The photoregulation of a mechanochemical polymer scission


Control over mechanochemical polymer scission by another external stimulus may offer an avenue to further advance the fields of polymer chemistry, mechanochemistry, and materials science. Herein, we demonstrate that light can regulate the mechanochemical behavior of a diarylethene-conjugated Diels–Alder adduct (DAE/DA) that reversibly isomerizes from a weaker open form to a stronger closed form under photoirradiation. Pulsed ultrasonication experiments, spectroscopic analyses, and density functional theory calculations support the successful photoregulation of the reactivity of this DAE/DA mechanophore, which is incorporated at the mid-chain of a polymer, and indicate that higher force and energy are required to cleave the closed form of the DAE/DA mechanophore relative to the open form. The present photoregulation concept provides an attractive approach toward the generation of new mechanofunctional polymers.


Mechanophores, i.e., force–responsive molecules, represent a defining feature of the remarkable advancements that have been accomplished in polymer research in the past decade.1,2 Embedding mechanophores into polymer backbones enables the transfer of an applied force through them, providing a new powerful platform to endow polymeric materials with fascinating functionalities, such as chromism,3,4,5,6,7 luminescence,8,9,10,11,12 strengthening by cross-linking,7,13,14,15 activation of latent metal catalysts,13,14,16,17,18,19,20 and the generation of reactive species21,22 in response to force instead of heat or light. The focus of previous mechanophore studies can be broadly categorized into the search for novel mechanophores and the development of unique functionalities originated from them in polymers2,23,24,25,26 or the elucidation of the influence of the mechanophore structure, its peripheral environment, and macromolecular structure on the mechanophore activation.27,28,29,30,31,32,33,34,35,36,37 This innovative research has significantly advanced the emerging field of polymer mechanochemistry. To the best of our knowledge, successful examples of the regulation of mechanochemical polymer reactions by another external stimulus have not been reported so far.

Here, we report an example for the photoregulation of the mechanochemical reactivity of a mechanophore. In the present study, we focused on a Diels–Alder (DA) adduct, which can be regarded as a representative group of mechanophores,37,38,39,40,41 and regulated the mechanical cleavage of the DA bond by another external stimulus. DA adducts that emit fluorescence or release small molecules upon mechanical cleavage of the DA bond have already been developed, and these have provided deep insight into the fundamental aspects of polymer mechanochemistry.11,37,42,43 We envisaged that control over the mechanical cleavage could possibly be established by photoisomerization of a photochromic diarylethene (DAE).44 Recently, control over the thermally induced bond cleavage of DAE-conjugated DA adducts (DAE/DA) has been reported using a light stimulus,45,46,47,48,49,50 and this approach also holds promise for mechanically induced retro-DA reactions. The structure of the DAE/DA unit used in this study is shown in Fig. 1. We expected that the open form (DAE-open/DA), when incorporated in a polymer chain, would experience mechanical scission via a retro-DA reaction upon sonication of its solution; an event that would be less likely for the closed isomer (DAE-closed/DA). Therefore, we synthesized a polymer, which contained a DAE/DA moiety at the mid-chain, and investigated the chain scission by sonication before and after irradiation with UV light. The difference in the scission rates of the polymers bearing the open and closed isomers demonstrates the potential of this system to regulate other properties that involve the application of force.

Fig. 1

Conceptual illustrations. Photoregulated mechanochemical polymer scission based on DAE/DA


Synthesis and model photoregulation reaction of (DAE-open/DA)-diol

(DAE-open/DA)-diol, i.e., a model DAE/DA unit and the polymer precursor, was synthesized in five steps (see Fig. 2a for structure, Supplementary Method for synthesis, Supplementary Figs. 1933 for NMR spectra, and Supplementary Fig. 1 for thermal reactivity). The photoisomerization of this unit was investigated by UV–vis absorption measurements, prior to “locking” and “unlocking” its retro-DA reaction by sonication after insertion in a polymer chain. Upon exposure to UV light (λ = 313 nm), the intensity of the absorption band with a maximum at 260 nm, which corresponds to (DAE-open/DA)-diol, gradually decreased, while a new broad band emerged with a maximum at 437 nm (Fig. 2b). Extension of the π-conjugation in the DAE segment by isomerization from the open to the planar closed form causes such a bathochromic shift of the absorption, which is consistent with the observed color change (colorless→yellow) of the solution (inset in Fig. 2b). The ring-closing reaction reached a photostationary state (PSS) after 60 min of irradiation with UV light (Fig. 2c); the PSS corresponds to ca. 50% of (DAE-closed/DA)-diol, as determined by comparing the integral area of the signals in the 1H NMR spectrum (Supplementary Fig. 2). Almost all closed molecules in the mixture returned to the open form after 10 min of irradiation with visible light (λ > 440 nm) (Supplementary Fig. 3); this reversible isomerization was observed repeatedly by monitoring the absorbance at 437 nm (Fig. 2d). These results suggest the potential to reversibly lock and unlock the mechanochemical retro-DA reaction in the DAE/DA unit.

Fig. 2

Model photoregulation reaction of (DAE-open/DA)-diol. a Reversible photoisomerization of DAE/DA-diol. b Time dependence of the UV–vis absorption spectra of an acetonitrile solution of DAE/DA-diol (22.7 µmol L–1) under irradiation with UV light (λ = 313 nm). c Time dependence of the absorption at 437 nm under irradiation with UV light (λ = 313 nm). d Absorption changes at 437 nm under alternating irradiation with UV (313 nm; 1 h) and visible light (> 440 nm; 10 min)

Synthesis of polymers

Since the model reaction using (DAE-open/DA)-diol proceeded successfully, a series of polymers containing the DAE/DA unit were synthesized. A linear polymer with a DAE/DA functionality at the mid-chain (P1) was synthesized via esterification of (DAE-open/DA)-diol with 2-bromoisobutyryl bromide, followed by living radical polymerization of methyl acrylate (MA) from the two initiating sites (see Fig. 3 for the structure and Supplementary Fig. 4 for thermal reactivity). Three linear PMAs were prepared as control samples: one without DAE/DA (C1), one containing a DAE/DA unit located at a chain end (C2) (Supplementary Fig. 5), and one where the polymer chains are attached across the DAE/DA unit (C3) (Supplementary Fig. 6), whereas the PMA chains in P1 are linked only to the DA part. C1 should enable the estimation of the relative mechanochemical reactivity of both isomers, C2 should preclude any substantial transferal of force into the DAE/DA unit and eliminate any concerns regarding localized heating, and C3 will help to understand the mechanisms of both the DA and DAE mechanochemistry. All the polymers used in this study exhibited a number-average molecular weight (Mn) of 131–149 kDa with polydispersity indices (PDI) of 1.17–1.23 (Supplementary Table 1).

Fig. 3

Chemical diagrams. Polymer structures used in this study

Sonication of the polymers

The mechanochemical reactivity of these polymers in acetonitrile was evaluated using pulsed ultrasonication (10.6 W cm–2) in a water ice bath. P1 underwent a steady decrease in molecular weight with increasing sonication time, which was monitored by size-exclusion chromatography (SEC) (Fig. 4a). The initial polymer peak (Mn = 136 kDa) was attenuated upon sonication, while a new well-defined peak appeared at approximately half of the original molecular weight (Mn = 68 kDa). Mechanochemical scission of P1 was further investigated by 1H NMR spectroscopy. Upon sonication for 45 min, the 1H NMR spectrum of P1 showed new signals at 4.12, 4.95, 6.07, 6.81, and 7.89 ppm (Fig. 4b), which is consistent with the signals of the retro-DA products, i.e., furan and maleimide groups, that were also observed in a heat-induced retro-DA reaction. This result clearly indicates that sonication of P1 induces a retro-DA reaction in the mid-chain DAE/DA unit. A rough comparison of the two peak areas in the SEC curve revealed that 50% of the polymer chains were cleaved after sonication for 45 min. As estimated from the integrals in the 1H NMR spectrum, 80% corresponded to a selective cleavage at the DAE/DA unit through the retro-DA reaction, while 20% should be attributed to random cleavages in the PMA backbone. In contrast, no new peaks resulting from a retro-DA reaction were observed after sonication of C2 (bearing an end-chain DAE/DA unit) as well as of C1 (without a DAE/DA functionality) (Supplementary Figs. 10, 11). These results clearly confirm that the applied mechanical force is responsible for the selective scission at the DAE/DA unit in P1, thus precluding other alternative pathways such as thermal activation. Surprisingly, sonication of C3, where the PMA chain is attached to both the DAE and DA fragments, did not afford selective cleavage through a retro-DA reaction (Supplementary Fig. 12). To investigate the reasons behind the mechanochemical inertness of the DAE/DA unit in C3, we performed CoGEF calculations on the DAE/DA models (MP1 and MC3) incorporated in P1 and C3, as well as on the C1 PMA chain (MC1). The cleavage in MC3 required much higher energy and force (Emax = 770 kJ mol–1 and Fmax = 5.19 nN) than those for MP1 (236 kJ mol–1/3.88 nN) (Supplementary Figs. 16, 17, and Supplementary Table 2). The energy and force required for the cleavage of the C1 PMA chain (647 kJ mol–1/5.15 nN) were higher than those for P1 but lower than those for C3 (Supplementary Fig. 15). These results indicate that preferential cleavage occurs at the DAE/DA unit prior to random PMA cleavage under sonication in the case of P1, while sonication of C3 affords random cleavage as the mid-chain DAE/DA unit is extremely inert toward elongational forces. These findings are consistent with reports by Bo et al.37 and Makarov et al.51, who showed that cleavage of DA isomers with distal geometry (similar to that of the unit in C3) requires higher energy and force than cleavage in the case of proximal geometry (similar to that of P1).

Fig. 4

Mechanical retro-DA reaction of P1. a SEC curves for P1 upon sonication. A 2 mg mL–1 polymer solution was exposed to pulsed ultrasound (10.6 W cm–2) under an atmosphere of argon in an ice bath. b 1H NMR spectra of P1 before and after sonication (45 min), as well as after heating (3 h), showing the products of the retro-DA reaction (Supplementary Fig. 4)

Photoregulation of the mechanical polymer scission

To demonstrate the photoregulation of the mechanochemical cleavage of the DA bond by DAE isomerization at the chain center, we determined the rate constants for the chain scission in the sonicated polymer solutions before and after irradiation with UV light using SEC measurements (see Supplementry Information Equation (2) for detail). The cleavage rate constant for P1, i.e., the slope of the black line in Fig. 5a, was 12.0 × 10–5 min–1 kDa–1; exposure to UV light (λ = 313 nm) for 1 h to form P1-closed decreased the rate constant to 9.38 × 10–5 min–1 kDa–1 (see SI for details). After UV irradiation, P1 contained 60% of ring-closed DAE/DA, as calculated from the UV–vis spectrum of the solution using the molar absorptivity of (DAE-closed/DA)-diol at 437 nm (Supplementary Fig. 7), and the individual cleavage rate constant of P1-closed was accordingly estimated to be 7.63 × 10–5 min–1 kDa–1. This rate is lower than that of C1 (8.18 × 10–5 min–1 kDa–1), which barely changed after UV irradiation (Fig. 5b). In the UV–vis measurements of P1 after UV irradiation under sonication, an attenuation of the absorption at 437 nm was observed, which was attributed to the presence of DAE-closed/DA (Supplementary Fig. 13), indicating the slow destruction of the DAE-closed/DA skeleton. In contrast to P1, the rate constant of C2 was almost that of C1 and barely decreased upon exposure to UV light (Fig. 5c), while 43% of the DAE/DA unit at the chain end isomerized into the closed form (Supplementary Fig. 8). Moreover, the UV–vis spectrum of C2 after exposure to UV light remained unchanged upon sonication (Supplementary Fig. 14a). These results indicate that random cleavage occurs except at the chain-end DAE/DA isomers, and that the DAE/DA unit in P1 is responsible for the successful photoregulation of the mechanical chain scission. Despite the mid-chain functionality of C3, the rate constant corresponds to the random cleavage of PMA, which remained almost unchanged after exposure to UV light accounting for 53% of the isomerization (Supplementary Fig. 9) of the DAE/DA unit (Fig. 5d). A destruction of the closed skeleton under sonication was not observed in the UV–vis measurements of C3 (Supplementary Fig. 14b). These results indicate that the closed DAE isomer is inert toward elongational mechanical forces, although other DAE units that are bound differently to a polymer chain may serve as mechanophores.

Fig. 5

Rate of polymer chain scission upon exposure to pulsed ultrasound. a–d Cleavage rate of P1, C1, C2, and C3 before and after irradiation with UV light (313 nm, 1 h). A 2 mg mL–1 polymer solution was sonicated with pulsed ultrasound (10.6 W cm–2) under an atmosphere of argon in an ice water bath. Measurements were performed in triplicate, and the error bars represent a standard deviation

To demonstrate the reversibility of the photoregulated mechanochemical scission rate, we alternately irradiated a P1 solution with UV (λ = 313 nm) and visible (λ > 440 nm) light during intermittent sonication. The scission rate declined upon exposure to UV light but recovered after irradiation with visible light (Supplementary Fig. 18). This procedure was repeated for several cycles, although the rate for P1 scission slightly decreased with each cycle. This is probably due to the generation of some non-scission byproducts via the destruction of the DAE-close/DA unit upon sonication of the UV-irradiated P1 solution. Nevertheless, it has been clearly demonstrated that the mechanoreactivity of the DAE/DA mechanophore can be reversibly changed using light as a key.


The development of a mechanophore having the feature enabling control its mechanical responsiveness with external stimuli requires accurate and flexible designing of mechanophore. The fact that the thermal retro-DA reaction of DAE/DA-diol was controllable with irradiation of light suggests that control of mechanical retro-DA reaction is also possible. The progress of retro-DA reaction with the ultrasonication for polymer containing DAE/DA at the mid-chain (P1) verified that DAE/DA works as a mechanophore. The photo-irradiation for P1 induced the decreasing of cleavage rate of polymer chain. This change derives from the ring-closing reaction of DAE inducing strengthen of structure of DAE/DA mechanophore. The experiment using DAE/DA having different polymer connecting point (C3) (not work as mechanophore) remarkably prove the change in cleavage rate of P1 derived from not the change in steric structure of DAE, but the specific character of DAE/DA. The property controlling strength of chemical bond to mechanical stress will enable us to create the innovative material that can change the mechanical property with light. The results presented in this paper enable others to quest for such materials in parallel with our own ongoing effort.

In summary, combining a well-known DA mechanophore with a photochromic DAE unit has provided a photoregulated lock for its mechanoreactivity (retro-DA reaction). The scission rate of the polymer bearing a DAE/DA moiety at the mid-chain was reversibly regulated by sonication using irradiation with UV and visible light. This is the first example of how to control mechanophore reactivity using another external stimulus. Since a wide variety of polymer systems containing DA mechanophores have been developed, we are convinced that our mechanoreactivity lock has the potential to be a common tool for the regulation of the fascinating force-utilizing properties of such systems.


Preparation of polymers containing DAE/DA

The synthesis, purification, and characterization, which includes the NMR, IR, and GPC data, mechanical characterization, control experiments, and additional details for all polymers, are described in detail in Supplementary Information.

Photochemical reactions

The photochemical reactions were performed employing a Xe lamp equipped with either an optical filter at 313 nm (ring-closing reactions) or an optical glass > 440 nm (ring-opening reactions). The reactions were carried out in anhydrous acetonitrile at concentrations below 30 µmol L–1.


Ultrasound experiments were performed in anhydrous acetonitrile using a Branson sonifire model 250D with a 1.1 cm diameter titanium probe on solutions of the polymers at a concentration of 2 mg mL–1. The solutions were degassed by argon sparging (30 min) prior to sonication and the argon atmosphere was retained during the experiments. Pulsed ultrasound was delivered at a power of 10.6 W cm–2 with on/off periods of one second.

Data availability

All data supporting the findings of this study are available within the article and its Supplementary Information. All other data are available from the corresponding author upon reasonable request.


  1. 1.

    Beyer, M. K. & Clausen-Schaumann, H. Mechanochemistry: the mechanical activation of covalent bonds. Chem. Rev. 105, 2921–2948 (2005).

    Article  PubMed  CAS  Google Scholar 

  2. 2.

    Li, J., Nagamani, C. & Moore, J. S. Polymer mechanochemistry: from destructive to productive. Acc. Chem. Res. 48, 2181–2190 (2015).

    Article  PubMed  CAS  Google Scholar 

  3. 3.

    Davis, D. A. et al. Force-induced activation of covalent bonds in mechanoresponsive polymeric materials. Nature 459, 68–72 (2009).

    ADS  Article  PubMed  CAS  Google Scholar 

  4. 4.

    Imato, K. et al. Mechanophores with a reversible radical system and freezing-induced mechanochemistry in polymer solutions and gels. Angew. Chem. Int. Ed. 127, 6266–6270 (2015).

    Article  Google Scholar 

  5. 5.

    Zhang, H. et al. Mechanochromism and mechanical-force-triggered cross-linking from a single reactive moiety incorporated into polymer chains. Angew. Chem. Int. Ed. 128, 3092–3096 (2016).

    Article  Google Scholar 

  6. 6.

    Robb, M. J. et al. Regioisomer-specific mechanochromism of naphthopyran in polymeric materials. J. Am. Chem. Soc. 138, 12328–12331 (2016).

    Article  PubMed  CAS  Google Scholar 

  7. 7.

    Verstraeten, F., Göstl, R. & Sijbesma, R. P. Stress-induced colouration and crosslinking of polymeric materials by mechanochemical formation of triphenylimidazolyl radicals. Chem. Commun. 52, 8608–8611 (2016).

    Article  CAS  Google Scholar 

  8. 8.

    Cho, S.-Y., Kim, J.-G. & Chung, C.-M. A fluorescent crack sensor based on cyclobutane-containing crosslinked polymers of tricinnamates. Sens. Actuators B. 134, 822–825 (2008).

    Article  CAS  Google Scholar 

  9. 9.

    Chen, Y. et al. Mechanically induced chemiluminescence from polymers incorporating a 1,2-dioxetane unit in the main chain. Nat. Chem. 4, 559–562 (2012).

    ADS  Article  PubMed  CAS  Google Scholar 

  10. 10.

    Song, Y.-K. et al. Fluorescence sensing of microcracks based on cycloreversion of a dimeric anthracene moiety. J. Mater. Chem. 22, 1380–1386 (2012).

    Article  CAS  Google Scholar 

  11. 11.

    Göstl, R. & Sijbesma, R. P. π-extended anthracenes as sensitive probes for mechanical stress. Chem. Sci. 7, 370–375 (2016).

    Article  PubMed  CAS  Google Scholar 

  12. 12.

    Sumi, T., Goseki, R. & Otsuka, H. Tetraarylsuccinonitriles as mechanochromophores to generate highly stable luminescent carbon-centered radicals. Chem. Commun. 53, 11885–11888 (2017).

    Article  CAS  Google Scholar 

  13. 13.

    Jakobs, R. T. M. & Sijbesma, R. P. Mechanical activation of a latent olefin metathesis catalyst and persistence of its active species in ROMP. Organometallics 31, 2476–2481 (2012).

    Article  CAS  Google Scholar 

  14. 14.

    Ramirez, A. L. B. et al. Mechanochemical strengthening of a synthetic polymer in response to typically destructive shear forces. Nat. Chem. 5, 757–761 (2013).

    Article  PubMed  CAS  Google Scholar 

  15. 15.

    Wang, J., Piskun, I. & Craig, S. L. Mechanochemical strengthening of a multi-mechanophore benzocyclobutene polymer. ACS Macro Lett. 4, 834–837 (2015).

    Article  CAS  Google Scholar 

  16. 16.

    Karthikeyan, S., Potisek, S. L., Piermattei, A. & Sijbesma, R. P. Highly efficient mechanochemical scission of silver-carbene coordination polymers. J. Am. Chem. Soc. 130, 14968–14969 (2008).

    Article  PubMed  CAS  Google Scholar 

  17. 17.

    Piermattei, A., Karthikeyan, S. & Sijbesma, R. P. Activating catalysts with mechanical force. Nat. Chem. 1, 133–137 (2012).

    Article  CAS  Google Scholar 

  18. 18.

    Balkenende, D. W. R. et al. Mechanochemistry with metallosupramolecular polymers. J. Am. Chem. Soc. 136, 10493–10498 (2014).

    Article  PubMed  CAS  Google Scholar 

  19. 19.

    Clough, J. M., Balan, A., van Daal, T. L. J. & Sijbesma, R. P. Probing force with mechanobase-induced chemiluminescence. Angew. Chem. Int. Ed. 128, 1467–1471 (2015).

    Article  Google Scholar 

  20. 20.

    Wei, K. et al. Mechanical activation of platinum–acetylide complex for olefin hydrosilylation. ACS Macro Lett. 6, 1146–1150 (2017).

    Article  CAS  Google Scholar 

  21. 21.

    Diesendruck, C. E. et al. Proton-coupled mechanochemical transduction: a mechanogenerated acid. J. Am. Chem. Soc. 134, 12446–12449 (2012).

    Article  PubMed  CAS  Google Scholar 

  22. 22.

    Larsen, M. B. & Boydston, A. J. Successive mechanochemical activation and small molecule release in an elastomeric material. J. Am. Chem. Soc. 136, 1276–1279 (2014).

    Article  PubMed  CAS  Google Scholar 

  23. 23.

    Diesendruck, C. E. et al. Mechanically triggered heterolytic unzipping of a low-ceiling-temperature polymer. Nat. Chem. 6, 623–628 (2014).

    Article  PubMed  CAS  Google Scholar 

  24. 24.

    Hickenboth, C. R. et al. Biasing reaction pathways with mechanical force. Nature 446, 423–427 (2007).

    ADS  Article  PubMed  CAS  Google Scholar 

  25. 25.

    Wang, J., Kouznetsova, T. B., Boulatov, R. & Craig, S. L. Mechanical gating of a mechanochemical reaction cascade. Nat. Commun. 7, 1–8 (2016).

    Google Scholar 

  26. 26.

    Chen, Z. & Xia, Y. Mechanochemical unzipping of insulating polyladderene to semiconducting polyacetylene. Science 357, 475–479 (2017).

    ADS  Article  PubMed  CAS  Google Scholar 

  27. 27.

    Kryger, M. J., Munaretto, A. M. & Moore, J. S. Structure–mechanochemical activity relationships for cyclobutane mechanophores. J. Am. Chem. Soc. 133, 18992–18998 (2011).

    Article  PubMed  CAS  Google Scholar 

  28. 28.

    Fang, X. et al. Biomimetic modular polymer with tough and stress sensing properties. Macromolecules 46, 6566–6574 (2013).

    ADS  Article  CAS  Google Scholar 

  29. 29.

    Church, D. C., Peterson, G. I. & Boydston, A. J. Comparison of mechanochemical chain scission rates for linear versus three-arm star polymers in strong acoustic fields. ACS Macro Lett. 3, 648–651 (2014).

    Article  CAS  Google Scholar 

  30. 30.

    Imato, K. et al. Mechanochromic dynamic covalent elastomers: quantitative stress evaluation and autonomous recovery. ACS Macro Lett. 4, 1307–1311 (2015).

    Article  CAS  Google Scholar 

  31. 31.

    May, P. A., Munaretto, N. F., Hamoy, M. B., Robb, M. J. & Moore, J. S. Is molecular weight or degree of polymerization a better descriptor of ultrasound-induced mechanochemical transduction? ACS Macro Lett. 5, 177–180 (2016).

    Article  CAS  Google Scholar 

  32. 32.

    Li, J., Hu, B., Yang, K., Zhao, B. & Moore, J. S. Effect of polymer grafting density on mechanophore activation at heterointerfaces. ACS Macro Lett. 5, 819–822 (2016).

    Article  CAS  Google Scholar 

  33. 33.

    Oka, H. et al. Enhancing mechanochemical activation in the bulk state by designing polymer architectures. ACS Macro Lett. 5, 1124–1127 (2016).

    Article  CAS  Google Scholar 

  34. 34.

    Imato, K. et al. Repeatable mechanochemical activation of dynamic covalent bonds in thermoplastic elastomers. Chem. Commun. 52, 10482–10485 (2016).

    Article  CAS  Google Scholar 

  35. 35.

    Kosuge, T., Imato, K., Goseki, R. & Otsuka, H. Polymer–Inorganic Composites with Dynamic Covalent Mechanochromophore. Macromolecules 49, 5903–5911 (2016).

    ADS  Article  CAS  Google Scholar 

  36. 36.

    Imato, K. et al. Dynamic covalent diarylbibenzofuranone-modified nanocellulose: mechanochromic behaviour and application in self-healing polymer composites. Polym. Chem. 8, 2115–2122 (2017).

    Article  CAS  Google Scholar 

  37. 37.

    Stevenson, R. & De, Bo,G. Controlling reactivity by geometry in retro-diels–alder reactions under tension. J. Am. Chem. Soc. 139, 16768–16771 (2017).

    Article  PubMed  CAS  Google Scholar 

  38. 38.

    Li, J. et al. Mechanophore activation at heterointerfaces. J. Am. Chem. Soc. 136, 15925–15928 (2014).

    Article  PubMed  CAS  Google Scholar 

  39. 39.

    Min, Y. et al. Sonochemical transformation of epoxy–amine thermoset into soluble and reusable polymers. Macromolecules 48, 316–322 (2015).

    ADS  Article  CAS  Google Scholar 

  40. 40.

    Lyu, B. et al. Surface confined retro diels–alder reaction driven by the swelling of weak polyelectrolytes. ACS Appl. Mater. Interfaces 7, 6254–6259 (2015).

    Article  PubMed  CAS  Google Scholar 

  41. 41.

    Li, H. et al. Promoting mechanochemistry of covalent bonds by noncovalent micellar aggregation. ACS Macro Lett. 5, 995–998 (2016).

    Article  CAS  Google Scholar 

  42. 42.

    Larsen, M. B. & Boydston, A. J. Successive mechanochemical activation and small molecule release in an elastomeric material. J. Am. Chem. Soc. 136, 1276–1279 (2014).

    Article  PubMed  CAS  Google Scholar 

  43. 43.

    Duan, H.-Y. et al. An investigation of the selective chain scission at centered diels–alder mechanophore under ultrasonication. Macromolecules 50, 1353–1361 (2017).

    ADS  Article  CAS  Google Scholar 

  44. 44.

    Irie, M. Diarylethenes for memories and switches. Chem. Rev. 100, 1685–1716 (2000).

    Article  PubMed  CAS  Google Scholar 

  45. 45.

    Asadirad, A. M., Boutault, S., Erno, Z. & Branda, N. R. Controlling a polymer adhesive using light and a molecular switch. J. Am. Chem. Soc. 136, 3024–3027 (2014).

    Article  PubMed  CAS  Google Scholar 

  46. 46.

    Göstl, R. & Hecht, S. Controlling covalent connection and disconnection with light. Angew. Chem. Int. Ed. 53, 8784–8787 (2014).

    Article  CAS  Google Scholar 

  47. 47.

    Göstl, R. & Hecht, S. Photoreversible prodrugs and protags: switching the release of maleimides by using light under physiological conditions. Chem. Eur. J. 21, 4422–4427 (2015).

    Article  PubMed  CAS  Google Scholar 

  48. 48.

    Fuhrmann, A. et al. Conditional repair by locally switching the thermal healing capability of dynamic covalent polymers with light. Nat. Commun. 7, 1–7 (2016).

    Article  CAS  Google Scholar 

  49. 49.

    Kida, J., Imato, K., Goseki, R., Morimoto, M. & Otsuka, H. Photoregulation of retro-diels–alder reaction at the center of polymer chains. Chem. Lett. 46, 992–994 (2017).

    Article  CAS  Google Scholar 

  50. 50.

    Fuhrmann, A., Broi, K. & Hecht, S. Lowering the healing temperature of photoswitchable dynamic covalent polymer networks. Macromol. Rapid Commun. 39, 1700376 (2018).

    Article  CAS  Google Scholar 

  51. 51.

    Konda, S. S. M. et al. Molecular catch bonds and the anti-hammond effect in polymer mechanochemistry. J. Am. Chem. Soc. 135, 12722–12729 (2013).

    Article  PubMed  CAS  Google Scholar 

Download references


This work was supported by KAKENHI grants 17H01205 (H.O.) from the Japan Society for the Promotion of Science (JSPS), as well as by the ImPACT Program of the Council for Science, Technology, and Innovation (Cabinet Office, Government of Japan).

Author information




J.K., K.I. and H.O. conceived and designed the experiments. M.M. contributed molecular design of diarylethene. J.K. performed all the experiments. J.K., K.I., R.G. and D.A. analyzed the data. J.K., K.I. and H.O. wrote the manuscript.

Corresponding author

Correspondence to Hideyuki Otsuka.

Ethics declarations

Competing interests

The authors declare no competing interests.

Additional information

Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Electronic supplementary material

Rights and permissions

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Kida, J., Imato, K., Goseki, R. et al. The photoregulation of a mechanochemical polymer scission. Nat Commun 9, 3504 (2018).

Download citation

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing