Abstract
Metal-organic framework glasses feature unique thermal, structural, and chemical properties compared to traditional metallic, organic, and oxide glasses. So far, there is a lack of knowledge of their mechanical properties, especially toughness and strength, owing to the challenge in preparing large bulk glass samples for mechanical testing. However, a recently developed melting method enables fabrication of large bulk glass samples (>25 mm3) from zeolitic imidazolate frameworks. Here, fracture toughness (KIc) of a representative glass, namely ZIF-62 glass (Zn(C3H3N2)1.75(C7H5N2)0.25), is measured using single-edge precracked beam method and simulated using reactive molecular dynamics. KIc is determined to be ~0.1 MPa m0.5, which is even lower than that of brittle oxide glasses due to the preferential breakage of the weak coordinative bonds (Zn-N). The glass is found to exhibit an anomalous brittle-to-ductile transition behavior, considering its low fracture surface energy despite similar Poisson’s ratio to that of many ductile metallic and organic glasses.
Similar content being viewed by others
Introduction
Metal–organic frameworks (MOFs), which are porous hybrid materials formed from inorganic nodes connected to organic ligands, have potential applications in membrane-based gas sorption, gas separation, shock absorbers, catalysis, and ion transport1,2,3,4,5,6,7. However, MOF crystals are not available in bulk pieces. The newly emerged family of MOF glasses overcomes this challenge8,9, and displays numerous interesting features such as relatively high Poisson’s ratio10,11, high transparency12 and luminescence13, and in some cases microporosity14,15. A certain number of zeolitic imidazolate frameworks (ZIFs)16,17,18 can be melted and subsequently quenched to the glassy state before thermal decomposition. ZIFs have topology analogous to those of silica or zeolite networks, whose tetrahedron consists of a metal ion (e.g., Mg2+, Co2+, Zn2+, Li+ and B+) and four imidazolate-based ligands, connected by coordinative bonds14,16,17,19,20,21. An interesting member of the ZIF family is ZIF-62 (ZnIm1.75bIm0.25, where Im is imidazolate, C3H3N2−, and bIm is benzimidazolate, C7H5N2−) concerning its ultrahigh glass-forming ability and possibility to be prepared in large size for mechanical tests10,22. Structural studies14,16,17,19,20,21 have shown that the ZIF-62 glass and crystal exhibit long-range disorder and order, respectively.
Therefore, ZIF-62 glass is in this work chosen to be the object for investigating the mechanical properties of MOF glasses. In contrast to MOF glasses, the mechanical properties of crystalline MOFs have been studied extensively23. MOF crystals are typically characterized by relatively low moduli of elasticity14,23 and hardness14,23,24, but to our knowledge, the only reported fracture toughness (KIc) values are for two copper phosphonoacetate polymorphs, with KIc in the range of 0.08–0.33 MPa m0.5 as estimated by nanoindentation25. More generally, correlations between the mechanical properties and the extent of the network porosity have been observed, showing decreasing moduli and hardness with decreasing density14,23,26,27. Given the overall differences in the fracture mechanics of crystalline and glassy materials, such as lack of anisotropy and dislocation-type defects in glasses, there is a need to study the mechanical properties of MOF glasses. To our knowledge, the present work is the first one devoted to understanding the fracture behavior of melt-quenched MOF bulk glasses using a non-indentation technique, being in contrast to two recent studies11,15. Li et al.15 studied the scratch resistance and creep behavior of ZIF-4, ZIF-62, and ZIF-76 glasses by nanoindentation. Using strain-rate jump tests, the ZIF glass members were found to have similar strain-rate sensitivity to glassy polymers and Se-rich chalcogenide glasses. In another indentation study, Stepniewska et al.11 revealed the anomalous indentation cracking behavior of ZIF-62 glass by atomic force microscopy, and observed apparent shear bands on the indented faces, which are not typically observed in fully polymerized glasses. Although such indentation studies provide useful information on the surface deformation processes, they cannot easily reveal the strength and fracture toughness28, which are crucial properties for predicting the critical stress and flaw size that induce failure29. Indeed, to determine the suitability of MOF glasses for future applications, their mechanical properties including strength and fracture toughness need to be understood. This includes possible application fields within gas storage30,31, membrane technologies32, radioactive waste storage33, and photonics12,13, which all require knowledge of the underlying mechanical properties to ensure mechanical stability for optimal and reliable performance. However, both measurement and analysis of the fracture toughness of ZIF glasses are challenging for various reasons. First, only relatively small bulk samples of ZIF-62 glass can be produced by melt-quenching (pellets of 11 mm diameter and 1–2 mm thickness). Second, due to its low hardness (~0.6 GPa)11,15 and low Young’s modulus (~3–6 GPa)11,15, it is difficult to prepare and process specimens without deformation and breakage. Third, there is currently no standard method to determine fracture toughness of brittle materials shorter than 20 mm in length34.
Here, we study the fracture behavior of ZIF-62 glass in terms of its fracture toughness and flexural strength. Unlike the existing fracture toughness data for MOF crystals25, this work reports fracture toughness measurements of a MOF material with a non-indentation method. To overcome the experimental challenges listed above, we have performed careful sample preparation to obtain polished specimens with final dimensions of 1.5 × 1.9 × 10 mm3 and designed a new set-up for single-edge precracked beam (SEPB) measurement of fracture toughness, which complies with the span-beam ratio required in the ASTM standard34. To understand the structural origin of the fracture behavior of the ZIF-62 glass, we have also performed molecular dynamics (MD) simulations using a previously validated reactive force field (ReaxFF)35. Finally, we have also compared the fracture toughness values to theoretically predicted ones based on the bond strength and the crack path in the glass network. This work contributes to obtaining a general picture about the relation between the fracture and the chemical bonding types for different families of glasses.
Results
Molecular dynamics simulations
We initially validate the ability of the utilized ReaxFF MD potential to replicate the ZIF-62 glass structure. Figure 1a shows the differential correlation function (D(r)) from previous X-ray total scattering experiments27 and the present simulations. Good agreement between the number of peaks and intensities are found, with some minor differences in the peak positions. Overall, this suggests only minor differences between local order structures as determined by experiments and simulation, generally within 0.2 Å and similarly to what has been found for simulated ZIF-4 glass in the original paper introducing the potential35. Considering that we also find matching density values (1.60 g cm-3 for both present simulations and previous experiments27), we use this potential to simulate the fracture mechanism of the ZIF glass, especially given the explicit possibility for bond-breaking to occur in ReaxFF-based MD simulations.
Figure 1b shows an example of a stress(σ)-strain(ε) curve starting from a relaxed simulation box that is subjected to tensile strain until fracture to compute the ultimate strength (see Table 1). To estimate the C11 and C44 components of the stiffness matrix elements for an isotropic material, we calculate the slope of the stress–strain curve in the low-\(\varepsilon\) part of a simulation with smaller strain steps, as described in the Methods section (see inset of Fig. 1b). We show similar plots of the other used structures in Supplementary Fig. 1. The determined stiffness constants are then used to calculate the Young’s modulus (E) and Poisson’s ratio (ν), which are found to be 4.1 ± 0.9 GPa and 0.395 ± 0.035, respectively. The E value obtained from the simulation is slightly lower than that obtained from ultrasonic echography (Table 1) and slightly higher than that previously measured by Brillouin spectroscopy10. The ν value obtained from the simulation is also in between the values obtained from ultrasonic echography (Table 1 and ref. 11) and Brillouin spectroscopy10.
Next, we consider the simulated fracture behavior of the ZIF-62 glass. To this end, we employ the in silico method of Brochard et al.36, which has successfully been used to estimate the fracture toughness of a number of materials, including \(\alpha\)-cristabolite36, silica glass37, calcium aluminosilicate glass37, and calcium-silicate-hydrate gels38. The method involves the introduction of a precrack in the sample (to induce stress concentration), which is subsequently elongated normal to the longest dimension of the crack to induce bond rupture (i.e., mode I fracture). By computing the stress related to the forced elongation in the direction of strain, we obtain a stress–strain curve of the fracture process, which in turn can be used to estimate the fracture surface energy (γ). Figure 1c shows an example of an unrelaxed induced crack, while Supplementary Fig. 2 shows the same crack after relaxation, revealing notable relaxation of the structure around the crack, yet with some reformation of bonds across the crack surface. Similar or even less bond reformation has been found for other quenches. We ascribe this large relaxation of the crack to the ductile nature of the system at the nanoscale, but it has a negligible influence on the results of the following fracture simulations, as only 0.6 ± 0.2% of bonds are reformed during the structural relaxation of the crack.
Figure 1d presents an example of a stress–strain curve for the precracked ZIF-62 glass. For comparison, we included two other amorphous materials, a-SiO237 and a calcium aluminosilicate (CAS) glass37, for which the fracture process has been simulated using the same procedure with an induced precrack, although with a slightly different crack-to-box ratio. In the inset of Fig. 1d, the stress–strain curve of glassy ZIF-62 is magnified to highlight the large degree of nanoductility even in the presence of a precrack. While a-SiO2 features a very brittle fracture behavior, both the CAS glass and ZIF-62 glass show evidence of nanoductility. In the latter, complete fracture is typically achieved at an extreme strain of 70–130%. The remaining stress–strain curves are shown in Supplementary Fig. 3. Based on these data, we compute the critical energy release rate (GC) and KIc to be 1.96 ± 0.22 J m−2 and 0.097 ± 0.009 MPa m0.5, respectively. For one simulated structure, we increased the crack size (from 36 Å to 42 and 48 Å) and found no apparent relation between crack size and the resulting fracture toughness (see Supplementary Fig. 4). As it will be shown below, these results are in excellent agreement with the present experiments. For comparison, the values are roughly an order of magnitude lower than those for silica glass and a factor of 3-4 lower than those for the CAS glass37.
To quantify the degree of ductility, we evaluate the so-called brittleness index38 as \(B_{{\mathrm{index}}} = {\mathrm{2}}\gamma _sG_C^{ - {\mathrm{1}}}\), where \(\gamma _s\) is the surface energy estimated in a separate simulation (see Methods for details). We estimate the surface energy to be 0.69 J m−2, in good agreement with that reported previously for crystalline ZIF-8 (0.43–0.72 J m−2)39. This brittleness parameter thus gives a measure for how brittle or ductile a fracture is, where 1 is indicative of a perfectly brittle material (i.e., for which the fracture energy is solely used to create some new surface). We find the ZIF-62 glass to have \(B_{{\mathrm{index}}} = 0.70\), which is fairly similar to the value obtained for a disordered calcium-silicate-hydrate gel (0.62)38, but well below that of a-SiO2 glass (0.90). Despite the presence of nanoductility, the ZIF-62 glass shows no evidence of macro-ductility as it will be discussed in the following.
Fracture toughness and strength measurements
Figure 2a–c present the single-edge precracked beam (SEPB) method for determining KIc of glassy ZIF-62. SEPB is known as a self-consistent fracture toughness method29,34 for both ceramics and glasses. However, currently, the longest possible sample dimension of the ZIF-62 glass (10 mm) is lower than the shortest one recommended in the ASTM standard (20 mm)34. However, the three-point bending span of 7.5 mm (four times the beam height of 1.9 mm) is in the norm of the span-beam ratio of the ASTM standard34. To validate the present adapted SEPB method (see Methods section), we have initially used it to measure KIc of a standard soda lime silicate glass sample with dimensions of 1.5 × 1.9 × 10 mm3. The obtained result (0.72 ± 0.02 MPa m0.5, see Supplementary Table 1) is in excellent agreement with that obtained using the standard SEPB method (0.70 ± 0.01 MPa m0.5)29,40.
Figure 2a shows a typical Vickers-indented beam specimen, including an enlargement of the indentation area to show the typical five indents using a load of 2.5 N on the broadest side (B = 1.5 mm) of the beam. The five indents remain visible in the post-fracture image of the SEPB specimen, i.e., the precrack starts from the indents (Fig. 2b). The uneven state of the precrack front is not significant. By measuring the precrack length at various fractions (25%, 50%, and 75%) of B, we obtain the difference between the average precrack length and any measurement at 0.25B, 0.50B, and 0.75B to be acceptable according to the ASTM standard (less than 10%)34. An example of the load-deflection curve from the three-point bending experiment on the precracked specimen is shown in Fig. 2c, revealing a partially unstable fracture with instability at the maximum load (Pmax), which is required for not being influenced by stress corrosion40. KIc is then calculated from the precrack length and Pmax (see Methods section).
Table 1 presents a comparison of the results from SEPB experiments and MD simulations. Experimental KIc (0.104 ± 0.02 MPa m0.5) and γ (0.82 ± 0.31 J m-2, calculated using Eq. (8) in Methods) values agree well with the simulated ones, thus revealing low damage tolerance of the hybrid organic-inorganic network glass. The three-point bending strength is determined to be 8 ± 2 MPa (Fig. 2d), which is two orders of magnitudes lower than the simulated value (703 ± 87 MPa). Accordingly, the corresponding strain at fracture for the experiment is two orders of magnitude lower than that for the simulation. We infer that this difference is due to the difference in the surface flaw size distribution in the experimental specimen and the ideally flawless and surfaceless simulated specimen, as well as the major difference in sample size between experimental and simulated specimens. As a brittle solid, the surface flaw dependence of strength of experimental ZIF-62 glass is significant41. Similarly, the size of the simulated specimen (nanometer scale) limits the size of the obtainable defects, thus lowering the possibility of having defects with critical dimensions. In other words, experimental strength varies primarily with the surface flaw size and not with the strength of the flawless bulk material. This is also the reason why we introduce a precrack in both simulation and experiment to induce stress concentration and remove effects of surface flaws on fracture behavior.
Structural origin of ZIF-62 fracture behavior
To understand the structural origin of the low fracture toughness and fracture energy of the ZIF-62 glass observed in both experiments and simulations, we investigate the atomic-scale crack propagation mechanism using the ReaxFF-based MD simulations. By considering a representative example of the atomic configuration of the glass with an induced precrack, we observe an initial stretching of bonds both within the crack and in the bulk areas at the ends of the crack for small strain values (Fig. 3a). Upon increasing strain, actual bond breaking initiates and the crack then propagates by increasing its width. Interestingly, nanocavities also appear, found to be in the same plane as the precrack, while smaller voids are observed within the bulk glassy phase. The appearance of cracks not directly in conjunction with the precrack gives rise to molecular bridges across the two fracture surfaces (Fig. 3a), causing the observed nanoscale ductility in the stress–strain curve (Fig. 1d).
This fracture behavior is largely similar to previous experimental observations of crack propagation by initiation, growth, and coalescence of nanocavities42. Noticeably, such mechanism has been argued to provide nanoductility while maintaining brittleness at the macroscale, in agreement with the findings herein. The molecular bridges consist of two- to four-fold coordinated Zn atoms. In many cases, the bond breaking occurs for the two- and three-fold coordinated Zn atoms, but interestingly, visual inspection reveals that when four-fold coordinated sites are present, they also appear to break instead of nearby two- and three-fold coordinated Zn atoms under intensive strain (Fig. 3b). As such, it is the relatively weak Zn–N coordinative bonds in the present ZIF-62 glass compared to the stronger bonds in other categories of glasses (e.g., oxide or metallic) that ultimately gives rise to its low fracture toughness. This argument is based on an analysis of the simulated bond breaking during fracture, in which we find that only Zn–N bonds are breaking. However, surprisingly we found a larger number of total bonds after full fracture compared to before the forced deformation of the simulation box (see Supplementary Fig. 5). This is caused by structural rearrangement stimulated by the applied stress, ultimately increasing the connectivity of the network. In addition, we performed a stress analysis during fracture on all eight simulated structures, illustrating that Zn, N, and C atoms all carry stress during fracture, as expected since they are the backbone of the network (see Supplementary Figs. 6 and 7). These findings, combined with the relatively low bond energy of Zn–N43, explains why only these bonds break during fracture.
To quantitatively understand the low fracture toughness and verify the assumption about the importance of the coordinative bonds as found by MD simulations, we next compare the experimental KIc with a theoretical one obtained using Rouxel’s recent model44 (Fig. 3c). In this approach, fracture toughness is predicted by means of the similarity principle, \(K_{{\mathrm{Ic}}}^{{\mathrm{the}}{\mathrm{.}}} = \sqrt {2\gamma ^t E^{\prime}}\) (here E′ = E/(1 − ν2) for plane strain), where E and v are here taken as the experimental values from ultrasonic echography and \(\gamma ^t\) is the theoretical fracture surface energy. In turn, \(\gamma ^t\) is predicted based on the experimental density (ρ), the molar mass of the glass, the interatomic bond strength, and the bond concentration along a fracture surface44. Here, we first assume that the network topology of ZIF-62 glass is analogous to that of amorphous silica. The central atom in ZIF-62 glass is Zn (Si in a-SiO2), which is connected to three Im ligands and one bIm ligand (four atoms of O in a-SiO2). For the crack to propagate, we further assume that the crack breaks one Zn–N bond in the ZnX4 unit (where X is Im or bIm) before proceeding to the next ZnX4 unit. We assume a bond energy of 160 kJ mol−1, which is the value found for the Zn–N bond in ZIF-zni43, a crystal having similar composition to ZIF-4, yet with a denser crystal structure and thus a good representative of the bonding found in the glassy state of ZIF-4 and ZIF-62. By applying the model, we calculate KIc of ZIF-62 glass to be 0.06 MPa m0.5 (Fig. 3c), in reasonable agreement with both the experimental and MD-simulated KIc values (Table 1). The slight underestimation may be explained by the difference between O in SiO2 and X in ZnX2, since X here is not just an atom, but an organic molecule (i.e., a large 3D-dispersed structure) in the glass network. That is, the crack should need more energy to (i) escape from the strong intramolecular bonds of Im and bIm in the ZIF-62 glass and (ii) form the nanocavities in tensile stress before fracture as explained above. In fact, the variation in energy between Rouxel’s theoretical model and that obtained from experiments (or MD simulations) is equal to the difference of half the critical energy release rate and the surface energy, i.e., GC/2 - γs, suggesting that the theoretical model used to calculate γt covers only the elastic part of the system. On the other hand, following ref. 45, we can predict the needed energy by assuming that the energy required to escape from the strong intramolecular bonds of Im and bIm is equal to that required to break the weakest bonds of bIm, as bIm is larger in volume than Im. By applying this approach, we found a very good agreement of KIc between model prediction (0.097 MPa m0.5) and experiment (0.104 MPa m0.5). As an alternative view, we may estimate the required bond energy directly from the experimental KIc value under the similar set of assumptions. In this case, we obtain a bond energy of 471 kJ mol−1, which is considerably higher than the bond energy of Zn–N (160 kJ mol−1)43, yet lower than those of C=C (>600 kJ mol−1) and C=N (>750 kJ mol−1). This again stresses that the observed fracture requires considerably more energy than a purely brittle one, highlighting the need to consider cohesive and plastic effects when estimating KIc.
Finally, we note that the present MOF glass exhibits an anomalous behavior in the fracture surface energy-Poisson’s ratio (γ-ν) landscape (Fig. 3d), in which a sharp brittle-to-ductile transition exists at Poisson’s ratio value around 0.32 for various non-crystalline materials46,47,48,49. That is, although the present MOF glass features a relatively high Poisson’s ratio in the range of many metallic and organic glasses, it has a much lower fracture surface energy, which is similar to that of the lower Poisson’s ratio materials like ice, chalcogenide glasses, and some borate glasses. Moreover, the MOF glass does not belong to any other group of materials in the Ashby plot of KIc vs. E (Fig. 3e). Although ZIF-62 glass has a Young’s modulus similar to that of the group of natural materials, it exhibits lower fracture toughness in the range between foams and elastomers.
Discussion
The modified SEPB experiment for small (10 mm in length) samples, which has been validated on standard window glass, has enabled us to measure the fracture toughness of the ZIF-62 glass. The validity of the small SEPB setup to measure KIc is two-fold. First, the span-to-width (S/W = 7.5/1.9) ratio of the new setup is about 4, as permitted by ASTM standard (4 ≤ S/W ≤ 10)34 and the width-to-broadness (W/B = 1.9/1.5) ratio is about 1.27, as also permitted by the standard (1 ≤ W/B ≤ 2). Second, the use of an indentation line to join the corner cracks lowers the compression load in the precracking stage and thus facilitates the straight through precrack, i.e., the low compression load ensures that the indented specimen produces a precrack before compressive breaking. We expect that this modified SEPB setup can also be applied to other families of glasses and ceramics, which can only be produced in small size and quantity as the present MOF glass.
Based on the ReaxFF-based MD simulations, we have found that the rupture of weak Zn–N coordinative bonds is the origin of the low fracture toughness of the ZIF-62 glass. Taken as a whole, this glass features a number of unique properties, such as pressure-promoted melting50, ultra-high resistance to crystallization10, and broad mid-infrared luminescence13, and, as shown herein, also uniqueness in its fracture behavior. First, it features pronounced nanoductility compared to other glasses e.g. silica37 (Fig. 1d), but yet it exhibits very low fracture toughness on the macroscale, similarly to that of elastomers or high-toughness foams (Fig. 3e). Moreover, with this low toughness, the ZIF-62 glass possesses a much larger Young’s modulus (E = 4–6 GPa) than foams and elastomers (E < 1 GPa). These characteristics position the MOF glass in a hitherto unoccupied region of the Ashby KIc vs. E plot (Fig. 3e). The small fracture toughness and relatively large Young’s modulus gives rise to a small fracture surface energy (γ), comparable to that of oxide glasses. With a Poisson’s ratio (ν = 0.34–0.35) as high as many metallic and organic glasses, the studied hybrid glass shows another anomalous feature in the brittle-to-ductile transition curve (Fig. 3d). This work thus has a far-reaching implication for understanding the fracture behavior and mechanical properties of the entire family of MOF glasses.
Methods
Experimental sample preparation
A metal–organic framework glass, namely ZIF-62 glass, was produced by melt-quenching crystalline ZIF-62 in a tube furnace under flowing nitrogen gas. The solvothermal synthesis of the crystalline ZIF-62 was previously reported in details10,11,12,51,52. Briefly, the mixture of zinc nitrate hexahydrate (Zn(NO3)2)·6H2O, Merck), imidazole (C3H4N2, Merck), and benzimidazole (C7H6N2, Merck) solutions in N,N’-dimethylformamide (DMF, VWR) was magnetically stirred for 20 min, before placing it in a furnace for 48 h at 403 K. The obtained crystalline powder was washed thrice in DMF, once in dichloromethane (DCM, Merck), and then dried in a furnace at 373 K for 4 h. To confirm the obtained powder was ZIF-62, powder X-ray diffraction was performed (see Supplementary Fig. 8). The crystalline powder (200 mg) was pressed uniaxially (pressure of 40 MPa) into a pellet with a diameter of 13 mm and a thickness of ~2 mm. The pellet was heated to 738 K with a heating rate of 10 K min−1 and held isothermally for 5 min in an electrically heated tube furnace with the nitrogen gas flow set to 5 mL min−1. Then the sample was cooled down to room temperature (~295 K) at a cooling rate of 10 K min−1. The final ZIF-62 glass is a bulk homogeneous glass with 11 mm diameter without visible bubbles52.
The 11 mm diameter glass pellet was carefully cut into beams of dimension of 2 × 3 × 10 mm3 by using a thin diamond disk (thickness of 0.15 mm). To cut the cracking-prone ZIF-62 glass without breaking, we first tested cutting under various rotation speeds of the disk and translation speeds of the specimen. We finally chose the rotation and translation speeds of 2000 rpm and 0.015 mm s−1, respectively. To grind and polish the ZIF-62 glass without breaking, we mounted it together with three pieces of standard window (soda-lime-silicate) glass with similar dimensions. This was done to the four edges of the specimen to have the final dimension of about 1.5 × 1.9 × 10 mm3 after grinding and polishing down to 9 µm diamond paste.
Experimental elastic properties and strength
The Young’s modulus (E) and Poisson ratio (ν) of the prepared ZIF-62 glass were measured by means of ultrasonic echography. Generated by 10 MHz piezoelectric transducers, the velocities of longitudinal (VL) and transverse (VT) waves were calculated. Using the density (ρ) measured by means of Archimedes’ method in distilled water at room temperature (295.8 K), E and ν were then obtained by means of the following relations,
To obtain the flexural strength of the prepared glass, the as-polished specimen was mounted on a three-point flexure with a supporting span of 7.5 mm between two rollers with diameter of 4 mm. The mounted specimen was loaded with a cross-head speed of around 0.06 mm min−1, depending on the specimen dimension, to have a strain rate of 1 × 10−4 s−1 according to the ASTM standard C1161-1353 at room temperature (20 °C) and relative humidity of 60%. The average strength was calculated from four tests.
Experimental fracture toughness
Fracture toughness (KIc) was determined by means of the single-edge precrack beam (SEPB) method adapted for small dimension specimen (1.5 × 1.9 × 10 mm3), following the experimental procedure given in ASTM standard C1421-1034 and recent literature40,45,54. In this modified SEPB approach, five Vickers indents with a load of 2.5 N for a dwell time of 5 s were placed on a line (200 µm from one indent to another) on the broadest side (B = 1.5 mm), as shown in Fig. 2a. The indented specimen was then positioned in the compression fixture with a groove size of about 3 mm (~1.5 times the specimen width, W = 1.9 mm) to produce a precrack (before the fracturing step) with a cross-head speed of 0.02 mm min−1. Under the compression fixture, the specimen experiences tensile stress in the lower part (indented or groove part) and compressive stress in the upper part. The tensile stress opens up the crack from the five indents, and the crack grows until it reaches the compressive stress (about the middle of the specimen width). This prevents further extension of the precrack and we obtain a precrack with the size about half-length of W. A three-point bending fixture, as the one used in the flexural strength testing, was used to fracture the precracked specimen with a cross-head speed of 10 µm s−1 to avoid the humidity effects (see ref. 40 for details). We note that this adapted three-point bending span (S) of 7.5 mm was designed to fulfill the span-to-width ratio of about 4 as required in the standard34. KIc was then calculated from the peak load (Pmax)34,40,55,
where α is the precrack-width ratio (a/W) and f(α) = [1.99 − (α − α2)(2.15 −3 .93α + 2.7α2)]/(1 + 2α). We validated this adapted SEPB approach for small specimens on standard window glass (soda-lime-silicate glass), giving the value KIc = 0.72 ± 0.02 MPa m0.5, which agrees with that obtained from SEPB experiments on larger specimens40. The average KIc value is calculated from five valid tests.
MD simulations of glass formation
All simulations were performed using LAMMPS56. As a starting point, we used the unit cell structure of crystalline ZIF-62 from the work of Widmer et al.50, which was then replicated into a 2 × 2 × 2 supercell (2368 atoms) for better statistical averaging of structures. To prepare the ZIF-62 glass, we employed the ReaxFF parameters as introduced by Yang et al.35 since the ReaxFF bond order potential is ideally suited for the bond breaking and reformation that are needed to study the melting and fracture characteristics of the MOF glass herein35,57. To prepare the glassy structure, we performed potential energy minimization of the initial unit cell structure, followed by 7.5 ps of relaxation at 10 K using a Berendsen thermostat. The structure was then heated to 300 K at a rate of 232 K ps−1 with 12.5 ps of equilibration at 300 K. Afterwards the structure was heated to 1500 K at 24 K ps−1 and again cooled to 300 K at a similar rate before equilibration of the structure for another 12.5 ps, and finally 6.25 ps of statistical averaging. All quenching steps, besides the final statistical averaging, were performed in the NPT ensemble at 1 atm, while the statistical averaging was performed in the NVT ensemble. Eight structures were made by varying the initial temperature profile induced when starting dynamics. A timestep of 0.25 fs and periodic boundary conditions in all three directions were used for all steps of MD simulations including all following analyses. We have provided an example structure of the ZIF-62 glass as a Supplementary File in the standard LAMMPS data file format, referring to the LAMMPS documentation for an introduction to the data format and visualization software for format conversion (e.g., OVITO).
MD simulations of elastic properties and ultimate strength
The obtained melt-quenched glass structures were subjected to elastic property analysis at 300 K by stepwise deforming the relaxed simulation box in strain steps of \(\varepsilon \approx 0.001\) for elongation and \(\varepsilon \approx 0.003\) for shear deformation in the NVT ensemble. After each step, the structure was first equilibrated for 2.5 ps, while the next 2.5 ps of simulation time was used for averaging the pressure in the elongated direction. The linear parts of the obtained stress–strain curves were used to obtain the stiffness matrix elements C11, C22, C33, C44, C55, and C66. Under the assumption of an isotropic nature of the glass structure, we calculated the C11 as an average of C11, C22, and C33 and C44 as an average of C44, C55, and C66. Next, we calculated C12 as ref. 58,
Finally, Young’s modulus and Poisson’s ratio were determined as ref. 58,
In addition, ultimate strength tests were performed in a similar manner to the above estimation of the elastic modulus, but using stepwise elongations of \(\varepsilon = 0.01\).
MD simulations of fracture toughness
To compute the fracture toughness by MD simulations, we employed the method introduced by Brochard et al.36 and subsequently applied and validated in various studies37,38,59 (these references also provide the detailed introduction to the method). Initially the quenched structures were replicated into 2 × 6 × 4 supercells (thus 1 × 3 × 2 replications of the quenched structures) of 14208 atoms. In this structure, the atoms were removed in an ellipsoidal cylinder of length 36 Å and height 4 Å in the center of the simulation box to induce a precrack. This removal leaves a number of organic linkers incomplete. To ensure proper stability of the following simulation, we removed all incomplete linkers by identifying C, H, and N atoms of inadequate coordination numbers (using cutoffs of 2 Å for C–C and C–N bonds, and 1.5 Å for C–H bonds). Before fracture toughness simulations, the precracked structures were equilibrated in the NPT ensemble at 300 K for 100 ps at zero pressure, which was found to be a reasonable time to obtain convergence of potential energy of the new structure. This equilibration was followed by a potential energy minimization. The ensemble was now changed to NVT and was then equilibrated for another 10 ps. This was followed by step wise elongation of the simulation box of 1% every 5 ps. This step rate is more than an order of magnitude slower than what has previously been found to cause rate dependency of the fracture characteristics of other systems59,60. After each step, the structure was allowed to relax for 2.5 ps, followed by averaging of the pressure in the direction of elongation (z) for another 2.5 ps. The recorded pressure was used to plot a stress–strain curve up until and including fracture, which subsequently was integrated to yield the critical energy release rate under the assumption of elongation in the z-direction,
where \(L\) is the length of the specified direction, \(\Delta A_\infty\) is created crack surface area during fracture61, and \(\sigma _z\) is the recorded pressure in the z-direction. By assuming \(\gamma = G_{\mathrm{C}}/2\), \(K_{Ic}\) was finally estimated by the Irwin formula,
using the Young’s modulus and Poisson’s ratio from the simulations.
MD simulations of surface energy
To evaluate the brittleness parameter (Bindex), we used the quenched 2 × 2 × 2 supercells, which were initially equilibrated for 10 ps in the NVT ensemble. The bulk potential energy was then estimated from this equilibration period. Two largely planar surfaces were then induced by splitting the simulation box in two, yet only allowing Zn–N bonds to break. Afterwards the structure was equilibrated for another 50 ps, which was found to give a reasonable potential energy convergence. The difference between the potential energy before and after fracture process gave a measure for the surface energy (\(\gamma _s\)) used in the calculation of Bindex. In the calculation of \(\gamma _s\), we estimated the actual induced surface area, but found only minor deviations from planarity. We note that \(\gamma _s\) is different from \(\gamma\) in that \(\gamma _s\) is exclusively taking surface energies into account, while \(\gamma\) incorporates effects of plastic deformation and various rearrangements occurring during fracture.
MD simulations of atomic stress
We evaluated atomic stress using the incorporated stress/atom function in LAMMPS56. Note that, although stress is intrinsically a macroscopic property that is not properly defined for individual atoms, the “stress per atom” simply captures the contribution of each atom to the virial of the system and, hence, can be used to assess which elements are carrying the macroscopic stress imposed on the bulk glass. We followed the general scheme as for the estimation of KIc. To remove the effect of atomic velocity on stress, we performed a potential energy minimization before forcing atoms at rest only while performing the stress calculation. The output stress of LAMMPS is in a stress × volume formulation; hence, to obtain the presented stress results, we divide by the atomic volume of each elemental species as computed by the average of Voronoi volumes of each element (from bulk structures).
Data availability
Code availability
The code used for the molecular dynamics simulations within this paper is available from the corresponding author upon reasonable request.
References
Mason, J. A. et al. Methane storage in flexible metal-organic frameworks with intrinsic thermal management. Nature 527, 357–361 (2015).
Su, Z. et al. Shock Wave Chemistry in a metal-organic framework. J. Am. Chem. Soc. 139, 4619–4622 (2017).
Yoon, J. W. et al. Selective nitrogen capture by porous hybrid materials containing accessible transition metal ion sites. Nat. Mater. 16, 526–531 (2017).
Mondloch, J. E. et al. Destruction of chemical warfare agents using metal-organic frameworks. Nat. Mater. 14, 512–516 (2015).
Wu, T., Feng, X., Elsaidi, S. K., Thallapally, P. K. & Carreon, M. A. Zeolitic imidazolate framework-8 (ZIF-8) membranes for Kr/Xe separation. Ind. Eng. Chem. Res. 56, 1682–1686 (2017).
Rodenas, T. et al. Metal-organic framework nanosheets in polymer composite materials for gas separation. Nat. Mater. 14, 48–55 (2015).
Horike, S., Umeyama, D. & Kitagawa, S. Ion conductivity and transport by porous coordination polymers and metal-organic frameworks. Acc. Chem. Res. 46, 2376–2384 (2013).
Tian, T. et al. A sol-gel monolithic metal-organic framework with enhanced methane uptake. Nat. Mater. 17, 174–179 (2018).
Furukawa, S., Reboul, J., Diring, S., Sumida, K. & Kitagawa, S. Structuring of metal-organic frameworks at the mesoscopic/macroscopic scale. Chem. Soc. Rev. 43, 5700–5734 (2014).
Qiao, A. et al. A metal-organic framework with ultrahigh glass-forming ability. Sci. Adv. 4, eaao6827 (2018).
Stepniewska, M. et al. Observation of indentation-induced shear bands in a metal−organic framework glass. Proc. Natl Acad. Sci. USA https://doi.org/10.1073/pnas.2000916117 (2020).
Qiao, A. et al. Optical properties of a melt-quenched metal-organic framework glass. Opt. Lett. 44, 1623–1625 (2019).
Ali, M. A. et al. Broad mid-infrared luminescence in a metal-organic framework glass. ACS Omega 4, 12081–12087 (2019).
Tan, J. C., Bennett, T. D. & Cheetham, A. K. Chemical structure, network topology, and porosity effects on the mechanical properties of Zeolitic Imidazolate Frameworks. Proc. Natl Acad. Sci. USA 107, 9938–9943 (2010).
Li, S. et al. Mechanical properties and processing techniques of bulk metal-organic framework glasses. J. Am. Chem. Soc. 141, 1027–1034 (2019).
Park, K. S. et al. Exceptional chemical and thermal stability of zeolitic imidazolate frameworks. Proc. Natl Acad. Sci. USA 103, 10186–10191 (2006).
Tian, Y.-Q. et al. Design and generation of extended zeolitic metal-organic frameworks (ZMOFs): synthesis and crystal structures of zinc (II) imidazolate polymers with zeolitic topologies. Chem. Eur. J. 13, 4146–4154 (2007).
Gustafsson, M. & Zou, X. Crystal formation and size control of zeolitic imidazolate frameworks with mixed imidazolate linkers. J. Porous Mater. 20, 55–63 (2013).
Liu, Y., Kravtsov, V. C., Larsen, R. & Eddaoudi, M. Molecular building blocks approach to the assembly of zeolite-like metal-organic frameworks (ZMOFs) with extra-large cavities. Chem. Commun. 14, 1488–1490 (2006).
Huang, X.-C., Lin, Y.-Y., Zhang, J.-P. & Chen, X.-M. Ligand-directed strategy for zeolite-type metal-organic frameworks: zinc (II) imidazolates with unusual zeolitic topologies. Angew. Chem. Int. Ed. 45, 1557–1559 (2006).
Zhang, J.-P. & Chen, X.-M. Crystal engineering of binary metal imidazolate and triazolate frameworks. Chem. Commun. 16, 1689–1699 (2006).
Zhou, C. et al. Thermodynamic features and enthalpy relaxation in a metal-organic framework glass. Phys. Chem. Chem. Phys. 20, 18291–18296 (2018).
Tan, J. C. & Cheetham, A. K. Mechanical properties of hybrid inorganic-organic framework materials: Establishing fundamental structure-property relationships. Chem. Soc. Rev. 40, 1059–1080 (2011).
Bahr, D. F. et al. Mechanical properties of cubic zinc carboxylate IRMOF-1 metal-organic framework crystals. Phys. Rev. B 76, 184106 (2007).
Tan, J. C., Merrill, C. A., Orton, J. B. & Cheetham, A. K. Anisotropic mechanical properties of polymorphic hybrid inorganic-organic framework materials with different dimensionalities. Acta Mater. 57, 3481–3496 (2009).
Han, S. S. & Goddard, W. A. Metal-organic frameworks provide large negative thermal expansion behavior. J. Phys. Chem. C. 111, 15185–15191 (2007).
Bennett, T. D. et al. Melt-quenched glasses of metal-organic frameworks. J. Am. Chem. Soc. 138, 3484–3492 (2016).
Quinn, G. D. & Bradt, R. C. On the Vickers indentation fracture toughness test. J. Am. Ceram. Soc. 90, 673–680 (2007).
Rouxel, T. & Yoshida, S. The fracture toughness of inorganic glasses. J. Am. Ceram. Soc. 100, 4374–4396 (2017).
Zhou, C. et al. Metal-organic framework glasses with permanent accessible porosity. Nat. Commun. 9, 5042 (2018).
Frentzel-Beyme, L., Kloß, M., Kolodzeiski, P., Pallach, R. & Henke, S. Meltable mixed-linker zeolitic imidazolate frameworks and their microporous glasses: from melting point engineering to selective hydrocarbon sorption. J. Am. Chem. Soc. 141, 12362–12371 (2019).
Wang, Y. et al. A MOF glass membrane for gas separation. Angew. Chem. Int. Ed. 59, 4365–4369 (2020).
Tao, H., Bennett, T. D. & Yue, Y. Z. Melt-quenched hybrid glasses from metal-organic frameworks. Adv. Mater. 29, 1601705 (2017).
ASTM C1421-10. Standard test methods for determination of fracture toughness of advanced ceramics at ambient temperature (ASTM International, West Conshohocken, PA, 2010).
Yang, Y. et al. Enabling computational design of ZIFs using ReaxFF. J. Phys. Chem. B 122, 9616–9624 (2018).
Brochard, L., Hantal, G., Laubie, H., Ulm, F. J. & Pellenq, R. J.-M. Fracture mechanisms in organic-rich shales: role of kerogen. Poromechanics V. 5, 2471–2480 (2013).
Wang, B., Yu, Y., Lee, Y. J. & Bauchy, M. Intrinsic nano-ductility of glasses: the critical role of composition. Front. Mater. 2, 11 (2015).
Bauchy, M. et al. Fracture toughness of calcium-silicate-hydrate from molecular dynamics simulations. J. Non Cryst. Solids 419, 58–64 (2015).
Pang, S. H., Han, C., Sholl, D. S., Jones, C. W. & Lively, R. P. Facet-specific stability of ZIF-8 in the presence of acid gases dissolved in aqueous solutions. Chem. Mater. 28, 6960–6967 (2016).
To, T. et al. Fracture toughness, fracture energy and slow crack growth of glass as investigated by the Single-Edge Precracked Beam (SEPB) and Chevron-Notched Beam (CNB) methods. Acta Mater. 146, 1–11 (2018).
Griffith, A. A. VI. The phenomena of rupture and flow in solids. Philos. Trans. R. Soc. Lond. Ser. A 221, 163–198 (1921).
Célarié, F. et al. Glass breaks like metal, but at the nanometer scale. Phys. Rev. Lett. 90, 075504 (2003).
Gaillac, R., Pullumbi, P. & Coudert, F. X. Melting of zeolitic imidazolate frameworks with different topologies: insight from first-principles molecular dynamics. J. Phys. Chem. C. 122, 6730–6736 (2018).
Rouxel, T. Fracture surface energy and toughness of inorganic glasses. Scr. Mater. 137, 109–113 (2017).
To, T. et al. Elastic properties and fracture toughness of SiOC-based glass-ceramic nanocomposites. J. Am. Ceram. Soc. 103, 491–499 (2020).
Ngai, K. L., Wang, L. M., Liu, R. & Wang, W. H. Microscopic dynamics perspective on the relationship between Poisson’s ratio and ductility of metallic glasses. J. Chem. Phys. 140, 044511 (2014).
Greaves, G. N., Greer, A. L., Lakes, R. S. & Rouxel, T. Poisson’s ratio and modern materials. Nat. Mater. 10, 823–837 (2011).
Lewandowski, J. J., Wang, W. H. & Greer, A. L. Intrinsic plasticity or brittleness of metallic glasses. Philos. Mag. Lett. 85, 77–87 (2005).
Østergaard, M. B. et al. Revisiting the dependence of poisson’s ratio on liquid fragility and atomic packing density in oxide glasses. Mater. (Basel) 12, 2439 (2019).
Widmer, R. N. et al. Pressure promoted low-temperature melting of metal–organic frameworks. Nat. Mater. 18, 370–376 (2019).
Hou, J. et al. Metal-organic framework crystal-glass composites. Nat. Commun. 10, 2580 (2019).
Stepniewska, M., Østergaard, M. B., Zhou, C. & Yue, Y. Z. Towards large-size bulk ZIF-62 glasses via optimizing the melting conditions. J. Non Cryst. Solids 530, 119806 (2020).
ASTM C1161-13. Standard test method for flexural strength of advanced ceramics at ambient temperature. (2013).
Januchta, K., To, T., Bødker, M. S., Rouxel, T. & Smedskjaer, M. M. Elasticity, hardness, and fracture toughness of sodium aluminoborosilicate glasses. J. Am. Ceram. Soc. 102, 4520–4537 (2019).
Srawley, J. E. Wide range stress intensity factor expressions for ASTM E 399 standard fracture toughness specimens. Int. J. Fract. 12, 475–476 (1976).
Plimpton, S. Fast parallel algorithms for short-range molecular dynamics. J. Comput. Phys. 117, 1–19 (1995).
Gaillac, R. et al. Liquid metal–organic frameworks. Nat. Mater. 16, 1149–1154 (2017).
Gersten, J. I. & Smith, F. W. The Physics and Chemistry of materials. (Wiley, 2001).
Brochard, L., Hantal, G., Laubie, H., Ulm, F. J. & Pellenq, R. J. M. Capturing material toughness by molecular simulation: accounting for large yielding effects and limits. Int. J. Fract. 194, 149–167 (2015).
Swiler, T. P., Simmons, J. H. & Wright, A. C. Molecular dynamics study of brittle fracture in silica glass and cristobalite. J. Non-Cryst. Solids 182, 68–77 (1995).
Stukowski, A. Computational analysis methods in atomistic modeling of crystals. J. Min. 66, 399–407 (2014).
Tian, K. V. et al. Atomic and vibrational origins of mechanical toughness in bioactive cement during setting. Nat. Commun. 6, 8631 (2015).
Conner, R. D., Dandliker, R. B. & Johnson, W. L. Mechanical properties of tungsten and steel fiber reinforced Zr41.25Ti13.75Cu12.5Ni10Be22.5 metallic glass matrix composites. Acta Mater. 46, 6089–6102 (1998).
Conner, R. D., Rosakis, A. J., Johnson, W. L. & Owen, D. M. Fracture toughness determination for a beryllium-bearing bulk metallic glass. Scr. Mater. 37, 1373–1378 (1997).
Keryvin, V., Hoang, V. H. & Shen, J. Hardness, toughness, brittleness and cracking systems in an iron-based bulk metallic glass by indentation. Intermetallics 17, 211–217 (2009).
Yuan, C. C. & Xi, X. K. On the correlation of Young’s modulus and the fracture strength of metallic glasses. J. Appl. Phys. 109, 033515 (2011).
Rajendran, V., Begum, A. N., Azooz, M. A. & Batal, F. H. El. Microstructural dependence on relevant physical-mechanical properties on SiO2-Na2O-CaO-P2O5 biological glasses. Biomaterials 23, 4263–4275 (2002).
Tiegel, M., Hosseinabadi, R., Kuhn, S., Herrmann, A. & Rüssel, C. Youngʼs modulus, Vickers hardness and indentation fracture toughness of alumino silicate glasses. Ceram. Int. 41, 7267–7275 (2015).
Matzke, H., Toscano, E., Routbort, J. & Reimann, K. Temperature dependence and fracture toughness and elastic moduli of a waste glass. J. Am. Ceram. Soc. 69, C-138-C-139 (1986).
Sampaio, J. A. et al. Rare earth doping effect on the elastic moduli of low silica calcium aluminosilicate glasses. J. Non Cryst. Solids 304, 293–298 (2002).
Shinkai, N., Bradt, R. C. & Rindone, G. E. Elastic modulus and fracture toughness of ternary PbO-ZnO-B2O3 glasses. J. Am. Ceram. Soc. 65, 123–126 (1982).
Le Bourhis, E. et al. Temperature dependence of the mechanical behaviour of a GeAsSe glass. Scr. Mater. 45, 317–323 (2001).
Guin, J.-P., Rouxel, T., Sanglebœuf, J.-C., Melscoët, I. & Lucas, J. Hardness, toughness, and scratchability of germanium-selenium chalcogenide glasses. J. Am. Ceram. Soc. 85, 1545–1552 (2002).
Miura, T., Watanabe, T., Benino, Y. & Komatsu, T. Unusual elastic and mechanical behaviors of copper phosphate glasses with different copper valence states. J. Am. Ceram. Soc. 84, 2401–2408 (2001).
Ashby, M. F. & Cebon, D. Materials selection in mechanical design. Le. J. Phys. IV 3, C7–1 (1993).
Acknowledgements
The authors acknowledge K. Januchta and M.B. Østergaard for valuable discussions, and T. Kirwa for help with producing the three-point bending setup. This work was supported by VILLUM FONDEN under research grant no. 13253. M.B. acknowledges funding from the National Science Foundation under grant no. 1762292. We also thank Aalborg University for funding access to computational resources at the DeIC National HPC Center (ABACUS 2.0) at University of Southern Denmark and CLAAUDIA at Aalborg University.
Author information
Authors and Affiliations
Contributions
M.M.S. and Y.Y. conceived the study. T.T., S.S.S., and M.M.S. planned the experiments and simulations. M.S., A.Q., and T.T. prepared the samples. T.T. and L.R.J. performed the mechanical testing. S.S.S. performed the MD simulations and analyses, with input from M.B. All authors participated in discussing the data. T.T., S.S.S., and M.M.S. wrote the manuscript with revisions from Y.Y. and M.B.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Mohammad Naraghi, Hai-Bin Yu, and other, anonymous, reviewers for their contributions to the peer review of this work. Peer review reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
To, T., Sørensen, S.S., Stepniewska, M. et al. Fracture toughness of a metal–organic framework glass. Nat Commun 11, 2593 (2020). https://doi.org/10.1038/s41467-020-16382-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-020-16382-7
This article is cited by
-
Micro-optical elements from optical-quality ZIF-62 hybrid glasses by hot imprinting
Nature Communications (2024)
-
Forging links in molecular glasses
Nature Synthesis (2023)
-
Precise control over gas-transporting channels in zeolitic imidazolate framework glasses
Nature Materials (2023)
-
Desolvation of metal complexes to construct metal–organic framework glasses
Nature Synthesis (2023)
-
In situ micropillar compression of an anisotropic metal-organic framework single crystal
Communications Chemistry (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.