Continuous wave amplified spontaneous emission in phase-stable lead halide perovskites


Sustained stimulated emission under continuous-wave (CW) excitation is a prerequisite for new semiconductor materials being developed for laser gain media. Although hybrid organic-inorganic lead-halide perovskites have attracted much attention as optical gain media, the demonstration of room-temperature CW lasing has still not been realized. Here, we present a critical step towards this goal by demonstrating CW amplified spontaneous emission (ASE) in a phase-stable perovskite at temperatures up to 120 K. The phase-stable perovskite maintains its room-temperature phase while undergoing cryogenic cooling and can potentially support CW lasing also at higher temperatures. We find the threshold level for CW ASE to be 387 W cm-2 at 80 K. These results indicate that easily-fabricated single-phase perovskite thin films can sustain CW stimulated emission, potential at higher temperatures as well, by further optimization of the material quality in order to extend the carrier lifetimes.


Recently, solution-processed metal-halide perovskite semiconductors have started to challenge the performance of traditional inorganic semiconductors in the field of thin-film photovoltaics1,2. These perovskites possess the chemical structure ABX3, where A is an organic or inorganic cation, such as methylammonium (CH3NH3/MA), formamidinium (CH(CH2)2)/FA) or cesium (Cs), B is a metal (commonly Pb), and X is a halide (Cl, Br, or I). With an impressive tolerance to grain boundaries and defects, perovskite thin films exhibit high charge carrier mobilities, as well as excellent absorption and emission properties3. These properties of thin films of perovskite deposited, e.g., by spin-coating, can be surprisingly close to the performance of perovskite single crystals4. As a direct bandgap semiconductor, perovskites are well-suited not only for solar cells, but also for light-emitting devices5,6. Perovskites can be integrated in light-emitting diodes (LEDs) as the emitting semiconductor layer6,7,8,9, or applied in the form of nanocrystals for color conversion with InGaN-based LEDs as a potential replacement for traditional phosphors10. Of most relevance to the current work is the ability of perovskites to exhibit stimulated emission and serve as optical gain media in the near infrared and across the visible range11,12. The progress in perovskite lasers has been summarized in several recent reviews6,13,14,15,16,17,18. Low-threshold lasing under pulsed optical excitation has been demonstrated using various resonator geometries, including at wavelengths within the “green gap”19,20, where conventional III–V-semiconductors suffer from low efficiencies21,22,23. However, to become commercially relevant (ultimately in an electrically pumped configuration), any novel gain material (such as perovskites) should demonstrate the ability to maintain optical gain under continuous wave (CW) operation and ideally at room temperature, or at least at temperatures accessible by Peltier cooling (>220 K).

Obtaining CW operation has proven to be a major challenge for most solution-processable semiconductors, such as organic semiconductors and colloidal semiconductor nanocrystals. While the former class of materials has never demonstrated CW lasing, the latter only recently made this step, almost two decades after the initial investigations24,25,26,27. Despite this impressive achievement, further progress towards electrically pumped lasing is expected to be highly challenging for colloidal semiconductor nanocrystal devices due to their limited electrical transport characteristics.

Demonstrating CW lasing in thin perovskite films is of great interest, as this would present a solution-processable gain material exhibiting excellent electrical transport properties. However, to date CW stimulated emission has not been demonstrated in technologically relevant single-phase thin films. First demonstrations of CW lasing in perovskites were made in nanowires, where lasing was attributed to a condensate of polaritons enabled by the strong light–matter interaction between the photons and the cavity excitons28,29. True CW photon lasing in thin films, which is more relevant for practical applications, has proven to be difficult to achieve with the perovskite workhorse material methylammonium lead triiodide (CH3NH3PbI3). This difficulty has been ascribed to the phase instabilities of the crystal lattice with temperature, the limited thermal conductivity, screening effects and/or the rotational freedom of the methylammonium cation30,31,32. Clear proof of CW lasing in CH3NH3PbI3 was demonstrated by Jia et al. at a very specific temperature of 100 K, where different crystalline phases coexist upon optical pumping32. The requirement of the simultaneous presence of two crystal phases limited CW lasing to these special conditions, whereas at other temperatures, photon lasing has only been possible at pulsed excitation32. In this sense, although this previous demonstration of CW lasing was an impressive achievement, the need for the mixed-phase structure does not establish the ability of conventional, single-phase, perovskites to serve as gain material of sufficient quality for CW lasing.

Here, we demonstrate sustained CW lasing in a mixed cation system at the A site of the perovskite crystal structure. We use a mixed cation perovskite as it undergoes no phase change during the transition from room temperature to cryogenic temperatures. Consequently, we show that this phase-stable mixed-cationic perovskite can support CW optical gain at any temperature up to 120 K. These findings are a significant step towards practical perovskite CW lasers operating at room temperature, which opens new avenues to the development of perovskite semiconductor laser diodes and the solution of the green gap problem.


Temperature-dependent amplified spontaneous emission (ASE) under pulsed excitation

In our study we employ a triple cation system with a non-stoichiometric ratio of Cs0.1(MA0.17FA0.83)0.9Pb0.84(I0.84Br0.16)2.68 in the precursor solution as reported previously in order to obtain low optical gain thresholds and an improved stability12. The partial replacement of the MA cation results in an identical crystal phase for arbitrary iodine bromine ratios at room temperature. No phase transitions are known at lower temperatures33,34, or have been observed in the current work. The perovskite layers were prepared on sapphire substrates and post treated by an imprinting step to reduce the surface roughness and to improve the morphology35,36,37 (see Supplementary Figure 1 for atomic force microscopy images of both pristine and imprinted layers). The smaller roughness decreases the waveguide scattering losses and is, therefore, expected to reduce the ASE threshold12,35,38. ASE, a type of mirrorless lasing39, is highly suited for studying the material’s gain characteristics by eliminating the influences of the laser resonator (which can induce a strong temperature dependence through the thermo-optic coefficient of the material). Additionally, this approach eliminates any ambiguity that may arise from cavity effects, such as angular-dependent diffraction of certain wavelengths from gratings or spectral filtering from DBR mirrors, which can change the detected shape of the spontaneous emission spectra even without stimulated emission being involved. Accurately establishing the existence of lasing is indeed not experimentally trivial and for more information on the experimental verification of real lasing the reader is referred to the commentary by Samuel et al.40.

Figure 1 depicts the temperature-dependent ASE thresholds measured under 0.8 ns pulsed excitation. An example of the evolution of the emission spectra from a 185 nm-thick perovskite film over a range of pump fluences at room temperature is shown in Fig. 1a. The film was mounted inside a cryostat (Janis STVP-100, see Supplementary Figure 2 for a schematic of the experimental setup) allowing the intensity-dependence of the emission spectrum to be measured as a function of temperature. In order to unambiguously identify ASE, it is important to monitor the broadband spectra below threshold (the spontaneous emission (PL), PL refers to the spectral part not containing stimulated emitted photons), as well as the narrowband spectra above threshold. The change of the luminescence profile below and above threshold distinguishes the onset of ASE from artifacts in thin films, such as a spectral modification of the detected PL due to photon propagation in a waveguide close to cut-off conditions. At low excitation fluences, the PL spectrum can be clearly identified by a broadband emission profile with a full width at half maximum (FWHM) of ~40 nm and a nearly Gaussian shape. As the pump fluence increases, an intense emission shoulder between 773 and 785 nm (superimposed onto the PL spectra) emerges, indicating the onset of ASE. There are different methods to extract the threshold value for ASE41, here we follow the approach suggested by Sutherland et al.42. In the transition region from “predominant PL” to “predominant ASE”, the spectrum consists of a superposition of contributions from both processes. The PL contribution is proportional to the integral of the emission in the higher energy half of the PL-spectrum, which does not contain the ASE part (680–767 nm, area A in Fig. 1b). The ASE contribution can be estimated by integrating the low-energy half of the spectrum (area B in Fig. 1b) and subtracting the PL (area A) as illustrated in Fig. 1b. The integration boarder is chosen as the center wavelength of a Gaussian Fit to the spectra recorded at the lowest fluence (Supplementary Figure 3). Figure 1c depicts the total integrated PL intensity (approximated by twice the area A), the integrated ASE intensity (approximated by the difference between area B and area A) and the narrowing of the FWHM as a function of the pump fluence. The threshold level is determined by the intersection of a linear fit of the ASE contribution with the pump fluence axis, yielding a threshold level of 95.3 µJ cm−2. This value agrees well with the values reported in the literature for perovskite semiconductors6,15,16. Figure 1d depicts the dependence of the threshold levels on the temperature. As the temperature is reduced from 290 to 80 K, the ASE threshold decreases down to .2 µJ cm−2. It is empirically well-known that temperature-dependent current threshold in semiconductor diode lasers follows an exponential law43. Figure 1d shows a fit of the pulsed threshold fluence using the following formula:

$$F_{{\mathrm{th}}} = F_0 \cdot \exp \left( {\frac{T}{{T_0}}} \right)$$

where T is the temperature, F0 the threshold when T approaches zero and T0 is the characteristic temperature. As can be seen, there is a good agreement between the measurements and the fit, yielding a characteristic temperature of T0 = 46 K. We note that this characteristic temperature is lower than that of most inorganic semiconductor laser diodes, implying a stronger dependence of the threshold levels of our perovskites on the temperature43. The reduction of the thresholds at lower temperatures can be attributed mainly to two distinct mechanisms. First, the temperature dependence of the carrier distribution in the conduction and valence bands leads to lower threshold values for achieving population inversion at lower temperatures. However, this effect by itself yields a temperature dependence that scales as \(T^{\frac{3}{2}}\) (see Supplementary Note 1), indicating the impact of additional mechanisms. Second, the recombination lifetime increases for lower temperatures, leading to larger carrier densities (at a given excitation intensity) at lower temperatures. Consequently, the threshold density level is obtained at lower pump fluences when the temperature is low. The dependence of the carrier lifetime on the temperature was carried out using streak camera measurements. Consistent with the literature44, a significant increase of the carrier lifetime was found when the temperature was reduced from 290 to 80 K (Fig. 2a and Supplementary Figure 4). Additionally, the total signal strength at constant excitation fluence increases substantially at lower temperatures due to the typical increase of the photoluminescence quantum yield (PLQY)45,46. Consequently, the ratio of radiative to non-radiative recombination increases, leading to a lower ASE onset threshold. In contrast to CH3NH3PbI3, where the structural phase change at 160 K leads to a drastic and sudden change in the PL properties, the PL spectrum in our triple cation material shifts steadily over the entire temperature range without any noticeable hysteresis (Supplementary Figure 5). The PL peak wavelength shifts gradually from 766 to 783 nm while its FWHM narrows from 46 to 16 nm as the temperature is decreased from 290 to 80 K (Fig. 2b), clearly indicating the existence of a single phase across the transition from room to cryogenic temperatures.

Fig. 1

Amplified spontaneous emission properties under pulsed excitation (~0.8 ns). a Example of data for room temperature showing the evolution of the emission spectra from which the amplified spontaneous emission (ASE) threshold is established. Different colors for the spectra are chosen for better distinguishability. b Regions of the spectrum used to determine spontaneous emission (PL) and ASE contributions. The inset graphically shows the assigned PL contribution (blue, area A and area A mirrored at the center wavelength) and ASE contribution (orange, area B–area A) and the real spectrum (black line). c PL, ASE, and full width at half maximum (FWHM) as a function of the pulse fluence. d ASE threshold as a function of temperature. The threshold decreases by more than an order of magnitude from room temperature to 80 K. The red line is a fit to the empirical exponential threshold law typically observed in inorganic semiconductors. The characteristic temperature T0 is found to be 46 K

Fig. 2

Temperature-dependent PL properties. a Transient PL images showing the integrated intensity as a function of time after fs-excitation and temperature at an excitation fluence of 60 nJ cm−2. The red dots denote the carrier lifetime τ0 defined as the time when the integrated intensity dropped to 1/e of its initial intensity. The dotted line is drawn as a guide to the eye. b Peak wavelength and FWHM of the thin film PL. The blue symbols are extracted from the measurement while cooling down and the red symbols are extracted while heating up

ASE under CW excitation

The source used for the CW pumping experiments was a diode-pumped solid-state laser (Millennia, Spectra Physics, 532 nm, Pmax = 3.3 W). Figure 3a depicts the normalized emission spectra at several different CW pump intensities measured at 80 K. Similar to the pulsed excitation case, the typical ASE shoulder evolves in the spectra between 786 and 794 nm and develops into a dominating peak. Figure 3b depicts a log-scale plot of the luminescence spectra for all recorded pump intensities (Supplementary Figure 6 includes the detailed pump powers and include a linear scale plot, Supplementary Figures 7 and 8 depict the normalized spectra). Above the ASE threshold, most of the additional pump power is fed into ASE when the excitation intensity is increased. Using the above-mentioned approach, the ASE threshold intensity under CW excitation was found to be Ith,CW = 387 W cm−2 (see Fig. 3c). Note that above threshold, the FWHM of the ASE peak collapses rapidly, reaching values of ~2 nm at high pumping intensities. The clear threshold and the dramatic narrowing of the peak proves the generation of ASE under CW excitation. Figure 2d presents a comparison of the emission spectra under CW excitation at low intensity (well below threshold, 6 W cm−2), at high intensity (well above threshold, 1258 W cm−2), as well as the corresponding spectra under pulsed excitation above threshold fluence (~14 µJ cm−2). The spectra at high CW intensities and pulsed excitation are comparable, proving that the material’s emission properties and the crystal phase remain unchanged when CW ASE starts. Note that sustaining the same crystal morphology under pulsed and CW excitation constitutes a significant improvement with respect to the previous CW lasing observations in CH3NH3PbI332, thus demonstrating that CW stimulated emission can be sustained in single-phase perovskites. The limited thermal conductivity of perovskites does not seem to be a major issue since the ASE peak wavelengths for pulsed and CW excitations are identical.

Fig. 3

Characterization of CW ASE at 80 K. a The emission spectrum changes for increasing excitation intensities from a broadband PL spectrum (FWHM~15–20 nm) to a narrowband ASE spectrum (FWHM ~2 nm). b Logarithmic representation of the luminescence spectra for increasing excitation intensities showing the rise of ASE between 786 and 794 nm. c PL, ASE, and FWHM as a function of the CW excitation intensity. At the threshold intensity of 387 W cm−2, the FWHM decreases significantly and most of the additional pump intensity is fed into the ASE band. d Comparison of CW PL, CW ASE, and pulsed ASE spectra at 80 K

The CW threshold Ith,CW value is nearly an order of magnitude lower than the corresponding peak intensity at pulsed excitation (Ith,pulsed = 2750 W cm−2), calculated as the threshold fluence divided by the pump duration (0.8 ns) under pulsed excitation. This is, however, not surprising as the carrier lifetime at 80 K is substantially longer than the pump pulse duration. When the excitation pulse is shorter than the carrier lifetime, the threshold power and the pulse energy are rather related by47

$$I_{{\mathrm{th}},{\mathrm{CW}}} \cdot \tau = F_{{\mathrm{th}}}$$

where τ is the carrier lifetime. Dividing our observed values of Fth and Ith,CW results in a coarse estimate for the carrier lifetime at low temperature of 5.7 ns, which is entirely reasonable considering our streak camera measurements, even when considering the significant additional Auger processes for higher excitation densities (Fig. 2a).

The plausibility of the ASE threshold can be tested using the Bernard–Duraffourg condition48 which, for equal effective masses for both carriers, requires the quasi-Fermi levels for electrons and holes to reach the conduction and valence band energy levels, respectively. Assuming me = mh for perovskite semiconductors3 and using standard equations for the carrier density in 3D semiconductors with parabolic bands, the carrier density at the point when the quasi-Fermi levels reach the band edges can be estimated to be 1.54 × 1017 cm−3 at 80 K (see Supplementary Note 1 for detailed calculations). Therefore, the minimal carrier lifetime required for reaching a given carrier density at a given excitation rate can be readily estimated (see Supplementary Note 2 for details). Using a generation rate based on the threshold intensity of 387 W cm−2, we find that a carrier lifetime of at least 3.9 ns is required in order to reach (or exceed) a density of 1.54 × 1017 cm−3, required for net optical gain. As seen in Fig. 2a, the measured carrier lifetime at low excitations is well above this value.

In addition to low thresholds, lasing stability is an important requirement for any laser gain medium. Figure 4a shows the integrated emission intensity under constant CW excitation of 720 W cm−2 for a period of 10 min at a temperature of 80 K. Figure 4b depicts the corresponding spectra at the beginning and at the end of the measurement. A small decrease of the integrated and peak intensities of the ASE is visible, nevertheless, the stability of the emission is remarkable at such harsh excitation conditions. This demonstrates that the stability under CW excitation is comparable to the stability under pulsed excitation reported previously11,12,32,49. Additionally, we note that the wavelength of the ASE peak did not change during the experiment. The absence of such a shift, which is observed in CH3NH3PbX3 perovskites due to a redistribution of the halides50, confirms the stability of the perovskite crystal lattice with mixed cations at the A-site33,34.

Fig. 4

ASE stability at CW excitation with an excitation intensity of 720 W cm−2 at 80 K. a Integrated emission intensity over a time frame of 10 min of continuous excitation. b Spectra at the beginning of the measurement (black) and after 10 min (red)

Next, we tracked the emission properties at higher temperatures under fixed CW pumping conditions as shown in Fig. 5. All measurements were carried out at a CW pump intensity of 1512 W cm−2. As the temperature is increased, the ASE peak decreases and a larger portion of the absorbed photons is reemitted by spontaneous emission (instead of stimulated emission). The ASE peak fades out at temperatures above 120 K. At this temperature (and above), a further increase of the pump intensity could not recover the ASE peak, but rather led to a fast degradation of the PL intensity. This indicates that at higher temperatures the material degrades before the CW ASE threshold is reached. However, the fact that the ASE peaks can be observed over the full range between 80 and 120 K, is another indication that the ASE is obtained by a single crystalline phase and not due to the coexistence of different phases as in CH3NH3PbI3, which requires a very specific temperature32.

Fig. 5

ASE spectra under CW excitation at various temperatures and constant pump intensity. The amount of photons emitted into the ASE mode decreases with increasing temperature until ~120 K, after which spontaneous emission dominates. The excitation power was kept constant at 1512 W cm−2

Several approaches can be employed in order to increase the temperature range where ASE can be achieved before material degradation starts. This includes better thermal management, such as pumping the layer using photons with lower energy, closer to the bandgap, consequently introducing less heating during the thermalization of carriers to the band edges. In addition, an enhancement of the carrier lifetime and the PLQY at higher temperatures by a further improvement of the material quality should also allow for ASE generation at higher temperatures. Furthermore, the use of high-Q cavities can decrease the threshold values for laser devices compared to our ASE threshold in thin films. Our work manifests a crucial step towards the realization of a new class of laser materials, which can potentially support room-temperature CW lasing under optical pumping. In view of the high charge carrier mobilities in our material, this also raises prospects for future electrically pumped devices. Thus, a new class of low-cost and solution processable laser diodes with tunability over the full visible spectrum might be at the horizon.


Materials and sample preparation

The precursor powders PbI2 (AlfaAesar), PbBr2 (AlfaAesar), CsI (Alfa Aesar), FAI (Greatcell Solar Ltd.), and MABr (Greatcell Solar Ltd.) were mixed in a non-stoichiometric ratio of Cs0.1(MA0.17FA0.83)0.9Pb0.84(I0.84Br0.16)2.68 and dissolved in a mixture of dimethylformamide (DMF, Sigma Aldrich) and dimethyl sulfoxide (DMSO, Sigma Aldrich) in a ratio of 3:1. All chemicals and solvents were used as received without further purification. The sapphire substrates (1‶ diameter, 1 mm thick, Plano GmbH) were cleaned in an ultrasonic bath using acetone and isopropanol for 10 min each and treated by O2 plasma for 2 min at 100 W. Directly after the plasma treatment 70 µl of the solution were dynamically spin-casted at 1000 rpm for 10 s and 6000 rpm for 20 s in nitrogen atmosphere. Six seconds before the end of the spinning process, 160 μl of chlorobenzene were dropped onto the spinning sample. The resulting films were annealed at 100 °C for 60 min in N2. Afterwards, the films were post treated by imprint lithography. The imprint step used in this work is based on previously published studies35,36,37 and conducted using a commercially available nanoimprint lithography instrument (FC-150, SET) with the following recipe: A glass substrate covered with a thin layer of OrmoStamp® was pressed into the perovskite substrate with a pressure of 10 bar to form an initial contact between the mold and the substrate. This was followed by heating the system to 125 °C, the final imprint temperature. Then, the imprint pressure was raised to 125 bar for a duration of 6 min followed by the cooling of the system for a duration of 6.5 min to achieve a final temperature of ~50 °C.

ASE measurements

A schematic of the gain characterization setup is shown in Supplementary Figure S2: For the experiments under pulsed excitation, a frequency doubled Nd:YLF laser (Innolas GmbH), emitting pulses of 0.8 ns pulse duration at 532 nm was used. For the CW excitation experiments, a CW laser emitting at the same wavelength was used (Millennia, Spectra Physics). The pump intensities were controlled using variable neutral density filter wheels. The laser power was measured using a Coherent LabMax2 power meter with various power heads. The samples were mounted in an optical cryostat (Janis STVP-100) and connected via heat-conductive paste to a copper sample holder. The spot area at the sample position inside the cryostat was determined by the moving knife edge method to be 1.28 × 10−4 cm2 for the pulsed beam and 5.01 × 10−4 cm2 for the CW laser beam. The sample emission was coupled through a pair of lenses to a spectrograph (Acton Research Corporation, SpectraPro 300i, variable grating) connected to an intensified CCD camera (Princeton Research, PiMax 512).

Time resolved and temperature-dependent PL

The PL transients in Fig. 2a were recorded by a streak camera (Hamamatsu Universal C10910) coupled to a spectrometer (Acton SpectraPro SP2300). The camera was used in single sweep mode to allow for a 2 μs time window and a FWHM of the instrumental response function of 28 ns. The steady-state PL spectra shown in Fig. 2b were recorded by a fiber-coupled spectrometer (Avantes, AvaSpec-2048L). In both cases, the temperature of the sample was controlled by a closed cycle cryostat (Oxford, Optistat Dry TLEX). For the excitation, a second harmonic generator (Coherent, Chameleon Compact OPO-Vis) was used to double the frequency of a mode-locked Ti:sapphire laser (Coherent, Chameleon Ultra) with a wavelength of 960 nm, a pulse width of 140 fs and a repetition rate of 80 MHz. The repetition rate of the laser system was reduced to 400 kHz using a pulse picker (APE, pulseSelect).

Data availability

The data that support the findings of this study are available from the corresponding author upon reasonable request.


  1. 1.

    Zhang, W., Eperon, G. E. & Snaith, H. J. Metal halide perovskites for energy applications. Nat. Energy 1, 16048 (2016).

  2. 2.

    Correa-Baena, J.-P. et al. Promises and challenges of perovskite solar cells. Science 358, 739–744 (2017).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Herz, L. M. Charge-carrier mobilities in metal halide Perovskites: fundamental mechanisms and limits. ACS Energy Lett. 2, 1539–1548 (2017).

    CAS  Article  Google Scholar 

  4. 4.

    Brenes, R. et al. Metal halide Perovskite polycrystalline films exhibiting properties of single crystals. Joule 1, 155–167 (2017).

    CAS  Article  Google Scholar 

  5. 5.

    Colella, S., Mazzeo, M., Rizzo, A., Gigli, G. & Listorti, A. The bright side of Perovskites. J. Phys. Chem. Lett. 7, 4322–4334 (2016).

    CAS  Article  Google Scholar 

  6. 6.

    Sutherland, B. R. & Sargent, E. H. Perovskite photonic sources. Nat. Photonics 10, 295–302 (2016).

    ADS  CAS  Article  Google Scholar 

  7. 7.

    Cho, H. et al. Overcoming the electroluminescence efficiency limitations of perovskite light-emitting diodes. Science 350, 1222–1225 (2015).

    ADS  CAS  Article  Google Scholar 

  8. 8.

    Tan, Z.-K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 1–6 (2014).

    ADS  Article  Google Scholar 

  9. 9.

    Lin, K. et al. Perovskite light-emitting diodes with external quantum efficiency exceeding 20 per cent. Nature 562, 245–248 (2018).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Kovalenko, M. V., Protesescu, L. & Bodnarchuk, M. I. Properties and potential optoelectronic applications of lead halide perovskite nanocrystals. Science 358, 745–750 (2017).

    ADS  CAS  Article  Google Scholar 

  11. 11.

    Xing, G. et al. Low-temperature solution-processed wavelength-tunable perovskites for lasing. Nat. Mater. 13, 476–480 (2014).

    ADS  CAS  Article  Google Scholar 

  12. 12.

    Brenner, P. et al. Triple cation mixed-halide perovskites for tunable lasers. Opt. Mater. Express 7, 4082 (2017).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Zhang, Q. et al. Advances in small Perovskite-based lasers. Small Methods 1, 1700163 (2017).

    Article  Google Scholar 

  14. 14.

    Suárez Alvarez, I. Active photonic devices based on colloidal semiconductor nanocrystals and organometallic halide perovskites. Eur. Phys. J. Appl. Phys. 75, 30001 (2016).

    ADS  Article  Google Scholar 

  15. 15.

    Wang, K., Wang, S., Xiao, S. & Song, Q. Recent advances in Perovskite micro- and nanolasers. Adv. Opt. Mater. 6, 1800278 (2018).

    Article  Google Scholar 

  16. 16.

    Li, G., Price, M. & Deschler, F. Research update: challenges for high-efficiency hybrid lead-halide perovskite LEDs and the path towards electrically pumped lasing. APL Mater. 4, 091507 (2016).

    ADS  Article  Google Scholar 

  17. 17.

    Veldhuis, S. A. et al. Perovskite materials for light-emitting diodes and lasers. Adv. Mater. 28, 6804–6834 (2016).

    CAS  Article  Google Scholar 

  18. 18.

    Quan, L. N., García de Arquer, F. P., Sabatini, R. P. & Sargent, E. H. Perovskites for light emission. Adv. Mater. 30, 1801996 (2018).

    Article  Google Scholar 

  19. 19.

    Harwell, J. R., Whitworth, G. L., Turnbull, G. A. & Samuel, I. D. W. Green Perovskite distributed feedback lasers. Sci. Rep. 7, 11727 (2017).

    ADS  CAS  Article  Google Scholar 

  20. 20.

    Chen, S. & Nurmikko, A. Stable green Perovskite vertical-cavity surface-emitting lasers on rigid and flexible substrates. ACS Photonics 4, 2486–2494 (2017).

    CAS  Article  Google Scholar 

  21. 21.

    Pust, P., Schmidt, P. J. & Schnick, W. A revolution in lighting. Nat. Mater. 14, 454–458 (2015).

    ADS  CAS  Article  Google Scholar 

  22. 22.

    Auf Der Maur, M., Pecchia, A., Penazzi, G., Rodrigues, W. & Di Carlo, A. . Efficiency drop in green InGaN/GaN light emitting diodes: the role of random alloy fluctuations. Phys. Rev. Lett. 116, 1–5 (2016).

    Article  Google Scholar 

  23. 23.

    Strauss, U. et al. in GaInN laser diodes from 440 to 530 nm: a performance study on single-mode and multi-mode R&D designs, Proc. SPIE vol. 10123 (eds. Belyanin, A. A. & Smowton, P. M.) 101230A (International Society for Optics and Photonics, 2017).

  24. 24.

    Fan, F. et al. Continuous-wave lasing in colloidal quantum dot solids enabled by facet-selective epitaxy. Nature 544, 75–79 (2017).

    ADS  CAS  Article  Google Scholar 

  25. 25.

    Sandanayaka, A. S. D. et al. Toward continuous-wave operation of organic semiconductor lasers. Sci. Adv. 3, e1602570 (2017).

    ADS  Article  Google Scholar 

  26. 26.

    Grim, J. Q. et al. Continuous-wave biexciton lasing at room temperature using solution-processed quantum wells. Nat. Nanotechnol. 9, 891–895 (2014).

    ADS  CAS  Article  Google Scholar 

  27. 27.

    Yang, Z., Pelton, M., Fedin, I., Talapin, D. V. & Waks, E. A room temperature continuous-wave nanolaser using colloidal quantum wells. Nat. Commun. 8, 143 (2017).

    ADS  Article  Google Scholar 

  28. 28.

    Evans, T. J. S. et al. Continuous-wave lasing in cesium lead bromide perovskite nanowires. Adv. Opt. Mater. 6, 1–7 (2018).

    Article  Google Scholar 

  29. 29.

    Su, R. et al. Room-temperature polariton lasing in all-inorganic Perovskite nanoplatelets. Nano Lett. 17, 3982–3988 (2017).

    ADS  CAS  Article  Google Scholar 

  30. 30.

    Jia, Y. et al. Diode-pumped organo-lead halide perovskite lasing in a metal-clad distributed feedback resonator. Nano Lett. 16, 4624–4629 (2016).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Cadelano, M. et al. Can trihalide lead Perovskites support continuous wave lasing? Adv. Opt. Mater. 3, 1557–1564 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Jia, Y., Kerner, R. A., Grede, A. J., Rand, B. P. & Giebink, N. C. Continuous-wave lasing in an organic–inorganic lead halide perovskite semiconductor. Nat. Photonics 11, 784–788 (2017).

    ADS  CAS  Article  Google Scholar 

  33. 33.

    Saliba, M. et al. Cesium-containing triple cation perovskite solar cells: improved stability, reproducibility and high efficiency. Energy Environ. Sci. 9, 1989–1997 (2016).

    CAS  Article  Google Scholar 

  34. 34.

    McMeekin, D. P. et al. A mixed-cation lead mixed-halide perovskite absorber for tandem solar cells. Science 351, 151–155 (2016).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Pourdavoud, N. et al. Photonic nanostructures patterned by thermal nanoimprint directly into organo-metal halide Perovskites. Adv. Mater. 29, 1605003 (2017).

    Article  Google Scholar 

  36. 36.

    Mayer, A. et al. Thermal nanoimprint to improve the morphology of MAPbX3 (MA=methylammonium, X=I or Br). J. Vac. Sci. Technol. B 35, 06G803 (2017).

    Article  Google Scholar 

  37. 37.

    Bar‐On, O., Brenner, P., Lemmer, U. & Scheuer, J. Micro lasers by scalable lithography of metal‐halide perovskites. Adv. Mater. Technol. 3, 1800212 (2018).

    Article  Google Scholar 

  38. 38.

    Qin, L. et al. Enhanced amplified spontaneous emission from morphology-controlled organic–inorganic halide perovskite films. RSC Adv. 5, 103674–103679 (2015).

    CAS  Article  Google Scholar 

  39. 39.

    Siegman, A. E. Lasers. (Univ. Science Books, Sausalito, CA, USA, 1986).

    Google Scholar 

  40. 40.

    Samuel, I. D. W., Namdas, E. B. & Turnbull, Ga. How to recognize lasing. Nat. Photonics 3, 546–549 (2009).

    ADS  CAS  Article  Google Scholar 

  41. 41.

    Ning, C. Z. What is laser threshold? IEEE J. Sel. Top. Quantum Electron. 19, 1503604–1503604 (2013).

    ADS  Article  Google Scholar 

  42. 42.

    Sutherland, B. R., Hoogland, S., Adachi, M. M., Wong, C. T. O. & Sargent, E. H. Conformal organohalide perovskites enable lasing on spherical resonators. ACS Nano 8, 10947–10952 (2014).

    CAS  Article  Google Scholar 

  43. 43.

    Coldren, L. A., Corzine, S. W. & Mašanović, M. L. Diode Lasers and Photonic Integrated Circuits. Series in Microwave and Optical Engineering. (John Wiley & Sons, Inc., Hoboken, NJ, USA, 2012).

    Google Scholar 

  44. 44.

    Milot, R. L., Eperon, G. E., Snaith, H. J., Johnston, M. B. & Herz, L. M. Temperature-dependent charge-carrier dynamics in CH3NH3PbI3 Perovskite thin films. Adv. Funct. Mater. 25, 6218–6227 (2015).

    CAS  Article  Google Scholar 

  45. 45.

    Stranks, S. D. et al. Recombination kinetics in organic–inorganic Perovskites: excitons, free charge, and subgap states. Phys. Rev. Appl. 2, 1–8 (2014).

    Article  Google Scholar 

  46. 46.

    Braly, I. L. et al. Hybrid perovskite films approaching the radiative limit with over 90% photoluminescence quantum efficiency. Nat. Photonics 12, 355–361 (2018).

    ADS  CAS  Article  Google Scholar 

  47. 47.

    Noginov, M. A., Fowlkes, I. N., Zhu, G. & Novak, J. Random laser thresholds in cw and pulsed regimes. Phys. Rev. A 70, 043811 (2004).

    ADS  Article  Google Scholar 

  48. 48.

    Bernard, M. G. A. & Duraffourg, G. Laser conditions in semiconductors. Phys. Status Solidi 1, 699–703 (1961).

    CAS  Article  Google Scholar 

  49. 49.

    Brenner, P. et al. Highly stable solution processed metal-halide perovskite lasers on nanoimprinted distributed feedback structures. Appl. Phys. Lett. 109, 141106 (2016).

    ADS  Article  Google Scholar 

  50. 50.

    Hoke, E. T. et al. Reversible photo-induced trap formation in mixed-halide hybrid perovskites for photovoltaics. Chem. Sci. 6, 613–617 (2015).

    CAS  Article  Google Scholar 

Download references


The authors are grateful to the all members of the perovskite taskforce at KIT. Funding is gratefully acknowledged from the following sources: (i) the Deutsche Forschungsgemeinschaft via project LE 878/17-1; (ii) the Helmholtz Research Program Science and Technology of Nanosystems (STN), the Initiating and Networking funds of the Helmholtz Association (HYIG of Dr. U.W. Paetzold, Recruitment Initiative of Prof. B.S. Richards, the Helmholtz Energy Materials Foundry (HEMF); and PEROSEED project); (iii) the Karlsruhe School of Optics & Photonics (KSOP) as well as (iv) the 373 Excellence Cluster “3D Matter Made to Order (3DMM2O)”.

Author information




The project was designed and conceptualized by P.B., U.W.P, I.A.H. and U.L. P.B. performed the ASE and AFM measurements, analyzed data and wrote the first draft of the paper. O.B.-O. performed imprinting of perovskites films and discussed the results. M.J. performed time-resolved measurements and temperature-dependent PL spectroscopy. I.A.H. assisted in the experimental work. B.S.R., U.W.P., I.A.H, J.S., and U.L. supervised the overall conception. All authors contributed to the discussion of the results and in writing the manuscript.

Corresponding author

Correspondence to Uli Lemmer.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Brenner, P., Bar-On, O., Jakoby, M. et al. Continuous wave amplified spontaneous emission in phase-stable lead halide perovskites. Nat Commun 10, 988 (2019).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing