The field of plasmonics has emerged as an interesting area for fundamental studies, with important application possibilities in miniaturized photonic components. Plasmonic crystals are of particular relevance because of large field enhancements and extraordinary transmission that arise from plasmonic interactions between periodic arrays of metallic elements. Here we report methods to enhance and modify the plasmonic resonances in such structures by strongly coupling them to optical modes of Fabry–Perot type cavities. First, we illustrate a type of plasmonic, narrow-band (~15 nm), high-contrast (>20 dB) absorber and an opto-fluidic modulator based on this component. Second, we use optimized samples as substrates to achieve strong amplification (>350%) and modulation (>4×) of surface-enhanced Raman scattering from surface-bound monolayers. Cavity-coupling strategies appear to be useful not only in these two examples, but also in applications of plasmonics for optoelectronics, photovoltaics and related technologies.
Surface plasmons are coherent oscillations of electrons at metal-dielectric interfaces that can exist either in localized or propagating forms1. Such electromagnetic disturbances can be exploited for wide-ranging applications, from biological and chemical sensors based on changes in near-surface refractive index or Raman scattering2, to devices for sub-wavelength manipulation of light3, wave-guiding4, optical modulation5, Bragg reflection6, photo detection7,8, lasers9 and solar energy generation10. Methods to modify plasmonic interactions by controlling the shapes and sizes of the metal structures,11,12 the types of metals13,14 or the indices of refraction of the surrounding materials2,15 are firmly established. Newer approaches integrate plasmonic components into equivalent circuit structures such as metal–insulator–metal stacks16,17,18.
Here we report a different strategy in which light transmitted through a quasi-three-dimensional (quasi-3D) plasmonic crystal strongly couples with an underlying, Fabry–Perot cavity. We show that, in certain configurations, this arrangement leads to strongly enhanced or diminished reflections (~23 dB change), due to significant modifications in the nature of the plasmonic modes, in a way that can be tuned reversibly using the techniques of opto-fluidics. Associated amplification in the surface plasmon field can also be exploited, to increase signal levels in surface-enhanced Raman scattering (SERS) experiments, by up to ~350% and to modulate SERS signals (>4×) in ways that are not possible with other known techniques. We capture all of these effects in a quantitative way by finite-difference time-domain (FDTD) electromagnetic modelling and systematic experiments. The design possibilities enabled by these ideas, especially when implemented using simple, large-area soft-imprint lithography techniques, lead to new classes of photonic/plasmonic components.
Cavity-coupled plasmonic crystal system
The structures are formed by first imprinting a square array of sub-wavelength cylindrical depressions19,20,21 on the surface of a thin polymer film cast on a glass substrate coated with a layer of gold. Blanket deposition of a thin layer of gold on the imprinted surface of the polymer completes the fabrication. Here a two-dimensional plasmonic crystal, formed by the top gold coating, optically couples to an array of isolated disks of gold in the bottoms of the cylindrical depressions. Light transmitted through this 'quasi-3D' crystal via plasmonic coupling between the nanoholes and recessed disks22 coherently reflects from the back mirror (that is, the layer of gold on glass) which in turn, influences the plasmonic resonances, constructively or destructively depending on the cavity length.
Figure 1 shows a large area (5 mm×5 mm) optical image (Fig. 1a) and a schematic illustration (Fig. 1b) of the plasmonic crystal–optical cavity system. A scanning electron microscope (SEM) top view image appears in Figure 1c, along with a magnified view of an individual nanohole/nanodisk (Fig. 1d). Figure 1e presents a cross-sectional SEM image and a schematic illustration (Fig. 1f) of a unit cell, showing the top gold film with a square lattice of circular holes, recessed circular gold disks (with some gold on the sidewalls near the base) and the gold back reflector (HBR). The choice of nanohole period, P=740 nm, and diameter, D=500 nm, maximizes the strengths of localized surface plasmon resonances (LSPRs) of interest for present purposes20. This system embeds two asymmetric Fabry–Perot cavities, both with the thick gold as a back reflector: one formed by the gold in the raised regions of the top surface (Cavity (I)) and the other by the gold in the recessed regions (Cavity (II)). The lengths of these two cavities are related by the depth of moulded relief (HRD), as shown in Figure 1f.
The geometries of the depressions, the thicknesses of the gold layers and the indices of the surrounding dielectric media (air and polymer) define the wavelengths of the LSPRs. The optical cavities strongly modify these resonances. Figure 2a shows the far-field reflectivity spectra measured experimentally and computed by FDTD, for a cavity-coupled plasmonic crystal with L1=1,170 nm and HBR=200 nm, along with FDTD results for a case without the cavity (that is, HBR=0 nm). The cavity clearly enhances the LSPR resonance that appears in the wavelength range 780–900 nm, as manifested by a strong, sharp dip in the reflection at ~845 nm. The long-wavelength region (1.5–6 μm), which lies away from the plasmonic resonances, shows unmodulated cavity modes, due to the combined effects of Cavity (I) and Cavity (II) (Supplementary Fig. S1). To reveal further features, Figure 2b shows computed variations in the electric field intensity (|Ē|2) spatially averaged across a conformal surface that extends over a unit cell of the plasmonic crystal at a position 10 nm above the raised and recessed regions of the gold layers, as a function of cavity length (L1) and the excitation wavelength, with all other structure parameters fixed, except for L2, which changes according to L2=L1−HRD. The results show that the plasmon resonances bend and repeat with changes in L1, as they come into and out of overlap with the cavity modes (Supplementary Figs S2 and S3). As might be expected, the cavity length and refractive index of the dielectric layer influence the effective optical-path lengths and, therefore, the positions of the cavity-mode resonances. By contrast, the index of the surroundings predominantly affects only the plasmonic component of the responses. Figure 2c shows the FDTD-computed variation of the far-field reflection as a function of this index, for a structure with L1=1,170 nm. Here the LSPR, initially near 850 nm, moves to higher wavelengths with increasing index, hence reducing field enhancements due to de-tuning away from the cavity resonance. The phenomenon repeats because of overlap between the shifted LSPR and another cavity mode at an index of ~1.22 at a wavelength ~885 nm. The nature of the coupling is clearly visible in the cross-sectional intensity distributions of Figure 2d, computed using FDTD for linearly polarized light at a wavelength of 850 nm for air (n=1) as the surrounding medium. Specifically, the main plasmonic resonance is strongly enhanced when L1 is 1,170 or 1,990 nm and when L1 is 1,090 or 1,890 nm, due to the presence of standing waves (that is, cavity modes) corresponding to the action of Cavity (I) and Cavity (II), respectively. For reference, when L1=1,300 nm, no cavity mode is present and no enhancement results. The cross-sectional intensity distribution for HBR=0 (that is, non-cavity case) at L1=1,090 nm provides further evidence of the importance of the cavity (Supplementary Fig. S2).
Narrow-band plasmonic absorber/filter and opto-fluidic modulator
There are several ways to exploit the behaviours illustrated in Figure 2. The physics that governs the responses of these structures is different than that associated with absorbers that use other types of plasmonic structures and metamaterials23,24,25. The remarkably strong absorption and narrow-band operation reported here represent appealing features for applications in tunable filters, substrates for SERS, and other devices, as described in the following. In a first example, we demonstrate a class of narrow-band absorber, or reflective notch filter, and a modulator based on this component. The underlying effect is that light can be either nearly completely absorbed or completely reflected, depending on cavity lengths, by virtue of cavity controlled excitation of LSPRs on the gold surfaces. Figure 3a shows the variation of far-field reflection as a function of wavelength for L1=710 nm and 920 nm. The former configuration results in an enhanced plasmonic resonance and low far-field reflection, which we label as the 'Absorption ON' state. The latter corresponds to a suppressed plasmonic resonance and high far-field reflection, that is 'Absorption OFF'. Coupling between LSPR modes and standing waves in the Fabry–Perot cavity originates from coherent interference effects. When the cavity produces constructive (destructive) interference near the surface of the structure, the fields available to excite LSPR modes are maximized (minimized), and the resonance is thereby enhanced (suppressed). For example, when L1=710 nm, the round trip phase delay from propagation in the cavity is ~4π for the wavelength, λ=857 nm, that coincides with the main LSPR. In this scenario, constructive interference occurs, thereby enhancing the LSPR. Similarly, for L1=920 nm, the phase delay is ~5π, destructive interference obtains, and the LSPR is suppressed. These outcomes are apparent in the results of Figure 3a, where the transmission dip associated with the LSPR is large and small for L1=710 nm and 920 nm, respectively. The measured bandwidth (15 nm, FWHM) and depth of the resonant dip in reflection at λ=857 nm closely match FDTD predictions. Figure 3b shows top (X–Y) and cross-sectional (X–Z) views of the intensity distributions. The 'Absorption ON' case shows a complex coupled Cavity (II) type mode, whereas the 'Absorption OFF' configuration indicates an absence of cavity effects. These two states also appear in characteristic features of Figure 2b (white vertical dashed lines on the left, at L1=710 and 920 nm). This structure, then, represents an unusual optical component, with absorption properties that can be designed by appropriate choice of cavity dimensions. The position of the plasmonic absorption band depends strongly on the geometry of the plasmonic crystal (for example, P, D)9 and the intrinsic properties of the gold. Alternative metals can provide further flexibility in design13. When viewed as a reflective filter, the extinction coefficient (>−25 dB) and bandwidth (~15 nm) of this three-layer plasmonic device are comparable to parameters that require, in a multilayer dielectric thin film Bragg structures, at least 20 alternating quarter-wave stacks with low index contrast (Δn ~0.05–0.1) plus a half-wave defect layer followed by another 20-layer quarter wave stack26.
An extra attractive aspect of this type of cavity-coupled plasmonic component is that its properties can be tuned, dynamically, by changing either the dimensions or index of refraction of the cavity. For example, adjusting the cavity index by amounts (~5–10%) achievable with organic electro-optic materials27 can accomplish complete switching (Supplementary Fig. S4). An alternative, and simpler, mode of tuning involves changing the surrounding refractive index, using effects summarized in Figure 2c. Figure 4a shows, as a demonstration, reflection spectra collected from a sample with L1=710 nm, switched between ON (−25 dB) and OFF (2 dB) states at λ0=857 nm by replacing the surrounding air with ethanol (n=1.3614). The techniques of opto-fluidics allow this type of switching to be achieved in an integrated manner. Figure 4b shows a schematic illustration (left) and picture (right) of a device consisting of micro channel created by the contact of an embossed elastomer against a substrate that supports a cavity-coupled plasmonic structure. Optical images of this plasmonic crystal system in air and immersed in ethanol, collected in reflection mode through a narrow band bandpass filter (815–885 nm), appear in Figure 4c. Significant changes in brightness correspond to large differences in reflectivity between the air and ethanol cases. These changes occur uniformly over the entire imaged area, as expected based on the high quality of samples formed by soft imprint lithography procedures. Using a syringe pump, the surrounding material can be switched from ethanol to air, and back again, in a reversible manner. Here the LSPR, initially near 857 nm, moves to higher wavelengths because of the increased index of the surroundings. As a result, the LSPR and cavity modes are no longer in resonance, thereby eliminating the enhancement effects. The process operates in a reversible manner such that the reflectivity goes down to its original value as the surrounding medium is switched from ethanol back to air, as shown in Figure 4d. The same channel system allows more systematic study with different liquids having refractive indices between 1.36–1.5. The change in reflectivity at λ0=857 nm as a function of refractive index appears in Figure 4e; FDTD results indicate a linear variation with index up to ~Δn=0.15, after which the absorption saturates to its OFF-state value.
Cavity-induced enhancement and deep modulation of SERS
In a different application example, the enhanced field strengths associated with cavity-coupled plasmonics (Fig. 2b) can be exploited to improve performance in SERS-based sensors. To demonstrate this possibility, we examined scattering from a monolayer of benzenethiol formed on samples like the one of Figure 1c, using linearly polarized excitation light at λEx=785 nm. Figure 5a shows measured 'Raman counts' (Rc) for 3 cases, all with L1=850 nm, but with 3 different values for HBR: 0, 15 and 200 nm. The spectra show expected signatures for benzenethiol, but with signal enhancements, defined as Enh(L1, HBR)=Rc(L1, HBR)/Rc(L1, HBR=0), of ~350% and ~200% for the bands at 1,574 and 1,073 cm−1, respectively. This outcome is consistent with the physics summarized in Figure 2. Figure 5b shows the average intensity computed by FDTD on a conformal surface 10 nm above top and bottom Au layer for HBR=200 nm and L1=850 nm, where benzenethiol is considered as the surrounding medium. The dominant local maximum observed in this plot is identified as an LSPR. The wavelengths of the Raman peaks are λRaman1=857 nm and λRaman2=896 nm. The LSPR resonance (λLSPR) spans across wavelengths that lie halfway between λEx and λRaman, for both peaks, thereby simultaneously satisfying the approximate requirement (λLSPR≈(λEx+λRaman)/2) for maximum SERS enhancement1,28,29. Figure 5c shows the measured variation of enhanced Raman counts at λRaman2, as a function of HBR, together with FDTD-computed values of normalized field intensity squared (ENor4) where ENor=|EaveBR|/|EaveBR=0|, spatially averaged at 10 nm away from the surfaces, as in the other cases, at a wavelength of 850 nm, normalized to a structure with HBR=0, all with L1=850 nm. The experimental and FDTD results show remarkably good agreement, thereby providing confirmation of the cavity-related physics and origins of SERS signals.
The plasmon resonances can be constructively or destructively influenced by cavity modes. Figure 5d shows the result of this effect on the SERS measurement, in which the enhancement in Raman counts for λRaman2 appears as a function of cavity length for constant HBR=200 nm. As with Figure 5c, the Raman counts and FDTD-computed average values of |E|4, again normalized to the case where HBR=0, exhibit good agreement. The results show SERS signals that follow cavity-coupling effects discussed previously in the context of Figure 2b. The ability to control the response over a range of >4×, including strong amplification (that is, 350% increase) by adjusting only the cavity length is a notable outcome of the physics. Further optimized structures and materials offer promise for achieving even larger effects.
This collective set of results indicates that simple strategies for coupling optical cavities to plasmonic modes can induce responses with practical interest in photonics and sensing. The out-of-plane cavities and the quasi-3D plasmonic crystals presented here are not the only types of structures that can be configured in this way. Arrays of metallic particles, waveguide resonators, in-plane cavities and many other possibilities also appear interesting to consider. A broad consideration of these layouts, together with other materials, in homogeneous or heterogeneous configurations, represent directions for future work.
Plasmonic cavity fabrication
Large area (5 mm×5 mm) square arrays of sub-wavelength cylindrical depressions were moulded onto the surface of a thin layer of a photo curable epoxy (SU8, MicroChem), using the techniques of solvent-assisted soft imprint lithography, wherein a small amount of ethanol was used to wet the epoxy surface before pressing the substrate against a poly(dimethylsiloxane) (PDMS, 10:1 Sylgard 184) mould containing the inverse pattern. The thickness of the epoxy was controlled through dilution of SU8 photoresist in cyclopentanol and conditions for the spin-coating process. A gold-coated glass substrate served as the substrate. Blanket deposition of a thin layer of gold (~50 nm) by electron beam evaporation completed the fabrication process.
The opto-fluidic system was created with a piece of a PDMS with suitable structures of relief on its surface, formed by casting and curing against a pattern of photoresist on a silicon wafer. Contacting the PDMS against a substrate that supports a cavity-coupled plasmonic crystal led to the formation of a liquid-tight seal, thereby establishing a microfluidic channel. Liquid was injected into the channel, through tubes inserted into inlets machined through the thickness of the PDMS, using a syringe pump. For refractive index sensing, we used ethanol (n=1.3614), tetrahydrofuran (n=1.4072), chloroform (n=1.4458) and toluene (n=1.4969).
The detailed FDTD model of the actual structure of Figure 1e appears in Supplementary Figure S5 where Cavity (I) and Cavity (II) lengths are L1, L2 and the back reflector, top and bottom gold layer, relief depth, side wall height and thicknesses are HBR, Htop, Hbottom, HRD, Hsidewall and tsidewall, respectively. A Drude plus two-pole Lorentzian model for the complex frequency-dependent gold permittivity was employed, with parameters fit to empirical dielectric constant data30. The structure was excited with linearly polarized, plane-wave light. Here we used FDTD to 'fit' our transmission data as shown in Supplementary Figure S6, and then used that model, with those fitted parameters, to explore various trends and effects with cavity length, index and back reflector thicknesses. To establish correspondence between experiment and modelling (Supplementary Fig. S5), transmission through two different geometries, one with no back reflector (HBR=0) and one with a thin back reflector (HBR=15 nm), were compared, both with L1=710 nm and HRD=360 nm. We then varied Htop between 45–55 nm, Hbottom between 45–55 nm, Hsidewall between 90–120 nm, and tsidewall between 10–25 nm, in an iterative fashion, to yield a good match between experiment and modelling. The best fit was found for constant L1=710 nm, HRD=360 nm and Htop=50 nm, Hbottom=40 nm, Hsidewall=100 nm, and tsidewall=15 nm thicknesses. A final optimization was then performed by varying L1 by ±20 nm to yield a 'best' fit to study the effects of cavity length on LSPR keeping all other parameters constant. In all cases, the magnitudes of variations explored for each parameter were within uncertainties in physical measurements (ellipsometer, SEM). The transmission through the fabricated structure and FDTD model (Supplementary Fig. S5), for two different geometries, one non-cavity geometry having no back reflector (HBR=0) and the other one with cavity geometry having a thin back reflector (HBR=15 nm), were compared for constant L1=710 nm, HRD=360 nm, Htop=50 nm, Hbottom=40 nm, Hsidewall=100 nm and tsidewall=15 nm. Supplementary Figure S6a,b shows experimental as well as FDTD-predicted 0-th order transmissions of these two structures, respectively. It can be observed that for the given set of experimentally measured thicknesses, FDTD predictions of transmissions through these two structures matches well with experimental observations. To emulate the actual SERS experimental procedures in FDTD simulation, a 5-nm thick Benzenethiol layer was created on nanohole surface and similar mapping of cavity length versus plasmon resonance was computed. As expected, we observed red-shift of plasmon resonances when the sample is coated with Benzenethiol having higher refractive index (n=1.588) than air.
Far-field reflection measurements
Reflection spectra were collected using a ×2.5, 0.07 numerical objective on an optical microscope (Hyperion 2000) coupled to a Fourier transform infrared spectrometer (Vertex 70) and outfitted with a spatial aperture having a diameter of 3.75 mm. Reflection spectra were normalized to a silver mirror with 96% reflectivity over the wavelengths examined.
Raman spectra were acquired using a confocal Raman microscope (Senterra, Bruker Optics) with a 75-mm focal-length achromatic lens for both illumination and collection, in place of a microscope objective. The diameter of the pinhole aperture was set to 50 μm. For all measurements, the spectral region from 400–1,800 cm−1 was collected with 3–5 cm−1 spectral resolution. The laser power at the sample was 33 mW with a spot size of 95 μm. The acquisition times were 30 s for all measurements. The sample was illuminated with linearly polarized laser light with a wavelength of 785 nm. The laser beam filled an 2 mm region on the back aperture of the achromatic lens, corresponding to an angular incidence of illumination with a numerical aperture of ~0.02. Data processing of Raman spectra was achieved using OPUS 6.5 (Bruker), including background corrections to account for the dark current response and quantum efficiency of the charge-coupled detector device. Wavelength calibration was also accomplished using OPUS 6.5 to adjust the Raman shift using the atomic emission spectrum of mixed neon and argon gases.
How to cite this article: Chanda, D. et al. Coupling of plasmonic and optical cavity modes in quasi-three-dimensional plasmonic crystals. Nat. Commun. 2:479 doi: 10.1038/ncomms1487 (2011).
Maier, S. A. Plasmonics: Fundamentals and Applications (Springer, 2007).
Homola, J. Surface plasmon resonance sensors for detection of chemical and biological species. Chem. Rev. 108, 462–493 (2008).
Bozhevolnyi, S. I., Volkov, V. S., Devaux, E., Laluet, J. Y. & Ebbesen, T. W. Channel plasmon subwavelength waveguide components including interferometers and ring resonators. Nature 440, 508–511 (2006).
Chen, L., Shakya, J. & Lipson, M. Subwavelength confinement in an integrated metal slot waveguide on silicon. Opt. Lett. 31, 2133–2135 (2006).
Pacifici, D., Lezec, H. J. & Atwater, H. A. All-optical modulation by plasmonic excitation of CdSe quantum dots. Nat. Photonics 1, 402–406 (2007).
Ditlbacher, H., Krenn, J. R., Schider, G., Leitner, A. & Aussenegg, F. R. Two-dimensional optics with surface plasmon polaritons. Appl. Phys. Lett. 81, 1762–1764 (2002).
Tang, L., Latif, S. & Miller, D. A. B. Plasmonic device in silicon CMOS. Electron. Lett. 45, 706–708 (2009).
Rosenberg, S., Shenoi, R. V., Vandervelde, T. E., Krishna, S. & Painter, O. A multispectral and polarization-selective surface-plasmon resonant midinfrared detector. Appl. Phys. Lett. 95, 161101 (2009).
Perahia, R., Alegre, T. P. M., Safavi-Naeini, A. H. & Painter, O. Surface-plasmon mode hybridization in subwavelength microdisk lasers. Appl. Phys. Lett. 95, 201114 (2009).
Atwater, H. A. & Polman, A. B. Plasmonics for improved photovoltaic devices. Nat. Mat. 9, 205–213 (2006).
Lassiter, J. B. et al. Fano resonances in plasmonic nanoclusters: geometrical and chemical tunability. Nano Lett. 10, 3184–3189 (2010).
Fan, J. A. et al. Self-assembled plasmonic nanoparticle clusters. Science 328, 1135–1138 (2010).
Langhammer, C., Schwind, M., Kasemo, B. & Zorić, I. Localized surface plasmon resonances in aluminum nanodisks. Nano Lett. 8, 1461–1471 (2008).
Sherry, L. J., Chang, S., Schatz, G. C. & Duyne, R. P. V. Localized surface plasmon resonance spectroscopy of single silver nanocubes. Nano Lett. 5, 2034–2038 (2005).
Stewart, M. E. et al. Nanostructured plasmonic sensors. Chem. Rev. 108, 494–521 (2008).
Choi, Y., Choi, D. & Lee, L. P. Metal–insulator–metal optical nanoantenna with equivalent-circuit analysis. Adv. Mater. 22, 1754–1758 (2010).
Xu, T., Wu, Y., Luo, X. & Guo, L. J. Plasmonic nanoresonators for high-resolution colour filtering and spectral imaging. Nat. Commun. 1, 59 (2010).
Diest, K., Dionne, J. A., Spain, M. & Atwater, H. A. Tunable color filters based on metal-insulator-metal resonators. Nano Lett. 9, 2579–2583 (2009).
Malyarchuk, V. et al. High performance plasmonic crystal sensor formed by soft nanoimprint lithography. Opt. Express 13, 5669–5675 (2005).
Baca, A. J. et al. Molded plasmonic crystals for detecting and spatially imaging surface bound species by surface-enhanced Raman scattering. Appl. Phys. Lett. 94, 243109 (2009).
Lee, M. H., Huntington, M. D., Zhou, W., Yang, J. & Odom, T. W. Programmable soft lithography: solvent-assisted nanoscale embossing. Nano Lett. 11, 311–315 (2010).
Stewart, M. E. et al. Quantitative multispectral biosensing and 1D imaging using quasi-3D plasmonic crystals. Proc. Natl Acad. Sci. USA 103, 17143–17148 (2006).
Landy, N. I., Sajuyigbe, S., Mock, J. J., Smith, D. R. & Padilla, W. J. Perfect metamaterial absorber. Phys. Rev. Lett. 100, 207402 (2008).
Kravets, V. G., Schedin, F. & Grigorenko, A. N. Plasmonic blackbody: almost complete absorption of light in nanostructured metallic coatings. Phys. Rev. B 78, 205405 (2008).
Hu, C., Zhao, Z., Chen, X. & Luo, X. Realizing near-perfect absorption at visible frequencies. Opt. Express 17, 11039–11044 (2009).
Yariv, A. & Pochi, Y. Photonics: Optical Electronics in Modern Communications, 6th edn (Oxford University Press, 2007).
Geis, W. et al. Fabrication of crystalline organic waveguides with an exceptionally large electro-optic coefficient. Appl. Phys. Lett. 84, 3729–3731 (2004).
Reilly, T. H., Chang, S., Corbman, J. D., Schatz, G. C. & Rowlen, K. L. Quantitative evaluation of plasmon enhanced Raman scattering from nanoaperture arrays. J. Phys. Chem. C 111, 1689–1694 (2007).
Chu, Y., Banaee, M. G. & Crozier, K. B. Double-resonance plasmon substrates for surface-enhanced Raman scattering with enhancement at excitation and stokes frequencies. ACS Nano 4, 2804–2810 (2010).
Gray, S. K. & Kupka, T. Propagation of light in metallic nanowire arrays: finite-difference time-domain studies of silver cylinders. Phys. Rev. B 68, 045415 (2003).
The work at University of Illinois was supported by a grant from the Office of Naval Research. We thank Audrey M. Bowen for providing photoresist masters for the opto-fluidic chips.
The authors declare no competing financial interests.
About this article
Cite this article
Chanda, D., Shigeta, K., Truong, T. et al. Coupling of plasmonic and optical cavity modes in quasi-three-dimensional plasmonic crystals. Nat Commun 2, 479 (2011). https://doi.org/10.1038/ncomms1487
Graphene Plasmonic Crystal: Two-Dimensional Gate-Controlled Chemical Potential for Creation of Photonic Bandgap
Light: Science & Applications (2018)
Ultra-broadband Tunable Resonant Light Trapping in a Two-dimensional Randomly Microstructured Plasmonic-photonic Absorber
Scientific Reports (2017)
Effect of Surface Plasmon Coupling to Optical Cavity Modes on the Field Enhancement and Spectral Response of Dimer-Based sensors
Scientific Reports (2017)