Three-dimensional monolithic integration in flexible printed organic transistors

Abstract

Direct printing of thin-film transistors has enormous potential for ubiquitous and lightweight wearable electronic applications. However, advances in printed integrated circuits remain very rare. Here we present a three-dimensional (3D) integration approach to achieve technology scaling in printed transistor density, analogous to Moore’s law driven by lithography, as well as enhancing device performance. To provide a proof of principle for the approach, we demonstrate the scalable 3D integration of dual-gate organic transistors on plastic foil by printing with high yield, uniformity, and year-long stability. In addition, the 3D stacking of three complementary transistors enables us to propose a programmable 3D logic array as a new route to design printed flexible digital circuitry essential for the emerging applications. The 3D monolithic integration strategy demonstrated here is applicable to other emerging printable materials, such as carbon nanotubes, oxide semiconductors and 2D semiconducting materials.

Introduction

Direct printing of thin-film transistors on plastic foil has been shown to be a highly promising technology for fabricating ubiquitous and lightweight wearable electronic applications1. The potential of this additive manufacturing technique for low-cost mass production, rapid prototyping of small series, and low-temperature fabrication on flexible substrates renders it an attractive alternative to conventional fabrication methods for electronics2,3. Solution-processable semiconductor materials in the forms of organic compounds, graphene, carbon nanotubes, and oxides have been developed to be compatible with current printing techniques4,5,6,7. Among these materials, organic semiconductor (OSC) small molecules or polymers have been distinguished from other candidates as softer materials and have been successfully demonstrated in many flexible printed devices, such as transistors in an array8, nonvolatile memory cells9, electrochemical transistor-based biosensors for biological research10, display light-emitting diodes11, and solar cells for energy harvesting12.

Nevertheless, advances in printed organic integrated circuits (ICs) remain very rare. The primary challenge is the lack of technology scaling in printed transistors. The scaling capability of conventional silicon transistors, i.e., Moore’s law, which calls for the transistor density to be doubled every 18 months, has made ICs an excellent example of a general purpose technology13. Although organic transistors patterned by photolithography or shadow mask evaporation have been applied to microprocessors and smart tags14,15, most functional organic ICs fabricated by printing have less than a hundred transistors16,17,18,19,20,21. The progress in printed organic ICs has been slow because the low resolution (typically 10–100 μm) and large feature size (typically 100–200 μm) of current printing techniques have limited the transistor counts in processable areas22. Emerging flexible printed IC applications beyond displays are now requiring technology scaling to increase transistor density, which is analogue to the Moore’s law.

Another challenge in using flexible printed organic transistors in IC design is their low device performance. In particular, flexible printed organic transistors still suffer from partial depletion of the OSC bulk and low transconductance gm. Partial depletion, which indicates the accumulation of the majority of carriers in the OSC bulk even when the gate-to-source voltage VGS is zero, leads to undesirable effects: decreased intrinsic gain, static noise margin, and drain current ID on-off ratio and increased subthreshold swing SS (dec/mV) and standby power23. Moreover, low gm is mainly attributed to the low carrier mobilities of OSC materials. Instead of a reduction in the channel length, which is highly limited in printed organic transistors24, the gm can be easily elevated by widening the channel width. However, changing the channel geometry necessitates the sacrifice of considerable substrate area.

We previously introduced a three-dimensional (3D) organic transistor structure with a shared gate joining two complementary transistors using drop-on-demand inkjet printing20. The study reported an array of the vertically stacked complementary transistors and their logic gates. Building on the approach, here we propose the 3D monolithic integration of flexible printed organic transistors to realize technology scaling and performance enhancement. In addition, we adopt a dual-gate configuration in the 3D transistor-on-transistor structure for the improvement of their electrical characteristics such as SS, transconductance, and ID on-off ratio. The 3D monolithic integration of dual-gate organic transistors is successfully implemented on a plastic foil with a record density of 60 printed transistors per square centimetre. These transistors exhibits high yield, uniformity, and year-long stability, which prove that this technology is extendable to large-scale printed electronics. By interconnecting those 3D-integrated dual-gate transistors, we finally propose a 3D universal logic gate and its array as a new facile route to design printed digital circuitries that are essential for emerging flexible electronics applications.

Results

3D device configuration

To provide a proof of principle for the 3D monolithic integration, we first demonstrate dual-gate and transistor-on-transistor configurations in printed complementary transistors by vertically stacking functional layers. Starting from a conventional single-bottom-gate transistor on a flexible plastic sheet (Fig. 1a), we fabricated a dual-gate transistor by depositing a top-gate dielectric and inkjet-printing a top-gate Ag electrode on the top (Fig. 1b). This 3D integration of the top and bottom-gate structures enhances the control of the channel by gating on both sides and maximizes the utilization of the transistor. We adopted this dual-gate structure for complementary OSCs: a n-type benzobis(thiadiazole) derivative (TU-3) and a p-type small molecule, dithieno[2,3-d;2′,3′-d′]benzo[1,2-b;4,5-b′]dithiophene (DTBDT-C6) (the OSC chemical structures and the polarized microscopic images are provided in Supplementary Fig. 1). We then implemented a complementary stacked two-transistor (2-T) device by building a dual-gate p-type transistor on top of the n-type transistor (Fig. 1c). The in-between printed gate electrode was shared by the two complementary transistors. The further scalability of the 3D integration was shown by vertically stacking another n-type dual-gate transistor on top of the stacked 2-T device (Fig. 1d). The functional layers of the stacked three-transistor (3-T) device were monolithically integrated via simple repeats of single transistor fabrication without an additional process for 3D integration. These stacked 2-T and 3-T devices are proposed as inverters and universal logic gates, respectively, which are the basic building blocks of fully flexible digital circuits on a plastic sheet.

Fig. 1
figure1

3D monolithic integration in flexible printed transistors. a, b Printed single-gate and dual-gate organic transistors. c, d 3D-integrated two (n-/p-type, stacked 2-T) and three (n-/p-/n-type, stacked 3-T) complementary dual-gate organic transistors with shared gate electrodes. All the films were printed except for the Parylene dielectric layers

The stacked 3-T device configuration has 24 functional layers: a plastic substrate, seven conductor layers, three OSC layers, seven Parylene layers (one basement and six gate insulator films), three charge injection self-assembled monolayers, and three bank layers. For all the devices, the source/drain (S/D) and gate (G) electrodes were inkjet-printed, and the semiconducting inks were dispenser-printed within a rectangular hydrophobic fluoropolymer bank that was also made by dispenser-printing. Figure 2a shows optical images of all the metal layers inkjet-printed on each dielectric layer, which can be interconnected on the top floor through laser-drilled via-holes. The availability of the seven metal layers, which is an exceptional number in printed transistors, is key to enabling complex IC designs. A polarized microscopy image of the vertically overlapping semiconducting layers in the transistor area is shown in Fig. 2b. As seen in atomic force microscopy (AFM) data of Fig. 2c, the repeats of the printing processes produced a rough surface morphology in the accumulated polycrystalline semiconductor layers and Ag electrodes (the AFM topology images of the Parylene-coated plastic substrate and individual complementary OSCs can be found in Supplementary Fig. 2). However, conformal chemical vapour deposition of the Parylene dielectrics provided pinhole-free electrical insulation and strong chemical resistance, leading to high yield and uniform device performances. A scanning electron microscopy (SEM) image of the stacked 3-T device confirms that all the functional layers were conformally deposited as designed without physical damage (Fig. 2d). Detailed information on material preparation, inkjet printing, and device fabrication is described in the Methods section. The entire fabrication process of the stacked 3-T devices is summarized in Supplementary Table 1.

Fig. 2
figure2

Images of a stacked 3-T device. a Sequential images of the process of printing seven metal layers (scale bar is 1 mm). b A polarized microscopy image of the transistor area (scale bar is 200 μm). c A topographic AFM image (scan area is 100 × 100 μm) measured on top of the channel area. The inset graph shows the profile along the cross-section line. d Cross-sectional SEM image of the stacked 3-T device (M1-7: metal layers, GI1-6: dielectric insulator layers, OSC1-3: organic semiconductor layers, scale bar is 250 nm, Pt was sputtered on the top prior to the SEM measurement)

Characteristics of 3D-integrated dual-gate transistors

The dual-gate configuration yielded several advantages that helped overcome the chronic problems of conventional single-gate organic transistors. It provides a fully depleted OSC bulk and enhanced gm due to the effective control of charge transport within the bulk of the semiconductor beyond the highly accumulated region several nanometres in depth25. The electrical characteristics of n-type and p-type printed dual-gate transistors, as presented in Fig. 3a, are exceptionally improved compared to those of single-bottom-gate and single-top-gate transistors (schematic cross-section and microscopic images of the transistors are shown in Supplementary Fig. 3). Both gates of the dual-gate transistors were electrically connected for the VGS sweeps. The printed transistor properties were highly uniform and consistent (Supplementary Fig. 4). To demonstrate the compatibility with low-power portable electronics, a relatively low supply voltage VDD of 5 V was used. Surprisingly, for the n-type transistors, the partially depleted OSC behaviour observed in the single-gate transistors was effectively removed in the dual-gate transistors. The turn-on gate voltage shifted from negative to near zero, thereby reducing the subthreshold leakage IOFF. In this study, we defined the IOFF as an ID at zero VGS, not as the minimum ID in a negative bias as often used in the literature, because IOFF is a practical indicator of how much power a transistor wastes in standby when considering actual circuit operations.

Fig. 3
figure3

Device characteristics. a |ID|–VGS transfer characteristics of the n-type and p-type organic transistors in single-gate (bottom-gate and top-gate) and dual-gate configurations. b The subthreshold swings and c the ID on-off ratios. d The extracted carrier mobilities in the 3D-integrated complementary organic transistors. e The channel length dependency of the extracted carrier mobilities. Error bars represent standard deviation

In addition, the dual-gate transistors had higher gm values than single-gate transistors in both complementary OSCs. The improved gating of the fully depleted dual-gate transistors also resulted in the n-type and p-type transistors having a low SS of ≈110 and ≈80 mV dec−1, respectively, which are far lower than those of the single-gate transistors (Fig. 3b). These values are competitive with the lowest SS values reported to date for complementary organic transistors26. The low SS enabled a near-zero threshold voltage VTH of 0.27 and −0.30 V on average for the n-type and p-type transistors, respectively. The increased gm and reduced IOFF of the complementary dual-gate transistors led to a considerable improvement in the drain current on-off ratio ION/IOFF (Fig. 3c). The average ION/IOFF values of the n-type and p-type dual-gate transistors were increased by ≈710 and ≈470% compared to those of the bottom-gate transistors, respectively, and by ≈1300 and ≈60% compared those of the top-gate transistors. The improvements in the IOFF, gm, and SS properties are analogous to the advantages observed in conventional fully depleted silicon-on-insulator multi-gate transistors27. Importantly, we first verified that all these benefits of full depletion, which were found in conventional dual-gate silicon transistors, are also observed in printed complementary organic dual-gate transistors on a flexible substrate. The information on the channel lengths L and widths W, the extracted carrier mobilities, and the threshold voltages is provided in Supplementary Table 2 with the average values and standard deviations.

Ensuring that the 3D stacking process including consecutive printing and annealing steps does not affect the performance of transistors on the lower floors is important. The carrier mobilities of the stand-alone and stacked dual-gate transistors, which were extracted from |ID|1/2VGS transfer characteristics in the saturation regime, are shown in Fig. 3d. It is noteworthy that there was no significant performance degradation during the 3D stacking process in either complementary dual-gate transistor. In the stacked 3-T device, for example, the carrier mobility of the n-type transistor on the first floor (1F), which went through 14 thermal annealing steps, was almost identical to that of the n-type transistor on the top floor (3F). This result proves that the additive manufacturing process of this work is robust and extendable to further 3D integration of printed transistors.

We observed that the extracted carrier mobilities of the n-type transistors decreased with shortening the channel length, while those of the p-type devices remained unchanged (Fig. 3e). The extracted mobility values are influenced by contact resistance28. Thus, we hypothesized that the behaviour of the n-type transistors was dominated by charge injection due to high contact resistance. To support this, we measured and analyzed the contact resistance of the transistors using the transmission line method. As can be seen in Supplementary Fig. 5a, the contact resistance of the n-type dual-gate transistors was 21.4 kΩ cm at VGS = 5 V which was ten times higher than that of the p-type dual-gate transistors (2.2 kΩ cm at VGS = −5 V). The n-type transistors showed the functional dependence of the contact resistance with the gate bias, which resulted in the improvement of the extracted mobility, whereas the carrier mobilities of the p-type transistors were weakly dependent on the gate bias due to sufficiently low contact resistance (Supplementary Fig. 5b). In addition, the n-type dual-gate devices exhibited highly asymmetrical performance between top-gate and bottom-gate operation modes due to the difference in charge injection efficiency between the staggered top-gate structure and the bottom-gate structure in the dual-gate transistors (Fig. 4a). In contrast, remarkably symmetrical dual-gate operation was exhibited for the p-type devices because of the high charge ejection efficiency (Fig. 4b).

Fig. 4
figure4

Dual-gate complementary transistor operations. a Saturation transfer characteristics (VDS = 5 V) of the n-type dual-gate transistor in top-gate (left) and bottom-gate (right) sweeping modes (VTG: top-gate voltage, VBG: bottom-gate voltage). b Saturation transfer characteristics (VDS = −5 V) of the p-type dual-gate transistor in top-gate (left) and bottom-gate (right) modes

3D-integrated flexible circuits

Next, we implemented a 3D inverter using the stacked 2-T device, the two drain nodes of which are interconnected through a via-hole (the schematic circuit is seen in Fig. 5a). The different combinations of gate connections in the stacked dual-gate complementary transistors were able to maximize static noise margin of the 3D inverter. The inverter output-input voltage characteristics are shown in Fig. 5b according to the four combinations of input gate connections. The inverter switching threshold was optimized to be 50% of VDD when the p-type transistor was operated in bottom-gate mode and the n-type transistor was operated in dual-gate mode (VG1 = VG2 = VIN, VG3 = 5 V). Furthermore, we explored the dynamic operation of the 3D-integrated complementary dual-gate transistors by fabricating a 7-stage ring oscillator. The circuit consists of seven inverters for the ring oscillation operation and two inverters for the voltage buffering. The ring oscillator operated with the supply voltage VDD varying between 1 and 15 V. The gate delay was 13 ms at VDD = 1 V and 340 μs at VDD = 15 V. Figure 5c depicts the schematic circuit and the oscillation operation at 48.5 Hz when the VDD is 5 V.

Fig. 5
figure5

Stacked 2-T dual-gate devices. a Schematic circuit of the 3D-integrated dual-gate inverter (VG1, VG2, VG3: gate inputs, IDD: static current from the source). b Voltage transfer characteristics (left) and static currents (right) of the inverter operation according to the combinations of electrical gate connections. c Schematic circuit of the ring oscillator which is composed of seven 3D-integrated dual-gate inverters and its oscillation operation. The buffer output stage consists of serially connected two inverters, where the transistor W of the last inverter is designed to be eight times larger than that of the others

We demonstrated a universal logic gate NAND in a 3D configuration by interconnecting transistors in the stacked 3-T device. Unlike a conventional NAND consisting of four complementary transistors, we implemented the NAND gate by using the three vertically stacked dual-gate transistors (Fig. 6a). The independent gate control enabled one p-type transistor in the middle of the stacked 3-T device to operate as two p-type transistors connected in parallel. In the 3D NAND gate, the symmetric bottom-gate and top-gate mode operations of the p-type dual-gate transistor made the output characteristics for the two inputs almost identical (Fig. 6b). To optimize the static noise margin in the 3D NAND gates, we matched the ID of the dual-gate n-type transistors in dual-gate mode to that of the dual-gate p-type transistor in bottom-gate or top-gate mode by adjusting the thickness of dielectric layers as well as the channel lengths. The two output characteristics exhibited ideal switching operations.

Fig. 6
figure6

3D NAND digital circuit design based on stacked 3-T dual-gate devices. a Schematic circuits of a conventional NAND gate and a proposed 3D NAND gate. b DC VOUTVIN characteristics of a 3D NAND gate. c 3D NAND array-based logic design (scale bar is 2 mm). d DC VINVOUT characteristics of a 1-input NOT gate and 2-input (A and B) logic gates (OR, AND, NOR, XOR, and XNOR) implemented by interconnecting 3D NANDs. A fixed voltage (0 or 5 V) is applied to one port while a voltage input on the other port is swept. e A large-scale flexible logic circuitry implemented by using a 12 × 8 3D NAND gate array (scale bar is 4 mm)

We then introduce a programmable 3D NAND array as a new approach for printed organic digital IC design on a flexible film. The array of the uncommitted gates can be quickly configured for different logic functions by routing them (Fig. 6c). The pitch of 3 × 2.2 mm between the 3D NAND gates was determined by considering the space for interconnection routing. The programmable devices allow end users to share a common platform that can be customized with much reduced time and cost. We implemented the first examples of programmable 3D NAND arrays of digital logic circuits, including NOT, AND, OR, NOR, XOR, and XNOR (Fig. 6d). The fabrication process was scaled to produce a large-scale array of 3D NAND gates (Fig. 6e). This work has a record transistor density of approximately 60 transistors per square centimetre for printed ICs when the 3D NAND design is considered to consist of four transistors (Fig. 7)16,17,20,21,29,30,31,32,33,34,35,36,37,38,39,40. Based on this technology, we could fabricate up to ≈2700 programmable transistors on the size of a standard credit card (85.60 × 53.98 mm), which is compatible with the transistor count of the first commercial 4-bit microprocessor.

Fig. 7
figure7

Transistor density trend of printed organic circuits fabricated by various printing techniques

Device reliabilities

Finally, we tested the reliabilities of the 3D-integrated dual-gate complementary transistors fabricated on a flexible substrate under given mechanical, electrical, and environmental stresses. When attached on a curved surface with a bend radius of 8 mm, the dual-gate complementary transistors of a stacked 3-T device had slight changes in their static transfer characteristics (Fig. 8a). In addition, they exhibited highly stable operation when biased at VGS = ±5 V for 104 s (Supplementary Fig. 6). Compared to those of the n-type and p-type dual-gate transistors before the bias stress tests, the ION values of the n-type and p-type dual-gate transistors after the bias stress test were changed by 3 and 5%, respectively, and their VTH shifts were negligible (Fig. 8b). Remarkably, the electrical operations of the printed complementary organic transistors were maintained for 1 year with acceptable performance changes when stored in a dry ambient environment (Fig. 8c). When we observed the corresponding n-type dual-gate transistors 4 months and 1 year after the fabrication, the μn was decreased by 20 and 50%, and the VTH was shifted by 0.4 and 0.7 V, respectively. The p-type transistors exhibited exceptionally small changes in their device parameters: at 1 year after fabrication, the μp decreased by only 5%, and the VTH was shifted by less than 0.1 V. In this long-term stability test, we rarely found a significant difference between the stand-alone and stacked devices or between the single-gate and dual-gate transistors (Supplementary Fig. 7). Further reliability tests under temperature and humidity stress conditions were conducted. Both types of transistors were heated from 30 to 150 °C and cooled down to 30 °C through the consecutive five thermal stress steps and their transfer characteristics were measured at the end of every step (Fig. 8d). The printed transistors exhibited severe performance degradation only under the thermal stress of 150 °C. When exposed to a high humidity environment (90% rh, 30 °C) for 1 day, they rarely exhibited significant changes in the transfer characteristics (Fig. 8e).

Fig. 8
figure8

Mechanical, electrical, long-term, and environmental reliabilities a Images of the stacked 3-T device under bending test (white dotted area is magnified) and its saturation transfer characteristics as bent on a curved surface (scale bars in the top and bottom images are 1 cm and 1 mm, respectively). b Shift of the saturation transfer characteristics of the printed stand-alone complementary transistors after electrical bias stress for 10,000 s (at VGS = VDS = 5 V for the n-type and −5 V for the p-type). c Year-long observation on the carrier mobilities and threshold voltages of the stand-alone and stacked 2-T devices (μn, μp: carrier mobility, μn0, μp0: initial carrier mobility, VTH,n, VTH,p: threshold voltage, error bars represent standard deviation). d Shift of the saturation transfer characteristics of the complementary dual-gate transistors under consecutive five thermal stress steps. e Shift of the saturation transfer characteristics of the complementary dual-gate transistors under a humid environment (90% rh, 30 °C) for 24 h (rh: relative humidity)

Discussion

The 3D monolithic integration is a promising strategy for achieving technology scaling while enhancing device performance in flexible printed transistors. This study proved the feasibility of the continuous stacking of printed complementary transistors by demonstrating both ‘p-type-on-n-type’ and ‘n-type-on-p-type’ fabrication manners. We anticipate that this approach will open up possibilities for the design and production of innovative flexible printed ICs for internet of everything, wearable healthcare monitoring and smart packaging, where high device performance and the integration of hundreds of transistors into a limited plastic sheet are essential requirements. We also believe that the 3D monolithic integration strategy can extend to other printable functional materials, such as carbon nanotubes, oxide semiconductors, and 2D materials.

Methods

Material preparation

All the organic transistors used in this work were fabricated on 125 μm-thick polyethylene naphthalate (Teonex PEN, DuPont) films. A hydrocarbon-based Ag-nanoparticle ink containing 55 wt% Ag nanoparticles with an average diameter of 7 nm in tetradecane (Nanopaste NPS-JL, Harima Chemicals, Inc.) was used as a conductive metal ink. The Ag nanoparticles have a relatively low sintering temperature of 120 °C, which was critical for the use of the flexible PEN substrate, whose glass transition temperature is 122 °C. To modify the work function of the printed Ag contact electrodes by self-assembled monolayer (SAM) treatment, 4-methylbenzenethiol (4-MBT) and pentafluorobenzenethiol (PFBT) were prepared in 10 mM and 30 mM solutions, respectively, using isopropanol. For the n-type semiconductor ink, an electron-transporting small-molecule (TU-3, Future Ink Corporation) was prepared in a 0.045 wt% solution using 1-methylnaphthalene (TCI Co., Ltd.) as the solvent. For the p-type semiconductor ink, a hole-transporting small molecule, dithieno[2,3-d;2’,3’-d’]benzo[1,2-b;4,5-b’]dithiophene (DTBDT-C6, Tosoh Corporation) and polystyrene (PS) were dissolved in mesitylene at concentrations of 0.6 and 0.2 wt%, respectively. Observation with polarized microscopy showed that the printed n-type semiconductor TU-3 pattern has a number of small crystal grains, while the PS-blended p-type semiconductor DTBDT-C6 pattern shows a highly crystalline morphology. A hydrophobic fluoropolymer (Teflon AF1600, DuPont) prepared in a 1 wt% solution using perfluorotributylamine (Fluorinert FC-43, 3 M) as the solvent was used for surface energy modification to precisely define the semiconductor area. All the semiconductor and metal inks were filtered by using polytetrafluoroethylene membrane filters with a 0.45 μm pore size. For the conformal deposition of dielectric layers, which is critical for high-yield device fabrication processes, chemical vapour deposition (CVD) of a poly(p-xylylene) derivative (Parylene diX-SR, KISCO Ltd.) was used.

Device fabrication

For the fabrication of n-type dual-gate organic transistors, a 1 μm-thick Parylene film was formed on a 125 μm-thick PEN substrate surface by CVD to provide a controlled surface condition in the following inkjet printing step. On the Parylene-coated surface, bottom-gate electrodes were inkjet-printed using an Ag-nanoparticle ink and a drop-on-demand inkjet printer. Then, a bottom-gate dielectric Parylene film was conformally deposited to a thickness of 180 nm by the CVD process. Pairs of Ag-nanoparticle S/D parallel lines were inkjet-printed on the Parylene dielectric layer. Using a dispenser, a hydrophobic fluoropolymer, Teflon, was printed along the rectangular outlines of the transistor active areas to store OSC ink inside. For the work function modification of the printed S/D electrodes by using SAM treatment, the sample was dipped into 4-MBT solution and then rinsed. An n-type semiconductor TU-3 ink was printed by a dispenser to fill the inside of the Teflon bank area. Again, a 180 nm-thick Parylene film was conformally formed as a top-side dielectric layer. The n-type transistor fabrication is finished by inkjet-printing top-gate electrodes. To fabricate the p-type transistors, bottom-gate electrodes of the p-type transistors were printed on the same surface. Then, a 360 nm-thick bottom-gate dielectric Parylene film, Ag S/D electrodes, Teflon bank lines, a PFBT SAM, p-type OSC DTBDT-C6 patterns, a 360 nm-thick top-gate dielectric Parylene film, and top-gate electrodes were formed sequentially using the same fabrication processes. The stand-alone p-type organic transistors were not directly stacked on the n-type organic transistors but instead were fabricated next to the n-type transistors.

Inkjet printing of Ag nanoparticles

A drop-on-demand inkjet printer (DMP 2831, Fujifilm Dimatix) was used to print different types of Ag-nanoparticle electrodes, such as source/drain, gate, and routing interconnection. The inkjet printer was equipped with a cartridge having 16 piezo-driven nozzles for ejecting 10pl volume droplets (orifice diameter = 21.5 μm), and only a single nozzle was used for accurate and stable printing. The nozzle temperature was set at 40 °C. The positioning repeatability of the printer (±25 μm) indicates pattern-to-pattern alignment resolution in the stacking process of the functional layers. In this work, up to seven metal layers were constructed for 3D-integrated complementary organic transistors, and the layout of each layer was designed considering the maximum positioning error in order to not go beyond the alignment margin.

Device characterization

All the static (or DC) characteristic measurements of the printed devices were conducted by using a semiconductor parameter analyser (Keithley, 4200-SCS). The output of the 7-stage ring oscillator was measured by an oscilloscope (Tektronix, DPO2024B). The carrier mobility values of this work were extracted by fitting ID1/2VGS curves in saturation regime with the following device parameters: dielectric constant, dielectric thickness, and W/L. A stylus profiler (Bruker, Dektak XT) was used to measure the thicknesses and roughness of thin films. The dielectric constant of the Parylene dielectric (4.1) was measured with an LCR meter (NF Corporation, ZM2376) at the lowest possible frequency (100 Hz) to rule out carrier mobility overestimation due to slow polarization.

Data availability

The data that support the findings of this study are available from J.K. and S.J. on reasonable request.

References

  1. 1.

    Wang, S. et al. Skin electronics from scalable fabrication of an intrinsically stretchable transistor array. Nature 555, 83–88 (2018).

    ADS  CAS  Article  Google Scholar 

  2. 2.

    Baeg, K.-J., Caironi, M. & Noh, Y.-Y. Toward printed integrated circuits based on unipolar or ambipolar polymer semiconductors. Adv. Mater. 25, 4210–4244 (2013).

    CAS  Article  Google Scholar 

  3. 3.

    Kang, B., Lee, W. H. & Cho, K. Recent advances in organic transistor printing processes. ACS Appl. Mater. Interfaces 5, 2302–2315 (2013).

    CAS  Article  Google Scholar 

  4. 4.

    Lim, J. A., Lee, H. S., Lee, W. H. & Cho, K. Control of the morphology and structural development of solution-processed functionalized acenes for high-performance organic transistors. Adv. Funct. Mater. 19, 1515–1525 (2009).

    CAS  Article  Google Scholar 

  5. 5.

    Torrisi, F. et al. Inkjet-printed graphene electronics. ACS Nano 6, 2992–3006 (2012).

    CAS  Article  Google Scholar 

  6. 6.

    Cai, L., Zhang, S., Miao, J., Yu, Z. & Wang, C. Fully printed stretchable thin-film transistors and integrated logic circuits. ACS Nano 10, 11459–11468 (2016).

    CAS  Article  Google Scholar 

  7. 7.

    Li, Y. et al. All inkjet-printed metal-oxide thin-film transistor array with good stability and uniformity using surface-energy patterns. ACS Appl. Mater. Interfaces 9, 8194–8200 (2017).

    CAS  Article  Google Scholar 

  8. 8.

    Fukuda, K. et al. Fully-printed high-performance organic thin-film transistors and circuitry on one-micron-thick polymer films. Nat. Commun. 5, 4147 (2014).

    CAS  Article  Google Scholar 

  9. 9.

    Sekitani, T. et al. Printed nonvolatile memory for a sheet-type communication system. IEEE Trans. Electron Devices 56, 1027–1035 (2009).

    ADS  MathSciNet  CAS  Article  Google Scholar 

  10. 10.

    Khodagholy, D. et al. In vivo recordings of brain activity using organic transistors. Nat. Commun. 4, 1575 (2013).

    Article  Google Scholar 

  11. 11.

    Zhou, L. et al. Inkjet-printed small-molecule organic light-emitting diodes: halogen-free inks, printing optimization, and large-area patterning. ACS Appl. Mater. Interfaces 9, 40533–40540 (2017).

    CAS  Article  Google Scholar 

  12. 12.

    Gu, X. et al. Roll-to-roll printed large-area all-polymer solar cells with 5% efficiency based on a low crystallinity conjugated polymer blend. Adv. Energy Mater. 7, 1602742 (2017).

    Article  Google Scholar 

  13. 13.

    Khan, H. N., Hounshell, D. A. & Fuchs, E. R. H. Science and research policy at the end of Moore’s law. Nat. Electron 1, 14–21 (2018).

    Article  Google Scholar 

  14. 14.

    Myny, K. et al. An 8-bit, 40-instructions-per-second organic microprocessor on plastic foil. IEEE J. Solid-State Circuits 47, 284–291 (2012).

    ADS  Article  Google Scholar 

  15. 15.

    Myny, K. et al. Bidirectional communication in an HF hybrid organic/solution-processed metal-oxide RFID tag. IEEE Trans. Electron Devices 61, 2387–2393 (2014).

    CAS  Article  Google Scholar 

  16. 16.

    Daami, A. et al. Fully printed organic CMOS technology on plastic substrates for digital and analog applications. In 2011 IEEE International Solid-State Circuits Conference 328–330 (IEEE, 2011).

  17. 17.

    Abdinia, S. et al. A 4b ADC manufactured in a fully-printed organic complementary technology including resistors. In 2013 IEEE International Solid-State Circuits Conference Digest of Technical Papers 56, 106–107 (IEEE, 2013).

  18. 18.

    Fiore, V. et al. 30.4 A 13.56MHz RFID tag with active envelope detection in an organic complementary TFT technology. In 2014 IEEE International Solid-State Circuits Conference Digest of Technical Papers (ISSCC) 57, 492–493 (IEEE, 2014).

  19. 19.

    Nga, Ng,T. et al. Printed dose-recording tag based on organic complementary circuits and ferroelectric nonvolatile memories. Sci. Rep. 5, 13457 (2015).

    ADS  Article  Google Scholar 

  20. 20.

    Kwon, J. et al. Three-dimensional, inkjet-printed organic transistors and integrated circuits with 100% yield, high uniformity, and long-term stability. ACS Nano 10, 10324–10330 (2016).

    CAS  Article  Google Scholar 

  21. 21.

    Sankhare, M. A., Bergeret, E., Guerin, M., Pannier, P. & Coppard, R. Design of fully-printed organic circuits on plastic foils for wireless systems. IEEE J. Emerg. Sel. Top. Circuits Syst. 7, 102–113 (2017).

    ADS  Article  Google Scholar 

  22. 22.

    Derby, B. Inkjet printing of functional and structural materials: fluid property requirements, feature stability, and resolution. Annu. Rev. Mater. Res. 40, 395–414 (2010).

    ADS  CAS  Article  Google Scholar 

  23. 23.

    Myny, K. et al. Unipolar organic transistor circuits made robust by dual-gate technology. IEEE J. Solid-State Circuits 46, 1223–1230 (2011).

    ADS  Article  Google Scholar 

  24. 24.

    Noh, Y., Zhao, N., Caironi, M. & Sirringhaus, H. Downscaling of self-aligned, all-printed polymer thin-film transistors. Nat. Nanotechnol. 2, 784–789 (2007).

    ADS  CAS  Article  Google Scholar 

  25. 25.

    Mativenga, M., An, S. & Jang, J. Bulk accumulation a-IGZO TFT for high current and turn-on voltage uniformity. IEEE Electron Device Lett. 34, 1533–1535 (2013).

    ADS  CAS  Article  Google Scholar 

  26. 26.

    Shiwaku, R. et al. Printed organic inverter circuits with ultralow operating voltages. Adv. Electron. Mater. 3, 1600557 (2017).

    Article  Google Scholar 

  27. 27.

    Ferain, I., Colinge, C. A. & Colinge, J. P. Multigate transistors as the future of classical metal-oxide-semiconductor field-effect transistors. Nature 479, 310–316 (2011).

    ADS  CAS  Article  Google Scholar 

  28. 28.

    Liu, C. et al. Device physics of contact issues for the overestimation and underestimation of carrier mobility in field-effect transistors. Phys. Rev. Appl. 8, 034020 (2017).

    ADS  Article  Google Scholar 

  29. 29.

    Ng, T. N. et al. Scalable printed electronics: an organic decoder addressing ferroelectric non-volatile memory. Sci. Rep. 2, 585 (2012).

    Article  Google Scholar 

  30. 30.

    Schwartz, D. E. & Ng, T. N. Comparison of static and dynamic printed organic shift registers. IEEE Electron Device Lett. 34, 271–273 (2013).

    ADS  Article  Google Scholar 

  31. 31.

    Mandal, S. et al. Fully-printed, all-polymer, bendable and highly transparent complementary logic circuits. Org. Electron. 20, 132–141 (2015).

    CAS  Article  Google Scholar 

  32. 32.

    Takeda, Y. et al. Integrated circuits using fully solution-processed organic TFT devices with printed silver electrodes. Org. Electron. 14, 3362–3370 (2013).

    CAS  Article  Google Scholar 

  33. 33.

    Takeda, Y. et al. Flip-flop logic circuit based on fully solution-processed organic thin film transistor devices with reduced variations in electrical performance. Jpn. J. Appl. Phys. 54, 04DK03 (2015).

    Article  Google Scholar 

  34. 34.

    Takeda, Y. et al. Fabrication of ultra-thin printed organic TFT CMOS logic circuits optimized for low-voltage wearable sensor applications. Sci. Rep. 6, 25714 (2016).

    ADS  CAS  Article  Google Scholar 

  35. 35.

    Knobloch, A., Manuelli, A., Bernds, A. & Clemens, W. Fully printed integrated circuits from solution processable polymers. J. Appl. Phys. 96, 2286–2291 (2004).

    ADS  CAS  Article  Google Scholar 

  36. 36.

    Chang, J., Zhang, X., Ge, T. & Zhou, J. Fully printed electronics on flexible substrates: High gain amplifiers and DAC. Org. Electron. Phys., Mater. Appl. 15, 701–710 (2014).

    CAS  Google Scholar 

  37. 37.

    Fiore, V. et al. 30.4 A 13.56MHz RFID tag with active envelope detection in an organic complementary TFT technology. Dig. Tech. Pap. - IEEE Int. Solid-State Circuits Conf. 57, 492–493 (2014).

    Google Scholar 

  38. 38.

    Jung, M. et al. All-printed and roll-to-roll-printable 13.56-MHz-operated 1-bit RF tag on plastic foils. IEEE Trans. Electron Devices 57, 571–580 (2010).

    ADS  CAS  Article  Google Scholar 

  39. 39.

    Noh, J. et al. Fully Gravure-printed D flip-flop on plastic foils using single-walled carbon-nanotube-based TFTs. IEEE Electron Device Lett. 32, 638–640 (2011).

    ADS  CAS  Article  Google Scholar 

  40. 40.

    Kwon, J. et al. Vertically stacked complementary organic field-effect transistors and logic circuits fabricated by inkjet printing. Adv. Electron. Mater. 2, 1600046 (2016).

    Article  Google Scholar 

Download references

Acknowledgements

We thank Dr. H. Matsui for thoughtful discussion on the preparation of semiconducting inks. We also thank Tosoh Corporation for supplying DTBDT-C6. This work was supported by grants (Code No. 2012M3A6A5055728 and 2015M3A6A5072945) from the Center for Advanced Soft Electronics under the Global Frontier Research Program of the Ministry of Science and ICT of South Korea, by the IT Consilience Creative Program (IITP-2018-2011-1-00783) supervised by IITP (Institute for Information & Communications Technology Promotion).

Author information

Affiliations

Authors

Contributions

J.K. and S.J. conceived the project. J.K. performed most experiments and Y.T. performed some of device environmental tests. Y.T. and R.S. optimized the semiconductor inks for printing. S.T., K.C. and S.J. supervised the project. J.K., S.T., K.C. and S.J. analyzed and interpreted the data, and wrote the manuscript.

Corresponding authors

Correspondence to Shizuo Tokito or Kilwon Cho or Sungjune Jung.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Journal peer review information: Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. Peer reviewer reports are available.

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Supplementary information

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Kwon, J., Takeda, Y., Shiwaku, R. et al. Three-dimensional monolithic integration in flexible printed organic transistors. Nat Commun 10, 54 (2019). https://doi.org/10.1038/s41467-018-07904-5

Download citation

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.