Abstract
Aqueous rechargeable microbatteries are promising on-chip micropower sources for a wide variety of miniaturized electronics. However, their development is plagued by state-of-the-art electrode materials due to low capacity and poor rate capability. Here we show that layered potassium vanadium oxides, KxV2O5·nH2O, have an amorphous/crystalline dual-phase nanostructure to show genuine potential as high-performance anode materials of aqueous rechargeable potassium-ion microbatteries. The dual-phase nanostructured KxV2O5·nH2O keeps large interlayer spacing while removing secondary-bound interlayer water to create sufficient channels and accommodation sites for hydrated potassium cations. This unique nanostructure facilitates accessibility/transport of guest hydrated potassium cations to significantly improve practical capacity and rate performance of the constituent KxV2O5·nH2O. The potassium-ion microbatteries with KxV2O5·nH2O anode and KxMnO2·nH2O cathode constructed on interdigital-patterned nanoporous metal current microcollectors exhibit ultrahigh energy density of 103 mWh cm−3 at electrical power comparable to carbon-based microsupercapacitors.
Similar content being viewed by others
Introduction
Continuous miniaturization of self-powered flexible and portable electronics, implantable medical devices, and microelectromechanical systems (MEMS) has raised urgent demands for sufficiently compact and/or flexible energy storage to realize safe and reliable energy autonomy1,2. Many types of miniaturized energy-storage devices are being developed to power microelectronic devices as stand-alone micropower sources or intermediate energy-storage units complementing energy conversion devices (e.g., solar cells, piezoelectric nanogenerators, or thermalelectric cells)1,2. These include traditional lithium-ion microbatteries based on volumetric reactions3,4,5,6,7 and microsupercapacitors based on surface adsorption/desorption or/and redox reactions8,9,10,11,12,13,14,15,16,17. Although lithium-ion microbatteries have high gravimetric/volumetric energy3,4,5,6,7, the safety issues associated with highly toxic and flammable organic electrolytes besides the inferior rate capability and stability essentially impede their practical use in microelectronic devices. Whereas microsupercapacitors can tackle these problems by making use of (pseudo)capacitive energy storage in low-cost and safe water-based electrolytes, few of them have energy density approaching that of microbatteries8,9,10,11,12,13,14,15,16,17. Therefore, it is highly desirable to explore alternative electrochemical energy-storage technologies that can store/deliver energy with lithium-ion microbattery-like capacity and microsupercapacitor-like rate performance for satisfying the versatile requirements in micro/nano-systems.
Battery chemistries based on electrochemical intercalation of alkaline or alkali-earth cations (M = Li+ (ref. 18,19,20), Na+ (ref. 21,22,23,24), K+ (ref. 25,26,27,28), Mg2+ (ref. 29), and Zn2+ (refs. 30,31)) in aqueous electrolytes are currently the most encouraging tentative, wherein the hydrated metal cations, instead of their crystalline ions, serve as charge carriers to take part in the electrochemical processes because of strong ion-solvent interactions32. By virtue of the K+ cations having the smallest hydrated radii and the highest conductivity in water-based electrolytes33,34, aqueous rechargeable potassium ion microbatteries (AR-PIMBs) hold a great promise as highly safe energy-storage microdevices to store/deliver high-density energy at fast charge/discharge rates. However, few electrode materials such as transition-metal oxides (TMOs) with a layered structure (e.g., polymorphic vanadium oxides25) and Prussian Blue analogs (PBAs)26,27 (nickel hexacyanoferrate35, iron hexacyanoferrate dihydrate49, and nickel ferrocyanide36) have been explored for reversible hydrated K+ cation intercalation. Compared with these PBAs with limited capacities (~60 mAh g−1), layered vanadium pentoxides without/with pre-intercalation of alkaline or alkali-earth ions, typically amorphous V2O5 xerogel (V2O5·nH2O)37,38 and MxV2O5·nH2O25,39, have large interlayer distances, which are expected to facilitate diffusion and storage of guest hydrated cations with a high theoretical capacity of 443 mAh g−1. Nevertheless, the state-of-the-art layered vanadium pentoxide-based electrode materials often exhibit practical capacities far below the theoretical value and deliver much lower levels of electrical power than capacitor materials40,41. This is due to the basic structure units comprised of bilayer V2O5 sheets and a large number of crystalline water molecules sandwiched between them34, wherein the former suffers from a low electrical conductivity and the latter blocks the intercalation of hydrated cations42,43. When removing the crystalline water to alleviate the blocking influence on the intercalation of hydrate cations, crystallization usually takes place to produce the orthorhombic V2O5 (o-V2O5) or the monoclinic MxV2O5 with small interlayer spacing38,40,44,45, which not only fails to improve the specific capacity and rate capability but leads to extra massive volume change during the insertion/extraction of hydrated cations to limit microbattery lifetime38,39,40,41,43. Such structure tradeoff always leads to their low capacity, poor rate capability, and short lifetime, restricting the wide use of vanadium oxide-based electrode materials in AR-PIMBs.
Here we show layered potassium vanadium oxides composed of amorphous/crystalline K0.25V2O5·nH2O/o-V2O5 dual phases (ac-KxV2O5) as promising anode materials of high-performance AR-PIMBs when integrated on three-dimensional (3D) bicontinuous nanoporous Au current microcollectors (NP Au/ac-KxV2O5). Therein, the amorphous K0.25V2O5·nH2O serves as molecular pillars to keep the large interlayer spacing while the crystalline o-V2O5 offers sufficient room to accommodate more guest hydrated K+ cations. As a consequence, the NP Au/ac-KxV2O5 electrodes exhibit a volumetric capacity of as high as ~715 mAh cm−3 with an exceptional rate performance. This enlists the AR-PIMBs with the ac-KxV2O5 anode and the cryptomelane KxMnO2·nH2O (c-KxMnO2) cathode integrated on interdigital-patterned nanoporous Au current microcollectors (V-Mn) to store/deliver charge with volumetric energy of ~103 mWh cm−3 (14-fold higher than that of 4V-500 μAh thin-film lithium battery) at electrical power comparable to carbon-based microsupercapacitors. Meanwhile, these V-Mn AR-PMIBs exhibit a long-term cycling stability because the large interlayer spacing can effectively relieve volume expansion/contraction during the insertion/extraction of hydrated K+. The superior electrochemical properties make them promising candidates as micropower sources to complement other energy conversion devices such as commercial solar cells.
Results
Preparation and structural characterizations
Our fabrication strategy of NP Au/ac-KxV2O5 microelectrodes is to electrodeposit the hydrated amorphous KxV2O5·nH2O (a-KxV2O5) on one polarity of interdigital-patterned NP Au current microcollectors, followed by an annealing procedure that triggers the amorphous/crystalline dual-phase nanostructuring of the constituent a-KxV2O5 via removing some crystal water sandwiched between V2O5 bilayers. Hereinto, the ac-KxV2O5 not only creates new ion diffusion pathways and accommodation sites but keeps the large interface spacing of crystalline V2O5 bilayers (∼10.8 Å) by making use of amorphous K0.25V2O5·nH2O as molecular pillars. This unique nanoarchitecture is expected to substantially facilitate the intercalation of guest hydrated K+ cations in the ac-KxV2O5 (Fig. 1a), in sharp contrast with the K+-free ac-V2O5 that undergoes atrocious volume change and encounters sluggish diffusion kinetics due to the narrow interlayer spacing (Fig. 1b)38,40,41,43. Figure 1c illustrates a schematic of on-chip AR-PIMB full cells, which are monolithically constructed on glassy substrates by further integrating the c-KxMnO2 cathode on the other polarity of interdigital-patterned NP Au current microcollectors (NP Au/c-KxMnO2), with aqueous electrolyte of 0.5 M K2SO4. Therein, the current microcollectors built of 60 NP Au interdigitated microelectrodes (30 electrodes per polarity) are produced by chemically dealloying Ag75Au25 (at%) alloy precursor patterns with gaps of ∼50 μm in HNO3 solution (Fig. 1d)46. Each NP Au microelectrode has a 3D and bicontinuous nanoporous structure consisting of quasi-periodic Au ligaments and nanopore channels with a characteristic length of ∼70 nm (Supplementary Fig. 1)46. Representative cross-sectional scanning electron microscope (SEM) images of AR-PIMB microelectrodes, i.e. the NP Au/ac-KxV2O5 anode (Fig. 1e) and the NP Au/c-KxMnO2 cathode (Fig. 1f), demonstrate that both the electroactive materials are uniformly grown onto ∼750-nm-thick nanoporous skeleton along Au ligaments.
The crystallographic structures of the constituent ac-KxV2O5 are controlled by annealing treatment of the as-electrodeposited a-KxV2O5 precursors, in which the hydrated K+ cations with various components (x = 0, 0.1, 0.2, and 0.25) are introduced by tuning K+ concentrations in the electrolytes (Supplementary Fig. 2, Supplementary Table 1). Along thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) behaviors (Supplementary Fig. 3), the NP Au/a-KxV2O5 microelectrodes are annealed at 25, 200, and 300 °C for 12 h, respectively, wherein a crystallization phenomenon occurs with successively removing crystal water and structure water. As shown in X-ray diffraction (XRD) patterns for the representative a-KxV2O5 (x = 0.25) annealed at 200 °C (Fig. 2a), there appear characteristic diffraction peaks corresponding to (101), (110), and (301) planes of the layer-structured o-V2O5 (JCPDS 41–1426)40,44,47, apart from the bump one at 2θ = 8.16° due to the (100) plane of the layered a-KxV2O5 (x = 0.25)37. This implies the presence of amorphous/crystalline dual-phase nanostructure in the ac-KxV2O5 with a interlayer spacing of ∼10.8 Å, the value that is almost the same as that of the a-KxV2O5 (x = 0.25) (Table 1). Typical high-resolution transmission electron microscope (HRTEM) image (Fig. 2c) with evident crystalline and amorphous fast Fourier transform (FFT) patterns (Fig. 2d, e) compellingly evidences the unique dual-phase nanostructure, in which the amorphous nanodomains are embedded in the crystalline o-V2O5 matrix. Meanwhile, the ac-KxV2O5 displays the same characteristic Raman bands as the a-KxV2O5 with the fingerprints of layer-type structure: the skeleton bent vibration at 163 cm−1 and the stretching vibration of vanadyl V = O at 1015 cm−1, attesting that it keeps the layered structure (Supplementary Fig. 4)48,49. When further increasing the annealing temperature to 300 °C, the a-KxV2O5 is completely transformed into a crystalline mixture composed of the o-V2O5 and the monoclinic K0.25V2O5 (m-K0.25V2O5). As demonstrated by XRD patterns for the crystalline KxV2O5 (c-KxV2O5), the additional diffraction peaks are ascribed to the (100), (002), (004), and (300) planes of the m-K0.25V2O5 (JCPDS 39–0889) (Fig. 2a). Supplementary Figure 4c schematically illustrates the atomic structure of the m-K0.25V2O5, where the [V4O12]n sheets consisting of V(1)O6 and V(2)O6 octahedra zigzag chains are linked by oxygen atoms to form 2D layered structure along the (001) plane, with K+ cations intercalating between the layers. The [V4O12]n layers are further connected by V(3)O5 and edge-sharing oxygen atoms to form a 3D tunnel structure50. Figure 2f shows the typical HRTEM image of the c-KxV2O5, where the interplanar distances of 0.23 and 0.21 nm correspond to the lattice planes of the m-K0.25V2O5(400) and the o-V2O5(002) (Fig. 2g), respectively. In view that the layered o-V2O5 is the primary phase in the c-KxV2O5 (Fig. 2a), the interlayer spacing is evaluated to be ∼4.42 Å according to the (001) diffraction peak position of the o-V2O5 (Table 1)38,40,44. In the structure evolution of the constituent KxV2O5 (x = 0.25), X-ray photoelectron spectroscopy (XPS) analysis of oxygen-containing species justifies the change of water component sandwiched between the V2O5 bilayers. As shown in Fig. 2b for high-resolution O 1s XPS spectra, there are three different oxygen species, i.e., the O2− in the V2O5 lattice, the OH−, and the H2O, to correspond to the peaks at the binding energies of 529.80, 530.90, and 533.01 eV51. Compared with that in the pristine a-KxV2O5 (left plot in Fig. 2b), the O 1s peak of H2O gradually attenuates in the ac-KxV2O5 (middle plot of Fig. 2b), and then disappears in the c-KxV2O5 (right plot of Fig. 2b) due to the loss of crystal water and structure water, respectively. Similar crystalline phenomenon also occurs in the K+-free a-V2O5 to generate the ac-V2O5, but with a interlayer spacing directly decreasing to 4.36 Å as a consequence of squeezing out the crystal water at 200 °C (Table 1, Supplementary Figs. 5, 6)38,40,44. This observation is in sharp contrast with the ac-KxV2O5, demonstrating the significant role of the amorphous K0.25V2O5·nH2O as molecular pillars in maintaining large interlayer spacing. Owing to the decrease of the hydrated K+ pillars, the interlayer spacing of ac-KxV2O5 decreases with the K+ concentration (Table 1, Supplementary Fig. 7).
Electrochemical characterizations
The electrochemical measurements of NP Au/KxV2O5 microelectrodes are performed in 0.5 M K2SO4 aqueous electrolyte on the basis of a three-electrode configuration with a Pt foil as the counter electrode and an Ag/AgCl electrode as the reference electrode. Figure 3a shows typical cyclic voltammograms (CVs) of NP Au/KxV2O5 (x = 0.25) microelectrodes within a voltage window of −0.8 to 0 V (versus Ag/AgCl) at a scan rate of 50 mV s−1. Relative to NP Au/a-KxV2O5 and NP Au/c-KxV2O5, the NP Au/ac-KxV2O5 exhibits remarkably enhanced current density because of the unique dual-phase nanostructure of the constituent ac-KxV2O5, which offers more room to accommodate guest hydrated K+ cations and facilitate their solid-state diffusion kinetics in the pillar supported interlayer space. Associated with the nanoporous Au current microcollectors that enables the constituent ac-KxV2O5 to be sandwiched between highly conductive ion and electron transport pathways, the CV curves at various scan rates from 5 to 1000 mV s−1 retain a quasi-rectangular shape, indicating the exceptional high-rate capability of NP Au/ac-KxV2O5 (Supplementary Fig. 8a, b). Although both NP Au/a-KxV2O5 and NP Au/c-KxV2O5 microelectrodes also benefit from such microelectrode architecture with fast electron and ion transports, they encounter rate-limited electrochemical energy-storage behaviors due to the poor accessibility and diffusion of hydrated K+ cations in the constituent electroactive materials, i.e., the a-KxV2O5, in which too much crystal water fills in large interlayer spacing, and the c-KxV2O5, of which the interlayer spacing is too narrow (Supplementary Fig. 8c, d). As a result, they exhibit much lower volumetric capacities than the NP Au/ac-KxV2O5 at various scan rates (Fig. 3b). Therein, the gravimetric capacity of the constituent ac-KxV2O5 reaches 382 mAh g−1 at 5 mV s−1 and retains 81 mAh g−1 at 1000 mV s−1, outperforming the constituent a-KxV2O5 and c-KxV2O5 (Supplementary Fig. 9a), as well as some of the best V2O5-based electrode materials in a full rate range reported previously for aqueous energy storage (Supplementary Fig. 9b). Electrochemical impedance spectroscopy (EIS) analysis in a frequency ranging from 100 kHz to 10 mHz demonstrates that the outstanding energy storage/delivery behavior of the constituent ac-KxV2O5 results from the enhanced intercalation kinetics of hydrated K+ cations in the dual-phase nanostructure. In the Nyquist plot, the EIS spectrum displays a quasi-semicircle with a ultrasmall diameter in the high- and middle-frequency ranges, followed by inclined lines in the low-frequency range (Supplementary Fig. 10a). At very high frequencies, the intercept at the real part represents the ohmic resistance (RI) of the electrolyte and the intrinsic resistance of microelectrode; the semicircular behavior in the middle-frequency range corresponds to the charge transfer resistance (RCT) and the double-layer capacitance (CF); the slope of the inclined line at the low frequencies is the Warburg resistance (Zw), which is a result of the frequency dependence of ion diffusion/transport inside the electrode. Using the complex nonlinear least-squares fitting method (Supplementary Fig. 10b), the NP Au/ac-KxV2O5 is revealed to exhibit the lowest equivalent series resistances (RI = 5.53 Ω and RCT = 0.28 Ω) (Supplementary Fig. 10c) and the highest Zw value (3358 S s1/2) (Supplementary Fig. 10d), reflecting the superior ion accessibility/diffusion and charge transfer in the dual-phase nanostructure during the electrochemical energy storage. The distinguished electrochemical behavior of the NP Au/ac-KxV2O5 microelectrode is further elucidated by charge/discharge kinetics analysis with an assumption that the current density (i) obeys a power-law relationship with the scan rate (v)52,53, namely i = avb, where a is an adjustable parameter, the b value of 0.5 or 1 represents a diffusion- or surface-controlled process, respectively. In the ln(i)−ln(v) plots (Supplementary Fig. 8e), the b value of the NP Au/ac-KxV2O5 is determined to be 0.86 due to enhanced insertion/extraction kinetics of the hydrated K+ cations, in contrast with those of the NP Au/a-KxV2O5 (0.60) and NP Au/c-KxV2O5 (0.64) with evident limitations of poor accessibility and slow diffusion.
Figure 3c and Supplementary Fig. 11a–d compare the CV curves of NP Au/ac-KxV2O5 microelectrodes, of which the constituent ac-KxV2O5 has K+ components changed from 0 to 0.25, at various scan rates. Owing to the maintenance of amorphous nanodomains of K0.25V2O5·nH2O in the constituent ac-KxV2O5, the NP Au/ac-KxV2O5 microelectrodes exhibit evidently improved current densities compared with the one with the constituent K+-free ac-V2O5, i.e., NP Au/ac-V2O5. Furthermore, the current density of NP Au/ac-KxV2O5 microelectrode increases with the increasing x value, which enlists the NP Au/ac-KxV2O5 with x = 0.25 to achieve a volumetric capacity of as high as ~715 mAh cm−3 at 5 mV s−1 (Fig. 3b), about threefold the value of NP Au/ac-V2O5 (~242 mAh cm−3) (Supplementary Fig. 11e, f). Even when increasing the scan rate to 1000 mV s−1, it still retains the capacity of 153 mAh cm−3, which is more than six times higher than the NP Au/ac-V2O5 (Supplementary Fig. 11e). These facts demonstrate the important roles of amorphous K0.25V2O5·nH2O nanodomains in improving energy-storage behaviors of the ac-KxV2O5, i.e., serving as molecular pillars to support large interlayer spacing for facilitating the accessibility and diffusion of guest hydrated K+ cations29,30, and acting as dopants to ameliorate the electronic conductivity of V2O5 bilayers for boosting electron transfer54,55. This is further demonstrated by their distinct EIS spectra in the Nyquist plots (Fig. 3d). As shown in Supplementary Fig. 12a, all the NP Au/ac-KxV2O5 (x = 0.10, 0.20, and 0.25) microelectrodes have much lower intrinsic electrode resistances (RI = ∼5.5–5.7 Ω) and charge transfer resistances (RCT = ∼0.28–0.61 Ω) than the NP Au/ac-V2O5 (RI = ~19.9 Ω and RCT = ~0.94 Ω), despite slight variations as a function of K+ component. While for the Warburg slope reflecting the ion diffusion kinetics (Supplementary Fig. 12b), it increases with the component of the hydrated K+ pillars and reaches the highest value for the NP Au/ac-KxV2O5 (x = 0.25).
Electrochemical performance of microdevices
In view of the outstanding electrochemical properties of NP Au/ac-KxV2O5 (x = 0.25) microelectrodes, they are used as anodes to pair with the NP Au/c-KxMnO2 cathodes (Supplementary Fig. 13) to build full microcells of on-chip V-Mn AR-PIMBs when integrating the c-KxMnO2 on the other polarity of interdigitated NP Au current microcollectors (Fig. 1c–f). By virtue of the potential difference between the NP Au/ac-KxV2O5 anode (−0.8 to 0 V) and the NP Au/c-KxMnO2 cathode (0–0.8 V) (Fig. 4a), the working voltage window of full microcells is extended to 1.6 V in the aqueous electrolyte of 0.5 M K2SO4. Figure 4b shows CV curves of the V-Mn AR-PIMBs at various scan rates corresponding to a full charge or discharge time from ~1.6 s to ~5.3 min, during which they are able to achieve a stack capacity of as high as ~64 mAh cm−3 based on the total volume of the full microcells. About half of the stack capacity (31 mAh cm−3) can be retained at exceptionally high discharge rates of 1000 mV s−1 (namely, full discharge in less than 2 s) (Fig. 4c). This exceptional rate performance enlists the V-Mn AR-PIMBs to outperform some of the best rechargeable aqueous metal-ion batteries reported previously: such as aqueous K+-ion batteries with carbon-encapsulated Fe3O4 nanorod array anode and carbon nanotube film cathode in 3 M KOH electrolyte (Fe–C PIBs)56, Li+-ion batteries with Bi2O3 anode, and LiMn2O4 cathode in a mixed electrolyte of Li2SO4 and LiCl (Bi–Mn LIBs)57, as well as symmetric Na+-ion batteries of biphase cobalt–manganese oxide nanosheets in 0.1 M Na2SO4 (CoMn–CoMn SIBs)21. Meanwhile, the V-Mn AR-PIMBs displays very low self-discharge, with less than 3.6 mV h−1, much better than LIBs assembled with Mo6S8 anode and LiFePO4 cathode (Mo-Fe LIBs) in Li-TFSI: H2O = 1 (21.1 mV h−1), Bi–Mn LIBs (58.9 mV h−1)58, and Zn2+-ion batteries with Zn anode and polyaniline film cathode (Zn–PANI ZIBs) in 1 M ZnCl2 (12.7 mV h−1) (Fig. 4d). Figure 4e shows that the cycling performance of the V-Mn AR-PIMB, which retains 80% of its initial capacity after 10,000 CV cycles at a scan rate of 500 mV s−1 (inset of Fig. 4e), demonstrates the impressive long-term stability in the voltage window between 0 and 1.6 V.
In the Ragone plot, Fig. 4f compares the stack-volumetric power and energy densities of V-Mn AR-PIMB with the values of commercially available devices including 4 V/500 µAh Li thin-film battery and 2.75 V/44 mF activated carbon supercapacitors9,14. Our microbattery has a volumetric energy density of ~103 mWh cm−3 based on the whole devices volume, which is 14-fold higher than 4 V/500 µAh Li thin-film battery, when delivering at the electrical power (1.2 W cm−3) compared to 2.75 V/44 mF activated carbon supercapacitors. As a result of monolithic integration of on-chip V-Mn AR-PIMB constructed on 3D bicontinuous nanoporous Au current microcollectors, which minimizes the internal resistance and facilitates rapid ion transport, the electrical power of V-Mn AR-PIMB can reach as high as ~600 W cm−3 with the energy density of ~27 mWh cm−3, much higher than microsupercapacitors based on onion-like carbon9. To our knowledge, the volumetric energy and power densities of V-Mn AR-PIMBs is the highest value among recently reported aqueous alkaline-metal-ion batteries on the basis of Li+20, Na+26, K+56, and Zn2+59 to date (Fig. 4f).
To meet specific micropower needs for portable or wearable electronics, all-solid-state flexible V-Mn AR-PIMBs are further developed by using a gel electrolyte of polyvinyl alcohol (PVA)/KCl and shifting on polymethyl methacrylate (PMMA) substrates (Fig. 5a). Because of the outstanding mechanical flexibility (inset of Fig. 5b), the all-solid-state microbatteries achieve almost the same capacity when bended from 0° to 90° (Fig. 5b). Furthermore, they can be connected in series to increase the working voltage and in parallel to store more energy, showing potential applications as stand-alone micropower sources or intermediate energy-storage components in electronic and optoelectronic microdevices. As demonstrated by a self-powered system that is constructed with 2-V thin-film solar cells to harvest energy from renewable and sustainable sunlight (Supplementary Fig. 14a), two V-Mn AR-PIMBs in series are charged to store energy and then discharged to power LED light when sunlight is available and unavailable (Fig. 5c). Figure 5d displays their typical voltage–time profile during the processes of charge and discharge in a working voltage window of 0–3.2 V. When solar cells are irradiated by sunlight, the voltage of the two-series V-Mn AR-PIMBs increases to 3.2 V in 136 s, meaning that the microbatteries can be charged successfully. While sunlight is unavailable, the V-Mn AR-PIMBs are discharged for 100 s at 2.64 A cm−3, powering the LED light (Supplementary Fig. 14b).
Discussion
In summary, we have demonstrated representative layered TMOs, KxV2O5, with an amorphous/crystalline dual-phase nanostructure, as promising anode materials of AR-PIMB when they are integrated on 3D bicontinuous nanoporous metal current microcollectors. Dual-phase nanostructuring of the layered ac-KxV2O5 is to remove some crystal water and use the amorphous K0.25V2O5·nH2O as molecular pillars to support the large interlayer distance, which creates additional room in interlayer space to accommodate guest hydrated K+ cations with significantly enhanced accessibility/diffusion kinetics. Associated with the unique architecture of 3D bicontinuous nanoporous metal-based current microcollectors, which simultaneously facilitate electron and ion transports in the whole microelectrodes, the NP Au/ac-KxV2O5 exhibits exceptionally energy storage with volumetric capacity of as high as ~715 mAh cm−3, and high rate capability. The outstanding electrochemical properties enlist AR-PIMB, which are constructed by integrating the ac-KxV2O5 anode and the c-KxMnO2 cathode on interdigitated 3D nanoporous Au current microcollectors, to really realize energy storage with lithium-ion microbattery-like capacity and supercapacitor-like rate performance and long-term cycling stability. Their maximum energy and power densities reach ~103 mWh cm−3 and ~ 600 W cm−3, outperforming not only commercially available energy-storage devices, such as 4 V/500 µAh Li thin-film battery and 2.75 V/44 mF activated carbon supercapacitors, but also previously reported aqueous alkaline ion batteries based on Li+, Na+, and K+, in addition to Zn2+. The superior performance makes them promising candidates as next-generation micropower sources for satisfying the demand of high-energy and -power densities in miniaturized portable electronics and MEMS.
Methods
Fabrication of aqueous potassium ion microbatteries
Microbattery devices were constructed by electrodepositing vanadium oxides and manganese oxides as anode and cathode, respectively, on interdigital-patterned Au current microcollectors with a 3D bicontinuous nanoporous architecture. Pure Cr (~50-nm-thick), Au (~100-nm-thick) and Ag75Au25 (at %) alloy (~750-nm-thick) films were consecutively sputtered on micropatterned molds consisting of 30 pairs of interdigital channels with the width of 50 μm and the gap of 100 μm, which were firstly fabricated on glass substrates by a general lithography technology. After stripping the micropatterned mold in 5 wt% NaOH, the metallic patterns were annealed in Ar air at 500 °C for 2 h and then chemically dealloyed in concentrated HNO3 for 15 min. Electrodeposition of electroactive TMOs on the as-prepared interdigital nanoporous Au patterns were carried out on a classic three-electrode setup (Iviumstat electrochemical analyser; Ivium Technology), in which Pt foil and Ag/AgCl electrode were employed as the counter electrode and the reference electrode, respectively. For the anodes, potassium vanadium oxide (KxV2O5·nH2O) was electrodeposited by a potentiodynamic method in a pH = 1.8 electrolyte containing 100 mM VOSO4, 30 mL pure water and 70 mL ethanol, as well as K2SO4 with various concentrations from 0 to 30 mM, followed by annealing at 25, 200, and 300 °C under ambient conditions for 12 h. Based on the total transfer charge in the electrodepositing process, the loading density of KxV2O5·nH2O is calculated to be 1.88 g cm−3. While for the cathode, the cryptomelane KxMnO2·nH2O was incorporated into the nanoporous Au microelectrodes by a pulse electrodeposition technology in 0.1 M KMnO4 neutral electrolyte. The loading mass of these TMOs was controlled by the transferred charges during the electrodeposition processes based on an assumption of 100% efficiency.
To develop all-solid-state flexible potassium ion microbatteries, PMMA film was deposited on the as-prepared nanoporous Au current microcollectors by dispersing 2 mL PMMA solution (4 wt% in ethyl lactate) and then baking on a hotplate at 80 °C for 30 min. After etching the Cr layer in 0.5 M (NH4)2Ce(NO3)6 solution, the PMMA supported nanoporous gold micropatterns was exfoliated and incorporated with the ac-KxV2O5 anode and the c-KxMnO2 cathode by the same procedures as that in the fabrication of rechargeable aqueous potassium ion microbatteries. Using PVA/KCl gel electrolyte, all-solid-state flexible potassium ion microbatteries are fabricated and sealed by PDMS for electrochemical test.
Microstructural and chemical characterizations
The microstructure and chemical composition of the anodic and cathodic electrodes in the microbatteries were characterized using a field-emission scanning electron microscope (JEOL JSM-6700F, 15 keV) equipped with an X-ray energy-dispersive spectroscopy and a field-emission transmission electron microscope (JEOL JEM-2100F, 200 keV). XRD measurements were carried out on a D/max2500pc diffractometer using Cu Kα radiation. XPS was performed on an ESCAlab220i-XL electron spectrometer from VG Scientific using Al Kα radiation. TGA and DSC were measured on a DSC 7 analyzer at the ramping rate of 10 °C min−1 in Ar air. Raman spectra were collected on a micro-Raman spectrometer (Renishaw) with a laser wavelength of 532 nm at 1 mW.
Electrochemical measurements
Electrochemical properties of single anodic and cathodic electrodes were characterized in 0.5 M K2SO4 aqueous electrolyte on a classic three-electrode setup with Pt foil as the counter electrode and Ag/AgCl as the reference electrode. Electrochemical behaviors of battery microdevices were measured by a two-electrode setup in 0.5 M K2SO4 aqueous electrolyte. Cycling stability test of potassium ion microbatteries was performed in a voltage window from 0 to 1.6 V at a scan rate of 500 mV s−1 for over 10000 cycles. Self-discharge measurements were carried out by charging aqueous potassium ion microbattery to 1.6 V at 110 μA, followed by open-circuit potential self-discharging for 100 h.
Data availability
All relevant data are available from the corresponding authors upon request.
References
Wang, Z. L. Self-power nanosensors and nanosystems. Adv. Mater. 24, 280–285 (2012).
Sun, H., Zhang, Y., Zhang, J., Sun, X. M. & Peng, H. S. Energy harvesting and storage in 1D devices. Nat. Rev. Mater. 2, 17023 (2017).
Oudenhoven, J. F. M., Baggetto, L. & Notten, P. H. L. All-solid-state lithium-ion microbatteries: a review of various three-dimensional concepts. Adv. Energy Mater. 1, 10–33 (2011).
Pikul, J. H., Zhang, H. G., Cho, J., Braun, P. V. & King, W. P. High-power lithium ion microbatteries from interdigitated three-dimensional bicontinuous nanoporous electrodes. Nat. Commun. 4, 1732 (2013).
Sun, K. et al. 3D printing of interdigitated Li-ion microbattery architectures. Adv. Mater. 25, 4539–4543 (2013).
Ning, H. et al. Holographic patterning of high-performance on-chip 3D lithium-ion microbatteries. Proc. Natl. Acad. Sci. USA 112, 6573–6578 (2015).
Hur, J. I., Smith, L. C. & Dunn, B. High areal energy density 3D lithium-ion microbatteries. Joule 2, 1187–1201 (2018).
Chmiola, J., Largeot, C., Taberna, P. L., Simon, P. & Gogotsi, Y. Monolithic carbide-derived carbon films for micro-supercapacitors. Science 328, 480–483 (2010).
Pech, D. et al. Ultrahigh-power micrometer-sized supercapacitors based on onion-like carbon. Nat. Nanotechnol. 5, 651–654 (2010).
Gao, W. et al. Direct laser writing of micro-supercapacitors based hydrated graphite oxide films. Nat. Nanotechnol. 6, 496–500 (2011).
Kyeremateng, N. A., Brousse, T. & Pech, D. Microsupercapacitors as miniaturized energy-storage components for on-chip electronics. Nat. Nanotechnol. 12, 7–15 (2017).
Peng, Y. Y. et al. All-MXene (2D titanium carbide) solid-state microsupercapacitors for on-chip energy storage. Energy Environ. Sci. 9, 2847–2854 (2016).
Lang, X. Y., Hirata, A., Fujita, T. & Chen, M. W. Nanoporous metal/oxide hybrid electrodes for electrochemical supercapacitors. Nat. Nanotechnol. 6, 232–236 (2011).
Yu., D. S. et al. Scalable synthesis of hierarchically structured carbon nanotube-graphene fibers for capacitive energy storage. Nat. Nanotechnol. 9, 555–562 (2014).
Huang, P. et al. On-chip and freestanding elastic carbon films for micro-supercapacitors. Science 351, 691–695 (2016).
Xia, Y. et al. Thickness-independent capacitance of vertically aligned liquid-crystalline MXenes. Nature 557, 409–412 (2018).
Liu, Y., Zhao, H. P. & Lei, Y. Advances on three-dimensional electrodes for microsupercapacitors: a mini-review. InfoMat 1, 74–84 (2019).
Li, W., Dahn, J. R. & Wainwright, D. S. Rechargeable lithium batteries with aqueous electrolytes. Science 264, 1115–1118 (1994).
Kim, H. et al. Aqueous rechargeable Li and Na ion batteries. Chem. Rev. 114, 11788–11827 (2014).
Dong, X., Chen, L., Su, X., Wang, Y. & Xia, Y. Flexible aqueous lithium-ion battery with high safety and large volumetric energy density. Angew. Chem. Int. Ed. 55, 7474–7477 (2016).
Shan, X. Q. et al. Biphase cobalt–manganese oxide with high capacity and rate performance for aqueous sodium-ion electrochemical energy storage. Adv. Funct. Mater. 28, 1703266 (2018).
Guo, Z. W. et al. Multi-functional flexible aqueous sodium-ion batteries with high safety. Chem 3, 348–362 (2017).
Xie., F., Zhang, L., Su, D., Jaroniec, M. & Qiao, S. Z. Na2Ti3O7@N-doped carbon hollow spheres for sodium-ion batteries with excellent rate performance. Adv. Mater. 29, 1700989 (2017).
Zhang, B. W. et al. Long-life room-temperature sodium-sulfur batteries by virtue of transition-metal-nanocluster-sulfur interactions. Angew. Chem. Int. Ed. 58, 1484–1488 (2019).
Charles, D. S. et al. Structural water engaged disordered vanadium oxide nanosheets for high capacity aqueous potassium-ion storage. Nat. Commun. 8, 15520 (2017).
Wessells, C. D., Peddada, S. V., McDowell, M. T., Huggins, R. A. & Cui, Y. The effect of insertion species on nanostructured open framework hexacyanoferrate battery electrodes. J. Electrochem. Soc. 159, A98–A103 (2012).
Su, D., McDonagh, A., Qiao, S. Z. & Wang, G. High-capacity aqueous potassium-ion batteries for large-scale energy storage. Adv. Mater. 29, 1604007 (2017).
Zeng, C. et al. Ultrathin titanate nanosheets/graphene films derived from confined transformation for excellent Na/K ion storage. Angew. Chem. Int. Ed. 57, 8540–8544 (2018).
Wang, F. et al. High-voltage aqueous magnesium ion batteries. ACS Cent. Sci. 3, 1121–1128 (2017).
Pan, H. et al. Reversible aqueous zinc/manganese oxide energy storage from conversion reactions. Nat. Energy 1, 16039 (2016).
Kundu, D., Adams, B. D., Duffort, V., Vajargah, S. H. & Nazar, L. F. A high-capacity and long-life aqueous rechargeable zinc battery using a metal oxide intercalation cathode. Nat. Energy 1, 16119 (2016).
Smith, D. W. Ionic hydration enthalpies. J. Chem. Edu. 54, 540–542 (1977).
Nightingale, E. R. Phenomenological theory of ion solvation: effective radii of hydrated ions. J. Phys. Chem. 63, 1381–1387 (1959).
Esfandiar, A. et al. Size effect in ion transport through Angstrom-scale slits. Science 358, 511–513 (2017).
Wessells, C. D., Peddada, S. V., Huggins, R. A. & Cui, Y. Nickel hexacyanoferrate nanoparticles electrodes for aqueous sodium and potassium ion batteries. Nano Lett. 11, 5421–5425 (2011).
Ren, W., Chen, X. & Zhao, C. Ultrafast aqueous potassium-ion batteries cathode for stable intermittent grid-scale energy storage. Adv. Energy Mater. 8, 1801413 (2018).
Petkov, V. et al. Structure of V2O5 nH2O xerogel solved by the atomic pair distribution function technique. J. Am. Chem. Soc. 124, 10157–10162 (2002).
Augustyn, V. & Gogotsi, Y. 2D materials with nanoconfined fluids for electrochemical energy storage. Joule 1, 443–452 (2017).
Clites, M. & Pomerantseva, E. Bilayered vanadium oxides by chemical pre-intercalation of alkaline and alkali-earth ions as battery electrodes. Energy Storage Mater. 11, 30–37 (2018).
Wang, J., Curtis, C. J., Schulz, D. L. & Zhang, J.-G. Influences of treatment temperature and water content on capacity and rechargeability of V2O5 xerogel films. J. Electrochem. Soc. 151, A1–A7 (2004).
Liu, Q. et al. Graphene-modified nanostructured vanadium pentoxide hybrids with extraordinary electrochemical performance for Li-ion batteries. Nat. Commun. 6, 6127 (2015).
Coustier, F., Hill, J., Owens, B. B., Passerini, S. & Smyrl, W. H. Doped vanadium oxides as host materials for lithium intercalation. J. Electrochem. Soc. 146, 1355–1360 (1999).
Levi, E., Gofer, Y. & Aurbach, D. On the way to rechargeable Mg batteries: the challenge of new cathode materials. Chem. Mater. 22, 860–868 (2010).
Soga, N. & Senna, M. Change in the dehydration and crystallization processes of V2O5 xerogel due to mechanical pretreatment. J. Solid State Chem. 107, 159–165 (1993).
He, P. et al. Sodium ion stabilized vanadium oxide nanowire cathode for high-performance zinc-ion batteries. Adv. Energy Mater. 8, 1702463 (2018).
Erlebacher, J., Aziz, M. J., Karma, A., Dimitrov, N. & Sieradzki, K. Evolution of nanoporosity in dealloying. Nature 410, 450–453 (2001).
Yue, Y. & Liang, H. Micro- and nano-structured vanadium pentoxide (V2O5) for electrodes of lithium-ion batteries. Adv. Energy Mater. 7, 1602545 (2017).
Baddour-Hajean, R., Raekelboom, E. & Pereira-Ramos, J. P. New structural characterization of the LixV2O5 system provided by Raman spectroscopy. Chem. Mater. 18, 3548–3556 (2006).
Su, D. & Wang, G. Single-crystalline bilayered V2O5 nanobelts for high-capacity sodium-ion batteries. ACS Nano 7, 11218–11226 (2013).
Baddour-Hadjean, R., Boudaoud, A., Bach, S., Emery, N. & Pereira-Ramos, J. P. A comparative insight of potassium vanadates as positive electrode materials for Li batteries: Influence of the long-range and local structure. Inorg. Chem. 53, 1764–1772 (2014).
Sathiya, M., Prakash, A. S., Ramesha, K., Tarascon, J. M. & Shukla, A. K. V2O5-anchored carbon nanotubes for enhanced electrochemical energy storage. J. Am. Chem. Soc. 133, 16291–16299 (2011).
Lindström, H. et al. Li+ ion insertion in TiO2 (anatase). 2. Voltmmetry on nanoporous films. J. Phys. Chem. B 101, 7717–7722 (1997).
Augustyn, V. et al. High-rate electrochemical energy storage though Li+ intercalation pseudocapacitance. Nat. Mater. 12, 518–522 (2013).
Yuan, Y. et al. The influence of large cations on the electrochemical properties of tunnel-structured metal oxides. Nat. Commun. 7, 13374 (2016).
Yao, X., Zhao, Y., Castro, F. A. & Ma, L. Rational design of preintercalated electrodes for rechargeable batteries. ACS Energy Lett. 4, 771–778 (2019).
Li, R. Z. et al. Carbon-stabilized high-capacity ferroferric oxide nanorod array for flexible solid-state alkaline battery–supercapacitor hybrid device with high environmental suitability. Adv. Funct. Mater. 25, 5384–5394 (2015).
Zuo, W. H. et al. Bismuth oxide: a versatile high-capacity electrode material for rechargeable aqueous metal-ion batteries. Energy Environ. Sci. 9, 2881–2891 (2016).
Mirmohseni, A. & Solhjo, R. Preparation and characterization of aqueous polyaniline battery using a modified polyaniline electrode. Eur. Polym. J. 39, 219–223 (2003).
Huang, Y. et al. Wearable, conductive yarn-based NiCo//Zn textile battery with high energy density and rate capability. ACS Nano 11, 8953–8961 (2017).
Acknowledgements
This work was supported by National Natural Science Foundation of China (Nos. 51871107, 51631004), Top-notch Young Talent Program of China (W02070051), Chang Jiang Scholar Program of China (Q2016064), the Program for JLU Science and Technology Innovative Research Team (JLUSTIRT, 2017TD-09), the Fundamental Research Funds for the Central Universities, and the Program for Innovative Research Team (in Science and Technology) in University of Jilin Province.
Author information
Authors and Affiliations
Contributions
X.-Y.L., Q.J. and Y.-Q.L. conceived and designed the experiments. Y.-Q.L., H.S., S.-B.W., Y.-T.Z., Z.W. and X.-Y.L. carried out the fabrication and analysis of materials and performed the electrochemical and microstructural characterizations. X.-Y.L., Q.J. and Y.-Q.L. wrote the paper, and all authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Peer review information Nature Communications thanks Wei Luo, Shizhang Qiao, and the other, anonymous, reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Li, YQ., Shi, H., Wang, SB. et al. Dual-phase nanostructuring of layered metal oxides for high-performance aqueous rechargeable potassium ion microbatteries. Nat Commun 10, 4292 (2019). https://doi.org/10.1038/s41467-019-12274-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-019-12274-7
This article is cited by
-
Insights into Nano- and Micro-Structured Scaffolds for Advanced Electrochemical Energy Storage
Nano-Micro Letters (2024)
-
Aluminum-copper alloy anode materials for high-energy aqueous aluminum batteries
Nature Communications (2022)
-
Interface Reversible Electric Field Regulated by Amphoteric Charged Protein-Based Coating Toward High-Rate and Robust Zn Anode
Nano-Micro Letters (2022)
-
Recent advances in anode materials for potassium-ion batteries: A review
Nano Research (2021)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.