Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

# Nucleation-controlled growth of superior lead-free perovskite Cs3Bi2I9 single-crystals for high-performance X-ray detection

### Subjects

A Publisher Correction to this article was published on 10 June 2020

## Abstract

The organic-inorganic hybrid lead halide perovskites have emerged as a series of star materials for solar cells, lasers and detectors. However, the issues raised by the toxic lead element and marginal stability due to the volatile organic components have severely limited their potential applications. In this work, we develop a nucleation-controlled solution method to grow large size high-quality Cs3Bi2I9 perovskite single crystals (PSCs). Using the technique, we harvest some centimeter-sized single crystals and achieved high device performance. We find that X-ray detectors based on PSCs exhibit high sensitivity of 1652.3 μC Gyair−1 cm−2 and very low detectable dose rate of 130 nGyair s−1, both desired in medical diagnostics. In addition, its outstanding thermal stability inspires us to develop a high temperature X-ray detector with stable response at up to 100 °C. Furthermore, PSCs exhibit high X-ray imaging capability thanks to its negligible signal drifting and extremely high stability.

## Introduction

Sensitive X-ray detection is of great significance for broad applications such as therapeutic and diagnostic healthcare, industrial inspection, security screening, scientific research, etc1,2. There are two general approaches for X-ray detection, one is indirect conversion using scintillators and the other is direct conversion of X-ray photons into electronic signals. The latter strategy is more advantageous for its higher spatial resolution and simpler system configuration3. It is often desired to use reduced X-ray dose rate, particularly for applications related to human and environmental security, therefore it is paramount to develop X-ray detectors with high sensitivity. In this regard, the semiconductor used for direct X-ray detection must exhibit following intrinsic properties: large average atomic number (Z), large carrier mobility-charge carrier lifetime product (µτ), and high resistivity (ρ). More specifically, the X-ray absorption coefficient, α is determined by Z4/E3 where E is the X-ray photon energy4. The µτ product determines the charge collection efficiency at given electric field5. For an X-ray detector, a high signal-to-noise ratio is needed for high sensitivity. Since the shot noise is strongly related to the dark current, an appropriately high resistivity enables a low dark current and, hence, reduces the noise current and increases the signal-to noise ratio, further lowering the detection limit6. As for the applications involving human body and biological system, it is apparently desired to reduce radiation dose. Some traditional semiconductors, such as α-Se, have been commercialized for X-ray detection because they can be readily deposited onto thin-film transistor (TFT) to be read out in large flat panels for high space resolution2,7,8. However, α-Se is limited by its low µτ (about 10−7 cm2 V−1) and high operating electrical fields (10–40 V μm−1), leading to limited sensitivity and detection. Therefore, X-ray detectors with improved sensitivity and lower detection limit are highly desired.

The organic-inorganic hybrid lead-halide perovskites are not only known for their high solar cell efficiency, they are also attractive for radiation detection due to its excellent properties such as high absorption, high µτ product and low-cost solution process for fabrication3,9,10,11,12. A wafer-scale MAPbI3 film and MAPbBr3 single crystals have been reportedly used in direct X-ray detection with high sensitivities of 2527 µC Gyair−1 cm−2 and 80 µC Gyair−1 cm−2, respectively13,14. The integrated MAPbBr3-silicon unit also shows an impressive sensitivity of 2.1 × 104 µC Gyair−1 cm−2 under 8 keV radiation15. However, with its volatile organic component that associates with instability and toxic lead element that causes environmental concern, its potential is severely limited16,17,18. Among all candidate elements to replace the toxic Pb element, Bi is the most promising for similar electronic structure19,20. Hence double-perovskite Cs2AgBiBr6 single crystals have been grown for X-ray detection21, exhibiting detection limit of 59.7 nGyair s−1. Unfortunately, its sensitivity is only as low as 105 μC Gy−1 cm−2, even worse, the largest crystal size obtained using the technique was limited to about three millimeters, too small for more detailed studies, not to mention practical application. More recently, the layered perovskite-like (NH4)3Bi2I9 single crystals were developed with high performance of anisotropic response to X-ray22, but its long-term stability was limited by its volatile NH4+. Therefore, it is imperative to develop more suitable materials with low toxicity, suppressed ionic migration, high stability and high sensitivity.

In this work, we develop a nucleation-controlled method to grow centimeter-sized all-inorganic lead-free Cs3Bi2I9 perovskite single crystals (PSCs). The crystals exhibit very low trap state densities, high μτ products and low dark current noise. As a result, the Cs3Bi2I9 PSCs X-ray detector shows sensitivity as high as 1652.3 μC Gyair−1  cm−2 and detection limit less than 130 nGyair−1 s−1. Benefitting from the suppressed ion migration, the X-ray detector based on the Cs3Bi2I9 PSC shows exceptional stability in 13 h of continuous operation with superior X-ray imaging capability. In addition, its outstanding thermal stability inspires us to develop a high temperature X-ray detector with stable response at up to 100 °C. It is anticipated that availability of the Cs3Bi2I9 PSCs will inspire research for next generation of X-ray detectors with better performance.

## Results

### Growth of Cs3Bi2I9 PSC

The Cs3Bi2I9 adopts a derivative structure of the MX6 octahedra, just as in the AMX3 perovskite, in which a pair of [BiI6]3− octahedra share a common face to form a [Bi2I9]3− dioctahedral cluster and the voids between the dioctahedral are filled with Cs+ cations to forming an isolated zero-dimensional (0D) Cs3Bi2I9 molecular salt structure23. It is found that large number of sub-millimeter crystallites can be readily formed shortly after stoichiometric molar ratio of CsI and BiI3 powder (CsI:BiI3 = 3:2) are mixed in solvent, indicating that the process is nucleation controlled. In order to grow large size single crystals, the number of nuclei has to be critically controlled. In other words, extraneous nucleation seeds, including dusts, bubbles, particulates, defects and scratches on the container surface, etc. need to be removed. For this purpose, we designed a nucleation-controlled method to firstly eliminate the nucleation seeds existed in the system before the intended single crystal growth process. Figure 1a provides an illustration to the process. In brief, 14.04 g CsI and 21.24 g BiI3 were dissolved in a 30 mL mixed solvent (DMF/DMSO = 7:3) to prepare precursor with concentration equivalent to 0.6 M Cs3Bi2I9 (Fig. 1a1). After careful filtration, the solution, actually a colloid to be more accurate, was relocated into a temperature-controlled oven (Fig. 1a2. When the system temperature was heated to 80 °C, a large number of sub-millimeter reddish-brown Cs3Bi2I9 crystallites were precipitated on the bottom of the container (Fig. 1a3). To ensure all possible nucleation seeds are removed from the solution, the system was maintained at the temperature for at least 24 hours. At this point, the solution portion is fully saturated and the over-saturated part is recrystallized and precipitated. The upper portion of supernatant is then carefully transferred into another clear container (Fig. 1a4) to grow large single crystals. For the ease of later discussion, this process is referred to as the solution refinement process. Finally, the refined solution was heated from 80 to 95 °C at a ramp rate of 2 °C per day (Fig. 1a5). As a result, a large Cs3Bi2I9 PSC (12 mm × 12 mm × 3 mm) was obtained.

### Nucleation process control

A red laser beam at 635 nm was used to examine the precursor solution to ensure no detectable particulates exist before the crystallization process. As shown in Fig. 1b, the original solution without refinement process shows plenty of particulates under laser illumination. In comparison, after the refinement, the precursor solution shows uniform scattering without observable particulates (Fig. 1c), indicating that nucleation seeds are effectively eliminated. By carefully regulating the temperature from 80 °C to 95 °C, the just-saturated solution became slightly oversaturated to initiate the crystallization on satisfactory nucleation seed. Finally, after about 200 h, large Cs3Bi2I9 PSCs are harvested.

The thermodynamics of the nucleation-controlled method to grow Cs3Bi2I9 PSCs can be explained using Gibbs free energy5,24, as discussed in Supplementary Information. As predicted based on the classical nucleation theory, when there are sites with radius r larger than the critical nucleation radius r0 (r > r0), they will grow spontaneously into bigger crystallites or precipitates (as illustrated in Fig. 1d, e). If these crystallites continue to grow, they would reach adjacent ones and merge into a continuous solid, as shown in Fig. 1f. In contrast, after the refinement process removing extraneous nucleation sites, only several large high-quality single crystals with well-defined octahedron are harvested, as shown in Fig. 1g.

Figure 2a shows the photo taken on well-shaped Cs3Bi2I9 PSCs. The top-view scanning electron microscopy (SEM) image shows only smooth surface with no observable grain boundary (Supplementary Fig. 1a,b), indicating impeccable quality of the single crystal, further demonstrating that the crystal growth method is indeed advantageous. The corresponding SEM-energy-dispersive spectrum (SEM-EDS) analysis shows that the ratio of Cs, Bi and I is 2.58: 2: 7.76 (Supplementary Fig. 1c), consistent with the stoichiometric ratio of Cs3Bi2I9. Additionally, the uniformity of the PSCs is demonstrated by the mapping measurements, as shown in Supplementary Fig. 2). X-ray photoelectron spectroscopy (XPS) was performed to confirm the elemental composition and valence states of the Cs, Bi and I of the Cs3Bi2I9 PSC (Supplementary Fig. 3). According to the survey spectrum of the Cs3Bi2I9 PSC, the elements detected include Cs, Bi, I, O, and C. Note that the O and C originate from carbon dioxide adsorbed from the air during sample preparation. High-resolution XPS spectra for I 3d, Bi 4f, and Cs 3d are shown in Supplementary Fig. 3b–d. Peaks for Cs 3d3/2 (738.4 eV) and 3d5/2 (724.5 eV), Bi 4f5/2 (163.9 eV) and 4f7/2 (158.6 eV), and I 3d3/2 (630.3 eV) and 3d5/2 (618.9 eV) can be attributed to the characteristic signals from the Cs+, Bi3+ and I species, respectively.

### Structural characterization

X-ray diffraction (XRD) is a powerful tool to probe single-crystalline quality and structural information25. Figure 2b shows the powder XRD pattern acquired using a typical Cs3Bi2I9 PSC after being crushed and ground into fine powder. Careful comparison with the library data shows that the crystal adopts a hexagonal structure (space group P63/mmc). This was confirmed by the single crystal diffraction measurement that gives the lattice parameter a = b = 8.39 Å, c = 21.20 Å (the main crystallographic data is presented in Supplementary Table 1). Figure 2c shows the single crystal X-ray diffraction pattern of a Cs3Bi2I9 PSC, in which the well-aligned lattice diffraction spots demonstrate high crystalline quality. Figure 2d presents the hexagonal crystal structure, in which the isolated [Bi2I9]3− anions (formed by face-sharing of [BiI6]3− octahedra anions) filling in the voids formed zero-dimensional (0D) structure. In this hexagonal structure, distinct dimer [Bi2I9]3− anions placed in a layered arrangement along ab (00Ɩ) plane. Therefore, it is considered as a layered crystal structure in the (00Ɩ) plane. To further examine the crystalline quality of the Cs3Bi2I9 PSC, high-resolution XRD analysis was carried on a fresh sample. Figure 2e shows five diffraction peaks present at the (002) diffraction plane. A more-detailed rocking-curve analysis shows that the (002) and (004) peaks have very small full width at half maximums (FWHMs), specifically 0.059° and 0.058°, respectively (Fig. 2f,g).

### Optical and transport properties

To evaluate the potential of the Cs3Bi2I9 PSCs for photoelectronic applications, we measured the optical absorption spectra which show a quite sharp absorption edge at approximately 650 nm, as shown in Fig. 3a. The Tauc plot was calculated from the absorption spectrum (Fig. 3b) displaying a band gap of 1.96 eV, very similar to the value of 1.94 eV reported by Zhang, etc26. Figure 3c shows electronic band structure of Cs3Bi2I9 based on the density functional theory (DFT), with a band gap 2.24 eV, in good agreement with prior art results of ~2.30 eV (refs.23,26). In addition, the valence and conduction bands are well distributed in energy, which is presented from the projected density of states (Supplementary Fig. 4). The PDOS feature resembles the case of lead-halide perovskites, with the valence band maximum dominated by the Bi 6s, I 5p states and the conduction band minimum originated from the Bi 6p, I 5p states. Ultraviolet photoelectron spectroscopy (UPS) was also used to determine the Fermi energy (Ef) and the valence band energy (Ev) levels of the Cs3Bi2I9 PSCs, as shown in Fig. 3d. The Ef was measured to be 5.63 eV, from Ef = 21.22–15.59, using the cutoff energy (15.59 eV). Using linear extrapolation in the low-binding-energy region, the value of Ev − Ef is obtained and the value of Ev is determined to be 6.37 eV. The conduction band energy (Ec) is then calculated to be 4.41 eV from (Ev + Eg). Using above data, the band diagram can be plotted as shown in Fig. 3e (ref. 27). Thermal stability was investigated using a thermogravimetric analysis instrument. Figure 3f shows that no detectable mass loss until 550 °C, indicating no decomposition. The thermal stability of the Cs3Bi2I9 PSC is also confirmed by an in-situ XRD measurement, and the results in Supplementary Fig. 5 show that there is no phase change in the XRD pattern. It should be mentioned that the diffraction peaks in the XRD patterns gradually shift toward smaller diffraction angle, because of lattice expansion with temperature increasing gradually from room temperature to 400 °C. Furthermore, the long-term moisture stability of the Cs3Bi2I9 was measured at relative humidity of about 70% without encapsulation. Supplementary Fig. 6 shows that there is no observable change in XRD pattern after being exposed in high humidity for 70 days, demonstrating excellent moisture stability.

In order to identify the trap densities in the Cs3Bi2I9 PSCs, the relative dielectric constants (ε) of the Cs3Bi2I9 PSC were estimated from the capacitance-frequency measurement. Capacitance-frequency curves (Fig. 3g) of the Cs3Bi2I9 PSCs were measured using an impedance analyzer, and the relative dielectric constants (Fig. 3h) were calculated from the measured capacitance using the equation $$\varepsilon = \frac{{cd}}{{\varepsilon _0A}}$$ (where c and ε0 are the capacitance and the vacuum permittivity, and d and A are the thickness and the electrode area of the Cs3Bi2I9 PSC device, respectively)6. After determining the relative dielectric constant of 13.2 ± 1.1, the trap state density of the Cs3Bi2I9 PSC was obtained from the space-charge-limited current (SCLC) method by measuring the dark current–voltage (I–V) curve of Cs3Bi2I9 PSC hole-only device. As shown in Fig. 3i, with increasing bias voltage, the current increased from the first linear ohmic region and then a second trap-filled limited (TFL) region. From the second TFL region, the trap density could be calculated using the relation: $$n_{{\mathrm{trap}}} = \frac{{2V_{{\mathrm{TFL}}}\varepsilon \varepsilon _0}}{{eL^2}}$$ (where VTFL is the trap-filled limit voltage, L thickness, ε0 vacuum permittivity, ε relative dielectric constant, and e electron charge)28. The calculated trap density of the Cs3Bi2I9 PSCs is 1.4 × 1010 cm−3, close to 3D perovskite or 2D perovskite, and significantly lower than the well-known inorganic semiconductors, including polycrystalline Si, CIGS, CdTe, etc6,29,30,31,32.

The high-quality of the Cs3Bi2I9 PSC along with the good thermal stability (up to 550 °C), superior moisture stability, excellent uniformity and low trap state density point to a highly attractive material for optoelectronic devices. Therefore, planar type photodetectors are designed and fabricated. A pair of interdigitated gold (Au) wires are used as the electrodes, the spacing between adjacent ones is 22 µm and the effective illumination area of each detector is 1.68 × 10−3 cm2, the device configuration is shown in Fig. 4a.

### Device performance of photodetector

Low dark current is very important for high-performance photodetectors because it helps in achieving high detectivity, responsivity, low noise current and thus large signal-to-noise ratio. Here, we measured the resistivity of the Cs3Bi2I9 SCs. Specifically, a pair of Gold (Au) electrodes (area: 1.8 mm2) were deposited using thermal evaporation on the opposite-sides of a crystal with 1.4 mm in thickness. As shown in Supplementary Fig. 7, the calculated resistivity for the Cs3Bi2I9 SC is 2.79 × 1010 Ω cm, at least two orders of magnitudes higher than MAPbBr3 and other lead-based perovskites (107–108 Ω cm)13,29. Note that the high resistivity is desired to reduce background current noise. The dark I–V curve of the planar detector was measured, as shown in Fig. 4a. At a 10 V bias, the dark current is as low as 6 pA; such ultra-low dark current is advantageous for detecting very weak signals. Figure 4b shows the I–V curves taken in the dark and with illumination at different intensities from 9.2 × 10−6 to 300.1 mW cm−2. It shows that the photocurrent rises sharply with increasing light intensity (Supplementary Fig. 8), and it reaches 42 nA at 300.1 mW cm−2 (462 nm), an increase of 7000 times comparing to the dark current. The responsivity (R) is a signature of how effectively the photodetector responds to the optical signal. It is defined by the equation $${{R}} = \frac{{I_{\mathrm{p}} - I_{\mathrm{d}}}}{{A \cdot P}}$$, where IP is the photocurrent, Id dark current, A effective illumination area and P light intensity33. The external quantum efficiency (EQE) represents the photoelectron conversion efficiency defined as $$EQE = R\frac{{hc}}{{\lambda e}}$$, where R represent the responsivity, h the Planck’s constant, λ wavelength of incident light, e the elementary charge, and c velocity of light34. According to these photocurrent measurements, the corresponding R and EQE were calculated and plotted in Fig. 4c, d. The response is found to increase as the illumination intensity decreases, as more charge recombination is expected under high light intensity. Under the lowest measured incident light intensity, the highest R and EQE are obtained as high as 1.1 × 103 mA W−1 and 288%, respectively, both are among the highest for this type of materials26,35.

The detectivity (D*), which characterizes the smallest detectable light signal, is a key figure-of-merit for photodetectors. It is determined by the responsivity and the noise of a photodetector $$D^\ast = \frac{{R\sqrt {AB} }}{{i_{\mathrm{n}}}}$$, where R is responsivity, A effective illumination area, B electrical bandwidth, and in measured noise current. Generally, a low dark current would lead to low noise current27. When the noise current is mainly dominated by the shot noise, it may be directly calculated from the dark current. However, in many cases, charge defects in the materials may change the intrinsic noise. It is believed that frequency-dependent noise current is commonly caused by carrier trapping and de-trapping, and it is often higher than the shot noise36. Therefore, the exact noise level should be measured from the device rather than calculated simply from dark current. In this work, the noise current of the photodetector was directly measured at different frequencies, as shown in Fig. 4e. It shows that the total noise current measured from the Cs3Bi2I9 PSC photodetector is only 2.2 × 10−15 A Hz−1/2 at 4 V bias; such a low noise current is expected to result in high detectivity. With the responsivity of the Cs3Bi2I9 PSC photodetector, the peak D* value is calculated to be ~4.7 × 1012 cm Hz1/2 W−1 (Jones), as plotted in Fig. 4f.

### Device performance of X-ray detector

Based on the above studies, we conclude that excellent crystal quality and optoelectronic properties has been obtained from the Cs3Bi2I9 PSCs. These excellent properties are also essential for high-performance X-ray detection. For example, the high resistivity, high band gap and ultralow trap density enables an extremely low dark current noise, which is critical for achieving an X-ray detector with a low detection limit. In addition, long-term stability and high temperature resistance indicate this material has great potential for X-ray detection applications. To quantify the X-ray absorption, the absorption coefficient of the Cs3Bi2I9 PSC is obtained as a function of photon energy calculated using the photon cross-section database37. As shown in Fig. 5a, it is slightly higher than those of the traditional inorganic semiconductor materials including CsI and CdTe, much higher than those of commercial carbon and silicon materials. Furthermore, the absorption coefficient of the present Cs3Bi2I9 PSC is also higher than those of the popular perovskites studied for X-ray detection12,13,14,15,21,38,39. The higher the absorption coefficient, the higher the attenuation coefficient. As is evident from Fig. 5b, the all-inorganic lead-free Cs3Bi2I9 PSC has a stronger attenuation than other perovskites at the same thickness. For example, 0.5 mm thick SC is enough for the Cs3Bi2I9 to attenuate 94.7% of the incident X-ray photons, comparing to MAPbI3 87.7%, Cs2AgBiBr6 85.7%, MAPbBr3 65.9%, and MAPbCl3 54.2%. Therefore, the high-quality Cs3Bi2I9 PSC was selected to fabricate the vertically structured X-ray detector (Au/Cs3Bi2I9 PSC/Au). As shown in Fig. 5c, the electrode area is 1×1 mm2, and the Cs3Bi2I9 PSC thickness is 1.2 mm. The μτ product is determined by fitting the modified Hecht equation27:

$$I = \frac{{I_0\mu \tau V}}{{L^2}}\,\frac{{1 - {\mathrm{exp}}( - \frac{{L^2}}{{\mu \tau V}})}}{{1 + \frac{{Ls}}{{V\mu }}}}$$
(1)

where I0 is the saturated photocurrent, and L and V are the sample thickness and the applied voltage, respectively. In Fig. 5d presents the bias-dependent photoconductivity of the Cs3Bi2I9 PSC. Numerical fitting using the modified Hecht equation gives a μτ value of 7.97 × 10-4 cm2 V−1, more than 20 × higher than melt-grown Cs3Bi2I9 crystals20 and comparable with other perovskite single crystals21,27,40.

A high sensitivity and low detectable dose rate are two vital characteristics required of an X-ray detector for applications. To evaluate the sensitivity, the on/off photocurrent response under various electric field and dose rates are measured, as shown in Supplementary Fig. 9. It is found that the generated photocurrent density shows a linear relationship with the X-ray dose rate, as plotted in Fig. 5e. The slope of a linear fit is defined as the sensitivity of the detector. Figure 5f shows the sensitivity as a function of the electric field applied. At 50 V mm−1, the sensitivity is 1652.3 μC Gyair−1 cm−2, more than 3.7 times higher than that of α-Se detectors (440 µC Gyair−1 cm−2) measured under even much higher electric field of 15,000 V mm−1 (ref. 41). Furthermore, the gain factor G is plotted vs. dose rate used at 50 V mm−1 (Fig. 5e, right axis) (the calculation process is provided in Supplementary Information. It should be noted that the gain value gradually increases from 15.1 to 17.3 when the dose rate is decreased from 58.1 to 6.8 µGyair s−1. This phenomenon is commonly observed as the dynamic-range enhancing gain compression in photoconductive photodetectors42. Furthermore, to find the lowest detectable dose rate, we applied the same method used by Huang et al.13. Figure 5g shows the response of the Cs3Bi2I9 PSC X-ray detector collected under different X-ray dose rates at a 50 V mm−1 electric field. According to the dark current and photocurrent of a device as shown in Supplementary Fig. 10, the SNR is calculated as 6.8 when the device was exposed under the dose rete of 130 nGyair s−1. The international union of pure and applied chemistry (IUPAC) defines the detection limit as the equivalent dose rate to produce a signal greater than 3 times the noise level at a given electric field. Therefore, the lowest detectable X-ray dose rate of the present Cs3Bi2I9 PSC device is 130 nGyair s−1, more than two orders of magnitude better than the state-of-the-art MAPbI3 SCs (19.1 µGyair s−1)43 and about 42 times lower than what required for regular medical diagnostics (5.5 µGyair s−1)44,45. With the ultra-low dark current noise, and highly stable SNR, which guarantee the ignorable baseline drift and highly stable photocurrent output signal, it is expected that the Cs3Bi2I9 PSC device would exhibit excellent imaging capability. As shown in Fig. 5h, i, the images of a metallic key and a nut were reproduced by the X-ray imaging. The distinct color contrast demonstrates that these objects were clearly resolved. For higher resolution imaging applications, the spatial resolution can be further increased by reducing the pixel size and test distance46.

### Stability of X-ray detector

Device stability is another important figure-of-merit for practical applications. Supplementary Fig. 11 presents photocurrent response of a Cs3Bi2I9 PSC X-ray detector to the radiation in ambient air under a 30 V mm−1 applied electric field. It is clear that when the X-ray is turned on, the photocurrent raises rapidly to the max value 703 pA. As soon as the radiation is off, the current drops to the dark current value 102 pA. Furthermore, there is no detectable photocurrent degradation after being tested in air for the entire period for 50 cycles. In fact, as illustrated in Supplementary Fig. 12, the photocurrent remains unchanged at 724 ± 10 pA for the entire period of 13 h under continuous X-ray illumination and electric field (60 µGyair s−1, 30 V mm−1). It is also found that the Cs3Bi2I9 PSC device shows long-term stability when exposed to ambient atmosphere. As shown in Supplementary Fig. 13, the response current, resistivity and on/off ratio display no noticeable change after being exposed in ambient for 47 days. Compared with organic-inorganic hybrid perovskite, all inorganic perovskite has better thermal stability. Therefore, we measured the thermal stability of the MA3Bi2I9 SC X-ray detectors under X-ray illumination at different electric field. The on/off photocurrent response under various electric field and dose rates is shown in Fig. 6a–d. Figure 6e presents the generated photocurrent density versus dose rate under different applied electric field when the Cs3Bi2I9 PSC device was maintained at 100 °C. The calculated sensitivity as a function of applied electric field is shown in Fig. 6f. It can be seen that, when at electric field of 50 V mm−1, the sensitivity is calculated to be 1146.7 μC Gyair−1 cm−2, which is 69.4% of the value measured at 22 °C, demonstrating that the X-ray detector is capable of being used at high temperature 100 °C. Besides, we find that the detector shows a stable photocurrent response at 100 °C for long time under continuous X-ray illumination and high electric field (63.4 µGyair s−1, 50 V mm−1), as shown in Supplementary Fig. 14. The surprisingly good stability of the present device can be attributed to its inorganic nature without volatile component, its low ionic migration, and low density of defects18,47.

## Discussion

In summary, we have demonstrated a nucleation-controlled method to grow large size high-quality, all-inorganic, lead-free Cs3Bi2I9 perovskite single crystals, which reduces the number of crystal nuclei to ensure that each one grows independently. The Cs3Bi2I9 single crystal shows low trap density, high μτ product, ultra-low dark current noise and high stability. The photocurrent of the Cs3Bi2I9 PSC device was studied under both visible light and X-ray irradiation. The Cs3Bi2I9 PSC photodetector exhibits a high photoresponse on/off ratio (exceeding 103) and high detectivity (1012 Jones) to visible light (462 nm). Additionally, high μτ product of 7.97 × 10−4 cm2 V−1 was measured, leading to high X-ray sensitivity 1652.3 μC Gyair−1 cm−2, over 3.7 times higher than that of α-Se detectors; and the detection limit of 130 nGyair s−1, about 42 times lower than that of required for medical diagnostics. In addition, the Cs3Bi2I9 PSCs exhibit superior X-ray imaging capability thanks to its ultra-low dark current, negligible baseline drift, and extremely high stability. With all above characteristics, we anticipate that the Cs3Bi2I9 may become a promising material in X-ray detection and imaging applications.

## Methods

### Chemicals and regents

N,N-dimethylformamide (DMF, 99.5%) and dimethyl sulfoxide (DMSO, 99.9%) were purchased from Aladdin Reagent Ltd. Bismuth triiodide (BiI3, 98%) and cesium iodide (CSI, 99%) were purchased from Mackin Biochemical Co., Ltd. All the chemicals were used as received without further purification.

### Crystallization of Cs3Bi2I9 perovskite single crystals (PSCs)

The crystallization procedure is schematically illustrated in Fig. 1a–d. Briefly, 14.04 g CsI and 21.24 g BiI3 (3:2 molar ratio) were dissolved in 30 mL DMF/DMSO (7:3) at room temperature under active mixing for 24 h to generate the Cs3Bi2I9 precursor solution (0.6 M). After filtration with an 0.8 μm filter, a brownish red solution was obtained. The filtered precursor solution was heated to 80 °C and the temperature was maintained at least 24 h, until numerous small crystals formed at the bottom of the petri dish. Then, the upper solution from the petri dish was transferred to another petri dish and heated to 95 °C with a slow ramp rate of 2 °C per day. As a result, the desired single crystals were obtained.

### Characterization

X-ray diffraction data were collected using a DX-2700BH with a Cu Kα (λ = 1.54186 Å) tube operated at 40 kV and 30 mA. High-resolution X-ray diffraction rocking curve was measured using an X’Pert MRD, with the Cu Kα1 line (λ = 1.5406 Å) with V = 40 kV and I = 20 mA. The SEM images and EDS were collected with a tungsten filament scanning electron microscope (HITACHI SU-3500) equipped with Energy Dispersive X-ray Spectrometer. The absorption spectra of the Cs3Bi2I9 PSCs were measured using a UV-Vis-NIR spectrophotometer (Lambda 950, Perkin-Elmer). The X-ray Photoelectron Spectroscopy (XPS) and Ultraviolet Photoelectron Spectroscopy (UPS) were measured using a photoelectron spectrometer (ESCALAB 250Xi, Thermo Fisher Scientific). The thermogravimetric analysis (TGA) was implemented on a TA SDT-Q600 V20.9 (Build 20). Capacitances of the Cs3Bi2I9 PSCs were measured using an impedance analyzer (Agilent 4294A Precision LCR Meter) over a wide frequency range from 100 kHz to 30 MHz. The photographs of the Cs3Bi2I9 PSCs were collected using an eight-mega-pixel digital camera.

### Device fabrication and characterization

Several devices were fabricated by depositing Au on two opposite surfaces of the Cs3Bi2I9 PSCs. The vertical Au/Cs3Bi2I9 PSC/Au devices were used to measure the capacitance (Au, 100 nm), trap state density (Au, 100 nm), resistivity (Au, 100 nm) and μτ product (Au, 50 nm) along the (002) plane. The μτ product was measured under X-ray and the device thickness is 1 mm. Planar-type photodetectors with structure Au/Cs3Bi2I9 PSC/Au were fabricated by depositing interdigitated Au (200 nm) fingers on the Cs3Bi2I9 PSC’s (002) plane. The effective illumination area of each device is approximately 1.68 × 10−3 cm2, as inserted in Fig. 4a. For the X-ray detectors, 100 nm thick Au coating was deposited on opposite sides of the SCs to form vertical structure Au/Cs3Bi2I9 SC/Au X-ray detectors along (002) plane, the device area (electrode area) is 1 × 1 mm2 and 1.2 mm in thickness, as shown in Fig. 5c. The photo-response data of the Cs3Bi2I9 SCs devices were collected using a Keithley 4200 semiconductor characterization system. Dark current noise was measured using a spectrum analyzer (Keysight 35670A). All characterization was conducted in dark with optical and electrical shielding to eliminate the influence from electromagnetic and ambient light.

### X-ray detection performance and imaging measurement

The X-ray detection performance was measured on a home-made measurement system housed in the chamber of an X-ray diffractometer. The tungsten anode X-ray tube (DX-DS2901/24) was used as the source and operated with a constant 40 kV voltage. The operational current was tuned from 40 to 5 mA to adjust the emitted X-ray dose rate. In addition, several pieces of 2-mm-thick Al foils were inserted between the source and the Cs3Bi2I9 SC X-ray detector to serve as the attenuator. The distance between the source and detector is fixed at 16 cm. A metallic optical chopper was used to generate pulsed X-rays. The X-ray dose rate was calibrated using a Fluke Si diode (RaySafe X2 R/F) dosimeter. A Keithley 4200 source meter was used to provide the bias voltage and recorded the response current. All characterization of the X-ray response was conducted in a dark metal chamber to minimize electromagnetic and ambient light disturbance. X-ray imaging capability of the Cs3Bi2I9 SC X-ray detector was measured by moving the objects on a home-built x–y scanning system that can collect the current signal of the detector matched with the object positions. Specifically, the object was fixed on an x–y scanning stage and was allowed to move in and out of the X-ray beam in both the x and y directions to obtain a complete image. A Keysight B2902A source meter connected to the x–y scanning system was used to provide an electric field and record the response current and corresponding position coordinates.

### Computational details

In this work, the density-functional theory (DFT) calculations were performed using the Vienna Ab initio Simulation Package (VASP). The projected augmented wave (PAW) method and the Perdew–Burke–Ernzerhof (PBE) functional within the generalized gradient approximation (GGA) were employed to describe the interaction between ion-cores and valence electrons and the exchange-correlation effects, and an energy cutoff of 500 eV was set for the plane-wave function’s expansion. The van der Waals (vdWs) dispersion correction was applied and described by the DFT-D3 correction. A Γ-centered k-point sampling of 5 × 5 × 2 for Brillouin zone integration was generated using the Monkhorst-Pack scheme during the structural optimization. The lattice parameters and atomic positions of all the structures were relaxed until the total energy changes were less than 1.0 × 10-5 eV and the maximum force component acting on each atom was less than 0.01 eV Å−1. The electronic properties are calculated based on a denser k-point of 7 × 7 × 3. Normally, due to the self-interaction error inherent in GGA + PBE method, the predication of band gaps of semiconductors is usually much smaller than the accurate values. However, the good agreement between experimental band gaps and theoretical GGA+PBE band gaps has been widely reported for Pb-, Bi-based perovskites. Error cancellation of the underestimation of standard DFT band gap calculation and the overestimation due to the negligence of the spin-orbit coupling (SOC) effects in the heavy element is responsible for this agreement.

### Thermodynamics in the nucleation process

The perovskite nucleation process is rather complex for it is involves different ions48,49. At first, is the ions (Cs+, Bi3+, I) react to form perovskite (Cs3Bi2I9) colloid. Secondly, the colloid particles grow larger to form bulk perovskite crystal. The typical colloid size is around 1.5 nm (ref. 24). In colloid science50, the colloid particles are often treated as “big atoms” for theoretical consideration. According to the classical nucleation theory, a supersaturated precursor solution will naturally form clusters, tiny crystalline nuclei and precipitates. As illustrated in Fig. 1d, across the critical radius r0, the change of ΔGtotal goes negative when the particle grows larger. In other words, it becomes a spontaneous process. The ΔGtotal, therefore is often referred to as the nucleation barrier. It can be simplified into the sum of the free energy gain due to the new surface generated (ΔGs) and the free energy loss (ΔGv) associated with the conversion of a unit volume of precursor solution into a solid nucleus24:

$${\mathrm{\Delta }}G_{total} = 4{\uppi}r^2\gamma + \frac{4}{3}\pi r^3 \cdot \left( { - \varepsilon + \varepsilon _A - k_BT\ln N_A} \right)$$
(2)

where r is the nucleus radius, γ the surface energy per unit area, ε the cohesive energy, KB the Boltzmann constant, T the temperature, and NA the mole fraction of isolated molecules. The crystallization of the perovskite will not occur unless a nucleus is provided and it is large enough to overcome the free energy barrier ΔGtotal. At the critical point, $$d\Delta G_{{\mathrm{total}}}/dr = 0$$. Hence, the critical nucleus radius5:

$${\it{r}}_0 = 2\gamma /(\varepsilon - \varepsilon _{\mathrm{A}} + k_{\mathrm{B}}T\ln \,N_{\mathrm{A}})$$
(3)

and the critical free energy barrier:

$$\Delta G_{{\mathrm{total}}} = \frac{{16\pi }}{3} \cdot \frac{{\gamma ^3}}{{(\varepsilon - \varepsilon _{\mathrm{A}} + k_{\mathrm{B}}T\ln \,N_{\mathrm{A}})^2}}$$
(4)

As shown in Fig. 1d, the maximum of ΔGtotal or ΔG0 occurs at the critical nucleus radius (r0). Taking into account the surface free energy gain (ΔGs) and the bulk free energy loss (ΔGv), the formation of a nucleus in solution is mainly dependent on the critical radius (r0). In other words, a nucleus with radius (rs) smaller than the critical radius (r0) will be dissolved back into the solution, while a larger nucleus with radius (rp) larger than r0 are thermodynamically favorable, or it will grow larger spontaneously (Fig. 1e). Thus, the critical nucleus radius is the minimum size at which the particle can grow larger spontaneously in solution.

According to classical nucleation theory, the critical radius of nucleus r0 is51:

$$r_0 = 2\gamma /\left| {\Delta \mu } \right|$$
(5)

where γ ≈ 40 mN/m is the interfacial energy between solid and liquid of the perovskite24 and Δμ the chemical potential difference between solid and liquid of the perovskite. Further, Δμ can be estimated as lattice energy of ionic crystals and typically 1000 kJ m−3 (ref. 51). Therefore, the estimated perovskite critical radius is around 80 nm.

### Calculation of sensitivity

X-ray sensitivity (S) of the detectors can be calculated by the following equation52:

$$S = \frac{{\Delta I}}{{DA}}$$
(6)

where ∆I is the photocurrent (∆I = IlighIdark), D the dose rate of incident X-ray radiation, and A the area of the detector.

### Calculation of signal-to-noise ratio

The signal-to-noise ratio (SNR) was calculated as13:

$$SNR = \frac{{I_{{\mathrm{signal}}}}}{{I_{{\mathrm{noise}}}}}$$
(7)

the signal current (Isignal) is calculated by subtracting the average photocurrent $$({\bar I_{photo}})$$ by the average dark current $$({\bar I_{dark}})$$. The noise current (Inoise) is the standard deviation of the photocurrent:

$$I_{{\mathrm{noise}}} = \sqrt {\frac{1}{N}\mathop {\sum }\limits_i^N (I_i - \bar I_{{\mathrm{photo}}})^2}$$
(8)

### Calculation of gain factor

the gain factor (G) of the device was calculated as:

$$G = \frac{{I_{\mathrm{R}}}}{{I_{\mathrm{P}}}}$$
(9)

where IR is the measured current, IP is the theoretical current. The theoretical current IP is defined as IP = φβe (ref. 53), in which φ is the photon absorption rate and β the maximum number of carriers generated by a photon. The photon absorption rate φ (photons s−1) is:

$$\varphi = \frac{{\varepsilon Dm_s}}{{E_{{\mathrm{ph}}}}}$$
(10)

where ε is the fraction of absorbed photons (in this work, ε = 100% for the 1.2 mm Cs3Bi2I9 SC), D the dose rate, ms is the crystal mass, and Eph the X-ray energy. The maximum number of photogenerated carrier per photon β is calculated as:

$$\beta = \frac{{E_{{\mathrm{ph}}}}}{\Delta }$$
(11)

where ∆ is the empirical ionization energy, which is calculated by ∆ = 1.43 + 2Eg (ref.54). Therefore, the theoretical current IP can be calculated as:

$$I_P = \varphi \beta e = \frac{{\varepsilon Dm_{\mathrm{s}}}}{{E_{{\mathrm{ph}}}}} \times \frac{{E_{{\mathrm{ph}}}}}{{1.43 + 2E_{\mathrm{g}}}} = \frac{{\varepsilon Dm_{\mathrm{s}}e}}{{1.43 + 2E_{\mathrm{g}}}}$$
(12)

In this work, ∆ is calculated to be 5.35 eV for Cs3Bi2I9 SC.

### Reporting summary

Further information on experimental design is available in the Nature Research Reporting Summary linked to this paper.

## Data availability

The data that support the plots within this paper are available from the corresponding author upon request. The source data underlying Fig. 1b, c, f, g, 2a–g, 3a–d, 3f–i, 4a–f, 5a, b, d–i, 6a–f and Supplementary Figs. 314 are provided as a Source Data file.

## Change history

• ### 10 June 2020

An amendment to this paper has been published and can be accessed via a link at the top of the paper.

## References

1. Yaffe, M. et al. X-ray detectors for digital radiography. Phys. Med. Biol. 42, 1–39 (1997).

2. Kasap, S. et al. Amorphous and polycrystalline photoconductors for direct conversion flat panel x-ray image sensors. Sensors 11, 5112–5157 (2011).

3. Heiss, W. et al. Perovskites target X-ray detection. Nat. Photonics 10, 288–289 (2016).

4. Grodstein, G. W. X-ray Attenuation Coefficients from 10 keV to 100 MeV Vol. 1 (US Department of Commerce, National Bureau of Standards, 1957).

5. Liu, Y. et al. Surface-tension-controlled crystallization for high-quality 2D perovskite single crystals for ultrahigh photodetection. Matter 1, 1–16 (2019).

6. Liu, Y. et al. Multi-inch single-crystalline perovskite membrane for high-detectivity flexible photosensors. Nat. Commun. 9, 5302 (2018).

7. Jeong, M. et al. Radiation hardness characteristics of Si-PIN radiation detectors. Nucl. Instrum. Meth. A 784, 119–123 (2015).

8. Wei, H. et al. Halide lead perovskites for ionizing radiation detection. Nat. Commun. 10, 1066 (2019).

9. Stoumpos, C. C. et al. Crystal growth of the perovskite semiconductor CsPbBr3: a new material for high-energy radiation detection. Cryst. Growth Des. 13, 2722–2727 (2013).

10. Yang, D. et al. High efficiency planar-type perovskite solar cells with negligible hysteresis using EDTA-complexed SnO2. Nat. Commun. 9, 3239 (2018).

11. Wei, H. et al. Dopant compensation in alloyed CH3NH3PbBr3-xClx perovskite single crystals for gamma-ray spectroscopy. Nat. Mater. 16, 826–833 (2017).

12. Yakunin, S. et al. Detection of X-ray photons by solution-processed lead halide perovskites. Nat. Photonics 9, 444–449 (2015).

13. Wei, H. et al. Sensitive X-ray detectors made of methylammonium lead tribromide perovskite single crystals. Nat. Photonics 10, 333–339 (2016).

14. Shrestha, S. et al. High-performance direct conversion X-ray detectors based on sintered hybrid lead triiodide perovskite wafers. Nat. Photonics 11, 436–440 (2017).

15. Wei, W. et al. Monolithic integration of hybrid perovskite single crystals with heterogenous substrate for highly sensitive X-ray imaging. Nat. Photonics 11, 315–321 (2017).

16. Babayigit, A. et al. Toxicity of organometal halide perovskite solar cells. Nat. Mater. 15, 247–251 (2016).

17. Park, B. et al. Intrinsic instability of inorganic-organic hybrid halide perovskite materials. Adv. Mater. 31, 1805337 (2019).

18. Yuan, Y. et al. Ion migration in organometal trihalide perovskite and its impact on photovoltaic efficiency and stability. Acc. Chem. Res. 49, 286–293 (2016).

19. Mohan, R. Green bismuth. Nat. Chem. 2, 336 (2010).

20. McCall, K. et al. α-Particle Detection and Charge Transport Characteristics in the A3M2I9 Defect Perovskites (A = Cs, Rb; M = Bi, Sb). ACS Photonics 5, 3748–3762 (2018).

21. Pan, W. et al. Cs2AgBiBr6 single-crystal X-ray detectors with a low detection limit. Nat. Photonics 11, 726–732 (2017).

22. Zhuang, R. et al. Highly sensitive X-ray detector made of layered perovskite-like (NH4)3Bi2I9 single crystal with anisotropic response. Nat. Photonics 13, 602–608 (2019).

23. Ghosh, B. et al. Poor photovoltaic performance of Cs3Bi2I9: an insight through first-principles calculations. J. Phys. Chem. C 121, 17062–17067 (2017).

24. Zhumekenov A. et al. The role of surface tension in the crystallization of metal halide perovskites. ACS Energy Lett. 2, 1782–1788 (2017).

25. Liu, S. et al. The structure of the C60 molecule: X-ray crystal structure determination of a twin at 110 K. Science 254, 408–410 (1991).

26. Zhang, H. et al. Lead free halide perovskite Cs3Bi2I9 bulk crystals grown by a low temperature solution method. CrystEngComm 20, 4935–4941 (2018).

27. Zhang, Y. et al. Two-dimensional (PEA)2PbBr4 perovskite single crystals for a high performance UV-detector. J. Mater. Chem. C 7, 1584–1591 (2019).

28. Liu, Y. et al. Two-inch-sized perovskite CH3NH3PbX3 (X = Cl, Br, I) Crystals: Growth and Characterization. Adv. Mater. 27, 5176–5183 (2015).

29. Shi, D. et al. Low trap-state density and long carrier diffusion in organolead trihalide perovskite single crystals. Science 347, 519–522 (2015).

30. Balcioglu, A. et al. Deep-level impurities in CdTe/CdS thin-film solar cells. J. Appl. Phys. 88, 7175–7178 (2000).

31. Capan, I. et al. Dislocation-related deep levels in carbon rich p-type polycrystalline silicon. Sol. Energy Mater. Sol. Cells 91, 931–937 (2007).

32. Kerr, L. et al. Investigation of defect properties in Cu(In,Ga)Se2 solar cells by deep-level transient spectroscopy. Solid-State Electron 48, 1579–1586 (2004).

33. Liu, Y. et al. Thinness- and shape-controlled growth for ultrathin single-crystalline perovskite wafers for mass production of superior photoelectronic devices. Adv. Mater. 28, 9204–9209 (2016).

34. Zhang, Y. et al. High-quality perovskite MAPbI3 single crystals for broad-spectrum and rapid response integrate photodetector. J. Energy Chem. 27, 722–727 (2018).

35. Sun, Q. et al. Optical and electronic anisotropies in perovskitoid crystals of Cs3Bi2I9 studies of nuclear radiation detection. J. Mater. Chem. A 6, 23388–23395 (2018).

36. Wei, H. et al. Trap engineering of CdTe nanoparticle for high gain, fast response, and low noise P3HT:CdTe nanocomposite photodetectors. Adv. Mater. 27, 4975–4981 (2015).

37. Berger, M. J. et al. XCOM: photon cross sections database. NIST http://physics.nist.gov/xcom (2013).

38. Wangyang, P. et al. Solution-processable methylammonium lead iodide single crystal photodetectors for visible light and X-ray. Phys. Status Solidi 214, 170053 (2017).

39. Kim, Y. et al. Printable organometallic perovskite enables large-area, low-dose X-ray imaging. Nature 550, 87–91 (2017).

40. Yin, L. et al. Controlled cooling for synthesis of Cs2AgBiBr6 single crystals and its application for X-ray detection. Adv. Optical Mater. 7, 1900491 (2019).

41. Choquette, M. et al. Direct selenium X-ray detector for fluoroscopy, R&F, and radiography. Proc. SPIE 3977, 128–136 (2000).

42. He, J. et al. Synergetic effect of silver nanocrystals applied in PbS colloidal quantum dots for high-performance infrared photodetectors. ACS Photon. 1, 936–943 (2014).

43. Huang, Y. et al. A-site cation engineering for highly efficient MAPbI3 single-crystal X-ray detector. Angew. Chem. Int. Ed. 58, 17834–17842 (2019).

44. Clairand, I. et al. Use of active personal dosemeters in interventional radiology and cardiology: Tests in laboratory conditions and recommendations-ORAMED project. Radiat. Meas. 46, 1252–1257 (2011).

45. Shearer, D. et al. Dose rate limitations of integrating survey meters for diagnostic x-ray surveys. Health Phys. 79, 20–21 (2000).

46. Jiang, C. et al. An ultrahigh-resolution digital image sensor with pixel size of 50 nm by vertical nanorod arrays. Adv. Mater. 27, 4454–4460 (2015).

47. Chen, B. et al. Imperfections and their passivation in halide perovskite solar cells. Chem. Soc. Rev. 48, 3842–3867 (2019).

48. De Yoreo, J. J., Gilbert, P. U., Sommerdijk, N. A., Penn, R. L., Whitelam, S. & Joester, D. et al. Crystallization by particle attachment in synthetic, biogenic, and geologic environments. Science 349, aaa6760 (2015).

49. Zhou, Y., Game, O. S., Pang, S. & Padture, N. P. Microstructures of organometal trihalide perovskites for solar cells: their evolution from solutions and characterization. J. Phys. Chem. Lett. 6, 4827–4839 (2015).

50. Gasser, U., Weeks, E. R., Schofield, A., Pusey, P. N. & Weitz, D. A. Real-space imaging of nucleation and growth in colloidal crystallization. Science 292, 258–262 (2001).

51. Bai, G., Gao, D., Liu, Z., Zhou, X. & Wang, J. Probing the critical nucleus size for ice formation with graphene oxide nanosheets. Nature 576, 437–441 (2019).

52. Dvoryankin, V. F., Dvoryankina, G. G., Kudryashov, A. A., Petrov, A. G., Golyshev, V. D. & Bykova, S. V. X-ray sensitivity of Cd0.9Zn0.1Te detectors. Tech. Phys. 55, 306–308 (2010).

53. Fraboni, B. et al. Organic semiconducting single crystals as next generation of low-cost, room-temperature electrical X-ray detectors. Adv. Mater. 24, 2289–2293 (2012).

54. Devanathan, R., Corrales, L. R., Gao, F. & Weber, W. J. Signal variance in gamma-ray detectors—a review. Nucl. Instrum. Methods Phys. Res. Sect. A 565, 637–649 (2006).

## Acknowledgements

Y.Z. and Y.L. contributed equally to this work. This work was funded by the National Key Research and Development Program of China (2017YFA0204800/2016YFA0202403), the Strategic Priority Research Program of Chinese Academy of Sciences (Grant No. XDA17040506), the National Natural Science Foundation of China (91733301/61704098/61604091/51673218), the China Scholarship Council, the DNL Cooperation Fund CAS (DNL180311), the 111 Project (B14041), the Changjiang Scholars and Innovative Research Team (IRT_14R33), and the Fundamental Research Funds for the Central Universities (2018CBLZ006). At Northwestern University work was supported by the U.S. Department of Energy, Office of Science, Basic Energy Sciences, under Grant SC0012541 (electrical transport measurments).

## Author information

Authors

### Contributions

S.L. conceived and supervised the project. Y.Z. and Y.L. synthesized the crystals and fabricated the devices. Y.Z., Y.L., Y.H., M.G.K., and Z.Y. characterized the material properties. Y.L. and J.Y. analyzed the the nucleation in the single crystal growth. Y.Z., Y.L., H.Y., and Z.Y. measured the optoelectronic properties. Y.Z. and Y.L. measured the X-ray detector response. Z.X. performed the simulations. Y.Z., Y.L., and Z.Y. calibrated the X-ray dose rate. M.L. carried out the high-resolution X-ray rocking curve measurements. S.(F.)L., Y.Z. and Y.L. wrote the paper, and all the authors reviewed the paper.

### Corresponding author

Correspondence to Shengzhong (Frank) Liu.

## Ethics declarations

### Competing interests

The authors declare no competing interests.

Peer review information Nature Communications thanks Yadong Xu and the other, anonymous, reviewer(s) for their contribution to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

## Rights and permissions

Reprints and Permissions

Zhang, Y., Liu, Y., Xu, Z. et al. Nucleation-controlled growth of superior lead-free perovskite Cs3Bi2I9 single-crystals for high-performance X-ray detection. Nat Commun 11, 2304 (2020). https://doi.org/10.1038/s41467-020-16034-w

• Accepted:

• Published:

• DOI: https://doi.org/10.1038/s41467-020-16034-w

• ### Ultrafast (600 ps) α-ray scintillators

• Richeng Lin
• Yanming Zhu
• Xiaoping Ouyang

PhotoniX (2022)

• ### Cs2TiI6: A potential lead-free all-inorganic perovskite material for ultrahigh-performance photovoltaic cells and alpha-particle detection

• Peng Zhao
• Jie Su
• Jingjing Chang

Nano Research (2022)

• ### Visible colorimetric dosimetry of UV and ionizing radiations by a dual-module photochromic nanocluster

• Huangjie Lu
• Jian Xie
• Jian Lin

Nature Communications (2021)

• ### Lead-free perovskites: growth, properties, and applications

• Fan Yang
• Aocheng Wang
• Xinfeng Liu

Science China Materials (2021)

• ### Lead-free halide perovskite Cs3Bi2Br9 single crystals for high-performance X-ray detection

• Xiang Li
• Xinyuan Du
• Xutang Tao

Science China Materials (2021)