Abstract
Previous studies have shown that a large solidstate entropy of reduction increases the thermodynamic efficiency of metal oxides, such as ceria, for twostep thermochemical water splitting cycles. In this context, the configurational entropy arising from oxygen offstoichiometry in the oxide, has been the focus of most previous work. Here we report a different source of entropy, the onsite electronic configurational entropy, arising from coupling between orbital and spin angular momenta in lanthanide f orbitals. We find that onsite electronic configurational entropy is sizable in all lanthanides, and reaches a maximum value of ≈4.7 k _{B} per oxygen vacancy for Ce^{4+}/Ce^{3+} reduction. This unique and large positive entropy source in ceria explains its excellent performance for hightemperature catalytic redox reactions such as water splitting. Our calculations also show that terbium dioxide has a high electronic entropy and thus could also be a potential candidate for solar thermochemical reactions.
Similar content being viewed by others
Introduction
Ceria (CeO_{2}) has been among the very first^{1} and most widely studied^{2} materials for catalytic and energy applications. It is used in threeway exhaust automotive catalysts^{2,3,4,5,6}, solidstate fuel cells^{7,8,9,10}, twostep thermochemical water splitting cycles (TWSC)^{11,12,13,14}, lowtemperature water–gas shift reactions^{15}, and several other industrial catalytic applications^{16,17,18,19,20}. To a large extent, the performance of ceria in these applications depends strongly on its oxygen storage capacity and facile Ce^{4+}/Ce^{3+} redox reaction.
Ceria is a highly promising redox active material for TWSC^{14}, in which a metal oxide is reduced at high temperature, T _{H}, and subsequently reoxidized by exposure to H_{2}O at a lower (but still elevated) temperature T _{L}:
δ _{L} and δ _{H} are, respectively, the lowtemperature (T _{L} typically around 800 °C) and hightemperature (T _{H} typically around 1600 °C) oxygen nonstoichiometries^{14, 21}. Meredig and Wolverton^{22} examined the thermodynamics of these twostep reaction cycles and showed that a key thermodynamic quantity for increased efficiency is a large solidstate entropy of reduction \(\left( {\Delta S_{{\rm{red}}}^{{\rm{solid}}}} \right)\). Stoichiometric oxides typically have \({\rm{\Delta }}S_{{\rm{red}}}^{{\rm{solid}}} < 0\), so an additional source of entropy in the reduced phase is required for a high performance in TWSC. Among all the studied stoichiometric oxide reactions in ref. ^{22} 2CeO_{2} → Ce_{2}O_{3} + \(\frac{1}{2}\)O_{2} is the only one that shows \({\rm{\Delta }}S_{{\rm{red}}}^{{\rm{solid}}} >0\).
The entropy of reduction of Eq. (1) in the TWSC process is conventionally defined as^{23}:
where ΔS _{conf} includes both electronic and ionic configurational entropy of ceria. The electronic part associated with electron or hole localization contributes to the total entropy in the same fashion as the ionic configurational entropy due to vacancies. Both configurational contributions can be determined accurately by Monte Carlo simulations based on a cluster expansion^{24}. ΔS _{vib} is the vibrational entropy of reduction and \(\Delta {S_{{{\rm{O}}_2}}}\) is the gas phase entropy. The latter does not depend on the choice of materials, and at temperatures higher than 1000 K, which is relevant for TWSC, is ~ 15 k _{B} per oxygen atom^{23, 25}—hereafter, all the reported entropic contributions are per one oxygen vacancy, unless stated otherwise. By excluding the gas phase entropy, we have the solidstate entropy of reduction \(\left( {{\rm{\Delta }}S_{{\rm{red}}}^{{\rm{solid}}}} \right)\), which is the material dependent contribution.
The first experimental studies on the entropy of reduction of CeO_{2} by Bevan et al.^{26} and successively Panlener et al.^{23} showed that this quantity has a logarithmic dependence on the nonstoichiometry, δ, of CeO_{2−δ }. They associated this behavior with the change in the configurational entropy (ΔS _{conf}) with varying degrees of nonstoichiometry, while vibrational entropy was estimated to be negligible. Grieshammer et al.^{27} calculated the ΔS _{vib} of defect formation in ceria at a fixed nonstoichiometry and found it to be ~ 2.5 k _{B}, which is not negligible, but smaller than other entropic contributions. Gopal et al.^{28} did comprehensive calculations using Monte Carlo simulations based on the DFTderived cluster expansion Hamiltonian. They calculated all configurational and vibrational entropic contributions (see Eq. (3)) for different values of δ at a temperature of 1480 K and found that the actual configurational entropy is much smaller than that of commonly assumed ideal solution model. For δ > 0.12 their calculated total entropy agrees with that of experiment, however, in the δ range of 0.01–0.12 they underestimate the experimental entropy, leading to a 4.5 k _{B} ^{28} gap between their calculations and the experimental measurement^{23}.
In the present paper, we demonstrate that particularly in the case of lanthanides, a different type of electronic entropy should be considered. This source of electronic entropy, which becomes important for elements with partially filled f shells arises when electrons can be distributed over a large number of multiplet states. This entropy results only from onsite configurational entropy in extremely localized f orbitals, which stems from the possible configurations associated with occupations of the same atomic orbitals, and is hereafter denoted \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\). Our results, show that the \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) contributes to the high performance of ceria in TWSC and fills the ≈4.7 k _{B} gap between previous theoretical and experimental entropy values. We calculate the entropy of reduction (M ^{n+}/M ^{(n−1)+}) for several other lanthanide cations (praseodymium, neodymium, europium, and terbium) that are stable in two valence states and for which reliable spectroscopic data are available (see ref. ^{29}). We calculate the crystal field (CF) parameters of Ce^{3+} in the host fluorite CeO_{2} structure, where each cerium atom experiences a cubic crystal field from eight oxygen atoms. The results show that the electronic entropy of reduction of Ce^{4+} is the highest among f elements, even surpassing the calculated configurational entropy^{28} at large offstoichiometry values, thereby explaining the unique entropic properties of the reduction of CeO_{2}.
Results
L − S coupling and crystalfield splitting
Electronic configurational entropy \(\left( {S_{{\rm{elec}}}^{{\rm{onsite}}}} \right)\) arises from thermal excitations among orbital microstates created by Russel–Saunders (L–S) coupling. In multielectron atoms, L–S coupling between orbital and spin angular momenta (L–S) results in the creation of microstates, which are further split by CF interactions. As the interaction of the very contracted forbitals of the lanthanide ions with the CF is small^{30}, it is reasonable to first treat the electronic energy levels of the lanthanide oxides by considering only free ion energies and then subsequently apply the crystal field. For forbitals of lanthanides, defining the electronic configuration by just number of valence electrons (4f ^{n}) is far less descriptive than the term symbol described by the L–S coupling scheme^{31}. In this scheme, coupling of orbital and spin angular momentum results in ^{2S+1} L _{ J } term symbols in which 2S + 1 is the spinmultiplicity, L is the total orbital quantum number and J is the total angular momentum quantum number, ranging from L + S to L − S by steps of one. Indeed, Hund’s rules imply that the term with the largest value of multiplicity (2S + 1) is the most stable one. If several terms have the same multiplicity, then the term with the largest L is the most stable one. If the f shell is less than halffilled then the state with the lowest J has the lowest energy. On the other hand, if the f shell is more than halffilled then the state with the highest J has the lowest energy. The degeneracy of each Jmultiplet is (2J + 1) and the total number of microstates (m) for a given term symbol ^{2S+1} L is (2S + 1) × (2L + 1).
When a free ion is placed in a crystal, the CF further splits each of the degenerate J states to several subsets and breaks the spherical symmetry of the fshell charge distribution, depending on the local symmetry of the ionic environment. Here, we used a fully abinitio method, opposing crystal potential (OCP)^{32}, to calculate the crystal field parameters of Ce^{3+} in the host fluorite CeO_{2} structure, where each cation is coordinated to eight oxygen atoms. This method is motivated by the above mentioned lowering of the spherical symmetry of the d/f charge distribution, e.g., to cubic symmetry in CeO_{2}, due to crystal field interactions. OCP iteratively computes and subtracts CF interactions in order to effectively cancel them and recover spherical d/f charge distribution upon convergence. An onsite potential \({\lambda _{mm'}}\) is introduced as a matrix of Lagrange multipliers in constrained DFT calculations, and crystal field parameters are then obtained as linear combinations of \({\lambda _{mm'}}\) (see ref. ^{32} for details). As previously discussed^{32}, the goal of the constrained DFT calculations was to extract CF parameters rather than to introduce band gap and selfinteraction corrections. Consequently the commonly adopted LDA + U approach was not necessary. As a benchmark, the CF parameters of PrO_{2} from constrained OCP calculations were in good agreement with our previous LDA + U calculations that directly compute the energy difference of different crystal field levels^{33}.
Figure 1 shows the f ^{1} (Ce^{3+}) energylevel splitting scheme in the presence of spinorbit coupling (SOC) and calculated CF. Without CF, the f ^{1} states split into ^{2} F _{5/2} and ^{2} F _{7/2} separated by approximately 0.28 eV^{29}. The CF interaction further splits the sixfold degenerate ^{2} F _{5/2} ground state into a fourfold degenerate Γ_{8} and twofold degenerate Γ_{7} subsets, separated by 0.12 eV. Crystal field—calculated by OCP method for Ce^{3+}—splits the eightfold degenerate ^{2} F _{7/2} state into states with energies 0.25, 0.32, 0.46 eV. These results are comparable with experimental and theoretical CF splittings of Ce^{3+} doped in CaF_{2} ^{34,35,36} and YAG (Y_{3}Al_{5}O_{12})^{34, 37} hosts.
Onsite electronic entropy
By having the energy E _{ i } and degeneracy (g _{ i }) of each microstate, \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) of a system with m different microstates can be calculated by
where the probability of thermal excitation (p _{ i }) to the state with energy E _{ i } is proportional to the Boltzmann factor by
and Z is the partition function defined by
Equations (4) and (6) indicate that \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) directly depends on two key factors; the probability (p) and the total number of microstates (m) that varies from 14 in f ^{1}/f ^{13} to 66 in f ^{5}/f ^{9} (see Table 1 for the number of degenerate microstates in other occupations). From Ce to Nd, both the total number of microstates and SOC increase. A stronger SOC implies a larger multiplet splitting between the levels which leads to microstates with higher energies. At low temperature, i.e., limited thermal excitations, those highenergy microstates are less probable to be occupied. However, in Ce^{3+} with a moderate SOC, at temperatures relevant for TWSC (T ≈ 1900 K), a large fraction of microstates are accessible due to the increased thermal excitation, as seen in Fig. 1. Therefore, \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) of Ce^{3+} approaches the ideal limit of k _{B} ln(m). As seen in Table 1, \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) weakly depends on the number of electrons and degenerate states. Once the f orbitals get occupied by a single electron—generating 14 microstates with ln (14) k _{B} (≈2.6 k _{B}) entropic contribution—the system gains a large entropy. For example \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) of f ^{1} (Ce^{3+}) is 2.34 k _{B} and f ^{4} (Nd^{2+}) is 3.52 k _{B}.
Myers et al.^{38} extracted the electronic entropy contribution of lanthanide ions (Ln^{3+}) in lanthanide trihalides from absolute entropy data. Our calculated electronic entropies per ion at ≈300 K in units of k _{B} compared with Myers et al.^{38} data (value inside parentheses) are the following: Ce^{3+}, 1.79 (1.77); Pr^{3+}, 2.19 (2.18), Nd^{3+}, 2.30 (2.27); Eu^{3+}, 1.13 (1.10); Tb^{3+}, 2.56 (2.54). The calculated \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) based on L–S coupling shows excellent agreement with previously reported data. Below, we will consider the effect of crystal field splitting on the calculation of \(S_{{\rm{elec}}}^{{\rm{onsite}}}\).
For TWSC applications, the absolute electronic entropy does not matter, only the entropy difference before (f ^{n}) and after (f ^{n+1}) reduction is relevant, \(\Delta S_{{\rm{elec}}}^{{\rm{onsite}}} = 2\left( {S_{{\rm{elec}}}^{{\rm{n}}  1}  S_{{\rm{elec}}}^{\rm{n}}} \right)\). The factor two is due to the fact that two Ce^{4+} ions are reduced per oxygen vacancy. As discussed in the previous paragraph and shown in Table 1, because of the large \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) gain upon occupation of an f orbital, in TWSC systems the electronic entropy of reduction reaches its maximum, when the entropy of the oxidized state is zero, \(S_{{\rm{elec}}}^{{n}} = 0\). As a result, the largest \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) is found in Ce^{4+} → Ce^{3+}, which undergoes an f ^{0} → f ^{1} redox reaction. Having the oxidized state f ^{0} (^{1} S) with zero onsite electronic entropy is a unique feature of ceria, resulting in a large \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) of 4.68 k _{B} per oxygen vacancy, which is a maximum for the reduction of any rareearth cation. We assert that this unique entropic characteristic of the Ce^{4+}/Ce^{3+} redox reaction helps facilitate the TWSC properties of CeO_{2}. The second largest value of \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) is found in terbium (Tb^{4+} → Tb^{3+}) with 2.30 k _{B} per oxygen vacancy at 1900 K (Fig. 2). There, the nonreduced Tb^{4+} has a halffilled shell with only eight spindegenerate (2S + 1) states but with only one orbital degeneracy (L = 0), while Tb^{3+}, has an orbital degeneracy of 7 (L = 3), providing extra entropy, see Table 1. This extra source of entropy could make Tb^{4+} based materials promising candidates for TWSC applications, as Tb, like Ce, is stable in two valence states (Tb^{4+}/Tb^{3+}). This prediction agrees with a recent thermodynamic study that also suggested^{39} TbO_{2} as a potential candidate for TWSC applications.
In contrast to TbO_{2}, reduced Eu^{2+} has a halffilled shell with eight spin and only one orbitaldegeneracy, resulting in a temperature independent entropy of 2 × ln(8)k _{B} = 4.16 k _{B} per oxygen vacancy. On the other hand nonreduced Eu^{3+} has a large number of total degeneracy of 49 (see Table 1). Since \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}} = 2\left( {S_{{\rm{elec}}}^{{\rm{E}}{{\rm{u}}^{2 + }}}  S_{{\rm{elec}}}^{{\rm{E}}{{\rm{u}}^{3 + }}}} \right)\), by increasing temperature \(S_{{\rm{elec}}}^{{\rm{E}}{{\rm{u}}^{3 + }}}\) rapidly increases which decreases \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) making it negative at high temperature.
To examine the effect of crystal field on the reduction entropy, we calculated CF parameters for Ce^{3+} in the CeO_{2} host lattice. We should note that a previous study^{40} using inelastic neutron scattering demonstrated that reducing nearest neighbor oxygen atoms have little effect on the overall energy level. This indicates that formation of vacancy next to Ce^{3+} can not dramatically change the CF splitting of a perfect cubic field. Using ab initio CF parameters, previous calculations^{41} of \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) for actinides showed an excellent agreement with the available experimental data. Here, we calculate electronic entropy of Ce^{3+}. As seen in Fig. 2, CF only affects the \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) at low temperatures while at temperatures higher than 1000 K the CF effect is small; therefore, one can just rely on Jmultiplet states resulting from L–S coupling. Table 1 shows that at such elevated temperatures, even pure \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) weakly depends on CF. For example, the effect of CF on \(S_{{\rm{elec}}}^{{\rm{onsite}}}\) of Pr^{4+} and Ce^{3+} is about < 3%. This percentage is in fact an upper limit, as the calculated CF is at DFT lattice parameters at zero Kelvin. The temperature dependent measurement of CF splitting by Walsh et al.^{42} showed that the CF splitting significantly decrease with temperature and lattice thermal expansion. Therefore, at 1900 K, which corresponds to typical temperature required for TWSC applications, CF field plays only a minor role.
Other entropy contributions
Finally, we compare \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) with the other sources of entropy. For simplicity we consider a fixed composition of δ = 0.03 roughly corresponding to one oxygen vacancy in a 96atom supercell. For this composition, we were able to find several reported experimental and theoretical data points (Table 2). At this composition the calculated ΔS _{vib} is ~ 2.5 k _{B} ^{27}. The ΔS _{conf } of CeO_{2−δ }, assuming ideal mixing entropy^{23, 28} (ΔS _{c} = −nk _{B} ln(δ)), where n depends on the defect structure and here n = 3, is ≈10.4 k _{B}. However, we note that a system with extensive ordering of oxygen vacancies^{43}, such as ceria, will have short range order and hence the actual configurational entropy is nonideal and smaller than the ideal solution model. For instance, the nonideal ΔS _{conf} + ΔS _{vib}, calculated by Monte Carlo simulation based on a cluster expansion Hamiltonian, is about 5.9 k _{B} ^{28}, less than half of the ideal ΔS _{conf}. Our calculations show that the neglected electronic entropy (ΔS _{elec}) is >4.7 k _{B}, which is comparable to these other widely considered sources of entropy and can explain the ≈5 k _{B} gap between the calculation and experiment. We note that as long as oxygen vacancy is compensated by two polarons Ce′ (i.e., Ce^{4+}) \(\left( {\left[ {{\rm{Ce}}\prime\!_{{\rm{Ce}}} } \right] = 2\left[ {V_{\rm{O}}^{..}} \right]} \right)\), \({\rm{\Delta }}S_{{\rm{elec}}}^{{\rm{onsite}}}\) is not a function of offstoichiometry (δ). Being independent of offstoichiometry implies that at large δ the contribution from the electronic entropy surpasses that of the configurational entropy (which decreases with δ) and becomes the major entropy contribution. Using the calculated ΔS _{conf} in ref. ^{28}, we estimate that this crossover occurs at (δ ≈ 0.05).
Our results show that the electronic contribution to the entropy of reduction explains the gap between the results of the currently most detailed theoretical calculations of ref. ^{28} and the experimental data of Panlener et al.^{23} for small deviations from stoichiometry corresponding to δ < 0.03. At larger deviations, adding a constant onsite electronic entropy to the vibrational and configurational entropies from ref. 28 would overestimate the experimental data. There could be several reasons for this apparent discrepancy. For instance, at higher δ values most of the polarons become bound to oxygen vacancies forming singly charged V\(_{\rm{O}}^{2  }\)–Ce^{3+} or neutral V\(_{\rm{O}}^{2  }\)–2Ce^{3+} complexes^{44}; the proximity of Ce^{3+} to an oxygen vacancy could slightly modify the electronic structure and hence reduce the electronic entropy associated with Ce^{3+}, but as already discussed the overall effect of oxygen vacancy on the energy levels^{40} and electronic entropy is expected to be small. Furthermore, the experimental measurements of Panlener et al.^{23} found that the enthalpy of reduction is composition dependent even at very small δ; however, this finding has been challenged due to the large experimental uncertainty^{23, 26}. As the entropy is obtained from TΔS = ΔH − ΔG, the entropy values of Panlener et al. may be contaminated by contributions from the composition dependent contribution to ΔH. Indeed, the results of ref. ^{28} suggest that the entropy stays approximately constant for δ in the 0.05 to 0.15 range, while the data of Panlener et al.^{23} show a pronounced decrease in this range.
Measurements of the Seebeck coefficient provide another means of estimating the electronic entropy contribution in the dilute limit where all polarons are unbound^{6, 45}. Unfortunately, the experimental data here are also contradictory. The data of Tuller and Nowick^{45} suggest that for small δ the spin degeneracy factor is one, which contradicts the Kramers theorem requiring that the ground state must be at least doubly degenerate. However, a later study by the same authors^{6} concluded that the agreement between the polaron model with spin degeneracy one and the experimental data for the Seebeck coefficient was poor, especially at low δ where impurities were thought to play an important role. On the theory side, the vibrational entropy of an isolated Ce^{3+} polaron has not been established accurately. Grieshammer et al.^{27} have calculated a very large value of about 7 k _{B} for the entropy of polaron formation at zero pressure, but the largest contribution to this value is due to a volume contribution from the CeO_{2} host, which was treated in an approximate fashion. Such a large positive entropy is inconsistent with the available data on the Seebeck coefficients in the dilute limit^{6, 45}. Hence, thermoelectric measurements on pure, wellequilibrated samples of CeO_{2} and more accurate calculations of the vibrational entropy associated with free polarons are highly desirable.
Discussion
We calculated electronic entropies of different lanthanides in the presence of SOC and CF. We calculated CF splittings for Ce^{3+} and Pr^{4+} and found that at temperatures above 1000 K, CF interactions affect the S _{elec} by >3%. The results show that, in ceria, the magnitude of the entropy of reduction due to the commonly neglected onsite electronic entropy (ΔS _{elec}) reaches a maximum of 4.7 k _{B} per oxygen vacancy, which is twice as large as the vibrational entropy contribution and can be larger than the configurational entropy. This surprisingly large entropy is the result of the very unique electronic structure of cerium in ceria, where redox reactions change its electronic state from f ^{0} to f ^{1}. These entropic properties, together with the excellent chemical stability and tolerance for large nonstoichiometry, put ceria in a unique position for twostep solar thermochemical CO_{2}/H_{2}O splitting cycles. In addition, we find that Tb (IV) based materials have the next highest electronic entropy, for Tb^{4+} → Tb^{3+} redox reactions. We therefore propose compounds containing Tb^{4+} should be experimentally investigated as promising candidates for TWSC applications.
Methods
Constrained DFT calculations, required for the calculation of crystal field parameters using OCP method, were performed in the VASP package^{46} using the Perdew–Becke–Ernzerhof^{47} functional, projector augmentedwave potentials^{48}, a 6 × 6 × 6 kpoint mesh an energy cutoff of 520 eV and a convergence criterion of 10^{−10} eV/atom for the electronic structure to ensure satisfactory convergence of CF parameters. One electron was added to the neutral CeO_{2} cell in order to model Ce^{3+}. Note that as previously discussed^{32}, the goal of the constrained DFT calculations was only to extract CF parameters rather than to introduce band gap and selfinteraction corrections.
Data availability
The data that support the findings of this study are available within the paper or from the corresponding author on request.
References
Goggs, A. B. An investigation on the ceria–thoria catalysts. J. Chem. Soc. 1928, 2667–2669 (1928).
Mogensen, M., Sammes, N. M. & Tompsett, G. A. Physical, chemical and electrochemical properties of pure and doped ceria. Solid State Ion. 129, 63–94 (2000).
Gandhi, H., Graham, G. W. & McCabe, R. W. Automotive exhaust catalysis. J. Catal. 216, 433–442 (2003).
Yao, H. & Yu Yao, Y. F. Ceria in automotive exhaust catalysts I. Oxygen storage. J. Catal. 86, 254–265 (1984).
Kašpar, J., Fornasiero, P. & Graziani, M. Use of CeO_{2}based oxides in the threeway catalysis. Catal. Today 50, 285–298 (1999).
Tuller, H. L. & Nowick, A. S. Defect structure and electrical properties of nonstoichiometric CeO[sub 2] single crystals. J. Electrochem. Soc. 126, 209 (1979).
Steele, B. C. H. & Heinzel, A. No title. Nature. 414, 345–352 (2001).
Steele, B. Appraisal of Ce_{1y }Gd_{ y }O_{2y/2} electrolytes for ITSOFC operation at 500C. Solid State Ionics 129, 95–110 (2000).
Sharma, S., Hilaire, S., Vohs, J., Gorte, R. & Jen, H.W. Evidence for oxidation of Ceria by CO_{2}. J. Catal. 190, 199–204 (2000).
Navrotsky, A. Thermodynamics of solid electrolytes and related oxide ceramics based on the fluorite structure. J. Mater. Chem. 20, 10577 (2010).
Otsuka, K., Hatano, M. & Morikawa, A. Hydrogen from water by reduced cerium oxide. J. Catal. 79, 493–496 (1983).
Abanades, S. & Flamant, G. Thermochemical hydrogen production from a twostep solardriven watersplitting cycle based on cerium oxides. Sol. Energy 80, 1611–1623 (2006).
Roeb, M. et al. Materialsrelated aspects of thermochemical water and carbon dioxide splitting: a review. Materials 5, 2015–2054 (2012).
Chueh, W. C. et al. Highflux solardriven thermochemical dissociation of CO_{2} and H_{2}O using nonstoichiometric Ceria. Science 330, 1797–1801 (2010).
Fu, Q., Weber, A. & FlytzaniStephanopoulos, M. Nanostructured AuCeO_{2} catalysts for lowtemperature watergas shift. Catal. Lett. 77, 87–95 (2001).
Schneider, J. J. et al. Templateassisted formation of microsized nanocrystalline CeO_{2} tubes and their catalytic performance in the carboxylation of methanol. Beilstein J. Nanotechnol. 2, 776–784 (2011).
Deluga, G. A., Salge, J. R., Schmidt, L. D. & Verykios, X. E. Renewable hydrogen from ethanol by autothermal reforming. Science 303, 993–997 (2004).
Park, S., Vohs, J. M. & Gorte, R. J. Direct oxidation of hydrocarbons in a solidoxide fuel cell Seungdoo. Nature 404, 265–267 (2000).
Inaba, H. & Tagawa, H. Ceriabased solid electrolytes. Solid State Ionics 83, 1–16 (1996).
Sun, C., Li, H. & Chen, L. Nanostructured ceriabased materials: synthesis, properties, and applications. Energy Environ. Sci. 5, 8475 (2012).
Chueh, W. C. & Haile, S. M. A thermochemical study of ceria: exploiting an old material for new modes of energy conversion and CO_{2} mitigation. Philos. Trans. R. Soc. A 368, 3269–3294 (2010).
Meredig, B. & Wolverton, C. Firstprinciples thermodynamic framework for the evaluation of thermochemical H_{2}O or CO_{2}splitting materials. Phys. Rev. B 80, 245119 (2009).
Panlener, R., Blumenthal, R. & Garnier, J. A thermodynamic study of nonstoichiometric cerium dioxide. J. Phys. Chem. Solids 36, 1213–1222 (1975).
Zhou, F., Maxisch, T. & Ceder, G. Configurational electronic entropy and the phase diagram of mixedvalence oxides: The Case of Li_{ x }FePO_{4}. Phys. Rev. Lett. 97, 155704 (2006).
Nakamura, T. Estimation of the standard entropy change on complete reduction of oxide M_{ m }O_{ n }. J. Solid State Chem. 36, 234–240 (1981).
Bevan, D. & Kordis, J. Mixed oxides of the type MO_{2} (fluorite)M_{2}O_{3}I oxygen dissociation pressures and phase relationships in the system CeO_{2}Ce_{2}O_{3} at high temperatures. J. Inorg. Nuclear Chem. 26, 1509–1523 (1964).
Grieshammer, S., Zacherle, T. & Martin, M. Entropies of defect formation in ceria from first principles. Phys. Chem. Chem. Phys. 15, 15935 (2013).
Gopal, C. B. & van de Walle, A. Ab initio thermodynamics of intrinsic oxygen vacancies in ceria. Phys. Rev. B 86, 134117 (2012).
Kramida, A., Yu, R., Reader, J. & NIST ASD Team. NIST Atomic Spectra Database (ver. 5.3), [Online]. Available: http://physics.nist.gov/asd (November 17, 2015) (National Institute of Standards and Technology, Gaithersburg, 2015).
Aspinall, H. Chemistry of the fBlock Elements. Advanced chemistry texts (Taylor & Francis, 2001).
Russell, H. N. & Saunders, F. A. New regularities in the spectra of the alkaline earths. Astrophys. J. 61, 38 (1925).
Zhou, F. & Åberg, D. Crystalfield calculations for transitionmetal ions by application of an opposing potential. Phys. Rev. B 93, 085123 (2016).
Zhou, F. & Ozolins, V. Obtaining correct orbital ground states in felectron systems using a nonspherical selfinteractioncorrected LDA + U method. Phys. Rev. B 80, 125127–125132 (2009).
Hu, L., Reid, M. F., Duan, C.K., Xia, S. & Yin, M. Extraction of crystalfield parameters for lanthanide ions from quantumchemical calculations. J. Phys. Condens. Matter. 23, 045501 (2011).
van Pieterson, L., Reid, M. F., Wegh, R. T., Soverna, S. & Meijerink, A. 4f ^{n} → 4f ^{n−1}5d transitions of the light lanthanides: experiment and theory. Phys. Rev. B 65, 045113 (2002).
Venstrom, L. J., Petkovich, N., Rudisill, S., Stein, A. & Davidson, J. H. The effects of morphology on the oxidation of ceria by water and carbon dioxide. J. Sol. Energy Eng. 134, 011005 (2012).
Gracia, J. et al. Ab initio calculations on the local structure and the 4f5d absorption and emission spectra of—doped YAG. J. Lumin. 128, 1248–1254 (2008).
Myers, C. E. & Graves, D. T. Vaporization thermodynamics of lanthanide trihalides. J. Chem. Eng. Data 22, 440–445 (1977).
Bhosale, R., Kumar, A. & AlMomani, F. Solar thermochemical hydrogen production via terbium oxide based redox reactions. Int. J. Photoenergy 2016, 1–9 (2016).
Furrer, A. et al. Crystalfield interaction and oxygen stoichiometry effects in strontiumdoped rareearth cobaltates. Phys. Rev. B 90, 064426 (2014).
Zhou, F. & Ozoliņš, V. Selfconsistent density functional calculations of the crystal field levels in lanthanide and actinide dioxides. Phys. Rev. B 85, 075124 (2012).
Walsh, W. M., Jeener, J. & Bloembergen, N. Temperaturedependent crystal field and hyperfine interactions. Phys. Rev. 139, A1338–A1350 (1965).
Murgida, G. E., Ferrari, V., GandugliaPirovano, M. V. & Llois, aM. Ordering of oxygen vacancies and excess charge localization in bulk ceria: A DFT + U study. Phys. Rev. B 90, 1–12 (2014).
Zacherle, T., Schriever, A., De Souza, R. A. & Martin, M. Ab initio analysis of the defect structure of ceria. Phys. Rev. B 87, 1–11 (2013).
Tuller, H. & Nowick, A. Small polaron electron transport in reduced CeO_{2} single crystals. J. Phys. Chem. Solids 38, 859–867 (1977).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmentedwave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Blochl, P. E. Projector augmentedwave method. Phys. Rev. B 50, 17953–17979 (1994).
Yen, W. M. General factors governing the efficiency of luminescent devices. Phys. Solid State 47, 1393 (2005).
Acknowledgements
S.S.N., A.A.E., C.W., V.O. were supported by US Department of Energy, Office of Science, Basic Energy Sciences, under grant DEFG0207ER46433. The work of F.Z. was performed under the auspices of the U.S. Department of Energy by Lawrence Livermore National Laboratory under Contract No. DEAC5207NA27344.
Author information
Authors and Affiliations
Contributions
All authors contributed to writing and editing the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Naghavi, S.S., Emery, A.A., Hansen, H. et al. Giant onsite electronic entropy enhances the performance of ceria for water splitting. Nat Commun 8, 285 (2017). https://doi.org/10.1038/s41467017003812
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467017003812
This article is cited by

Defect graph neural networks for materials discovery in hightemperature cleanenergy applications
Nature Computational Science (2023)

Hydrogen production via microwaveinduced water splitting at low temperature
Nature Energy (2020)

Dynamic charge and oxidation state of Pt/CeO2 singleatom catalysts
Nature Materials (2019)

Recent Progress and Approaches on CarbonFree Energy from Water Splitting
NanoMicro Letters (2019)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.