Diatomite derived hierarchical hybrid anode for high performance all-solid-state lithium metal batteries


Lithium metal based anode with hierarchical structure to enable high rate capability, volume change accommodation, and dendritic suppression is highly desirable for all-solid-state lithium metal battery. However, the fabrication of hierarchical lithium metal based anode is challenging due to the volatility of lithium. Here, we report that natural diatomite can act as an excellent template for constructing hierarchical silicon-lithium based hybrid anode for high performance all-solid-state lithium metal battery. This hybrid anode exhibits stable lithium stripping/plating performance over 1000 h with average overpotential lower than 100 mV without any short circuit. Moreover, all-solid-state full cell using this lithium metal composite anode to couple with lithium iron phosphate cathode shows excellent cycling stability (0.04% capacity decay rate for 500 cycles at 0.5C) and high rate capability (65 mAh g−1 at 5C). The present natural diatomite derived hybrid anode could further promote the fabrication of high performance all-solid-state lithium batteries from sustainable natural resources.


Lithium (Li) metal anode is one of the most attractive anodes for next-generation rechargeable batteries, due to its lowest electrochemical potential (−3.04 V vs. standard hydrogen electrode) and highest theoretical specific capacity (3860 mAh  g−1)1,2,3. However, the application of Li metal anode in conventional liquid electrolyte-based batteries has been long-term hindered by safety issues caused by thermodynamic instability of Li metal and the flammability of organic liquid electrolyte. The heterogeneous and fragile solid electrolyte interphase (SEI) caused by the high reactivity between Li metal anode and liquid electrolyte raises up the growth of dendrite, resulting in the short circuit, thermal runaway, and eventually uncontrollable safety issues4,5,6,7,8,9. Although much effort has been made recently to reinforce as-formed SEI layer or build up an artificial SEI layer to stabilize Li metal anode to some extent, the flammable nature of liquid organic electrolyte still makes it almost unacceptable in Li metal-based batteries10,11.

Replacement of liquid electrolytes by uninflammable solid electrolytes (SEs) to build up all-solid-state Li metal batteries is in high demand for future high-energy density and safe energy-storage systems12,13,14,15. Generally, the SEs could be divided into inorganic solid electrolytes (ISEs) and solid polymer electrolytes (SPEs)11,12. Although ISEs usually exhibit high ionic conductivity at room temperature and good mechanical strength16,17,18,19, the performances of solid-state Li metal batteries based on ISEs are limited by poor rigid solid–solid contact, leading to great interfacial resistance and low interfacial compatibility between ISEs and Li metal anode20,21. The uneven current density distribution at the interface of Li metal and ISEs would further promote the dendrite growth along the grain boundaries of ISEs22,23. In contrast, the SPEs comprising a soft polymer matrix and a Li ion salt exhibit much better flexibility and wettability with Li metal anode than ISEs, endowing intimate interface contact and lower interfacial resistance24,25,26,27. However, the low Li ion conductivities of SPEs at crystalline states, in particular, polyethylene oxide-based solid polymer electrolytes (PEO-SPEs), require the operating temperature over glass-phase transition temperature25,28, with sacrificing the mechanical strength to suppress the growth of Li dendrites22,26,29.

Considering beyond the electrolytes, the aforementioned limitations of SEs in solid-state Li metal batteries are significantly originated from the limited active surface area and low volume accommodation capability of mostly used planar Li metal anodes. A hierarchically structured design in advanced Li metal anode to improve its rate capability, accommodate the volume change, and eliminate dendrite growth is highly demanded in solid-state Li metal batteries14,30,31,32,33,34,35. It can be expected that a suitable combination of hierarchically structured Li composite anode with PEO-SPE could have the following advantages: the intensively enhanced electrode–electrolyte contact for low interfacial resistance and therefore improving the rate capability; the hierarchical ionic conductive framework to enable homogeneously stripping/plating of Li and maintain the integrity of the whole electrode.

To realize the merits of a hierarchically structured Li composite anode with PEO-SPE, a unique hierarchical framework material has to reach the requirements of low cost, good rigidity, high affinity to Li, and enough pore spaces30,31,34 to accommodate sufficient Li inside. Nature is a master to produce various hierarchical materials and has offered us many inspirations for advanced battery electrode designs36,37,38. For instance, a pomegranate-inspired nanoscale design has been used to accommodate large volume change of silicon anode and achieve high areal capacity36. After screening various hierarchically structured materials from nature, we find that the diatomite is an ideal hierarchical framework material to meet the requirements for preparing hierarchical Li composite anode. First, naturally abundant diatomite is low cost and its unique hierarchical structure with extremely high porosity is attractive for Li accommodation39,40,41. Second, with a facile magnesium reduction treatment, the unique hierarchical structure of diatomite could be totally inherited into the as-obtained silicon framework42. Third, the highly lithiophilic property of hierarchical silicon framework facilitates the lithiation process to yield a rigid Li4.4Si framework to loading Li metal inside, forming a unique lithium silicide–Li hybrid anode39,43.

Herein, we report a stable, dendritic free, and hierarchically structured Li metal-based hybrid anode derived from natural diatomite to realize high-performance all-solid-state Li metal battery. The natural diatomite is first transformed into a hierarchical silicon framework via a magnesiothermic reduction process. As shown in Fig. 1a, the diatomite-derived silicon (DF-Si) powder is mixed with molten Li to yield hierarchical lithium silicide–Li hybrid fragments, which could be cold-pressed into a composite anode after the PEO-SPE coating decoration. In as-fabricated PEO-SPE-coated diatomite-derived lithium silicide–Li (PEO-DLSL) composite anode, Li is embedded in the hierarchical pores of the Li4.4Si framework and PEO coatings, resulting in a high electroactive contact area to homogenize the Li+ ion flux and enable the anode integrity without Li dendrite growth (Fig. 2b). In contrast, the limited electroactive area of a planar Li-foil anode cannot efficiently avoid the growth of Li dendrites, which would easily penetrate the soft PEO-SPE causing the short circuit.

Fig. 1

Schematic illustration of the PEO-DLSL anode fabrication process and Li stripping/plating behaviors in comparison with a planar Li anode. a The fabrication process of PEO-DLSL. The DF-Si powder was mixed with molten Li to form the DLSL fragments and the PEO-DLSL composite anode was fabricated by cold-pressing the DLSL fragments with PEO-SPE coatings. b, c Li stripping/plating behavior in all-solid-state Li metal batteries with PEO-DLSL anode and a planar Li-foil anode, respectively. The effective Li+ ion flux in PEO-DLSL anode was much more uniform than that in a planar Li foil, leading to a dendrite-free anode without the short circuit

Fig. 2

Morphology and surface area characterizations of pristine DF, DF-SiO, and DF-Si, respectively. ac SEM images of pristine DF (a scale bar = 5 μm), DF-SiO (b scale bar = 5 μm), and DF-Si (c scale bar = 5 μm), respectively. df TEM images of pristine DF (d scale bar = 1 μm), DF-SiO (e scale bar = 500 nm), and DF-Si (f scale bar = 500 nm), respectively. gi N2 adsorption/desorption curves of pristine DF (g), DF-SiO (h), and DF-Si (i), respectively. jl SXT images of DF (j scale bar = 2 μm), DF-SiO (k scale bar = 2 μm), and DF-Si (l scale bar = 2 μm), respectively


Diatomite-templated fabrication of a hierarchical silicon framework for lithiation

An individual diatomite has a Petri dish morphology with a fine hierarchical pore structure, which is confirmed by both the scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images (Fig. 2a, d). The bigger-sized pores (400–800 nm in diameter) are distributed in the central area, whereas the smaller-sized pores (100–200 nm in diameter) are uniformly distributed in the whole diatomite framework (DF). After a facile magnesiothermic reduction process, the main phase of the diatomite framework could be converted into SiO (denoted as DF-SiO) or Si (denoted as DF-Si) from initial SiO2 (JCPDS 46-1045), depending on the mass ratio of Mg powder to pristine diatomite. According to the powder X-ray diffraction (PXRD) analysis (Supplementary Fig. 1), the SiO phase (JCPDS 30-1127) could be obtained if the mass ratio of Mg to DF is 0.5:1. When the mass ratio increased to 1:1, the pure phase Si (JCPDS 27-1402) could be yielded. In addition, the PXRD peaks corresponding to the crystalline phase SiO2 in diatomite (asterisk) gradually disappeared with increasing the amount of Mg powder. As confirmed by the SEM and TEM images (Fig. 2b, c and e, f), the generated DF-SiO and DF-Si have a similar hierarchical structure as that of pristine diatomite, especially in which the pores are maintained very well. To further reveal a good hierarchical pore structure in as-obtained frameworks, we conducted nitrogen adsorption/desorption analysis to study the variation of the specific surface area and pore structures of pristine DF, DF-SiO, and DF-Si, respectively (Fig. 2g–i). The surface area of the DF-SiO and DF-Si analyzed by Brunauer–Emmett–Teller (BET) method was 199.6 m2 g−1 and 271.6 m2 g−1, respectively, higher than that of pristine DF (100.3 m2 g−1), indicating that the removing oxygen by magnesiothermic reduction process produced more void space in the framework. The three-dimensional (3D) structures of pristine DF, DF-SiO, and DF-Si were further characterized by the soft X-ray tomography (SXT) as well (Fig. 2j–l, Supplementary Movies 13), in which the translucent pink area is corresponding to the solid Si-based component, while the blue area could be ascribed to the hierarchical pores in the framework. It is evident that DF-Si behaves as a more porous structure with smaller sizes than that of pristine DF and DF-SiO, which will facilitate the lithiation process of as-obtained frameworks.

To evaluate the potentials of DF to fabricate a hierarchical hybrid anode via direct lithiation process, the aforementioned three products were mixed with molten Li with the same mass ratio of MDF/DF-SiO/DF-Si:MLi = 1:1.6 to proceed the lithiation of frameworks. Then the obtained lithiated powders were cold-pressed into pallets, as the electrodes and their Li-stripping performances were tested and compared (Supplementary Fig. 2, stripped to 1.0 V vs. Li+/Li). For the lithiated DF-Si anode (DF-Si–Li), a total specific capacity of ~1153 mAh g−1 could be extracted (based on the total electrode weight), in which the specific capacity of ~838 mAh g−1 below the potential of 0.2 V is attributed from the Li metal. In contrast, the extracted specific capacity of DF-SiO-Li and DF-Li electrode was ~1031 mAh g−1 and ~924 mAh g−1, with only ~399 mAh g−1 and ~265  mAh g−1 of capacity contributed from the stripping of Li metal rather than the delithiation from Li4.4Si or Li2O, respectively. This is because the DF-Si consumed a least amount of Li to achieve full lithiation without formation of Li2O, leaving a maximum amount of Li to serve as Li metal anode. Beyond that, the lithiation product of DF-Si is pure Li4.4Si instead of the Li4.4Si-Li2O composites formed in DF-SiO-Li and DF-Li framework, which further lowers the inner resistance of the as-formed hybrid anode. As a result, the interfacial resistance of DF-Si–Li is superior to DF-SiO-Li and DF-Li44,45. Therefore, it is evident that the full magnesiothermic reduction of diatomite into a silicon framework is required for a desirable hybrid anode framework fabrication.

Overstoichiometric lithiation of DF-Si to prepare a hybrid anode

To study the influence of the lithiation extent on DF-Si, a different amount of Li (0.2, 0.5,, and 0.8 g) was employed to react with the same mass (0.5 g) of DF-Si powder. The obtained products were denoted as DF-Si-Li0.2, DF-Si-Li0.5, and DF-Si-Li0.8, respectively. When the amount of Li was 0.2 g, the fractured fragments from the DF disk (Fig. 3a) could be observed due to the strain and volume expansion induced by the lithiation (Fig. 3b). When the amount of Li increased to 0.5 g, microparticles of lithiated DF were formed (Fig. 3c). By further increasing the amount of Li to 0.8 g, the dense microparticles were generated, which could be ascribed to the embedding of Li into the hierarchical Li4.4Si particles (Fig. 3d). The photograph of the products at the different extents of lithiation (Supplementary Fig. 3) also showed the overstoichiometric lithiation process. The color of products changed from brown (similar to that of DF-Si) to black (the color of Li4.4Si) and then to silvery gray (the mixed color of black Li4.4Si and glossy Li). To further reveal the peculiarity of a hierarchical structure of DF-Si for promoting the embedment of Li, we applied a “phase field” method46,47 (Supplementary Note 1 and Supplementary Table 1) to simulate the variation of Li concentration and stress evolution in the DF-Si framework during the lithiation process. As shown in Fig. 3e, the Li concentration in the DF-Si framework first increases at the edge of macropores and then spreads out to the whole framework, coinciding with the lithiation initiation from the macropore surface contacted with molten Li and the followed migration of the Li front toward the unlithiated silicon framework. This indicates that the hierarchical structure of DF-Si played a crucial role on the thoroughly gradual spreading of Li in the matrix. Also, the lithiation-induced expansion of the as-formed lithiated phase stretches the unlithiated silicon (Supplementary Fig. 4). As a consequence, the unlithiated part suffers from tensile stress, which promotes the propagation of cracks and leads to the fragmentation of lithiated DF-Si. Comparably, the lithiation simulation of silicon microflake without hierarchical pores showed a totally different Li concentration and stress evolution within the lithiation process. In the dense silicon microflake, the lithiation preferred to occur at the edge of silicon microflake and only slowly spread from the edge to the center area (Supplementary Fig. 5). Due to the absence of macropores, the stress amplitude in the dense silicon microflake is lower than that in the DF-Si framework. Besides the simulation, a control lithiation experiment was conducted on silicon microparticle powder to show the superior Li uptaking capability of DF-Si. As shown in Supplementary Fig. 6, after reaction with 0.8 g of Li, the silicon microparticle first became a lump of black mixture tightly adhered onto the bottom of a tantalum crucible after the lithiation, strongly contrasting to the silvery powder of as-formed DF-Si-Li0.8. To confirm the loading of Li in the hierarchical particles, the DF-Si-Li0.8 microparticles were treated by focused ion beam (FIB) etching (Supplementary Fig. 7), which showed the appearance of interconnected pores in the matrix of DF-Si-Li0.8, indicating the embedment of Li in the as-formed lithium silicide framework. The SXT image of an individual DF-Si-Li0.8 microparticle (Fig. 3f, Supplementary Movie 4) was rendered according to X-ray absorption differences of Li and Li4.4Si (Supplementary Fig. 8). We could also observe the embedment of Li (red area) in the interconnected pores of the Li4.4Si framework (translucent purple area), forming the hierarchically structured hybrid anode. This hybrid anode is highly desirable to endow the good Li distribution in a sub-microscale hierarchical framework, leading to more uniform Li+ flux and faster Li+ transfer rate of solid Li metal anode.

Fig. 3

Characterizations and simulations of DF-Si powder lithiated by different amounts of Li. ad SEM images of pristine DF-Si, DF-Si-Li0.2, DF-Si-Li0.5, and DF-Si-Li0.8, respectively (scale bar = 10 μm for Figure a, scale bar = 5 μm for Figure b, c, d). e The simulation of Li diffusion into the DF-Si framework during the lithiation process. The variation from the blue color to red color represents the increase of Li concentration and lithiation extent of DF-Si along with the lithiation process. f SXT image of the DF-Si-Li0.8 microparticle (scale bar = 1 μm). The image was rendered based on the difference of X-ray adsorption. The red color represents Li4.4Si, while blue color corresponds to Li. g PXRD patterns of DF-Si lithiated with different amounts of Li. With a higher Li/DF-Si mass ratio, the relative intensity of the metallic peak (red asterisk) became more significant. The blue triangle denotes the peak of sample pack, the blue cycles denote the peaks of Si, and the green squares denote the peaks of Li4.4Si. h Li- stripping voltage plateau curves of different DF-Si–Li anodes

The phase change of the lithiated DF-Si with using different amounts of Li was revealed by the PXRD (Fig. 3g). The main phase of DF-Si-Li0.2 could be still indexed as silicon (JCPDS No. 27-1402), demonstrating that only a little amount of DF-Si was lithiated at this low amount of Li. For DF-Si-Li0.5, the main phase could be ascribed to Li4.4Si (JCPDS No. 18-0747) but the metallic Li (asterisk, JCPDS 65-9346) also existed due to the accommodation of a hierarchical framework for Li. When the mass of Li further increased to 0.8 g, the relative intensity of metallic Li peaks became more significant, indicating that the overstoichiometric lithiation was conducted and the Li was accommodated in the matrix of Li4.4Si as confirmed by SXT (Fig. 3f). To demonstrate the essential role of the overstoichiometric amount of Li, we further tested the specific capacities that can be extracted from different lithiated DF-Si products. As shown in Fig. 3h, the DF-Si-Li0.8 anode showed a much lower charge overpotential and a higher specific capacity compared with the DF-Si-Li0.5 and DF-Si-Li0.2. In particular, the main specific capacity contribution of DF-Si-Li0.8 was from the metallic Li stripping (838 mAh/g, charge potential < 0.2 V), while the specific capacity of DF-Si-Li0.5 was all from the delithiation of Li4.4Si (332 mAh/g at the potential of 0.4~1.0 V). The charge curve of DF-Si-Li0.8 is very smooth, whereas DF-Si-Li0.5 is quite fluctuant due to the instability of Li4.4Si frameworks during the Li stripping. The DF-Si-Li0.2 electrode showed minimal specific capacity of only 6.4 mAh/g and the voltage raised very fast over 1.0 V. Therefore, the overstoichiometric Li is very crucial to achieve desired electrochemical behaviors of Li metal anode. In this case, the DF-Si-Li0.8 hybrid anode materials were used to fabricate all-solid-state Li metal composite anodes.

Fabrication and characterizations of PEO-DLSL composite anode

To fabricate the PEO-DLSL composite anode, a thin layer of PEO-SPE was first coated onto the surface of the DF-Si-Li0.8 microparticles by a solution mixing and drying process (see the “Methods” section). As shown in Fig. 4a, the surface of DF-Si-Li0.8 microparticles became smooth and no cracks could be observed, implying the uniform coating of PEO-SPE. After facile cold-pressing of as-synthesized powders, the obtained PEO-DLSL electrode shows silvery color on the surface (inset in Fig. 4b), and the SEM image of the electrode surface indicates its uniform and dense structure (Fig. 4b). The magnified cross-sectional SEM image at a stretched point (Supplementary Fig. 9a) clearly shows the silk-like structure of an elastic PEO-SPE to connect the stretched solid electrode. Furthermore, the energy-dispersive X-ray spectroscopy (EDX) mapping results (Supplementary Fig. 9b, c) show that the oxygen signal (blue) well overlaps with the PEO-SPE coating and the silicon signal (green) distributes throughout the solid electrode, implying the uniform PEO-SPE coating onto the whole 3D network of the DF-Si-Li0.8 matrix. In this composite anode, the elastic PEO-SPE could enhance the contact area between the hybrid anode and solid electrolyte. Further, PEO-SPE could construct a continuous Li+ ion transport channel throughout the entire electrode, thus shortening Li+ ion transportation pathway and homogenizing the Li+ ion flux in the solid composite electrode. It is also worth noting that the PEO-SPE exhibits a relatively high Li+ ion conductivity at the operating temperature (4.63 × 10−4  S cm−1 at 60 °C, Supplementary Fig. 10). With the assistance of PEO-SPE, Li+ ion diffusion and transportation capability in the PEO-SPE/Li–Si composite framework could be significantly improved. Therefore, the PEO-DLSL electrode could have a stable electrode dimensionality during the Li stripping/plating, endowed by both the rigid 3D Li+ ion-conductive framework of lithiated silicon and PEO-SPE coatings. To show the sturdiness of the as-constructed 3D electrode network at the solid state, the PEO-DLSL electrode in a half-cell was charged to 1.0 V to ensure fully tripping out of all Li. The obtained delithiated electrode still kept good rigid structural integrity, with only the color change from silvery to black, because of the formation of a porous framework, indicating the stability and interconnected nature of the PEO-DLSL framework (Supplementary Fig. 11a). In addition, hierarchical pores could be observed from the SEM image of the “black” area of the stripped electrode, where it was initially occupied by Li (Supplementary Fig. 11b).

Fig. 4

Morphological and structural characterizations of PEO-DLSL and PEO-Li-foil electrode at different states. a SEM image showing the DF-Si-Li0.8 microparticles after a thin layer of PEO-SPE coating (scale bar = 50 μm). b SEM image demonstrating the flat surface morphology of the PEO-DLSL electrode (scale bar = 20 μm). The inset is the photograph of the as-fabricated composite anode. ce Cross-sectional SEM images of pristine PEO-DLSL electrode (c), after 4 mAh cm−2 of Li stripping (d), and 4 mAh cm−2 of plating Li back (e). The current density was set at 0.5 mA cm−2 for all of the above characterizations (scale bar = 200 μm). fh The corresponding magnified SEM images of the electrode from c to e, showing the morphologies at the interface of the PEO-DLSL electrode and PEO-SPE (scale bar = 5 μm). ik, Cross-sectional SEM images showing the morphologies at the interfaces of Li foil and PEO-SPE (scale bar = 20 μm). The intimal surface of Li foil is smooth (i). After 4 mAh cm−2 of Li stripping out, a rough Li-foil surface could be observed (j). When 4 mAh cm−2 of Li was plated back, a layer of deposited Li (~17 μm) appeared at the interface with pores and cracks (k)

Furthermore, the ex situ SEM characterizations were carried out to show the thickness variation of the electrode and the interfacial stability between the electrode and PEO-SPE in one cycle of the Li stripping/plating. As shown in Fig. 4c–e, the thickness of the PEO-DLSL electrode was maintained around ~240 μm during the stripping out and plating back 4 mAh cm−2 of Li, indicating that the Li stripping and plating occurred inside the 3D framework of the composite electrode. The corresponding magnified SEM images (Fig. 4f–h) show the uniform electrode structure and dense interface between the electrode and PEO-SPE, further confirming the homogeneous Li stripping/plating in the network of the composite electrode. In contrast, for a planar Li-foil anode, after stripping out 4 mAh cm−2 of Li, the surface of Li foil at the electrode/electrolyte interface became from smooth (Fig. 4i) to uneven like hills (Fig. 4j). When 4 mAh cm−2 of Li was plated back, an independent layer of Li could be observed at the PEO-SPE/Li-foil interface. The average thickness of the deposited Li was about ~17 μm, which was in consistent with the amount of plated Li (Fig. 4k). Besides, the pores and cracks appeared at both interfaces of the deposited Li layer, indicating the reduced contact area and potential growth of dendrites. It is predictive that the contact issues of Li foil became more severe with repeat Li stripping/plating process due to the extensive volume change and uneven Li deposition behavior.

Electrochemical performance of the PEO-DLSL anode in comparison with the Li-foil anode

To demonstrate the good Li+ ion transfer property of the PEO-DLSL composite anode, the interfacial resistance of the symmetric cell was evaluated at first by electrochemical impedance spectroscopy (EIS). According to the EIS results in Supplementary Fig. 12, the interfacial resistance of the PEO-DLSL cell was only 124 Ω cm−2, while the value of Li-foil cell was 397 Ω cm−2, confirming the improved interfacial Li+ transportation induced by the 3D Li+ ion-conductive framework in the composite anode. As shown in Fig. 5a, the PEO-DLSL symmetric cell exhibited a smaller Li stripping/plating overpotential compared with the Li-foil cell at 60 °C. When the current density is 0.1 mA cm−2, the average overpotential for the PEO-DLSL cell was 18 mV, lower than that of Li-foil cell (38 mV, Fig. 5b). The difference became more significant when the cell operated at a higher current density. For example, when the current density was 0.5 mA cm−2, the average overpotential of PEO-DLSL was only 98 mV, while the value of Li foil was 276 mV (Fig. 5c). It was observed that the voltages slowly decreased to zero when the polarizations were switched at the current density higher than 0.2 mA cm−2. This could be attributed to the concentration polarization (CP) when cycled at high current density. Li+ ion transportation and diffusion rate at the electrode/electrolyte interface and in the electrolyte is order of magnitudes smaller than the electrochemical reaction rate. Therefore, the depolarization of CP required time to recover homogeneous Li+ ion concentration distribution and achieve a steady state, due to the unsatisfied Li+ ion conductivity in the solid-state cell, and thus the voltages slowly decreased to zero when the polarizations were switched off. Furthermore, the Li+ ion diffusion pathway in our 3D hierarchical PEO-DLSL electrode is much longer than that at the planar Li-PEO electrolyte interface. Hence, the slowly decreasing of voltage is more obvious for PEO-DLSL than Li foil. Noticeably, at the current density of 1 mA cm−2, the overpotential of PEO-DLSL was 269 mV, while the Li foil cannot be operated at 1 mA cm−2 due to the large overpotential exceeding the instrument voltage range (5 V). The PEO-DLSL electrode can be operated at 2 mA cm−2 as well, which exhibited stable cycling performance over 95 h with polarization voltage around 4 V (Supplementary Fig. 13). Moreover, the PEO-DLSL anode outperformed the planar Li foil in terms of cycling stability (Fig. 5d). More than 1000 h of stable Li stripping/plating with little overpotential increase can be realized at a relatively high current density and areal capacity (0.5 and 0.5 mAh cm−2). In contrast, the planar Li-foil cell showed a gradual increase in voltage hysteresis over cycles, due to the accumulating interfacial impedance, followed by an internal short circuit within 100 h. The superior rate and cycling performance of PEO-DLSL undoubtedly demonstrate the key role of a 3D hierarchical structure derived from diatomite on improving the performance of solid composite anode.

Fig. 5

Electrochemical performance comparison of the cells using PEO-DLSL and planar Li-foil anode, respectively. a Voltage profiles of symmetric cells using different anodes at different current densities. b, c Detailed voltage profiles at the current density of 0.1 and 0.5 mA cm−2, respectively. d Comparison of the long-term cycling stability of the symmetric cells with PEO-DLSL and Li-foil anodes at a current density of 0.5 mA cm−2. e Rate capability comparison of Li-LFP full batteries with PEO-DLSL and Li-foil anode. f GDC curves of PEO-DLSL/LFP and Li-foil/LFP full cells at 2 C current density. g Long-term cycling performance of batteries at a current density of 0.5 C. All cells were operated at 60 °C

To demonstrate the feasibility of a hierarchal PEO-DLSL composite anode for all-solid-state Li battery, the full cells coupled with LiFePO4 (LFP) cathodes and PEO-SPE layers were assembled to test the rate capability and long-term cycling stability. Supplementary Fig. 14a shows the EIS results of full cells based on the PEO-DLSL anode and Li-foil anode. The areal resistance of LFP/PEO-DLSL was ~90 Ω cm−2, much smaller than that of LFP/Li foil (~190 Ω cm−2), indicating the lower interfacial resistance in the PEO-DLSL-based full cell. As shown in Fig. 5e, the LFP/PEO-DLSL full cell displayed a much better rate performance compared with the Li-foil-based full cell. At low current densities, the specific discharge capacity of a planar Li-foil- based cell was 148 and 144 mAh g−1 at 0.1 and 0.2 C (1 C = 170 mA g−1, corresponding to 0.4 mA cm−2), respectively, whereas the values of the PEO-DLSL-based full cell were 167 and 155 mAh g−1. The Li-foil-based cell exhibited a very low specific charge capacity of only 7 mAh g−1 at 5 C, indicating poor rate capability. In contrast, the PEO-DLSL-based cell still retained 65 mAh g−1 at 5 C. After decreasing the current density back to 0.2 C, the capacity of PEO-DLSL-based full cell quickly increased to 152 mAh g−1, disclosing a fine capacity recovery. The improved rate performance could be attributed to the fast Li+ ion transportation property at both the interface and inside the electrode induced by the PEO-SPE coating and 3D Li+ ion-conductive Li4.4Si framework. This benefit was further confirmed by the galvanostatic discharge–charge (GDC) voltage profiles. As shown in Supplementary Fig. 14b, the LFP/PEO-DLSL and LFP/Li cells both demonstrated typical LiFePO4 charge/discharge voltage plateaus at 0.2 C. However, when cycled at 2 C, the LFP/PEO-DLSL cell exhibited a much lower charge–discharge overpotential and a higher specific capacity than that of LFP/Li (Fig. 5f). As to the long-term cycling performance, the LFP/PEO-DLSL cell delivered the specific discharge capacity of 117 mAh g−1 over 500 cycles with a very slow degradation rate (0.04% per cycle) at 0.5 C, whereas the LFP/Li-foil full cell was short circuited at the 70th cycle (Fig. 5g). The stable composite anode integrity and intimate interface contact together helped to improve the cycling stability of the as-fabricated all-solid-state LFP/PEO-DLSL full cell. Among the electrochemical performance summarized in Supplementary Table 2, our developed PEO-DLSL composite anode exhibited an outstanding performance in overpotential, cycling stability, and rate capability in comparison with the previously reported Li metal anode and SPE designs for solid-state Li batteries.


In our proposed hierarchical PEO-DLSL electrode design, the Li+ ion-conductive channels are provided by the PEO-SPE decorated Li4.4Si (PEO-Li4.4Si) frameworks. In this context, owing to the high Li+ ion conductivity of the PEO-Li4.4Si framework, our fabricated PEO-DLSL composite anode with embedded Li in a porous Li4.4Si framework and PEO-SPE coatings exhibit the following advantages. First, the porous Li4.4Si framework could act as the host to accommodate Li in the hierarchical pores, resulting in a robust electrode structure for electrochemical plating/stripping of Li. Second, the 3D Li4.4Si framework together with PEO-SPE coatings possesses a large electrode–solid electrolyte interfacial surface area, which could reduce localized current density and suppress the dendritic growth for improving the interfacial stability. To confirm this merit, we investigated the interfacial impedance variation of symmetric and full cells using PEO-DLSL and Li-foil anodes before and after cycling, and the results are shown in Supplementary Fig. 15. In the full cells, the original areal Rct of PEO-DLSL/LiFePO4 was ~116 Ω cm−2, and it changed a little to ~126 Ω cm−2 after ten cycles. Significantly, the areal Rct of Li/LiFePO4 increased obviously from ~153 to ~212 Ω cm−2. For symmetric cells, the areal Rct of PEO-DLSL/PEO-DLSL and Li/Li was ~124 Ω cm−2 and ~292 Ω cm−2, respectively. After 20 cycles, the corresponding areal Rct was ~138 Ω cm−2 and ~307 Ω cm−2, respectively. These comparisons demonstrate that the significant role of the as-proposed 3D hierarchical design in improving the interfacial stability between the anode and the PEO-based solid electrolyte. Finally, the a 3D porous Li4.4Si/PEO-SPE framework with a rigid mechanical characteristic could support the electrode with a negligible volume change during cycling, which would ensure intimate interfacial contact to further maintain the stability of the electrode.

To enable high efficiency of a hierarchical 3D electrode, the high Li+ ion conductivity inside the electrode is highly desirable. In our fabricated composite anode, the Li+ ionic conductivity is contributed both by the PEO-SPE decoration layer and Li4.4Si framework. It is well known that PEO-SPE is a good Li+ ion conductor when working at 60 °C, showing a high Li+ ionic conductivity of 4.63 × 10−4 S cm−1 at 60 °C (Supplementary Fig. 10). This means that the Li+ ions can be conducted along the surface of the Li4.4Si framework in the as-fabricated hierarchical 3D composite anode. For the evaluation of Li+ ionic conductivity in the Li4.4Si framework, the previously reported Li+ ion diffusion coefficient of Li4.4Si was in the range from 10−7 to 10−13 cm2 S−1 at room temperature48,49,50,51,52,53, making it hard to judge the capability of the Li4.4Si framework for the Li+ ionic conduction in our composite anode. In this case, we adopted the EIS comparison of the Li4.4Si electrode and PEO-SPE decorated Li4.4Si (PEO-Li4.4Si) electrode to reveal the Li+ ionic conduction contribution of the Li4.4Si framework in our fabricated composite anode. As shown in Supplementary Fig. 16, the resistance of the Li4.4Si electrode was measured as ~54 Ω cm−2, which means that the Li+ ions can be conducted in the Li4.4Si framework. After making decoration of PEO on the framework, the measured resistance reduced a little to ~37 Ω cm−2, indicating that the PEO decoration could enhance the Li+ ion conductivity of the PEO-Li4.4Si electrode. On the basis of the above results, we consider that the Li+ ionic conduction in the as-fabricated hierarchical 3D composite anode is endowed by both the PEO-SPE decoration layer and the Li4.4Si framework.

Beside the high Li+ ion conductivity, the balance between the ionic conductivity and electronic conductivity in the solid Li metal anode is also needed for its interfacial stability. During the plating process, the Li would be deposited at where the sufficient Li+ ions and electrons are both provided (electron/ion interface). In the traditional electrode, the electronic conductivity is much higher than Li+ ion conductivity and thus the deposition of Li is likely to be appeared at the electrode/electrolyte interface. But in our fabricated composite electrode, the Li+ ionic conductivity is dominant to make the deposition of Li occurring in the electrode framework, because of the low electronic conductivity of LixSi (3.06 × 104 Ω cm)54. The electron transfer is likely to be conducted in the metallic Li. As demonstrated in Supplementary Fig. 17a, plating of Li within the PEO-Li4.4Si framework starts from the bottom electron-conductive Li layer/PEO-Li4.4Si interface (denoted as interface I). “Fresh” Li first arises at interface I and then grows along the horizontal direction to fill the gap (Supplementary Fig. 17b). At the same time, the deposited Li could conduct electrons to the upper adjacent framework particle surface, generating a new electron/Li+ interface (interface II) and resulting in the rise of plated Li (Supplementary Fig. 17c). In our opinion, Li plating occurs at two orientations to fill the whole framework up31. It is noteworthy that the difference in electronic transfer ability could also explain the low charge capacity and fluctuation curve of DF-Si-Li0.2 and DF-Si-Li0.5 electrodes.

In summary, we report an efficient strategy to construct 3D hierarchical PEO-DLSL composite anode derived from natural abundant diatomite. The hierarchical structure of the PEO-DLSL composite anode inherited from natural diatomite facilitates the intimate contact between the electrode and the solid-state electrolyte, providing highly Li+ ion-conductive channels, which is crucial for accommodating the interfacial fluctuation during battery cycling. As a result, low overpotential and good cycling stability could be realized in symmetric and full cells using PEO-DLSL composite anodes. This hierarchical Li composite anode is promising to fabricate a safe solid-state Li metal battery with high energy/power density.


Purification of diatomite

Ultrapure bio-silica microflakes (BSM) were obtained from raw diatomite after a specific purification process. Typically, the as-received diatomite powders were immersed and stirred overnight in sulfuric acid (1 M) and nitric acid (2 M) to remove the metal impurities and the organic constituents. The purified products were collected by filtration and washed by deionized water (DIW) and ethanol, respectively. Then the BSM with different particle sizes were separated using recycled sedimentation processes in acetone. Finally, the obtained microflakes were dried and annealed at 500 °C in air for 12 h.

Magnesiothermic reduction of diatomite

In total, 1.0 g of purified diatomite was mixed with 3.0 g of sodium chloride (Sinopharm Chemical Reagent Co., Ltd) and a different mass of magnesium powder (99.5%, Aladdin) by hand grinding. The mass of Mg was determined by the desired mass ratio (Mdiatomite/MMg). Then the mixed powder was sealed in a tantalum crucible and transferred into a tube furnace. The crucible was then heated at 650 °C for 6 h in 5% H2/Ar. The magnesiated diatomite (DF-SiO or DF-Si depending on the mass ratio) was dispersed in DIW and reacted with concentrated HCl and 0.5% HF (Sinopharm Chemical Reagent Co., Ltd) for 6 h by stirring. After that, the product was collected by filtration and washed with DIW and ethanol, respectively, and finally dried at 80 °C overnight.

Overstoichiometric lithiation and PEO-SPE decoration of DF

The synthesized DF powders were first heated at ~120 °C in the argon-filled glove box for 12 h to remove the adsorbed O2/H2O before performing overstoichiometric lithiation progress. To overlithiate the DF-Si, 0.5 g of DF-Si powders were put into a tantalum crucible and heated on a hot plate at ~350 °C. After that, Li metal (China Energy Lithium Co., Ltd) was weighted in a desired amount and put into the crucible under stirring to achieve a homogeneous reaction. Once the reaction was completed, the obtained products were cooled in the glove box to room temperature. PEO-SPE for surface decoration was synthesized by stirring a certain amount of PEO (Mw = 100,000, Alfa Aesar) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI, TCI Chemicals) in anhydrous acetonitrile (Energy Chemical, www.energy-chemical.com). Then the DF-Si–Li powders were mixed with PEO-SPE solution and stirred for 2 h, and then dried at 60 °C. The PEO-SPE used for the electrochemical test was fabricated by mixing a certain amount of PEO (Mw = 600,000, Sigma–Aldrich) and LiTFSI with gentle stirring to form a viscous solution, and then the solution was poured into a square Teflon mold (5 cm) and dried at 60 °C for 24 h. Finally, the PEO-SPE membrane was peeled off from the Teflon mold and cut into a round disk (diameter = 16 mm) for the electrochemical test.

PEO-DLSL electrode fabrication

Cold-pressing method was applied to fabricate the PEO-DLSL electrode. A certain amount of DF-Li-PEO powders were weighted and put into the pellet die (diameter = 12 mm) followed by ~10 tons of pressure. All the steps were conducted in the glove box with H2O and O2 content below 0.1 ppm. Typically, the weight of the PEO-DLSL was about ~60 mg.

Li extraction behavior of different electrodes

The Li extraction behavior of the synthesized electrodes was measured in 2032 coin cells and discharged to 1.0 V. The composite electrodes were used as a cathode, while the Li foil was used as an anode. The electrolyte used for Li extraction is 1 M LiPF6 in EC/DEC (3:7, v:v) and the current density was 10 μA mg−1.

Electrochemical performance of symmetric cells

Electrochemical performance of symmetric cells using PEO-DLSL and Li foil (diameter = 15.6 mm, www.dodochem.com) was evaluated by 2032-coin cell batteries. The cells were assembled in an argon-filled glove box with oxygen and water content below 0.5 ppm. The electrolyte was PEO-SPE (Mw = 600,000 for PEO with LiTFSI) for solid-state cells, while 1 M LiPF6 in EC/DEC (www.dodochem.com) was used as liquid electrolyte. The plating/stripping performance of symmetric cells was conducted on a Land multichannel electrochemical testing system with different current density and areal capacity. Electrochemical impedence spectroscopy tests were recorded by a Bio-Logic VMP3 electrochemical working station between 1 M Hz and 1 Hz. It is noteworthy that we set the standing time as 30 min for the symmetric cell cycling when the current densities were higher than 200 μA cm−2 to release possible polarization. As a result, the voltage slowly decreased to zero at the end of charge/discharge process.

Electrochemical performance of all-solid-state LiFePO4/Li batteries using different Li anodes

To study the electrochemical performance of Li/LiFePO4 batteries, 2032 coin cells were assembled. The anode was PEO-DLSL and planar Li foil, respectively. For preparing the working cathode, PEO-SPE was first made by mixing PEO and LiTFSI in anhydrous acetonitrile (Energy Chemical, www.energy-chemical.com) and used as a binder. Then, LiFePO4 (MTI Inc.) powder, super-P acetylene black (Alfa Aesar), and PEO-SPE were mixed at a weight ratio of 80:10:10 in the N-methyl-2-pyrrolidone (NMP, Sigma-Aldrich) solvent to form a uniform slurry. Afterward, the slurry was casted on an Al-carbon foil (MTI) by a doctor blade and dried at 60 °C in vacuum. The diameter of the electrode slices was 11 mm with active material loading of ~2.4 mg cm−2. The electrolyte was PEO-LiTFSI SPEs. The operating temperature was 60 °C. The rate capability test was carried out on a Land multichannel test system with different current densities between 2.3 and 3.8 V (vs. Li+/Li).


Powder X-ray diffraction (PXRD) patterns were carried out on a Philips X’Pert PRO SUPER X-ray diffractometer equipped with graphite-monochromatized Cu Kα radiation. Transmission electron microscope (TEM, Hitachi H-7650) and scanning electron microscope (SEM, JEOL-6700F) were employed to visualize the morphologies, sizes, structures, and elemental compositions of the products. The nitrogen absorption/desorption isotherms were obtained at 77 K on a Quantachrome autosorb iQ2 automated gas sorption analyzer, using BET calculations for surface area and BJH for pore size distribution at 77 K. The soft X-ray beam was focused on the samples using an elliptical capillary condenser. A total of 122 projections were collected at tilt angles of −57 to 66° at 1° increments with 2 seconds exposures at 520 eV X-ray energy. All of the projections were corrected based on a reference image with a flat field intensity and aligned to the rotation axis. Tomographic reconstruction of the projections was carried out by the total variation (TV)-based simultaneous algebraic reconstruction technique.

Data availability

The data that support the findings of this study are available from the corresponding author upon request.


  1. 1.

    Bruce, P. G., Freunberger, S. A., Hardwick, L. J. & Tarascon, J.-M. Li-O2 and Li-S batteries with high energy storage. Nat. Mater. 11, 19 (2011).

    ADS  Article  Google Scholar 

  2. 2.

    Lin, D., Liu, Y. & Cui, Y. Reviving the lithium metal anode for high-energy batteries. Nat. Nanotech. 12, 194 (2017).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Xu, W. et al. Lithium metal anodes for rechargeable batteries. Energy Environ. Sci. 7, 513–537 (2014).

    CAS  Article  Google Scholar 

  4. 4.

    Yang, C., Fu, K., Zhang, Y., Hitz, E. & Hu, L. Protected lithium-metal anodes in batteries: from liquid to solid. Adv. Mater. 29, 1701169 (2017).

    Article  Google Scholar 

  5. 5.

    Cheng, X.-B., Zhang, R., Zhao, C.-Z. & Zhang, Q. Toward safe lithium metal anode in rechargeable batteries: a review. Chem. Rev. 117, 10403–10473 (2017).

    CAS  Article  Google Scholar 

  6. 6.

    Lu, Y., Tu, Z. & Archer, L. A. Stable lithium electrodeposition in liquid and nanoporous solid electrolytes. Nat. Mater. 13, 961 (2014).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Zheng, G. et al. Interconnected hollow carbon nanospheres for stable lithium metal anodes. Nat. Nanotech. 9, 618 (2014).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Bhattacharyya, R. et al. In situ NMR observation of the formation of metallic lithium microstructures in lithium batteries. Nat. Mater. 9, 504 (2010).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Zhao, J. et al. Air-stable and freestanding lithium alloy/graphene foil as an alternative to lithium metal anodes. Nat. Nanotech. 12, 993 (2017).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Gao, Z. et al. Promises, challenges, and recent progress of inorganic solid-state electrolytes for all-solid-state lithium batteries. Adv. Mater. 30, 1705702 (2018).

    Article  Google Scholar 

  11. 11.

    Sun, C., Liu, J., Gong, Y., Wilkinson, D. P. & Zhang, J. Recent advances in all-solid-state rechargeable lithium batteries. Nano Energy 33, 363–386 (2017).

    CAS  Article  Google Scholar 

  12. 12.

    Varzi, A., Raccichini, R., Passerini, S. & Scrosati, B. Challenges and prospects of the role of solid electrolytes in the revitalization of lithium metal batteries. J. Mater. Chem. A 4, 17251–17259 (2016).

    CAS  Article  Google Scholar 

  13. 13.

    Motavalli, J. Technology: a solid future. Nature 526, S96 (2015).

    ADS  CAS  Article  Google Scholar 

  14. 14.

    Monroe, C. & Newman, J. The impact of elastic deformation on deposition kinetics at lithium/polymer interfaces. J. Electrochem. Soc. 152, A396–A404 (2005).

    CAS  Article  Google Scholar 

  15. 15.

    Duan, H. et al. Dendrite-free li-metal battery enabled by a thin asymmetric solid electrolyte with engineered layers. J. Am. Chem. Soc. 140, 82–85 (2018).

    CAS  Article  Google Scholar 

  16. 16.

    Murugan, R., Thangadurai, V. & Weppner, W. Fast lithium ion conduction in garnet-type Li7La3Zr2O12. Angew. Chem. Int. Ed. 46, 7778–7781 (2007).

    CAS  Article  Google Scholar 

  17. 17.

    Herbert, E. G., Tenhaeff, W. E., Dudney, N. J. & Pharr, G. M. Mechanical characterization of LiPON films using nanoindentation. Thin Solid Films 520, 413–418 (2011).

    ADS  CAS  Article  Google Scholar 

  18. 18.

    Kamaya, N. et al. A lithium superionic conductor. Nat. Mater. 10, 682 (2011).

    ADS  CAS  Article  Google Scholar 

  19. 19.

    Kato, Y. et al. High-power all-solid-state batteries using sulfide superionic conductors. Nat. Energy 1, 16030 (2016).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Fu, K. et al. Toward garnet electrolyte-based Li metal batteries: an ultrathin, highly effective, artificial solid-state electrolyte/metallic Li interface. Sci. Adv. 3, e1601659 (2017).

    ADS  Article  Google Scholar 

  21. 21.

    Yue, J., Yan, M., Yin, Y.-X. & Guo, Y.-G. Progress of the interface design in all-solid-state Li-S batteries. Adv. Funct. Mater. 28, 1707533 (2018).

    Article  Google Scholar 

  22. 22.

    Liu, Y. et al. Transforming from planar to three-dimensional lithium with flowable interphase for solid lithium metal batteries. Sci. Adv. 3, eaao0713 (2017).

    Article  Google Scholar 

  23. 23.

    Jung, Y. S., Oh, D. Y., Nam, Y. J. & Park, K. H. Issues and challenges for bulk-type all-solid-state rechargeable lithium batteries using sulfide solid electrolytes. Isr. J. Chem. 55, 472–485 (2015).

    CAS  Article  Google Scholar 

  24. 24.

    Bouchet, R. et al. Single-ion BAB triblock copolymers as highly efficient electrolytes for lithium-metal batteries. Nat. Mater. 12, 452 (2013).

    ADS  CAS  Article  Google Scholar 

  25. 25.

    Tao, X. et al. Solid-state lithium-sulfur batteries operated at 37 °C with composites of nanostructured Li7La3Zr2O12/carbon foam and polymer. Nano. Lett. 17, 2967–2972 (2017).

    ADS  CAS  Article  Google Scholar 

  26. 26.

    Xue, Z., He, D. & Xie, X. Poly(ethylene oxide)-based electrolytes for lithium-ion batteries. J. Mater. Chem. A 3, 19218–19253 (2015).

    CAS  Article  Google Scholar 

  27. 27.

    Zeng, X.-X. et al. Reshaping lithium plating/stripping behavior via bifunctional polymer electrolyte for room-temperature solid Li metal batteries. J. Am. Chem. Soc. 138, 15825–15828 (2016).

    CAS  Article  Google Scholar 

  28. 28.

    Long, L., Wang, S., Xiao, M. & Meng, Y. Polymer electrolytes for lithium polymer batteries. J. Mater. Chem. A 4, 10038–10069 (2016).

    CAS  Article  Google Scholar 

  29. 29.

    Lin, Y., Wang, X., Liu, J. & Miller, J. D. Natural halloysite nano-clay electrolyte for advanced all-solid-state lithium-sulfur batteries. Nano Energy 31, 478–485 (2017).

    CAS  Article  Google Scholar 

  30. 30.

    Lin, D. et al. Three-dimensional stable lithium metal anode with nanoscale lithium islands embedded in ionically conductive solid matrix. Proc. Natl Acad. Sci. USA 114, 4613 (2017).

    CAS  Article  Google Scholar 

  31. 31.

    Yang, C. et al. Continuous plating/stripping behavior of solid-state lithium metal anode in a 3D ion-conductive framework. Proc. Natl Acad. Sci. USA 115, 3770 (2018).

    CAS  Article  Google Scholar 

  32. 32.

    Fu, K. et al. Flexible, solid-state, ion-conducting membrane with 3D garnet nanofiber networks for lithium batteries. Proc. Natl Acad. Sci. USA 113, 7094 (2016).

    ADS  CAS  Article  Google Scholar 

  33. 33.

    Fu, K. et al. Three-dimensional bilayer garnet solid electrolyte based high energy density lithium metal-sulfur batteries. Energy Environ. Sci. 10, 1568–1575 (2017).

    CAS  Article  Google Scholar 

  34. 34.

    Liang, Z. et al. Composite lithium metal anode by melt infusion of lithium into a 3D conducting scaffold with lithiophilic coating. Proc. Natl Acad. Sci. USA 113, 2862 (2016).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Lin, D. et al. Layered reduced graphene oxide with nanoscale interlayer gaps as a stable host for lithium metal anodes. Nat. Nanotech. 11, 626 (2016).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Liu, N. et al. A pomegranate-inspired nanoscale design for large-volume-change lithium battery anodes. Nat. Nanotech. 9, 187 (2014).

    ADS  CAS  Article  Google Scholar 

  37. 37.

    Yao, H. et al. Crab shells as sustainable templates from nature for nanostructured battery electrodes. Nano. Lett. 13, 3385–3390 (2013).

    ADS  CAS  Article  Google Scholar 

  38. 38.

    Kovalenko, I. et al. A major constituent of brown algae for use in high-capacity Li-Ion batteries. Science 334, 75 (2011).

    ADS  CAS  Article  Google Scholar 

  39. 39.

    Chen, K. et al. Growing three-dimensional biomorphic graphene powders using naturally abundant diatomite templates towards high solution processability. Nat. Commun. 7, 13440 (2016).

    ADS  CAS  Article  Google Scholar 

  40. 40.

    Jeffryes, C., Campbell, J., Li, H., Jiao, J. & Rorrer, G. The potential of diatom nanobiotechnology for applications in solar cells, batteries, and electroluminescent devices. Energy Environ. Sci. 4, 3930–3941 (2011).

    CAS  Article  Google Scholar 

  41. 41.

    Li, J. et al. Diatomite-templated synthesis of freestanding 3D graphdiyne for energy storage and catalysis application. Adv. Mater. 30, 1800548 (2018).

    Article  Google Scholar 

  42. 42.

    Ryu, J., Hong, D., Choi, S. & Park, S. Synthesis of ultrathin Si nanosheets from natural clays for lithium-ion battery anodes. ACS Nano 10, 2843–2851 (2016).

    CAS  Article  Google Scholar 

  43. 43.

    Nassif, N. & Livage, J. From diatoms to silica-based biohybrids. Chem. Soc. Rev. 40, 849–859 (2011).

    CAS  Article  Google Scholar 

  44. 44.

    Luo, W. et al. Transition from superlithiophobicity to superlithiophilicity of garnet solid-state electrolyte. J. Am. Chem. Soc. 138, 12258–12262 (2016).

    CAS  Article  Google Scholar 

  45. 45.

    Wang, B. et al. Atomic layer deposited lithium silicates as solid-state electrolytes for all-solid-state batteries. ACS Appl. Mater. Interfaces 9, 31786–31793 (2017).

    CAS  Article  Google Scholar 

  46. 46.

    Lu, Y. & Ni, Y. Effects of particle shape and concurrent plasticity on stress generation during lithiation in particulate Li-ion battery electrodes. Mech. Mater. 91, 372–381 (2015).

    Article  Google Scholar 

  47. 47.

    Chang, L., Lu, Y., He, L. & Ni, Y. Phase field model for two-phase lithiation in an arbitrarily shaped elastoplastic electrode particle under galvanostatic and potentiostatic operations. Int. J. Solids Struct. 143, 73–83 (2018).

    CAS  Article  Google Scholar 

  48. 48.

    Wang, Z., Su, Q., Deng, H. & Fu, Y. Composition dependence of lithium diffusion in lithium silicide: a density functional theory study. Chem. Electro Chem. 2, 1292–1297 (2015).

    CAS  Google Scholar 

  49. 49.

    Arie, A. A. & Lee, J. K. Estimation of Li-Ion diffusion coefficients in C60 coated Si thin film anodes using electrochemical techniques. Defect Diffus. Forum 326–328, 87–92 (2012).

    Article  Google Scholar 

  50. 50.

    Jung, S. C., Jung, D. S., Choi, J. W. & Han, Y.-K. Atom-level understanding of the sodiation process in silicon anode material. J. Phys. Chem. Lett. 5, 1283–1288 (2014).

    CAS  Article  Google Scholar 

  51. 51.

    Wen, C. J. & Huggins, R. A. Chemical diffusion in intermediate phases in the lithium-silicon system. J. Solid State Chem. 37, 271–278 (1981).

    ADS  CAS  Article  Google Scholar 

  52. 52.

    Ding, N. et al. Determination of the diffusion coefficient of lithium ions in nano-Si. Solid State Ion. 180, 222–225 (2009).

    CAS  Article  Google Scholar 

  53. 53.

    Chou, C.-Y. & Hwang, G. S. Surface effects on the structure and lithium behavior in lithiated silicon: a first principles study. Surf. Sci. 612, 16–23 (2013).

    ADS  CAS  Article  Google Scholar 

  54. 54.

    Tang, W. et al. Lithium silicide surface enrichment: a solution to lithium metal battery. Adv. Mater. 30, 1801745 (2018).

    Article  Google Scholar 

Download references


We acknowledge the funding support from the National Natural Science Foundation of China (Grants 51571184, 21501165, 21431006, 51571184, and 21805268), the Foundation for Innovative Research Groups of the National Natural Science Foundation of China (Grants 21521001 and 11472262), the Users with Excellence and Scientific Research Grant of Hefei Science Center of CAS (2015HSC-UE007, 2015SRG-HSC038), Key Research Program of Frontier Sciences, CAS (Grant QYZDJ-SSW-SLH036), the Chinese Academy of Sciences (Grant KJZD-EW-M01-1), the Fundamental Research Funds for the Central Universities (Grant WK 2060190085), and the Strategic Priority Research Program of the Chinese Academy of Sciences (Grant No. XDB22040502). This work was partially carried out at the USTC Center for Micro and Nanoscale Research and Fabrication.

Author information




F.Z. and H.-B.Y. conceived the concept. H.-B.Y. and S.-H.Y. supervised the project. F.Z., Z.L. and B.S. carried out the synthesis and performed materials characterization and electrochemical measurements. Y.Y.L and Y.N. conducted the simulation of lithiation process and stress evolution. Y.G., X.-X.W. and B.-S.Z. assisted in the characterization of the electrode materials. Y.-C.Y. and L.-L.L. assisted in drawing figures and analyzing the electrochemical performance data. S.-H.Y. and Y.C. provided important experimental insights. F.Z., H.-B.Y. and S.-H.Y. cowrote the paper. All authors discussed the results and commented on the paper.

Corresponding authors

Correspondence to Hong-Bin Yao or Shu-Hong Yu.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks Kun Fu,Chih-Long Tsai and other anonymous reviewer(s) for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Zhou, F., Li, Z., Lu, YY. et al. Diatomite derived hierarchical hybrid anode for high performance all-solid-state lithium metal batteries. Nat Commun 10, 2482 (2019). https://doi.org/10.1038/s41467-019-10473-w

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing