Amending soil with biochar (pyrolized biomass) is suggested as a globally applicable approach to address climate change and soil degradation by carbon sequestration, reducing soil-borne greenhouse-gas emissions and increasing soil nutrient retention. Biochar was shown to promote plant growth, especially when combined with nutrient-rich organic matter, e.g., co-composted biochar. Plant growth promotion was explained by slow release of nutrients, although a mechanistic understanding of nutrient storage in biochar is missing. Here we identify a complex, nutrient-rich organic coating on co-composted biochar that covers the outer and inner (pore) surfaces of biochar particles using high-resolution spectro(micro)scopy and mass spectrometry. Fast field cycling nuclear magnetic resonance, electrochemical analysis and gas adsorption demonstrated that this coating adds hydrophilicity, redox-active moieties, and additional mesoporosity, which strengthens biochar-water interactions and thus enhances nutrient retention. This implies that the functioning of biochar in soil is determined by the formation of an organic coating, rather than biochar surface oxidation, as previously suggested.
Biochar is the product of O2-limited thermal treatment of biomass (pyrolysis) and is used in agriculture as a livestock feed supplement, compost additive and soil amendment as well as for manure treatment1. It is applied to improve animal, plant and soil health, to reduce nutrient losses by volatilization or leaching, to prevent soil erosion, and to improve soil water retention, soil carbon content and the long-term fertility of agricultural soils2, 3. Biochar is very recalcitrant and can contribute to climate change mitigation by the sequestration of stable carbon4 and reduction of agricultural emissions of CO2, N2O and CH4 5.
Positive impacts of biochar on (agro)ecosystems are often explained by the porosity and sorption capacity3, redox properties6, 7, and liming capacity of biochar8 and by biochar's influence on soil structure9, 10, water holding capacity11 and nutrient transformations in soil2. However, despite these insights into biochar functioning in soil, a detailed mechanistic understanding of how biochar influences plant growth is still lacking. Biochar was shown to increase crop yield by up to 400% compared to fully fertilized controls12, while the overall mean of biochar-induced yield increases is 18% according to meta-analyses13. However, many studies used high biochar application amounts of >10 t ha−1, which is not economically feasible. Recent research suggested that biochar should be combined with organic amendments to increase soil fertility even when biochar is applied at low (0.5–2 t ha−1) biochar application rates14, 15. Co-composting, which consists of mixing biochar with manure or other compost feedstock with high contents of both nutrients and labile organic carbon before starting an aerobic composting process, was shown to enhance the agronomic performance of biochar as a soil amendment16. The co-composted biochar handpicked from the final biochar-amended compost was shown to promote plant growth beyond the combination of pristine biochar with either mineral fertilizer or mature non-biochar-amended compost. This phenomenon was explained by co-composted biochar’s slow release of essential plant nutrients like nitrate and phosphate16. However, despite evidence for surface oxidation, sorption of organic molecules and increase in carboxyl groups on biochar surfaces17, 18, the underlying mechanisms and the impact of co-composting on the biochar microstructure remain unclear. A mechanistic understanding of how co-composting impacts biochar’s reactivity and function is a prerequisite for large-scale and global beneficial use of biochar in agriculture, additionally for understanding the formation of extremely fertile Amazonian and African Dark Earths that received anthropogenic input of both nutrient-rich organic matter and pyrogenic carbon centuries ago19, 20, and eventually for the development of low-cost biochar-based fertilizers that can promote high crop yields with comparably small application doses of biochar21, 22. In addition, mechanistic insights into biochar co-composting will help to improve our current understanding of how biochar ages in soil23.
On the surface of co-composted biochar, we identified an organic coating by applying a suite of spectro(micro)scopical techniques and argue that this coating controls the interaction of co-composted biochar with water and nutrients. We found that a similar coating was present in non-composted but soil-aged biochar. This study demonstrates why co-composted or organically amended biochar helps optimize its agronomic performance.
Extraordinary nutrient retention by co-composted biochar
We manually picked co-composted biochar particles (BCcomp) after 60 days of aerobic composting plus 6 months of storage and analyzed them without any further sample preparation24. BCcomp contained 2.0 ± 0.1 g NO3 −-N kg−1, of which only 43% could be extracted by conventional extraction (Fig. 1), clearly demonstrating the potential of co-composted biochar as a slow release fertilizer. We investigated both pristine (fresh, no post-production treatment, no detectable nitrate) biochar (BCprist) and BCcomp with a suite of spectro(micro)scopic and mass-spectrometric techniques to identify the underlying molecular mechanism(s) for the remarkable retention of anionic and cationic nutrients by co-composted biochar16 and to evaluate the impact of co-composting on the long-term stability of biochar, i.e., its carbon sequestration potential.
Spectromicroscopy and mass spectrometry
First, we used13C solid-state nuclear magnetic resonance (NMR) spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) to identify co-composting-induced changes in biochar carbon speciation on the bulk level and structural and chemical changes of the biochar surface. NMR spectroscopy did not reveal significant differences in C speciation between BCprist and BCcomp on the bulk level (Supplementary Fig. 1). In line with this, bulk XPS, i.e., XPS of biochar particles powdered and sieved to 100 µm, only showed a minor increase in oxidized carbon species (C–O, C = O, COO, Fig. 2a-b). However, XPS applied on whole particles revealed a considerable increase in the O/C ratio and increase in N content by co-composting (Fig. 2a-b). Since XPS is a surface sensitive technique that provides information on the outermost ~10 nm this also suggests that only the biochar surface, not the bulk biochar particles, is altered during co-composting. SEM revealed that this surface alteration of BCcomp is not homogeneous, but that there were regions of degraded biochar pores (Fig. 2c) and hotspots of partially and completely coated biochar surfaces (Fig. 2d, e). Elemental mapping using energy dispersive X-ray spectroscopy (EDS) indicated heterogeneous contents of Fe, Al and Si in the coating (Fig. 2f).
We characterized the coating in situ with mass spectrometry and spectroscopic techniques across a range of both spatial and energy resolutions to identify the chemical and physical properties of the surface modification. Desorption atmospheric pressure photoionization Fourier-transformed ion-cyclotron resonance mass spectrometry (DAPPI FT-ICR MS) applied to biochar particles provides precise information on the elemental composition of compounds available for desorption on the biochar surface. According to DAPPI FT-ICR MS, co-composting increased the relative abundance of CHON (CWHXOyNz) class compounds and decreased the relative abundance of CHO (CxHyOz) class compounds (Fig. 3). Furthermore, co-composting increased the abundance-weighted N/C ratio of all formulas assigned to the compounds that desorbed from the biochar surface at atmospheric pressure from 0.008 to 0.029, and increased the abundance-weighted O/C ratio of such formulas from 0.388 to 0.618. Within the CHON class, the van Krevelen diagram (Supplementary Fig. 2) suggests an increase in the O/C ratio of the desorbed compounds, consistent with an actual increase in the abundance-weighted O/C ratio from 0.278 to 0.566. To accurately identify carbon functional groups and spatial distribution of N in ultra-thin sections of BCcomp, we used scanning transmission X-ray microscopy (STXM) which has a spot size of 30–50 nm. We could clearly demonstrate the heterogeneous distribution of nitrogen suggesting that there are hotspots of nutrient retention on the outer surface and inside pores of the biochar, rather than a homogenous enrichment and these hotspots showed a higher absorption by carboxylic moieties (Fig. 4). However, beyond this change, there are neither considerable differences in carbon speciation between bulk co-composted biochar and these hotspots nor between pristine and co-composted biochar (Supplementary Fig. 3).
Scanning transmission electron microscopy (STEM) equipped with electron energy loss spectroscopy (EELS) allows sub-micron scale resolutions on ultra-thin sections of the biochars and information on the carbon and nitrogen speciation in precisely (nm-range) defined regions. With STEM, we identified a meso-porous organic coating of up to 200 nm thickness on a substantial share of the investigated surfaces of BCcomp (Fig. 5 and Supplementary Fig. 4). STEM samples were sputter-coated with gold on a three-dimensional (3D) moving sample holder prior to sample preparation to clearly differentiate the sample-epoxy resin border. The organic coating was thicker on pore surfaces than on exposed, outer surfaces, where it was mostly limited to 10–20 nm non-porous spots (Supplementary Fig. 4D). The coating was completely absent in BCprist (Supplementary Fig. 5). EELS revealed a higher N content of the coating compared to the carbonaceous biochar matrix and minor alterations of the C speciation (Fig. 5b–e) including peak shifts of the aromatic C = C 1s–π* transition by 0.5 eV from co-composted biochar matrix to the coating (Fig. 5c, d). Additionally, we found nanometer-sized hot-spots of silica and other elements in both pristine and co-composted biochar (Supplementary Fig. 5B). Similar hotspots of calcium were identified on the surface of the co-composted biochar, right under the coating (Fig. 5f, g). A similar phenomenon was described for pyrogenic organic matter isolated from Terra Preta25.
Additional STEM on crushed BCcomp revealed the formation of complex organo-mineral associations involving Ca and redox-active Fe (Supplementary Fig. 6). Similar structures have been suggested as hotspots for redox reactions in the liquid and gaseous phase of soils and suggest that the organic coating is not only a porous matrix for nutrient retention, but also a potential location for nutrient transformations26, 27.
To obtain more detailed information on the identity and properties of this organic coating, the material was characterized ex situ by first pre-washing the BCprist and BCcomp with water to remove loosely attached compost organic matter followed by extraction of the biochar particles with 0.05 M NaOH28 to isolate the organic coating for further analysis after filtration to <0.45 µm. After this procedure, the co-composted biochar lost its brownish color and is almost completely black again (Supplementary Fig. 7). Ion chromatography and elemental analysis of the extracted coating revealed an increased content of N and C, especially nitrate, organic carbon, carbonate, Ca and K in BCcomp compared to extracts obtained from BCprist (Supplementary Table 4). The1H solution NMR spectrum of the BCprist extract comprised only few defined peaks, while the spectrum of BCcomp extracts was dominated by broad peaks that did not allow detailed evaluation (Supplementary Fig. 10). The complexity of the spectrum showed that the formation of the organic coating in the co-composted biochar cannot solely be explained by oxidation of the original biochar carbon but entirely new species/entities of carbon were evidently introduced into the biochar porous system during co-composting, which is supported by data obtained by spectrofluorometry (Supplementary Fig. 11). This compost derived organic carbon have had to be sorbed on the biochar because if it just had been weakly associated with the biochar, it would have been removed already by the first washing step (10 min with water), while analysis was performed on the eluate of the third washing step. In line with that, Fourier-transformed infrared (FTIR) spectroscopy of freeze-dried BCcomp extracts revealed similar bands as found in both a powdered BCprist and powdered compost reference (Fig. 6a). This suggests that biochar nano-particles were associated with compost organic matter to form the porous coating. Biochar nano-particles can form during co-composting by physical disintegration, potentially by graphitic sheet expansion, when biochar sorbs water from the compost29. Quantification of the electron exchange capacity (EEC), i.e., the sum of electron accepting and donating capacity6, revealed that the EEC per mmol of carbon of BCcomp eluates is higher than the EEC both of BCprist and of compost eluates (Fig. 6b). Thus, the chemistry of the coating is different from both of these compounds. Our data suggests that the reaction of compost organic matter with biochar created more reactive carbon moieties that then formed the organic coating. Although, looking at EDC/EEC ratios, eluate of co-composted biochar presents similar ratio than compost, indicating that the co-composted biochar presents the same redox state than the compost. From an absolute point of view, pristine biochar shows lower EEC which is increased by co-composting which could be attributed to conformational re-arrangements of carbon moieties taking place during the sorption compost organic matter onto pristine biochar, making the redox-active moieties more exposed to the electrochemical techniques. Alternatively, biochar might have preferentially sorbed compounds with a higher EEC than the average EEC of the compost. However, there was no clear evidence of fractionation of the organic matter as consequence of the sorption, as suggested by fluorescence emission spectroscopy (Supplementary Fig. 11).
Porosity and interaction with water
To identify the mechanism responsible for the retention of polar nutrients such as nitrate by the observed porous organic coating of biochar surfaces, we used fast field cycling NMR (FFC NMR) relaxometry quantifying the strength of biochar interactions with water30. We found that co-composting changed the distribution of relaxation times (Fig. 7 and Supplementary Fig. 12), i.e., time needed for protons to recover the longitudinal component after magnetization31. The different relaxation times indicate the strengths of interactions of water molecules with biochar pore surface as well as with pore water-dissolved or suspended compounds30, 32. Lower relaxation times in BCcomp suggest the presence of non-homogeneously distributed H-bond donor/acceptor groups. Thus, water is better anchored to the surfaces of BCcomp and thus less mobile, which can explain the retention of water-dissolved nutrients, such as nitrate. Liquid chromatography organic carbon detection (LC-OCD, Supplementary Tables 5–7, Supplementary Fig. 17 and Supplementary Discussion) of aqueous biochar extracts revealed a high content of humic-substance-like organic molecules, that might act as surfactants that facilitate this process. In addition, the organic coating can shrink pore sizes thereby reducing water mobility31. This is supported by gas adsorption measurements that showed that co-composting led to ~18% reduction in specific surface area (SSA) according to CO2 adsorption, especially in the pore size range of 0.65–0.85 nm, and ~64% SSA reduction to N2 adsorption, especially in the pore size range of 1.25–1.45 nm (Fig. 8, Supplementary Fig. 13 and Supplementary Discussion). Thus, among micropores, the larger, more accessible pores were preferentially clogged. Pores > 3 nm were not affected; however, pore clogging might be underestimated due to new mesopores of the organic coating increasing total porosity. In essence, CO2 gas adsorption reveals that the reduction of SSA by composting is less severe than reported previously33.
Collectively, our data showed that co-composting results in the formation of a heterogeneous, meso-porous and hydrophilic organic coating on biochar surfaces including inner pore surfaces. The coating was identified as a composite of the original compost organic matter and biochar nano-particles and it is enriched in N (especially NO3 −), K, Ca, Si, Fe and Al. It has a higher N/C ratio than the biochar matrix, a higher redox activity, and adds another porous component to the porous biochar. However, bulk carbon speciation of the biochar were not altered by co-composting. This suggests that co-composting of biochar does not affect its long-term stability in soil, however, this needs further evidence from incubation studies.
Our data provide, for the first time, mechanistic evidence on a molecular scale as to why the combination of biochar and organic amendments yields optimal agronomic benefits by biochar amendment. The enhanced interaction of co-composted biochar with water (hydrophilicity of organic coating decreases biochar’s hydrophobicity) is most likely responsible for its improved nutrient retention and therefore its superior agronomic performance16. Co-composting of biochar with nutrient-rich feedstock or other ways of treating nutrient-rich waste streams with biochar (e.g., liquid manure) is therefore key to increase biochars’ agronomic value.
Organic coating on soil-aged biochars
We additionally found that the organic coating is not restricted to the biochar example presented in this study. STEM also revealed an organic coating in another co-composted wood biochar (Supplementary Fig. 14) and in a soil-aged biochar (BCsoil, Supplementary Fig. 15). Basic biochar properties of BCsoil were similar to those of BCprist and BCcomp (similar feedstock, same process and pyrolysis conditions), but it was produced in 2012 and amended to a field experiment after soaking in a fertilizer solution. The organic coating on BCsoil has slightly different properties (lower electron accepting capacity, no evidence for incorporation of biochar nano-particles, different interaction with water, Supplementary Fig. 16) compared to BCcomp. Nevertheless, the evidence of organic coatings on both the composted and the soil-aged biochar strongly suggests that the organic coating of natural and anthropogenic (biochar) pyrogenic carbon is likely a ubiquitous phenomenon and corresponds to the finding that biochar stabilizes rhizodeposits34. This could explain the previously reported nitrate-retention capacity of biochar particles aged for 2.5 years in a field experiment35. Hence it is reasonable to assume that similar coatings may also have formed both on anthropogenic pyrogenic carbon in Amazonian and African Dark Earths soils and as well on natural pyrogenic carbon in soils, which was recently shown to account for on average 13.7% of the global soil organic carbon pool36.
Our study revealed that the formation of an organic coating on biochar, that was observed on all biochar particles investigated in this study, is the dominant molecular mechanism of biochar alteration by co-composting and soil ageing. This mechanism replaces the paradigm of surface oxidation of native biochar carbon as the dominant process of ageing. It might partially explain biochar’s longevity in soil4, as the organic coating might protect aromatic biochar surfaces to some extent from further (oxidative) degradation. Surface oxidation might play a certain role, as biochar particles are not completely covered by the organic coating (Fig. 2c, d). Moreover, functionalization of biochar surfaces by oxidation might facilitate the formation of the organic coating, as oxidized carbon moieties facilitate the interaction of biochar with organic molecules by hydrogen bonds18. However, our study clearly shows that increased abundance of oxidized carbon moieties like carboxylic groups or increased O/C ratios of biochar should not be simply assigned to surface oxidation, when the data is obtained from bulk analysis.
Future research needs look at the mechanisms of the formation of the organic coating. Although we presented evidence through LC-OCD that the organic coating consists of humic-like substances, microbial activity could play an important role in the formation of the organic coating. It needs to be clarified if the increase in EEC is the result a chemical alteration of organic matter or the result of preferential sorption of organic matter with a high EEC.
We conclude that the combination of biochar with non-pyrogenic organic matter (e.g., manure) is the key strategy to develop carbon-fertilizer carriers that are effective at low application rates21, 22. Annual application of such biochar-based fertilizers could sequester carbon and mitigate global warming5—a global mitigation strategy that could be implemented due to its economic value for farmers, without the necessity for further subsidies.
Biochar was produced from mixed woody waste materials via slow pyrolysis (700 °C) by Swiss Biochar (Belmont-sur-Lausanne, VD, Switzerland) with a Pyreg reactor37 and was characterized by Eurofins Umwelt Ost GmbH, Halsbrücke-Tuttendorf, Germany, as requested by the European Biochar Certificate1. Results are displayed in Supplementary Tables 1–3. This biochar was part of the COST Action-TD1107 biochar ring trial38 and both pristine/non-co-composted and co-composted aliquots from the same composting experiment were subject to previous studies39.
Biochar was co-composted at the Ithaka Institute at St. Léonard, VS, Switzerland, from August to October 2014. Biochar was mixed into compost feedstock composed of cow, horse and poultry manure and green waste at a rate of 4.3% (dry matter w/w). Compost was managed aerobically as described by Kammann et al.24 resulting in temperatures above 60 °C for more than 2 weeks. Compost feedstock was composted without biochar amendment as a control. After frost-protected storage during winter, biochar was picked manually from the mature compost in spring 2015. For biochar picking, 50 kg of biochar-amended compost were stored for analysis in a plastic bag. For each analytical procedure (extraction, characterization), a subsample of compost was collected as a composite sample from this bag. 10–30 char particles were separated from this individual subsample and then prepared for analysis. The actual number of biochar particles finally involved in analysis varied strongly between the different techniques. E.g. only 3 particles of each treatment could by analyzed by STEM and 2 for STXM, while extraction or powder-based analysis (gas adsorption) where based on at least 20 particles.
The same type of biochar was already purchased from Swiss Biochar in 2012 (separate analysis in Supplementary Tables 1–3). It was soaked in a diluted commercial fertilizer solution overnight (1:1 w/v, 1.25 g N kg−1 biochar) and incorporated at a rate of 60 Mg ha−1 into the upper 15 cm of a Terric Anthrosol (top- and subsoil of a Cambisol mixed by construction activities) at the Tuebingen-Sand field site (lat. 48.5342, long. 9.0711). The plot was cropped with Emmer wheat (Triticum dicoccon) in 2012 and winter vetch (Vicia villosa) in 2013 and green fallow thereafter. Biochar was manually picked from soil samples obtained from the upper 15 cm of three sampling sites in spring 2015.
Serial extraction of nitrate
Nitrate was repeatedly extracted from both pristine and co-composted biochar 1:10 (w/v) with 2 M KCl in 50 ml Falcon tubes (n = 3) on a roller shaker (ROLLER 10 digital, IKA, Staufen, Germany) at 50 r.p.m. at room temperature (22 ± 3 °C). After each extraction step, the extractant was decanted through a 0.5 mm sieve. The volume of the decanted extractant was measured to correct the data for the residual extractant (2 M KCl) that cannot be removed by decanting (residual = water content of biochar + added extractant—decanted extractant) which carries a small quantity of already extracted nitrate from one to the subsequent extraction. Fresh 2 M KCl was added to the biochar at the same volume. Each sample was extracted six times: three times for 1 h, for 18 h, for 48 h and for 96 h, respectively, resulting in a total extraction time of 167 ± 1 h. Nitrate was quantified using a continuous flow analyzer (SEAL Analytical, Germany) after reduction of the nitrate to nitrite with hydrazine, which was prepared according to SEAL’s advice for soil extracts. Nitrite was quantified by UV–vis absorption at 550 nm after reaction with N-1-naphtyl-ethylendiamin. The SEAL system is equipped with a dialysis membrane that removes any extraneous microparticles to prevent side reactions or additional absorbance. Standards were prepared in 2 M KCl to provide the same matrix.
13C solid-state nuclear magnetic resonance spectroscopy
Solid-state NMR spectra were collected using a Bruker (Billerica, USA) Avance III 600 MHz spectrometer equipped with a 4.0 mm magic-angle spinning Efree triple resonance HCN probe. 22–29 mg of each sample were packed into 50 µl 4.0 mm zirconia rotors. 1D-13C-spectra were acquired using standard Bruker cross-polarization (CP) pulse sequence at 10 or 12 kHz sample rotation frequency and at 27.0 °C VT inlet gas temperature. 24,576 scans were signal averaged for each spectrum with 3 s recycle delay.13C polarization was achieved using a ramped-amplitude1H-13C CP pulse for 2.0 ms, and the spectra were acquired for 15 ms under 81 kHz two-phase-modulated (TPPM)1H decoupling.13C chemical shifts were referenced externally to 2,2-dimethyl-2-silapentane-5-sulfonate sodium salt using the adamantane methylene peak at 40.48 ppm40. All data were processed with applying a 30 Hz exponential line broadening using Bruker Topspin 3.5.
N2 and CO2 adsorption were combined to characterize the SSA and pore volume (PV) of the biochar samples. To this end, the adsorption and desorption isotherms for both gases were measured at 77 K and 273 K, respectively. Before the measurements, the char samples were pretreated to clean the char surface from other adsorbed species (degassing) by heating them in vacuum at 120 °C during 6 h. The samples were also milled to reduce the influence of transport limitations on the measurements, especially in the case of N2 adsorption, due to the low temperatures. The N2 isotherms were determined measuring the amount of N2 adsorbed/desorbed as function of the N2 relative pressure P/P0 in the measurement station, where P is the pressure of N2 in the measurement station and P0 is the N2 saturation pressure at the measurement temperature (~77 K). The relative pressure P/P0 ranged from ~0.005 to ~0.995. In the case of CO2 the relative pressure ranged from ~0.00005 to ~0.028. For both degassing and adsorption/desorption measurements the gas sorption system Nova 2000 provided by Quantachrome Instruments (Boynton Beach, FL, USA) was used. Several methods were applied to the isotherms in order to derive pore surfaces areas and volumes, which are included in the NovaWin software (Quantachrome Instruments). In the case of N2 adsorption, the Brunauer, Emmett and Teller (BET)41 method was used to determine the total internal SSA of the samples. The DFT (density functional theory)42 method was applied to the adsorption isotherm to characterize the pore size distribution, in particular, the QSDFT (quenched solid-state functional theory) method, considering slit/cylindrical pores. With this method, micropores and mesopores up to ~34 nm in pore width could be measured. The Barrett, Joyner and Halenda (BJH)43 method was applied to characterize mesopores bigger than ~3 nm and macropores up to the detectable limit of N2 adsorption. The total pore volume was determined from the volume of N2 adsorbed at a relative pressure (P/P0) ≈1, assuming that at this point the pores are filled with liquid N2. For CO2 adsorption, the nonlinear DFT (NLDFT) was applied to determine the SSA and volume due to micropores.
X-ray photoelectron spectroscopy
XPS uses X-rays to excite atoms of a sample and analyzes the energy of the emitted photoelectrons, which provides information on both elemental composition and chemical bonds of the outermost 10 nm44. XPS was performed on an ESCALAB250Xi (Thermo Scientific, UK) using monochromated Al K α (1486.68 eV, 150 W) at a spot size of 500 µm under high-vacuum conditions (<2×10−9 mbar) and a photoelectron takeoff angle of 90° was used. It was calibrated with Au (Au 4f7 = 83.96 eV), Ag (Ag 3d5 = 368.21 eV) and Cu (Cu 2p3 = 932.62 eV). Pass energy was 100 eV for survey scans and 20 eV for region scans. Biochar particles were gently washed with DI water three times, dried at 40 °C and were measured both as a particle and as a powder after grinding in an agate mortar.
Scanning electron microscopy
In SEM, a focused beam of accelerated electrons scans over the samples and creates a multitude of characteristic secondary emissions. We used secondary electrons, which provide predominantly topographic information of the sample, and EDS. The energy of the X-rays is characteristic for the atom that was excited by a primary electron (beam electron) and thus provides information about the elemental content of the outermost hundreds of nm to ~2 µm of the sample, depending on the composition of the sample and the energy of the incident electron beam45. SEM micrographs and X-ray spectra were obtained on a Zeiss Sigma SEM with Bruker EDS at a working distance of 8–9 mm and an acceleration voltage of 10–15 kV. Individual biochar particles were mounted on SEM stubs with conductive carbon paint. Sputter coating was not necessary.
Scanning transmission X-ray microscopy
Ultra-thin-sections for STXM were prepared by cutting pieces of biochar (no pretreatment, no drying) under cryo-conditions in an ultramicrotome Leica UCT, gluing the sample with a droplet of 2.3 M saccharose and catching the ultra-thin-sections with saccharose, too. They were placed on formvar-coated 200 mesh copper grids. Grids were carefully rinsed with water to remove the saccharose and mounted on a STXM sample plate. Despite the rinsing, saccharose was still present on all samples. Therefore, a reference spectrum of pure saccharose was used to quantitatively map saccharose by spectral decomposition in the samples. Ultra-thin-sections were obtained from both center and the edge of pristine biochar particles as well as the edge of co-composted biochar particles. Measurements were conducted at the Canadian Light Source beamline 10ID-1.
Analytical scanning transmission electron microscopy
Pieces of biochar were covered in gold all-around in the Leica EM ACE 600 (Leica Microsystems, Vienna, Austria; 45 mA, 8,0 × 10−3 mbar, working distance 50 mm) using a rotating device to enable 3D coating. This resulted in a minimum of 25-nm-thick gold layer on the biochar. These nuggets were embedded in Spezifix40 (Struers, Willich, Germany) and after hardening carefully trimmed with a trim 90 blade (Diatome, Switzerland). The preparation of 50 nm slices was done at room temperature with the ultra-sonic-knife (Ultra Sonic, Diatome) for reducing compression and allowing best structure preservation in the ultramicrotome Leica EM UC6 (Leica Microsystems). The slices were transferred from the water with a perfect loop (Diatome) on a 200 mesh grid. STEM investigations were performed on a monochromated probe corrected FEI Titan G2 60–300 (STEM) microscope with an X-FEG Schottky field-emission electron source operated at 60 kV. The microscope is equipped with a FEI Super-X detector (Chemi-STEM technology), consisting of four separate silicon drift detectors46 (120 mm acquisition area) and a Dual EELS – Gatan Imaging Filter (GIF) Quantum47. The microscope was run in monochromated mode with a spatial resolution of 0.1 nm and an energy resolution at full-width at half-maximum of 0.17 eV. Two different detectors: high angular annular dark field (HAADF) and annular dark field (ADF), a beam current of approximate 120 pA and acquisition times ranging from 20 to 30 μs/pixel were used for micrographs acquisition. Analytical investigations involved electron energy loss (EELS) and X-ray (EDX) spectroscopy in STEM mode by line scans and spectrum imaging, which, however, were acquired with different acquisition times and pixel sizes depending on the investigated area. Energy loss near edge structure (ELNES) of carbon-, nitrogen- and oxygen- K ionization edges were analyzed considering the specific finger prints and energy shifts of different types of bonding which might be present in the sample, with graphite as a reference. Elemental quantification has been performed by using the k-factor method45, 48. Sample thickness in different areas was determined by EELS48. However, for the mean free path of the sample with the major constituent carbon a calculated value of 76.6 nm (Malis formula48) was used. The images and spectra were recorded by a Gatan Digiscan unit and Digital Micrograph software and were corrected for dark current and gain variations.
Desorption atmospheric pressure photoionization FT-ICR MS
A modified ThermoFisher LCQ atmospheric pressure photoionization (APPI) source (ThermoFisher Corp., Bremen, Germany) was used for all Fourier-transformed ion cyclotron resonance mass spectrometry (FT-ICR MS) experiments49. Pieces of pristine and co-composted biochar were held by tweezers ∼ 1 mm from the exit of the heated ceramic nebulization tube and ~10 mm from the FT-ICR MS inlet. Gas-phase neutrals were produced through a combination of thermal and chemical desorption50, and ionized by dopant-assisted APPI51. Nitrogen was used as nebulizer gas at 100 psi with toluene as dopant at a flow rate of 50 μl min−1. The temperature of the heated nebulizer gas/solvent plume ranged from 100 to 500 °C depending upon the sample. Mass spectra were acquired by a custom-built FT-ICR MS based on a passively shielded 9.4 T horizontal 200 mm bore diameter superconducting solenoid magnet (Oxford Corp., Oxford Mead, UK) operated at room temperature52. A modular ICR data station (Predator) facilitated instrument control, data acquisition, and data analysis53. Positive ions were accumulated in an external quadrupole for 50–500 ms, and passed through an rf-only quadrupole into an octopole equipped with tilted wire extraction electrodes for improved ion extraction and transmission54. Helium gas was introduced into the octopole to collisionally cool the ions before transfer through rf-only quadrupoles (total length 127 cm) into a seven-segment open cylindrical ICR cell with capacitively-coupled excitation electrodes based on the Tolmachev configuration55. Approximately 25–50 time-domain acquisitions were co-added, Hanning-apodized, and zero-filled once prior to fast Fourier transform and magnitude calculation. ICR frequencies were converted to m/z values by the quadrupolar electric trapping potential approximation56. Spectra were internally calibrated from abundant homologous alkylation series (compounds that differ in elemental composition by integer multiples of CH2). Mass spectral peaks with signal magnitude greater than six times the baseline root-mean-square (r.m.s.) noise level were assigned elemental composition values (C0–100H0–200N0–5O0–15S0–2) with PetroOrg software (Y.E. Corilo; Florida State University; all rights reserved), subject to the following constraints for chemical feasibility: mass error < 1 p.p.m.; the computed ring and double bond equivalent must be an integer value ≥ 0; neutral formulas containing an odd number of nitrogen atoms must have an odd nominal mass, and neutral formulas containing zero or an even number of nitrogen atoms must have an even nominal mass (nitrogen rule); 2 ≤ H ≤ (2 C + 2); 0.33 ≤ H/C ≤2.25; 0 ≤ O ≤ (C + 2); O/C <1.2; N/C <0.5; S/C <0.257.
DAPPI FT-ICR MS was performed both on original biochar samples and on washed biochar as described below. However, data on the washed samples was more comprehensive and better calibrated, i.e., more detected masses could be assigned to formulas. In the original co-composted biochar, 6,063 detected masses were not assigned formulas, while only 4,350 could not be assigned after washing.
Biochar washing for liquid extraction of the organic coating
Biochar particles were washed in four steps to remove any compost induced surface alterations and, at the same time, to obtain a suspension of the co-composting derived material that forms the coating of the biochar as identified with STEM. 15 mL DI water were added to 2.5 g moist biochar in a Falcon tube (step 1). After 5 min on a roller shaker at 50 rpm (Roller 10 digital, IKA, Staufen, Germany), water was decanted through a 0.5 mm mesh sieve and 15 ml of DI water were added to repeat this procedure (step 2). After decanting, 15 ml of 0.05 M NaOH solution were added as suggested by Tsechansky and Graber28 and Falcon tubes were placed on the shaker for 90 min (step 3). After decanting, 15 ml of DI water were added for 20 min to remove residual NaOH (step 4). Separate washing procedures were conducted for fresh and co-composted biochar. Afterwards, the biochar was dried at 40 °C for 72 h for DAPPI FT-ICR MS, SEM and STEM as described above. After washing, co-composted biochar was almost black again (Supplementary Fig. 7). Washed biochar was analyzed using SEM and STEM to verify the removal of the coating. SEM showed that the original biochar surface structure was widely exposed again, while few regions still showed surface alterations (Supplementary Fig. 8). In STEM we could not identify a coating after washing, but granular aggregations of Ca and O were present on the biochar surface (Supplementary Fig. 9).
Washing solution of step 3 (0.05 M NaOH) was analyzed by FTIR,1H NMR, excitation–emission matrix (EEM) fluorescence spectroscopy, ion chromatography, and for dissolved organic and inorganic carbon (DOC/DIC) and electron accepting and donating capacity (EAC/EDC). Before analysis, resulting washing solutions were filtered through a 0.45 µm syringe filter. For FTIR, washing solutions and original 0.05 M NaOH solution were freeze-dried. For1H NMR, washing procedure was repeated and 0.05 M NaOH was prepared with D2O instead of H2O. Major anions and cations were quantified by ion chromatography (IC, DX-120, Dionex, Sunnyvale, CA, USA). DOC + DIC was quantified on a Vario cube (Elementar, Hanau, Germany), DOC was quantified on the same device after acidifying the samples to pH 1 with HCl. DIC was calculated as [DOC + DIC]—[DOC].
EEM fluorescence spectra of washing solution were analyzed using a Fluoromax4 (Horiba, Jobin-Yvon) spectrofluorometer. EEM fluorescence spectra were recorded over a range of excitation wavelength (300–500 nm) and emission wavelength (400–600 nm) relevant for natural organic matter58.
Electron accepting and donating capacity
The redox properties, i.e., electron accepting and donating capacities (EAC/EDC) of biochar washing solutions were determined by mediated electrochemical reduction (MER) and oxidation (MEO) following established procedures6, 59. In brief, the electrochemical system consists of a glassy carbon cell (Sigradur G, HTW, Germany) as working electrode, a Ag/AgCl as reference electrode (Bioanalytical systems Inc., USA) and a platinum wire (0.5 mm, 99.9 %, Sigma-Aldrich Co., USA) attached to a platinum gauze (52 mesh, 99.9 %, Sigma-Aldrich Co., USA) as auxiliary electrode. The applied potential was measured against Ag/AgCl electrode but is reported against standard hydrogen electrode (EH = −0.49 V in MER and EH = + 0.61 V in MEO). Electron transfer mediators were used during the measurements to ensure a fast electron transfer between the electrodes and the analyte59; diquat-dibromide monohydrate (DQ, Sigma-Aldrich Co., USA) was used for MER and 2,2′-azino-bis(3-ethylbenzothiazoline-6-sulfonic acid) diammonium salt (ABTS, Sigma-Aldrich Co., USA) for MEO. EAC and EDC are calculated from the measured reductive and oxidative currents considering normalization to carbon content (µmol e-/mmol C)6. The total EEC is the sum of the individual accepting and donating capacities (EEC = EAC + EDC). As an additional reference, dissolved organic matter was extracted from non-biochar-amended control compost in analogy to the biochar washing procedure (0.05 M NaOH, 1.5 h, same shaker).
Fourier-transformed infrared spectroscopy
Fourier-transformed infrared (FTIR) Spectroscopy provides information on bonding modes in organic molecules by absorption of infrared radiation, which depends the vibrational response of the functional groups60. FTIR absorbance spectra of KBr pellets prepared with 0.2% biochar, 0.4% freeze-dried washing solutions or 0.4% freeze-dried control compost were measured with a Vertex 80 v (Bruker) with 128 scans. A KBr pellet without sample was used for background measurements.
1H solution nuclear magnetic resonance spectroscopy
2 ml of the pristine and the co-composted biochar washing solutions were lyophilized (freeze-dried) overnight. The dry samples were rehydrated up to 500 µl using 100% D2O. NMR spectra were collected using a Bruker Avance III 600 MHz spectrometer equipped with a Bruker 5 mm SmartProbeTM.1H 1D spectra were acquired for 2 s with a 20 s recycle delay and 1024 scans using standard Bruker pulse sequence with water suppression. All spectra were processed with applying a 0.30 Hz exponential line broadening using Bruker Topspin 3.5.
Fast field cycling nuclear magnetic resonance relaxometry
1 g of each biochar sample was suspended in 3 g of MilliQ grade water (resistivity of 18.2 MΩ cm at 298 K). Milli-Q water was produced by a Milli-Q Advantage A10 Ultrapure Water Purification System (Millipore Corporation, Massachusetts, USA). The suspensions were allowed to sediment overnight prior to the relaxometry investigations. The samples were put in the probe of a Stelar SpinMaster FFC-2000 fast field cycling relaxometer (Stelar s.r.l., Mede, PV−Italy) and analyzed at 25 °C. The basic theory about FFC NMR relaxometry and the sequence applied for the experiments reported in this study have been already summarized by Conte and Alonzo31. In brief, non-polarized (NP) and polarized (PP) sequences were applied. In the NP sequence, a relaxation field (B RLX) was changed between proton Larmor frequency (ω L) values ranging in the interval 0.01–30 MHz. Each B RLX was applied for a period τ arrayed with 32 logarithmic spaced time sets, each of them adjusted at every relaxation field in order to optimize the sampling of the decay/recovery curves. At the end of each B RLX field a1H 90° pulse was applied into an acquisition magnetic field (B ACQ) held for a fixed time at the ω L value of 7.2 MHz. The 1H 90° pulse was needed to make magnetization observable and the free induction decay acquirable. A time domain of 100 µs sampled with 1000 points was applied. Field-switching time was 3 ms, while spectrometer dead time was 15 µs. For all of the experiments a recycle delay of 20 s was used. In the PP sequence, a polarization field (B POL) set at the ω L of 9 MHz was applied prior to each B RLX field. The period of time during which B POL was applied (referred to as polarization time or T POL) corresponded to five times the T 1 estimated at this frequency.
The crossover field between NP and PP sequences was approximately retrieved when the relaxation field intensity was half of that of the polarization field31.
FFC NMR relaxometry data elaboration
The longitudinal relaxation time (T 1) values of the observed nuclei were obtained for each B RLX by changing the τ values as reported above. The relationship between signal intensity and τ is modeled by Eq. 1:
Here, I(τ) is the 1H signal intensity at each fixed B RLX, I0 is the 1H signal intensity at the thermal equilibrium, T 1 is the average proton spin-lattice relaxation time and k is a heterogeneity parameter related to the stretching of the decay process. This function, which accounts for the large sample heterogeneity resulting in a multi-exponential behavior of the decay/recovery curves31, can be considered as a superposition of exponential contributions, thereby describing the likely physical picture of some distribution in T 1. Eq. 1 has the advantage that it is able to handle a wide range of behaviors within a single model. For this reason, assumptions about the number of exponentials to be used in modeling nuclear magnetic dispersion (NMRD) data are not necessary. The NMRD profiles resulting from the elaboration of the decay/recovery curves are reported in Supplementary Fig. 13. The data acquired at the relaxation field of 0.01 MHz were transformed by applying the Uniform PENalty regularization (UPEN) algorithm31 which allowed the achievement of the distribution of the longitudinal relaxation times (also referred to as relaxograms).
Liquid chromatography organic carbon detection
1 g of pristine, co-composted and soil-aged biochar was added to 10 ml of distilled water at 50 °C for 24 h and regularly stirred, and then centrifuged and filtered (10,170 g, 5 min, 0.45 µm) to separate the solid and liquid phases. The supernatant solutions were analyzed by Liquid Chromatography – Organic Carbon Detection LC-OCD model 8 (DOC Labor, Germany). Details of the measurement procedure have been described in full by Huber et al61. In this study, a Toyopearl TSK HW50S LC column was used with a phosphate buffered mobile phase of pH 6.4 at a flow rate of 1.1 ml min-1. Injection volumes were 1,000 µl. The supernatant solutions are also analyzed to determine total organic nitrogen and carbon and total inorganic carbon using a thermocatalytic high-temperature oxidation process (Multi N/C 2100, Analytic Jena, Germany).
The chromatographic eluent subdivides into six sub-fractions, biopolymers, humics, building blocks, low molecular-weight neutrals and hydrophobic organic carbon (Supplementary Table 5), as suggested by Huber et al.61
The data sets generated during and/or analyzed during the current study are available from the corresponding author on reasonable request.
EBC. European Biochar Foundation - Epuropean Biochar Certificate - Guidelines for a Sustainable Production of Biochar. European Biochar Foundation (EBC) Version 6.1 of June 19, 2015. 1–17 (2012).
Hagemann, N., Harter, J. & Behrens, S. Elucidating the impacts of biochar applications on nitrogen cycling microbial communities. Biochar Appl. 1, 163–198 (2016).
Gul, S., Whalen, J. K., Thomas, B. W., Sachdeva, V. & Deng, H. Y. Physico-chemical properties and microbial responses in biochar-amended soils: mechanisms and future directions. Agric. Ecosyst. Environ. 206, 46–59 (2015).
Kuzyakov, Y., Bogomolova, I. & Glaser, B. Biochar stability in soil: decomposition during eight years and transformation as assessed by compound-specific 14C analysis. Soil Biol. Biochem. 70, 229–236 (2014).
Woolf, D., Lehmann, J. & Lee, D. R. Optimal bioenergy power generation for climate change mitigation with or without carbon sequestration. Nat. Commun. 7, 13160 (2016).
Kluepfel, L., Keiluweit, M., Kleber, M. & Sander, M. Redox properties of plant biomass-derived black carbon (biochar). Environ. Sci. Technol. 48, 5601–5611 (2014).
Kappler, A. et al. Biochar as an electron shuttle between bacteria and Fe(III) minerals. Environ. Sci. Technol. Lett. 1, 339–344 (2014).
Van Zwieten, L. et al. Effects of biochar from slow pyrolysis of papermill waste on agronomic performance and soil fertility. Plant Soil 327, 235–246 (2010).
Baiamonte, G. et al. Structure alteration of a sandy-clay soil by biochar amendments. J. Soils Sediments 15, 816–824 (2014).
Ajayi, A. E., Holthusen, D. & Horn, R. Changes in microstructural behaviour and hydraulic functions of biochar amended soils. Soil Tillage Res. 155, 166–175 (2016).
Kammann, C. I., Linsel, S., Gößling, J. & Koyro, H.-W. Influence of biochar on drought tolerance of Chenopodium quinoa Willd and on soil–plant relations. Plant Soil 345, 195–210 (2011).
Cornelissen, G. et al. Biochar effect on maize yield and soil characteristics in five conservation farming sites in Zambia. Agronomy 3, 256–274 (2013).
Jeffery, S., Abalos, D., Spokas, K. & Verheijen, F. G. A. in: Biochar for Environmental Management: Science, Technology and Implementation 2nd edn (eds Lehmann, J. & Joseph, S. D.) Ch. 12 (Taylor and Francis, 2015).
Schulz, H., Dunst, G. & Glaser, B. Positive effects of composted biochar on plant growth and soil fertility. Agron. Sustain. Dev. 33, 817–827 (2013).
Glaser, B. & Birk, J. J. State of the scientific knowledge on properties and genesis of anthropogenic dark earths in Central Amazonia (terra preta de Índio). Geochim. Cosmochim. Acta. 82, 39–51 (2012).
Kammann C. I. et al. Plant growth improvement mediated by nitrate capture in co-composted biochar. Sci. Rep. 5, 11080 (2015).
Wiedner, K. et al. Acceleration of biochar surface oxidation during composting? J. Agric. Food Chem. 63, 3830–3837 (2015).
Conte, P. & Laudicina, V. A. Mechanisms of organic coating on the surface of a poplar biochar. Curr. Org. Chem. 21, 1–7 (2017).
Solomon, D. et al. Indigenous African soil enrichment as a climate-smart sustainable agriculture alternative. Front. Ecol. Environ. 14, 71–76 (2016).
Glaser, B., Haumaier, L., Guggenberger, G. & Zech, W. The’Terra Preta’phenomenon: a model for sustainable agriculture in the humid tropics. Naturwissenschaften 88, 37–41 (2001).
Qian, L. et al. Biochar compound fertilizer as an option to reach high productivity but low carbon intensity in rice agriculture of China. Carbon Manag. 5, 145–154 (2014).
Schmidt, H. P. et al. Fourfold increase in pumpkin yield in response to low-dosage root zone application of urine-enhanced biochar to a fertile tropical soil. Agric. Basel 5, 723–741 (2015).
Mukherjee, A., Zimmerman, A., Hamdan, R. & Cooper, W. Physicochemical changes in pyrogenic organic matter (biochar) after 15 months of field aging. Solid Earth 5, 693 (2014).
Kammann, C. I., Glaser, B., Schmidt, H.-P. in: Biochar in European Soils and Agriculture: Science and Practice (eds Shackley, S., Ruysschaert, G., Zwart, K. & Glaser, B.) (Routledge, 2016).
Jorio, A. et al. Microscopy and spectroscopy analysis of carbon nanostructures in highly fertile Amazonian anthrosoils. Soil Tillage Res. 122, 61–66 (2012).
Joseph, S. et al. Shifting paradigms: development of high-efficiency biochar fertilizers based on nano-structures and soluble components. Carbon Manag. 4, 323–343 (2013).
Joseph, S. et al. The electrochemical properties of biochars and how they affect soil redox properties and processes. Agronomy 5, 322–340 (2015).
Tsechansky, L. & Graber, E. R. Methodological limitations to determining acidic groups at biochar surfaces via the Boehm titration. Carbon 66, 730–733 (2014).
Spokas, K. A. et al. Physical disintegration of biochar: an overlooked process. Environ. Sci. Technol. Lett. 1, 326–332 (2014).
Conte, P. et al. Nature of water-biochar interface interactions. GCB Bioenergy 5, 116–121 (2013).
Conte, P. & Alonzo, G. Environmental NMR: fast-field-cycling relaxometry. eMagRes 2, 389–398 (2013).
Bubici, S., Korb, J.-P., Kučerik, J. & Conte, P. Evaluation of the surface affinity of water in three biochars using fast field cycling NMR relaxometry. Magn. Reson. Chem. 54, 365–370 (2016).
Prost, K. et al. Biochar affected by composting with farmyard manure. J. Environ. Qual. 42, 164–172 (2013).
Weng, Z. H. et al. Biochar built soil carbon over a decade by stabilizing rhizodeposits. Nat. Clim. Change 7, 371–376 (2017).
Haider, G., Steffens, D., Muller, C. & Kammann, C. I. Standard extraction methods may underestimate nitrate stocks captured by field-aged biochar. J. Environ. Qual. 45, 1196–1204 (2016).
Reisser, M., Purves, R. S., Schmidt, M. W. I. & Abiven, S. Pyrogenic carbon in soils: a literature-based inventory and a global estimation of its content in soil organic carbon and stocks. Front. Earth Sci. 4, (2016).
Sehn, W., Gerber, H., Siekmann, K. & Scherer, J. Thermally mineralized: pyreg - a process for the decentralized sewage sludge treatment. BWK - Das Energie-Fachmagazin 62, 55–58 (2010).
Bachmann, H. J. et al. Toward the standardization of biochar analysis: the cost action TD1107 interlaboratory comparison. J. Agric. Food Chem. 64, 513–527 (2016).
Morcombe, C. R. & Zilm, K. W. Chemical shift referencing in MAS Solid State NMR. J. Magn. Reson. 162, 479–486 (2003).
Brunauer, S., Emmett, P. H. & Teller, E. Adsorption of gases in multimolecular layers. J. Am. Chem. Soc. 60, 309–319 (1938).
Seaton, N. A., Walton, J. P. R. B. & quirke, N. A new analysis method for the determination of the pore size distribution of porous carbons from nitrogen adsorption measurements. Carbon 27, 853–861 (1989).
Barrett, E. P., Joyner, L. G. & Halenda, P. P. The determination of pore volume and area distributions in porous substances. I. Computations from nitrogen isotherms. J. Am. Chem. Soc. 73, 373–380 (1951).
Zubritsky, E. Product review: XPS up close. Anal. Chem. 73, 279 A–283 A (2001).
Goldstein, J. I., Williams, D. B. & Cliff, G. in: Principles of Analytical Electron Microscopy (eds Joy, D. C., Romig, A. D. & Goldstein, J. I.). (Plenum Press, 1986).
Schlossmacher, P., Klenov, D. O., Freitag, B. & von Harrach, H. S. Enhanced detection sensitivity with a new windowless xeds system for aem based on silicon drift detector technology. Microscopy Today 18, 14–20 (2010).
Gubbens, A. et al. The GIF Quantum, a next generation post-column imaging energy filter. Ultramicroscopy 110, 962–970 (2010).
Egerton, R. F. Electron Energy-Loss Spectroscopy in the Electron Microscope (Springer, 2011).
Podgorski, D. C. et al. Characterization of pyrogenic black carbon by desorption atmospheric pressure photoionization Fourier transform ion cyclotron resonance mass spectrometry. Anal. Chem. 84, 1281–1287 (2012).
Haapala, M. et al. Desorption atmospheric pressure photoionization. Anal. Chem. 79, 7867–7872 (2007).
Robb, D. B., Covey, T. R. & Bruins, A. P. Atmospheric pressure photoionisation: an ionization method for liquid chromatography-mass spectrometry. Anal. Chem. 72, 3653–3659 (2000).
Kaiser, N. K., Quinn, J. P., Blakney, G. T., Hendrickson, C. L. & Marshall, A. G. A novel 9.4 Tesla FTICR mass spectrometer with improved sensitivity, mass resolution, and mass range. J. Am. Soc. Mass Spectrom. 22, 1343–1351 (2011).
Blakney, G. T., Hendrickson, C. L. & Marshall, A. G. Predator data station: a fast data acquisition system for advanced FT-ICR MS experiments. Int. J. Mass Spectrom. 306, 246–252 (2011).
Wilcox, B. E., Hendrickson, C. L. & Marshall, A. G. Improved ion extraction from a linear octopole ion trap: SIMION analysis and experimental demonstration. J. Am. Soc. Mass Spectrom. 13, 1304–1312 (2002).
Kaiser, N. K. et al. Electrically compensated Fourier transform ion cyclotron resonance cell for complex mixture mass analysis. Anal. Chem. 83, 6907–6910 (2011).
Shi, S. D. H., Drader, J. J., Freitas, M. A., Hendrickson, C. L. & Marshall, A. G. Comparison and interconversion of the two most common frequency-to-mass calibration functions for Fourier transform ion cyclotron resonance mass spectrometry2. Int. J. Mass Spectrom. 195–196, 591–598 (2000).
Stubbins, A. et al. Illuminated darkness: molecular signatures of Congo River dissolved organic matter and its photochemical alteration as revealed by ultrahigh precision mass spectrometry. Limnol. Oceanogr. 55, 1467–1477 (2010).
Chen, J., LeBoeuf, E. J., Dai, S. & Gu, B. Fluorescence spectroscopic studies of natural organic matter fractions. Chemosphere 50, 639–647 (2003).
Aeschbacher, M., Sander, M. & Schwarzenbach, R. P. Novel electrochemical approach to assess the redox properties of humic substances. Environ. Sci. Technol. 44, 87–93 (2010).
Kleber, M. et al. Mineral–organic associations: formation, properties, and relevance in soil environments. In Advances in Agron omy, Vol. 130 (ed. Sparks, D.) Ch. 1 (Elsevier, 2014).
Huber, S. A., Balz, A., Abert, M. & Pronk, W. Characterisation of aquatic humic and non-humic matter with size-exclusion chromatography–organic carbon detection – organic nitrogen detection (LC-OCD-OND). Water Res. 45, 879–885 (2011).
Keiluweit, M., Nico, P. S., Johnson, M. G. & Kleber, M. Dynamic molecular structure of plant biomass-derived black carbon (biochar). Environ. Sci. Technol. 44, 1247–1253 (2010).
Cody, G. D. et al. Molecular signature of chitin-protein complex in paleozoic arthropods. Geology 39, 255–258 (2011).
Hagemann, N et al. Nitrate capture and slow release in biochar amended compost and soil. PLOS ONE 12, e0171214 (2017).
We thank E. Struve, K. Mayer and P. Riede for laboratory support, G. Müller for support at Canadian Light Source, P. Ingio and F. Zeitvogel for support during STXM data evaluation, H. Chen for support at NHFML, W. Gerber for photographs, D. Mitchell for input on EELS and A. Flicker and M. Nowak for FTIR access and support. N.H. was financially supported by a BMBF PhD scholarship provided by the Rosa Luxemburg Foundation, Berlin, Germany. T.B. and R.B.Y. were supported by the Agriculture and Food Research Initiative Competitive (grant no. 2013-67019-21359) from the USDA National Institute of Food and Agriculture and a National Science Foundation SusChEM Award (grant no. EAR1451494). The co-composted biochar was obtained from a compost that was produced during a ‘Short Term Scientific Mission’ (STSM) granted to NH by the EU COST Action TD1107 ‘Biochar as option for sustainable resource management’. Access to the ASTEM Titan3 60–300 at TU Graz was enabled by European Union through the EC Grant ESTEEM2 (20141212‐Hagemann and 20150703-Hagemann). Research described in this work was performed at the Canadian Light Source, which is supported by the Natural Sciences and Engineering Research Council of Canada, the National Research Council Canada, the Canadian Institutes of Health Research, the Province of Saskatchewan, Western Economic Diversification Canada and the University of Saskatchewan. A portion of this work was performed at the National High Magnetic Field Laboratory, which is supported by the National Science Foundation Division of Materials Research through DMR 11-54790, the State of Florida and Florida State University. We thank E. Graber and K. Spokas for valuable discussions.
The authors declare no competing financial interests.
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hagemann, N., Joseph, S., Schmidt, HP. et al. Organic coating on biochar explains its nutrient retention and stimulation of soil fertility. Nat Commun 8, 1089 (2017). https://doi.org/10.1038/s41467-017-01123-0
This article is cited by
Water-dispersible carbon nanomaterials improve lettuce (Latuca sativa) growth and enhance soil biochemical quality at low to medium application rates
Plant and Soil (2023)
Biochar Addition Balanced Methane Emissions and Rice Growth by Enhancing the Quality of Paddy Soil
Journal of Soil Science and Plant Nutrition (2023)
Salt-affected marginal lands: a solution for biochar production
Bibliometric analysis of biochar research in 2021: a critical review for development, hotspots and trend directions
Effect of nano-biochar on mechanical, barrier and mulching properties of 3D printed thermoplastic polyurethane film
Polymer Bulletin (2023)
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.