Thank you for visiting You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

An iron-based green approach to 1-h production of single-layer graphene oxide


As a reliable and scalable precursor of graphene, graphene oxide (GO) is of great importance. However, the environmentally hazardous heavy metals and poisonous gases, explosion risk and long reaction times involved in the current synthesis methods of GO increase the production costs and hinder its real applications. Here we report an iron-based green strategy for the production of single-layer GO in 1 h. Using the strong oxidant K2FeO4, our approach not only avoids the introduction of polluting heavy metals and toxic gases in preparation and products but also enables the recycling of sulphuric acid, eliminating pollution. Our dried GO powder is highly soluble in water, in which it forms liquid crystals capable of being processed into macroscopic graphene fibres, films and aerogels. This green, safe, highly efficient and ultralow-cost approach paves the way to large-scale commercial applications of graphene.


Graphene has been the focus of significant attention for its potential across a broad spectrum of applications due to its unrivalled mechanical, electrical and thermal properties1,2,3. Thus far, two main strategies have been developed for the production of graphene from graphite: mechanical exfoliation (including solvent and ultrasonic-assisted methods)4,5,6 and chemical oxidation–reduction7,8,9,10,11,12,13,14,15,16,17,18. Mechanically exfoliated graphene possesses few or no defects6,19, but suffers from poor solubility (<0.1 mg ml−1)4 and extremely low productivity (for example, ~2.0 × 10−3 g h−1)20. In addition, because of strong π–π stacking, such graphene is prone to irreversible aggregation after concentration and drying.

A recently applied process of high rate-shear exfoliation in N-methyl-2-pyrrolidone provides notable increases in productivity (~5.3 g h−1 (ref. 19), still far too low for commercial needs); however, the addition of polymer surfactants is necessary, otherwise the pristine graphene would aggregate and precipitate. Such graphene sheets are a mixture of different layers, limiting experimental reproducibility and inhibiting its use in fine applications. By comparison, preparation by chemical oxidation yields highly soluble single-layer graphene oxide (slGO; solubility>110 mg ml−1)21 in large-scales (up to tons scale), enabling easy processing of slGO into high performance composites and macroscopic materials such as fibres22,23, films/papers24 and aerogels25 by solution-based polymer-type techniques. Although slGO is often denounced for containing defects16 that may influence its properties, such defects can be easily repaired through simple chemical reduction26. Thermal treatment has the capacity to restore the chemically converted graphene (CCG) back to a material with ultrahigh electrical conductivity (1.83 × 105 S m−1) and thermal conductivity (1434 W m−1 K−1)27. These values are far higher than those of mechanically exfoliated defect-free graphene (2.2 × 104 S m−1, 313 W m−1 K−1)28. For these reasons, the slGO–CCG route is the more attractive of the two for the industrial production of graphene.

Generally, GO is prepared by the ultrasonic exfoliation of graphite oxide29. The preparation methods of GO can be classified by the oxidant employed as either the KClO3-based Brodie–Staudenmaier8,9,10 method or the KMnO4-based Hummers method11,12,13,14. The KClO3-based method was first introduced by Brodie8 in 1859, modified by Staudenmaier9 in 1898 and again modified by Hofmann10 in 1937. The reaction medium for this process is nitric acid, which presents the inherent disadvantages of explosion risk, release of hazardous gases (for example, NOX and ClO2) and the generation of carcinogenic ClO. The Hummers method was first reported in 1958 (ref. 11). Although the change of oxidant circumvented a number of KClO3-based issues, it is plagued by the necessity of polluting heavy metal ions (Mn2+) and the explosion risk that accompanies the unstable Mn2O7 intermediates30. Various modifications involving minor optimization of the Hummers method have been employed for the synthesis of GO; however, no significant improvements have been made despite the intensive interest in this material1,7,31. In addition, the two methodologies used to obtain slGO require long reaction times (6 h–5 days), relatively high temperatures (>50 °C) and often additional intercalation and ultrasonication processes. These shortcomings result in a costly process in terms of time and energy, a complicated fabrication procedure and carry high costs related to waste treatment. Hence, a green (free of toxic gases and polluting heavy metals), safe (no explosive risk), ultrafast and low cost methodology is eagerly sought.

Herein, we propose a strong yet green oxidant, K2FeO4, and establish an ultrafast, safe and non-toxic methodology for the scalable production of slGO. The entire fabrication process requires only 1 h, and the as-prepared large GO sheets are nearly 100% single layered without any ultrasonic treatment. Our slGO has a similar chemical structure and solubility to materials prepared using the conventional long-time modified Hummers method. Furthermore, the GO powder obtained by drying slGO solutions can be re-dissolved in water or organic solvents to form stable liquid crystals (LC) and subsequently assembled into macroscopic materials such as one-dimensional (1D) fibres, 2D films and 3D aerogels. In addition, sulphuric acid is recycled in our protocol. Through the refreshing of oxidant, our approach dramatically reduces the effluent and lowers the operating cost. This method paves the way for cheap, eco-friendly, large-scale production of slGO and its macroscopic materials.


Selection of oxidant

Oxidant is the most important controlling factor in the preparation of GO. The Brodie–Staudenmaier8,9,10 method and Hummers11,12,13,14 method essentially differ in their choice of oxidant. The prevailing oxidants, predominantly KClO3 and KMnO4, provide high oxygen content to the resultant GO materials; however, their byproducts are highly polluting and intermediates in the processes carry a high risk of explosion. For example, KClO3 is a key ingredient in blasting caps and is prone to explode when mixed with combustible materials. It is also frequently used in explosives and fireworks, and is thus strictly controlled in China. In the synthesis of GO with KClO3, the toxic and explosive gas ClO2 is generated in the concentrated sulphuric acid solvent. In addition, KMnO4 is easily converted into Mn2O7, which is prone to explode above 55 °C in an acidic environment30. The use of KMnO4 generates massive amounts of the heavy metal pollutant Mn2+, which can cause great damage to human and plant life in an ecosystem. The various modifications of these two methodologies over the past decade have not been able to remedy the substantial inherent environmental and safety issues related to the production of toxic gases and heavy metal pollutants or the risk of explosion.

To resolve the problems posed by the conventional methods, an alternative oxidant for GO production is sought. The new oxidant must satisfy the following prerequisites: (1) high oxidation efficiency, (2) no risk of explosion and (3) no toxic or polluting byproducts. After numerous experiments, we identified K2FeO4 as the novel oxidant of choice. K2FeO4 is an eco-friendly and highly efficient oxidant with harmless byproducts. Currently, it is widely used in the fields of environmental protection and water treatment32,33. K2FeO4 has an electrode potential of 2.2 V, which is much higher than that of KMnO4 (1.36 V) in acid environments, and should thereby considerably decrease the required reaction time. As opposed to KMnO4, K2FeO4 can be safely used at temperatures as high as 100 °C, due to the absence of explosive intermediates. In addition, as a commonly used water treatment agent, K2FeO4 is inexpensive and commercially available. Therefore, K2FeO4 is attractive as a new-generation oxidant for the preparation of GO in the desired eco-friendly and highly efficient manner.

Preparation and characterization of GO

Typically, concentrated sulphuric acid, K2FeO4 and flake graphite were loaded into a reactor and stirred for 1 h at room temperature. The dark green suspension gradually became a grey viscous fluid. After recycling the H2SO4 reaction medium by centrifugation, the precipitate was purified by repeated centrifugation and water-washing to obtain highly water soluble slGO (solubility>27 mg ml−1), coined as GOFe. Because the reaction process is extremely simple and requires no energy transfer (either heating or cooling), it is straightforward to scale up. For instance, we successfully used a 20-l reactor to prepare 750 g of GOFe in one pot (Supplementary Fig. 1), corresponding to a 75 l GOFe aqueous solution with a concentration of 10 mg ml−1 (Fig. 1a).

Figure 1: Large-scale synthesis of single-layer GO Fe via K 2 FeO 4 -based methodology.
figure 1

(a) Seventy-five litre GOFe aqueous solution with a concentration of 10 mg ml−1. (b) GOFe solution in H2O and N,N-dimethylformamide (DMF) with a concentration of 3 mg ml−1. (c) SEM image of GOFe on Si/SiO2 substrate. (d) The size distribution of the GOFe sheets, counted and calculated from c and Supplementary Fig. 2. (e) TEM image of GOFe and its SAED diffraction patterns (inset). (f) Tapping mode AFM image and height profile of GOFe. (g) GOFe solution of H2O and DMF with a concentration of 3 mg ml−1 after storage for 1 year. (h) Image of aqueous LCs in a quartz tube between crossed polarisers and POM image between crossed polarisers in planar cells of aqueous GOFe LCs at a concentration of 3 mg ml−1. Scale bars, 20 μm (c), 2 μm (e), 4 μm (f) and 5 mm (h, left), 1 μm (h, right).

The composition of GOFe was analyzed via combustion analysis, quantitative X-ray photoelectron spectroscopy (XPS) and inductively coupled plasma mass spectrometry (ICP-MS). Combustion analysis showed that GOFe has a relative composition of CO0.51H0.22S0.028. The XPS spectrum confirmed the composition of GOFe as follows (at.%): C (68.51%), O (31.14%), S (0.30%), Si (0.03%), N (0.01%), P (0.01%). ICP-MS measurements demonstrated the existence of negligible metal ion content: Fe (0.13 p.p.m.), Mn (0.025 p.p.m.), Co (0.073 p.p.m.), Cu (0.017 p.p.m.), Pb (0.033 p.p.m.) and Ni (0.014 p.p.m.). Notably, despite the high concentration of K2FeO4 in the reaction, the negligible iron content in the final GOFe after purification by the centrifugation/water-washing protocol indicates that no insoluble byproducts, such as Fe2O3, are generated in the fabrication and post-treatment processes.

The single-layered nature of the GOFe dispersion was demonstrated via scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM; Fig. 1). Under SEM inspection (Fig. 1c), the GOFe sheets show typical wrinkles, implying fine flexibility in the slGO sheets. According to the statistics from the SEM images, the GOFe sheets have a number-average width of ~10 μm and 53% of the relative size distribution (σw; Fig. 1d). TEM image also shows an abundance of wrinkles (Fig. 1e), and the selected area electron diffraction patterns (the insert) indicate its single-layer character34. The thickness of the GOFe, as measured by AFM, is ~0.9 nm (Fig. 1f), which confirms the single-layered state and the presence of oxygen-containing functional groups on the basal plane17.

Raman spectra, X-ray diffraction and ultraviolet–visible spectra show that the GOFe has a similar structure to GO prepared by the modified Hummers method24 using KMnO4 as the oxidant (GOMn; average lateral size=8 μm; σw=79%, Supplementary Fig. 3). The Raman spectrum (Fig. 2a) of GOFe shows the typical D peak (1,353 cm−1), G peak (1,600 cm−1), 2D peak (2,698 cm−1) and D+G peak (2,945 cm−1) with an ID/IG intensity ratio of 0.93, confirming lattice distortions induced by oxidation16. The XRD curve of the vacuum-assisted filtration paper indicates that the interlayer spacing of GOFe is ~9.0 Å (Fig. 2b), which is similar to that of GOMn (8.7 Å). The ultraviolet/Vis spectra of both GOFe and GOMn present a strong absorption peak at 230 nm (π→π* transitions of the conjugation domains) and a weak shoulder peak at ~300 nm (n→π* transitions of the carbonyl groups; Fig. 2c), revealing their similar domain structures35.

Figure 2: Comparison of GOFe and GOMn.
figure 2

(a) Raman spectra recorded using 514 nm laser excitation, (b) XRD spectra, (c) ultraviolet–visible spectra recorded in aqueous solution at 0.05 mg ml−1, (d) TGA plots, (e) Fourier transform infrared spectra and (fh) XPS spectra and its C1s XPS spectra of GOFe and GOMn. 1 and 2 denote GOFe and GOMn, respectively. All of these data show that GOFe and GOMn have similar composition and structures.

The thermogravimetric analysis (TGA) profiles of both GOFe and GOMn show similar weight loss plots (48–50% mass loss at 800 °C, Fig. 2d). The Fourier transform infrared spectra identify the same functional groups in GOFe as GOMn (Fig. 2e): O–H stretching vibrations (3,412 cm−1), C=O stretching vibration (1,726 cm−1), C=C from sp2 bonds (1,624 cm−1), O–C–O vibrations (1,260 cm−1) and C–O vibration (1,087 cm−1). As shown in Fig. 2f–h, the XPS spectra confirm the presence of similar chemical bonds in both GOFe and GOMn: C=C (284.86 eV), epoxy/hydroxyls (C–O, 287.0 eV), C=O (288.0 eV) and O–C=O (289.2 eV) (ref. 21).

The oxygen-rich functional groups impart a high zeta potential to GOFe (−58 mV) and excellent solubility in both water and polar organic solvents, as is the case for GOMn (Fig. 1b). The GOFe solution retains a homogenously dispersive constitution, without any precipitate, even after storage for 1 year at a concentration of 3 mg ml−1 in water or N,N-dimethylformamide (Fig. 1g). The excellent solubility of the highly asymmetrical GO sheets may enable the formation of a lyotropic LC23,36 phase, which is a criterion used to evaluate the ‘true’ solubility of graphene derivatives. Our GOFe aqueous dispersions display the vivid textures typical of nematic LCs between crossed polarizers (Fig. 1h).

Recycling and post-treatment of sulphuric acid

In addition to the problems of polluting heavy metals, toxic gases and tedious reaction times associated with the conventional methods, another persistent criticism of GO production is the pollution associated with the use of concentrated sulphuric acid, the disposal of which significantly adds to the costs of GO. We resolved this issue by recycling concentrated sulphuric acid, a process which was enabled by the strong oxidation ability of K2FeO4. We recycled the concentrated sulphuric acid at least 10 times without change to the fabrication efficiency (1 h) or the GO quality. Notably, even if the collected sulphuric acid was not immediately reused, its removal proved greatly beneficial to the subsequent GO purification by either centrifugation or sieving/filtration, as well as to the subsequent waste treatment steps. The small amount of H2SO4 complexed to K2SO4 and Fe2(SO4)3 in the washing water was neutralized with ammonia, forming mixtures consisting of (NH4)2SO4, K2SO4 and Fe2(SO4)3, which are used as fertilisers in agriculture. This protocol significantly decreases the cost of slGO.


To deeply understand the fast oxidation–exfoliation process in our K2FeO4-based system, we investigated the effects of oxidation on the dispersive state in water for samples collected at different reaction times. Supplementary Figure 4 shows the dispersion states of the materials after standing for 24 h. Only the solution observed at 1 h of reaction time has no precipitate, implying that the functional group density is high enough to overwhelm the aggregation tendency. Furthermore, the colour of the solutions becomes lighter with increasing oxidation time due to the gradual destruction of π–π conjugate structures by the formation of functional groups. More subtle analyses by XRD, TGA and zeta potential demonstrated that the entire reaction process (1 h) can be divided into two stages: intercalation–oxidation (IO) and oxidation–exfoliation (OE; Fig. 3)37.

Figure 3: Mechanism of GOFe synthesis with the oxidant of K2FeO4.
figure 3

The whole synthetic process (1 h) contains two main stages: intercalation–oxidation (IO) and oxidation–exfoliation (OE). The in situ generated FeO42− and atomic oxygen [O] act as oxidants and the O2 formed from residual [O] provides mild and durative gas exfoliation. In the IO stage, the concentrated sulphuric acid and oxidants intercalate into the layers of graphite to form intercalated graphite oxide (GIO). During the intercalation, the oxidants break the π–π conjugated structures of graphite, generating negatively charged functional groups, and increasing the interlayer spacing. In the following OE stage, the oxidants further oxidize the carbon basal planes of GIO, giving rise to more functional groups and enlarging the interlayer space. After recycling of sulphuric acid and washing with water, 100% slGO is achieved.

In the first IO stage, concentrated sulphuric acid and K2FeO4 intercalate into the interlayer spacing of graphite. The oxidant then breaks the π–π conjugated structures at the edges and defects of the graphite, weakening the conjugate forces between pristine graphitic lamellae. In the corresponding XRD patterns (Fig. 4a), the appearance of a new peak at 2θ=11.4° accompanies the gradual fading of the 002 peak at 2θ=26.5° with increasing reaction time. At ~15 min, the diffraction peak of graphite at 26.5° disappears completely, indicating the completion of the IO stage and the formation of intercalated and partially oxidized graphite (GIO). An increase of the d-spacing of GIO is observed from 0.34 to 0.75 nm due to intercalation and oxidation. Intercalation and oxidation of graphite occur simultaneously, as confirmed by the dramatic mass loss from 0 to 30 wt % at 15 min in the corresponding TGA curves (Fig. 4c,d). The zeta potential also decreases rapidly to −52 mV (Fig. 4d), demonstrating the generation of negatively charged functional groups.

Figure 4: Kinetics of the synthesis of GOFe.
figure 4

(a) XRD spectra of the samples taken from the synthesis process at the reaction times=0 min, 3 min, 5 min, 8 min, 11 min, 15 min 30 min, 45 min, 1 h and 2 h (110), respectively. (b) Interlayer spacing of selected samples at the OE stage versus reaction time. (c) TGA plots of the same samples as shown in a. (d) Weight loss of GOFe at 600 °C (left, red) and corresponding zeta potential (right, blue) as a function of reaction time. The kinetics of GOFe confirms that the whole reaction process completes in 1 h, including ~15 min of intercalation–oxidation and 45 min of oxidization–exfoliation. (e) Sample-H, Sample-T and GOFe (2 mg ml−1) placed in water, indicating that only GOFe is well-soluble. (f) XRD spectra, (g) C1s XPS spectra and (h) TGA plots of GOFe, Sample-H and Sample-T with the reaction time 1 h. (ik) SEM images of graphite, Sample-T and Sample-H, showing that the conventional Hummers methods with the oxidant of KMnO4 can only result in thick graphite-like particles rather than slGO in 1 h of reaction time. Scale bar, 20 μm (ik).

In the following OE stage, the oxidant further oxidized the carbon basal planes of GIO, giving rise to more functional groups and enlarging the d-spacing from 0.75 to 0.91 nm (Fig. 4a,b). In the TGA curves, the weight loss at 600 °C further increases from 30% at 15 min to 43% at 60 min (Fig. 4c). Notably, 100% slGO was achieved by 1 h, verifying the ultrafast OE process of our protocol. In fact, further extending the reaction time to 2 h gave little changes in the d-spacing, weight loss or zeta potential.

The entire reaction process is proposed by the following two steps:

In addition, FeO42− reacts with H+ or water to produce atomic oxygen [O] that also effectively oxidizes carbon38. FeO42− and [O] work synergistically to efficiently yield slGO. The residual [O] forms oxygen gas, making both intercalation and exfoliation much more powerful and ultrafast39. Accordingly, all the reactions can be listed as follows:

This unique reaction mechanism results in an ultrafast oxidation and exfoliation rates, providing slGO without additional ultrasonic treatment.

To analyze the oxidation efficiency of K2FeO4, we quantified the oxygen yield during GOFe production (Supplementary Methods). The results show that 70.2% of the K2FeO4 is consumed in the oxidation of graphite, 17.3% is decomposed into oxygen and 12.5% remains in the reaction suspension. This indicates that ~80% of the reacted K2FeO4 is converted into the oxygen-containing moieties of GO, confirming the extremely high oxidation efficiency of K2FeO4.

For comparison, we also studied samples oxidized for 1 h by two popular modified Hummers methods: Tour’s method14 (Sample-T) and Hirata’s method13 (Sample-H). Figure 4e shows that the two samples precipitated completely after 1 h of sonication after storage for 12 h, showing almost no solubility. XRD profile of Sample-H shows a strong graphite peak at 2θ=26.5° without the characteristic peak of graphite oxide. The Sample-T exhibits an obvious graphite peak and a graphite oxide peak at 2θ=11.9° (Fig. 4f), indicating strong oxidation but poor exfoliation. The XPS spectra of Sample-T and Sample-H reveal C/O ratios of 7.3 and 18.5, which are much higher than those found in GOFe (2.2; Fig. 4g). From the TGA plots of the two samples, ~32 and 10% mass losses are found, which are much lower than those found in GOFe (45%; Fig. 4h). A sample oxidized by KClO3 (Sample-B) for 1 h was also prepared and tested, indicating no solubility in water, a small degree of oxidation (C/O=13.4, 25 % wt loss) and poor exfoliation (with a strong graphite peak at 2θ=26.5° and graphite oxide peak at 2θ=12.5o; Supplementary Fig. 5). SEM images show that Sample-H has a similar thickness (~0.6 μm) as that of raw graphite and that a portion of Sample-T has a similar appearance to that of raw graphite, which confirm their multilayered state (Fig. 4i–k). These results demonstrate that our K2FeO4-based methodology, capable of both highly efficient oxidation and ultrafast exfoliation, is superior to the conventional methods.

Table 1 lists the comprehensive comparison of our K2FeO4-based methodology with the conventional methods. Generally, the new method possesses the following merits: ultrafast reaction rate, safe and environmentally friendly processing, no heavy metal pollution and ultralow cost. In our new method, 1 h is sufficient to obtain slGO without any additional post treatments such as ultrasonication or H2O2 washing, which are normally required in the Hummers methods. By comparison, the conventional methods require ~6 h–5 days of reaction time, as described in the 57 most cited studies on GO preparation (Supplementary Table 1). All of the conventional methods based on the KClO3 and KMnO4 oxidants as well as their optimized modifications produce toxic gases (ClO2, NOX) and explosive intermediates (for example, Mn2O7). In addition, for the KMnO4-based methodology, consumption of 1 ton of graphite would result in 1–5 ton of neat Mn2+ and 40–120 ton of sulphuric acid waste, leading to pollution, tedious post treatments and high costs. The high concentration of manganese in the system also stains GO with a Mn content of up to 97 p.p.m., which may cause significant injury to the body in cases where GO is used as a vehicle for drugs40,41. On the contrary, our K2FeO4-based approach has no safety or pollution issues, and the Mn content in GOFe is negligible (~0.025 p.p.m.). Moreover, the GOFe contains almost no iron (0.13 p.p.m.) despite the use of an iron-based oxidant, to the benefit of the eventual applications of GO and CCG.

Table 1 A comparison of our K2FeO4-based methodology with KClO3- and KMnO4-based methodologies.

Even though the fabrication is ultrafast at room temperature, the resulting GOFe is highly soluble in water and polar organic solvents and has both a composition and morphology comparable to GOMn. As such, GOFe can be directly used in fields where GOMn has been demonstrated to be effective.

The preparation of GO powders is another very important issue that greatly affects the practical use of GO and its transport. Freeze-drying is commonly used to obtain solid GO. As shown in Supplementary Fig. 6, commercial GO powders apparently precipitate in minutes at 2 mg ml−1 even after 12 h of ultrasonic agitation. GO sheets laminate together as a result of π–π conjugation in the process of solvent removal. These aggregates are difficult to disrupt by the re-addition of solvents. We adopt a spray-drying method to control the morphology of the GOFe sheets and obtain only soluble GO powders (Fig. 5b). The dried GO powders can be completely dissolved in water and N,N-dimethylformamide (Fig. 5e) to form lyotropic LCs (Fig. 5h), identical to the fresh GO solutions before drying (Fig. 1b,h). The GO sheets are all dispersed in a single-layered state, as confirmed by SEM and AFM measurements (Fig. 5f,g).

Figure 5: Spray-dried GO Fe powder for re-dissolving.
figure 5

(a) Fresh GOFe LC solution of H2O with a concentration of 6 mg ml−1. (b) Macroscopic photograph of spray-dried GOFe powders with a density of 224 mg cm−3. (c,d) SEM images of GOFe powders, showing that the GOFe individual particles have a peony-like morphology. The insert of d is a peony. (e) Re-dissolved GOFe solutions of H2O and N,N-dimethylformamide with a concentration of 4 mg ml−1. (f) SEM image of re-dissolved single-layered GOFe sheets on Si/SiO2 substrate. (g) Tapping mode AFM image and height profile of re-dissolved GOFe. (h) POM images of re-dissolved GOFe aqueous LCs in a quartz tube and a planar cell between crossed polarisers at a concentration of 4 mg ml−1. Scale bars, 3 μm (c), 500 nm (d), 10 μm (f), 2 μm (g) and 5 mm (h, left), 1 μm (h, right).

As shown in Fig. 5c,d, the surfaces of the dried GO sub-microspheres are full of folds because the GO sheets shrink inwardly, forming peony-like 3D crumpled structures under the surface tension experienced in the spray-drying process. Such 3D crumpled sub-microsphere morphologies effectively prevent GO stacking, favouring the unfolding of sub-microspheres into plane sheet morphologies when re-dissolved in solvents. The GOFe sub-microsphere powder has a specific surface area of 1,467 m2 g−1, indicating 1–2 atomic layer structures (Supplementary Fig. 7). The dried GOFe powders are highly soluble in water and polar organic solvents. Significantly, our GOFe powder has a very high density (>224 mg cm−3), which facilitates its storage, transport and application. By comparison, despite a very low density (<30 mg cm−3) resulting from the freeze-drying process, the undissolved commercial GO powders have a very low specific surface area (<10 m2 g−1) due to their multilayer structure (Supplementary Fig. 8).

The excellent dispersibility of the GOFe powders gives them superior solution processability, which is important in the fabrication of macroscopic materials (for example, 1D fibres, 2D films and 3D frameworks). A re-dissolved aqueous GOFe solution (~6 mg ml−1) shows a colourful optical texture typical of a nematic LC mesophase, identical to the appearance of fresh aqueous GOFe solutions (Fig. 5a and Supplementary Fig. 9)36. In a macroscopic quartz tube, the birefringence Schlieren texture between crossed polarisers can be seen with the naked eye across the entire solution (Fig. 5h). Such a LC suspension establishes the foundation to fabricate GO fibres, which has been demonstrated by our group and other independent researchers22,42. We subsequently obtained a continuous fibre by wet-spinning of the LC dope (Fig. 6a–c and Supplementary Fig. 10). It shows a highly compact and ordered structure, similar to previous GO fibres made directly from undried GO suspensions.

Figure 6: Macroscopic assembled materials of re-dissolved GOFe.
figure 6

(ac) A wet-spun 14-m long continuous fibre with diameter 10 μm and its SEM images at the cross-section of fibre. (df) A film made by the filtration method and its SEM image of a section. (gi) Ultralight weight GOFe aerogel with a density of 2 mg cm−3 and its SEM images showing CNT-coated graphene morphology. Scale bars, 3 cm (a), 1 μm (b), 500 nm (c), 1 cm (d), 3 μm (e), 400 nm (f), 2 cm (g), 30 μm (h) and 2 μm (i).

A film was made from the re-dissolved GOFe solution (Fig. 6d–f and Supplementary Fig. 11a) by the vacuum-assisted filtration method, which shows a well-aligned lamellar structure and comparable mechanical performance to GOMn papers43. After reduction with HI, our graphene film exhibits an electrical conductivity of 374 S cm−1 (Supplementary Fig. 11c), close to that (400 S cm−1) of defect-free graphene made by a high-shear exfoliation method19. A 3D aerogel prepared by a synergistic assembly of GOFe and carbon nanotubes (CNTs, 50 wt %) shows the same appearance and internal structure (Fig. 6g–i and Supplementary Fig. 12a) as an assembly prepared from GOMn and CNTs reported by our group previously25. After reduction with N2H4, an aerogel with a density of 2.0 mg cm−3 shows complete recovery even after 1,000 cycles of 87% compression. Significantly, the aerogel still remains elastic and intact after being compressed by a weight 5,000 times its own (Supplementary Fig. 12b). These results demonstrate the ‘true’ solution state of our re-dissolved GOFe and suggest the wide application of GO and CCG.

In conclusion, we established an industrially viable one-pot method for the production of slGO in 1 h at room temperature with ultralow cost based on the use of the novel oxidant of K2FeO4. The reaction process includes ~15 min of intercalation–oxidation and ~45 min of oxidization–exfoliation. The excellent oxidation capabilities of both K2FeO4 and the in situ generated atomic oxygen, accompanied by the exfoliation capacity of oxygen gas, make the intercalation, oxidation and exfoliation extremely powerful and ultrafast. The as-prepared slGO has a similar composition, chemical structure and solubility to materials prepared by the conventional Hummers method. Significantly, our dried slGO powders maintain excellent solubility in water and polar organic solvents and readily form stable LCs. Therefore, they retain the capacity to assemble into macroscopic materials such as continuous fibres, films and aerogels displayed by fresh GO solutions. The sulphuric acid solvent can be recycled in our protocol due to the ultrastrong oxidation capability of K2FeO4, which dramatically reduces the effluent and lowers the cost of GO. Our fast, eco-friendly and safe K2FeO4-based methodology circumvents the intrinsic problems associated with the prevailing methods of GO production, and it is easily amenable to the scalable production and industrial application of GO and CCG.


Synthesis of GOFe

K2FeO4 (60 g, 6 wt equiv.) was added to concentrated H2SO4 (93%, 400 ml) at room temperature. Graphite (10 g, 1 wt equiv., 40 μm) was then added and the mixture was kept at room temperature for 1 h (note: the flask was not sealed due to the release of oxygen during the reaction). The mixture was centrifuged (10,000 r.p.m. for 3 min) to recycle the concentrated sulphuric acid. The paste-like product was collected by repeated centrifugation and washing with 1 l of water until the pH of the supernatant solution approached 7.

Apparatus for characterizations

AFM images of GO sheets were taken in the tapping mode on a Nano Scope IIIA, with samples prepared by spin-coating diluted aqueous solutions onto freshly exfoliated mica substrates at 1,000 r.p.m.. SEM images were taken on a Hitachi S4800 field-emission SEM system. TEM was performed on a JEM-1200EX with an accelerating voltage of 120 kV. Zeta potential measurements were performed on a ZET-3000HS apparatus. Fourier transform infrared spectra were recorded on a PE Paragon 1000 spectrometer (film or KBr disk). Ultraviolet–visible spectra were obtained using a Varian Cary 300 Bio UV-visible spectrophotometer. Tensile tests were carried out on a HS-3200C at a loading rate of 1 mm min−1. XPS was performed using a PHI 5000C ESCA system operated at 14.0 kV. All binding energies were referenced to the C1s neutral carbon peak at 284.8 eV. TGA was carried out using a thermogravimetric analyser (PerkinElmer Pyris 1) from room temperature to 850 °C at 10 °C min−1 heating rate under air atmosphere. XRD data were collected with an X’Pert Pro (PANalytical) diffractometer using monochromatic Cu Kα1 radiation (λ=1.5406 Å) at 40 kV. Raman spectra were recorded on a Labram HRUV spectrometer operating at 632.8 nm. Mechanical property tests were carried out on a HS-3002C at a loading rate of 10% per minute. Elemental analyses were performed using an Agilent model 7700 × ICP-MS. BET surface area measurements were performed by nitrogen adsorption on a Quantachrome NOVA 2000 surface analyzer. POM observations were performed with a Nikon E600POL, and the liquid samples were loaded into the planar cells for observations. Combustion analysis was performed on an elemental analyzer (Vario Micro).

Additional information

How to cite this article: Peng, L. et al. An iron-based green approach to 1-h production of single-layer graphene oxide. Nat. Commun. 6:5716 doi: 10.1038/ncomms6716 (2015).


  1. Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).

    CAS  Article  ADS  Google Scholar 

  2. Tung, V. C., Allen, M. J., Yang, Y. & Kaner, R. B. High-throughput solution processing of large-scale graphene. Nat. Nanotechnol. 4, 25–29 (2009).

    CAS  Article  ADS  Google Scholar 

  3. Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).

    CAS  Article  ADS  Google Scholar 

  4. Hernandez, Y. et al. High-yield production of graphene by liquid-phase exfoliation of graphite. Nat. Nanotechnol. 3, 563–568 (2008).

    CAS  Article  ADS  Google Scholar 

  5. Coleman, J. N. et al. Two-dimensional nanosheets produced by liquid exfoliation of layered materials. Science 331, 568–571 (2011).

    CAS  Article  ADS  Google Scholar 

  6. Smith, R. J. et al. Large-scale exfoliation of inorganic layered compounds in aqueous surfactant solutions. Adv. Mater. 23, 3944–3948 (2011).

    CAS  Article  Google Scholar 

  7. Dreyer, D. R., Park, S., Bielawski, C. W. & Ruoff, R. S. The chemistry of graphene oxide. Chem. Soc. Rev. 39, 228–240 (2010).

    CAS  Article  Google Scholar 

  8. Brodie, B. C. On the atomic weight of graphite. Phil. Trans. R. Soc. Lond. 149, 249–259 (1859).

    Article  ADS  Google Scholar 

  9. Staudenmaier, L. Verfahren zur darstellung der graphitsäure. Ber. Dtsch. Chem. Ges. 31, 1481–1487 (1898).

    CAS  Article  Google Scholar 

  10. Hofmann, U. & König, E. Untersuchungen über graphitoxyd. Z. Anorg. Allg. Chem. 234, 311–336 (1937).

    CAS  Article  Google Scholar 

  11. Hummers, W. S. & Offeman, R. E. Preparation of graphitic oxide. J. Am. Chem. Soc. 80, 1339–1339 (1958).

    CAS  Article  Google Scholar 

  12. Kovtyukhova, N. I. et al. Layer-by-layer assembly of ultrathin composite films from micron-sized graphite oxide sheets and polycations. Chem. Mater. 11, 771–778 (1999).

    CAS  Article  Google Scholar 

  13. Hirata, M., Gotou, T., Horiuchi, S., Fujiwara, M. & Ohba, M. Thin-film particles of graphite oxide 1. Carbon 42, 2929–2937 (2004).

    CAS  Google Scholar 

  14. Marcano, D. C. et al. Improved synthesis of graphene oxide. ACS Nano 4, 4806–4814 (2010).

    CAS  Article  Google Scholar 

  15. Pei, S., Zhao, J., Du, J., Ren, W. & Cheng, H. M. Direct reduction of graphene oxide films into highly conductive and flexible graphene films by hydrohalic acids. Carbon 48, 4466–4474 (2010).

    CAS  Article  Google Scholar 

  16. Stankovich, S. et al. Synthesis of graphene-based nanosheets via chemical reduction of exfoliated graphite oxide. Carbon 45, 1558–1565 (2007).

    CAS  Article  Google Scholar 

  17. Becerril, H. A. et al. Evaluation of solution-processed reduced graphene oxide films as transparent conductors. ACS Nano 2, 463–470 (2008).

    CAS  Article  Google Scholar 

  18. Moon, I. K., Lee, J., Ruoff, R. S. & Lee, H. Reduced graphene oxide by chemical graphitization. Nat. Commun. 1, 73 (2010).

    Article  ADS  Google Scholar 

  19. Paton, K. R. et al. Scalable production of large quantities of defect-free few-layer graphene by shear exfoliation in liquids. Nat. Mater. 13, 624–630 (2014).

    CAS  Article  ADS  Google Scholar 

  20. Hamilton, C. E., Lomeda, J. R., Sun, Z., Tour, J. M. & Barron, A. R. High-yield organic dispersions of unfunctionalized graphene. Nano Lett. 9, 3460–3462 (2009).

    CAS  Article  ADS  Google Scholar 

  21. Xu, Z., Zhang, Y., Li, P. & Gao, C. Strong, conductive, lightweight, neat graphene aerogel fibers with aligned pores. ACS Nano 6, 7103–7113 (2012).

    CAS  Article  Google Scholar 

  22. Xu, Z. & Gao, C. Graphene chiral liquid crystals and macroscopic assembled fibres. Nat. Commun. 2, 571 (2011).

    Article  ADS  Google Scholar 

  23. Xu, Z. & Gao, C. Graphene in macroscopic order: liquid crystals and wet-spun fibers. Acc. Chem. Res. 47, 1267–1276 (2014).

    CAS  Article  Google Scholar 

  24. Han, Y., Xu, Z. & Gao, C. Ultrathin graphene nanofiltration membrane for water purification. Adv. Funct. Mater. 23, 3693–3700 (2013).

    CAS  Article  Google Scholar 

  25. Sun, H., Xu, Z. & Gao, C. Multifunctional, ultra-flyweight, synergistically assembled carbon aerogels. Adv. Mater. 25, 2554–2560 (2013).

    CAS  Article  Google Scholar 

  26. Bagri, A. et al. Structural evolution during the reduction of chemically derived graphene oxide. Nat. Chem. 2, 581–587 (2010).

    CAS  Article  Google Scholar 

  27. Xin, G. et al. Large-area freestanding graphene paper for superior thermal management. Adv. Mater. 26, 4521–4526 (2014).

    CAS  Article  Google Scholar 

  28. Wu, H. & Drzal, L. T. Graphene nanoplatelet paper as a light-weight composite with excellent electrical and thermal conductivity and good gas barrier properties. Carbon 50, 1135–1145 (2012).

    CAS  Article  Google Scholar 

  29. Liang, Y. et al. Co3O4 nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. Nat. Mater. 10, 780–786 (2011).

    CAS  Article  ADS  Google Scholar 

  30. Koch, K. R. & Krause, P. F. Oxidation by Mn2O7—an impressive demonstration of the powerful oxidizing property of dimanganeseheptoxide. J. Chem. Educ. 59, 973–974 (1982).

    CAS  Article  Google Scholar 

  31. Dreyer, D. R., Ruoff, R. S. & Bielawski, C. W. From conception to realization: an historial account of graphene and some perspectives for its future. Angew. Chem. Int. Ed. 49, 9336–9344 (2010).

    CAS  Article  Google Scholar 

  32. Hoppe, M. L., Schlemper, E. O. & Murmann, R. K. Structure of dipotassium ferrate(VI). Acta Crystallogr. B38, 2237–2239 (1982).

    CAS  Article  Google Scholar 

  33. Audette, R. J., Smith, P. J. & Quail, J. W. Oxidation of substituted benzyl alcohols with ferrate (Vi) ion. J. Chem. Soc. Chem. Commun. 38–39 (1972).

  34. Park, S. & Ruoff, R. S. Chemical methods for the production of graphenes. Nat. Nanotechnol. 5, 309 (2010).

    CAS  Article  ADS  Google Scholar 

  35. Gao, X., Jang, J. & Nagase, S. Hydrazine and thermal reduction of graphene oxide: reaction mechanisms, product structures, and reaction design. J. Phys. Chem. C 114, 832–842 (2010).

    CAS  Article  Google Scholar 

  36. Xu, Z. & Gao, C. Aqueous liquid crystals of graphene oxide. ACS Nano 5, 2908–2915 (2011).

    CAS  Article  Google Scholar 

  37. Dimiev, A. M. & Tour, J. M. Mechanism of graphene oxide formation. ACS Nano 8, 3060–3068 (2014).

    CAS  Article  Google Scholar 

  38. Rush, J. D. & Bielski, B. H. J. Kinetics of ferrate (V) decay in aqueous solution. A pulse-radiolysis study. Inorg. Chem. 28, 3947–3951 (1989).

    CAS  Article  Google Scholar 

  39. Geng, X. et al. Interlayer catalytic exfoliation realizing scalable production of large-size pristine few-layer graphene. Sci. Rep. 3, 1134 (2013).

    Article  Google Scholar 

  40. Liu, Z., Robinson, J. T., Sun, X. M. & Dai, H. PEGylated nanographene oxide for delivery of water-insoluble cancer drugs. J. Am. Chem. Soc. 130, 10876–10877 (2008).

    CAS  Article  Google Scholar 

  41. Sun, X. et al. Nano-graphene oxide for cellular imaging and drug delivery. Nano Res. 1, 203–212 (2008).

    CAS  Article  ADS  Google Scholar 

  42. Cong, H., Ren, X., Wang, P. & Yu, S. Wet-spinning assembly of continuous, neat, and macroscopic graphene fibers. Sci. Rep. 2, 613 (2012).

    Article  Google Scholar 

  43. Dikin, D. A. et al. Preparation and characterization of graphene oxide paper. Nature 448, 457–460 (2007).

    CAS  Article  ADS  Google Scholar 

Download references


This work is supported by the National Natural Science Foundation of China (no. 21325417) and Fundamental Research Funds for the Central Universities (no. 2013XZZX003).

Author information




C.G., L.P. and Z.X. conceived and designed the research; L.P. conducted the experiments and analyzed the data; Z. Liu, Z. Li, H.S., X.Z. and Y.W. discussed the data and provided some useful suggestions; C.G. supervised and directed the project; all of the authors read and revised the paper.

Corresponding author

Correspondence to Chao Gao.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures 1-12, Supplementary Tables 1, Supplementary Methods and Supplementary References (PDF 488 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Peng, L., Xu, Z., Liu, Z. et al. An iron-based green approach to 1-h production of single-layer graphene oxide. Nat Commun 6, 5716 (2015).

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI:

Further reading


By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.


Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing