The electrochemical reduction of carbon monoxide is a promising approach for the renewable production of carbon-based fuels and chemicals. Copper shows activity toward multi-carbon products from CO reduction, with reaction selectivity favoring two-carbon products; however, efficient conversion of CO to higher carbon products such as n-propanol, a liquid fuel, has yet to be achieved. We hypothesize that copper adparticles, possessing a high density of under-coordinated atoms, could serve as preferential sites for n-propanol formation. Density functional theory calculations suggest that copper adparticles increase CO binding energy and stabilize two-carbon intermediates, facilitating coupling between adsorbed *CO and two-carbon intermediates to form three-carbon products. We form adparticle-covered catalysts in-situ by mediating catalyst growth with strong CO chemisorption. The new catalysts exhibit an n-propanol Faradaic efficiency of 23% from CO reduction at an n-propanol partial current density of 11 mA cm−2.
The electrochemical reduction of CO2 to fuels using renewable electricity is of interest to close the carbon cycle1,2,3,4,5. Copper shows appreciable selectivity and activity for catalyzing the CO2 reduction reaction (CO2-RR) toward multi-carbon products6,7,8,9. During CO2-RR, *CO (* denotes adsorbed species) is formed and is then further reduced and coupled to produce hydrocarbons and oxygenates7,10,11,12. The direct electrochemical reduction of CO (CO-RR) shares a similar product spectrum to CO2-RR on Cu, and both approaches have seen significant progress in recent years1,7,13,14.
In the creation of Cu electrocatalysts, strategies such as morphology control, facet tailoring, and oxygen engineering have been pursued to improve catalyst activity, selectivity, and durability6,15,16,17,18. Despite major advances in the efficiency and selectivity for C1 and C2 product electrosynthesis via CO2/CO-RR, efficient carbon-chain upgrading to C3 products has remained elusive.
N-propanol, a valuable C3 alcohol that can be used as an engine fuel due to its high octane number of 118, has been reported in prior CO2/CO-RR studies13,15,19,20. For example, an activated Cu mesh catalyst displayed a peak 13% n-propanol Faradaic efficiency (FE) from CO2-RR at −0.9 V vs. a reversible hydrogen electrode (RHE)20. Prior work also reported 10% n-propanol FE using oxide-derived Cu catalysts from CO-RR at a much reduced applied potential of −0.4 V vs. RHE13.
An challenge on the path toward more efficient and productive n-propanol production from CO2/CO-RR arises from both the insufficient surface coverage of *CO and a large activation barrier for C–C coupling21. The inadequate stabilization of *C2 intermediates on pristine Cu surfaces leads to desorption rather than further intermolecular reduction with *CO for C3 generation. It is desirable to develop electrocatalysts that address these limitations.
Electrocatalytic conversion of CO is motivated by the potential to produce higher carbon products and the increasing availability of CO feedstock from industrial steel manufacturing and increasingly via CO2 electroreduction to CO3,22,23. In particular, it has been shown that the two-step CO2 to CO, then CO to C2+ electrosynthesis outperforms the one-step CO2 to C2+ electroproduction based on established technoeconomic analysis owing to the more optimistic performance evaluation of each separate reaction and then overall better efficiency in the former case24. Additionally, feeding CO directly as the feedstock could boost the *CO adsorption on Cu and potentially facilitate the production of higher carbon products.
Here we report an adparticle structure that enables selective n-propanol electrosynthesis from CO-RR. Density functional theory (DFT) calculations suggest that the introduction of adparticles on metallic Cu surfaces facilitates C3 formation due to the increase of *CO surface coverage and *C2 stability, and the decrease of energy barriers towards intermolecular C–C coupling between *CO and *C2. Experimentally, Cu adparticle electrocatalysts are achieved by in-situ electroreduction of an oxide precursor under a rich CO condition. This process, mediated by strong CO chemisorption, enables simultaneously rapid oxide reduction and adparticle growth as disclosed by operando X-ray absorption spectroscopy. The in-situ-derived Cu adparticle electrocatalysts exhibit the highest n-propanol FE of 23% ever achieved on Cu-based materials as well as an exceptional n-propanol partial current density of 11 mA cm−2 at a moderate applied potential of −0.47 V vs. RHE.
In light of previous reports regarding the activation of metal surfaces by promoting surface cluster growth25,26,27,28, we hypothesized that the introduction of adparticles, surface clusters possessing a high population of low-coordinated surface sites, on pristine Cu surfaces could drive C3 production by increasing both the adsorption of CO and the binding energy of *C2 intermediates. Specifically, increased surface concentrations of CO and *C2 would decrease the reaction energy requirement for generating C3 product (i.e., n-propanol). We employed DFT to assess the hypothesis that Cu adparticles could provide such benefits. We include a different number of adatoms on various Cu basal planes to construct one polycrystalline Cu adparticle model with a possibility of possessing various low-coordinated Cu sites (Fig. 1a; Supplementary Table 1).
We first examined CO adsorption energies on various Cu surfaces in the presence and absence of Cu adparticles (Supplementary Fig. 1). Our DFT calculations (Fig. 1b; Supplementary Figs. 2–4; Supplementary Table 2) clearly show that when CO adsorbs on the Cu adparticle, its adsorption can be significantly increased compared to adsorption over the pristine Cu surfaces ((i.e., Cu(100), Cu(111), and Cu(211)). Consequently, the modified Cu surfaces with Cu adparticles can increase CO adsorption densities compared to the pristine Cu surfaces.
As one of the most probable rate-limiting steps for generating *C2 intermediates is the *CO dimerization29,30, we then studied how Cu adparticle influences the reaction energies of the *CO dimerization reactions (Fig. 1c; Supplementary Figs. 5 and 6; Supplementary Table 3). The Cu adparticles on Cu(111) and Cu(211) surfaces show decreased reaction energies for the *CO dimerization step by ~0.8 and ~0.2 eV, respectively, compared to the bare (111) and (211) surfaces. In addition, for the most thermodynamically favorable flat Cu(111) surface, the Cu adparticle can stabilize the adsorption of *C2 intermediates (i.e., *CCH2 and *OCCOH) compared to the pristine Cu(111) surface (Supplementary Tables 4 and 5).
We further studied the effects of Cu adparticle on the reaction energy requirements of the possible intermolecular C–C coupling between *CO and *C2 for n-propanol production. To date, few theoretical and experimental works have investigated reaction mechanisms for CO2/CO-RR to n-propanol. From both theoretical and experimental point of views30,31,32, the possible mechanisms of generating n-propanol can be narrowed down to the two likely coupling steps, CO–OCCOH and CO–CCH2. Based on these previous findings, we computationally examined the CO–OCCOH and CO–CCH2 coupling mechanisms over various Cu surfaces in the presence and absence of Cu adparticle via DFT calculations (Fig. 1d, e; Supplementary Figs. 7–10; Supplementary Tables 6 and 7). The results further indicate that the Cu adparticle on the most favorable Cu surfaces (i.e., Cu(111), Cu(100), and Cu(211) surfaces) could essentially decrease the reaction energies of C–C coupling of *CO and *C2 intermediates proposed (i.e., *OCCOH and *CCH2).
Taken together, the DFT calculations predict that Cu adparticle on pristine Cu surfaces exhibit enhanced catalytic effects (~0.4–0.8 eV decrease in reaction energy) for *CO dimerization or C1–C2 coupling. Some of the adparticle simulation results show a reduction from the base case, for example *CO dimerization on Cu(100) (Fig. 1c) or CO–OCCOH coupling on Cu(111) (Fig. 1d). The reduction, however, is ~0.1 eV, which is approximately the DFT self-interaction error. The simulations indicate that Cu adparticles decrease—on average—the reaction energy required to generating n-propanol during the CO-RR process. In addition, we varied the external fields and surface charge via the Neugebauer and Scheffler method33, and the results support Cu adparticles enhancement of C3 electroproduction during CO-RR (Supplementary Figs. 11–13).
Synthesis and characterization of Cu adparticle catalysts
Inspired by DFT predictions, we sought to control experimentally the growth of Cu adparticles and investigate their impact on CO-RR selectivity and efficiency towards n-propanol production. CO interacts strongly with Cu surfaces and, in particular, chemically adsorbs on oxygen-covered Cu surfaces readily26,27,34,35, resulting in oxygen removal from the Cu lattice and ultimately large-scale Cu surface reconstruction. Thus, we hypothesized that intense CO interaction with copper oxide during the initial electrochemical reduction with oxygen leaching and lattice restructuring would promote the simultaneous growth of adparticles from defects and under-coordinated sites. Accordingly, we prepared nanoparticulate copper oxide pre-catalysts (Fig. 2a–c) via a facile and scalable surfactant-directed wet chemistry method (see Methods for details)36. Then we directly deposited them onto a gas-diffusion electrode (GDE) embedded in a flow cell electrolyzer7,37. In contrast to an H-shaped electrocatalytic cell, the flow cell provides the high CO concentrations near the three-phase interface needed to synthesize the adparticle-covered Cu catalyst (Fig. 2d), and ultimately facilitate CO conversion.
The in-situ-derived Cu catalysts share a similar overall size of ~300 nm with the oxide pre-catalysts (Fig. 2e). However, the surface roughness of the derived Cu catalysts increases significantly and an aggregated nanostructure morphology is observed, resulting from the intense surface reconstruction. High-resolution scanning electron microscopy shows the presence of densified adparticles as a form of aggregated nanoclusters (Fig. 2f, g). A number of possibly rich uncoordinated sites such as edge and corner atoms are also present26, which, from our DFT studies, may function as surface active sites that catalyze CO-RR conversion to n-propanol formation (see below). Further evidence is offered by a high-resolution transmission electron microscopy examination (Fig. 2h–j), where adparticles, clearly distinguished from the Cu backbone, with an average size of ~3.2 nm are observed (Supplementary Fig. 14). Although the resulting adparticles are significantly larger than those simulated, particles of this size are expected to result in a variety of coordination numbers38, as exemplified in the simplified, small-particle DFT simulations.
Operando X-ray absorption spectroscopy
To explore the in-situ growth of adparticles and their electronic nature, we employed operando hard X-ray absorption spectroscopy (hXAS) at the Cu K-edge. With this technique the real-time Cu valence states were tracked during the in-situ metallic reduction process. To verify the role of CO in the surface restructuring, we performed the experiments under CO and helium (inert) gas conditions using a flow cell setup identical to the one used for evaluating CO-RR performance (see below, Supplementary Fig. 15). For the case of Cu reduction under a CO gas environment, the oxide pre-catalysts, consisting dominantly of copper(I) oxide, are quickly reduced to a pure metallic Cu in less than 2 min at an applied potential of −0.44 V vs. RHE in a 1 M KOH electrolyte (Fig. 3a). Consistent results are illustrated by tracking the associated Cu bonding environment with the application of a Fourier transform filter (Fig. 3b). A linear combination fitting analysis of the Cu K-edge hXAS spectra was employed to quantitatively assess the Cu valence composition during the in-situ reaction. We found that the oxide-to-metallic Cu transition under CO gas is two-fold faster than that under He gas (Fig. 3c, d; Supplementary Fig. 16). This suggests that the intense CO chemisorption/reaction on oxygen-containing Cu surface during oxide reduction accelerates oxygen removal, promoting defect formation and driving Cu to reconstruct towards adparticle formation (Fig. 3e)27. Consequently, no trace of oxygen is resolved in fully-derived Cu irrespective of applied gas condition, in agreement with ex-situXRD results (Supplementary Fig. 17). A fitting analysis of the Cu hXAS spectra (Supplementary Fig. 18) further shows a lower Cu coordination in the derived Cu species compared to that in bulk Cu foil, indicating the presence of under-coordinated Cu sites in oxide-derived Cu. In addition, a further in-situ analysis using the more surface- and valence-sensitive Cu L3-edge soft XAS (sXAS) (Supplementary Fig. 19)6,39, compared to the Cu K-edge hXAS, also confirms the metallic Cu nature during CO-RR. These findings, taken together, demonstrate that the initial oxide reduction step can be boosted by CO chemisorption/reaction on the oxygen-covered Cu surface, which then directs the growth of metallic adparticles.
The CO-RR catalytic behavior
Adparticle-enhanced n-propanol electrosynthesis is then tested by a CO-RR product analysis. Potential screening from −0.32 to −0.66 V vs. RHE of Cu adparticles (Fig. 4a) demonstrates a gradual enhancement of CO-RR over the hydrogen evolution reaction with more negative applied potentials. A sharp increase in the FE of C2+ products (FEC2+) from 35% to 72% is achieved within a narrow applied potential range from −0.32 to −0.44 V vs. RHE, and a maximum 89% of FEC2+ is reached at −0.66 V vs. RHE. With increasing overpotential (Fig. 4b), the FE of the product of interest, n-propanol, first shows a dramatic increase from 2.8% at −0.32 V to 21% at −0.39 V vs. RHE, then reaches the peak value of 23% at both −0.44 V and −0.47 V vs. RHE, and finally drops to ~11% at −0.66 V vs. RHE. The decrease is likely due to the depletion of CO at Cu surface at higher reaction rates (Supplementary Fig. 20). While both ethylene and ethanol exhibit an increase of FE with increasing overpotential, the FE of acetate first decreases and then reaches a plateau, which suggests a possible relationship between acetate and C2+ chemicals. In particular, a prompt product switchover between acetate and ethylene/n-propanol at a narrow potential window from −0.3 to −0.4 V vs. RHE, indicates that acetate, ethylene, and n-propanol may share similar pathways. However, these pathways diverge depending on applied potentials, consistent with previous analysis40.
To correlate the adparticle structure with the observed increase in n-propanol production from CO-RR, we compared performance against two different control samples. The first control was commercially available Cu nanoparticles (Cu NPs) with a size of ~100 nm. The formation of adparticles was not observed on these Cu NPs after CO-RR (Supplementary Fig. 21). The second control sample was prepared by in-situ reduction of oxide pre-catalysts under a nitrogen (inert) gas condition instead of using CO. In the absence of CO during the initial metallic reduction, the surface did not reconstruct to form adparticles, but instead formed rich grain boundaries on the surface of derived Cu (Supplementary Fig. 22). After CO-RR, the Cu surface displays an abundant amount of nanobumps (denoted as Cu NBs) with an average size of ~7.5 nm (Supplementary Fig. 23). These nanobumps appear to emerge upon the elimination of surface grain boundaries during the CO-RR reaction. The implication is that strong CO interactions during CO-RR with under-coordinated Cu sites can cause the samples that are reduced under purely N2 conditions to restructure. This restructuring and elimination of grain boundaries relieves strain and forms undulate Cu NBs26; however, the formation of adparticles on Cu NBs is not observed (Supplementary Fig. 23). A direct comparison of the CO-RR performance among these three Cu species (Figs 4c, d; Supplementary Table 8) demonstrates the superior selectivity and activity of the Cu adparticle catalysts (Cu ADs; Supplementary Fig. 24) towards n-propanol production. Compared to the 23% FE for n-propanol achieved on the adparticle catalysts, the Cu NBs deliver a peak 16% of FEn-propanol at −0.44 V vs. RHE while Cu NPs show the least n-propanol selectivity with a maximum 12% of FEn-propanol obtained at −0.47 V vs. RHE. A further FEn-propanol over FEC2 ratio comparison (Fig. 4e) suggests the selective n-propanol generation enabled by adparticles, where Cu AD presents a two-fold improvement over Cu NP. After normalizing to the electrochemical surface area, an intrinsic n-propanol activity of Cu AD catalysts is confirmed (Supplementary Figs. 25 and 26; Supplementary Table 9), in accordance with our DFT results showing the decreased intermolecular coupling barriers of *CO and *C2 intermediates on various Cu surfaces with the inclusion of adparticles. To further exclude additional morphology effects among Cu AD, NB, and NP species on CO-RR performance, we thermal-annealed Cu AD catalysts at 150 ℃ under N2 gas condition. This processing erases the adparticle texture while maintaining the overall morphology (Supplementary Fig. 27). A dramatic decrease of FEn-propanol commensurate with the increase of FEethylene is observed, further supporting the adparticle role in promoting n-propanol production. Compared to a nanobump (an undulate Cu surface), an adparticle (an isolated cluster) possesses a higher population of low-coordinated surface sites and thus a stronger CO chemisorption38. The larger surface area of an adparticle also has a higher chance of offering optimized geometries for CO adsorption and, therefore, more efficient n-propanol formation (Supplementary Fig. 2). By comparing to existing reports (Supplementary Table 10), adparticle-assisted n-propanol formation with an FEn-propanol up to 23% associated with a jn-propanol of 11 mA cm−2 surpasses the best reported ~13% and 1.74 mA cm−2, achieved separately, by a 1.8-fold selectivity and a six-fold activity enhancements. Additionally, an exceptionally high n-propanol partial current density of ~46 mA cm−2 is also achieved from Cu AD at −0.66 V vs. RHE with an appreciable FEn-propanol of ~11%. These results, taken together, demonstrate that adparticle-covered Cu surfaces are active and selective for n-propanol generation from CO-RR.
To assess the n-propanol generation process, we tested the Cu AD catalysts at reduced CO partial pressures (Fig. 5). Note that the decrease of CO partial pressure in gas feedstock would directly reduce the local CO concentration at the Cu catalysts surface (Fig. 5a). Gas mixtures of CO and N2 with a composition of 15%, 35%, and 65% CO, respectively, at 1 atm were introduced at a constant potential of −0.44 V vs. RHE in 1 M KOH. As CO partial pressure is increased, we observe an increase of FEn-propanol from 11% to 23% commensurate with a decrease of FEethylene from ~42% to ~30% (Fig. 5b). The FE changes of ethanol and acetate are relatively small at all CO partial pressures. The ratio of FEn-propanol to FEC2 (Fig. 5c) shows the increase of n-propanol production at the expense of C2 (mainly ethylene). The shift from ethylene to n-propanol is consistent with *C2 intermediates that contribute to ethylene formation (such as *OCCOH and *CCH2; Fig. 1) being major intermediates for n-propanol as well. The similar ~11% FEn-propanol obtained on both Cu NP catalysts under 100% CO and Cu AD catalysts under 15% CO highlights the role of adparticles in concentrating CO and stabilizing *C2 intermediates for n-propanol generation.
In this study, DFT and experimental results, taken together, portray an efficient Cu AD electrocatalyst enabling selective n-propanol production from CO-RR. It has been previously reported that derived Cu from the electrochemical reduction of oxide precursors would endure morphology reconstruction by exposing low-coordinated sites6. Meanwhile, strong CO interaction with low-coordinated Cu atoms would weaken the Cu–Cu bond and arouse large-scale Cu surface restructuring25,26,27. Therefore, the electroreduction of copper oxide with intense CO interaction enabled by the application of a flow cell could offer possibilities of forming new Cu structures, i.e., adparticle. Here we ascribed the adparticle growth to the CO-assisted rapid oxide reduction and Cu surface rearrangement under an in-situ flow cell CO-RR condition (Supplementary Fig. 15), in which abundant CO preferentially chemisorbs on defective sites during oxygen leaching, accelerating oxygen removal from the surface and driving Cu to reconstruct into adparticles as revealed from operando hXAS studies. Without the presence of intense CO reaction, the formation of dense grain boundary is observed (Supplementary Fig. 22a–c). It agrees with previous reports where oxide reduction carried out under a negligible CO environment (CO saturated KOH solution) results in grain boundary formation13,18. We further note that these grain boundaries are not stable under an intense CO reaction, which leads to the Cu surface restructuring towards nanobumps formation (Supplementary Fig. 22d, e) with the elimination of gain boundaries. Compared to Cu NP control, the inclusion of densified under-coordinated sites (e.g., adparticles and nanobumps) on Cu backbone significantly increases the density of active sites and accelerates the CO-RR reaction rates.
By carrying out a CO partial pressure analysis, we found a product formation trend where an increase of CO partial pressure favors n-propanol formation at the expense of C2 (mainly ethylene) generation. It indicates that intermolecular C–C coupling of CO and ethylene precursors contributes to n-propanol formation, in agreement with our DFT results. An analysis between the CO partial pressure and jn-propanol shows their linear correlation with a slope of ~1 (Supplementary Fig. 28), suggesting the first-order dependence of jn-propanol on local CO concentration41. A proton concentration dependency on n-propanol production was also examined (Supplementary Fig. 29). With a range of 0.5–5 M KOH, 1 M KOH is found to produce the highest FEn-propanol, a further increase of KOH concentration prioritizes the acetate formation due to the attack of n-propanol/ethylene intermediates in the concentrated OH− solution13. As previously reported, CO preferably bounds to low-coordinated Cu atoms25,26 which also provide means of stabilizing intermediate species18,42, insinuating the role of adparticle for concentrating CO and stabilizing *C2 being further reduced to C3. Indeed, by lowering the CO partial pressure to as low as 15%, Cu AD catalysts achieve an FEn-propanol of 11% (Fig. 5b) comparable to the FEn-propanol obtained on Cu NP controls under 100% CO condition (Fig. 4c). With this unique adparticle structure immobilized on bulky Cu surfaces, simulation results reveal that adparticle offers possibilities of increasing CO adsorption, promoting *CO dimerization, stabilizing *C2 intermediates, lowering energy barriers of intermolecular C–C coupling between *CO and *C2, and ultimately facilitating the formation of C3 chemicals.
In summary, a control over under-coordinated sites is essential for optimizing hetero-electrocatalysis. We have demonstrated that adparticle-covered Cu catalysts capable of enhancing CO adsorption and stabilizing *C2 intermediates. In CO-RR testing, Cu adparticle electrocatalysts promoted n-propanol production up to 23% FEn-propanol commensurate with an exceptional n-propanol partial current density of 11 mA cm−2. This adparticle approach not only provides an avenue to high-chain carbon products formation under CO-RR, but may also be extended to improve the performance of other metal catalysts.
DFT calculations were performed using the Vienna Ab Initio Simulation Package (VASP) code43,44. To treat the exchange–correlation interactions and solve the ion–electron interactions in a periodic boundary system, we chose Perdew–Burke–Ernzerhof (PBE)45 functionals and the projector-augmented wave (PAW) method46. We chose the most stable Cu(111) flat surface, the most active Cu(100) surface, and the most stable Cu(211) step surface in our study to validate the hypothesis that the Cu adparticles can decrease the reaction energies of the CO=CO dimerization and the C1–C2 coupling and, therefore, increase the Faraday efficiency (FE) of n-propanol production during electrochemical CO-RR. For the p(4 × 4) Cu(111) and Cu(100) supercell, a Monkhorst–Pack mesh47 with a grid of (3 × 3 × 1) k points and a plane wave expansion up to 400 eV was employed. In addition, for the p(2 × 4) Cu(211) facet, a Monkhorst–Pack mesh47 with a grid of (4 × 4 × 1) k points and a plane wave expansion up to 400 eV was used. All of the examined surfaces have a ~15 Å vacuum layer separation between each periodic unit cell. We also examined the CO adsorption energy (Supplementary Fig. 30) and reaction energy of CO dimerization (Supplementary Fig. 31) using RPBE functional, which is more accurate for the catalytic intermediate adsorption on single-crystal late transition-metal surfaces that involve pure chemisorption (i.e., CO over Cu)48,49. The main trend that Cu adparticles increase the adsorption strength of CO and decrease the reaction energies of CO dimerization is supported by the RPBE functional results. Computational details are included in the Supplementary Methods.
Preparation of oxide pre-catalysts
All reagents used in this work were from Sigma Aldrich without further purification. A surfactant-directed synthesis method was used to prepare the copper oxide precursor36. In general, 4.2 g triblock copolymer Pluronic P123 (MW 5800) was uniformly dispersed in 210 mL deionized water under a continuous stirring in a water bath at room temperature (~20 ℃) for 3 h to make clear solution I. Separately, 0.4 g copper(II) fluoride (CuF2·2H2O) was dissolved in 20 mL aqueous solution with the inclusion of 3 mL concentrated ammonia solution (~30%) under constant stirring to prepare dark blue solution II. Then solution II was quickly added to solution I under stirring for 30 min to obtain dark blue solution III. During this time, a clear solution IV containing 0.6 M l-ascorbic acid was made. Later, ~45 mL solution IV was added into solution III in a dropwise manner to obtain a final orange suspension. The final product was collected by repeating three times of centrifuging and ethanol rinsing, and dried overnight under vacuum at room temperature (~20 ℃).
Preparation of GDE
Ten milligrams of as-made oxide pre-catalysts were firstly dispersed in 1 mL methanol with the inclusion of 40 μL Nafion solution (~5 wt%) under constant stirring for 15 min, As-prepared suspension was then air-brushed onto a 2 × 4 cm2 (cut into two pieces after for two separate tests) Freudenberg gas-diffusion layer (GDL; Fuel Cell Store) using nitrogen as the carrier gas to make GDE, which was vacuum dried for at least 5 h before use. The loading amount of oxide precursor was determined to be ~0.75 mg cm−2 by the net weight gain before and after air-brushing.
Surface morphology was analyzed using a Hitachi SU9000 SEM/STEM at 2 kV. A Hitachi HF-3300 instrument with an acceleration voltage of 100 kV was employed for TEM analysis. For ultrahigh resolution TEM work an aberration-corrected FEI Titan 80-300 was used (200kV). XRD was performed on a MiniFlex600 instrument with a copper target (λ = 1.54056 Å) at room temperature. Operando hXAS measurements were conducted at 9BM and 20BM beamlines of the Advanced Photon Source (APS, Argonne National Laboratory, Lemont, Illinois), in partnership with the Canadian Light Source (CLS) in Saskatoon (Saskatchewan). In-situ soft X-ray absorption spectroscopy was carried out at the 8.0.1 beamline of the Advanced Light Source (ALS; Lawrence Berkeley National Laboratory, Berkeley, California).
Electroreduction of carbon monoxide
All CO reduction experiments were carried out in a gas–catholyte–anolyte three-compartment flow cell architecture7 using a three-electrode system, where as-made GDE, Ag/AgCl (with 1 M KCl solution filled), and nickel foam (1.6 mm thickness; MTI Corporation) were used as cathode, reference electrode, and anode, respectively. The catholyte and anolyte compartments were separated by an anion exchange membrane (Fumasep FAA-PK-130). The cell was powered by an electrochemical workstation (Autolab PGSTAT302N), and an electrolyte of 1 M KOH was used all times. During the CO-RR test, 1 M KOH was directed separately into the cathode and anode compartments using two variable-speed peristaltic tubing pumps (Control Company 3385) and circulated through the electrochemical cell. CO gas was flowed through the gas compartment at the backside of GDE with a flow rate of 30 standard cubic centimeters per minute (s.c.c.m.). Applied cathode potentials after iR compensation were converted to the RHE reference scale using ERHE = EAg/AgCl + 0.235 V + 0.059 × pH. In this study, both liquid and gas products were collected for identifications and quantifications. Liquid product dissolved in catholyte was identified and quantified with one-dimensional 1H nuclear magnetic resonance spectroscopy (1H NMR) using a Agilent DD2 500 spectrometer, in which a diluted dimethyl sulfoxide in D2O was used as an internal standard (Supplementary Fig. 32). Gas outlet from flow cell experiment was analyzed with a gas chromatograph (GC; PerkinElmer Clarus 680) equipped with a Molecular Sieve 5A capillary column and a packed Carboxen-1000 column. By using Argon (Linde, 99.999%) as a carrier gas, a thermal conductivity detector and a flame ionization detector equipped with a methanizer loaded in GC instrument were used to quantify hydrogen and ethylene, respectively.
Modeling of CO diffusion across the gas-diffusion layer
The concentration of CO in the electrolyte and present at the catalyst’s surface was determined using a 1D reaction-diffusion model. The model is adapted from a previous report which modeled the diffusion of CO2 across a gas-diffusion layer for various electrolytes, current densities, and pressures7. Unlike the CO2 model, CO diffusion into the electrolyte at 0 mA cm−2 does not directly affect the local pH or change the concentration of CO or OH− as a function of distance into the electrolyte. The governing equations for the simulation are shown below and extend from the gas–liquid interface of the gas-diffusion layer at x = 0 µm to an assumed diffusion layer boundary thickness of x = 500 µm into the electrolyte.
where RCO and ROH account for the consumption of CO in the reduction reaction and the production of OH−, respectively. These reactions are assumed to occur homogeneously throughout the catalyst layer such that the source and sink of CO and OH− are spatially dependent:
where F is the Faraday’s constant and is taken as 96485 C mol−1 and j is the geometric current density. As was done previously, a catalyst layer porosity, ε, of 60% was assumed. Based upon the experimental results, product selectivities of 15% hydrogen, 50% ethylene+ethanol, 10% acetate, and 25% n-propanol are assumed for all simulations to approximately account for the number of electrons transferred per CO molecule consumed. A reaction thickness of 100 nm was assumed for the catalyst layer (Lcatalyst = 100 nm). The maximum solubility of CO in the electrolyte was modeled using Henry’s constant at 1 atm and 298 K as well as taking salting out effects into account via the Sechenov equation.
A no-flux boundary condition was imposed at the left-hand boundary for OH− while the concentration of CO was initially described by the solubility of CO in the imposed KOH concentration and partial pressure conditions. Both CO and KOH were fixed to their bulk electrolyte concentrations at the boundary layer thickness of 500 µm. The concentration profiles of CO and OH− were then found at steady state for a variety of KOH concentrations, partial pressures, and current densities.
The data that support the findings of this study are available from the corresponding author on reasonable request
Zhang, L., Zhao, Z. J. & Gong, J. L. Nanostructured materials for heterogeneous electrocatalytic CO2 reduction and their related reaction mechanisms. Angew. Chem. Int. Ed. 56, 11326–11353 (2017).
Zhu, D. D., Liu, J. L. & Qiao, S. Z. Recent advances in inorganic heterogeneous electrocatalysts for reduction of carbon dioxide. Adv. Mater. 28, 3423–3452 (2016).
Liu, M. et al. Enhanced electrocatalytic CO2 reduction via field-induced reagent concentration. Nature 537, 382–386 (2016).
Wu, J. J. et al. A metal-free electrocatalyst for carbon dioxide reduction to multi-carbon hydrocarbons and oxygenates. Nat. Commun. 7, 13869 (2016).
Ren, D., Fong, J. H. & Yeo, B. S. The effects of currents and potentials on the selectivities of copper toward carbon dioxide electroreduction. Nat. Commun. 9, 925 (2018).
De Luna, P. et al. Catalyst electro-redeposition controls morphology and oxidation state for selective carbon dioxide reduction. Nat. Catal. 1, 103–110 (2018).
Dinh, C. T. et al. Sustained high-selectivity CO2 electroreduction to ethylene via hydroxide-mediated catalysis at an abrupt reaction interface. Science 360, 783–787 (2018).
Weng, Z. et al. Active sites of copper-complex catalytic materials for electrochemical carbon dioxide reduction. Nat. Commun. 9, 415 (2018).
Zhuang, T. T. et al. Steering post-C-C coupling selectivity enables high efficiency electroreduction of carbon dioxide to multi-carbon alcohols. Nat. Catal. 1, 421–428 (2018).
Xiao, H., Cheng, T. & Goddard, W. A. Atomistic mechanisms underlying selectivities in C1 and C2 products from electrochemical reduction of CO on Cu(111). J. Am. Chem. Soc. 139, 130–136 (2017).
Hori, Y., Murata, A., Takahashi, R. & Suzuki, S. Electroreduction of CO to CH4 and C2H4 at a copper electrode in aqueous-solutions at ambient-temperature and pressure. J. Am. Chem. Soc. 109, 5022–5023 (1987).
Hori, Y., Takahashi, R., Yoshinami, Y. & Murata, A. Electrochemical reduction of CO at a copper electrode. J. Phys. Chem. B 101, 7075–7081 (1997).
Li, C. W., Ciston, J. & Kanan, M. W. Electroreduction of carbon monoxide to liquid fuel on oxide-derived nanocrystalline copper. Nature 508, 504–507 (2014).
Feng, X. F., Jiang, K. L., Fan, S. S. & Kanan, M. W. A direct grain-boundary-activity correlation for CO electroreduction on Cu nanoparticles. ACS Cent. Sci. 2, 169–174 (2016).
Kim, D., Kley, C. S., Li, Y. F. & Yang, P. D. Copper nanoparticle ensembles for selective electroreduction of CO2 to C2-C3 products. Proc. Natl. Acad. Sci. USA 114, 10560–10565 (2017).
Loiudice, A. et al. Tailoring copper nanocrystals towards C2 products in electrochemical CO2 reduction. Angew. Chem. Int. Ed. 55, 5789–5792 (2016).
Mistry, H. et al. Highly selective plasma-activated copper catalysts for carbon dioxide reduction to ethylene. Nat. Commun. 7, 12123 (2016).
Verdaguer-Casadevall, A. et al. Probing the active surface sites for CO reduction on oxide-derived copper electrocatalysts. J. Am. Chem. Soc. 137, 9808–9811 (2015).
Ren, D., Wong, N. T., Handoko, A. D., Huang, Y. & Yeo, B. S. Mechanistic insights into the enhanced activity and stability of agglomerated Cu nanocrystals for the electrochemical reduction of carbon dioxide to n-propanol. J. Phys. Chem. Lett. 7, 20–24 (2016).
Rahaman, M., Dutta, A., Zanetti, A. & Broekmann, P. Electrochemical reduction of CO2 into multicarbon alcohols on activated Cu mesh catalysts: an identical location (IL) study. ACS Catal. 7, 7946–7956 (2017).
Liu, X. Y. et al. Understanding trends in electrochemical carbon dioxide reduction rates. Nat. Commun. 8, 15438 (2017).
Shen, J. et al. Electrocatalytic reduction of carbon dioxide to carbon monoxide and methane at an immobilized cobalt protoporphyrin. Nat. Commun. 6, 9177 (2015).
Zhang, X. et al. Highly selective and active CO2 reduction electro-catalysts based on cobalt phthalocyanine/carbon nanotube hybrid structures. Nat. Commun. 8, 14675 (2017).
Spurgeon, J. M. & Kumar, B. A comparative technoeconomic analysis of pathways for commercial electrochemical CO2 reduction to liquid products. Energy Environ. Sci. 11, 1536–1551 (2018).
Eren, B. et al. One-dimensional nanoclustering of the Cu(100) surface under CO gas in the mbar pressure range. Surf. Sci. 651, 210–214 (2016).
Eren, B. et al. Activation of Cu(111) surface by decomposition into nanoclusters driven by CO adsorption. Science 351, 475–478 (2016).
Eren, B., Liu, Z. Y., Stacchiola, D., Somorjai, G. A. & Salmeron, M. Structural changes of Cu(110) and Cu(110)-(2×1)-O surfaces under carbon monoxide in the Torr pressure range studied with scanning tunneling microscopy and infrared reflection absorption spectroscopy. J. Phys. Chem. C 120, 8227–8231 (2016).
Kim, J., Noh, M. C., Doh, W. H. & Park, J. Y. Thermal evolution and instability of CO-induced platinum clusters on the Pt(557) surface at ambient pressure. J. Am. Chem. Soc. 138, 1110–1113 (2016).
Xiao, H., Cheng, T., Goddard, W. A. & Sundararaman, R. Mechanistic explanation of the pH dependence and onset potentials for hydrocarbon products from electrochemical reduction of CO on Cu (111). J. Am. Chem. Soc. 138, 483–486 (2016).
Yang, K. D., Lee, C. W., Jin, K., Im, S. W. & Nam, K. T. Current status and bioinspired perspective of electrochemical conversion of CO2 to a long-chain hydrocarbon. J. Phys. Chem. Lett. 8, 538–545 (2017).
Kortlever, R., Shen, J., Schouten, K. J. P., Calle-Vallejo, F. & Koper, M. T. M. Catalysts and reaction pathways for the electrochemical reduction of carbon dioxide. J. Phys. Chem. Lett. 6, 4073–4082 (2015).
Cheng, T., Xiao, H. & Goddard, W. A. Full atomistic reaction mechanism with kinetics for CO reduction on Cu(100) from ab initio molecular dynamics free-energy calculations at 298 K. Proc. Natl. Acad. Sci. USA 114, 1795–1800 (2017).
Neugebauer, J. & Scheffler, M. Adsorbate-substrate and adsorbate-adsorbate interactions of Na and K adlayers on Al(111). Phys. Rev. B 46, 16067–16080 (1992).
Crew, W. W. & Madix, R. J. A scanning tunneling microscopy study of the oxidation of CO on Cu(110) at 400 K: site specificity and reaction kinetics. Surf. Sci. 349, 275–293 (1996).
Crew, W. W. & Madix, R. J. CO adsorption and oxidation on oxygen precovered Cu(110) at 150 K: reactivity of two types of adsorbed atomic oxygen determined by scanning tunneling microscopy. Surf. Sci. 356, 1–18 (1996).
Shang, Y., Zhang, D. F. & Guo, L. CuCl-intermediated construction of short-range-ordered Cu2O mesoporous spheres with excellent adsorption performance. J. Mater. Chem. 22, 856–861 (2012).
Ma, S. C. et al. One-step electrosynthesis of ethylene and ethanol from CO2 in an alkaline electrolyzer. J. Power Sources 301, 219–228 (2016).
Reske, R., Mistry, H., Behafarid, F., Cuenya, B. R. & Strasser, P. Particle size effects in the catalytic electroreduction of CO2 on Cu nanoparticles. J. Am. Chem. Soc. 136, 6978–6986 (2014).
Velasco-Velez, J. J. et al. The structure of interfacial water on gold electrodes studied by X-ray absorption spectroscopy. Science 346, 831–834 (2014).
Garza, A. J., Bell, A. T. & Head-Gordon, M. Mechanism of CO2 reduction at copper surfaces: pathways to C2 products. ACS Catal. 8, 1490–1499 (2018).
Lee, C. W. et al. Selective electrochemical production of formate from carbon dioxide with bismuth-based catalysts in an aqueous electrolyte. ACS Catal. 8, 931–937 (2018).
Cheng, T., Xiao, H. & Goddard, W. A. Nature of the active sites for CO reduction on copper nanoparticles; suggestions for optimizing performance. J. Am. Chem. Soc. 139, 11642–11645 (2017).
Kresse, G. & Furthmuller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Payne, M. C., Teter, M. P., Allan, D. C., Arias, T. A. & Joannopoulos, J. D. Iterative minimization techniques for ab initio total-energy calculations: molecular dynamics and conjugate gradients. Rev. Mod. Phys. 64, 1045–1097 (1992).
Monkhorst, H. J. & Pack, J. D. Special points for Brillouin-zone integrations. Phys. Rev. B 13, 5188–5192 (1976).
Gajdos, M., Eichler, A. & Hafner, J. CO adsorption on close-packed transition and noble metal surfaces: trends from ab initio calculations. J. Phys. Condens. Matter 16, 1141–1164 (2004).
Hensley, A. J. R. et al. DFT-based method for more accurate adsorption energies: an adaptive sum of energies from RPBE and vdW density functionals. J. Phys. Chem. C 121, 4937–4945 (2017).
This work was financially supported by the Ontario Research Fund Research-Excellence Program, the Natural Sciences and Engineering Research Council (NSERC) of Canada, the CIFAR Bio-Inspired Solar Energy program, and the University of Toronto Connaught grant. Synchrotron work was carried out at the Advanced Photon Source (APS) in partnership with the Canadian Light Source (CLS), and the Advanced Light Source. APS in Argonne National Laboratory and the ALS in Lawrence Berkeley National Laboratory are supported by the Office of Basic Energy Sciences of the US Department of Energy under Contract No. DE-AC02-06CH11357 and No. DE-AC02-05CH11231, respectively. CLS is funded by NSERC, the Canada Foundation for Innovation (CFI), National Research Council (NRC), Canadian Institute for Health Research (CIHR), and the University of Saskatchewan. Part of the HRTEM work (Titan 80-300) was carried out at the Canadian Centre for Electron Microscopy, a facility supported by CFI under the Major Science Initiative program, NSERC and McMaster University. All DFT computations were performed on the IBM BlueGene/Q supercomputer with support from the Southern Ontario Smart Computing Innovation Platform (SOSCIP). SOSCIP is funded by the Federal Economic Development Agency of Southern Ontario, the Province of Ontario, IBM Canada Ltd., Ontario Centres of Excellence, Mitacs and 15 Ontario academic member institutions. The authors thank Dr. M.J. Ward, Dr. Z.Q. Wang, and Mr. J.T. Cheng for technical support at 20BM beamline of APS. C.Z. gratefully acknowledges a scholarship under the International Academic Exchange Fund for Joint Ph.D. Student from Tianjin University. D.S. gratefully acknowledges support from a NSERC E.W.R. Steacie Memorial Fellowship. T.B. thanks Hatch for a Graduate Scholarship for Sustainable Energy Research. P.D.L. thanks NSERC for financial support in the form of the Canada Graduate Scholarship—Doctoral (CGS-D) award. J.L. and M.I.S. acknowledge the Banting Postdoctoral Fellowships program.
The authors declare no competing interests
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
About this article
Cite this article
Li, J., Che, F., Pang, Y. et al. Copper adparticle enabled selective electrosynthesis of n-propanol. Nat Commun 9, 4614 (2018). https://doi.org/10.1038/s41467-018-07032-0
Nature Communications (2021)
Low coordination number copper catalysts for electrochemical CO2 methanation in a membrane electrode assembly
Nature Communications (2021)
Nature Communications (2021)
Transactions of Tianjin University (2021)
Electrochemical Energy Reviews (2021)