowires were measured, decreasing from 70 μm (Fig. 2a, b) to 5.8 μm (Fig. 2c, d) and eventually to 170 nm (Fig. 2e, f). Zn-WC microwires of 70 μm from the first drawing were polished from the side surface and were characterized by SEM, indicating a homogeneous WC nanoparticle dispersion, shown in Supplementary Fig. 4. Energy-dispersive X-ray spectroscopy (EDS) line scanning was performed to measure the intensity of element Zn across the nanowire cross-section (indicated by the yellow arrow in Fig. 2f) to compensate for the resolution limitation, showing that Zn-WC nanocomposite wire reached a diameter of 171 nm (full width at half maximum) in Fig. 2g.

Fig. 2: Characterization of Zn-WC nanowires embedded in glass cladding.
figure2

a, b Cross-sectional optical/SEM images of Zn-WC nanocomposite nanowires after the first drawing (70 µm). c, d Cross-sectional SEM images after the second drawing (5.8 µm). e, f Cross-sectional SEM images after the third drawing (170 nm). g EDS line scanning of Zn-WC nanowire on the cross-section, indicated by the yellow arrow in f. The diameter of the nanowire was measured to be 170 nm.

Characterization of nanowire integrity

Although optical micrographs have resolution limits, it could still be utilized to verify the continuity of the 170 nm Zn-WC nanocomposite wire, since the broken wires, as the results of the Plateau–Rayleigh fluid instability, were usually observed with microscale gaps and satellite metal droplets32. The nanowires within the borosilicate cladding were characterized for continuity verification, and the results showed the longest metal nanowire of 31 cm within a glass cladding, as shown in Fig. 3a, b. Even though the curved borosilicate surfaces induced light distortion, the highly bright metal surface could verify the integrity of the Zn nanowires (Supplementary Fig. 5). Furthermore, electrical conductivity was measured for multiple wire segments of 1.5 cm to validate the integrity of the nanowire (Supplementary Fig. 6). Furthermore, anisotropic oxide etching was performed on a small piece of nanowire preserved in glass cladding to expose the bare Zn-WC nanowire. SEM images from the top view and the isometric view were shown in Fig. 3c–f. WC nanoparticles could be observed on the surface of the nanowire, instead of being embedded in the nanowire. The Zn-WC nanocomposite nanowires were also cut using the focused ion beam (FIB) for cross-sectional atomic analysis by transmission electron microscopy (TEM; Fig. 3g). Zn and WC crystalline phase and their corresponding images obtained from fast Fourier transform are shown in Fig. 3h–m.

Fig. 3: Characterization of Zn-WC ultrafine/nanowires integrity.
figure3

a 31-cm-long Zn-WC nanowire measured by a ruler. b Demonstration of the nanowire continuity characterization by optical microscope. SEM images of the top view (c, d) and isometric view (e, f) of Zn-WC nanocomposite nanowire after AOE deep etching. d, f are the corresponding magnified images. g TEM characterization of the cross-sectional nanowire samples, as shown in d, f by the yellow dashed line. h, j, l are the TEM images of high magnification for Zn and WC nanoparticles and surrounding borosilicate glass, respectively (scale bar 1 nm). i, k, m are the corresponding images of the diffraction pattern, indicating polycrystalline, single crystalline, and amorphous structures.

The successful fabrication of 170 nm nanowire validated the theoretical prediction of the promotion of instability growth time of τ by using WC nanoparticles to tune viscosity and interfacial energy of Zn melt. τ of Zn-10WC was calculated to be 1.3 s, which is of the same orders of magnitude as the experimental time, 3.1 s, according to Supplementary Eq. (1). Such theoretical results are not accurate enough without considering the stretching force, but still, sufficiently support the strategy of using nanoparticle to suppress the liquid instability. Besides the inherent property modification of the core metal, it should be noted that additional nanoparticle effects could contribute to the further enhancement of τ′. Nanoparticles at the Zn–borosilicate interface could induce lower interfacial energy locally, and they could act as boundary pinning points to reduce the wavelength of varicosity (Supplementary Note 3 and Supplementary Fig. 7).

As benchmarked in Fig. 4 with metal nanowires manufactured by various methods, including thermal fiber drawing, electrospinning, and laser drawn-cast process, the nanocomposite nanowire demonstrated in this work exhibits an aspect ratio of 1.8 × 106. It is noteworthy that the result even exceeds that of metal nanowires produced by chemical synthesis33,34,35, which has been one of the most reliable methods for metal nanowire fabrication to date.

Fig. 4: Comparison of metal nanowires among different fabrication methods.
figure4

The manufacturing methods of high-melting-temperature metal nanowires include thermal fiber drawing, electrospinning, laser drawn-cast process, and chemical synthesis. The green dash lines indicated the limitation that such traditional methods are unable to achieve nano/submicron metal wire fabrication with an aspect ratio of >106. Zn-WC has fundamentally enhanced the instability growth time to realize a much longer nanowire fabrication. Data adapted from the literature are specified in Supplementary Table 4.

In summary, this study presents a nanocomposite approach to fabricate metal nanowires with a high aspect ratio by overcoming fluid instability during thermal drawing. Nanoparticles modified the viscosity of the molten metal and interfacial energy between metal core and cladding when the metal wire diameter is at micrometers. However, once the diameter approaches a few hundreds of nanometers, where the fluid instability becomes almost impossible to control in conventional thermal drawing, nanoparticles can induce low interfacial energy and a pinning effect against the breakdown of the fine molten metal thread inside the glass cladding during thermal drawing. The success in drawing ultra-long metal nanowires by thermal drawing not only offers an exceptional aspect ratio of any metal nanowires produced by any methods so far but also demonstrates the feasibility of fabrication of long metal nanowire by a top-down method.

Methods

Fabrication of Zn-WC nanocomposite

WC nanoparticles (average size of 150 nm, US Research Nanomaterials, Inc.) and Zn powders (50 µm, Fisher Scientific) were first mixed by a mechanical shaker (SK-O330-Pro) at 300 RPM for an hour. The powder mixture was loaded to a cylindrical stainless-steel mold with an inner diameter of 2 cm, followed by cold compaction using a hydraulic press (Carver Laboratory Press, Fred S Carver Inc.) with 58 kN force to obtain Zn-10WC (vol.%) pellets. The Zn-WC nanocomposite pellets were then placed in an alumina crucible and were melted in an electric resistance furnace under argon (Ar) and sulfur hexafluoride (SF6) gas flow at 450 °C to disperse nanoparticles and eliminate porosity. Molten Zn-WC nanocomposite was then sucked into a 30-cm-long borosilicate glass tube (inner diameter: 1 mm, and outer diameter: 6.5 mm, National Quartz) by a vacuum pump to make the thermal drawing preforms. The 30-cm-long preform was finally fabricated through sealing both ends under vacuum by a high-temperature torch.

Thermal fiber drawing

The Zn-WC nanocomposite preform was fed into an electric resistance furnace with a constant feeding speed (vf). The temperature of the furnace was set to 820 °C (1093 K), which is an optimized temperature to obtain the most suitable cladding viscosity (106.6 Pa·s) for thermal drawing, after considering the softening point of borosilicate glass and the metal core–furnace temperature difference. The heated preform in the furnace was narrowed down when the temperature increased above the softening point, and the fiber was further pulled down at a constant speed (vp) by a motor-connected wheel. In a steady-state, the diameter of the drawn-out fiber is determined by the draw-down ratio Dr:

$$D_{\mathrm{r}} \equiv \frac{{v_{\mathrm{f}}}}{{v_{\mathrm{p}}}} = \left( {\frac{{d_{\mathrm{p}}}}{{d_{\mathrm{f}}}}} \right)^2,$$
(4)

where vf, vp, dp, and df are the fiber pulling speed, the preform feeding speed, the diameter of a preform, and the diameter of a drawn fiber, respectively. After the first drawing, the metal-in-glass fiber was collected and was inserted into another borosilicate glass tube, working as the preform for the next thermal drawing cycle. During the further drawing, layers of glass cladding could merge, forming a thicker cladding.

Sample preparation for characterization

The fiber was first mounted vertically on epoxy and polished to expose the metal core. Then the cross-section was polished, followed by 20-nm-thick Pt deposition and characterized under SEM at low excitation energy, while using FIB to etch off a thin layer on the top to prevent any polishing powder residues from interfering with the characterization. For characterization of bare wires, a combination of hydrofluoric acid (HF) wet etching and AOE oxide etching (STS MESC Multiplex AOE, SPTS Technologies Limited, 90 min) was performed. Due to the chemical reactivity of Zn, nanowires can barely be taken out of the borosilicate cladding massively by any scalable etching method to dissolve the glass claddings. Thus AOE etching was utilized to slowly remove the glass cladding residues after HF wet etching (35 min, 49% aqueous). The bare Zn-WC nanocomposite nanowires were finally exposed for characterization under SEM.

Data availability

The data that support the findings of this study are available from the corresponding author upon request.

References

  1. 1.

    Russell, P. Photonic crystal fibers: a historical account. IEEE Leos Newsl. 21, 11–15 (2007).

    Google Scholar 

  2. 2.

    Wang, P., Wang, Y. & Tong, L. Functionalized polymer nanofibers: a versatile platform for manipulating light at the nanoscale. Light Sci. Appl. 2, e102–e102 (2013).

    ADS  Article  Google Scholar 

  3. 3.

    Zou, D., Lv, Z., Cai, X. & Hou, S. Macro/microfiber-shaped electronic devices. Nano Energy 1, 273–281 (2012).

    CAS  Article  Google Scholar 

  4. 4.

    Argyros, A. Microstructures in polymer fibres for optical fibres, THz waveguides, and fibre-based metamaterials. Int. Sch. Res. Notices 2013, 785162 (2013).

  5. 5.

    Tuniz, A. et al. Drawn metamaterials with plasmonic response at terahertz frequencies. Appl. Phys. Lett. 96, 191101 (2010).

    ADS  Article  Google Scholar 

  6. 6.

    Ricciardi, A. et al. Lab-on-fiber devices as an all around platform for sensing. Opt. Fiber Technol. 19, 772–784 (2013).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Sparks, J. R., Sazio, P. J., Gopalan, V. & Badding, J. V. Templated chemically deposited semiconductor optical fiber materials. Annu. Rev. Mater. Res. 43, 527–557 (2013).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Abouraddy, A. et al. Towards multimaterial multifunctional fibres that see, hear, sense and communicate. Nat. Mater. 6, 336 (2007).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Tao, G., Stolyarov, A. M. & Abouraddy, A. F. Multimaterial fibers. Int. J. Appl. Glass Sci. 3, 349–368 (2012).

    CAS  Article  Google Scholar 

  10. 10.

    Kaufman, J. J. et al. Thermal drawing of high-density macroscopic arrays of well-ordered sub-5-nm-diameter nanowires. Nano Lett. 11, 4768–4773 (2011).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Yaman, M. et al. Arrays of indefinitely long uniform nanowires and nanotubes. Nat. Mater. 10, 494–501 (2011).

    ADS  CAS  Article  Google Scholar 

  12. 12.

    Kaufman, J. J. et al. In-fiber production of polymeric particles for biosensing and encapsulation. Proc. Natl Acad. Sci. USA 110, 15549–15554 (2013).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Kaufman, J. J. et al. Structured spheres generated by an in-fibre fluid instability. Nature 487, 463 (2012).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Suryavanshi, A. P., Hu, J. & Yu, M.-F. Meniscus-controlled continuous fabrication of arrays and rolls of extremely long micro-and nano-fibers. Adv. Mater. 20, 793–796 (2008).

    CAS  Article  Google Scholar 

  15. 15.

    Park, W. I., Zheng, G., Jiang, X., Tian, B. & Lieber, C. M. Controlled synthesis of millimeter-long silicon nanowires with uniform electronic properties. Nano Lett. 8, 3004–3009 (2008).

    ADS  CAS  Article  Google Scholar 

  16. 16.

    Ma, Z. et al. in Three-Dimensional Nanoarchitectures 117–132 (Springer, 2011).

  17. 17.

    Hou, J. et al. Metallic mode confinement in microstructured fibres. Opt. Express 16, 5983–5990 (2008).

    ADS  Article  Google Scholar 

  18. 18.

    Guan, Z., Hwang, I., Pan, S. & Li, X. Scalable manufacturing of AgCu40 (wt%)–WC nanocomposite microwires. J. Micro. Nano-Manuf. 6, 031008 (2018).

  19. 19.

    Tyagi, H. et al. Plasmon resonances on gold nanowires directly drawn in a step-index fiber. Opt. Lett. 35, 2573–2575 (2010).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Zhang, X., Ma, Z., Yuan, Z. Y. & Su, M. Mass-productions of vertically aligned extremely long metallic micro/nanowires using fiber drawing nanomanufacturing. Adv. Mater. 20, 1310–1314 (2008).

    CAS  Article  Google Scholar 

  21. 21.

    Percival, S. J., Vartanian, N. E. & Zhang, B. Laser-pulled ultralong platinum and gold nanowires. RSC Adv. 4, 10491–10498 (2014).

    CAS  Article  Google Scholar 

  22. 22.

    Araki, T. et al. Low haze transparent electrodes and highly conducting air dried films with ultra-long silver nanowires synthesized by one-step polyol method. Nano Res. 7, 236–245 (2014).

    CAS  Article  Google Scholar 

  23. 23.

    Jiu, J. et al. Facile synthesis of very-long silver nanowires for transparent electrodes. J. Mater. Chem. A 2, 6326–6330 (2014).

    CAS  Article  Google Scholar 

  24. 24.

    Tuniz, A., Lwin, R., Argyros, A., Fleming, S. C. & Kuhlmey, B. T. Fabricating metamaterials using the fiber drawing method. J. Vis. Exp. 18, e4299 (2012).

    Google Scholar 

  25. 25.

    Badinter, E., Ioisher, A., Monaico, E., Postolache, V. & Tiginyanu, I. Exceptional integration of metal or semimetal nanowires in human-hair-like glass fiber. Mater. Lett. 64, 1902–1904 (2010).

    CAS  Article  Google Scholar 

  26. 26.

    Tomotika, S. On the instability of a cylindrical thread of a viscous liquid surrounded by another viscous fluid. Proc. R. Soc. Lond. A 150, 322–337 (1935).

    ADS  Article  Google Scholar 

  27. 27.

    Donnelly, R. J. & Glaberson, W. Experiments on the capillary instability of a liquid jet. Proc. R. Soc. Lond. A 290, 547–556 (1966).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Zhao, J. & Li, X. A long wavelength model for manufacturing of continuous metal microwires by thermal fiber drawing from a preform. J. Micro. Nano-Manuf. 6, 011003 (2018).

  29. 29.

    Ma, C., Zhao, J., Cao, C., Lin, T.-C. & Li, X. Fundamental study on laser interactions with nanoparticles-reinforced metals—part II: effect of nanoparticles on surface tension, viscosity, and laser melting. J. Manuf. Sci. Eng. 138, 121002 (2016).

  30. 30.

    Fluegel, A., Varshneya, A. K., Earl, D. A., Seward, T. P. & Oksoy, D. in Melt Chemistry, Relaxation, and Solidification Kinetics of Glasses, Vol. 170 (eds Li, H. et al.) 129–143 (The American Ceramic Society, 2005).

  31. 31.

    Falke, W., Schwaneke, A. & Nash, R. Surface tension of zinc: the positive temperature coefficient. Metall. Trans. B 8, 301–303 (1977).

    Article  Google Scholar 

  32. 32.

    Shabahang, S., Kaufman, J., Deng, D. & Abouraddy, A. Observation of the Plateau-Rayleigh capillary instability in multi-material optical fibers. Appl. Phys. Lett. 99, 161909 (2011).

    ADS  Article  Google Scholar 

  33. 33.

    Zhang, D. et al. Synthesis of ultralong copper nanowires for high-performance transparent electrodes. J. Am. Chem. Soc. 134, 14283–14286 (2012).

    CAS  Article  Google Scholar 

  34. 34.

    Chang, Y., Lye, M. L. & Zeng, H. C. Large-scale synthesis of high-quality ultralong copper nanowires. Langmuir 21, 3746–3748 (2005).

    CAS  Article  Google Scholar 

  35. 35.

    Kim, F., Sohn, K., Wu, J. & Huang, J. Chemical synthesis of gold nanowires in acidic solutions. J. Am. Chem. Soc. 130, 14442–14443 (2008).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We thank Mr. Noah Bodzin for the assistance on FIB cutting and TEM sample preparation at UCLA. This work was supported by National Science Foundation (NSF) (Grant No. CMMI 1449395).

Author information

Affiliations

Authors

Contributions

X.L. conceived the idea and supervised the whole work; I.H. and Z.G. designed the study and conducted the thermal fiber drawing experiment. I.H., Z.G., and C.O.C. did the sample characterization of SEM and TEM; Z.G. conducted Matlab simulation and researched on the nanoparticle pinning theory; Z.G., C.O.C., W.T., and X.L. wrote the manuscript. All authors wrote the paper and discussed the results and commented on the manuscript.

Corresponding author

Correspondence to Xiaochun Li.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communications thanks Joshua Kaufman and the other anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Hwang, I., Guan, Z., Cao, C. et al. Nanoparticles suppress fluid instabilities in the thermal drawing of ultralong nanowires. Nat Commun 11, 5932 (2020). https://doi.org/10.1038/s41467-020-19796-5

Download citation

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing