Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Efficient upgrading of CO to C3 fuel using asymmetric C-C coupling active sites


The electroreduction of C1 feedgas to high-energy-density fuels provides an attractive avenue to the storage of renewable electricity. Much progress has been made to improve selectivity to C1 and C2 products, however, the selectivity to desirable high-energy-density C3 products remains relatively low. We reason that C3 electrosynthesis relies on a higher-order reaction pathway that requires the formation of multiple carbon-carbon (C-C) bonds, and thus pursue a strategy explicitly designed to couple C2 with C1 intermediates. We develop an approach wherein neighboring copper atoms having distinct electronic structures interact with two adsorbates to catalyze an asymmetric reaction. We achieve a record n-propanol Faradaic efficiency (FE) of (33 ± 1)% with a conversion rate of (4.5 ± 0.1) mA cm−2, and a record n-propanol cathodic energy conversion efficiency (EEcathodic half-cell) of 21%. The FE and EEcathodic half-cell represent a 1.3× improvement relative to previously-published CO-to-n-propanol electroreduction reports.


The CO2 electroreduction reaction (CO2RR) to high-energy-density liquid products is an attractive avenue to achieving the storage of renewable energy. In recent years, much progress has been made in CO2RR, but the main products reported have been C1 (CO, CH4, methanol, and formate) and C2 (ethylene, acetate, and ethanol) products1,2,3,4,5,6,7,8,9,10,11,12,13. n-propanol, a high-value and high-energy-density C3 product that can be generated via either CO2 or CO electroreduction14,15, has been produced with low-to-moderate Faradaic efficiencies (FEs) in prior reports10,12,16,17,18,19,20,21,22,23,24,25,26.

In CO2RR, the formation of multi-carbon products starts with the formation of the CO intermediate, followed by the CO electroreduction process27,28,29. Recently, significant progress has been made in CO2RR to CO with a FE nearly 100%30,31,32. To achieve the ultimate goal of high selectivity to high-value-added C3 products from CO2RR, it is of interest to improve significantly the FE for CO electroreduction (CORR) to C3 products.

The formation of C3 products from CORR relies on the sequential formation of two carbon–carbon (C–C) bonds, the main reaction mechanism for C3 formation reported previously25,33,34. Cu provides excellent C–C coupling and produces multi-carbon chemicals in the electroreduction of CO; however, the selectivity towards C3 products on Cu has remained low35,36. The generation of C3 products from CO requires multiple product/intermediate formation steps, and it is prone to the competing production of a wide variety of chemical products33,34,37,38.

Increasing selectivity in the electroreduction of CO to C3 products is thus an important challenge to address in the field of electrocatalysis. Until now, catalysts for CORR have focused on Cu and oxide-derived Cu catalysts, and a number of factors have been found to increase performance: these include engineering the oxidation state of the atoms making up the metal catalyst, as well as grain-boundary effects and the selective formation of desired facets16,21,22,23,24,25,26,39. However, the main products of these Cu and oxide-derived Cu catalysts have been C2 chemicals (ethanol, acetate, and ethylene), and the selectivity to C3 products has saturated in recent manuscripts based on Cu catalysts.

Here we explore instead a doping strategy involving different metal-doped Cu (M-doped Cu) catalysts in an attempt to increase C3 production in CORR. The low C3 selectivity on Cu catalysts is associated with the low rate of C–C bond formation, including C1–C1 and C1–C2 coupling. Mechanisms underpinning C1–C1 coupling to C2 products have been explored extensively in prior studies29,33,38,40,41,42; while C1–C2 coupling to C3 products is less explored. Here we screen the propensity to catalyze C1–C1 and C1–C2 coupling using density functional theory (DFT) based on M-doped Cu catalysts. We find that, among different M-doped Cu candidates explored, Ag-doped Cu is expected to offer the highest activity for both C1–C1 and C1–C2 coupling, and we pinpoint a role for the asymmetric C–C coupling active site in this high activity. Specifically, this active site consists of two neighboring Cu atoms that exhibit different electronic structures: this asymmetry among the neighbors’ energetics is determined by the combination of strain and ligand effects arising upon Ag doping. We then fabricate Ag-doped Cu nanocatalysts via a galvanic replacement approach. We demonstrate that the synthesized Ag-doped Cu catalyst exhibits higher FEs for n-propanol compared to all previous CORR reports10,12,16,17,18,19,20,21,22,23,24,25,26. This leads to superior energy conversion efficiency in the cathodic half-cell (EEcathodic half-cell) for n-propanol.


Computational modeling and catalyst design principles

Catalysts that convert CO into C3 chemicals require high activity for both C1–C1 and C1–C2 coupling. With the goal of designing better catalysts for C3 production, we investigated the energetics of C1–C1 and C1–C2 coupling reactions to illustrate the C2 and C3 formation rates with the aid of DFT (more details of DFT methods and choice of sequential mechanism can be found in Supplementary Information). Several M-doped Cu systems (M = Ag, Au, Ru, Rh, and Pd) were considered because bimetallic catalysts have been shown to tune catalyst performance in other catalytic reactions43,44. CO dimerization is one reaction pathway for C1–C1 coupling29,40, so we used the barrier of CO dimerization to describe the readiness of C1–C1 coupling. Due to the abundance of CO species in CORR, we used the barrier of OCCO and CO coupling as the indicator for the C1–C2 coupling (Supplementary Figs. 114 and Supplementary Tables 13). As shown in Fig. 1a, among the M-doped Cu systems studied, calculation results show that Ag-doped Cu possesses the lowest activation energies for both C1–C1 and C1–C2 coupling, suggesting that Ag-doped Cu is a promising catalyst for the formation of C3 products from CO.

Fig. 1
figure 1

DFT calculations on C1–C1 and C1–C2 coupling. DFT calculated reaction barriers (Ea) for C1–C1 and C1–C2 coupling on screened M-doped Cu systems (M = Ag, Au, Ru, Rh, and Pd). The geometries of M-doped Cu surface, C1, C2, and C3 on M-doped Cu are shown with the corresponding labels, respectively. Cu, M, C, and O are illustrated as orange, light blue, gray, and red balls, respectively, while water molecules are shown as lines

We carried out further theoretical investigations to uncover the physical origins of enhancement in C1–C1 and C1–C2 coupling on Ag-doped Cu. We used a model with one Ag atom doped in a Cu(111) slab with a 3 × 3 unit cell, which corresponds to about 3% doping concentration for four layers of Cu atoms. By a margin of 0.63 eV, Ag at the surface of Cu(111) is more favorable than in subsurface of Cu(111), inducing us to focus on surface-localized Ag in our ensuing studies.

As the radius of the Ag atom is larger than that of Cu atom, Ag doping produces surface strain. The bond length of Cu–Cu changed from 2.57 Å on the Cu(111) surface to 2.55 and 2.48 Å on the Ag-doped Cu surface, resulting in asymmetric compressive strain (Supplementary Fig. 15). The ligand effect45 caused by Ag doping in Cu also has the potential to affect C1–C1 and C1–C2 coupling. To evaluate the effect of the strain and ligand, we built a model with the same strain of Ag-doped Cu but without Ag substitution by fixing the bond length of Cu surface (denoted Cu with strain). We calculated the activation energies for C1–C1 and C1–C2 coupling steps on Cu, Cu with strain, and Ag-doped Cu models (Supplementary Table 4). Calculation results show that both compressive strain and ligand effects contribute to enhanced activity for C1–C1 and C1–C2 coupling (Supplementary Fig. 16a).

Ag doping in Cu leads to two classes of neighboring Cu atoms (denoted Cu-a and Cu-b atoms, Supplementary Fig. 16b). The two classes exhibit distinct electronic structures, as a result of strain and ligand effects. As to the strain effect, the bond length between Cu-a and Cu-b atoms is 2.55 Å, while the bond length between two Cu-b atoms is 2.48 Å (Supplementary Fig. 15), suggesting that Cu-a is more isolated than Cu-b. As to ligand effects, Cu-a coordinates with nine Cu atoms, while Cu-b coordinates with eight Cu atoms and one Ag atom (Supplementary Fig. 16). We term a pair of adjacent Cu atoms with different electronic structures an asymmetric C–C coupling active site. In this reaction, the asymmetric site interacts with two CO to yield asymmetric reactants—two adsorbed CO on Cu-a and Cu-b atoms with different electronic structures—enhancing C1–C1 coupling. In light of the similarity with C–C coupling, the same site can further promote C1–C2 coupling between asymmetric C1 and C2 intermediates (Supplementary Fig. 17). These findings are in ways analogous to the enhanced coupling effect of Cu0 and Cu+ proposed by Goddard and co-workers41. Taken together, these DFT calculation results suggest that Ag-doped Cu with asymmetric C–C coupling active sites is a good candidate for C3 production in CORR which appear to support both C1–C1 dimerization and C1–C2 coupling. It is worth mentioning that there exist other C1–C2 coupling possibilities: we also examined another C1–C2 coupling mechanism, OC-OCCOH (refs. 33,39), and found that Ag-doped Cu had a barrier of 0.76 eV, lower than 0.88 eV on Cu (Supplementary Figs. 18, 19, and Supplementary Table 5).

Preparation and characterization of nanocatalysts

We sought to prepare experimentally Ag-doped Cu catalysts. We employed a galvanic replacement reaction driven by the difference in the reduction potential of Ag vs. Cu (ref. 46). Firstly, we deposited a thin layer of commercial Cu nanoparticles with average size of 100 nm on a carbon-based gas diffusion layer (GDL) via spray-coating (Supplementary Fig. 20a). The Cu gas diffusion electrode (GDE) was then immersed in N2-saturated 5 μmol L−1 AgNO3 aqueous solution at 65 °C for 1 h to obtain the Ag-doped Cu GDE. The Ag-doped Cu catalyst retains the particle size and the morphology of the pristine Cu nanoparticles (Fig. 2a, b, and Supplementary Figs. 20 and 21). Electron energy loss spectroscopy (EELS) elemental mapping showed that Ag and Cu elements were uniformly distributed in the particle (Fig. 2c and Supplementary Fig. 22). In transmission wide angle X-ray scattering (WAXS) data and powder X-ray diffraction (XRD) patterns, we observed peaks for Cu2O in both Cu and Ag-doped Cu GDE (Fig. 2d, e, and Supplementary Fig. 23), which were attributed to oxidation of Cu in air during the preparation of GDE. Due to the low concentration of Ag (4.0% atomic fraction determined by XPS), a peak shift relative to Cu is not observed in WAXS data of the Ag-doped Cu GDE (Fig. 2e and Supplementary Table 6). X-ray photoelectron spectroscopy (XPS) of the Ag-doped Cu GDE also showed the existence of CuO on the surface and confirmed the presence of Ag0 (Fig. 2f, g).

Fig. 2
figure 2

Structural and compositional analyses of Ag-doped Cu catalyst. a High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) image taken from a single particle. Scale bar, 20 nm. b Atomic-resolution HAADF-STEM image taken from the edge of a nanoparticle marked by a box in (a). Inset, the corresponding Fourier transfer image. Scale bar, 2 nm. c HAADF-STEM image of an Ag-doped Cu nanoparticle and the corresponding EELS elemental mappings of Cu, Ag, and O. Scale bar, 20 nm. d,e WAXS map (d) and the corresponding sector-average of WAXS map (e) for Ag-doped Cu GDE. f, g High-resolution Cu 2p (f) and Ag 3d (g) spectra of Ag-doped Cu GDE

CORR performance and Operando X-ray absorption spectroscopy

We then investigated the performance of the Ag-doped Cu GDE in CORR flow cell reactors (Supplementary Fig. 24). Flow cells overcome the mass transfer limitation of CO and produce a triple-phase interface that allows the gas reactant to contact the catalyst-electrolyte interface during the reaction. Figure 3a shows FEs for C2+ products in the applied potential range of −0.36 to −0.56 V with reference to the reversible hydrogen electrode (RHE) in 1 M KOH electrolyte. The liquid products (n-propanol, ethanol, and acetate) and gas products (ethylene and H2) were quantified using nuclear magnetic resonance (NMR) and gas chromatography, respectively (Supplementary Fig. 25 and Supplementary Table 7). In the applied potential range of −0.36 to −0.56 VRHE, the total C2+ FEs on Ag-doped Cu GDE are higher than that on Cu GDE: indeed the total FE of C2+ products on Ag-doped Cu GDE reaches about 80% at -0.56 VRHE. In particular, at a low potential of −0.46 VRHE, the Ag-doped Cu GDE records a high n-propanol FE of (33 ± 1)% with the partial n-propanol current density of (4.5 ± 0.1) mA cm-2, whereas n-propanol FE on pristine Cu is (22 ± 1)% (Fig. 3b). This impressive n-propanol FE represents the highest value reported for n-propanol production via CO2RR and CORR (Supplementary Table 8). The higher FE for C2+ and C3 products on Ag-doped Cu relative to Cu is consistent with predictions from DFT. The intrinsic activities for n-propanol production on Ag-doped Cu and Cu are reported via the partial current density for n-propanol production normalized to the electrochemical surface area (ECSA) (Supplementary Figs. 26, 27, and Supplementary Table 9). The ECSA-normalized partial n-propanol current density on Ag-doped Cu is 0.124 mA cm-2, which is 3 times that on Cu. The n-propanol EEcathodic half-cell reaches 20% at a low potential of −0.46 VRHE when the overpotential of oxygen evolution in anode side is assumed to be 0. After correcting for ohmic loss (Supplementary Table 10), the n-propanol EEcathodic half-cell reaches 21% under a low overpotential of 0.616 V. This EEcathodic half-cell is higher than the best prior reports by a margin of 1.3× (Supplementary Sections 3, 4, and Supplementary Table 8).

Fig. 3
figure 3

CO electroreduction performance and operando structural characterizations of Ag-doped Cu catalyst in flow cell. a FEs of n-propanol (n-PrOH), ethanol, acetate, and ethylene on Ag-doped Cu and pristine Cu catalysts under different potentials. b Comparison of n-propanol FEs on Ag-doped Cu and Cu GDE under different potentials, as well as partial current density of n-propanol formation on Ag-doped Cu GDE. Error bars represent the standard deviation based on three separate measurements. c Operando Cu K-edge XANES spectra of Cu GDE following 10 s and Ag-doped Cu GDE following 10, 20, 30, 80, 600, 1200, 1800, and 2400 s at −0.46 VRHE during CORR. Bulk Cu foil, CuO, and Cu2O are listed as references. d Operando Cu K-edge EXAFS spectrum of Ag-doped Cu GDE following 10 s at −0.46 VRHE during CORR. Bulk Cu foil was listed as a reference. Inset, an enlarged view of the section from 0.7 to 5.3 Å for Ag-doped Cu GDE

It should be noted that the highest n-propanol FE on both Ag-doped Cu and Cu GDEs were achieved at relatively low potential (-0.46 VRHE), and n-propanol FE decreased when further increasing the potential to −0.56 VRHE (Fig. 3a and Supplementary Table 7). The total C2 product and ethylene FEs on both Ag-doped Cu and Cu GDEs exhibited an increasing trend with increased applied potentials. This result can be explained by noting that the C–C coupling step for n-propanol formation becomes slow at high potential, and thus C2 intermediate protonation reaction is more favored compared with C–C coupling step for n-propanol formation26,34.

To study the chemical state of the catalyst during CORR, we performed operando X-ray absorption spectroscopy (XAS) of Ag-doped Cu GDE under operando CORR conditions at a constant applied potential of −0.46 VRHE. Operando Cu K-edge X-ray absorption near edge structure (XANES) spectra of Ag-doped Cu GDE show that Cu atoms were reduced to Cu0 in the first 10 s during CORR (Fig. 3c and Supplementary Fig. 28). Thereafter, the valence state of Cu is maintained at zero throughout CORR. Consistent results are shown in the operando extended X-ray adsorption fine structure (EXAFS). An EXAFS fitting analysis at the Cu K-edge showed the presence of Ag and its strong interaction with Cu by having Cu–Ag distance value between pure Cu and pure Ag (Fig. 3d and Supplementary Table 11)13. Collectively, operando XAS results demonstrated that Ag atoms are doped in the lattice of Cu nanoparticles, and that each element remains in its metallic state during CORR. As a control experiment, we carried out operando Cu K-edge XANES on Cu GDE, and it also showed that Cu oxides were reduced to Cu0 in the first 10 s during CORR. These results further demonstrated that, rather than benefiting from oxidation states8,13,16,21,47, the high FE of n-propanol on Ag-doped Cu GDE is associated with metallic states of Cu and might be ascribed to the different structures of Ag-doped Cu relative to Cu.

To explore further the role of Ag doping in Cu in facilitating C1–C1 and C1–C2 coupling, we investigated the CORR performance of Ag-doped Cu catalysts with different Ag concentrations. To vary the Ag concentration, we changed the immersion time of the Cu GDE in AgNO3 solution to 20 min and 2 h, respectively, denoted Cu–Ag-20 min and Cu–Ag-2 h. As in Ag-doped Cu, both Cu–Ag-20 min and Cu–Ag-2 h catalysts also retained the particle size and the morphology of the pristine Cu nanoparticles (Supplementary Figs. 2931). Thus, the size and morphology effect can be excluded when comparing the CORR performance between Cu and different types of Ag-doped Cu catalysts. The atomic percentages of Ag doping in Cu were tuned to 2.4% and 7.8% (XPS), respectively, for Cu–Ag-20 min and Cu–Ag-2 h catalysts (Supplementary Figs. 32, 33, and Supplementary Table 6). Relative to Cu GDE, both Cu–Ag-20 min and Cu–Ag-2 h GDE exhibited enhanced FEs of n-propanol, as well as higher FEs of total C2+ products (Fig. 4a, b), in the potential range from −0.36 to −0.56 VRHE toward CORR. These results are in agreement with DFT predictions of enhancement in C1–C1 and C1–C2 coupling by Ag doping in Cu. Additionally, among Ag-doped Cu catalysts with different Ag concentrations, Ag-doped Cu with an atomic percentage of 4.0% Ag showed the highest n-propanol FE at -0.46 VRHE (Supplementary Fig. 34). The analysis of operando Cu K-edge XANES of Cu–Ag-20 min and Cu–Ag-2 h GDE also demonstrates that Cu oxides are reduced to Cu0 in the first 10 s during CORR (Fig. 4c) and it is Ag-doped Cu in metallic state that is associated with the enhanced selectivity to n-propanol during CORR.

Fig. 4
figure 4

CO electroreduction performance on different types of Ag-doped Cu catalysts and operando structural characterizations in flow cell. a FEs of n-propanol, ethanol, acetate, and ethylene on Cu–Ag-20 min, Cu–Ag-2 h, and Cu GDE under different potentials. b Comparison of n-propanol FEs on Cu–Ag-20 min, Cu–Ag-2 h, and commercial Cu GDE. Error bars represent the standard deviation based on three separate measurements. c Operando Cu K-edge XANES spectra of Cu–Ag-20 min, Cu–Ag-2 h, and Cu GDE following 10 s at −0.46 VRHE. Bulk Cu foil, Cu2O, and CuO are listed as references

The carbon-based GDLs suffer from liquid penetration and gas diffusion blockage, termed flooding, over time. To overcome the flooding issue on carbon-based GDE after long operation time, we fabricated the Ag-doped Cu polytetrafluoroethylene (PTFE) electrode based on a configuration (graphite/carbon nanoparticle/Ag-doped Cu/PTFE electrode) developed by our group7. The Ag-doped Cu layer was prepared by immersing a Cu layer in 5 μmol L1 AgNO3 aqueous solution at 65 °C for 1 h. When a potential of −0.46 VRHE was applied, the FE of n-propanol on the Ag-doped Cu PTFE electrode achieved 33% and operated stably over 200 min of CORR (Supplementary Figs. 35 and 36).

We also compared the CO2RR performance of Ag-doped Cu and pristine Cu to explore whether the asymmetric active sites enhance in this distinct context the C1–C1 and C1–C2 coupling (Supplementary Fig. 37 and Supplementary Table 12). In the potential range from −0.82 to −1.79 VRHE (after iR compensation), both C2+ and C3 FEs on Ag-doped Cu catalysts are notably higher than those on pristine Cu: at the potential of −2.96 VRHE (−1.31  VRHE after iR compensation), the partial C2+ and n-propanol current densities of Ag-doped Cu are 308 ± 6 mA cm2 and 36 ± 2 mA cm2, and C2+ and n-propanol FEs on Ag-doped Cu are 62 and 7%, respectively, providing a doubling compared to pristine Cu.


This work demonstrates Ag doping in Cu to facilitate C1–C1 and C1–C2 coupling and thus improve the selectivity to C3 products during CORR. DFT results show that the strain and ligand effects due to Ag doping jointly provide an asymmetric C–C coupling active site containing two neighboring Cu atoms with different electronic structures, and that these are capable of enhancing C1–C1 and C1–C2 coupling. Experimentally, we achieved a total C2+ FE of about 80% and a record n-propanol FE of (33 ± 1)% with a partial n-propanol current density (4.5 ± 0.1) mA cm-2 on Ag-doped Cu catalyst in CORR. The EEcathodic half-cell for n-propanol also reaches 21% at a low potential of 0.416  VRHE, with a low overpotential of 0.616 V. These findings provide a framework for rational catalyst design for tuning the CORR selectivity towards high-energy-density C3 liquid products, a crucial step in overcoming the bottleneck of the electroproduction of C3 products.


DFT calculations

In this work, all the DFT calculations were carried out with a periodic slab model using the Vienna ab initio simulation program (VASP) ( Detailed theoretical methods are found in the Supplementary Information.

Preparation of electrodes

A commercial Cu of 8.5 mg was dispersed in a mixture of 0.85 mL of methanol and 8.5 μL of 5% Nafion under ultrasonication for 30 min. The suspension was deposited on a carbon-based GDL using spray-coating with a catalyst loading of ≈1 mg cm2 to prepare the Cu GDE. We then immersed the prepared Cu GDE in 5 μmol L1 AgNO3 aqueous solution at 65 °C for a certain time period to prepare Ag-doped Cu GDE as cathodes. The main goal of the work was to focus on improving the efficiency of the cathodic side of CORR to propanol. Thus, we used Ni foam (1.6 mm thickness, MTI Corporation) as the oxygen evolution reaction (OER) catalyst in the anode side because it is commercially available and have been showed as a good OER catalyst48. Details of chemicals and materials information are found in the Supplementary Information.


Scanning electron microscopy (SEM) images were taken using a Quanta FEG 250 microscope (Certain commercial equipment, instruments, or materials are identified in this paper and Supplementary Information in order to specify the experimental procedure adequately. Such identification is not intended to imply recommendation or endorsement by the National Institute of Standards and Technology, nor is it intended to imply that the materials or equipment identified are necessarily the best available for the purpose). HAADF-STEM images were taken using an aberration-corrected FEI Titan 80–300 kV TEM/STEM microscope at 300 kV, with a probe convergence angle of 30 mrad and a large inner collection angle of 65 mrad to provide a nominal image solution of 0.7 Å. EELS elemental mapping was collected on aberration-corrected JEOL JEM-ARM200F electron microscope at 200 kV equipped with Gatan GIF quantum energy filters. Structural characterization of cathodes was obtained using XRD (MiniFlex600) with Cu-Kα radiation. The surface compositions of cathodes were determined by XPS (model 5600, Perkin-Elmer) using a monochromatic aluminum X-ray source. Operando XAS measurements were conducted at 9BM beamline at Advanced Photon Source (APS, Argonne national laboratory, IL). Athena and Artemis software included in a standard IFEFFIT package were used to process XAS data49. WAXS measurements were carried out in transmission geometry at the CMS beamline of the National Synchrotron Light Source II (NSLS-II), a U.S. Department of Energy (DOE) office of the Science User Facility operated for the DOE Office of Science by Brookhaven National Laboratory. Samples were measured with an imaging detector at a distance of 0.177 m using X-ray wavelength of 0.729 Å. Nika software package was used to sector average the 2D WAXS images50. Data plotting was done in Igor Pro (Wavemetrics, Inc., Lake Oswego, OR, USA).

Electrochemical measurements

All the electrochemical measurements were conducted in flow cell reactor. Electrocatalytic measurements were operated using the three-electrode system at an electrochemical station (AUT50783). In the flow cell reactor, the prepared GDEs, anion exchange membrane, and nickel foam were positioned and clamped together between silicone gaskets and PTFE flow fields. Then 10 mL of electrolyte (1 M KOH aqueous solution) was introduced into the anode chamber between anode and membrane, as well as the cathode chamber between membrane and cathode, respectively. The electrolytes in cathode and anode were circulated by two pumps at the rate of 10 mL min1. CO gas (Linde, 99.99%) or CO2 gas (Linde, 99.99%) was continuously supplied to gas chamber located at the back side of cathode GDE at the rate of 50 mL min1. Gas could diffuse into the interface between cathode and electrolyte, thus generating a triple-phase interface between gas, electrode, and electrolyte. The catalytic performance of cathodes was evaluated by performing potentiostatic electrolysis.

All potentials were measured against an Ag/AgCl reference electrode (3 M KCl, BASi). Gas and liquid products were respectively analyzed using gas chromatograph (PerkinElmer Clarus 600) equipped with thermal conductivity and flame ionization detectors, and NMR spectrometer (Agilent DD2 600 MHz) by taking dimethylsulfoxide (DMSO) as an internal standard. All the potentials were converted to values with reference to RHE using \(E_{{\rm{RHE}}} = E_{{\rm{Ag}}/{\rm{AgCl}}} + 0.210\;{\rm{V}} + 0.0591 \times {\rm{pH}}.\)

ECSA was determined based on the equation ECSA = RfS, where Rf was roughness factor and S was geometric area of electrode (1 cm−2). Rf = Cdl/29 μF cm−2, where Cdl is the double-layer capacitance of catalyst and the double-layer capacitance of a smooth Cu surface is assumed to be 29 μF cm−2 (ref. 21). Double-layer capacitances of catalysts were determined by measuring cyclic voltammetry (CV) with different scan rates (40, 60, 80, 100, 120, and 140 mV s−1, respectively) in the potential ranges between 0.20 and 0.24 VRHE where no Faradaic process occurred. The CV measurement was operated in the same flow cell reactor and 1 M KOH aqueous solution saturated with nitrogen (Linde, 99.998%) was used as the electrolyte. The flow cell reactor was filled with electrolyte prior to the CV measurement and the electrolyte was not circulated during the CV measurement. N2, instead of CO2, was continuously supplied to gas chamber of the cell. By plotting the average current j (j = (jajc)/2, where ja and jc are anodic and cathodic current densities, respectively) at 0.22 VRHE against the scan rate, Cdl value was given by the slope.

The electrochemical impedance spectroscopy (EIS) technique was used to measure the ohmic loss between the working and reference electrodes and 70% iR compensation was applied to correct the potentials manually.

Data availability

The data supporting this study are available in the paper and the Supplementary Information. All other relevant source data are available from the corresponding authors upon reasonable request.


  1. Liu, M. et al. Enhanced electrocatalytic CO2 reduction via field-induced reagent concentration. Nature 537, 382–386 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  2. Gao, S. et al. Partially oxidized atomic cobalt layers for carbon dioxide electroreduction to liquid fuel. Nature 529, 68–71 (2016).

    ADS  CAS  PubMed  Article  Google Scholar 

  3. Seifitokaldani, A. et al. Hydronium-induced switching between CO2 electroreduction pathways. J. Am. Chem. Soc. 140, 3833–3837 (2018).

    CAS  PubMed  Article  Google Scholar 

  4. Le, M. et al. Electrochemical reduction of CO2 to CH3OH at copper oxide surfaces. J. Electrochem. Soc. 158, E45–E49 (2011).

    ADS  CAS  Article  Google Scholar 

  5. Zhang, W. et al. Electrochemical reduction of carbon dioxide to methanol on hierarchical Pd/SnO2 nanosheets with abundant Pd–O–Sn interfaces. Angew. Chem. Int. Ed. 57, 9475–9479 (2018).

    CAS  Article  Google Scholar 

  6. Qiao, J., Liu, Y., Hong, F. & Zhang, J. A review of catalysts for the electroreduction of carbon dioxide to produce low-carbon fuels. Chem. Soc. Rev. 43, 631–675 (2014).

    CAS  PubMed  Article  Google Scholar 

  7. Dinh, C.-T. et al. CO2 electroreduction to ethylene via hydroxide-mediated copper catalysis at an abrupt interface. Science 360, 783–787 (2018).

    CAS  PubMed  Article  Google Scholar 

  8. Mistry, H. et al. Highly selective plasma-activated copper catalysts for carbon dioxide reduction to ethylene. Nat. Commun. 7, 12123 (2016).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  9. Liu, Y., Chen, S., Quan, X. & Yu, H. Efficient electrochemical reduction of carbon dioxide to acetate on nitrogen-doped nanodiamond. J. Am. Chem. Soc. 137, 11631–11636 (2015).

    CAS  PubMed  Article  Google Scholar 

  10. Zhuang, T.-T. et al. Steering post-C–C coupling selectivity enables high efficiency electroreduction of carbon dioxide to multi-carbon alcohols. Nat. Catal. 1, 421–428 (2018).

    CAS  Article  Google Scholar 

  11. Ren, D., Ang, B. S.-H. & Yeo, B. S. Tuning the selectivity of carbon dioxide electroreduction toward ethanol on oxide-derived CuxZn catalysts. ACS Catal. 6, 8239–8247 (2016).

    CAS  Article  Google Scholar 

  12. Kim, D., Kley, C. S., Li, Y. & Yang, P. Copper nanoparticle ensembles for selective electroreduction of CO2 to C2–C3 products. Proc. Natl Acad. Sci. USA 114, 10560–10565 (2017).

    CAS  PubMed  Article  PubMed Central  Google Scholar 

  13. Hoang, T. T. H. et al. Nanoporous Copper-silver alloys by additive-controlled electrodeposition for the selective electroreduction of CO2 to ethylene and ethanol. J. Am. Chem. Soc. 140, 5791–5797 (2018).

    CAS  PubMed  Article  Google Scholar 

  14. Jouny, M., Luc, W. & Jiao, F. General techno-economic analysis of CO2 electrolysis systems. Ind. Eng. Chem. Res. 57, 2165–2177 (2018).

    CAS  Article  Google Scholar 

  15. Clark, E. L., Hahn, C., Jaramillo, T. F. & Bell, A. T. Electrochemical CO2 reduction over compressively strained CuAg surface alloys with enhanced multi-carbon oxygenate selectivity. J. Am. Chem. Soc. 139, 15848–15857 (2017).

    CAS  PubMed  Article  Google Scholar 

  16. Verdaguer-Casadevall, A. et al. Probing the active surface sites for CO reduction on oxide-derived copper electrocatalysts. J. Am. Chem. Soc. 137, 9808–9811 (2015).

    CAS  PubMed  Article  Google Scholar 

  17. Handoko, A. D. et al. Mechanistic insights into the selective electroreduction of carbon dioxide to ethylene on Cu2O-derived copper catalysts. J. Phys. Chem. C. 120, 20058–20067 (2016).

    CAS  Article  Google Scholar 

  18. Ren, D. et al. Mechanistic insights into the enhanced activity and stability of agglomerated Cu nanocrystals for the electrochemical reduction of carbon dioxide to n-propanol. J. Phys. Chem. Lett. 7, 20–24 (2016).

    CAS  PubMed  Article  Google Scholar 

  19. Rahaman, M., Dutta, A., Zanetti, A. & Broekmann, P. Electrochemical reduction of CO2 into multicarbon alcohols on activated Cu mesh catalysts: an identical location (IL) study. ACS Catal. 7, 7946–7956 (2017).

    CAS  Article  Google Scholar 

  20. Jiang, K. et al. Metal ion cycling of Cu foil for selective C–C coupling in electrochemical CO2 reduction. Nat. Catal. 1, 111–119 (2018).

    CAS  Article  Google Scholar 

  21. Li, C. W., Ciston, J. & Kanan, M. W. Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper. Nature 508, 504–507 (2014).

    ADS  CAS  PubMed  Article  Google Scholar 

  22. Feng, X., Jiang, K., Fan, S. & Kanan, M. W. A direct grain-boundary-activity correlation for CO electroreduction on Cu nanoparticles. ACS Cent. Sci. 2, 169–174 (2016).

    CAS  PubMed  PubMed Central  Article  Google Scholar 

  23. Raciti, D. et al. Low-overpotential electroreduction of carbon monoxide using copper nanowires. ACS Catal. 7, 4467–4472 (2017).

    CAS  Article  Google Scholar 

  24. Li, J. et al. Copper adparticle enabled selective electrosynthesis of n-propanol. Nat. Commun. 9, 4614 (2018).

    ADS  PubMed  PubMed Central  Article  CAS  Google Scholar 

  25. Zhuang, T.-T. et al. Copper nanocavities confine intermediates for efficient electrosynthesis of C3 alcohol fuels from carbon monoxide. Nat. Catal. 1, 946–951 (2018).

    CAS  Article  Google Scholar 

  26. Jouny, M., Luc, W. & Jiao, F. High-rate electroreduction of carbon monoxide to multi-carbon products. Nat. Catal. 1, 748–755 (2018).

    CAS  Article  Google Scholar 

  27. Kortlever, R., Shen, J., Schouten, K. J. P., Calle-Vallejo, F. & Koper, M. T. M. Catalysts and reaction pathways for the electrochemical reduction of carbon dioxide. J. Phys. Chem. Lett. 6, 4073–4082 (2015).

    CAS  PubMed  Article  Google Scholar 

  28. Cheng, T., Xiao, H. & Goddard, W. A. Full atomistic reaction mechanism with kinetics for CO reduction on Cu(100) from ab initio molecular dynamics free-energy calculations at 298 K. Proc. Natl Acad. Sci. USA 114, 1795–1800 (2017).

    CAS  PubMed  Article  PubMed Central  Google Scholar 

  29. Montoya, J. H., Shi, C., Chan, K. & Nørskov, J. K. Theoretical insights into a CO dimerization mechanism in CO2. J. Phys. Chem. Lett. 6, 2032–2037 (2015).

    CAS  PubMed  Article  Google Scholar 

  30. Liu, S. et al. Shape-dependent electrocatalytic reduction of CO2 to CO on triangular silver nanoplates. J. Am. Chem. Soc. 139, 2160–2163 (2017).

    CAS  PubMed  Article  Google Scholar 

  31. Jhong, H.-R. M. et al. A nitrogen-doped carbon catalyst for electrochemical CO2 conversion to CO with high selectivity and current density. ChemSusChem 10, 1094–1099 (2017).

    CAS  PubMed  Article  Google Scholar 

  32. Gabardo, C. M. et al. Combined high alkalinity and pressurization enable efficient CO2 electroreduction to CO. Energy Environ. Sci. 11, 2531–2539 (2018).

    CAS  Article  Google Scholar 

  33. Xiao, H., Cheng, T. & Goddard, W. A. Atomistic mechanisms underlying selectivities in C1 and C2 products from electrochemical reduction of CO on Cu (111). J. Am. Chem. Soc. 139, 130–136 (2016).

    PubMed  Article  CAS  Google Scholar 

  34. Kuhl, K. P., Cave, E. R., Abram, D. N. & Jaramillo, T. F. New insights into the electrochemical reduction of carbon dioxide on metallic copper surfaces. Energy Environ. Sci. 5, 7050–7059 (2012).

    CAS  Article  Google Scholar 

  35. Vayenas, C. G., White, R. E. & Gamboa-Aldeco, M. E. Modern Aspects of Electrochemistry Vol. 42 (Springer, New York, 2008)

  36. Hori, Y., Takahashi, R., Yoshinami, Y. & Murata, A. Electrochemical reduction of CO at a copper electrode. J. Phys. Chem. B 101, 7075–7081 (1997).

    CAS  Article  Google Scholar 

  37. Loiudice, A. et al. Tailoring copper nanocrystals towards C2 products in electrochemical CO2 reduction. Angew. Chem. Int. Ed. 55, 5789–5792 (2016).

    CAS  Article  Google Scholar 

  38. Lum, Y., Cheng, T., Goddard, W. A. & Ager, J. W. Electrochemical CO reduction builds solvent water into oxygenate products. J. Am. Chem. Soc. 140, 9337–9340 (2018).

    CAS  PubMed  Article  Google Scholar 

  39. Pérez-Gallent, E., Figueiredo, M. C., Calle-Vallejo, F. & Koper, M. T. M. Spectroscopic observation of a hydrogenated CO dimer intermediate during CO reduction on Cu(100) electrodes. Angew. Chem. Int. Ed. 56, 3621–3624 (2017).

    Article  CAS  Google Scholar 

  40. Goodpaster, J. D., Bell, A. T. & Head-Gordon, M. Identification of possible pathways for C–C bond formation during electrochemical reduction of CO2: new theoretical insights from an improved electrochemical model. J. Phys. Chem. Lett. 7, 1471–1477 (2016).

    CAS  PubMed  Article  Google Scholar 

  41. Xiao, H., Goddard, W. A., Cheng, T. & Liu, Y. Cu metal embedded in oxidized matrix catalyst to promote CO2 activation and CO dimerization for electrochemical reduction of CO2. Proc. Natl Acad. Sci. USA 114, 6685–6688 (2017).

    ADS  CAS  PubMed  Article  PubMed Central  Google Scholar 

  42. Hussain, J., Jonsson, H. & Skulason, E. Calculations of product selectivity in electrochemical CO2 reduction. ACS Catal. 8, 5240–5249 (2018).

    CAS  Article  Google Scholar 

  43. Greeley, J. et al. Alloys of platinum and early transition metals as oxygen reduction electrocatalysts. Nat. Chem. 1, 552–556 (2009).

    CAS  PubMed  Article  Google Scholar 

  44. Studt, F. et al. Identification of non-precious metal alloy catalysts for selective hydrogenation of acetylene. Science 320, 1320–1322 (2008).

    ADS  CAS  PubMed  Article  Google Scholar 

  45. Liu, P. & Norskov, J. K. Ligand and ensemble effects in adsorption on alloy surfaces. Phys. Chem. Chem. Phys. 3, 3814–3818 (2001).

    CAS  Article  Google Scholar 

  46. Cobley, C. M. & Xia, Y. Engineering the properties of metal nanostructures via galvanic replacement reactions. Mater. Sci. Eng. R: Rep. 70, 44–62 (2010).

    Article  CAS  Google Scholar 

  47. Zhou, Y. et al. Dopant-induced electron localization drives CO2 reduction to C2 hydrocarbons. Nat. Chem. 19, 974–980 (2018).

    Article  CAS  Google Scholar 

  48. Zhu, W., Zhang, R., Qu, F., Asiri, A. M. & Sun, X. Design and application of foams for electrocatalysis. Chemcatchem 9, 1721–1743 (2017).

    CAS  Article  Google Scholar 

  49. Ravel, B. & Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 12, 537–541 (2005).

    CAS  PubMed  Article  Google Scholar 

  50. Jan, I. Nika: software for two-dimensional data reduction. J. Appl. Crystallogr. 45, 324–328 (2012).

    Article  CAS  Google Scholar 

Download references


This work was supported by the Ontario Research Fund Research-Excellence Program, the Natural Sciences and Engineering Research Council (NSERC) of Canada, the CIFAR Bio-Inspired Solar Energy program, and University of Toronto Connaught grant. The STEM imaging part of this research was completed at the Center for Nanophase Materials Sciences, which is a DOE Office of Science User Facility. Synchrotron measurements were carried out at APS, an Office of Science User Facility operated for U.S. DOE Office of Science by Argonne National Laboratory, and was supported by the U.S. DOE under Contract No. DE-AC02-06CH11357, the Canadian Light Source and its funding partners, and CMS beamline of the National Synchrotron Light Source II, a U.S. DOE Office of the Science User Facility operated for the DOE Office of Science by Brookhaven National Laboratory. All DFT computations were performed on the IBM BlueGene/Q supercomputer with support from the Southern Ontario Smart Computing Innovation Platform (SOSCIP) and Niagara supercomputer at the SciNet HPC Consortium. SOSCIP is funded by the Federal Economic Development Agency of Southern Ontario, the Province of Ontario, IBM Canada Ltd., Ontario Centres of Excellence, Mitacs, and 15 Ontario academic member institutions. SciNet is funded by the Canada Foundation for Innovation, the Government of Ontario, Ontario Research Fund - Research Excellence, and the University of Toronto. J.L. acknowledges the Banting Postdoctoral Fellowships Program and the receipt of support from the CLSI Graduate and Post-Doctoral Student Travel Support Program. The authors thank T.P.W., Y.Z.F., L.M., and G.S. for technical support at the 9BM beamline of APS. C.M.G. acknowledges support from NSERC in the form of a postdoctoral fellowship. A.R.K. and L.J.R. would like to thank R.L. and M.F. for their assistance in WAXS measurements.

Author information

Authors and Affiliations



E.H.S. supervised the project. X.W. designed and carried out the experiments, analyzed the data, and wrote the paper. Z.W. carried out DFT simulations and wrote the corresponding section. J.L., D.-H.N. and F.L. performed synchrotron X-ray spectroscopy measurements. C.-W.H., C.-S.T., Z.C., M.C. and S.-C.L. conducted the aberration-corrected TEM characterizations. C.M.G. performed SEM characterization. P.T. and A.P. carried out XPS measurements. A.R.K. and L.J.R. carried out the WAXS measurement and analysed the WAXS data. T.-T.Z., C.-T.D., A.S., Y.P., Y.W., A.H.I, B.S., A.O., S.O.K. and D.S. assisted with the discussions. All authors discussed the results and contributed to the preparation of manuscript.

Corresponding author

Correspondence to Edward H. Sargent.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Peer review information Nature Communication thanks William Goddard, Feng Jiao and other, anonymous, reviewers for their contributions to the peer review of this work.

Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, X., Wang, Z., Zhuang, TT. et al. Efficient upgrading of CO to C3 fuel using asymmetric C-C coupling active sites. Nat Commun 10, 5186 (2019).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing