Abstract
It is difficult to achieve high efficiency production of hydrophobic graphene by liquid phase exfoliation due to its poor dispersibility and the tendency of graphene sheets to undergo π−π stacking. Here, we report a water-phase, non-dispersion exfoliation method to produce highly crystalline graphene flakes, which can be stored in the form of a concentrated slurry (50 mg mL−1) or filter cake for months without the risk of re-stacking. The as-exfoliated graphene slurry can be directly used for 3D printing, as well as fabricating conductive graphene aerogels and graphene−polymer composites, thus avoiding the use of copious quantities of organic solvents and lowering the manufacturing cost. This non-dispersion strategy paves the way for the cost-effective and environmentally friendly production of graphene-based materials.
Similar content being viewed by others
Introduction
Following the discovery of graphene, many optimistic predictions have been made with regards to its applications in fields ranging from electronics to medicine1,2,3,4. Due to the lack of efficient large-scale production processes, the production of graphene faces a dilemma where a compromise has to be made between scalability and graphene quality4,5,6,7,8,9,10,11,12,13,14. Liquid-phase exfoliation is a promising approach to realize scalable production of high-quality graphene or graphene oxide. Graphite can be exfoliated in organic or aqueous solutions containing a surfactant15 by applying mechanical force (e.g., ultrasonic agitation5, mechanical shearing9, or ball-milling11)5,16. However, large quantities of solvent is always needed in these processes for purification and dispersion due to the limited dispersion stability of graphene flakes. Only a very small amount of graphene, typically <1 mg mL−1, can be dispersed in common solvents, and this is only marginally improved with the help of dispersing agents like superacids17 or ionic liquids18,19, or through sonication for extended periods of time19,20. Reducing the amount of solvent destabilizes the graphene dispersion and leads to the re-stacking of graphene by van der Waals interactions. This means that the production of 1 kg graphene by such dispersion approaches requires at least 1 ton of solvent, which is environmentally unfriendly and economically infeasible.
Three approaches have been explored previously to increase the concentration of graphene dispersions, which include the selection of a suitable solvent with a low enthalpy of mixing with graphene15,16, the introduction of cation−π interaction between graphene and the solvent18, and the creation of electrostatic repulsion between graphene flakes by protonation17,21 or adding surfactants22. Generally, these approaches are only partially effective because of the large ratio of area to thickness (>103) and the tendency of graphene flakes to undergo π−π stacking23. Chemical intercalation-exfoliation methods have also been explored to prepare high-quality graphene in high yields18,24,25. However, these methods require the use of designer ionic liquids18 and have limited scale-up capability (1 mg per batch)24, and suffer from the drawbacks of producing partially exfoliated flakes (>10 nm in thickness)25. Rheological analysis of graphene dispersions indicates that the viscosity increases steeply with increasing graphene contents; for instance, it was observed that graphene-ionic liquid systems had a critical gel concentration as low as 4.2 mg mL−126. The increased viscosity will reduce the efficiency of liquid phase exfoliation and limit its large-scale production. Furthermore, the strong inclination for graphene to undergo π−π stacking has to be overcome and one way to do this is by introducing segregating agents.
In contrast to the conventional exfoliations in a solvent-dispersed system, here, we propose a non-dispersion strategy in which graphene is produced and stored as a flocculated aqueous slurry with concentrations as high as 50 mg mL−1 (5 wt%). The presence of adsorbed ions prevents the re-stacking of graphene flakes and enables their re-dispersion in solution on demand. Partially oxidized graphite is used as the precursor, which is exfoliated by high-rate shearing in an alkaline aqueous solution of pH = 14. Our calculation of inter-sheet interaction energies indicates that under alkaline conditions, the ionization of oxygen-containing groups on graphene layers, even at very low concentrations (e.g., 5.9 atom%), can generate a large electrostatic repulsion energy (EE) to counteract the interlayer van der Waals attraction energy (EvdW). Due to the high ionic strength of the solution, exfoliated graphene flakes tend to form low-viscosity, flocculated slurry rather than a stable dispersion. Such graphene slurry can be easily re-dispersed in N-methyl-2-pyrrolidone (NMP) or alkaline water (pH = 12), and serves as a stock solution of graphene. Such graphene slurry possesses a three-dimensional (3D), loosely stacked microstructure with tunable modulus and viscosity, which can be directly used for 3D printing to form graphene aerogels and conductive polymer materials, without additional dispersion processes.
Results
Non-dispersion strategy for graphene production
To reduce the use of solvent, a non-dispersion strategy was applied to mass produce graphene and fabricate functional materials directly using the flocculated slurry, as opposed to conventional liquid phase method where a large amount of solvent was used (Fig. 1).
Pristine graphite was partially oxidized using a very low molar ratio of oxidizer to carbon in graphite (0.076) to generate a low density of ionizable oxygen-containing groups on graphene layers. Partial oxidation-induced peak at 22.5° in the X-ray diffraction (XRD) spectrum indicates the formation of a stage-1 graphite intercalation compound with an interlayer distance of 8.0 Å (Supplementary Fig. 6)27,28. The pretreated graphite was then exfoliated by applying high-speed shear (Fig. 1b) in an alkaline aqueous solution (pH = 14). Owing to the high ionic strength, the exfoliated graphene flakes instantly flocculated to form a highly concentrated graphene slurry (5 wt% for solid content, 2 L) within 2 h with a yield of 82.5 wt% (with respect to the weight of raw graphite) and a production efficiency of 82.5 g h−1. The yield of highly concentrated graphene and efficiency of graphene production are superior to those in other liquid-phase exfoliation techniques in Fig. 1c. The slurry can be further concentrated up to 23 wt% of solid content by centrifugation or filtration. Such slurry can serve as stock solution of graphene, which can be re-dispersed in NMP or alkaline water (pH = 12) even after standing for over a week (Supplementary Fig. 7). XRD of the aged slurry shows that no π−π stacking occurred in Supplementary Fig. 6. This demonstrates the excellent stability of graphene slurry, an important prerequisite for storage, transportation, and application of graphene flakes.
Meanwhile, the viscosity of system is a critical factor in liquid-phase exfoliation but it is often overlooked9,10,11,12,13,14,15,16. Due to its large aspect ratio, graphene easily forms sediments or gels in solution when exceeding the concentration limit of stable graphene dispersion (<1 mg mL−1)15,16,21,22,26. Although super acids or special ionic liquids may improve the dispersibility of graphene, these systems have high viscosity and limited exfoliation efficiency, and thus impractical for large-scale production17,18. In contrast, our graphene slurry displays a low shear viscosity of 0.064 Pa s at 50 s−1 at 5 wt% solid content, which is over one order of magnitude lower than those of other dispersion systems in Supplementary Fig. 1729,30. The viscosity at practical shear rate of 20,000 rpm, corresponding to 2094 s−1, may even be lower due to shear thinning effect. This affords opportunities for high concentration exfoliation and production of high-quality graphene sheets.
Characterization of graphene flakes
The quality of graphene produced was assessed by scanning transmission electron microscopy (STEM), Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS). In order to probe the quality of individual flakes, as-prepared graphene slurry was washed and re-dispersed prior to test. Atomic-resolution STEM image in Fig. 2a reveals the characteristic honeycomb lattice with long-range periodicity, confirming that the crystal structure of graphene is well retained after partial oxidation and shear-exfoliation. Raman spectra show two characteristic bands at 1325 cm−1 (D band) and 1580 cm−1 (G band), corresponding to the contributions from sp3 type carbon from defects and sp2 hybridized aromatic carbon in Fig. 2b. The ID/IG mapping clearly evidences that most of the defects are located at the edges (Supplementary Fig. 5). The presence of the 2D band at ~2700 cm−1 reflects the well-preserved aromatic structure of graphene, which is absent or negligible in reduced graphene oxide (rGO). The I2D/IG ratio is ~0.45, corresponding to that of ~3 layer graphene31. Since we have to spin-coat NMP dispersion on Si wafer for Raman, it is difficult to avoid the re-stacking of graphene nanosheets during solvent evaporation. The exfoliated graphene only contains a slightly higher oxygen content than pristine graphite (5.9 versus 2.3 atom%) from XPS and elemental analysis in Supplementary Table 1. The corresponding C1s spectrum shows a strong C=C peak at 284.7 eV together with a small tail at 286.4 eV from C−O bonds, while the carbonyl species at 288.6 eV is negligible25,32.
The morphology of graphene flakes was further analyzed by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and atomic force microscopy (AFM). SEM and high-resolution TEM images show micron-sized, single-layer graphene flakes with the typical six-fold symmetry selected-area electron diffraction (SAED) pattern in Supplementary Figs. 1, 3 and 4. This is consistent with the AFM images of the graphene flakes (Fig. 2d and Supplementary Fig. 2), where a statistical analysis of over 100 flakes shows that >90 % of the flakes are single layer (<1 nm in thickness) with a lateral size ranging from 0.5 to 5 μm (Fig. 2e, f). As a result, graphene film obtained by vacuum filtration exhibits a highly hydrophobic surface with a water contact angle of 89.6°, which is comparable to pristine graphene33. The electrical conductivity is measured as 2.5×104 S m−1 and can be further improved to 4.2×104 S m−1 by HI reduction (Supplementary Fig. 9). Such conductivities are among the best values for liquid phase exfoliated graphene, with the reference values tabulated in Supplementary Tables 2 and 39,15,16,17,18,24,26,34.
Mechanism of non-dispersion exfoliation and aqueous dispersion
It is challenging to obtain a stable graphene aqueous solution without adding surfactants21. The stability of our graphene aqueous dispersion is pH-dependent, with a maximum dispersion concentration at pH = 12 (Fig. 3a)35. Beyond pH = 12, the graphene dispersion becomes unstable due to ion-induced flocculation. Zeta potential (ζ) is a common indicator for the stability of nanomaterials. As shown in Fig. 3b, the graphene dispersion has a maximum ζ value of −42.4 mV at pH = 12, suggesting a strong electrostatic repulsive interaction between graphene flakes. This observation can be explained by the C1s XPS spectrum, where hydroxyl groups (−OH) are the primary oxygen-containing groups on our graphene. Since the dissociation constant of a phenolic hydroxyl group (pK a ) is ~10.036, the degree of ionization (W) increases at higher pH values (Fig. 3c). At pH values higher than 12, the hydroxyl groups on graphene will be fully ionized. Nevertheless, it remains an open question whether the presence of 5.9 atom% of oxygen-containing groups is sufficient to generate an electrostatic repulsive force against π−π re-stacking.
To investigate the interactive forces governing the dispersion of our graphene, we employ the classical Derjaguin−Landau−Verwey−Overbeek (DLVO) theory to explain our experimental observations. Two adjacent graphene flakes in the dispersion are treated as two parallel plates with a separation distance of h, where the electrical double layer (EDL, thickness denoted by κ−1) due to negatively charged oxygen groups on the surface and adsorbed counter ions determines the dispersion stability (Supplementary Fig. 14). The total interaction energy (ET) is given by the sum of the electrostatic repulsion energy EE and the van der Waals attraction energy EvdW37 or, ET = EE+EvdW. For graphene flakes, EvdW is given by \(E_{\rm vdW}{\mathrm{ = }} - {{d}}_0^4{\mathrm{\gamma }}/h^4\)22, where d0 = 0.335 nm and γ is the surface energy (70 mJ m−2). EE depends on the electrostatic potential on the graphene surface (ψ0), the electrolyte concentration (c), and the flake separation (h)38,39. In a previous study, EE was calculated by measuring the value of Zeta potential (ζ), which gives the change of EE as a function of h22. However, this calculation is applicable only when ζ < 25 mV22. To overcome this limit, we have calculated EE from available data for ψ0, h, and other constants (Supplementary Eqs. (2) and (3))38,39. Using the Poisson−Boltzmann (PB) equation to derive the relationship between ψ0 and surface charge density (σ), we can write \(\sigma = 4Lce{\mathrm{sinh}}(e\psi _0{\mathrm{/}}2kT){\mathrm{/}}\kappa\)39, where L is the Avogadro constant, e is the elementary electronic charge, k is the Boltzmann constant, κ is the Debye−Hückel parameter, and T is the absolute temperature. Assuming that all oxygen-containing groups on our graphene sheets are hydroxyl group, and σ is dependent on the density of −OH groups together with the degree of ionization W at different pH values, σ can be also expressed as σ=WAe/(2.62×10−20) (see Supplementary Notes 1 and 2), where A is the molar ratio of oxygen atoms to carbon atoms, that is:
At pH = 12, the obtained EE curve for graphene dispersion is presented in Fig. 3d, revealing that the repulsive force increases with decreasing h. After taking EvdW into account, the variation of the total interaction energy ET with h between two adjacent graphene flakes is displayed in Fig. 3d. A large energy barrier (EB = 5.22 mJ m−2) against aggregation is observed, which is ~8 times larger than that of a surfactant-stabilized graphene dispersion (~0.64 mJ m−2)22. Even at oxygen coverage of 1 atom%, the calculation result also shows a relatively large energy barrier (1.83 mJ m−2) in Supplementary Fig. 16 to prevent re-stacking. Figure 3e and Supplementary Fig. 15 further provide the EE and ET curves at different pH values. EE is nearly zero in the pH range of 7~8 due to the lack of ionized oxygen-containing groups, leading to the re-stacking of graphene flakes. In contrast, a large number of counter-ions (Na+) will be adsorbed onto the surface of graphene when pH > 13. This results in the compression of the EDL from 3.0 nm at pH = 12 to 0.3 nm at pH = 14 (Supplementary Table 4), and the flocculation of graphene flakes. We observe a similar flocculation behavior when an equivalent amount of NaCl was added to the graphene dispersion at pH = 12, suggesting that the absorbed ions prevent the π−π aggregation of graphene flakes40, similar to the flocculated clay nanoplatelets37,41 (Supplementary Fig. 12).
The mechanism of non-dispersion exfoliation can be explained by the pH-dependent stability of graphene dispersions. Indeed, the yield of graphene is very low (< 1.2 wt%) when the pretreated graphite is exfoliated at pH = 12, even though the dispersion stability is highest at this pH value. This is attributed to the inherent low dispersibility of graphene which sets a limit on the yield of high-concentration exfoliation. In contrast, when exfoliated at pH = 13 or 14, graphene flakes rapidly flocculate due to the compressed EDL, which reduces the system viscosity and facilitates exfoliation. The flocculated graphene flakes are unable to form π−π stacking due to the presence of absorbed ions and the loose stacking, so that they can be re-dispersed in NMP or alkaline solutions.
Storage and dispersion of graphene slurry
The microstructure of graphene slurry largely affects its solution processing capability and applications. Actually, we found that the morphology and solution behavior of graphene slurries are also pH-dependent. As shown in Fig. 4a and Supplementary Fig. 18, as-obtained graphene slurry (pH = 14) behaves like an elastic gel which has a steady viscosity over two orders of magnitude greater than that of the washed graphene slurry at pH = 7. The latter exhibits a fluid-like behavior, similar to the graphite suspension, for which the viscosity is controlled solely by the weak interaction between water molecules and graphite plates. To observe their microstructure, two samples were prepared through liquid nitrogen quenching and freeze-drying to avoid possible structural changes. As shown in Fig. 4b, as-obtained graphene slurry has a loosely stacking structure, similar to that of the flocculated inorganic clays37,41. In contrast, the slurry at pH = 7 exhibits a face-to-face aggregation due to the lack of electrostatic repulsion from charged functional groups (Supplementary Fig. 19a). In addition, we observed a ~3-fold volume shrinkage and one order of magnitude decrease in the specific surface area (SSA) from pH = 14 to pH = 7, which also reflects pH-dependent structure changes in graphene slurries (Supplementary Fig. 19).
To further quantify the stability of two graphene slurries, we calculate the interlayer interaction energies for the graphene slurries at pH = 14 and 7, respectively. As shown in Fig. 4c, a trough (the secondary minimum) appears at h = 1.8 nm at pH = 14 because the electrostatic energy EE decreases more rapidly with increasing distance compared to EvdW42. Moreover, since this trough is quite shallow (0.033 mJ/m2), the flocculated graphene slurry is re-dispersible, even in form of graphene cake with extreme high loading (23 wt%, Fig. 4d)37. For the case at pH = 7, however, ET decreases monotonically with h and has a deep primary minimum appeared at the very small h, where the van der Waals attractive force predominates, leading to unfavorable π−π aggregations37.
3D printing of concentrated graphene slurry
High-concentration graphene slurries are highly desired for the fabrication of many functional materials, for instance, printing or spin-coating typically requires a work window of high solid contents in Fig. 5a. The log−log plot of graphene content (c) against storage/loss modulus reveals a critical gel concentration (cg) of ~1.25 wt% for the graphene slurry at pH = 14. Below this cg, the flocculated graphene flakes form individual micro-scale flocs. The system exhibits a liquid-like behavior for which loss modulus (G″) is greater than storage modulus (G′) in the measured frequency range. Beyond cg, where G’′ is larger than G″, the slurry behaves like an elastic gel. Here, we have fabricated various graphene aerogel structures via 3D-printing of highly concentrated slurry at the elastic gel region in Fig. 5d. To the best of our knowledge, this is the first demonstration of water-phase 3D-printing of exfoliated graphene43,44. Previous efforts on graphene aerogels rely on the sol-gel chemistry, which is challenging for large-scale production45,46. The printed aerogel is macroporous (Fig. 5e, f) with good mechanical strength. Its SSA is determined from methyl blue (MB) absorption measurements (1240 m2 g−1, Supplementary Fig. 19b). The electrical conductivity reaches ~197 S m−1 at a density of 100 mg cm−3 (Fig. 5g), which is comparable to 3D-printed rGO networks by conventional dispersion approaches43,44, although it is inferior to that of CVD-grown method47. By incorporating high-temperature annealing in commercial graphite production, it is possible to further improve the electrical conductivity to a level comparable with that of CVD-grown aerogels48. The printed graphene aerogels can be used as 3D templates for in-situ polymerization, which are promising for applications in a wide range of energy storage devices49 and durable absorbent materials50. Owing to the porous structure of the graphene aerogels, the monomer can diffuse rapidly into the graphene framework. After polymerization, polydimethylsiloxane (PDMS)−graphene composites were obtained, where PDMS was evenly distributed in the graphene framework. The resulting composite exhibits nonlinear super-elastic behavior and ultra-large, reversible compressibility with a strain up to 40%. Multi-cycle compression test also shows that after the first loading−unloading loop, the stress was still stabilized at 53 kPa in the following nine loops (Supplementary Fig. 20), demonstrating a stable, bi-continuous texture in the PDMS−graphene composites.
In conclusion, we have demonstrated an industrially viable water-phase exfoliation strategy for preparing high-quality graphene and composites. This approach bypasses the destructive chemical oxidation processes, avoids the use of copious quantities of solvent, and addresses the critical issues related to the storage and transportation of graphene. Using this strategy, graphene flakes can be exfoliated in the form of highly concentrated slurries (5 wt%) with high production efficiencies (82~170 g h−1). The exfoliated flakes form loosely stacked, flocculated aggregates due to the presence of adsorbed ions on the weakly oxidized surface. Such graphene slurries possess a 3D loosely stacking microstructure with rheological properties that are markedly different from that of closely stacked graphene flakes; for example, they can be directly 3D-printed to fabricate conductive graphene aerogels and be used to fabricate high graphene content composites. Different from traditional oxidation-reduction approaches, this non-dispersion exfoliation strategy allows a cost-effective, large-scale production, storage and transport of graphene in aqueous medium.
Methods
Pretreatment of graphite
Pretreated graphite was obtained using the conventional intercalation process using sulfuric acid. KMnO4 (100 g, 1 wt equiv.) was added in batches into concentrated H2SO4 (2 L, 98%) over a period of 30 min in an ice-water bath. Then the ice-water bath was removed and natural graphite flake (100 g, 1 wt equiv., 500 μm) was added. The system was stirred at 35 °C for 2 h. After reaction, the black flakes were filtered through a 200-mesh sieve (Supplementary Fig. 11 and Movie 1) and separated from dark green solution. Concentrated H2SO4 was recovered for recycling. Then the filter cake was poured into 2 L of ice water to avoid sudden increase in temperature. Fifty milliliters of 30 wt% H2O2 was added to decompose the insoluble manganese dioxide. After filtering and washing, wet powders of pretreated graphite were obtained for subsequent water-phase exfoliation.
Water-phase exfoliation
Typically, 100 g of pretreated graphite (based on the weight of raw graphite) was added into 2 L of 1 M NaOH aqueous solution (pH = 14 alkaline water by adding 80 g of NaOH into 2 L of DI water). The mixture was subjected to shear at 20,000 rpm for 1 h at r.t. by using an FA 40 high shear dispersing emulsifier (Fluko) with a working tool, resulting in a black graphene slurry. For yield calculation, the graphene slurry was centrifuged at 10,000 rpm for 10 min and repeatedly washed by a large amount of water (4~6 times) until pH approaches 10. Then the washed slurry was re-dispersed in NMP at a concentration of ~0.1 mg mL−1 and sonicated for 1 min. The resulting graphene−NMP dispersion was centrifuged at 2000 rpm for 30 min. The supernatant in the upper two-third solution was collected and the precipitate was re-dispersed in NMP. The centrifugation and re-dispersing processes were repeated until the supernatant is colorless. The collected upper and lower sections of the supernatant were dried separately in a vacuum oven at 60 °C for 10 h. Finally, the mass yield of graphene flakes in slurry was calculated by the mass ratio of dried upper graphene to raw graphite. Control experiments can be found in Supplementary Figs. 8, 12 and 13. Large-scale production of 1 kg graphene is provided in Supplementary Fig. 10.
3D printing of graphene slurry
As-exfoliated graphene slurry at pH = 14 was concentrated to a suitable concentration (from 8 to 23 wt%) by filtration through a G4 funnel and subsequently used as a printable ink without modification. The concentrated graphene slurry was transferred to a 20 mL syringe barrels and printed using a robotic deposition device. The diameter of the printing nozzles ranged from 200 to 600 μm. The pressure was regulated during printing in air to maintain constant ink flow. After printing, the printed structures were frozen at −20 °C for 5 h and freeze-dried for 24 h. Then the dried structures were carefully immersed into water to remove the residual ions. Finally, graphene aerogels was obtained by freeze-drying process for 24 h.
Equipment
The following equipment was used: High-rate shearing (FA 40 emulsifying machine, Fluko), STEM (JEOL JEM-ARM200F with aberration-correction, 60 kV), TEM/SAED (Tecnai G2 20 TWIN and JEM-2100F, 200 kV), AFM (Multimode 8), XPS (AXIS UltraDLD, monochromatic Al K α ), Rheology (HAAKE MARS III, cone-plate or cylinder geometry at 25 °C), SEM (Ultra 55), Raman (XploRa, 532 nm), XRD (PANalytical X’Pert PRO, Cu K α , operated at 40 kV and 40 mA), UV-Vis (Lambda 35), Zeta (ZS90), EA (vario EL III), Conductivity (SX1944, four-point probe), Contact angle (JC2000 DM), 3D-printing (Bio-Architect®–Pro), Multi-cycle compression (Reger-RWT10).
Data availability
All data are available from the authors upon reasonable request.
References
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Zhu, Y. W. et al. Graphene and graphene oxide: synthesis, properties, and applications. Adv. Mater. 22, 3906–3924 (2010).
Zurutuza, A. & Marinelli, C. Challenges and opportunities in graphene commercialization. Nat. Nanotechnol. 9, 730–734 (2014).
Lin, S., Dong, L., Zhang, J. J. & Lu, H. B. Room-temperature intercalation and ~1000-fold chemical expansion for scalable preparation of high-quality graphene. Chem. Mater. 28, 2138–2146 (2016).
Yang, X. W., Cheng, C., Wang, Y. F., Qiu, L. & Li, D. Liquid-mediated dense integration of graphene materials for compact capacitive energy storage. Science 341, 534–537 (2013).
Prasai, D., Tuberquia, J. C., Harl, R. R., Jennings, G. K. & Bolotin, K. I. Graphene: corrosion-inhibiting coating. ACS Nano 6, 1102–1108 (2012).
Stankovich, S. et al. Graphene-based composite materials. Nature 442, 282–286 (2006).
Paton, K. R. et al. Scalable production of large quantities of defect-free, few-layer graphene by shear exfoliation in liquids. Nat. Mater. 13, 624–630 (2014).
Hernandez, Y. et al. High-yield production of graphene by liquid-phase exfoliation of graphite. Nat. Nanotechnol. 3, 563–568 (2008).
León, V., Rodriguez, A. M., Prieto, P., Prato, M. & Vázquez, E. Exfoliation of graphite with triazine derivatives under ball-milling conditions: preparation of few-layer graphene via selective noncovalent interactions. ACS Nano 8, 563–571 (2014).
Chiu, P. L. et al. Microwave- and nitronium ion-enabled rapid and direct production of highly conductive low-oxygen graphene. J. Am. Chem. Soc. 134, 5850–5856 (2012).
Peng, L. et al. An iron-based green approach to 1-h production of single-layer graphene oxide. Nat. Commun. 6, 5716 (2015).
Lu, J. et al. One-pot synthesis of fluorescent carbon nanoribbons, nanoparticles, and graphene by the exfoliation of graphite in ionic liquids. ACS Nano 3, 2367–2375 (2009).
Coleman, J. N. et al. Liquid-phase exfoliation of nanotubes and graphene. Adv. Funct. Mater. 19, 3680–3695 (2009).
Coleman, J. N. et al. Liquid exfoliation of defect-free graphene. Acc. Chem. Res. 46, 14–22 (2013).
Behabtu, N. et al. Spontaneous high-concentration dispersions and liquid crystals of graphene. Nat. Nanotechnol. 5, 406–411 (2010).
Matsumoto, M., Saito, Y., Park, C., Fukushima, T. & Aida, T. Ultrahigh-throughput exfoliation of graphite into pristine ‘single-layer’ graphene using microwaves and molecularly engineered ionic liquids. Nat. Chem. 7, 730–736 (2015).
Nuvoli, D. et al. High concentration few-layer graphene sheets obtained by liquid phase exfoliation of graphite in ionic liquid. J. Mater. Chem. 21, 3428–3431 (2011).
Khan, U., O’Neill, A., Lotya, M., De, S. & Coleman, J. N. High-concentration solvent exfoliation of graphene. Small 6, 864–871 (2010).
Bepete, G. et al. Surfactant-free single layer graphene in water. Nat. Chem. 9, 347 (2016).
Lotya, M. et al. Liquid phase production of graphene by exfoliation of graphite in surfactant/water solutions. J. Am. Chem. Soc. 131, 3611–3620 (2009).
Kole, M. & Dey, T. K. Investigation of thermal conductivity, viscosity, and electrical conductivity of graphene based nanofluids. J. Appl. Phys. 113, 084307 (2013).
Kovtyukhova, N. I. et al. Non-oxidative intercalation and exfoliation of graphite by Brønsted acids. Nat. Chem. 6, 957–963 (2014).
Dimiev, A. M., Ceriotti, G., Metzger, A., Kim, N. D. & Tour, J. M. Chemical mass production of graphene nanoplatelets in ~100% yield. ACS Nano 10, 274–279 (2016).
Zhang, B. Q. et al. Stable dispersions of reduced graphene oxide in ionic liquids. J. Mater. Chem. 20, 5401–5403 (2010).
Dimiev, A. et al. Direct real-time monitoring of stage transitions in graphite intercalation compounds. ACS Nano 7, 2773–2780 (2013).
Nishitani, R., Sasaki, Y. & Nishina, Y. Kinetic of staging transition in H2SO4-graphite intercalation compounds. Synth. Met. 34, 315–321 (1989).
Li, J. et al. Efficient inkjet printing of graphene. Adv. Mater. 25, 3985–3992 (2013).
Naficy, S. et al. Graphene oxide dispersions: tuning rheology to enable fabrication. Mater. Horiz. 1, 326–331 (2014).
Ferrari, A. C. et al. Raman spectrum of graphene and graphene layers. Phys. Rev. Lett. 97, 187401 (2006).
Pei, S. F., Zhao, J. P., Du, J. H., Ren, W. C. & Cheng, H. M. Direct reduction of graphene oxide films into highly conductive and flexible graphene films by hydrohalic acids. Carbon N. Y. 48, 4466–4474 (2010).
Wang, S., Zhang, Y., Abidi, N. & Cabrales, L. Wettability and surface free energy of graphene films. Langmuir 25, 11078–11081 (2009).
Dong, L. et al. Reactivity-controlled preparation of ultralarge graphene oxide by chemical expansion of graphite. Chem. Mater. 29, 564–572 (2017).
Li, D., Müller, M. B., Gilje, S., Kaner, R. B. & Wallace, G. G. Processable aqueous dispersions of graphene nanosheets. Nat. Nanotechnol. 3, 101–105 (2008).
Fernandez, L. P. & Hepler, L. G. Heats and entropies of ionization of phenol and some substituted phenols. J. Am. Chem. Soc. 81, 1783–1786 (1959).
Luckham, P. F. & Rossi, S. The colloidal and rheological properties of bentonite suspensions. Adv. Colloid Interface Sci. 82, 43–92 (1999).
Luo, G. X., Feng, R. J., Jin, J. & Wang, H. P. Strong interaction of colloidal particles: an extension of Langmuir’s method. Langmuir 17, 2167–2171 (2001).
Ohshima, H. Approximate expression for the potential energy of double-layer interaction between two parallel similar plates with constant surface potential. Colloid Surf. A 146, 213–216 (1999).
Zhang, C., Tjiu, W. W., Fan, W., Huang, S. & Liu, T. X. A novel approach for transferring water-dispersible graphene nanosheets into organic media. J. Mater. Chem. 22, 11748–11754 (2012).
Sohm, R. & Tadros, T. F. Viscoelastic properties of sodium montmorillonite (Gelwhite H) suspensions. Colloid Interface Sci. 132, 62–71 (1989).
Hahn, M. W., Abadzic, D. & O’Melia, C. R. Aquasols: on the role of secondary minima. Environ. Sci. Technol. 38, 5915–5924 (2004).
Zhu, C. et al. Highly compressible 3D periodic graphene aerogel microlattices. Nat. Commun. 6, 6962 (2015).
García-Tuñon, E. et al. Printing in three dimensions with graphene. Adv. Mater. 27, 1688–1693 (2015).
Worsley, M. A. et al. Synthesis of graphene aerogel with high electrical conductivity. J. Am. Chem. Soc. 132, 14067–14069 (2010).
Xu, Y., Sheng, K., Li, C. & Shi, G. Self-assembled graphene hydrogel via a one-step hydrothermal process. ACS Nano 4, 4324–4330 (2010).
Chen, Z. P. et al. Three-dimensional flexible and conductive interconnected graphene networks grown by chemical vapour deposition. Nat. Mater. 10, 424 (2011).
Worsley, M. A. et al. Synthesis and characterization of highly crystalline graphene aerogels. ACS Nano 8, 11013–11022 (2014).
Ye, S., Feng, J. & Wu, P. Highly elastic graphene oxide–epoxy composite aerogels via simple freeze-drying and subsequent routine curing. J. Mater. Chem. A 1, 3495–3503 (2013).
Li, R. et al. A facile approach to superhydrophobic and superoleophilic graphene/polymer aerogels. J. Mater. Chem. A 2, 3057–3064 (2014).
Acknowledgements
H. Lu appreciates financial support from 973 project (2011CB605702), the National Science Foundation of China (51173027), and Shanghai key basic research project (14JC1400600). K.P. Loh thanks National Research Foundation, Prime’s Minister Office for support for NRF Investigator award “Graphene oxide a new class of catalytic, ionic and molecular sieving materials, award number NRF-NRF12015-01”. L.D. acknowledges financial support from Fudan University. Z.C. acknowledges financial support in the form of a NGS scholarship.
Author information
Authors and Affiliations
Contributions
L.D. and Z.C. conceived the research and wrote the draft. L.D. conducted the exfoliation of graphene and DLVO calculations. X.Z. and Z.C. conducted TEM characterization and data analysis. L.D. and J.M. performed the 3D printing and performance analysis. Z.C., S.L., Y.B., L.C., J.M. and K.L. assisted in sample preparation and materials characterization. H.L. and K.P.L. supervised the research. All authors discussed and commented on this manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Dong, L., Chen, Z., Zhao, X. et al. A non-dispersion strategy for large-scale production of ultra-high concentration graphene slurries in water. Nat Commun 9, 76 (2018). https://doi.org/10.1038/s41467-017-02580-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-02580-3
This article is cited by
-
A review of magnetic nanocomposites for EMI shielding: synthesis, properties, and mechanisms
Journal of Materials Science (2024)
-
Impact of probe sonication and sulfuric acid pretreatment on graphene exfoliation in water
Scientific Reports (2023)
-
High-quality, binder-free, homogeneous, robust and multilayer functional graphene oxide films on copper by electrophoresis
Graphene and 2D Materials (2023)
-
Ground-state electron transfer in all-polymer donor:acceptor blends enables aqueous processing of water-insoluble conjugated polymers
Nature Communications (2023)
-
The fabrication of polyethylene/graphite nanoplatelets composites for thermal management and electromagnetic interference shielding application
Journal of Materials Science (2022)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.