Abstract
Pseudocapacitors that originate from chemisorption contain redox active sites mainly composed of transition metal ions with unsaturated coordination in lattice on the electrode surface. The capacitance is generally dictated by the synergy of the porous microstructure, electronic conduction and active sites in the porous electrode. Here we grow metallic porous nitride single crystals at 2-cm scale to enhance pseudocapacitance through the combination of large surface area with porous microstructure, high conductivity with metallic states and ordered active sites with unsaturated coordination at twisted surfaces. We show the enhanced gravimetric and areal pseudocapacitance and excellent cycling stability both in acidic and alkaline electrolyte with porous MoN, Ta5N6 and TiN single crystals. The long-range ordering of active metal-nitrogen sites account for the fast redox reactions in chemisorption while the high conductivity together with porous microstructure facilitate the charge transfer and species diffusion in electrodes.
Similar content being viewed by others
Introduction
Pseudocapacitance originates from chemisorption regions or ion insertion during electrochemical sweeping1,2,3. Pseudocapacitors that originate from redox reactions conventionally use nonstoichiometric metal-oxide electrodes and these materials are always facing the challenges of low conductivity and chemical stability while remarkable capacitance reduction is also present due to their irreversibility during the redox reactions. Ruthenium dioxide is a typical oxide electrode which has a high capacitance, reversible charge-discharge features, and significant electrical conductivity, all of which make it highly promising to achieve higher capacitance. However, the high cost makes it unsuitable for many applications. Transition metal oxides like MnO2 have attracted increasing attention; however, the low conductivity and chemical stability of these materials remain fundamental challenges.
Transition-metal nitrides with unsaturated nitrogen coordination are generally a kind of electronic conductors. The nearest neighboring metal ions with short distances would provide a possibility of formation of metallic bond that facilitates electron transport in the connected pathway4,5,6,7,8,9. Coordinatively unsaturated metal-nitrogen active sites on electrode surfaces normally offer the ability to host redox reactions that give rise to reversible energy storage in the form of pseudocapacitance. The local structures of transition metal ions with unsaturated nitrogen coordination would accommodate the reversible chemisorption of specific ions in electrolyte and therefore lead to the redox reactions on electrode surfaces10,11,12,13. Porous nitride materials could provide a large surface area to host chemisorption while the inside interconnected pores and channels would facilitate the ion diffusion in electrolyte. Porous nitride with exposed unsaturated metal-nitrogen active sites would therefore be highly anticipated to deliver the synergy of porous microstructure, electronic conduction and active sites in electrode for higher energy density.
Single-crystalline metallic porous nitride would provide the possibility to well fit these rigorous requirements. The structural coherence in single crystals would confine the ordered active sites with unsaturated nitrogen coordination in lattice, which hence creates the electrochemically active surface to host fast redox reactions in chemisorption7,8. The utmost atom termination layer is clear at atomic scale on the surface of nitride single crystals and may be another advantage to create active surfaces through tailoring the crystal surface structures. Porosity in crystals would create large surface areas while the interconnected pores would make them highly accessible in electrolyte, which would considerably facilitate the species diffusions and fast redox reactions in porous electrodes. Porous single-crystalline nitrides with unsaturated nitrogen coordination are generally a kind of electronic conductor, and some of them have been confirmed to be chemically stable both in acidic and alkaline electrolyte7.
Here we grow metallic porous transition-metal nitride single crystals at a 2-cm scale to enhance pseudocapacitance by a combination of long-range ordering of active sites on a twisted surface, electronic conduction of metallic states and large surface areas of porous microstructures. We show the enhanced gravimetric and areal pseudocapacitance and excellent cycling stability with a metallic porous nitride single crystal. We disclose the fast redox reactions in the reversible chemisorption on metal-nitrogen active sites which are composed of transition metal ions with unsaturated nitrogen coordination numbers.
Results
Crystal growth
In this work, we grow metallic porous MoN single crystals through a lattice reconstruction strategy by direct conversion of PbMoO4 single crystals in a vacuumed ammonia atmosphere at high temperature. Figure 1a shows the growth mechanism of MoN crystal in relation to different lattice channels in PbMoO4 crystals. The [001], [100], and [110] facets of PbMoO4 crystals show suitable lattice channels for the diffusion of atomic lead14. Upon evaporation of Pb/O from lattice, the meta-stable Mo–O framework is formed and simultaneously nitrided in ammonia by the substitution of O with N, which leads to the growth of metallic MoN single crystals and therefore maintains a porosity of ~60% in the porous microstructures. Figure 1b shows the XRD patterns of parent PbMoO4 single crystals with facets of [001], [100], and [110], while inset images show the corresponding optical images of polished PbMoO4 parent crystals15. Figure 1c shows the XRD pattern of porous MoN single crystal with <001> orientation which is directly grown from the parent PbMoO4 crystals even with three different facets of [001], [100], and [110] under the identical conditions. The [001] facet of MoN is the most thermodynamically stable facet, which therefore leads to the preferential growth of <001> orientation in ammonia at high temperature. We further conduct the measurement of rocking curves which give full width at half max (FWHM) as small as 0.179, 0.193, and 0.092° for the porous MoN, Ta5N6, and TiN single crystals, respectively, as shown in Supplementary Fig. 1. The porous MoN single crystal with dimensions of 20 × 10 × 0.5 mm is harvested and shown in the inset image. No residual oxygen is observed while the mole ratio between N and Mo is at 1.0 in the porous MoN single crystals according to our element analysis as shown in the EDX mapping in Supplementary Fig. 2. Figure 1d shows the microstructure of MoN single crystal with <001> orientation while the porosity can be further tailored by changing atmospheric pressure as shown in Supplementary Fig. 3. The interconnected pores maintain open frameworks, which therefore combines the advantage of structural coherence and porous microstructures. Metallic porous TiN and Ta5N6 single crystals are also grown through lattice reconstruction strategy, respectively, as shown in Supplementary Figs. 4 and 5. The specific surface areas are ~14 m2 g−1 with the average pore size of ~40 nm for porous MoN single crystals as shown in Supplementary Fig. 6, which indicates the homogeneous distribution of porous microstructures even with different thickness. The porous Ta5N6 single crystal gives ~2 m2 g−1 for specific surface area and ~40 nm for the average pore size while the porous TiN single crystal gives ~6 m2 g−1 for specific surface area and ~100 nm for the average pore size.
The microstructures of porous MoN single crystals are examined using transmission electron microscopy (TEM) coupled with focused ion beam (FIB). Figure 2e shows the cross-sectional view of the porous MoN crystal grown along the <001> direction of PbMoO4 parent crystal, which confirms the well-interconnected pores with the diameter of 40–50 nm. The selected area electron diffraction (SAED) at different locations further confirms the identical facet orientation, as well as the single-crystalline nature with hexagonal phase in Fig. 2a–d, f–i. The metallic porous MoN single crystal grown with [100] PbMoO4 shows similar microstructure as shown in Supplementary Fig. 7, in which the identical single-crystalline nature is also observed even at different locations. Both porosity and microstructure are similar for the porous MoN single crystals even though they are grown along different facet directions of PbMoO4 crystals. We use spherical aberration corrected scanning transmission electron microscope (Cs-corrected STEM) coupled with focused ion beam (FIB) to further investigate the nature of porous MoN crystal. Figure 3a shows the high-resolution Cs-corrected STEM image of porous MoN crystal and the lattice spacing of 0.561 and 0.248 nm are ascribed to the [001] and [020] lattice fringes of MoN, respectively. The single-crystalline structure is further confirmed by SAED pattern in the inset of Fig.3a. Details of partial enlargement of Cs-corrected STEM image and the corresponding atom distribution are shown in Fig. 3b, which further approves the single-crystalline features of porous MoN crystal in hexagonal phase.
Active sites
We use high-sensitive low energy ion scattering (HS-LEIS) with He+ (3 keV) and Ne+ (5 keV) ions sources to detect the outmost atomic surface of porous MoN single crystals. In Fig. 3c, both He+ and Ne+ ion scattering spectra show the presence of atomic Mo termination layer, while the N atoms are beneath Mo atom layer as confirmed in the He+ spectrum. The trace of O atoms signal is attributed to the adsorbed oxygen on surface. The ordered triangle Mo-N1/2 structure would function as active metal-nitrogen sites to host fast redox reactions in chemisorption on surface. X-ray photoelectron spectra (XPS) show the Mo–N interactions with a binding energy of 397.82 eV for N1s and two binding energies at 228.79 and 231.92 eV for Mo 3d5/2 and Mo 3d3/2 in Mo–N bonds, respectively16,17,18,19. Figure 3d shows the simulated charge density of ordered active Mo-N1/2 sites with partial charge transferring from Mo to N atoms that delivers strong Mo–N interactions. The atomic termination layer of Ta and Ti are also confirmed for the porous Ta5N6 and TiN single crystals as shown in Supplementary Figs. 4 and 5. The long-range ordering of active sites at twisted surfaces would deliver highly-accessible electrochemically active surfaces to host fast redox reactions in porous microstructures. We summarize the surface characteristics of the three porous single crystals as shown in Supplementary Fig. 8. The porous MoN, TiN and Ta5N6 single crystals atomically terminate with Mo, Ti and Ta atom layer, respectively, with nitrogen atom layer stacking beneath the surface metal atom layer. The ordered active sites are confirmed to be Mo–N1/2, Ti-N1/2, and Ta-N3/5 which give rise to electrochemically active surfaces to host fast redox reactions in chemisorption.
The pseudocapacitance originates from the fast redox reactions through species chemisorption which would be dominated by the ordered active sites composed of transition metal ions with unsaturated nitrogen coordination. According to the charge balance, only pseudocapacitance with OH− adsorption would be observed for the porous TiN single crystal while pseudocapacitance both with OH− and H+ adsorption would be observed for porous MoN and Ta5N6 single crystals. To get atomistic insight to chemisorption on ordered active sites, density functional theory (DFT) calculation is conducted to investigate the adsorption energy of specific species on crystal surface both in acidic and alkaline electrolytes. In our work, we consider the H+ in acidic electrolyte and OH− in alkaline electrolyte as the adsorbed species when we calculate the adsorption energy of species on the surface of porous single crystals20,21,22. We have compared the calculated parameters with theoretical and experimental values as listed in Supplementary Table 123,24,25,26,27,28. The computed values of MoN, TiN, and Ta5N6 are well consistent with the theoretical and experimental values, which further indicates the reliability of theoretical calculation in our work. We further conduct the calculation of the band gaps and electronic structures for the porous MoN, TiN, and Ta5N6 single crystals. These nitrides are typical electronic conductors with band gaps of 0 eV as shown in Supplementary Fig. 9, which further validates the metallic properties of these porous nitride single crystals. We can clearly see from the density of states (DOS) map that the valence band is mainly composed of 2s and 2p orbital of N atoms and 3d orbital transition metal atoms. The conduction band is mainly dominated by the 3d orbital of transition metal atoms while the 2p orbital of N atoms also has a small contribution.
Chemical adsorption
Figure 4a shows the adsorption energy of H+ on [001] MoN surface, where the H binds with the nearest three Mo atoms with bond lengths in the range of 1.97–2.01 Å, indicating a strong chemisorption with a redox reaction. The adsorption energies range from approximately −0.7 to −0.1 eV for the different adsorption configurations which confirms the effective chemisorption in acidic electrolyte. Figure 4b shows the adsorption energies of OH− on [001] MoN surface, where the O binds with the nearest three Mo atoms with bond lengths in the range of 2.18–2.22 Å. The chemisorption of OH− leads to the partial oxidation of Mo in Mo–N local structures, showing the adsorption energies of approximately −1.63 to −1.82 eV for different adsorption configurations. The higher adsorption energy of OH− than H+ on MoN surface would deliver higher pseudocapacitance in alkaline electrolyte in contrast to the performance in acidic electrolyte, which well fits the phenomena observed in our experimental results both in KOH and H2SO4 electrolytes. Actually, the chemisorption is only a necessary condition while the higher adsorption energy indicates the higher energy barrier of desorption on surface. Reasonable chemisorption energy would be favorable to the enhanced pseudocapacitance with porous single crystals.
Figure 4c shows the chemisorption of OH− on [001] Ta5N6 surface, where the O atom binds with the nearest three Ta atoms, leading to the partial oxidation of Ta in Ta–N local structures. The adsorption energies of OH− are in the range of approximately −2.19 to −2.56 eV for different chemisorption configurations. In contrast, the chemisorption energies of H+ on [001] Ta5N6 surface are as high as approximately −1.10 to −1.32 eV for different configurations as shown in Supplementary Fig. 10. Higher adsorption energies give rise to enhanced pseudocapacitance with Ta5N6 in acidic electrolyte than that in alkaline electrolyte, which is well consistent with our experimental results. Figure 4d shows the chemisorption of OH− on [100] TiN surface where the nearest three Ti atom bind with three O atoms, leading to the bond lengths of 1.89–2.24 Å with the adsorption energy of approximately −0.55 to −1.0 eV. The chemisorption of OH− is indeed a process of partial oxidation of Ti in Ti–N local structures that results in a proper pseudocapacitance in alkaline electrolyte. However, the adsorption energy of H+ on [100] TiN surface is an endothermic process with positive adsorption energies, which well fits the negligible pseudocapacitance with porous TiN single crystal as observed in acidic electrolyte. We further summarize the adsorption energies of H+ and OH− on similar surfaces in reported work and list them in Supplementary Table 229,30,31,32,33,34,35,36. The adsorption energy is normally below 0 which indicates an exothermic process that favors the chemisorption on different surfaces of metallic substrates. The calculated adsorption energy in our work is well consistent with the reported values. The chemisorption of specific species like H+ and OH− on ordered active sites would lead to redox reactions that deliver pseudocapacitance, while reasonably high chemisorption energy greatly would favor the enhancement of pseudocapacitance.
Pseudocapacitor performance
These transition-metal nitrides are electronic conductors with conductivity as high as 0.77 × 104 for MoN, 0.8 × 104 for TiN, and 0.45 × 104 S cm−1 for Ta5N6 single crystals as shown in Supplementary Fig. 11. All these three porous single crystals demonstrate metallic conduction behaviors with the highest conductivity observed at the temperatures of ~ 50 K while the conductivity is decreased by ~50% at room temperature. Figure 5a shows the CV curve with porous MoN single crystal electrode in 1 M KOH solution. The nearly rectangular CV curve indicates the good capacitance property, which may be due to the excellent charge propagation of electrons in the metallic porous MoN single crystals. The triangular CD curves in Fig. 5b shows the exceptional symmetrical characteristic of charge-discharge curves in alkaline electrolyte, which further reveals that the metallic porous MoN single crystals have excellent electrochemical capability and reversibility. In Fig. 5c, the bulk solution resistance (Rs) is estimated to be 1.6 Ω while the absence of an impedance arc in the high-frequency region indicates a very low resistivity of MoN single crystal in aqueous alkali solution, due to the synergy of highly accessible surface area, intrinsic electrical conductivity and electrochemical activity. Figure 5d shows the exceptionally high stability of cycling performance with no degradation being observed even after 10,000 cycles. We believe that there may be two reasons for the excellent cycling stability. Firstly, these transition metal nitrides are chemically stable both in acid and alkaline solutions even in the presence of chemical adsorption of H+ or OH− on surfaces. Secondly, these porous single crystals, free of grain boundary, have the unique advantage of structural coherence, which reduces the interface defects at the largest extent and hence enhances the stability. Figure 5e shows that the current density is linearly changed versus the scan rate, indicating that the pseudocapacitance is mainly dominated by the chemisorption of the OH− and H+ on ordered active sites on the surface of porous MoN single crystal.
The chemisorption of OH− ions is an oxidation process of Mo in ordered local structures, which therefore delivers the exceptionally high pseudocapacitance in alkaline electrolyte. We further conduct Electron Paramagnetic Resonance (EPR) to analyze the porous MoN single crystal which shows EPR signals with g factor of 2.27 that originate from the free electrons in the coordinatively unsaturated Mo–N local structures37. We then summarize the unsaturated metal-nitrogen active sites and adsorption energies as shown in Supplementary Fig. 12. The metal-nitrogen coordination structure would function as active sites to accommodate the fast redox reactions in chemisorption on electrode surfaces, which therefore gives the enhanced pseudocapacitance with metallic porous single crystals. Similarly, enhanced pseudocapacitance performance and cycling stability are also observed in acidic electrolyte, which is mainly originating from the chemisorption of H+ that leads to the reduction of Mo in ordered local structures as shown in Supplementary Fig. 13. Improved pseudocapacitance performance is observed for Ta5N6 electrode with reversible chemisorption both in alkaline and acidic electrolyte as shown in Supplementary Figs. 14 and 15. It should be noted that only oxidation reactions with chemisorption of OH− on the surface of porous TiN single crystal electrode leads to pseudocapacitance in alkaline electrolyte in Supplementary Fig. 16 while the chemisorption of H+ that results in reduction of Ti is not favorable and contributes negligible pseudocapacitance in acidic electrolyte in Supplementary Fig. 17.
Pseudocapacitance mechanism
The linear dependence of capacitance performance on the current densities and sweep rates clearly confirms the typical characteristics of pseudocapacitance that originates from the reversible redox chemical reactions on electrode surfaces. We further summarize the correlation of pseudocapacitance with the current densities and sweep rates for the porous MoN, TiN and Ta5N6 single crystals as shown in Supplementary Fig. 18. The linear fitting gives the correlation coefficients of 0.954–0.999, which indicates that the capacitance performance is mainly dominated by the pseudocapacitance from the redox reactions on electrode surfaces. As shown in Fig. 5f, we summarize the areal capacitance with metallic porous MoN single crystals as a function of sweeping current densities. The porous MoN single crystal reaches a very high value of 8.8 F cm−2 at a current density of 5 mA cm−2 in a CD measurement, and remains 3 F cm−2 even at 100 mA cm−2, indicating the excellent performance with metallic porous single crystals at high constant current charge-discharge process. We further summarize the reported areal pseudocapacitance with different nano-scale materials and show that the areal pseudocapacitance with porous MoN single crystals is among the first level with sulfide electrode and ~3–10 times higher than reported values with most oxide and nitride electrodes as shown in Supplementary Table 338,39,40,41,42,43,44,45,46,47,48,49,50.
We further grow porous MoN single crystals with the thickness of 18 and 36 μm and measure the specific area capacitance normalized relative to their BET surface areas. We get a very high normalized area capacitance value of more than 3500 μF cm−2 which is among the highest values of current materials that exhibit pseudocapacitance and hundreds to thousands times larger than the value of the EDLC of carbon materials51. The pseudocapacitance is mainly dominated by the surface chemisorption on nitride surfaces. We further grow the porous MoN single crystals with the thickness ranging to 500 μm and investigate the correlation of pseudocapacitance with the electrode thickness. As shown in Supplementary Fig. 19, it is observed that the effective chemisorption takes place below the thickness of ~70 μm in the porous microstructures which delivers the pseudocapacitance for porous single crystals. The highest specific area capacitance is therefore observed for the porous MoN single crystals with the thickness of 70 μm. We further summarize the relationship between coordination structure, surface area, gravimetric capacitance and areal capacitance for porous MoN, TiN, and Ta5N6 single crystals as shown in Supplementary Fig. 20. Coordinatively unsaturated metal-nitrogen sites account for the chemisorption while reasonable adsorption energy gives rise to enhanced pseudocapacitance. The porous MoN single crystal shows the highest gravimetric capacitance of ~2000 F g−1 in alkaline electrolyte and ~800 F g−1 in acidic electrolyte. And the area capacitance of ~8 F cm−2 in alkaline electrolyte and ~5 F cm−2 in acidic electrolyte are also obtained with porous MoN single crystal.
Discussion
In conclusion, we demonstrate the long-range ordering of the active site on metallic porous nitride single crystals to enhance pseudocapacitance. The synergy of porous microstructure, electronic conduction and ordered active sites in metallic porous single-crystalline electrode facilitates the fast reversible redox reactions and therefore contributes to the enhanced pseudocapacitance. We show the improved gravimetric and areal pseudocapacitance and excellent cycling stability with porous metal-nitride single crystals both in acidic and alkaline electrolytes. The current work would shed a light on the growth of metallic porous single crystals to tailor resolved local structures with unsaturated coordination on surface and hence to engineer the fast redox reactions in chemisorption that results in pseudocapacitance. The lattice reconstruction strategy would also open a new route to grow porous single crystals in wealth of other materials to enhance the capability of the materials themselves.
Methods
Experiment
The MoN single crystal is prepared by directly treating PbMoO4 single crystals in ammonia atmosphere using chemical vapor deposition system7,8,9. The PbMoO4 substrates (20 × 10 × 0.5 mm), both side polished, are washed with ultrasonic wave in distilled water and organic solvents (ethanol, acetone) for several times. The substrates are dried in a stream of dry nitrogen and immediately put into an alumina tube furnace. The substrates are annealed in NH3 at 750 °C for 10 h under the pressure of 25–500 Torr. Ammonia gas (99.999%) is passed through the tube at a flow rate of 600 mL min−1. Then the outlet gas is cooled with cycling water to room temperature while the Pb and PbO are collected in the steel chamber in the form of solid powder out of the furnace. The solid Pb/PbO powders are collected and disposed in the form of toxic chemicals. We show the optical photo of the experimental setup in Supplementary Fig. 21.
We use 100 mL of 1 M KOH and 0.5 M H2SO4 as the electrolyte solutions. The electrochemical experiments are carried out using a three electrode setup. A Pt foil with a dimension of 1 cm × 1 cm works as the counter electrode and a saturated calomel electrode (0.244 V versus SHE) is used as reference electrode. All experiments are performed using an electrochemical workstation (IM6 Zahner, Germany). The electrochemical impedance spectra (EIS) are recorded in the frequency range of 0.1–105 Hz at the applied amplitude of AC potential of 5 mV. The Nyquist plots are recorded from the fitted EIS results. Conductivities of the synthesized electrode are measured by the four point probe method in PPMS (Quantum Design).
Calculation
Density functional theory (DFT) calculations are performed using Vienna Ab Initio Simulation Package (VASP) code52. Based on the projector augmented wave (PAW) approach, the plane-wave cutoff energy of 500 eV is used, which gives well converged relative energies for the system. The Perdew-Burke-Ernzerhof (PBE) function is chosen here to describe the exchange correlation interactions. The energies and residual force are converged to 10−6 eV with an d 0.02 eV Å−1 in the process of electronic and geometric optimizations. We calculate the unit cell and obtain the lattice parameters of MoN: a = b = 5.73 Å and c = 5.61 Å (a 6 × 6 × 6 k-point grid). A p(2 × 2) superstructure with Mo termination of the [001] surface is used for the slab model34,53. In this model, which includes three layers, the atoms in the bottom layers are frozen to its bulk geometry during the optimization and other atoms are fully relaxed. A 24-Å vacuum region is insert along the c direction to avoid the interactions between the slab and its repeating image. A 3 × 3 × 1 k-point grid is used for Brillouin zone sampling. Spin-polarization is considered for all calculation.
Data availability
The data that support the findings of this study are available from the corresponding author upon request. All reported data are included in the paper and supplementary materials. The Source Data can be downloaded from: https://yunpan.360.cn/surl_yuZg3ueVvAY (Code: 5f09).
References
Ghidiu, M., Lukatskaya, M. R., Zhao, M.-Q., Gogotsi, Y. & Barsoum, M. W. Conductive two-dimensional titanium carbide ‘clay’ with high volumetric capacitance. Nature 516, 78–81 (2014).
Li, J. et al. Achieving high pseudocapacitance of 2D titanium carbide (MXene) by cation intercalation and surface modification. Adv. Energy Mater. 7, 1602725 (2017).
Augustyn, V. et al. High-rate electrochemical energy storage through Li+ intercalation pseudocapacitance. Nat. Mater. 12, 518–522 (2013).
Bera, G. et al. Multifunctionality of partially reduced graphene oxide–CrVO4 nanocomposite: electrochemical and photocatalytic studies with theoretical insight from density functional theory. J. Phys. Chem. C. 122, 21140–21150 (2018).
Pathak, A., Gangan, A. S., Ratha, S., Chakraborty, B. & Rout, C. S. Enhanced pseudocapacitance of MoO3-reduced graphene oxide hybrids with insight from density functional theory investigations. J. Phys. Chem. C. 121, 18992–19001 (2017).
Ratha, S. et al. Urea-assisted room temperature stabilized metastable β-NiMoO4: experimental and theoretical insights into its unique bifunctional activity toward oxygen evolution and supercapacitor. ACS Appl. Mater. Interfaces 9, 9640–9653 (2017).
Zhang, F. et al. Metallic porous iron nitride and tantalum nitride single crystals with enhanced electrocatalysis performance. Adv. Mater. 31, 1806552 (2019).
Lin, G., Xi, S., Pan, C., Lin, W. & Xie, K. Growth of 2 cm metallic porous TiN single crystals. Mater. Horiz. 5, 953–960 (2018).
Chen, C., Sun, S., Chou, M. M. C. & Xie, K. In situ inward epitaxial growth of bulk macroporous single crystals. Nat. Commun. 8, 2178 (2017).
Yan, C. et al. Coordinatively unsaturated nickel-nitrogen sites towards selective and high-rate CO2 electroreduction. Energy Environ. Sci. 11, 1204–1210 (2018).
Wang, X. et al. Regulation of coordination number over single co sites: triggering the efficient electroreduction of CO2. Angew. Chem. Int. Ed. 57, 1944–1948 (2018).
Wang, J. et al. High-density iron nanoparticles encapsulated within nitrogen-doped carbon nanoshell as efficient oxygen electrocatalyst for zinc-air battery. Nano Energy 13, 387–396 (2015).
Chen, X., Yu, L., Wang, S., Deng, D. & Bao, X. Highly active and stable single iron site confined in graphene nanosheets for oxygen reduction reaction. Nano Energy 32, 353–358 (2017).
Li, X., Gao, C., Jiang, Y. Z. & Li, X. K. Pure phase MoN: preparation by chemical-diffused permeation and enhanced conductivity with rare earth Gd. Rare Met. 34, 137–142 (2015).
Atuchin, V. V., Andreeva, O. P., Korolkov, I. V., Maximovskiy, E. A. & Lim, C. S. Low-temperature synthesis and structural properties of PbMoO4 nanocrystals. Asian J. Chem. 26, 1287–1289 (2014).
Inumaru, K., Baba, K. & Yamanaka, S. Preparation of superconducting molybdenum nitride MoNx (0.5⩽x⩽1) films with controlled composition. Phys. B 383, 84–85 (2006).
Wang, S. T., Wang, X., Zhang, Z. D. & Qian, Y. T. Synthesis of nanocrystalline MoN from a new precursor by TPR method. J. Mater. Sci. 38, 3473–3478 (2003).
Zhang, L. et al. Efficient electrochemical N2 reduction to NH3 on MoN nanosheets array under ambient conditions. ACS Sustain. Chem. Eng. 6, 9550–9554 (2018).
Jeong, E., Park, J., Choi, S., Kang, J. & Kang, Y. C. Surface characteristics of monx thin films obtained by reactive rf magnetron sputtering in UHV system. Bull. Korean Chem. Soc. 36, 2446–2450 (2015).
Wang, Y. & Cheng, H. P. Oxygen reduction activity on perovskite oxide surfaces: a comparative first-principles study of LaMnO3, LaFeO3, and LaCrO3. J. Phys. Chem. C. 117, 2106–2112 (2013).
Zakaryan, H. A., Kvashnin, A. G. & Oganov, A. R. Stable reconstruction of the (110) surface and its role in pseudocapacitance of rutile-like RuO2. Sci. Rep. 7, 10357 (2017).
Tsai, H. C. et al. DFT study of oxygen reduction reaction on Os/Pt core–shell catalysts validated by electrochemical experiment. ACS Catal. 5, 1568–1580 (2015).
Kanoun, M. B., Goumri-Said, S. & Jaouen, M. Structure and mechanical stability of molybdenum nitrides: A first-principles study. Phys. Rev. B 76, 134109 (2007).
Ihara, H., Kimura, Y., Senzaki, K., Kezuka, H. & Hirabayashi, M. Electronic structures of B1 MoN, fcc Mo2N, and hexagonal MoN. Phys. Rev. B 31, 3177–3178 (1985).
Moreno, J. J. G. & Nolan, M. Ab initio study of the atomic level structure of the rutile TiO2(110) -titanium nitride (TiN) interface. ACS Appl. Mater. Interfaces 9, 38089–38100 (2017).
Hoerling, A. et al. Thermal stability, microstructure and mechanical properties of Ti1-xZrxN thin films. Thin Solid Films 516, 6421–6431 (2008).
Wang, J., Jiang, J., Chen, J., Li, Y. & Ma, A. Theoretical study of the oxygen impurity doped Ta5N6. Comput. Mater. Sci. 143, 368–373 (2018).
Petrunin, V. F., Sorokin, N. I., Borovinskaya, I. P. & Pityulin, A. N. Stability of cubic tantalum nitrides during heat treatment. Powder Metall. Met. Ceram. 19, 191–192 (1980).
Watanabe, E., Ushiyama, H. & Yamashita, K. Theoretical studies on the mechanism of oxygen reduction reaction on clean and O-substituted Ta3N5(100) surfaces. Catal. Sci. Technol. 5, 2769–2776 (2015).
Xu, L., Xiao, H. Y. & Zu, X. T. First-principles study on the geometry and stability of hydrogen on the Ta(001) (1 × 1) surface. Surf. Rev. Lett. 12, 809–817 (2005).
Ferrin, P., Kandoi, S., Nilekar, A. U. & Mavrikakis, M. Hydrogen adsorption, absorption and diffusion on and in transition metal surfaces: a DFT study. Surf. Sci. 606, 679–689 (2012).
Wang, T., Li, Y.-W., Wang, J., Beller, M. & Jiao, H. Dissociative hydrogen adsorption on the hexagonal Mo2C phase at high coverage. J. Phys. Chem. C. 118, 8079–8089 (2014).
Norskov, J. K. et al. Trends in the exchange current for hydrogen evolution. J. Electrochem. Soc. 152, J23–J26 (2005).
Zhao, J. et al. Insights into the mechanism of ammonia decomposition on molybdenum nitrides based on DFT studies. J. Phys. Chem. C. 123, 554–564 (2019).
Seifitokaldani, A., Savadogo, O. & Perrier, M. Density functional theory (DFT) computation of the oxygen reduction reaction (ORR) on titanium nitride (TiN) surface. Electrochim. Acta 141, 25–32 (2014).
Calatayud, M. & Minot, C. Effect of relaxation on structure and reactivity of anatase (100) and (001) surfaces. Surf. Sci. 552, 169–179 (2004).
Laguta, V. V. et al. Electron spin resonance study of Mo3+ centers in YAlO3. Radiat. Meas. 38, 735–738 (2004).
Cui, H. et al. Niobium nitride Nb4N5 as a new high-performance electrode material for supercapacitors. Adv. Sci. 2, 1500126 (2015).
Zhai, T. et al. Oxygen vacancies enhancing capacitive properties of MnO2 nanorods for wearable asymmetric supercapacitors. Nano Energy 8, 255–263 (2014).
Lukatskaya, M. R. et al. Ultra-high-rate pseudocapacitive energy storage in two-dimensional transition metal carbides. Nat. Energy 2, 17105 (2017).
Liu, J. et al. Co3O4 Nanowire@MnO2 ultrathin nanosheet core/shell arrays: a new class of high-performance pseudocapacitive materials. Adv. Mater. 23, 2076–2081 (2011).
Zhang, G. & Lou, X. W. General solution growth of mesoporous NiCo2O4 nanosheets on various conductive substrates as high-performance electrodes for supercapacitors. Adv. Mater. 25, 976–979 (2013).
Sumboja, A., Foo, C. Y., Wang, X. & Lee, P. S. Large areal mass, flexible and free-standing reduced graphene oxide/manganese dioxide paper for asymmetric supercapacitor device. Adv. Mater. 25, 2809–2815 (2013).
Xiao, X. et al. WO3-x/MoO3-x core/shell nanowires on carbon fabric as an anode for all-solid-state asymmetric supercapacitors. Adv. Energy Mater. 2, 1328–1332 (2012).
Dong, L. et al. Simultaneous production of high-performance flexible textile electrodes and fiber electrodes for wearable energy storage. Adv. Mater. 28, 1675–1681 (2016).
Zeng, Y. et al. Advanced Ti-Doped Fe2O3@PEDOT core/shell anode for high-energy asymmetric supercapacitors. Adv. Energy Mater. 5, 1402176 (2015).
Yuan, L. et al. Paper-based supercapacitors for self-powered nanosystems. Angew. Chem. Int. Ed. 51, 4934–4938 (2012).
He, Q., Wang, Y., Liu, X. X., Blackwood, D. J. & Chen, J. S. One-pot synthesis of self-supported hierarchical urchin-like Ni3S2 with ultrahigh areal pseudocapacitance. J. Mater. Chem. A 6, 22115–22122 (2018).
Chen, H. et al. In situ growth of NiCo2S4 nanotube arrays on Ni foam for supercapacitors: Maximizing utilization efficiency at high mass loading to achieve ultrahigh areal pseudocapacitance. J. Power Sources 254, 249–257 (2014).
Yao, B. et al. Efficient 3D printed pseudocapacitive electrodes with ultrahigh MnO2 loading. Joule 3, 1–12 (2019).
Sheberla, D. et al. Conductive MOF electrodes for stable supercapacitors with high areal capacitance. Nat. Mater. 16, 220–224 (2017).
Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comp. Mater. Sci. 6, 15–50 (1996).
Ren, J. et al. Thiophene adsorption and activation on MoP(001), γ-Mo2N(100), and Ni2P(001): density functional theory studies. J. Phys. Chem. B 110, 22563–22569 (2006).
Acknowledgements
We acknowledge the funding support from the National Key Research and Development Program of China (2017YFA0700102), Natural Science Foundation of China (91845202), Dalian National Laboratory for Clean Energy (DNL180404), and Strategic Priority Research Program of Chinese Academy of Sciences (XDB2000000).
Author information
Authors and Affiliations
Contributions
S.X. conducted the work related to metallic porous MoN and Ta5N6 single crystals. G.L. conducted the work related to metallic porous TiN single crystal. G.L. and L.J. helped to analyze the data and draw the figures. H.L. conducted the DFT calculation. K.X. supervised the work.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Xingbin Yan and other, anonymous, reviewers for their contributions to the peer review of this work. Peer review reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Xi, S., Lin, G., Jin, L. et al. Metallic porous nitride single crystals at two-centimeter scale delivering enhanced pseudocapacitance. Nat Commun 10, 4727 (2019). https://doi.org/10.1038/s41467-019-12818-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12818-x
This article is cited by
-
Potential of V-Si72, V-C72, and V-Al36N36 as catalysts for oxygen reduction reaction
Journal of Molecular Modeling (2024)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.