Coherent acoustic phonons modulate optical, electronic and mechanical properties at ultrahigh frequencies and can be exploited for applications such as ultratrace chemical detection, ultrafast lasers and transducers. Owing to their large absorption cross-sections and high sensitivities, nanoplasmonic resonators are used to generate coherent phonons up to terahertz frequencies. Generating, detecting and controlling such ultrahigh frequency phonons has been a topic of intense research. Here we report that by designing plasmonic nanostructures exhibiting multimodal phonon interference, we can detect the spatial properties of complex phonon modes below the optical wavelength through the interplay between plasmons and phonons. This allows detection of complex nanomechanical dynamics by polarization-resolved transient absorption spectroscopy. Moreover, we demonstrate that the multiple vibrational states in nanostructures can be tailored by manipulating the geometry and dynamically selected by acousto-plasmonic coherent control. This allows enhancement, detection and coherent generation of tunable strains using surface plasmons.
Plasmonic nanostructures have revolutionized nano-optics1,2,3 with their ability to generate strong localized electromagnetic fields when illuminated from the far-field, analogous to antennas for light4. The generation, detection and control of ultrahigh frequency phonons have been a topic of intense research5,6,7,8,9,10. Plasmons are effective for localizing light in a subwavelength volume and are ideal candidates for manipulating nanoscale mechanical motion because of their large absorption cross-sections, subwavelength field localization and high sensitivity to geometry and refractive index changes. This efficient absorption makes the plasmon an effective transducer of far-field radiation into phonons5: the plasmonic nanostructure absorbs energy from the laser pulse and rapidly expands, generating coherent acoustic phonons through impulsive thermal excitation11,12,13,14. When a metallic nanostructure first absorbs an ultrashort laser pulse, a localized surface plasmon, a coherent oscillation of electrons, is excited. The electrons rapidly dephase on a 5- to 20-fs timescale because of electron–electron scattering, electron–surface scattering and radiation damping15. The electrons then superdiffuse throughout the nanostructure at the Fermi velocity (~106 m s−1), distributing their kinetic energy over the nanostructure within ~100 fs (ref. 16). The electrons transfer energy to the lattice, resulting in a rapid thermal expansion of the structure that sets off oscillations between the initial and expanded lattice spacing, known as coherent acoustic phonons. The phonons can be detected afterwards with a weak probe pulse that senses the phonons through the strain-induced shift of the plasmon resonance6.
Opto-mechanical resonators allow strong light–matter interactions at increasingly smaller scales. Micron-scale dielectric resonators allow single-photon control of opto-mechanical properties17, tunable electromagnetically induced transparency18 and quantum-coherent coupling between light and mechanical modes19. Unique plasmonic dispersions allow researchers to investigate acoustic modes at subwavelength scales in simple structures such as spheres and bars6. Plasmonic nanoparticles offer the benefits of higher absorption, thus more efficient phonon excitation through impulsive thermal expansion, and higher detection sensitivity than equivalently sized dielectric nanoparticle because of their resonant nature and the large photoelastic coefficient of metal20. These characteristics allow phonon excitation and detection in nanostructures containing only hundreds of atoms21. Through electromagnetic coupling, larger nanoantennas have been used to enhance the phonon detection in adjacent smaller nanoparticles22. Recent advances in spatial control of surface plasmons from the far field have the potential to allow selective subwavelength detection of phonon modes—previously only possible using an X-ray free-electron laser9.
Here we show that in a multimodal nanostructure (plasmonic and phononic), manipulating the polarization of the probe laser allows dynamic control over the region in which mechanical motion is detected. We demonstrate selective excitation and detection of mechanical motion of plasmonic nanostructures through the design of the particle’s geometry and time domain-coherent control.
To demonstrate the capabilities of plasmons for nanoscale detection and manipulation of phonons, we designed and fabricated nano Swiss-cross samples (Fig. 1a) that exhibit localized phonon modes. The phonon modes of a metal nanostructure are high-frequency mechanical distortions of the metallic lattice and are the solutions of the Navier equation with continuity of displacement and stress at the nanostructure boundaries21. The displacement profile for the two lowest-order phonon modes of a Swiss-cross are shown in Fig. 1b,c. The mode in which the two arms oscillate in phase is the symmetric mode and the mode where the arms oscillate out of phase is the antisymmetric mode. These modes can be viewed as the hybridization of the extensional modes of the two arms. The modes are symmetric and antisymmetric in the context of coupled mode theory and not in terms of spatial symmetry23,24. The phonons modify the optical properties of a nanostructure through mechanical distortion of the geometry and strain-induced modifications20 of the refractive index of the metal. The two contributions to the optical response are of the same order of magnitude.
Through their sensitivity to geometry and material properties, the surface plasmon serves as a local probe of coherent acoustic phonons. The change in probe transmission after excitation by the pump pulse is shown in the inset of Fig. 1f. The sample is an array of 35-nm-thick gold Swiss-crosses with horizontal and vertical arm lengths of 120 and 90 nm, respectively, on a quartz substrate. The transient transmission is measured using time domain spectroscopy (pump–probe) at normal incidence as discussed in the Methods section. The pump excites a plasmon that rapidly decays to non-thermalized electrons25. The electrons thermalize through scattering processes on a sub-picosecond timescale raising the electronic temperature and changing the interband transition rates26: producing a sharp peak in the transient transmission measurement16. The electrons then rapidly heat the lattice through electron–phonon scattering, which generates coherent acoustic phonons, the sinusoidal oscillations with a period of ~100 ps. The Fourier transform of this time trace yields the frequency response of the vibrating nanostructure: the peaks at ~10 and ~15 GHz correspond to the antisymmetric and symmetric phonon modes with quality factors of ~16 and 9, respectively. Simulations of a periodic array of Swiss-crosses on a glass substrate with no internal damping yield quality factors (Q>500, see Supplementary Fig. 1) much larger than the experimentally observed quality factors, which suggests internal damping27,28,29 and inhomogeneous broadening may contribute to the linewidth of the measured signals.
Polarization-sensitive phonon detection
The spatial selectivity for detecting coherent acoustic phonons, in contrast to its generation, is determined by the spatial distribution of the probe plasmon and does not depend on the electron diffusion length of the constituent materials because of the short lifetime of the probe surface plasmons. Thus, the probe plasmon can resolve strain distributions at length scales below the superdiffusion length. For the Swiss-cross, the nanostructure supports two probe plasmon modes (see Supplementary Fig. 2 for the transmission spectrum), localized in different regions of the nanostructure that can be excited with horizontal (Fig. 1e) and vertical polarizations (Fig. 1g), which enable the local detection of phonon modes. The phonon modes that create symmetric strain profiles will shift the resonance frequency of the plasmon modes polarized along both axes in the same direction. For example, the initial expansion of the nanoparticle red-shifts both the vertical and horizontal plasmon modes. In contrast, an antisymmetric phonon mode (in which a compression along one axis is accompanied by an extension along the perpendicular axis) red-shifts one plasmonic resonance while blue-shifting the other resonance. In other words, the distortions because of the symmetric and antisymmetric modes will be in phase along one axis and π out of phase along the other axis.
Measuring this polarization-dependent phase allows one to determine the symmetry of the nanoscale phonon modes from a far-field measurement. We find that when the probe polarization is changed from horizontal (Fig. 1d) to vertical (Fig. 1f), a dip at 11 GHz appears. This destructive interference at 11 GHz in the transient transmission spectrum for a horizontally polarized probe pulse (Fig. 1d) indicates that the mechanical motion from the two phonon modes equals in magnitude and in opposite directions. This interference effect is a signature of two opposite sign perturbations to the plasmonic mode and is critical evidence for our ability to control the detection below the diffraction limit. When the probe polarization is vertical (Fig. 1f), the two perturbations are in phase and the interference effect is no longer observed. This measurement indicates a symmetry difference between the lower frequency and higher frequency phonon modes in excellent agreement with the nanomechanical simulations (Fig. 1b,c). The numerical calculation for an isolated gold nanostructure indicates antisymmetric and symmetric modes at 8.6 and 12.6 GHz, respectively. The observed splitting of the higher energy resonance is because of substrate effects; in particular, the substrate shifts the resonance frequencies of the modes and breaks the out-of-plane symmetry allowing the excitation of additional out-of-plane modes (see Supplementary Figs 3–6).
The observed polarization dependence of the phononic response demonstrates that plasmonic nanostructures can selectively detect mechanical displacements. Future applications of this technique can leverage the advances in coherent control of electromagnetic fields to selectively detect phonons on narrow tips30 and complex nanostructures31, revolutionizing the ability to detect phonons in nanoscale regions from the far field.
Tailoring the phonon modes via symmetry
The polarization manipulation of the probe surface plasmon allows selective detection; manipulating the pump polarization, however, does not allow selective excitation because of energy transport by superdiffusive electrons. The amplitudes of the phonon eigenmodes can be controlled through design of the nanostructures and understanding of the hot electron dynamics. In particular, we use the fact that the phonons are excited because of an isotropic heating to prevent the excitation of antisymmetric modes by designing the structure to be symmetric. As an example, we design a symmetric Swiss-cross and find that only the symmetric mode is excited as seen in Fig. 2a. Similar phonon modes are observed for all pump and probe polarization combinations, illustrating that in a small symmetric structure the phonon modes excited are relatively independent of the pump polarization. The antisymmetric mode is not excited despite the fact that the structure supports symmetric and antisymmetric modes as shown in the numerical model in Fig. 2b. In the numerical analysis, we first assume isotropic heating of the free-standing nanostructure, because of superdiffusive transport effects, and then calculate the resulting expansion of the nanostructure yielding a spatially dependent displacement. We then calculate the relative amplitude of each phonon mode by decomposing the initial displacement profile into the basis of vibrational eigenmodes32,33. The amplitudes of the two modes when one arm length is fixed and the other varied are shown in Fig. 2b. When the lengths of the arms are equal, we find that the predicted amplitude of the antisymmetric mode is zero, in agreement with experiments. In the limit of high aspect ratio Lx>>Ly, the antisymmetric mode becomes similar to the extensional mode of a bar, which is efficiently excited. The symmetric mode instead has a low excitation efficiency32 and approaches a breathing mode. The agreement between the experiments and the model indicates that the lattice heating is relatively uniform for both excitation polarizations. This is consistent with the literature values for the diffusion length of non-equilibrium electrons in gold, the characteristic length over which electrons deposit their kinetic energy, which is ~40 nm (refs 16, 34, 35). Future experiments on larger structures or structures composed of materials with shorter electron diffusion lengths can be used to study electron transport and their interaction with coherent phonons at the nanoscale.
Coherent control of acoustic phonons
In order to excite arbitrary acoustic modes, the spatially selective excitation method is less viable because of the fact that our nanostructures are comparable in size to the diffusion length of the electrons; therefore, hot electron superdiffusion will spread energy throughout the structure before the coherent acoustic phonon excitation, regardless of the initial energy distribution. In contrast, temporal coherent control does not require localized heating. Temporal coherent control was originally proposed to manipulate the quantum states of atoms and molecules to yield a desired reaction product36. It has since been used to manipulate spin qubits37, the near-field of surface plasmons31 and the vibrational state of single molecules38. In phononics, coherent control techniques39 have been used to selectively excite a specific subset of modes in nanoparticles40,41 and semiconductor superlattices42. Complex structures such as the ones studied in this work support a rich spectrum of acoustic eigenmodes and can be potentially used to synthesize arbitrary phonon pulses.
In order to control the behaviour of the phonons in the Swiss-cross structures, we generate a pair of excitation pulses (pump and control in Supplementary Fig. 7) with a variable temporal separation. We then measure the transient transmission with a probe pulse. Depending on the temporal separation of the two excitation pulses, the phonons can either be enhanced or suppressed. Two excitation pulses spaced in time by an integer number of phonon periods will enhance the mode, while a half integer spacing suppresses the mode by destructive interference. In this way, we can set the initial strain/displacement pattern to be a linear combination of the strain profiles of each eigenmode. The amplitudes of the phonon modes that are excited are shown in Fig. 3a. At zero delay between the pump and control pulses we see all of the modes of the system (trace i, Fig. 3a). With a properly timed control pulse delay (100 ps), we can make the normally weak antisymmetric mode stronger than the symmetric mode (trace iii, Fig. 3a). The phononic response for the full set of control pulse delays is shown in Fig. 3c,d. The amplitudes of the modes are shown in Fig. 3d (dots) along with a model in which we assume a phase delayed excitation of the phonon modes (solid line). We take the initial amplitudes from the single pump experiment and predict the amplitudes at different pump-control pulse delays in the coherent control experiment by assuming a coherent addition of the phonons generated by the two pulses. The agreement between the experiment and the model indicates that tailored frequency responses can be predicted and generated using the coherent control of phonons.
In conclusion, we have demonstrated optical manipulation and detection of the gigahertz mechanical motion of complex nanostructures using multimodal phonon interference effects. We observe optically the polarization-dependent interference of the symmetric and antisymmetric phonon modes. In addition, through coherent control and structure design we can tailor which modes are excited by the plasmonically generated superdiffusive electrons. Plasmonic nanostructures may expand the toolbox of phononics techniques43,44 at the nanoscale. The presented results open new routes for the development of coherent phonon sources and are a step towards the realization of nanophononic devices capable of probing electronic, thermal and phononic states.
The pump is generated by a titanium–sapphire femtosecond laser (Mai Tai HP, 820 nm, ~100 fs) with a power of 4 mW and the probe is from an optical parametric oscillator (Inspire, 700 nm, ~100 fs, <1 mW) pumped with the same laser. The repetition rate of both systems is 80 MHz. The pump and probe beams are collinear and are focused with a 0.25 NA objective and collected with a 0.65 NA objective. The pump and probe beam waists are 5 μm. Spectral filters are used to separate the pump and probe before detection. The analysis procedure for the transient transmission measurements is illustrated in Supplementary Fig. 8.
The phonon dynamics are simulated using the finite element solver COMSOL Multiphysics. We calculate, in the frequency domain, the response of a nanoparticle to an impulse strain in the metal because of the pulsed laser excitation. The thermal strain generates a force that sets the particle in motion. Given the mechanical motion, we take a simple model for the detection by the plasmon and assume that the transient transmission change will be proportional to the change in length.
As an example, we calculate the response, in the frequency domain, of a 40-nm-radius gold nanoparticle to an impulse strain in the metal because of the pulsed laser excitation. The thermal strain generates a force that sets the particle in motion. The phonon dynamics can be calculated by solving Navier’s equation, which governs linear elastodynamics in an isotropic medium:
where λ and μ are Lamé’s first and second parameters, ρ is the density, u is the displacement vector, F is the force generated by the thermal strain in the metal, εthermal=αΔT, and α is the coefficient of thermal expansion. We solve this equation in the frequency domain with continuity of displacement and stress at the interface between materials.
We now sketch out the solution for a model system: a spherical gold nanoparticle in an infinite glass matrix as shown in Supplementary Fig. 9b. With spherical symmetry, Navier’s equation simplifies to45:
where νp is the longitudinal (p-wave) speed of sound and Fr(ω) is the radial force in the frequency domain for a thermal strain46: Fr(ω)=(3λ+2μ)αΔT.
We solve for the displacement as a function of frequency and position analytically and with the finite element method using COMSOL Multiphysics. We see excellent agreement between the two methods for the radial displacement magnitude (Supplementary Fig. 9b) as a function of frequency at the surface of the sphere. In addition, we see excellent agreement in the displacement as a function of the distance from the centre of the sphere at the resonance frequency (Supplementary Fig. 9c). The region inside of the nanoparticle is highlighted in gold and the glass is coloured blue.
The oscillations in the glass indicate acoustic energy flow away from the particle. We note that the materials were considered to be lossless and both methods show a broad resonance (Q~10) because of radiation damping. For the finite element method simulations, we use a perfectly matched layer to simulate an infinite medium. The material parameters used in the calculations are listed in Supplementary Table 1.
For the Swiss-Cross nanostructures, an analytic solution is not available; therefore, we use the finite element method to simulate the dynamics.
How to cite this article: O’Brien, K. et al. Ultrafast acousto-plasmonic control and sensing in complex nanostructures. Nat. Commun. 5:4042 doi: 10.1038/ncomms5042 (2014).
Scholl, J. A., Koh, A. L. & Dionne, J. A. Quantum plasmon resonances of individual metallic nanoparticles. Nature 483, 421–427 (2012).
Kauranen, M. & Zayats, A. V. Nonlinear plasmonics. Nat. Photonics 6, 737–748 (2012).
Grady, N. K. et al. Terahertz metamaterials for linear polarization conversion and anomalous refraction. Science 340, 1304–1307 (2013).
Novotny, L. & van Hulst, N. Antennas for light. Nat. Photonics 5, 83–90 (2011).
Thomsen, C. et al. Coherent phonon generation and detection by picosecond light pulses. Phys. Rev. Lett. 53, 989–992 (1984).
Hartland, G. V. Optical studies of dynamics in noble metal nanostructures. Chem. Rev. 111, 3858–3887 (2011).
Brüggemann, C. et al. Laser mode feeding by shaking quantum dots in a planar microcavity. Nat. Photonics 6, 30–34 (2012).
Temnov, V. V. Ultrafast acousto-magneto-plasmonics. Nat. Photonics 6, 728–736 (2012).
Clark, J. N. et al. Ultrafast three-dimensional imaging of lattice dynamics in individual gold nanocrystals. Science 341, 56–59 (2013).
Fainstein, A., Lanzillotti-Kimura, N. D., Jusserand, B. & Perrin, B. Strong optical-mechanical coupling in a vertical GaAs/AlAs microcavity for subterahertz phonons and near-infrared light. Phys. Rev. Lett. 110, 037403 (2013).
Perner, M. et al. Observation of hot-electron pressure in the vibration dynamics of metal nanoparticles. Phys. Rev. Lett. 85, 792–795 (2000).
Kelf, T. A. et al. Mapping gigahertz vibrations in a plasmonic–phononic crystal. New J. Phys. 15, 023013 (2013).
Zijlstra, P., Tchebotareva, A. L., Chon, J. W. M., Gu, M. & Orrit, M. Acoustic oscillations and elastic moduli of single gold nanorods. Nano Lett. 8, 3493–3497 (2008).
Temnov, V. V. et al. Active magneto-plasmonics in hybrid metal–ferromagnet structures. Nat. Photonics 4, 107–111 (2010).
Sönnichsen, C. et al. Drastic reduction of plasmon damping in gold nanorods. Phys. Rev. Lett. 88, 077402 (2002).
Hohlfeld, J., Müller, J. G., Wellershoff, S.-S. & Matthias, E. Time-resolved thermoreflectivity of thin gold films and its dependence on film thickness. Appl. Phys. B 65, 681–681 (1997).
O’Connell, A. D. et al. Quantum ground state and single-phonon control of a mechanical resonator. Nature 464, 697–703 (2010).
Safavi-Naeini, A. H. et al. Electromagnetically induced transparency and slow light with optomechanics. Nature 472, 69–73 (2011).
Verhagen, E., Deléglise, S., Weis, S., Schliesser, A. & Kippenberg, T. J. Quantum-coherent coupling of a mechanical oscillator to an optical cavity mode. Nature 482, 63–67 (2012).
Garfinkel, M., Tiemann, J. J. & Engeler, W. E. Piezoreflectivity of the noble metals. Phys. Rev. 148, 695–706 (1966).
Juvé, V. et al. Probing elasticity at the nanoscale: terahertz acoustic vibration of small metal nanoparticles. Nano Lett. 10, 1853–1858 (2010).
Schumacher, T. et al. Nanoantenna-enhanced ultrafast nonlinear spectroscopy of a single gold nanoparticle. Nat. Commun. 2, 333 (2011).
Haus, H. & Huang, W.-P. Coupled-mode theory. Proc. IEEE 79, 1505–1518 (1991).
Cole, G. D., Wilson-Rae, I., Werbach, K., Vanner, M. R. & Aspelmeyer, M. Phonon-tunnelling dissipation in mechanical resonators. Nat. Commun. 2, 231 (2011).
Carpene, E. Ultrafast laser irradiation of metals: beyond the two-temperature model. Phys. Rev. B 74, 024301 (2006).
Conforti, M. & Della Valle, G. Derivation of third-order nonlinear susceptibility of thin metal films as a delayed optical response. Phys. Rev. B 85, 245423 (2012).
Kor, S. K., Tandon, U. S. & Rai, G. Ultrasonic attenuation in copper, silver, and gold. Phys. Rev. B 6, 2195–2197 (1972).
Pelton, M. et al. Damping of acoustic vibrations in gold nanoparticles. Nat. Nanotechnol. 4, 492–495 (2009).
Ruijgrok, P. V., Zijlstra, P., Tchebotareva, A. L. & Orrit, M. Damping of acoustic vibrations of single gold nanoparticles optically trapped in water. Nano Lett. 12, 1063–1069 (2012).
Berweger, S., Atkin, J. M., Xu, X. G., Olmon, R. L. & Raschke, M. B. Femtosecond nanofocusing with full optical waveform control. Nano Lett. 11, 4309–4313 (2011).
Aeschlimann, M. et al. Adaptive subwavelength control of nano-optical fields. Nature 446, 301–304 (2007).
Hu, M. et al. Vibrational response of nanorods to ultrafast laser induced heating: theoretical and experimental analysis. J. Am. Chem. Soc. 125, 14925–14933 (2003).
Petrova, H. et al. Time-resolved spectroscopy of silver nanocubes: Observation and assignment of coherently excited vibrational modes. J. Chem. Phys. 126, 094709 (2007).
Crowell, C. R., Spitzer, W. G., Howarth, L. E. & LaBate, E. E. Attenuation length measurements of hot electrons in metal films. Phys. Rev. 127, 2006–2015 (1962).
Juhasz, T., Elsayed-Ali, H. E., Smith, G. O., Suárez, C. & Bron, W. E. Direct measurements of the transport of nonequilibrium electrons in gold films with different crystal structures. Phys. Rev. B 48, 15488–15491 (1993).
Rabitz, H., Vivie-Riedle, R., de, Motzkus, M. & Kompa, K. Whither the future of controlling quantum phenomena? Science 288, 824–828 (2000).
Koehl, W. F., Buckley, B. B., Heremans, F. J., Calusine, G. & Awschalom, D. D. Room temperature coherent control of defect spin qubits in silicon carbide. Nature 479, 84–87 (2011).
Brinks, D. et al. Visualizing and controlling vibrational wave packets of single molecules. Nature 465, 905–908 (2010).
Nelson, K. A., Miller, R. J. D., Lutz, D. R. & Fayer, M. D. Optical generation of tunable ultrasonic waves. J. Appl. Phys. 53, 1144–1149 (1982).
Arbouet, A., Del Fatti, N. & Vallee, F. Optical control of the coherent acoustic vibration of metal nanoparticles. J. Chem. Phys. 124, 144701 (2006).
Li, Q. et al. Generation and control of ultrashort-wavelength two-dimensional surface acoustic waves at nanoscale interfaces. Phys. Rev. B 85, 195431 (2012).
Bartels, A., Dekorsy, T., Kurz, H. & Köhler, K. Coherent control of acoustic phonons in semiconductor superlattices. Appl. Phys. Lett. 72, 2844–2846 (1998).
Siemens, M. E. et al. Quasi-ballistic thermal transport from nanoscale interfaces observed using ultrafast coherent soft X-ray beams. Nat. Mater. 9, 26–30 (2010).
Minnich, A. J. et al. Thermal conductivity spectroscopy technique to measure phonon mean free paths. Phys. Rev. Lett. 107, 095901 (2011).
Verma, P., Cordts, W., Irmer, G. & Monecke, J. Acoustic vibrations of semiconductor nanocrystals in doped glasses. Phys. Rev. B 60, 5778–5785 (1999).
Landau, L. D. & Lifshitz, E. M. Theory of Elasticity Elsevier (1986).
This work was supported by the US Department of Energy under Contract No. DE-AC02-05CH11231. J.R. acknowledges a fellowship from the Samsung Scholarship Foundation, Republic of Korea.
The authors declare no competing financial interests.
About this article
Cite this article
O’Brien, K., Lanzillotti-Kimura, N., Rho, J. et al. Ultrafast acousto-plasmonic control and sensing in complex nanostructures. Nat Commun 5, 4042 (2014). https://doi.org/10.1038/ncomms5042
Journal of Nanoparticle Research (2018)
Large optical nonlinearity of ITO nanorods for sub-picosecond all-optical modulation of the full-visible spectrum
Nature Communications (2016)
Nonlinear optical observation of coherent acoustic Dirac plasmons in thin-film topological insulators
Nature Communications (2016)
Nature Communications (2015)