Rechargeable potassium-ion batteries with honeycomb-layered tellurates as high voltage cathodes and fast potassium-ion conductors


Rechargeable potassium-ion batteries have been gaining traction as not only promising low-cost alternatives to lithium-ion technology, but also as high-voltage energy storage systems. However, their development and sustainability are plagued by the lack of suitable electrode materials capable of allowing the reversible insertion of the large potassium ions. Here, exploration of the database for potassium-based materials has led us to discover potassium ion conducting layered honeycomb frameworks. They show the capability of reversible insertion of potassium ions at high voltages (~4 V for K2Ni2TeO6) in stable ionic liquids based on potassium bis(trifluorosulfonyl) imide, and exhibit remarkable ionic conductivities e.g. ~0.01 mS cm−1 at 298 K and ~40 mS cm–1 at 573 K for K2Mg2TeO6. In addition to enlisting fast potassium ion conductors that can be utilised as solid electrolytes, these layered honeycomb frameworks deliver the highest voltages amongst layered cathodes, becoming prime candidates for the advancement of high-energy density potassium-ion batteries.


With the advent of global warming, the urgency of meeting the world’s gigantic energy demands in a sustainable and ecological manner continues to grow exponentially. Lithium-ion (Li-ion) battery technology, which has been presented as an alternative solution to cater for the multifarious energy demands, is already being impeded by the threat of a projected paucity of its terrestrial mineral reserves. To address the escalating demand for large-scale rechargeable batteries, particularly for volume/weight-less-dependent applications such as the electric grid system, the development of de novo sustainable alternatives with comparable performance to that of Li-ion batteries has become a worldwide imperative1. Potassium (K), which is a low-cost, abundant and easily extractable element (that is, a large-ion lithophile element) unlike Li, is increasingly becoming favourable as an alternative choice. Another benefit is that K exhibits similar electrochemical properties to Li (technically speaking, K+/K redox couple tends to show a lower potential than Li+/Li in non-aqueous electrolytes), indicating that K-ion extraction/insertion chemistry can be applied to a similar high-voltage rechargeable battery concept as Li-ion system2. However, the advancement of K-ion batteries is heavily impeded by lack of materials that can facilitate the reversible insertion of the large K-ions and a limited understanding of the mechanistic aspects underlying the electrochemistry and safe utilisation of potassium-based compounds.

Potassium-based compounds are of particular interest in materials science owing to their myriad technological aspects, such as agrochemical and catalytic properties, magnetism, superconductivity, etc. Potassium adopts innumerable polyhedral coordination;3 thus, K-based compounds have an abundance of piquant physical properties such as ferroelectricity, piezoelectricity, pyroelectricity, multiferroicity, thermoelectricity, and optics4,5,6,7,8,9,10,11,12,13. K-based compounds have also found their niche application in energy storage as host frameworks for reversible reinsertion of Li and Na electrodes. Such compounds include lepidocrocite K0.8Li0.27Ti1.73O414, K2Ti6O1315, KFeF316, KASO4F (A = Fe, Co)17, KVPO4F18, fedotovite K2Cu3O(SO4)319, K2[(VO)2(HPO4)2(C2O4)]20, KV3O821, K1.33Fe11O1722, K2D2(SO4)3 (D = Cu, Fe)19, KxV2O521, Prussian analogues23, amongst others. Indeed, a great variety of K-based minerals and compounds have been documented, and most have yet to have their electrochemical properties studied.

In spite of the largely unexplored space of K-based materials, few K-ion insertion host materials have been reported. Whilst major breakthroughs have been reported in the use of graphite24, phosphorus25, oxides (such as K2Ti8O1726, K2Ti4O927, Co3O4-Fe2O3 composites28, etc.) and sulphides (namely, MoS229 and SnS230) as anode materials, identifying cathode frameworks that can facilitate reversible K-ion insertion is a daunting challenge. This can be attributed to the huge stress imparted in the host structures during K-ion reinsertion leading to structural collapse, as well as the difficulties in the preparation and handling of these materials due to hygroscopicity, thus debilitating the choice of cathode materials. Recently, however, feasible cathode materials such as K3V2(PO4)331, KVPO4F32, KVOPO432,ibid and KVP2O733 have been reported. They constitute the broad class of polyanionic compounds that show high voltage coupled with excellent thermal stability. A flurry of reports in recent years have also emerged on the use of organic moieties such as Prussian analogues as cathode hosts for K-ion34,35,36,37,38, as they not only are of low cost, but can also deliver relatively high voltage at moderate capacities. Layered transition metal oxide analogues of classic Li- and Na-ion cathodes, for instance, KxMnO239,40, KxCoO241,42, etc. have also been reported. Amongst them, reversible K-ion insertion at moderate energy density coupled with fast K-ion diffusion rate was observed in layered metal oxides adopting P2-type coordination (prismatic coordination of the K-ions and 2 brucite-like layers in the unit cell). P2-layered oxides with multi-transition metals such as K2/3Ni1/6Co1/6Mn2/3O243 and K2/3Fe1/2Mn1/2O244 have further been shown to deliver enhanced electrochemical performance compared to their parent components (i.e., KxMO2 (M = Mn, Co and Fe). This information was very beneficial to us when looking for related layered cathode frameworks with greater potentials.

Pursuing new layered cathode compounds led us to investigate the growing family of honeycomb-structured multi-transition metal-layered oxides. Besides the fascinating ion-exchange aspect that leads to the synthesis of, for instance, silver-based oxides that present very fast ion mobility45, honeycomb frameworks have been shown to be apposite structures for studying a diverse range of enigmatic magnetic properties, such as the Heisenberg–Kitaev model46. Therefore synthesis of new multifunctional K-based honeycomb cathode structures by suitable transition metal variations can be anticipated.

Herein, for the first time, a class of honeycomb-structured potassium-based tellurate compounds K2/3M2/3Te1/3O2 (M = transition metal) (hereafter denoted as K2M2TeO6) with rich structural chemistry and interesting physical properties is being presented. Their analogues in the mineral world are the Dagenaisite Zn3TeO6 and Mcalpineite Cu3TeO6 phases that adopt honeycomb-layered frameworks47,48. Taking advantage of the tellurate moiety, new designs of high-voltage cathode materials can be anticipated. Moreover, the substitution of Zn or Cu with potassium (K) and M-3d metal cations induces a transition in symmetry to hexagonal-ordered phases, which is unveiled with the structural analyses of K2Ni2TeO6 as a prototype functional material. This study shows that these layered tellurates are not only high-voltage cathode hosts for rechargeable K-ion batteries (particularly for K2Ni2TeO6 and its nickel-based derivatives), but are also a prolific scientific ground in the search for K-based compounds exhibiting high K-ion conductivities.


Material characterisation and crystal structure description

New tellurate compounds K2M2TeO6 (M = Ni, Mg, Zn, Co and Cu) were synthesised by a conventional solid-state ceramics route (see details furnished in Methods section). Figure 1a presents the powder X-ray diffraction (PXRD) pattern of K2Ni2TeO6 (equivalently written as K2/3Ni2/3Te1/3O2), for which high-quality synchrotron X-ray data were collected. Bragg peaks, taking into consideration the extinction conditions, indicate unambiguously that the titled compound crystallises in a centrosymmetric hexagonal space group (P63/mcm) with the following cell parameters: ahex = 5.2606(1) Å, chex = 12.4669(3) Å (V = 298.79(1) Å3). No extra reflections from impurity phases were observed at the 0.5% detection limit. In addition, ICP-AES and SEM-EDX analysis confirmed the composition of K2Ni2TeO6 was as anticipated (Supplementary Fig. 1 and Table 1). Inspection using high-resolution TEM (Fig. 1a inset), further reveals an array of pseudo-hexagonal symmetry dots indexable, using the hexagonal settings, as the [100] and [001] zone axes (further details are shown in Supplementary Fig. 2).

Fig. 1

Structural characterisation of honeycomb-layered K2Ni2TeO6 and syntheses of related solid solution derivatives. a Rietveld refinement data of the synchrotron X-ray diffraction powder pattern of K2Ni2TeO6 indexed in the ordered P63/mcm hexagonal space group (RB = 4.29%, χ2 = 1.77; low reliability values indicate a satisfactory fit). The calculated and experimental Bragg peaks are indicated in black and red, respectively. The deviation between the experimental and calculated intensity is shown in blue, whilst black ticks indicate the Bragg peaks position of the orthotellurate phase. Inset shows the corresponding SAED patterns along [100] and [001] zone axes. The scale bar shows the length scale in the reciprocal space (2 nm–1). b Polyhedral view of the P2-type-layered crystal structure of K2Ni2TeO6 along the c-axis: the Ni octahedra are shown in purple, Te octahedra are in blue, K ions are brown spheres and O ions are small red spheres. The prismatic polyhedra around the K ions are shown for simplicity. c A fragment of the P63/mcm structure of K2Ni2TeO6 in the ab plane (the magnetoactive honeycomb layers) with three major K sites (K1, K2, and K3). d 2D bond valency energy landscape (BVEL) map of K2Ni2TeO6 with isosurfaces (yellow) of 0.35 eV for K. e Solid solution derivatives of K2Ni2TeO6 showing colour evolution with different 3d metal compositions

Refinements were performed assuming the crystal structure model proposed for isotypic ordered Na2Ni2TeO649. The deduced structural parameters are detailed in the Supplementary Table 2. The hexagonal crystal structure of K2Ni2TeO6 displays layers consisting of edge-sharing TeO6 and NiO6 octahedra along the ab planes (see Fig. 1b). Furthermore, the NiO6 octahedra form regular honeycomb lattices with TeO6 octahedra (located at the centre of the honeycomb lattices) as is succinctly shown in Fig. 1c. The honeycomb lattices are separated along the c axis by an intermediate layer of K atoms, adopting triangular prismatic KO6 coordination. This forms a P2-type stacking mode, wherein P in this nomenclature stands for trigonal prismatic coordination of the K-ions and the digit denotes the number of brucite-like layers in the unit cell.

Moreover, the present crystal structure of P2-type K2Ni2TeO6 comprises three crystallographically distinguishable K atom sites, denoted as K1, K2 and K3, as identified in the refinement results (see also Supplementary Table 2, wherein K1, K2 and K3 wyckoff sites are designated as K3, K1 and K2, respectively, for clarity). All the three K sites adopt a prismatic coordination of oxygen atoms; three from both the bottom and top metal layers as shown in Fig. 1c. The K1 site is aligned between two face-sharing Te6+O6 polyhedra (each from top and bottom layers). For the K2 site, K atoms are located between apical oxygen atoms of two NiO6 and one TeO6 octahedra also from both the top and bottom layers, whilst for the K3 site the K atoms reside between triangular faces of Ni2+O6 octahedra existing on top and bottom layers. The three K sites are only partially occupied, leading to a highly disordered distribution of K atoms residing between the honeycomb layers. A similar observation was noted recently with the analogous layered P2-type Na2M2TeO6 phases which display superfast Na-ion conduction49. Bond valency energy landscape (BVEL) approach has thus been employed to garner insights into the diffusive nature of K cations within K2Ni2TeO6. The K diffusion pathway described by the calculated isosurface of the K-ion BVEL map reveals an in-plane circular K-ion diffusion pattern within the K layers along the ab plane (hence, two dimensional (2D)), as is deduced in Fig. 1d. Note that energy of 0.35 eV above the minimum is necessary to obtain an in-plane circular 2D diffusion pattern, suggesting the feasibility of having relatively fast K-ion conduction in K2Ni2TeO6 and related derivatives, as will be discussed in the proceeding section.

The importance of studying these layered tellurates has further been highlighted through the preparation of the complete solid solution derivatives, namely K2Ni2−xMTeO6 contiguous phases (M = Co and Mg; x = 0, 0.5, 1.0, 1.5 and 2.0), showing structural transitions and colour changes contingent on the combination of transition metal ions, as shown in Fig. 1e. Additional information can be found in Supplementary Figs. 3 and 4, and Supplementary Tables 3, 4 and 5. Lastly, thermal stability analyses reveal K2Ni2TeO6 and its analogues, to be stable before reaching their melting points at above 800 °C (see Supplementary Figures 5, 6, 7 and 8), far surpassing the thermal stabilities of layered oxides such as K0.3CoO250 and polyanionic compounds such as the fluorosulphates51. Nevertheless, the tellurates are hygroscopic and tend to degrade upon long-time moisture exposure (see Supplementary Fig. 9). We also need to mention that the tellurate compounds detailed here show no deterioration in their physicochemical properties, under minimal exposure to moist air.

Potassium ion dynamics and ionic conductivity measurements

To further sense the aptitude of the tellurates towards K-ion conduction, as envisaged in K2Ni2TeO6, diffusive barrier energies were generated based on the BVEL methodology (as aforementioned) developed by Adams and co-workers51. Further details are furnished in the Methods section, Supplementary Note 1 and Supplementary Fig. 10. It is important to stress that although the diffusive barrier values computed using BVEL approach have unclear physical meaning, the values are deemed legitimate in assessing the ease of cation mobility of materials relative to known compounds. The selected target materials were classified as possible cathodes and solid electrolytes, depending mainly on the constituent transition metal of compositions. A comparative plot of diffusive barrier energies of both new and documented potassium-based materials screened as shown in Fig. 2a, b, reveals very low diffusion barrier energy in the tellurate system which is comparable to K0.72In0.72Sn0.28O2 which exhibits high K-ion conductivity52. Further details pertaining to the K-ion diffusion pathways of the compounds are elaborated in the Supplementary Table 6 and 7. In light of this, high K-ion conductivity of the new K2M2TeO6 tellurates in ceramic form can be anticipated, an aspect we investigated through performing ionic conductivity measurements.

Fig. 2

Theoretical screening of tellurate frameworks (as feasible cathodes and potassium-ion conductors) and conductivity measurements of the true ionically conducting K2Mg2TeO6. Values of the diffusion barriers derived from BVEL isosurface maps of representative a potassium-based cathode materials and b solid electrolytes for rechargeable potassium-ion (K-ion) battery. Note that new compounds are highlighted in asterisks whereas the dimensionality of the K-ion diffusion are shown in brackets. c Alternating current (a.c.) bulk ionic conductivity plots for K2Mg2TeO6 at temperature ranges of between 25 and 300 °C. d Bar graphs benchmarking the performance of orthotellurate compositions with the reported K-ion superionic conductors at 300 °C (573 K), references of which are provided in the Supplementary Table 8

In what follows, temperature-dependent alternating current (a.c.) conductivity was measured on sintered K2M2TeO6, details of which are provided in the Methods section and Supplementary Fig. 11. Caution was exercised in performing ionic conductivity tests, considering the possible contribution from the electronic conductivity due to the presence of Ni and Co in K2Ni2TeO6 and K2Co2TeO6, respectively. With this caveat in mind, conductivity measurements were performed on the Mg-based analogue (i.e., K2Mg2TeO6) which is exempt of oxidisable cation species. A plot showing the temperature dependency of the bulk conductivity (Arrhenius plot) is represented in Fig. 2c. Ionic conductivity increased with increment in temperature, as is expected, and the highest conductivity values were found at 300 °C; which marks the highest temperature we measured (see also Supplementary Fig. 11). Worthy of mention is a drastic increase in conductivity observed at around 250 °C, which has typically been noted as a phase transition onset in superionic conductors such as AgI. Further details pertaining to the phase transformation are subject of future work. The activation energy (Ea) calculated (between 60 and 200 °C) was about 0.92 eV (or 88.8 kJ mol−1) as deduced upon fitting of the a.c. data with the well-known Arrhenius law and the conductivity was found to be 5.9 × 10–6 S cm–1 (translating to ~0.01 mS cm–1) at room temperature (25 °C) and ~3.8 × 10–2 S cm−1 (or 38 mS cm–1) at 300 °C for K2Mg2TeO6 (compactness of ~70%). Compared to the canonical fast K-ion conducting compounds such as K0.72In0.72Sn0.28O2 (compactness of 85%; 6 × 10–7 S cm–1 at 27 °C)52, K2Mg2TeO6 with suboptimal sample density (compactness of ~70%) demonstrates superior performance. Figure 2d shows a comparison plot of the bulk conductivities of the potassium-based tellurates with other reported K-ion superionic conductors. It is apparent that the tellurates present very high K-ion conductivity, warranting them as feasible solid electrolytes for K-ion battery. A practical contender is K2Mg2TeO6, and further denser ceramics can, in principle, be expected to show even higher K-ion conductivities as revealed via theoretical calculations (see Supplementary Notes 2 and 3, and Supplementary Fig. 12). We are aware that the realisation of potassium-ion conductors as viable solid electrolytes for potassium-ion battery is still far from reality. However, taking into account the high reactivity and the possible dendrite formation in using alkali metal as anode materials, the development of solid electrolytes certainly will be quintessential to the commercial deployment of safe potassium-ion batteries.

Electrochemistry of K2Ni2TeO6 and related solid solutions/derivatives

The layered structure of K2Ni2TeO6, comprising highly electronegative Ni2+ cations in the slabs that can be oxidised during potassium extraction, calls for an evaluation of its electrochemistry. Electrochemical behaviour of K2Ni2TeO6 and its solid solution derivatives as potential cathode materials for K-ion battery has been assessed in K half-cells using 0.5 M KTFSI in Pyr13TFSI ionic liquid as an electrolyte, which we found to be stable during galvanostatic cycling. Further details pertaining to the ionic liquid used can be found in Supplementary Figs. 13 and 14, and the Methods section. Figure 3a displays the galvanostatic charge/discharge voltage profiles of K2Ni2TeO6 over the first 70 cycles between 1.3 and 4.7 V at room temperature. The cells were cycled at a rate equivalent to fully charging the theoretical capacity of the material (viz. 128 mAh g–1) in 20 h (technically written as C/20). K2Ni2TeO6 delivers a discharge/charge capacity of ca. 70 mAh g–1, demonstrating the ability to reversibly extract/insert approximately one K-ion (K+) ion from/into K2Ni2TeO6, solely based on electron counting. This reversible capacity is well sustained on cycling for 70 cycles. K2Ni2TeO6 can still sustain moderate rate performance at room temperature (shown in Supplementary Fig. 15), in spite of the inherently low ionic conductivity of the ionic liquid (0.5 M KTFSI in Pyr13TFSI) employed. We further note that the average charge/discharge voltage is 3.6 V versus K+/K; which is nearly close to the calculated voltage (see Supplementary Fig. 16). K2Ni2TeO6 exhibits the highest voltage amongst the layered oxides reported so far (Fig. 3b). The layered K2/3Ni1/6Co1/6Mn2/3O2 does not present such a high redox voltage44. This can be rationalised, in principle, by considering Te6+ in K2Ni2TeO6 as a (TeO6)6– moiety that possesses high electronegativity than O22–. The redox potential is consequently increased via the inductive effect, as has been observed for instance in polyanionic compounds such as VOSO4 and VOPO4 upon substitution of SO42– units by PO453,54.

Fig. 3

Electrochemical performance of K2Ni2TeO6 prototype cathode material along with its K2Ni1–xMxTeO6 (M = Mg, Co, Zn) solid solution derivatives. a Voltage-capacity profiles (70 cycles) for K2Ni2TeO6 in K half-cells using ionic liquid (0.5 M KTFSI in Pyr13TFSI). Galvanostatic measurements were conducted at C/20 rate at room temperature. The grey dashed line indicates the calculated voltages. The 1st, 5th, 10th, 20th and 70th voltage profiles have been shown for brevity’s sake. b Performance of new tellurate compounds benchmarked with reported layered cathode frameworks for potassium-ion battery (KIB), underlining the tellurate cathodes as high-voltage contenders. Voltage-composition plots of c Co-substituted K2Ni1.5Co0.5TeO6 and d Mg-substituted K2Ni1.5Mg0.5TeO6 derivatives. For the sake of readability, the 1st, 5th, 10th and 20th voltage profiles have been shown. e The average (dis)charge voltage (V versus K+/K) against volumetric capacity (Ah L–1) and volumetric energy density (expressed as Wh L–1) for selected cathode materials for KIB. The volumetric energy densities of the cathode materials were calculated based on material density. Further details pertaining to the calculations of the selected cathode materials are provided in the Supplementary Tables 9 and 10

Figure 3c, d show the voltage-composition plots of K2Ni2TeO6 solid solution derivatives, which are also electrochemically active (see also Supplementary Fig. 17), depicting high average voltages and at decent capacities. Although unclear at this point, the Mg-and Zn-substituted derivatives tend to show high reversible K-ion capacity than the Co-substituted samples, despite the high voltage exhibited by the latter. Figure 3e shows a plot that compares the performance of various K-ion cathode materials, based on the average working voltage, volumetric capacity and volumetric energy density attained. Cathode materials for Li-ion battery generally exhibit the highest energy density; nonetheless, several K-ion battery cathodes exhibit relatively high values that bring them to the fore as potential candidates. Layered transition metal oxides such as K0.3MnO2 possess compact framework and generally exhibit high reversible capacities40, warranting them ideal for applications that require a high volumetric energy density. On another note, the inductive effect engendered by the polyanion moiety in oxyphosphates, fluorophosphates, fluorosulphates, etc., leads generally to higher voltages, as is exemplified in KVOPO432, KVPO4F32,ibid and KFeSO4F17. Some organic moieties such as Prussian analogues are also promising candidates, due to the facile and fast K-ion diffusion pathways conferred by their open frameworks. However, the low density inherent in most organic moieties, encumbers their high-power utilisation when it relates to volumetric energy density. The honeycomb-structured layered oxides, prime amongst them being K2Ni2TeO6 and related solid solution derivatives, present a high volumetric energy density as can be envisaged from Fig. 3e, thus future research directions will be inclined in the optimisation of their performance and further exploration of related P2-type layered oxide materials.

K-ion insertion/extraction mechanism

The evolution of the cyclic voltammograms (namely, first and second cycle) of K2Ni2TeO6 in K half-cells (see Supplementary Fig. 18) depicts multiple redox peaks (signature of myriad phase transitions) during K-ion insertion (extraction) into (from) K2–xNi2TeO6 coupled with Ni2+(3+) oxidation (reduction). For a deeper insight into the phase transition process of K2Ni2TeO6 cathode during cycling, ex situ XRD patterns of K2Ni2TeO6 were collected at various (dis)charging depths in K half-cells. Figure 4a–c present structural evolution of P2-type K2Ni2TeO6 upon K+ extraction and insertion. The evolution of the interslab distance, as derived from full-pattern matching, is shown in Fig. 4a. (002) and (004) Bragg diffraction peaks were examined, as they are most sensitive to the K+ extraction/insertion process. Analysis of other peaks aside from (00l), as can be noted in Fig. 4b, is difficult, owing to their low diffraction intensity. Amongst the (00l) Bragg peaks, shifts of the (004) peak is specifically the most discernible upon K-ion extraction (charging) and reinsertion

Fig. 4

Crystal and electronic structural changes of P2-type K2Ni2TeO6 prototype cathode material during K-ion extraction and insertion. a Interslab distances calculated from ex situ XRD patterns during XRD patterns whilst K2Ni2TeO6 is (dis)charged at a current density commensurate to C/20 rate (20 h of (dis)charge). b XRD patterns from 10° to 38° and c enlarged XRD pattern indicating peak shifts of the (00l) Bragg diffraction peaks during (dis)charging. d Ni K-edge XANES spectra during charging (K-ion extraction) and e discharging (K-ion insertion). f Te L3-edge XAS spectra of K2Ni2TeO6 taken at different states of (dis)charging

(discharging), as observed in Fig. 4c. The (002) and (004) peaks shift to lower angles upon charging whilst the P2-type framework is retained, as demonstrated in Fig. 4b, c. Moreover, asymmetric peak evolutions and different degrees of peak shifting are apparent, as has also been observed in P2-type K0.6CoO241 and K0.5MnO239, evincing a multitude of phase transitions accompanying K-ion extraction from K2–xNi2TeO6. At some juncture during charging, significant peak broadening occurs after which new sets of diffraction peaks appear to the left of the (002) and (004) Bragg peaks, signature of the phase transitions. Further attempts to determine explicitly the structures of the new phases hallmarking the phase transitions remained elusive, apparently owing to the limitation posed by the low resolution and significant broadening of peaks. Reversal of the phase evolution is observed during the discharge process, suggesting repeatable K extraction and insertion behaviour in P2-type K2Ni2TeO6. Noteworthy to also mention is that during the charge/discharge process, Bragg peaks tend to shift to lower/higher angles, indicating an underlying solid solution (monophasic or single-phase) mechanism. The emergence of new peaks (as is shown in Fig. 4c) is reminiscent of a two-phase (biphasic) reaction, but these Bragg peaks also progressively shift which is typical of a monophasic reaction. A continuous increase and decrease of the c lattice parameters (viz., along [00l] direction) upon charge and discharge, respectively, is the overall trend. Upon charging (00l), Bragg diffraction peaks monotonically shift towards low angles, in principle due to the enhancement in the electrostatic repulsion between the Ni/TeO6 octahedral slabs along the c-axis and vice versa during discharge. Further, a decrease/increase in the a-axis concomitantly proceeds with charging/discharging (Supplementary Table 11), due to the decrease/increase in nickel ion radius upon oxidation/reduction. The XRD results, in summary, demonstrate that P2-type K2Ni2TeO6 can reversibly reinsert K ions through a highly reversible topotactic process, which entails not only a monophasic but also a biphasic reaction. In addition, ex situ XRD results given in Supplementary Fig. 19 affirm that repeated K+ extraction/insertion does not affect significantly the structural integrity of the P2-type K2Ni2TeO6 cathode material.

Apart from XRD, spectroscopic techniques were also employed to investigate the charge compensation process during reversible K-ion insertion in K2Ni2TeO6. Generally, in order to maintain electroneutrality, the valency of the redox-active ions (in this case Ni2+ in K2Ni2TeO6) change upon reversible K-ion insertion. X-ray absorption spectroscopy (XAS) analysis was therefore conducted to divulge the valency changes of local chemical structure around the Ni atoms in K2–xNi2TeO6 electrodes during electrochemical cycling. As can be seen in Fig. 4d, e, the Ni K-edge XANES spectra shift to higher energy during charging and vice versa during discharging, indicating a reversible Ni valency change upon K-ion extraction and insertion. The evolution of the transition metal oxidation states of the pristine, charged, and discharged K2Ni2TeO6 samples were confirmed further by complementary XPS analyses (Supplementary Fig. 20). Turning to tellurium, Te L-edge XANES spectra (shown in Fig. 4e) reveal no discernible spectra variations for the entire charge–discharge process, and is further confirmed by XPS studies (see Supplementary Fig. 20).

To further understand the electronic structural changes of K2Ni2TeO6 upon K-ion extraction/insertion, theoretical calculations (more specifically, density functional theory (DFT) approaches) were carried out. Partial density of states (PDOS) of the 3d states of Ni, 4d states of Te and 2p states of O ions were calculated based on the lattice parameters of K2Ni2TeO6. Further details of the calculations are elaborated in the Methods section and Supplementary Note 2. PDOS data for the K2–xNi2TeO6 (x = 0, 1 and 2) is provided in Fig. 5a. Upon K-ion extraction, K2–xNi2TeO6 tends to become metallic, implying the ease to extract K-ion from K2-xNi2TeO6 with progressive charging. The PDOS plots show the O 2p electrons to lie more in the vicinity of the Fermi energy and more itinerant than the Ni 3d electrons, whilst Te 4d bands are energetically well localised and are dormant virtually throughout the K-ion extraction process in K2Ni2TeO6. These results suggest that, in comparison to Ni 3d, O 2p electrons are more dominant in the vicinity of the Fermi level and that the degree of hybridisation emanating from O 2p electrons in both the K2Ni2TeO6−KNi2TeO6 and KNi2TeO6−Ni2TeO6 regimes is very large. This is conspicuous from Fig. 5a wherein, the Fermi level moves further to low-energy region upon K-ion extraction, leading to partially unoccupied up-spin bands of Ni 3d and O 2p electrons. Additionally, using the Bader scheme for topological partitioning of charge densities in the electronic structure (Fig. 5b and Supplementary Table 12), the dominance of O 2p states over the Ni 3d states and the inert role of Te 4d states in the charge transfer associated with K-ion extraction/insertion process is apparent. Overall, the PDOS plots highlight a strong hybridisation of Ni 3d and O 2p states (being dominant) during K-ion extraction process in K2–xNi2TeO6.

Fig. 5

Theoretical and experimental (spectroscopic) analysis of the electronic structural changes of K2Ni2TeO6 during K-ion extraction and insertion. a The computed partial density of states (PDOS) decomposed into the up-spins (positive axis) and down-spins (negative axis) for different composition x in K2–xNi2TeO6 (x = 0, 1, 2) as function of energy (E). The PDOS of the up-spin nickel (d5d↓3 at x = 0, d4.5d3 at x = 1, and d4d3 at x = 2) and its directly bonded oxygen atoms are selected. The Fermi level (EF) is set at 0 eV with a vertical black dashed line. PDOS plots indicate a cumulative cationic (Ni 3d) and anionic (O 2p) redox activity during de-potassiation (K-ion extraction). b Bader charge allocation analysis on the total charge of Ni 3d, Te 4d and O 2p showing unequivocal charge fluctuations in not only Ni but also O in K2–xNi2TeO6 during K-ion extraction. c Normalised O K-edge ex situ XANES spectra of K2Ni2TeO6 cathode during (dis)charging taken in fluorescence yield (FY) mode, which is highly sensitive to the innate bulk properties of K2Ni2TeO6. Ligand holes are created in the O 2p bands during K-ion extraction and vice versa during K-ion reinsertion. d Schematic illustration of the electrochemistry of K2Ni2TeO6 utilising the ligand hole formation in the hybridised Ni 3d and O 2p states during K-ion extraction

O K-edge XAS measurements were conducted in order to glean, experimentally, information regarding the role of oxygen during potassium-ion extraction/insertion. Although the data were acquired from ex situ measurements, caution was taken not to expose the samples to air. Normalised XANES spectra at O K-edge of K2Ni2TeO6 during electrochemical K-ion extraction/insertion are shown in Fig. 5c. Galvanostatic measurements reveal a one-electron reaction, thus, the XAS measurements reflect the electronic structural changes occurring within the K2Ni2TeO6–KNi2TeO6 regime. A clear variation of the O K-edge XAS of the K2Ni2TeO6 cathode material before and after charging and discharging was observed. The peak around 532 eV arises from the hybridisation of O-2p and Ni-3d orbitals, whereas the peak on the high energy side emanates from the hybridisation of O-2p orbital and Ni-4s,p orbitals55,56. Emergence of a new peak is discernible at 528 eV (on the low-energy region) upon charging, ascribable to the formation of oxygen ligand hole. This behaviour is in excellent concordance with that observed in Li-excess LiNiO255, LaNiO357 and SrNiO358. The peak intensity increase observed at 528 eV, in principle reflects the degree of hybridisation between Ni 3d–O 2p orbitals, hence we can state that this strength is strongest upon K+ extraction from K2–xNi2TeO6. K+ extraction leads to the increase in the valency state from Ni2+ → Ni3+, the electronic ground state of Ni3+ predominantly being 3d7. However, owing to electronic configuration mixing triggered by the hybridisation with O-2p orbitals, the ground state tends to possess a 3d8 L orbital character (as has been observed in Li-excess compounds such as LiNiO255 upon charging). Presence in the ground state of this 3d8 L configuration invokes the increase in the pre-edge peak intensity conspicuous at 528 eV upon charging. It is therefore assignable to 3d8L → c d8 core transitions and can be rationalised, vide supra, as a signature of the hybridisation strength of O 2p–Ni 3d orbitals55. In summary, the trend observed in the O K-edge spectra (as was a priori revealed by first-principle calculations) signifies that, hybridisation or covalency is large upon potassium extraction from K2Ni2TeO6 and vice versa holds.


Potassium-ion (K-ion) batteries are a compelling grid-scale energy storage technology not only due to their low cost, but also to the attainable high volumetric energy density en par with the conventional lithium-ion batteries59. However, the advancement of K-ion batteries is thwarted particularly by the dearth of cathode materials that can endure repeatable K-ion (de)insertion at decent voltages and capacities. The new family of honeycomb-layered compounds with the general formula K2M2TeO6 (where M = Ni, Mg, Co, etc. or a combination of at least two transition metals) not only offer a fascinatingly rich playground for high-voltage cathode materials for potassium-ion (K-ion) battery (particularly for Ni-based analogues), but also enlists feasible solid electrolytes with high K-ion mobility as demonstrated in the purely ionic conducting K2Mg2TeO6. Only few potassium-based compounds have, to date, been reported to adopt honeycomb lattice: K2Mn2(H2O)2C2O4(HPO3)260 and K2D3(VO4)2(OH)2 (D = Mn, Co)61. Orthotellurate archetypes such as K2M2TeO6 augment this trove of exotic honeycomb-structured potassium-based compounds.

Besides the high volumetric capacity exhibited by P2-type K2Ni2TeO6 and its solid solution derivatives, their record high voltages (~4 V versus K+/K) in stable electrolyte (ionic liquid) and high thermal stabilities are great offsetting advantages that warrant their inclusion as high-energy-density cathode contenders for K-ion battery. Diffraction and spectroscopic techniques further reveal K2Ni2TeO6, as a prototype cathode, can sustain successive K-ion insertion/extraction via a complex topotactic reaction. This highlights related orthotellurates as perfect K-based cathode models to study a multitude of phase transition phenomena upon re-insertion of the large K-ion.

With a theoretical capacity in the range of 120–140 mA h g–1 and consisting of a non-terrigenous element such as tellurium (Te), it suffices to say that this study holds a more profound significance in the future application of K-ion batteries. Nevertheless, related materials can be propitious for practical applications inasmuch as a less heavy congener element to replace Te6+ (d10 shell occupancy) can be found. However, this study accentuates that the design of potassium-based layered cathode materials, demonstrating reversible K+ (de)insertion at preponderant high voltages, is not trivial in the absence of electronegative moieties such as TeO66– and augmented with in silico material screening. The low theoretical capacities displayed by the tellurates are compensated by their high cell voltages (3.6–4.3 V versus K+/K). It could be possible to assemble a high-voltage rechargeable K-ion battery system suited for large-scale volume-restricted applications, coupling such high-voltage potassium-based cathodes to suitable anodes. A high-voltage configuration not only increases the energy density, but also reduces the number of cells per battery pack. In fact, a series connection is normally applied to smaller cells in order to achieve the required voltage of large battery packs, for instance, for those utilised in electric vehicular applications. High-voltage battery configuration results in a reduction in the number of cells, thereby curtailing the volume and cost of the battery pack. For this reason, high-voltage potassium-ion battery configurations will indeed have considerable advantage in energy storage devices.

Whilst we have shown through the preparation of solid-solution derivatives of K2Ni2TeO6 that these high-voltage-layered honeycomb materials can be extended to include a vast variety of stoichiometries, we still feel that by heterovalent cation substitution of K2M2TeO6 the highest probability exists for synthesising new honeycomb-structured potassium-based materials with superior performance. A part of an ongoing work is the design of Te-free compounds demonstrating reversible K-ion (de)insertion at high voltages and capacities. Plausible candidates encompass the potassium-rich K2MAO4, K3MAO5, K4MAO6 (or equivalently written as K8M2A2O12), K3M2AO6 and K2M2AO6 compounds (where M and A are selected from a wide variety of metals, with the summation of M and A oxidation states being restricted to 6, 7, 8, 9 and 10 respectively, to maintain electroneutrality). The obvious A cations to try are Sb and Bi, based on the known stoichiometries of classic lithium- and sodium-based compounds. New potassium-based structural frameworks for rechargeable batteries such as the nascent K-ion battery technology still await further exploration. Moreover, it is our conviction that experimentalists and theorists looking for new research avenues in materials science, solid-state chemistry and physics will find it to be a worthwhile pursuit.



Polycrystalline K2Ni2TeO6 samples were prepared by solid-state reaction protocols. K2CO3 (Rare Metallic (Japan), 99.9%), NiO (Kojundo Chemical Laboratory (Japan), 99%) and TeO2 (Aldrich, purity of ≥99.0%) were first intimately ground (using an agate mortar and pestle) in stoichiometric proportions to obtain K2Ni2TeO6 precursor. To eliminate any adventitious water, K2CO3 was dried at 130 °C prior to weighing. The mixture was thereafter pelletised and fired in a gold or platinum crucible in air, argon (Ar) or oxygen (O2) flow under varying duration of 6−24 h in the temperature ranges of 600–800 °C (with intermediate grinding) with a ramp rate of +200 °C h–1. The furnace was switched off upon completion of the thermal treatment, and the samples left in the furnace to cool down. Unless otherwise stated, the obtained powders were transferred to a glove box (argon-purged), owing to the sensitivity of the materials upon exposure to air. Other related compounds of composition K2M2TeO6 (M = Mg, Cu, Co, Zn) were synthesised using K2CO3 (Rare Metallic (Japan), purity of 99.9%), MgO (Wako Chemicals (Japan), 99.9%), CuO (Kojundo Chemical Laboratory (Japan), 99%), Co3O4 (Kojundo Chemical Laboratory (Japan), ≥99.0%) and ZnO (Wako Chemicals (Japan), 95%) in the temperature ranges of 600–800 °C for 24–48 h. Conventional ceramic methods were also adopted to prepare the oxides with nominal compositions K2Ni2–xMgxTeO6, K2Ni2–xZnxTeO6, K2Ni2–xCoxTeO6 and K2Mg2–xCoxTeO6 (x = 0.0, 0.5, 1.0, 1.5 and 2.0).

Powdered samples of new quaternary transition-metal-layered oxides, K4MTeO6 (M = Co, Zn, Ni and Mg), were also confectioned by a solid-state ceramics reaction of K2CO3, CoC2O4 (Kojundo Chemical Laboratory (Japan), 99%), NiC2O4·2H2O (Kojundo Chemical Laboratory (Japan), 99.9%), MgO, ZnO and TeO2 at 750 °C for 60 h with intermediate grinding. Synthesis of other conceivable compositions such as K3M2BiO6 and K3M2SbO6 were attempted under a similar firing condition by mixing MgO, CuO or ZnO and Sb2O5 (Aldrich, 99.999%) or Bi2O3 (Aldrich, purity of 99.99%) with the aforementioned precursors in stoichiometric proportions. However, only the Ni analogue of K3M2SbO6 was formed as a fairly pure phase, whereas the other intermediate compounds resulted in two-phase products made up of the precursor compounds. Synthesis of high purity phases of analogous K2Mn2TeO6, K2Fe2TeO6, K2LiATeO6 (A = Al or Ga), K2LiFeWO6, K2M2WO6 (M = Cu or Ni), K2NiMSbO6 (M = Mn, Al or Fe) and K2NiAlTO6 (where T = Ta (tantalum) or Nb (niobium) were also in vain, whatever the synthesis route we undertook.

X-ray diffraction analyses

Powder X-ray diffraction (PXRD) measurements were conducted using a diffractometer (Bruker D8 ADVANCE) employing Cu–Kα radiation (i.e., λ = 1.54051 Å). Conventional PXRD measurements were performed in Bragg–Brentano geometry with a 2θ range of 10–80° at a step size of 0.01°. In addition, high-resolution synchrotron X-ray diffraction was performed at SPring-8 (Hyogo, Japan) using BL19B2 beamline with a wavelength of 0.500212(2) Å at 298 K. PXRD data analysis and refinement was carried out by the Rietveld procedure implemented in the JANA 2006 program, and the visualisation of the crystal structure was done using VESTA crystallographic software. The structural refinements for K2M2TeO6 (M = Ni, Co, Mg) were performed on PXRD data based on the Na2Ni2TeO6 (P63/mcm, No. 194) and Na2Co2TeO6 (P6322, No. 182) structural models. Fifteen terms of Chebyshev polynomials to describe the background were used during the structural refinement and with a damping factor of 0.1. To correct peak asymmetry, Berar–Baldinozzi method and pseudo-Voigt profile function were applied. Preferred orientation with respect to the (00l) axis was also taken into account to obtain a satisfactory refinement. Further details regarding the crystal structure investigation(s) can be retrieved from the Fachinformationszentrum Karlsruhe, D-76344 Eggenstein-Leopoldshafen (Germany) depository database, on quoting the accession numbers CSD-434032, -434033 and -434061.

XRD ex situ measurements were collected in Bragg–Brentano geometry (Cu–Kα radiation) for electrodes cycled at different (dis)charge depths at a rate of C/20. The trend in lattice parameters evolution during (dis)charge was determined via profile fitting of the patterns.

Morphological and elemental characterisation

The morphologies of the as-synthesised compounds were analysed by a scanning electron microscope (JSM-6510LA) where the elemental mapping of the constituent elements was carried out using the energy dispersive X-ray (EDX) imaging function. Transmission electron microscopy (TEM) and high-resolution images (HRTEM) were obtained on a TITAN80-300F at an accelerated voltage of 200 kV without exposure to neither air nor moisture. Simulations of the HRTEM images were performed using the JEMS 31(PECD) software. Electron diffraction experiments were conducted on many crystallites, and reproducible results were observed.

Stoichiometry quantifications and chemical compositions of the compounds were precisely determined by inductively coupled plasma absorption electron spectroscopy (ICP-AES) on a Shimadzu ICPS-8100 instrument. The measurements were repeated in several different spots of the samples, and there was no deviation in the calculated values.

Thermal analyses

Thermogravimetric and differential thermal analysis (TG-DTA) was carried out using a TG-DTA instrument 2020SA (Bruker AXS) in the temperature range 30–900 °C under flowing Ar or N2 at a ramp rate of 5 °C min–1. A baseline correction of the TG curve was carried out by measuring the empty Pt crucible prior to each measurement.

Ionic conductivity measurements

Pristine K2Mg2TeO6 was uniaxially pressed into 10 mm diameter pellets under a pressure of about 40 MPa. The obtained pellets were sintered at 800 °C for 4 h in air and thereafter cooled to ambient temperature inside the kiln. This pellet densification method conserves the phase purity whilst increasing the final density of the pellet, as was confirmed by X-ray diffraction analyses on pulverised powder of the sintered pellets. The sintered pellets density was approximately 70% of the theoretical ceramics density. The pellets were coated with a thin gold film via magnetron sputtering technique. The resistance (bulk) of the sintered pellets was measured using a two-probe alternating current (a.c.) impedance spectroscopy (Solartron SI 1260) over a frequency ranging from 0.01 Hz to 1 MHz at a perturbation of 100 mV. The impedance analyser was connected to a purpose-built apparatus that facilitated measurements to be carried out at various temperature ranges under argon. Impedance spectroscopic data were collected between 25 and 300 °C with impedance scans taken every 10 °C. Ionic conductivities (of the bulk) recorded at various temperatures were obtained by Nyquist plot fittings. Arrhenius graphs were plotted taking into consideration the errors arising from area measurements, device inductance (that was observed at high temperatures), and the impedance frequency analyser. The activation energy (Ea) for K-ion conduction was calculated through a linear fitting of the bulk ionic conductivity values at various temperatures by incorporating the well-established Arrhenius equation: σ = σ0 exp (–Ea/kBT), whereby Ea represents the activation energy (in this case, for K-ion conduction), σ0 as the absolute ionic conductivity (at zero temperature), σ denotes the temperature-contingent ionic conductivity, whilst T and kB have their conventional definitions.

Theoretical calculations

BVEL calculations were conducted using the bond valency parameters developed by Adams and co-workers51, which augment the polarisability of the mobile species, in this case K+, and the influence of the counter ions of the structure up to a distance of 10 Å. This approach allows the visualisation of conduction trajectories within the structure whilst giving hints to possible K-ion conduction mechanisms.

DFT calculations were conducted based on the generalised gradient approximation (GGA) with the Perdew–Burke–Ernzerhof (PBE) exchange-correlation functional and projector augmented wave (PAW) pseudopotentials as implemented in the Quantum-ESPRESSO (QE) Package. A plane-wave cutoff of 60 Rydberg (Ry) for the kinetic energy and 500 Ry for the charge density were used to expand the wave functions. Full cell relaxation for all the present structures were conducted with a tolerance of 10–10 Ry for total energy and 10–3 eV Å−1 for the residual forces on each ion. Spin-polarised GGA + U approach was applied for K2–xNi2TeO6 (x = 0, 1, 2) with an antiferromagnetic ordering of Ni akin to that of Na2Ni2TeO6 (adopting the same P63/mcm symmetry); where the effective Hubbard parameter Ueff ( = U – J) for Ni d orbitals were taken to be 6 eV62. Further details regarding the theoretical approach implemented can be found in the Supplementary Notes 1 and 2.

Electrochemical measurements

Assembly of the coin cells and pertinent protocols were carried out inside an Ar-filled glove box (MIWA, MDB-1KP-0 type) with H2O and O2 contents <0.1 ppm. Pertaining to electrode fabrication, K2Ni2TeO6 and related tellurates were mixed with polyvinylidene fluoride (PVdF) binder and carbon to attain a final weight formulation of cathode material: binder: carbon as 85: 7.5: 7.5. A viscous slurry was made by suspending the mixture in N-methyl-2-pyrrolidinone (NMP), which was then cast on aluminium foil with a mass loading of 4–5 mg cm–2. Composite cathodes, with a geometric area of 1 cm2, were punched out and dried in vacuo at 120 °C. Electrochemical performances were assessed in CR2032-type coin cells using K2Ni2TeO6 composite cathode (and related tellurates), separated from the K metal anode (counter electrode in technical terms) by glass fibres discs soaked with electrolyte. Owing to the pronounced decomposition of the common electrolytes like 0.8 mol dm–3 KPF6 (Potassium hexafluorophosphate) (Sigma Aldrich, 99.99%) in propylene carbonate (PC)/ethylene carbonate (EC) (1:1 volume %), diethylcarbonate (DEC)/EC (1:1 volume %) or 1 mol dm–3 KFSI (potassium bis(fluorosulfonyl)imide) in dimethylcarbonate (DMC)/EC (1:1) that we experimented, we have used a 0.5 mol dm–3 potassium bis(trifluoromethanesulfyonyl)imide (hereafter denoted as KTFSI) in 1-methyl-1-propylpyrrolidinium bis(trifluoromethanesulfonyl)imide (hereafter Pyr13TFSI) (Kanto Chemicals (Japan), 99.9%, <20 ppm H2O) ionic liquid, which was more stable against decomposition at high voltages and compatible with most potassium-based cathode materials. Unless stated otherwise, galvanostatic cycling was done at a current rate corresponding to C/20 (20 being the necessary hours to extract/insert 2 K+ per formula unit), and cyclic voltammetry tests were conducted between 2.8 V and 4.6 V (versus K+/K) and at a scan rate of 0.1 mV s–1. All electrochemical measurements were performed at room temperature.

X-ray photoelectron spectroscopy (XPS)

XPS analysis was performed on a PHI 5000 Versa Probe (Ulvac-Phi) instrument. The hygroscopic cathode samples were loaded onto a spectrometer and transferred into the chamber in a moisture-free environment. Gaussian functions were used to fit all the XPS spectra and data processing was performed using COMPRO software. The binding energy values of the obtained spectra were calibrated, as is customary, based on the C 1s peak at 285 eV corresponding to hydrocarbon. XPS spectra of pristine, charged (4.0 and 4.6 V) and discharged electrode samples (to 1.3 V) were collected at Ni 2p and Te 3d binding energy.

X-ray absorption spectroscopy (XAS)

For X-ray absorption measurements, ex situ measurements were also performed because high-quality oscillated data were required. Reference compounds were prepared as homogeneous self-supporting pellets. For the Ni K-edge and Te L3-edge XAS measurements, charged/discharged K2–xNi2TeO6 electrodes were hermetically sealed in packets inside a glove box (Ar-purged). The XAS spectra were measured in the Ni K-edge and Te L3-edge energy region (at room temperature) in transmission mode at BL01B1 of SPring-8 (Japan) synchrotron facility. Athena package was used to treat the raw X-ray absorption data, as is customary. As for the O K-edge and Ni L-edge XAS measurements, the (dis)charged electrode samples were transferred to a measurement vacuum chamber without air exposure. The spectra were measured in fluorescence yield mode (which is sensitive to the bulk state of a sample) using the beamline facility (BL-2) of SR Center located at Ritsumeikan University (Japan).

Data availability

Data that support the findings detailed in this study are available in the supplementary information and its article. Any other source data perceived as pertinent are available, on reasonable request, from the corresponding author [T.M.].


  1. 1.

    Pasta, M., Wessells, C. D., Huggins, R. A. & Cui, Y. A high-rate and long cycle life aqueous electrolyte battery for grid-scale energy storage. Nat. Commun. 3, 1149 (2012).

    ADS  Article  PubMed  Google Scholar 

  2. 2.

    Eftekhari, A. Potassium secondary cell based on Prussian blue cathode. J. Power Sources 126, 221–228 (2004).

    ADS  CAS  Article  Google Scholar 

  3. 3.

    Gagne, O. C. & Hawthorne, F. C. Bond-length distributions for ions bonded to oxygen: alkali and alkaline-earth metals. Acta Crystallogr. B72, 602–625 (2016).

    Google Scholar 

  4. 4.

    Abrahams, S. C. & Bernstein, J. L. Piezoelectric langbeinite-type K2Cd2(SO4)3: room temperature crystal structure and ferroelastic transformation. J. Chem. Phys. 67, 2146 (1977).

    ADS  CAS  Article  Google Scholar 

  5. 5.

    Luo, Y., Xia, Z., Liu, H. & He, Y. Synthesis and luminescence properties of blue-emitting phosphor K2Ca2Si2O7:Ce3+. Opt. Mater. 36, 723–726 (2014).

    ADS  CAS  Article  Google Scholar 

  6. 6.

    Daicho, H. et al. A novel red-emitting K2Ca(PO4)F:Eu2+ phosphor with a large Stokes shift. Chem. Commun. 54, 884–887 (2018).

    CAS  Article  Google Scholar 

  7. 7.

    Li, R. K. & Wang, Y. K2FeB2O7: a transparent nonlinear optical crystal with frustrated magnetism. J. Solid State Chem. 183, 1221–1225 (2010).

    ADS  Article  Google Scholar 

  8. 8.

    Tsyrenova, G. D. et al. New ferroeleastic K2Sr(MoO4)2: synthesis, phase transitions, crystal and domain structures, ionic conductivity. J. Solid State Chem. 237, 64–71 (2016).

    ADS  CAS  Article  Google Scholar 

  9. 9.

    Ju, G. et al. A reddish orange-emitting stoichiometric phosphor K3Eu(PO4)2 for white light-emitting diodes. Opt. Laser Technol. 44, 39–42 (2012).

    ADS  CAS  Article  Google Scholar 

  10. 10.

    Maeder, M. D., Damjanovic., D. & Setter, N. Lead free piezoelectric materials. J. Electroceram. 13, 385–392 (2004).

    CAS  Article  Google Scholar 

  11. 11.

    Mrotzek, A., Chung, D.-Y., Hogan, T. & Kanatzidis, M. G. Structure and thermoelectric properties of the new quaternary tin selenide K1−xSn5−xBi11+xSe22. J. Mater. Chem. 10, 1667–1672 (2000).

    CAS  Article  Google Scholar 

  12. 12.

    Hikita, T., Sekiguchi, H. & Ikeda, T. Phase transition in new langbeinite-type crystals. J. Phys. Soc. Jpn 43, 1327–1331 (1977).

    ADS  CAS  Article  Google Scholar 

  13. 13.

    Jodlauk, S. et al. Pyroxenes: a new class of multiferroics. J. Phys. Condens. Matter 19, 432201 (2007).

    Article  Google Scholar 

  14. 14.

    Shirpour, M., Cabana, J. & Doeff, M. Lepidocrocite-type layered titanate structures: new lithium and sodium ion intercalation anode materials. Chem. Mater. 26, 2502–2512 (2014).

    CAS  Article  Google Scholar 

  15. 15.

    Zhang, Q., Guo, Y., Guo, K., Zhai, T. & Li, H. Ultrafine potassium titanate nanowires: a new Ti-based anode for sodium ion batteries. Chem. Commun. 52, 6229–6232 (2016).

    CAS  Article  Google Scholar 

  16. 16.

    Cao, D. et al. Cubic perovskite fluoride as open framework cathode for Na-ion batteries. Adv. Funct. Mater. 27, 1701130 (2017).

    Article  Google Scholar 

  17. 17.

    Recham, N. et al. Preparation and characterization of a stable FeSO4F-based framework for alkali ion insertion electrodes. Chem. Mater. 24, 4363–4370 (2012).

    CAS  Article  Google Scholar 

  18. 18.

    Fedotov, S. S. et al. AVPO4F (A=Li, K): a 4V cathode material for high-power rechargeable batteries. Chem. Mater. 28, 411–415 (2016).

    CAS  Article  Google Scholar 

  19. 19.

    Lander, L. et al. Synthesis, structure, and electrochemical properties of K-based sulfates with M=Fe and Cu. Inorg. Chem. 56, 2013–2021 (2017).

    CAS  Article  PubMed  Google Scholar 

  20. 20.

    Hameed, A. S. et al. Room temperature large-scale synthesis of layered frameworks as low-cost 4V cathode materials for lithium ion batteries. Sci. Rep. 5, 16270 (2015).

    ADS  CAS  Article  PubMed  PubMed Central  Google Scholar 

  21. 21.

    Baddour-Hadjean, R., Boudaoud, A., Bach, S., Emery, N. & Pereira-Ramos, J. P. A comparative insight of potassium vanadates as positive electrode materials for Li batteries: influence of the long-range and local structure. Inorg. Chem. 53, 1764–1772 (2014).

    CAS  Article  PubMed  Google Scholar 

  22. 22.

    Ito, S., Ui, K., Koura, N. & Akashi, K. Lithium secondary battery using potassium-β-ferrite as a new cathode active material. Solid State Ion. 113–151, 17–21 (1998).

    Article  Google Scholar 

  23. 23.

    Wang, L. et al. A superior low-cost cathode for a Na-ion battery. Angew. Chem. Int. Ed. 52, 1964–1967 (2013).

    CAS  Article  Google Scholar 

  24. 24.

    Komaba, S., Hasegawa, T., Dahbi, M. & Kubota, K. Potassium intercalation into graphite to realize high-voltage/high-power potassium-ion batteries and potassium-ion capacitors. Electrochem. Commun. 60, 172–175 (2015).

    CAS  Article  Google Scholar 

  25. 25.

    Sultana, I., Rahman, M. M., Ramireddy, T., Chen, Y. & Glushenkov, A. M. High capacity potassium-ion battery anodes based on black phosphorus. J. Mater. Chem. A 5, 23506–23512 (2017).

    CAS  Article  Google Scholar 

  26. 26.

    Han, J. et al. Exploration of K2Ti8O17 as the anode materials for potassium-ion batteries. Chem. Commun. 52, 11274–11276 (2016).

    CAS  Article  Google Scholar 

  27. 27.

    Kishore, B., Venkatesh, G. & Munichandraiah, N. K2Ti4O9: a promising anode material for potassium ion batteries. J. Electrochem. Soc. 163, A2551–A2554 (2016).

    CAS  Article  Google Scholar 

  28. 28.

    Sultana, I. et al. K-ion and Na-ion storage performances of Co3O4-Fe2O3 nanoparticle-decorated super P carbon black prepared by a ball milling process. Nanoscale 9, 3646–3654 (2017).

    CAS  Article  PubMed  Google Scholar 

  29. 29.

    Ren, X., Zhao, Q., McCulloch, W. D. & Wu, Y. MoS2 as a long-life host material for potassium ion intercalation. Nano Res. 10, 1313–1321 (2017).

    CAS  Article  Google Scholar 

  30. 30.

    Lakshmi, V. et al. Nanocrystalline SnS2 coated onto reduced graphene oxide: demonstrating feasibility of a non-graphitic anode with sulfide chemistry for potassium-ion batteries. Chem. Commun. 53, 8272–8275 (2017).

    CAS  Article  Google Scholar 

  31. 31.

    Han, J. et al. Investigation of K3V2(PO4)3/C nanocomposites as high-potential cathode materials for potassium-ion batteries. Chem. Commun. 53, 1805–1808 (2017).

    CAS  Article  Google Scholar 

  32. 32.

    Chihara, K., Katogi, A., Kubota, K. & Komaba, S. KVPO4F and KVOPO4 toward 4 volt-class potassium-ion batteries. Chem. Commun. 53, 5208–5211 (2017).

    CAS  Article  Google Scholar 

  33. 33.

    Park, W. B. et al. KVP2O7 as a robust high-energy cathode for potassium-ion batteries: pinpointed by a full screening of the inorganic registry under specific search conditions. Adv. Energy Mater. 8, 1703099 (2017).

    Article  Google Scholar 

  34. 34.

    Bie, X., Kubota, K., Hosaka, T., Chihara, K. & Komaba, S. A novel K-ion battery: hexacyanoferrate(II)/graphite cell. J. Mater. Chem. A 5, 4325–4330 (2017).

    CAS  Article  Google Scholar 

  35. 35.

    He, G. & Nazar, L. F. Crystallite size control of Prussian white analogues for nonaqueous potassium-ion batteries. ACS Energy Lett. 2, 1122–1127 (2017).

    Article  Google Scholar 

  36. 36.

    Su, D., McDonagh, Qiao, S.-Z. & Wang, G. High-capacity aqueous potassium-ion batteries for large-scale energy storage. Adv. Mater. 29, 1604007 (2017).

    Article  Google Scholar 

  37. 37.

    Xue, L. et al. Low-cost high-energy potassium cathode. J. Am. Chem. Soc. 139, 2164–2167 (2017).

    CAS  Article  PubMed  Google Scholar 

  38. 38.

    Zhang, C. et al. Potassium Prussian blue nanoparticles: a low-cost cathode material for potassium-ion batteries. Adv. Funct. Mater. 27, 1604307 (2017).

    Article  Google Scholar 

  39. 39.

    Kim, H. et al. Investigation of potassium storage in layered P3-type K0.5MnO2 cathode. Adv. Mater. 29, 1702480 (2017).

    Article  Google Scholar 

  40. 40.

    Vaalma, C., Giffin, G. A., Buchholz, D. & Passerini, S. Non-aqueous K-ion battery based on layered K0.3MnO2 and hard carbon/carbon black. J. Electrochem. Soc. 163, A1295–A1299 (2016).

    CAS  Article  Google Scholar 

  41. 41.

    Kim, H. et al. K-ion batteries based on a P2-type K0.6CoO2 cathode. Adv. Energy Mater. 7, 1700098 (2017).

    Article  Google Scholar 

  42. 42.

    Hironaka, Y., Kubota, K. & Komaba, S. P2- and P3-KxCoO2 as an electrochemical potassium intercalation host. Chem. Commun. 53, 3693–3696 (2017).

    CAS  Article  Google Scholar 

  43. 43.

    Liu, C. et al. K0.67Ni0.17Co0.17Mn0.66O2: a novel cathode material for potassium-ion battery. Electrochem. Commun. 82, 150–154 (2017).

    CAS  Article  Google Scholar 

  44. 44.

    Wang, X. et al. Earth abundant Fe/Mn-based layered oxide interconnected nanowires for advanced K-ion full batteries. Nano. Lett. 17, 544–550 (2017).

    ADS  CAS  Article  PubMed  Google Scholar 

  45. 45.

    Kumar, V., Bhardwaj, N., Tomar, N., Thakral, V. & Uma, S. Novel lithium-containing honeycomb structures. Inorg. Chem. 51, 10471–10473 (2012).

    CAS  Article  PubMed  Google Scholar 

  46. 46.

    Singh, Y. et al. Relevance of the Heisenberg-Kitaev model for the honeycomb lattice iridates A2IrO3. Phys. Rev. Lett. 108, 127203 (2012).

    ADS  Article  PubMed  Google Scholar 

  47. 47.

    Roberts, A. C. et al. Mcalpineite, Cu3TeO6・H2O, a new mineral from the McAlpine mine, Tuolumne County, California, and from the Centennial Eureka mine, Juab County, Utah. Mineral. Mag. 58, 417–424 (1994).

    CAS  Article  Google Scholar 

  48. 48.

    Kampf, A. R., Housley, R. M. & Marty, J. Dagenaisite, a new zinc tellurate from the gold chain mine, tintic, Utah, U.S.A. Can. Mineral. 55, 867–873 (2017).

    CAS  Article  Google Scholar 

  49. 49.

    Evstigneeva, M. A., Nalbandyan, V. B., Petrenko, A. A., Medvedev, B. S. & Kataev, A. A. A new family of fast sodium ion conductors: Na2M2TeO6 (M=Ni, Co, Zn, Mg). Chem. Mater. 23, 1174–1181 (2011).

    CAS  Article  Google Scholar 

  50. 50.

    Park, S., Lee, Y., Si, W. & Vogt, T. Synthesis and structure of the monolayer hydrate K0.3CoO2・0.4H2O. Solid State Commun. 134, 607–611 (2005).

    ADS  CAS  Article  Google Scholar 

  51. 51.

    Adams, S. From bond valence maps to energy landscapes for mobile ions in ion-conducting solids. Solid State Ion. 177, 1625–1630 (2006).

    CAS  Article  Google Scholar 

  52. 52.

    Delmas, C., Fouassier, C., Reau, J. –M. & Hagenmuller, P. Sur de nouveaux conducteurs ioniques a structure lamellaire. Mat. Res. Bull. 11, 1081–1086 (1976).

    CAS  Article  Google Scholar 

  53. 53.

    Gaubicher, J., Mercier, T. L., Cahbre, Y., Angenault, J. & Quarton, M. Li/β-VOPO4: a new 4V system for lithium batteries. J. Electrochem. Soc. 146, 4375–4379 (1999).

    CAS  Article  Google Scholar 

  54. 54.

    Gaubicher, J., Cahbre, Y., Angenault, J., Lautie, A. & Quarton, M. Lithium electrochemical intercalation in β-VOSO4. J. Alloy. Compd. 262−263, 34–38 (1997).

    Article  Google Scholar 

  55. 55.

    Uchimoto, Y., Sawada, H. & Yao, T. Changes in electronic structure by Li ion deintercalation in LiNiO2 from nickel L-edge and O K-edge XANES. J. Power Sources 97−98, 326–327 (2001).

    Article  Google Scholar 

  56. 56.

    Kanda, H. et al. Cluster calculation of oxygen K-edge electron-energy-loss near-edge structure of NiO. Phys. Rev. B 58, 9693–9696 (1998).

    ADS  CAS  Article  Google Scholar 

  57. 57.

    Abbate, M. et al. Electronic structure and metal-insulator transition in LaNiO3–δ. Phys. Rev. B 65, 155101 (2002).

    ADS  Article  Google Scholar 

  58. 58.

    Orikasa, Y. et al. X-ray absorption spectroscopic study on La0.6Sr0.4CoO3−δ cathode materials related with oxygen vacancy formation. J. Phys. Chem. C 115, 16433–16438 (2011).

    CAS  Article  Google Scholar 

  59. 59.

    Kubota, K., Dahbi, M., Hosaka, T., Kumakura, S. & Komaba, S.-I. Towards K-ion and Na-ion batteries as “Beyond Li‐Ion”. Acc. Chem. Rec. 18, 459–479 (2018).

    CAS  Article  Google Scholar 

  60. 60.

    Orive, J., Sivasamy, R., de Luis, R. F., Mosquera, E. & Arriortua, M. I. K2MnII 2(H2O)2C2O4(HPO3)2: a new 2D manganese(II) oxalatophosphite with double-layered honeycomb sheets stabilized by potassium ions. CrystEngComm 20, 301–311 (2018).

    CAS  Article  Google Scholar 

  61. 61.

    Sanjeewa, L. D. et al. Honeycomb-like S=5/2 spin lattices in new manganese(II) vanadates. Inorg. Chem. 55, 9240–9249 (2016).

    CAS  Article  PubMed  Google Scholar 

  62. 62.

    Jain, A. et al. Formation enthalpies by mixing GGA and GGA+U calculations. Phys. Rev. B 84, 045115 (2011).

    ADS  Article  Google Scholar 

Download references


We gratefully acknowledge Dr. Godwill Mbiti Kanyolo, Dr. Stephen Njane, Dr. Linus Atisa, Mr. Tuesday Masaki, Ms. Josephine Mokeira, Ms. Catherine Nyaboke and Dr. Sou Taminato for useful discussion, particularly in giving an ‘outsiders’ perspective of the paper. We thank Dr. Keiichi Osaka for conducting synchrotron X-ray diffraction measurements at SPring-8 facility (Proposal number 2017B1773). Dr. Mineyuki Hattori, Dr. Shigenobu Hayashi and Dr. Yoshito Gotoh are thanked for help in conducting 125Te NMR measurements. We also acknowledge Ms. Kumi Shiokawa and Ms. Yumi Haiduka for advice and technical help during conducting the electrochemical, XRD and XAS measurements. Mr. Yoshinari Sakaguchi, Ms. Kimiko Sakaguchi and Ms. Natsumi Ishii are also thanked for fruitful comments.

Author information




T.M. contributed to the syntheses of most of the potassium-based compounds. K.K. performed the morphological and thermal characterisation of the compounds. Z.-D.H. and T.M. contributed to the crystal structural analyses of the materials. Y.Y performed the DFT calculations. T.O. performed conductivity measurements. K.Y. prepared the ionic liquids. K.Y., M.K. and T.M. performed the electrochemical measurements. K.Y., H.Sak. and H.Sen. interpreted the electrochemical measurement results. T.O. and T.M. performed XRD and hard XAS measurements of the electrodes. Y.O. and J.F. performed soft XAS measurements and interpreted the results. M.S. and K.Y. conducted XPS measurement of the electrodes. T.M., Y.O., Z.-D.H and H. Sak. wrote the manuscript. M.K. designed most of the graphics outlined in the work. H.Sen., H. Sak. and M.S. provided input with the data analysis, helped with the discussion and assisted with the manuscript correction. The ideas and experiments were conceived, analysed and planned by all co-authors under the supervision of M.S. All authors have given approval to the final version of the manuscript.

Corresponding authors

Correspondence to Titus Masese or Zhen-Dong Huang or Hikari Sakaebe.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Masese, T., Yoshii, K., Yamaguchi, Y. et al. Rechargeable potassium-ion batteries with honeycomb-layered tellurates as high voltage cathodes and fast potassium-ion conductors. Nat Commun 9, 3823 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Sign up for the Nature Briefing newsletter for a daily update on COVID-19 science.
Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing