Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

A robust zirconium amino acid metal-organic framework for proton conduction


Proton conductive materials are of significant importance and highly desired for clean energy-related applications. Discovery of practical metal-organic frameworks (MOFs) with high proton conduction remains a challenge due to the use of toxic chemicals, inconvenient ligand preparation and complication of production at scale for the state-of-the-art candidates. Herein, we report a zirconium-MOF, MIP-202(Zr), constructed from natural α-amino acid showing a high and steady proton conductivity of 0.011 S cm−1 at 363 K and under 95% relative humidity. This MOF features a cost-effective, green and scalable preparation with a very high space-time yield above 7000 kg m−3 day−1. It exhibits a good chemical stability under various conditions, including solutions of wide pH range and boiling water. Finally, a comprehensive molecular simulation was carried out to shed light on the proton conduction mechanism. All together these features make MIP-202(Zr) one of the most promising candidates to approach the commercial benchmark Nafion.


Proton exchange membrane fuel cells (PEMFCs) are among the most promising and attractive candidates for developing clean and renewable energy solutions due to their high energy density, low pollutant emissions, and mild operating conditions1. The proton conductive performance is a critical factor for the PEMFC materials and the current commercial benchmark for this application is Nafion2. However, the high cost and the eventually decreased performance over cycling of this sulfonated fluoropolymer call for the development of more efficient and cheaper proton conductive materials. Among those, metal-organic frameworks (MOFs) have been reported as a promising class of solids for such application3. Nevertheless, so far, the reported MOFs with high proton conduction are hardly environment-friendly to fulfill the sustainable development criteria, due to the involvement of either toxic metal ions or time and effort-consuming organic linker synthesis4,5,6,7,8,9,10,11. In this context, the design of highly proton conductive biocompatible MOFs combining excellent stability, low toxicity, and scalable preparation is still a challenging target.

One of the key criteria for biocompatible MOFs is that both inorganic metal and organic linker components show the lowest toxicity. High valence metals with rich natural abundances and long-term stability in their complexes that have been proven to be harmless to human body, such as Al3+, Fe3+, Ti4+, or Zr4+, are of prime interests12,13. On the other hand, l-α-amino acids which are encoded directly by the triplet codons in the genetic code of DNA are one family of the most attractive naturally occurring linkers suitable for MOFs, not only due to their innocuousness and natural abundant resources but also for their sufficient coordination and bonding abilities towards various metals under a wide range of chemical conditions14,15,16. However, very few examples of MOFs built from pure l-α-amino acids exclusively based on divalent transition metals and main group metals or rare earth metals have been reported so far17. Among them, three-dimensional (3D) MOFs with accessible porosity are even scarcer, primarily due to the common chelating coordination fashion of l-α-amino acids17.

Among the 20 standard l-α-amino acids, aspartic acid is the smallest one consisting of two carboxylate groups with a separation distance sought to be appropriate for energetically favorable robust bridging/linkage of inorganic nodes. A few crystal structures of metal-aspartate MOFs have been reported so far but in all cases they exhibit a limited hydrolytic stability18,19,20,21,22,23. Furthermore, following the Pearson hard and soft acid and base theory, aspartic acid should be appropriate to construct MOFs based on high valence hard transition metal cations while leaving the soft amino group free from coordination. However, no example of hard metal cations, especially Al3+, Fe3+, or Zr4+, has been reported to form MOFs based on amino acids up to now, possibly due to the fast and strong bonding between high valence metal ions with aspartate in solution which leads highly complex the generation of crystalline products24,25.

It is worth mentioning that the porous Zr-amino acids MOF would be of great interest since in general high stability and excellent performance in various applications have been highlighted for Zr-carboxylate MOFs over the last few years26. In the field of proton conductive materials, the design of Zr-MOFs based on non-commercially available linkers has been actively investigated, including a flexible tetraphosphonate coordination polymer27, a Zr-phosphonate based on glyphosine28,29, a phenolate-based MOF30, and PCMOF2031, outperforming in some cases Nafion. However, these MOFs suffer from either a lack of biocompatible character, the use of expensive or poorly environment-friendly chemicals and/or scale-up limitations. Series of Zr-carboxylate MOFs based on commercial (not bio-derived) linkers such as the Zr-terepthalate UiO-66 as well as the Zr-trimesate MOF-80832 have also been studied as proton conductive materials, in particular the UiO-66’s series of functionalized solids that exhibit interesting performances being tuned by (i) the decoration of the pore wall with pendent acid groups (−CO2H, −SO3H)4,33,34,35,36 or (ii) the incorporation of ligand defects saturated or not by acid treatment37,38,39. Some of these solids are however not exceeding the performances of Nafion.

We report herein an amino acid-based Zr-MOF, denoted as MIP-202(Zr) (MIP stands for the Materials of the Institute of porous materials from Paris), in which the 12-connected Zr6(μ3-O)4(μ3-OH)4 node and the l-aspartate spacer are assembled in water generating a 3D microporous framework with a UiO-6640 type structure. MIP-202(Zr) demonstrates excellent proton conductivity up to 0.011 S cm−1 at 363 K and under 95% of relative humidity (RH), with the crystal structure unchanged even after one week of test. This makes MIP-202(Zr) one of the best proton conductive MOF materials reported so far. The proton conduction mechanism was further investigated by means of molecular simulations. In addition, MIP-202(Zr) not only features green and scalable synthesis, but also is the only amino acid-based MOF material that possesses a very good hydrolytic stability and chemical stability.


Synthesis and characterization

The syntheses of most Zr-MOFs involves toxic organic solvents, such as dimethylformamide and dimethylacetamide, carried out in sealed reactors. Additionally, diluted solutions or suspensions of starting chemicals are generally preferred in order to yield Zr-MOF product with good crystallinity26. Thereby, it is hardly a scalable and environment-friendly preparation process, which is undoubtedly against the global sustainable development criteria41,42. Moreover, all the best proton conductive MOFs (σ > 10−2 S cm−1) have been obtained under harsh conditions so far11. The scale-up of those MOFs would therefore face severe problems such as the use of toxic and expensive chemicals, complicated linker synthesis, and reproduction issues (Supplementary Table 1). In sharp contrast, MIP-202(Zr) was synthesized by simply heating the mixture of ZrCl4 and l-aspartic acid in water for several hours under reflux with ambient pressure. Besides, the activation step only involves green solvents, such as water and ethanol, for washing and removing the excess of free linker and Cl extra-framework species. This approach is not only environment-friendly, but also highly beneficial in terms of cost and regeneration. This procedure also results in a high space-time yield of 7030 kg m−3 day−1 comparable to some industrial scale syntheses43,44.

It is worthy to note that only high concentration of reactants could generate the MIP-202(Zr) product efficiently. On the contrary, diluted solution of the same starting materials resulted in clear solution without any solid product under the same reaction condition. It could be due to the strong acidic condition associated with Zr4+ in solution that affects the presenting conformation of the amino group containing linkers. It has been documented before for UiO-66(Zr)-NH245 that a partial protonation of the weakly basic amino group occurs as a consequence of the highly acidic synthesis conditions that significantly slows down the kinetic of formation of this MOF in comparison with other functionalized UiO-66. Indeed, if one considers amino acids that possess much more basic −NH2 groups, this is likely that a full protonation of the amino group might occurs in the presence of strongly acidic metal cations, leading to zwitterionic ligand species, which certainly alters the ability of the amino acid to complex the high valence metal species. Thus, in the case of MIP-202(Zr), the full protonation of the amino group on the l-aspartic acid molecule is likely to slow down the crystallization process through the formation of stable highly polarized metal complexes in solution. Only when considering over saturated conditions, one can successfully shift the equilibrium towards the formation of precipitates and thus MIP-202(Zr).

Furthermore, the MIP-202(Zr) product particle size distribution can be tuned easily. For example, reaction without stirring leads to single crystals with a size range of 5–30 μm (Supplementary Figure 1), which is suitable for single crystal X-ray diffraction data collection under synchrotron radiation, easy recovery of the material during the filtration process to collect the MOF after the synthesis and/or activation/cleaning in solution as well. On the contrary, reactions with stirring under reflux result in much smaller particle size of the MOF product down to sub-micro level which can be advantageous to prepare thin films or membranes (Supplementary Figure 2). Consequently, this opens the way towards the use of MIP-202(Zr) in practical applications.

The crystal structure of MIP-202(Zr) was solved by employing our newly developed crystal structure prediction software which is based on the Automated Assembly of Secondary Building Units (AASBU)46 method (Supplementary Note 1 and Supplementary Figure 3). The structural framework was experimentally confirmed by synchrotron diffraction data collected with a microfocused X-rays on the Proxima 2A beamline (Synchrotron SOLEIL, France)47 using a microsized single crystal (Supplementary Note 2). It should be noted that MIP-202(Zr) is isostructural to the previously reported cubic (fcu topology) Zr-Fumarate (also known as MOF-801) compound (Fig. 1)48,49. Hence their Powder X-ray Diffraction (PXRD) patterns match with each other very well (Supplementary Figure 4), resulting in almost identical unit cell parameters—a = 17.8348(17) Å and 17.8260(21) Å for Zr-Fumarate and MIP-202(Zr), respectively—consistent with the similar molecular lengths of fumaric acid and aspartic acid. The uncoordinated amino groups are highly disordered over four positions. It is interesting to note that all the amino groups are pointing towards the pores, making the cavity environment of MIP-202(Zr) very different from that of the Zr-Fumarate compound.

Fig. 1

Crystal structural features of MIP-202(Zr). a The 12-connected Zr63-O)43-OH)4(COO)12 cluster SBU. b An aspartic acid linker. c The crystal structure of MIP-202(Zr) viewed along the a-axis. d The crystal structure of MIP-202(Zr) viewed along the (101) plane. Zr atoms or polyhedra, oxygen, carbon, nitrogen, and hydrogen atoms are in light blue, red, gray, dark blue, and white, respectively

Scanning electron microscopy coupled with energy-dispersive X-ray spectroscopy (SEM-EDX) evidenced that there are still Cl species trapped inside the porosity of MIP-202(Zr). Extensive washing the MOF sample in boiling ethanol or methanol over prolonged periods of time could effectively remove most of the free Cl residue, leading to a ratio of Cl to both Zr and N of 1:1. This suggests that all the amino groups of the aspartate linker molecules are protonated and are present in the form of –NH3+/Cl pair (Supplementary Table 2). The solid-state 15N magic-angle spinning (MAS) NMR spectrum (Supplementary Figure 5) collected on the MIP-202(Zr) sample supports the presence of the above-mentioned –NH3+/Cl pair in the MOF structure since the chemical shift of the nitrogen species in MIP-202(Zr) is very close to that of the amino group in a zwitterionic form50. Therefore, the NH3+ moieties in the aspartate ligands are considered along with Cl counter ions for the final structure optimization at the density-functional level of theory (DFT). It is important to note that the presence of this –NH3+/Cl pair plays a critical role on the accessibility of the MIP-202(Zr) porosity. As expected from the crystal structure, nitrogen sorption result collected on the fully protonated MIP-202(Zr) sample leads to a limited accessible pore volume of 0.1 cm3 g−1 and a free pore diameter less than 4 Å which falls into the range of ultra-microporous materials class (Supplementary Figures 68).

Since l-aspartic acid was applied as the linker to synthesize MIP-202(Zr), circular dichroism (CD) measurements were carried out to access its possible chirality. MIP-202(Zr) constructed from d-aspartic acid was prepared as well under the same reaction condition for comparison. After decomposition of the MOFs structures in concentrated NaOH solution, CD spectra were collected on the clear solutions containing released aspartate from the MOF frameworks. As expected, the digested MIP-202(Zr) samples display nearly the same CD response as that obtained from the enantiomers of aspartic acid and pre-prepared Na-aspartate salts under the same testing condition (Supplementary Figure 9), indicating the chiral pore environments of both L-MIP-202(Zr) and D-MIP-202(Zr) samples.

Of an utmost importance for practical applications, particularly in the case of proton conductivity, the hydrothermal stability of MOFs is prerequisite. Various conditions were applied to the MIP-202(Zr) sample in order to confirm its expected chemical resistance. MIP-202(Zr) not only shows an excellent stability in common organic solvents (e.g. methanol) as the other reported aspartate-based MOFs17 but also displays remarkably elevated hydrolytic stability in water. Boiling water did not affect at all the crystallinity of MIP-202(Zr) sample as supported by PXRD and nitrogen sorption measurement results (Supplementary Figures 7, 8 and 10a). Furthermore, the long-range order of the MIP-202(Zr) crystalline framework is stable over a large pH range in aqueous solutions from acidic (pH = 0, HCl) to basic (pH = 12, KOH) conditions as confirmed by PXRD. The increased nitrogen uptakes and pore sizes for the samples exposed to acidic and basic conditions are due to the removal of Cl counter ions or the generation of structural defects respectively, as evidenced by a combined analysis of TGA, EDX and elemental analysis results (Supplementary Figure 11, Supplementary Tables 3 and 4, Supplementary Note 3), with more defects being created under acidic treatment or a larger amount of Cl anions removed under basic conditions. The overall chemical stability of MIP-202(Zr) is therefore comparable to or to some extent even better than most of the previously reported Zr-MOFs based on multi-topic aromatic carboxylic linkers. In addition, to the best of our knowledge, MIP-202(Zr) is the first crystalline metal-amino acid-based porous solid material, MOFs or otherwise, that not only displays an excellent stability in the presence of water but also a remarkable resistance to both acidic and basic conditions.

Proton conductivity

MIP-202(Zr) can be considered as a potentially efficient proton conductor based on its following features prerequisite for such application: (i) the presence of accessible NH3+ Brønsted acidic groups (proton sources) that decorate the short aliphatic chain of the aspartate linker, (ii) the crystalline tunnel-like architecture and the small porosity that is expected to favor the formation of an orientated hydrogen-bonded network of the guest water molecules, and (iii) a good hydrolytic stability to ensure that the proton conductive performances can be maintained over cycles. AC impedance spectroscopy was employed to assess the performance of MIP-202(Zr) (Supplementary Note 4). Measurements were firstly carried out on the anhydrous solid, which was pre-treated under nitrogen flow at 363 K for 2 h. Figure 2a illustrates the Nyquist plot as a function of temperature for the anhydrous MIP-202(Zr) (RH = 0%). The semi-circle represents the bulk and grain boundary resistances, and the small tail at low frequency is indicative of the accumulation of ionic charges at the blocking electrode interface. It is worthy to note that the tail is poorly pronounced in relation with the very low conductivity values recorded at temperature lower than 363 K (σ ≤ 10−11 S cm−1; Supplementary Figure 12 and Supplementary Table 5). This observation evidences that the charge carriers are poorly mobile in the absence of water. In contrast, the evolution of the imaginary (Z″) part of the impedance vs the corresponding real part (Z′) drastically changes for the material equilibrated for 24 h under 95% RH (Fig. 2b). It results in a sharp increase of the conductivity by nine orders of magnitudes compared to the anhydrous state, leading to the value of 1.1 × 10−2 S cm−1 under the condition of 363 K/95% RH (Supplementary Figure 13). This value is among the highest conductivities reported for other water-mediated proton-conducting MOFs, including UiO-66-(SO3H)234, (Hpy)2[Zn2(ox)3].nH2O51, VNU-1552, JLU-Liu4453, Fe-CAT-55, PCMOF21/28, and PCMOF2031, and converges towards the performances of the benchmark Nafion based polymer54. Furthermore, MIP-202(Zr) is the best proton conductor among the MOFs showing a cationic framework, such as the Zn-(4-carboxyphenyl)imidazolium-based solid with a σ = 2.3 × 10−3 S cm−1 at 298 K/95% RH55, and the Cu-bipyridine glycoluril (BPG) based MOF with a σ = 4.4 × 10−3 S cm−1 at 363 K/95% RH56. In addition, the conductive performances of MIP-202(Zr) are well maintained over one week of experiments performed at 363 K and 95% RH (Supplementary Figure 14). This observation proves the robustness of MIP-202(Zr) under the operating conditions, as supported by the analysis of the PXRD pattern of the solid after the conductivity measurements, which confirms the integrity of the crystal structure during the impedance analysis (Supplementary Figure 10b). Finally, the variation of the conductivity performance with temperature was also studied at RH = 95% from 363 K to 298 K (Supplementary Table 6). The activation energy, deduced from the linear fitting of ln(σT) vs 1000 T−1 according to the Nernst–Einstein equation σ(T) = σ0/T exp(−Ea/kT), is 0.22 eV (Supplementary Figure 15). This value suggests that the proton diffusion is governed by a Grotthus mechanism involving proton hops between hydrogen-bonded water molecules (0.1–0.4 eV).

Fig. 2

Nyquist plots from AC impedance data for MIP-202(Zr). a at 0% RH. b at 95% RH

Molecular simulation

Monte Carlo (MC) calculations (Supplementary Note 1, Supplementary Figure 16 and Supplementary Tables 79) were further performed on the fully hydrated MIP-202(Zr) to analyze the preferential arrangements of the confined water molecules and the roles of both Cl and NH3+ in the formation of the hydrogen-bonded network (Supplementary Figures 1720). Such feature is a key to allow the proton propagation at the origin of the promising proton conductive performance of MIP-200(Zr). The analysis of the MC configurations indicated that H2O molecules are arranged in such a way that they interact with the MOF framework through their oxygen atoms (Ow) with (i) the proton of the NH3+ group of the linker as evidenced by a short mean distance between the two atoms pairs [d(Ow−HNH3) = 1.8 Å] (Fig. 3a) and (ii) the proton of the µ3-OH group of Zr oxocluster with a mean distance d(Ow−Hµ3-OH) of 1.9 Å (Fig. 3b), resulting in a well-ordered hydrogen-bonded network. Moreover, the confined water molecules themselves also form a 3D hydrogen-bonded network corresponding to the Hw–Ow mean distance of 1.8 Å (Fig. 3d), as short as those usually observed for water in the bulk state57. This spatial distribution and the interactions at play are reminiscent of those commonly reported for water-mediated proton-conducting MOFs58. Such predictions are consistent with the existence of a Grotthus-like mechanism, supported by the value of the activation energy estimated from the conductivity measurements (0.22 eV) which is far below 0.4 eV.

Fig. 3

Radial distribution functions calculated from the average over the MC configurations considered for hydrated MIP-202(Zr) at 90 °C. a N and H of NH3+ to O(H2O) atomic pairs. b O and H of µ3-OH to O(H2O) atomic pairs. c Cl to O and H of H2O atomic pairs. d O and H of H2O to O(H2O) atomic pairs

A quantitative analysis of the hydrogen bond number per H2O molecule was calculated using the following criteria: the distance between donor and acceptor oxygen centers (D−A) is shorter than 3.5 Å and the corresponding angle between the intramolecular O−H vector (OH of donor molecule) and the intermolecular O−O vector (O atoms of donor to acceptor) is less than 37°. These criteria are the same as we used previously to describe the hydrogen bonds in other porous materials35,36,58. The average number of hydrogen bond formed by a single H2O molecule over all the generated MC configurations is 4. Implying the same hydrogen bond definition for the NH3+ group (N as a donor, O of water as an acceptor and H of NH3+ as a proton), a single N donor exhibits maximum three hydrogen bonds with neighboring water molecules. Such hydrogen bonding extends in a way that forms water bridge with neighboring NH3+ moieties, simultaneously generating a −NH···:O:···HN− (where O is the oxygen of a bridging water) network (Fig. 4b). This strongly suggests that a hydrogen-bonded network can be initiated from the NH3+ functional groups and creates possible pathways for the proton movement throughout the framework. In addition, Cl ions present within the cavities also interact with protons and a large fraction of them fulfill the aforementioned hydrogen bonding criteria by taking the acceptor positions around NH3+ and H2O molecules (Fig. 4c). Some of these anions form single hydrogen bond with NH3+ or H2O, disrupting the potential hydrogen-bonded network in certain directions. In some cases, a single Cl- holds a position that favors multiple hydrogen bonds was noticed. Thus we assume that such an arrangement is not necessarily detrimental for the proton propagation.

Fig. 4

Illustration of the hydrogen bonding in MIP-202(Zr) structure. a Multiple water-mediated hydrogen-bonded network as evidenced by MC-NVT simulations performed at 90 °C for hydrated MIP-202(Zr). b A representative hydrogen-bonded water-bridge network formed by the NH3 and H2O molecules. c Hydrogen bonding with the possible involvement of Cl ions (MOF skeleton in gray, nitrogen of NH3+ group in blue, Cl ions in green and oxygen of µ3-OH, and H2O molecule in red)

We further performed quantitative analysis for the clustering of water molecules within the pores of MIP-202(Zr). A cluster is defined as a continuous network of water molecules interconnected by hydrogen bonds among themselves. We revealed that the adsorbed water molecules form hydrogen-bonded aggregates incorporating up to 10 H2O molecules, this cluster-size being slightly smaller than those observed for other MOFs with 1D channels, such as MIL-53(Cr) and MIL-47(V)59. Such arrangements of water make bridges among multiple proton sources, i.e., NH3+groups present in the adjacent or opposite pore walls, and this leads to a much more extended hydrogen-bonded network connection (Supplementary Figure 21). Indeed, the existence of such pathways offers an optimal situation for the water-mediated transport of protons over long distances, bridging different aspartate ligands that act as proton sources in MIP-202(Zr).

In summary, MIP-202(Zr), a Zr-MOF based on natural amino acid linker has been successfully synthesized and fully characterized. Unlike most of the previously reported proton conductive MOFs, MIP-202(Zr) features a green, scalable and facile preparation by using cost-effective and environment-friendly chemicals. This material displays an excellent hydrolytic and chemical stability in aqueous solutions with a wide range of pH. Our results therefore pave the way for the design of green, robust, and cheap MOFs based on amino acids. It is worth mentioning that MIP-202(Zr) features outstanding proton conduction performances under humid condition that are driven by the formation of an extended hydrogen-bonded network resulting from the interactions between the NH3+ groups acting as the proton source, and the water molecules present in the pores. To the best of our knowledge, MIP-202(Zr) is one of the most practical alternative materials to the commercial benchmark Nafion for ion-exchange membrane applications. Furthermore, the tunable product particle size, the pore system with chiral environment in the structure, and the bio-compatibility make MIP-202(Zr) as a potentially promising candidate in biological and pharmaceutical applications.


Typical synthesis of MIP-202(Zr)

l-Aspartic acid (2.8 g) was transferred into a 25 mL round bottom flask; 5 mL of water was added to disperse the linker. ZrCl4 (2.33 g) was added by portion into the water suspension, leading to a clear colorless solution. Another 5 mL of water was added to flush the inner face of the flask, trying to wash as much as possible the ZrCl4 powder down into the solution. The reaction was kept at reflux for 1 h (120 °C). After cooling down to room temperature, the expected product of MIP-202(Zr) was collected by filtration, washed with water/EtOH at room temperature, and air dry, leading to 2.93 g white solid product of the MOF with a crude yield of 90%. This preparation method could be applied to either smaller scale syntheses or larger scale ones when a reflux apparatus with suitable size is involved. For example, a scale-up synthesis was carried out in a 250 mL round bottom flask under the same condition results in 30.4 g of product (94% yield) with a space-time yield of 7296 kg m−3 day−1.


Powder X-ray diffraction (PXRD) data were recorded on a high-throughput Bruker D8 Advance diffractometer working on transmission mode and equipped with a focusing Göbel mirror producing CuKα radiation (λ = 1.5418 Å) and a LynxEye detector. Nitrogen porosimetry data were collected on a Micromeritics Tristar instrument at 77 K. SEM-EDX results were recorded with an FEI Magellan 400 scanning electron microscope. TGA data were collected on Mettler Toledo TGA/DSC 2, STAR System apparatus with a heating rate of 2 °C/min under the oxygen flow. Elemental analyses were performed on a Vario EL-III elemental analyzer. Solid-state NMR spectra were recorded with an Advance Bruker 500 NMR spectrometer. Circular dichroism (CD) spectra were recorded on a Chirascan™-plus CD Spectrometer (Applied Photophysics). The far ultraviolet spectra (185–260 nm) were measured at 20 °C in quartz cells of 0.4 cm optical path length. Spectra were acquired at a resolution of 1 nm, with time per points set at 0.7 s and a bandwidth of 1 nm.

Proton conductivity measurement

Impedance measurements were performed on a Broadband Dielectric Spectrometer, Novocontrol alpha analyzer over a frequency range from 1 Hz to 1 MHz with an applied ac voltage of 20 mV. Measurements were collected on the anhydrous and the hydrated solid, which was placed into an Espec Corp. SH-221 incubator, to control the temperature (298 < T (K) < 363) and the RH (95%). The solid was equilibrated for 24 h at given T and RH values to ensure fixed water content before recording the impedance. The measurements were performed using samples as a powder, introduced between two gold electrodes in a parallel plate capacitor configuration with an annular Teflon spacer for insulation, allowing the use of the two-probe method for the electrical measurements. The thickness l and surface S are as follows: l = 1.11 and 2.07 mm, S = 33.1 and 15.9 mm2 for the anhydrous and the hydrated MIP-202(Zr), respectively. Conductivity was deduced from the Bode diagram as well as from the Nyquist plot for comparison.

X-ray crystallography

The single crystal data of MIP-202(Zr) were collected on Proxima-2A microfocused beamline at the SOLEIL Synchrotron (λ = 0.70846 Å) at 100 K. The data were integrated and reduced using XDS software. The structure was then solved using SHELXT and refined with SHELXL software. The compound MIP-202(Zr) is isostructural to the previously reported cubic (fcu topology) Zr-Fumarate (MOF-801) compound. The aspartic acid linkers are highly disordered in the structure. Therefore, the nitrogen atom from the linker is located on four distinct positions with partial occupations (noted N1 and N2), corresponding to the four possible orientations of the linker. The central carbon atoms (noted C2) from the linker should also be disordered on two distinct positions. However, due to symmetry considerations and to the limited quality of the single crystal diffraction data, only the average position of these atoms has been determined.

Data availability

The X-ray crystallographic data for MIP-200(Zr) have been deposited at the Cambridge Crystallographic Data Centre (CCDC), under deposition number CCDC 1842337. These data can be obtained free of charge from the CCDC via All other relevant data supporting the findings of this study are available from the corresponding authors on request.


  1. 1.

    Barbir, F. PEM Fuel Cells: Theory and Practice (Elsevier Academic Press, New York, 2005).

    Chapter  Google Scholar 

  2. 2.

    Mauritz, K. A. & Moore, R. B. State of understanding of nafion. Chem. Rev. 104, 4535–4585 (2004).

    CAS  Article  Google Scholar 

  3. 3.

    Li, A.-L., Gao, Q., Xu, J. & Bu, X.-H. Proton-conductive metal-organic frameworks: recent advances and perspectives. Coord. Chem. Rev. 344, 54–82 (2017).

    CAS  Article  Google Scholar 

  4. 4.

    Phang, W. J. et al. Superprotonic conductivity of a UiO-66 framework functionalized with sulfonic acid groups by facile postsynthetic oxidation. Angew. Chem. Int. Ed. 54, 5142–5146 (2015).

    CAS  Article  Google Scholar 

  5. 5.

    Nguyen, N. T. et al. Three-dimensional metal-catecholate frameworks and their ultrahigh proton conductivity. J. Am. Chem. Soc. 137, 15394–15397 (2015).

    CAS  Article  Google Scholar 

  6. 6.

    Ramaswamy, P., Wong, N. E., Gelfand, B. S. & Shimizu, G. K. A water stable magnesium MOF that conducts protons over 10(−2) S cm(−1). J. Am. Chem. Soc. 137, 7640–7643 (2015).

    CAS  Article  Google Scholar 

  7. 7.

    Nagarkar, S. S., Unni, S. M., Sharma, A., Kurungot, S. & Ghosh, S. K. Two-in-one: inherent anhydrous and water-assisted high proton conduction in a 3D metal-organic framework. Angew. Chem. Int. Ed. 53, 2638–2642 (2014).

    CAS  Article  Google Scholar 

  8. 8.

    Kim, S., Dawson, K. W., Gelfand, B. S., Taylor, J. M. & Shimizu, G. K. Enhancing proton conduction in a metal-organic framework by isomorphous ligand replacement. J. Am. Chem. Soc. 135, 963–966 (2013).

    CAS  Article  Google Scholar 

  9. 9.

    Ponomareva, V. G. et al. Imparting high proton conductivity to a metal-organic framework material by controlled acid impregnation. J. Am. Chem. Soc. 134, 15640–15643 (2012).

    CAS  Article  Google Scholar 

  10. 10.

    Phang, W. J. et al. pH-dependent proton conducting behavior in a metal-organic framework material. Angew. Chem. Int. Ed. 53, 8383–8387 (2014).

    CAS  Article  Google Scholar 

  11. 11.

    Yang, F. et al. A flexible metal-organic framework with a high density of sulfonic acid sites for proton conduction. Nat. Energy 2, 7 (2017).

    Google Scholar 

  12. 12.

    Horcajada, P. et al. Metal-organic frameworks in biomedicine. Chem. Rev. 112, 1232–1268 (2012).

    CAS  Article  Google Scholar 

  13. 13.

    Gimenez-Marques, M., Hidalgo, T., Serre, C. & Horcajada, P. Nanostructured metal-organic frameworks and their bio-related applications. Coord. Chem. Rev. 307, 342–360 (2016).

    CAS  Article  Google Scholar 

  14. 14.

    Rauser, W. E. Structure and function of metal chelators produced by plants—the case for organic acids, amino acids, phytin, and metallothioneins. Cell Biochem. Biophys. 31, 19–48 (1999).

    CAS  Article  Google Scholar 

  15. 15.

    Aspinall, H. C. Chiral lanthanide complexes: coordination chemistry and applications. Chem. Rev. 102, 1807–1850 (2002).

    CAS  Article  Google Scholar 

  16. 16.

    Auld, D. S. Zinc coordination sphere in biochemical zinc sites. Biometals 14, 271–313 (2001).

    CAS  Article  Google Scholar 

  17. 17.

    Anderson, S. L. & Stylianou, K. C. Biologically derived metal organic frameworks. Coord. Chem. Rev. 349, 102–128 (2017).

    CAS  Article  Google Scholar 

  18. 18.

    Vaidhyanathan, R. et al. A family of nanoporous materials based on an amino acid backbone. Angew. Chem. Int. Ed. 45, 6495–6499 (2006).

    CAS  Article  Google Scholar 

  19. 19.

    Anokhina, E. V., Go, Y. B., Lee, Y., Vogt, T. & Jacobson, A. J. Chiral three-dimensional microporous nickel aspartate with extended Ni-O-Ni bonding. J. Am. Chem. Soc. 128, 9957–9962 (2006).

    CAS  Article  Google Scholar 

  20. 20.

    Barrio, J. P. et al. Control of porosity geometry in amino acid derived nanoporous materials. Chem. Eur. J. 14, 4521–4532 (2008).

    CAS  Article  Google Scholar 

  21. 21.

    Gould, J. A. et al. Nanoporous amino acid derived material formed via in-situ dimerization of aspartic acid. Cryst. Growth Des. 10, 2977–2982 (2010).

    CAS  Article  Google Scholar 

  22. 22.

    Gould, J. A., Jones, J. T., Bacsa, J., Khimyak, Y. Z. & Rosseinsky, M. J. A homochiral three-dimensional zinc aspartate framework that displays multiple coordination modes and geometries. Chem. Commun. 46, 2793–2795 (2010).

    CAS  Article  Google Scholar 

  23. 23.

    Antolini, L., Marcotrigiano, G., Menabue, L., Pellacani, G. C. & Saladini, M. Thermal, spectroscopic, magnetic, and structural properties of mixed-ligand complexes of copper(II) with L-aspartic acid and amines. Crystal and molecular structure of (L-aspartato)(imidazole)copper(II) dihydrate. Inorg. Chem. 21, 2263–2267 (1982).

    CAS  Article  Google Scholar 

  24. 24.

    Xin, Q. et al. Extracellular biocoordinated zinc nanofibers inhibit malignant characteristics of cancer cell. Nano Lett. 15, 6490–6493 (2015).

    ADS  CAS  Article  Google Scholar 

  25. 25.

    Ma, B. J. et al. Terbium-aspartic acid nanocrystals with chirality-dependent tunable fluorescent properties. ACS Nano 11, 1973–1981 (2017).

    CAS  Article  Google Scholar 

  26. 26.

    Bai, Y. et al. Zr-based metal-organic frameworks: design, synthesis, structure, and applications. Chem. Soc. Rev. 45, 2327–2367 (2016).

    CAS  Article  Google Scholar 

  27. 27.

    Costantino, F., Donnadio, A. & Casciola, M. Survey on the phase transitions and their effect on the ion-exchange and on the proton-conduction properties of a flexible and robust Zr phosphonate coordination polymer. Inorg. Chem. 51, 6992–7000 (2012).

    CAS  Article  Google Scholar 

  28. 28.

    Donnadio, A. et al. A layered mixed zirconium phosphate/phosphonate with exposed carboxylic and phosphonic groups: X-ray powder structure and proton conductivity properties. Inorg. Chem. 53, 13220–13226 (2014).

    CAS  Article  Google Scholar 

  29. 29.

    Taddei, M., Donnadio, A., Costantino, F., Vivani, R. & Casciola, M. Synthesis, crystal structure, and proton conductivity of one-dimensional, two-dimensional, and three-dimensional zirconium phosphonates based on glyphosate and glyphosine. Inorg. Chem. 52, 12131–12139 (2013).

    CAS  Article  Google Scholar 

  30. 30.

    Mileo, P. G. M. et al. Proton-conducting phenolate-based Zr metal-organic framework: a joint experimental-modeling investigation. J. Phys. Chem. C 120, 24503–24510 (2016).

    ADS  CAS  Article  Google Scholar 

  31. 31.

    Hassanzadeh Fard, Z. et al. Superprotonic phase change to a robust phosphonate metal–organic ramework. Chem. Mater. 30, 314–318 (2018).

    CAS  Article  Google Scholar 

  32. 32.

    Luo, H. B. et al. Proton conductance of a superior water-stable metal-organic framework and its composite membrane with poly(vinylidene fluoride). Inorg. Chem. 56, 4169–4175 (2017).

    CAS  Article  Google Scholar 

  33. 33.

    Planchais, A. et al. A joint experimental/computational exploration of the dynamics of confined water/Zr-based MOFs systems. J. Phys. Chem. C 118, 14441–14448 (2014).

    CAS  Article  Google Scholar 

  34. 34.

    Yang, F. et al. Proton conductivities in functionalized UiO-66: tuned properties, thermogravimetry mass, and molecular simulation analyses. Cryst. Growth Des. 15, 5827–5833 (2015).

    CAS  Article  Google Scholar 

  35. 35.

    Borges, D. D. et al. Proton transport in a highly conductive porous zirconium-based metal-organic framework: molecular insight. Angew. Chem. Int. Ed. 55, 3919–3924 (2016).

    CAS  Article  Google Scholar 

  36. 36.

    Borges, D. D. et al. Computational exploration of the water concentration dependence of the proton transport in the porous UiO–66(Zr)–(CO2H)2 metal–organic framework. Chem. Mater. 29, 1569–1576 (2017).

    CAS  Article  Google Scholar 

  37. 37.

    Taylor, J. M., Dekura, S., Ikeda, R. & Kitagawa, H. Defect control to enhance proton conductivity in a metal–organic framework. Chem. Mater. 27, 2286–2289 (2015).

    CAS  Article  Google Scholar 

  38. 38.

    Taylor, J. M. et al. The role of a three dimensionally ordered defect sublattice on the acidity of a sulfonated metal-organic framework. J. Am. Chem. Soc. 137, 11498–11506 (2015).

    CAS  Article  Google Scholar 

  39. 39.

    Zhang, G. & Fei, H. Missing metal-linker connectivities in a 3-D robust sulfonate-based metal-organic framework for enhanced proton conductivity. Chem. Commun. 53, 4156–4159 (2017).

    CAS  Article  Google Scholar 

  40. 40.

    Cavka, J. H. et al. A new zirconium inorganic building brick forming metal organic frameworks with exceptional stability. J. Am. Chem. Soc. 130, 13850–13851 (2008).

    Article  Google Scholar 

  41. 41.

    Rogelj, J. et al. Paris Agreement climate proposals need a boost to keep warming well below 2 degrees C. Nature 534, 631–639 (2016).

    ADS  CAS  Article  Google Scholar 

  42. 42.

    Prat, D. et al. CHEM21 selection guide of classical- and less classical-solvents. Green Chem. 18, 288–296 (2016).

    Article  Google Scholar 

  43. 43.

    Ren, J. W. et al. Review on the current practices and efforts towards pilot-scale production of metal-organic frameworks (MOFs). Coord. Chem. Rev. 352, 187–219 (2017).

    CAS  Article  Google Scholar 

  44. 44.

    Rubio-Martinez, M. et al. New synthetic routes towards MOF production at scale. Chem. Soc. Rev. 46, 3453–3480 (2017).

    CAS  Article  Google Scholar 

  45. 45.

    Ragon, F., Chevreau, H., Devic, T., Serre, C. & Horcajada, P. Impact of the nature of the organic spacer on the crystallization kinetics of UiO-66(Zr)-type MOFs. Chem. Eur. J. 21, 7135–7143 (2015).

    CAS  Article  Google Scholar 

  46. 46.

    Mellot-Draznieks, C., Dutour, J. & Ferey, G. Hybrid organic-inorganic frameworks: routes for computational design and structure prediction. Angew. Chem. Int. Ed. 43, 6290–6296 (2004).

    CAS  Article  Google Scholar 

  47. 47.

    Duran, D. et al. PROXIMA 2A—a new fully tunable micro-focus beamline for macromolecular crystallography. J. Phys. Conf. Ser. 425, 012005 (2013).

    Article  Google Scholar 

  48. 48.

    Wißmann, G. et al. Modulated synthesis of Zr-fumarate MOF. Microporous Mesoporous Mater. 152, 64–70 (2012).

    Article  Google Scholar 

  49. 49.

    Furukawa, H. et al. Water adsorption in porous metal-organic frameworks and related materials. J. Am. Chem. Soc. 136, 4369–4381 (2014).

    CAS  Article  Google Scholar 

  50. 50.

    Jönsson, P. G. & Kvick, Å. Precision neutron diffraction structure determination of protein and nucleic acid components. III. The crystal and molecular structure of the amino acid α-glycine. Acta Crystallogr. B 28, 1827–1833 (1972).

    Article  Google Scholar 

  51. 51.

    Yamada, T. & Nankawa, T. High proton conductivity of zinc oxalate coordination polymers mediated by a hydrogen bond with pyridinium. Inorg. Chem. 55, 8267–8270 (2016).

    CAS  Article  Google Scholar 

  52. 52.

    Tu, T. N. et al. High proton conductivity at low relative humidity in an anionic Fe-based metal–organic framework. J. Mater. Chem. A 4, 3638–3641 (2016).

    CAS  Article  Google Scholar 

  53. 53.

    Zou, L. F. et al. Enhancing proton conductivity in a 3D metal-organic framework by the cooperation of guest Me2NH2 (+) cations, water molecules, and host carboxylates. Cryst. Growth Des. 17, 3556–3561 (2017).

    CAS  Article  Google Scholar 

  54. 54.

    Hamrock, S. J. & Yandrasits, M. A. Proton exchange membranes for fuel cell applications. J. Macromol. Sci. Polym. Rev. 46, 219–244 (2006).

    CAS  Article  Google Scholar 

  55. 55.

    Sen, S., Nair, N. N., Yamada, T., Kitagawa, H. & Bharadwaj, P. K. High proton conductivity by a metal-organic framework incorporating Zn8O clusters with aligned imidazolium groups decorating the channels. J. Am. Chem. Soc. 134, 19432–19437 (2012).

    CAS  Article  Google Scholar 

  56. 56.

    Tayade, S. B. et al. Proton conduction in a hydrogen-bonded complex of copper(ii)-bipyridine glycoluril nitrate. Dalton Trans. 46, 6968–6974 (2017).

    CAS  Article  Google Scholar 

  57. 57.

    Jorgensen, W. L. & Jenson, C. Temperature dependence of TIP3P, SPC, and TIP4P water from NPT Monte Carlo simulations: seeking temperatures of maximum density. J. Comput. Chem. 19, 1179–1186 (1998).

    CAS  Article  Google Scholar 

  58. 58.

    Mileo, P. G. M. et al. Highly efficient proton conduction in a three-dimensional titanium hydrogen phosphate. Chem. Mater. 29, 7263–7271 (2017).

    CAS  Article  Google Scholar 

  59. 59.

    Salles, F. et al. Molecular insight into the adsorption and diffusion of water in the versatile hydrophilic/hydrophobic flexible MIL-53(Cr) MOF. J. Phys. Chem. C 115, 10764–10776 (2011).

    CAS  Article  Google Scholar 

Download references


S.W., G.M., and C.S. acknowledge the financial support of the European Community within the Seventh Framework Programme (FP7) under Grant Agreement No. 608490 (Project M4CO2). C.M. and G.M. are grateful for financial support from Institut Universitaire de France (IUF).

Author information




S.W. contributed to the synthesis and general characterization of MIP-202(Zr). M.W. and G.M. performed the computational assisted structure determination of MIL-202(Zr) and the modeling of the proton migration mechanism. L.D. and S.D.-V. carried out the proton conductivity data collection. A.T., J.M., and W.S. collected the synchrotron diffraction data on the single crystal and solved the crystal structure. C.M.-C. conducted the solid-state NMR characterizations. D.H. collected the CD data. C.S. closely supervised the synthesis and characterization part of the work. C.S. and S.D.-V. co-coordinated the entire study. All authors contributed to the writing and discussion.

Corresponding authors

Correspondence to Sabine Devautour-Vinot or Christian Serre.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Wang, S., Wahiduzzaman, M., Davis, L. et al. A robust zirconium amino acid metal-organic framework for proton conduction. Nat Commun 9, 4937 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing