Protein-based biogenic materials provide important inspiration for the development of high-performance polymers. The fibrous mussel byssus, for instance, exhibits exceptional wet adhesion, abrasion resistance, toughness and self-healing capacity–properties that arise from an intricate hierarchical organization formed in minutes from a fluid secretion of over 10 different protein precursors. However, a poor understanding of this dynamic biofabrication process has hindered effective translation of byssus design principles into synthetic materials. Here, we explore mussel byssus assembly in Mytilus edulis using a synergistic combination of histological staining and confocal Raman microspectroscopy, enabling in situ tracking of specific proteins during induced thread formation from soluble precursors to solid fibres. Our findings reveal critical insights into this complex biological manufacturing process, showing that protein precursors spontaneously self-assemble into complex architectures, while maturation proceeds in subsequent regulated steps. Beyond their biological importance, these findings may guide development of advanced materials with biomedical and industrial relevance.
How do living organisms fabricate complex polymeric materials from proteins? In systems from silk to tendon to hagfish slime, answering this complex question has the potential to transform the way humans manufacture polymers. Unlike current polymer processing methods, biological organisms employ bottom-up biomolecular assembly processes to produce a broad range of elaborate nano- and micro-architectured proteinaceous materials, the structural complexity of which is linked to their impressive performance1,2,3. However, there are still enormous gaps in our knowledge of the processing steps involved in the manufacture of complex biomolecular architectures and the relative roles of active and passive assembly processes. This mainly stems from the exceptional technical challenges inherent to observing in situ the rapid, localized processes in living biological tissues as they occur. In the present study, we overcome these obstacles by utilizing an innovative experimental approach combining traditional histology and confocal Raman spectroscopic imaging to investigate assembly of the byssus of marine mussels (Mytilus edulis).
The mussel byssus is a high-performance fibrous anchor that provides a hedge against dislodgement from crashing waves and hungry predators (Fig. 1)4. The byssus represents an ideal model system for investigating biofabrication due to the fact that it is acellular, it assembles and functions outside the body, its formation can be artificially induced to study active assembly processes5 and because a great deal is already known about byssus protein composition, structure and function6,7,8. Importantly, development of polymers inspired by the mussel byssus is a fast-emerging field8; however, as of yet, these polymers do not match the structural or mechanical complexity of the natural archetype – providing the potential for significant future advances if byssus biofabrication is understood.
A single byssal thread consists of three regions – the core, cuticle and plaque – that are integrated into a cohesive macroscopic fibre, yet possess completely distinct compositions, structural organization and functions (Fig. 1)6,7,8. The byssus core is an energy damping fibrous biopolymer comprised of a semi-crystalline array of collagenous proteins known as preCols (refs 9, 10). The core possesses an initial stiffness comparable to vertebrate tendon (nearly 900 MPa in some species)11; however, due to distinctive non-collagenous preCol domains, it is far more tough and extensible, and most notably, exhibits intrinsic self-healing capacity during cyclic loading12,13. The cuticle, which surrounds the stretchy core, is thought to play a protective role against abrasion due to its unusual combination of high hardness (H=100 MPa for Mytilus galloprovincialis similar to an engineering epoxy) and high extensibility (ɛult=70–100%)14. The cuticle exhibits a granular morphology resembling that of a particle-reinforced composite14,15 and is composed largely of mussel foot protein-1 (mfp-1), a repetitive protein rich in a rare post-translational modification of tyrosine called 3,4-dihydroxyphenylalanine (DOPA), which forms metal coordination cross-links with Fe3+ ions that contribute more than 80% of the material stiffness and hardness16. The plaque, which is also composed of a number of DOPA-rich proteins (mfp-2, -3, -4, -5 and -6) organized into an open-cell foam17, is able to adhere under wet conditions to almost any surface chemistry with enough strength to resist the forces produced by crashing waves–a feat unmatched by current industrial glues8.
The byssus as a whole functions as an effective anchoring holdfast due to the characteristic material properties of the core, cuticle and plaque, which are dependent on the exact localization, organization and cross-linking of specific protein building blocks into complex hierarchical structures across many length scales6,7,8. Remarkably, each byssal thread is formed in a 3–5 min process, in which more than 10 different types of protein building blocks are secreted and assembled ex vivo (Fig. 1)7,18. Currently, however, the mechanistic understanding of this dynamic assembly process is extremely limited and has advanced little in the last 30 years, aside from recent elegant studies on the formation of the plaque adhesive interface19,20. The little we do know about this process is principally based on histological and transmission electron microscopy (TEM) investigations, which identified three secretory glands within the mussel foot, each with vesicles of distinctive shape, size and texture5,21,22,23,24,25. During thread assembly, these three glands, which have accumulated an excessive number of names over time, presumably secrete the 11 known protein building blocks of the byssus26. However, there has been little direct correlation between the proteins identified in the threads and those present in the glands. At this point, we know only the ingredients and not the full recipe: it remains unclear how the protein building blocks assemble into native thread structure and cross-link within minutes.
Here, we reconcile the decades-old concept of byssus assembly ‘machinery’ with the current well-established understanding of byssus structure-function relationships by using traditional histological studies to guide cutting-edge confocal Raman microspectroscopy. Armed with this novel approach, we first localize byssus proteins in the foot tissue glands and then track morphological and chemical changes as they transit from soluble precursors to solid materials during artificially induced thread formation. Our findings reveal a biological workflow of regulated and non-regulated steps: spontaneous self-assembly of complex micro- and nano-scale biomolecular architectures from specific protein building blocks, followed by biologically controlled steps that function during thread maturation (for example, cross-link formation, macroscale molecular alignment). These insights into the byssus manufacturing process clarify the complementary roles and interactions of physically driven versus biologically controlled processing steps in natural material fabrication, with clear potential implications for the production of man-made polymers.
Histological staining of foot glands
Byssal threads are produced by a specialized organ called the mussel foot (Figs 1 and 2, Supplementary Movie 1). The tongue-shaped foot from M. edulis is 1–1.5 cm in length in the resting state, but during thread assembly can extend several times its original length (Fig. 1a,b). The ventral groove is a trench-like channel running from the base to the tip along the topside of the foot, where it terminates into a small divot, known as the distal depression (Fig. 1b). The ventral groove provides the mold in which the core and cuticle are formed, whereas the distal depression is the site of plaque formation18. Aside from the musculature, the bulk of the foot tissue is comprised of secretory glands surrounding the ventral groove and distal depression, in which the thread proteins are stored in secretory vesicles (Figs 1b and 2).
A key first step in elucidating the dynamic byssus assembly process is the localization of specific byssus proteins in the different foot glands (Table 1). For this purpose, mussel foot cryo-sections were treated with histological stains with affinities for certain byssus proteins (Fig. 2). For example, we utilized two common stains for connective tissues–namely, Masson’s trichrome and Sirius red–as preCols, comprising the majority of the thread core by weight, are ∼50% collagen by sequence10. Masson’s trichrome stains collagen bright blue and most other proteins red27, whereas Sirius red stains collagen bright red with high specificity and enhances birefringence of aligned collagen molecules in polarized light microscopy (PLM)28. Because most of the cuticle and plaque proteins contain elevated concentrations of DOPA (Table 1), foot sections were also treated with nitro-blue tetrazolium chloride (NBT)-glycinate stain, which turns dark blue in the presence of quinone moieties (for example, oxidized DOPA)29 and was previously used to identify DOPA-rich proteins in mussel foot extractions30.
Trichrome stained transverse cryo-sections of the distal mussel foot (Fig. 2a) revealed three glands with distinct staining signatures, similar in location to descriptions given in previous studies5,21,22,23. We provide evidence, however, that directly links the protein contents of each of the three glands to the core, cuticle or plaque of the thread. As gland names from previous studies26 have little correspondence to the functional roles we demonstrate in this study (Table 1), we designate the glands here as the core, cuticle and plaque glands, respectively, and use these names throughout the paper (Fig. 2a, Table 1).
Serial stained cryo-sections made along the entire mussel foot every 200 μm were digitally reconstructed into a high-resolution three-dimensional rendering, where each gland is arbitrarily assigned a specific colour that will be used throughout the paper (Fig. 2b, Supplementary Fig. 1). The plaque gland (shown in green; formerly phenol gland or purple gland) is localized near the distal depression, where the plaque is formed5. The core gland (blue; formerly collagen gland or white gland), believed to form the fibrous inner region of the thread22,23,24, is present along the entire length of the foot and comprises the largest volume. The cuticle gland(s) (red; formerly enzyme gland or accessory gland), which was originally thought to contain enzymes necessary for thread sclerotization23,31, but is now believed to form the cuticle25, is interdigitated with the core gland, confined to two thin strips on either side of the ventral foot groove. This three-dimensional (3D) rendering presents a more accurate and detailed depiction than previous hand-drawn illustrations21,22, but also provides a critical roadmap for the Raman imaging experiments described in the next sections.
Each gland contains specific secretory vesicles with distinctive sizes and morphologies, shown in Fig. 2a. The ovoid core gland vesicles stain bright blue with Masson’s trichrome and bright red with Sirius red, indicating the presence of collagenous proteins, likely the preCols27,28. The underlying cytoplasmic material is identified by its light pink colour, while fibrous collagen in the connective tissue also stains red, but is easily differentiated from the vesicles10. Strong birefringence in PLM indicates that the collagenous molecules in the core vesicles are well-aligned (Fig. 2d,h), which is consistent with previous TEM micrographs5,24 and supports the hypothesis that preCols are stored as a smectic liquid crystalline phase (that is, a fluid phase in which molecules are aligned as books on a shelf)7,32,33.
In contrast to the core vesicles, the spherical cuticle and plaque vesicles contain non-collagenous proteins that are not well-aligned, based on the fact that they stain red with Masson’s trichrome, do not stain with Sirius red and do not exhibit birefringence (Fig. 2c–j). Consistent with previous TEM studies23,25, the spherical vesicles of the plaque gland have a larger diameter (1–2 μm) than the cuticle gland vesicles (0.5–1 μm; Fig. 2a). Core, plaque and cuticle vesicles all stained positive with the NBT-glycinate assay indicating the presence of quinone moieties, likely arising from oxidized DOPA-containing proteins (Fig. 2f,j). Notably, however, the core gland vesicles stained the darkest with NBT, followed by the plaque gland and the cuticle gland. This was unexpected considering that the preCol and TMP-1 proteins thought to be in the core vesicles have a lower DOPA content (1–5 mol%) compared to the proteins comprising the cuticle (15 mol%) and plaque (between 2 and 30 mol%) (Table 1). However, because the intensity of NBT-glycinate staining depends on the amount of the oxidized quinone form of DOPA29,34 and not just total DOPA content, we posit that the cuticle and plaque vesicles may possess lower levels of DOPA oxidation, perhaps the result of different local conditions. In support, there is strong evidence that in the plaque secretion, the oxidation of DOPA is actively hindered both by the low ambient pH∼2 (ref. 35) and the presence of the thiol-rich anti-oxidant protein mfp-6 (refs 20, 36); however, verification of this hypothesis, also in the other vesicle types, requires further investigation.
Raman spectroscopy of foot glands
Histology provides important determination of the boundaries of glands and localization of their vesicles in the mussel foot. To obtain specific chemical and structural information about proteins within the glands, we utilized confocal Raman microspectroscopy, a form of vibrational spectroscopy that has been critical for elucidating structure-function relationships in the native byssus15,37. Here, Raman measurements enabled acquisition of spectral fingerprints from protein molecules in the foot tissue with sub-micron resolution. The combination of spectroscopic and histological maps of the foot enables assignment of specific byssus proteins to the different vesicles – information, which is crucial for studying dynamic assembly processes.
Because Raman measurements must be performed on unstained sections in which it is difficult to identify specific glands, an adjacent serial section from the same mussel foot was first stained with Sirius red to locate regions of interest at the core/plaque gland and core/cuticle gland interfaces (Fig. 3a,c). Raman spectra were acquired from each pixel of analogous regions of interest in the unstained serial section with 0.5 μm resolution. Examination of individual spectra from the Raman maps revealed distinctive spectral fingerprints in different regions, consistent with both collagenous proteins (for example, core proteins) and Tyr-rich proteins (for example, cuticle and plaque proteins). By integrating the intensity of Raman bands specific for collagenous proteins and Tyr-rich proteins in each spectrum, we generated composite two-dimensional maps showing their localization in the image–essentially, creating a spectroscopic histological image (Fig. 3b,d). Notably, spectra of collagen versus Tyr-rich proteins showed analogous distribution to staining patterns for the core gland and the cuticle/plaque glands, respectively, in adjacent Sirius red-stained sections, thus validating the approach. From these maps, averaged Raman spectra of the three different vesicles and underlying tissue were extracted (Fig. 3e), establishing the chemical identity of each gland’s vesicles.
By comparing the specific features of the Raman spectra from the different vesicles, we can extract important information about the biochemistry and structure of the contents and, by linking this to the existing knowledge of thread proteins, the destiny of the vesicles in the thread manufacture process. All major bands observed in the Raman spectra from the three vesicle types are consistent with a primarily proteinaceous composition, especially the amide I (1,630–1,700 cm−1) and amide III (1,200–1,350 cm−1) bands, which provide information about protein backbone conformation38,39. All three gland spectra indicate extended backbone structure based on their similar amide I band position (∼1,667 cm−1); however, a higher degree of conformational order in the proteins of the core gland is indicated by the sharper peak shape38. Variations in the relative intensities of the four roughly defined peaks present in the amide III band (∼1,243, 1,269, 1,315 and 1,340 cm−1) also indicate protein structural differences. Specifically, core gland proteins exhibit a primarily collagen triple helical or β-sheet conformation consistent with known preCol secondary structures40,41 based on the higher intensity of the peaks at 1,243 and 1,269 cm−1 relative to the other two peaks. In contrast, a less ordered protein conformation in the plaque and cuticle vesicles is indicated by the lower relative intensity of these peaks39,42,43. In light of the histological evidence, the Raman measurements confirm the presence of aligned preCol proteins in the core vesicles and are consistent with the predicted structural disorder of the plaque and cuticle proteins (that is, mfp-1 – mfp-6)44.
Aside from being disordered, the proteins that comprise the plaque and cuticle are distinctive because of their elevated composition of the amino acid tyrosine (Tyr), some of which is post-translationally converted to DOPA (Table 1)8. Thus, based on the notable Tyr (1,615 cm−1, a doublet at 829 and 850 and 643 cm−1) and DOPA (785 cm−1) Raman peaks observed in the respective spectra, we deduce the presence of DOPA-rich proteins and their precursors in the cuticle (mfp-1) and plaque (mfp-2–6) vesicles. Furthermore, the additional presence of the amino acid phenylalanine (Phe) in plaque vesicles based on the strong peak at 1,006 cm−1 specifically indicates the presence of mfp-2, which is the most abundant component of the plaque foam37.
Considering that interactions between DOPA residues and metal ions in the plaque and cuticle are critical for byssus function15,37, the absence in plaque and cuticle vesicle spectra of the distinctive and intense DOPA-metal resonance Raman peaks characteristic of the native plaque and cuticle15,37 is highly conspicuous, especially considering that both glands stained positive for DOPA with NBT (Fig. 2f,j). Because of the extremely high sensitivity of this Raman resonance signal to even very small amounts of DOPA-metal complexes over a large pH range45, we conclude that the metal ions that normally interact with DOPA in native thread cuticle and plaque (for example, Fe and V)16 are not stored together with the DOPA-rich proteins in the gland vesicles. In fact, it was previously predicted that cuticle and plaque proteins would not be stored together with metal ions, based on the observation that DOPA residues in purified plaque proteins undergo spontaneous oxidation and covalent cross-linking, when mixed in vitro with Fe3+ under acidic conditions similar to those in the secretory vesicles35,46. This has important implications for the way that the plaque and cuticle assemble, which will be discussed later.
Tracking thread assembly with induced threads
The combined histological and Raman-based investigations of the vesicles bridge older TEM/histological studies with more recent biochemical investigations of byssus proteins; however, they still present a very static perspective of assembly. To obtain a more dynamic view, we employed our combined histological/Raman spectroscopic approach to investigate artificially induced thread formation, which can be achieved by injecting 0.56 M KCl into the pedal nerve at the base of the foot5,47, leading to muscle contraction and vesicle secretion into the foot groove (Fig. 4a). This procedure was recently exploited to investigate the adhesive secretion in various mussel species19,20. Figure 4b shows that induced threads are severely morphologically impaired compared to native threads. Considering that the foot is essentially paralyzed during induction, we assume, as previous authors have17, that induced thread formation represents spontaneous rather than biologically regulated aspects of the assembly process. By investigating artificially induced thread formation, we are able to observe transport and changes in microstructure of vesicles (via histological staining), as well as chemical and nano-structural changes in byssal thread proteins (via Raman spectroscopy) as vesicle-bound soluble precursors transition to organized tissues. Whereas examination of induced thread formation provides information about unregulated self-assembly of byssal proteins, comparison with native threads highlights biologically regulated steps, allowing dissection of the relative contributions of biological versus physicochemical forces driving byssus manufacture.
By flash freezing dissected mussel feet within 5–10 min after induction with KCl, we were able to capture the thread formation process in progress (in comparison, previous studies collected fully formed induced threads after 30 min47). Trichrome-stained cryo-sections from within the ventral groove and from the distal depression of induced feet reveal formation of a nascent induced thread in which core and cuticle (Fig. 4c) and core and plaque (Fig. 4d) assembly are observed. Notably, the individual secretory vesicles in both regions can be seen coalescing to form tissues with microstructured morphologies resembling native thread tissues (Fig. 4c,d), indicating that much of the complexity of byssal thread tissue architecture is formed by unregulated and spontaneous self-assembly. The fact that vesicles coalesce only within the ventral groove or distal depression and not in the glands where they are densely packed supports the hypothesis that the physical conditions (for example, pH, ionic strength) within the groove help initiate assembly7,32,33,35. In the following sections, we address assembly of the induced core, cuticle and plaque separately and at a higher resolution, as a means of elucidating the finer scale aspects of composition and structure relevant for byssus fabrication.
The native byssal thread core consists of a semi-crystalline array of preCol molecules aligned over a length scale of centimeters9, leading to strong birefringence in PLM (Fig. 5c). The induced thread core also exhibits birefringence (Fig. 5d); however, it is patchy and restricted to regions of tens of microns, suggesting that local self-assembly of preCols into nano-architectured arrays is spontaneous, likely dictated by the liquid crystalline pre-ordering of molecules in the secretory vesicles24,32,33, whereas longer scale molecular ordering requires biologically regulated processing. Compared to the Raman spectra of the induced thread core, native thread core spectra indicate an increased content of collagen and/or β-sheet conformation based on the higher relative intensity of amide III bands at 1,240 and 1,270 cm−1 and the presence of a shoulder at ∼1,630 cm−1 in the amide I band42,43 (Fig. 5e). Furthermore, polarized Raman spectra of induced threads also indicate lower molecular alignment of preCol proteins within the induced threads relative to native threads based on the smaller dependence of laser polarization on the intensity of the amide I band (Supplementary Fig. 2).
These data suggest that induced thread formation lacks certain regulated steps critical for attaining native preCol conformation and alignment. Fibrous biological materials, such as silk and collagen, require careful control of ambient conditions (pH and ionic strength) or application of mechanical forces to attain native structure48,49. Along these lines, peptides based on terminal preCol cross-linking domains were found to undergo a sudden transition from disordered to highly ordered protein structure when brought from the acidic pH at which the preCols are thought to be stored (pH ∼4) up to the slightly basic pH of seawater (pH ∼8)50. This suggests that proper core self-assembly may depend on changes in the ambient environment during protein secretion.
Given that the foot is essentially paralyzed during the thread induction, it is highly feasible that mechanical forces are also necessary to facilitate proper folding and alignment of preCol molecules (for example, from peristaltic foot contractions or mechanical loading) as suggested by Waite18. In fact, careful observation of the natural formation process reveals that the mussel foot undergoes distinct muscular contractions during thread formation and immediately prior to releasing the nascent thread from the foot groove (Supplementary Movie 1). The role of mechanical force in aligning preCols during assembly is also supported by studies showing that dilute solutions of purified preCol proteins can be easily hand-drawn into aligned fibres32,51. Similarly, poly-aramid polymer fibre formation from liquid crystalline solutions also requires mechanical drawing, with the degree of alignment and mechanical performance closely correlated to the draw ratio (that is, the degree to which it is pre-stretched during fabrication)52,53. In any case, while our findings do support an important role for the liquid crystalline pre-organization of preCol molecules for self-assembly, this alone is clearly not sufficient to create centimetre scale ordered polymer fibres.
In native threads, the fibrous core is sheathed by the protective cuticle, which exhibits a knobby structure comprised of hard granules embedded in a softer matrix material, shown to be critical to the cuticle’s hard, yet extensible material performance (Fig. 6a)14,15. Our histological investigations provide evidence that the cuticle vesicles spontaneously coalesce into a continuous, granular surface layer on the induced core resembling a native thread (Fig. 6b,c). Notably, the cuticle vesicles begin coalescing within the ventral groove then spread over the surface of the already assembled core, indicating a clear temporal sequence of assembly. This also suggests that a specific interaction between core and cuticle vesicles might initiate assembly of the thin cuticle and that cuticle vesicle clusters may possess a low interfacial energy allowing them to spread in a fluid environment; however, presently almost nothing is known about the core-cuticle interface of native threads.
Whereas Raman spectra from cuticle vesicles and induced cuticles are rather similar, the spectrum of the native thread cuticle is strikingly dissimilar, due primarily to the presence of strong DOPA-metal coordination resonance bands (Fig. 6d). DOPA-metal interactions are critical load-bearing cross-links in the cuticle that account for more than 80% of its stiffness and hardness16. Thus, their notable absence in the induced thread cuticle indicates that during native thread assembly, a separate step must occur, whereby metals are infiltrated into the already assembled cuticle. Coalescence of cuticle vesicles in the absence of metal ions is contrary to the current hypothesis that DOPA-metal interactions are necessary for cuticle assembly45. This is a critical finding of this study, since the protein-metal co-mixing hypothesis provides the basis of current methods for producing mussel-inspired DOPA-rich metallopolymers45,54.
The byssal thread plaque has received the most attention from researchers due to its key role in mediating underwater adhesion, which if mimicked successfully, would precipitate a number a breakthroughs in technical and biomedical applications (for example, surgical adhesives)8. The native plaque has a complex micro- and nano-porous architecture resembling an open-cell foam (Fig. 7a), which is believed to be a critical design feature contributing to byssus toughness and adhesive strength17. The plaque is comprised of at least five protein families (Table 1) that are spatially arranged through a temporal sequence of secretion19,55, with certain plaque proteins secreted directly at the surface where they initiate adhesion (mfp-3, mfp-5 and mfp-6), whereas others comprise the foamy interior (mfp-2 and mfp-4)8. Additionally, preCol fibres from the core are anchored into the plaque foam, creating finger-like extensions (Fig. 7a). Although previous scanning electron microscopy-based studies indicated that plaque nano-structure is not present in induced threads forcibly removed from the mussel foot17, we observed with histological staining of cryo-sectioned induced mussel feet that the spherical plaque vesicles spontaneously coalesce within the distal depression into a tissue with a distinctive foamy microstructure resembling the native thread plaque (Fig. 7b). Furthermore, the highly intricate, branched plaque-core interface forms spontaneously as the plaque and core vesicles interact (Fig. 7b).
Raman mapping of the plaque (Fig. 7c) reveals that the core and plaque vesicles do not mix as they coalesce – rather, they remain completely separate, with distinctive Raman spectra resembling those obtained from the core and plaque glands (Fig. 7e). The immiscibility of the core and plaque proteins is noteworthy and consistent with the hypothesis that they are stored in densely packed phases (for example, liquid crystal32,33 and coacervate56, respectively). Notably, the characteristic root-like morphology of the interface qualitatively resembles the phenomenon of viscous finger formation57, suggesting a difference in the viscosity of the phases and likely also their interfacial energies. Regardless of the mechanism, the spontaneous self-assembly of this complex interface likely plays a critical role in anchoring the core into the plaque as the vesicles coalesce and then solidify.
In addition to the morphological transformation observed in the plaque vesicles during plaque formation, a concomitant molecular level transformation is indicated by Raman spectral analysis of the intensity ratio of the two peaks of the Tyr doublet (I850/I830), which provides information about the local environment of Tyr residues present in the plaque proteins58. The increase in the I850/I830 ratio from 1.1 in the plaque vesicles to 1.7 in the induced plaque tissue indicates that Tyr residues transition from a primarily hydrophobic to a hydrophilic environment during thread formation58. This suggests that a significant conformational transformation in the plaque proteins accompanies the physical transition from a fluid vesicular phase to a solid open-cell foam, which may be relevant to the hypothesis that plaque proteins are stored in vivo as dense fluid phases, known as coacervates56. However, this possibility must be further investigated.
Comparison of induced and native plaque foam Raman spectra both reveal the presence of a strong Phe signal (1,006 cm−1) indicating that mfp-2 is a major component; however, the similarities end there (Fig. 7d). As with the native cuticle, the native plaque spectrum is dominated by resonance Raman bands for DOPA-metal coordination, whereas these are clearly absent in induced plaque spectra. This indicates that the vesicle-bound proteins comprising the plaque spontaneously self-assemble into a complex foamy architecture without metal coordination, contradicting existing hypotheses of byssus assembly7,45. Rather, it appears that the tendency to self-assemble is a function of the environment and structure of the proteins and that metals are added in a later finishing step (as with the cuticle), to fortify the foamy structure with intermolecular cross-links37. In fact, it seems likely that premature metal binding would hamper proper assembly of such complex hierarchical structures and, as recently shown with bio-inspired adhesives, would interfere with DOPA-based adhesion to surfaces59. Future studies will focus on better understanding how and when metal ions are introduced into the native byssus.
Integrative model of byssus assembly
The rapid fabrication of mussel byssus hierarchical structure is an extraordinary feat of sustainable bottom-up manufacturing, which offers an excellent model system for investigating biological material assembly. Our findings indicate that spatially organized vesicles in the mussel foot containing pre-packaged byssal thread precursor proteins spontaneously coalesce and self-assemble into elaborate biomolecular micro- and nano-architectures during thread biofabrication. Integrating the insights gained from our novel experimental approach with what is already known about byssal thread structure-function relationships, we propose a model of the thread assembly process, illustrated in Fig. 8.
The most important finding from the current work is the clear indication that a significant portion of the byssus assembly process is governed by basic chemical and physical phenomena–including viscosity differences, interfacial tension and liquid crystalline alignment – which can be distilled and transferred readily to the lab bench56. On the other hand, careful comparison of induced versus native thread structure and chemistry reveals that additional biologically regulated steps are also required for thread curing and maturation. For example, centimetre scale alignment of preCols in the core may require physical loading of fibres to align liquid crystal domains, similar to what occurs in the processing of silk48 or poly-aramid fibres52,53. In addition, mechanical fortification of the thread via protein-metal interactions plausibly proceeds via infiltration of metal ions following structural assembly, similar to cuticle sclerotization in certain arthropods60, but in stark contrast to current methods of fabricating mussel-inspired metallopolymers45,54. This multi-step curing process – reminiscent of the way a baker defines bread’s internal structure by kneading and shaping the dough before baking the loaf – may be a subtle, but critical feature of the biofabrication process for achieving the remarkable structural organization and material performance of the byssus.
The interplay of physically and biologically driven processing steps in byssus formation has much to teach us about how to rapidly manufacture high-performance polymers with complex hierarchical structure under environmentally friendly conditions. These insights are especially relevant in the rapidly growing field of mussel-inspired polymers8,45,54, but are also broadly applicable. Once the physicochemical driving forces of assembly are better understood, for example, the fluid-to-solid transformation of byssal thread vesicles and subsequent time-dependent cross-linking in a physiological environment could inspire the development of injectable, self-assembling soft matter scaffolds (for example, for tissue repair or drug delivery61,62,63). Additionally, the phenomenon proposed for core-plaque interface formation, involving self-structuring of immiscible phases with different viscosities, could guide creation of complex 3D compositional and structural gradients at the interfaces of two polymeric materials. In this respect, the current study provides not only new insights into a complex and fascinating biological process, but also lays important foundation for the manufacture of next-generation polymeric material.
Blue mussels (M. edulis) from the North Sea were purchased and maintained at 16 °C in an aquarium with artificial salt water. Experiments were performed in accordance with regulations of the European commission. For histological and Raman spectroscopic investigation, adult mussels of 5–8 cm length were used. Whole feet were dissected from mussels and either immediately mounted in OCT medium (VWR International) and frozen in isopentane pre-cooled with liquid nitrogen (for Raman spectroscopy) or fixed in 4% paraformaldehyde overnight before freezing (for histological staining). Using a cryo microtome (Microm HM 560) at −18 °C, 5 μm sections of frozen mussel feet were cut and then post-fixed with methanol or Buin’s solution depending on the staining procedure. To investigate the dynamic thread formation process, thread production was induced by injecting a 0.56 M KCl solution in the base of the foot, as described previously in the literature5,47. Mussel feet were dissected between 5 and 10 min following induction and treated as described above to capture thread formation in progress. Histological and Raman spectroscopic investigations were each performed on eight different individual mussels with reproducible results.
Histological staining on cryo-sections of native and induced mussel feet was performed using three different stains – namely, Sirius red, Masson’s Trichrome and NBT. Sirius red staining, which is specific for collagen, was performed according to previous protocols28 in which sections were stained for 1 h in 0.1% solution of Sirius red in saturated picric acid and then washed in 0.5% acetic acid. Staining with Masson’s Trichrome (Sigma Aldrich) was performed according to the manufacturer’s protocol, which involved staining sections stepwise in separate solutions of Weigert’s Iron Hematoxylin, Biebrich Scarlet-Acid Fuchsin, phosphomolybdic-phosphotungstic acid and aniline blue (5 min in each solution). NBT-glycinate staining, which is used traditionally to detect the presence of quinone groups (for example, oxidized DOPA residues) was performed by incubating sections in a freshly made solution of NBT (0.2 mg ml−1) in 2 M potassium glycinate (pH 10) for 40 min in the dark at room temperature, according to existing protocols29. Following staining, all sections were washed in water, dehydrated through an ascending alcohol series, cleared in Roti-Histol and mounted in Canada balsam.
3D model of byssus gland distribution
To construct a 3D model of gland localization in mussel feet, cryo-sections of a single mussel foot were cut every 200 μm along the length of a foot and subsequently stained with Masson’s trichrome to distinguish the different glands. Using Adobe Photoshop the individual glands in the image files of each section were digitally highlighted with different grey values. The isoSurf software (version 1.5d by Graham Treece) was used to interpolate between sections generating a 3D object of the mussel foot and its glands. This 3D object was further processed with Amira software64 (Amira ZIB edition 2016.14, Zuse Institute Berlin). The steps of the reconstruction are illustrated in Supplementary Fig. 1.
For the microCT-scan, a whole foot was dissected from a mussel, fixed in 4% paraformaldehyde overnight and stained in Lugol’s solution (3.4 mg ml−1 iodine (I2) and 6.8 mg ml−1 potassium iodide) for 1 day. Scans were performed using a laboratory microCT (Skyscan-1072) at 80 keV, with an effective pixel size of 10 μm.
Raman spectroscopy of mussel tissue and induced threads was performed on dried and unstained mussel foot cryo-sections (5 μm thickness) before and after induction with KCl. A green laser (Nd:YAG laser, λ=532 nm) was focused using a Confocal Raman Microscope (Alpha300, Witec, Ulm, Germany) equipped with a piezo scanner (P-500, Physik Instrumente, Karlsruhe, Germany). The scattered light was detected by a thermoelectrically cooled CCD detector (DU401A-BV, Andor, Belfast, North Ireland) placed behind the spectrometer (UHTS 300, WITec, Ulm, Germany). At least five spectra from different spots inside one gland were collected with an integration time of 60 s using a 100 × objective (Nikon, numerical aperture (NA)=0.9) and averaged. Image scans were performed at an integration time of 5 s per point. To measure the orientation of proteins in the induced thread core, image scans with polarization angles of 0° (perpendicular of the fibre axis) and 90° (parallel to the fibre axis) of the incident laser light were performed at an integration time of 3 s per point. The native core of a byssal thread was measured using hydrated 5 μm sections, and spectra from different spots were collected with an integration time of 60 s using a 60 × objective (Nikon, NA=0.8). Raman spectra of the native plaque and native cuticle were measured using hydrated 20 μm-thick thread sections; however, due to high fluorescence using the green laser, a near-infrared laser (λ=785 nm, Toptica Photonics AG, Graefelfing, Germany) was used in combination with a confocal Raman microscope (CRM200, WITec, Ulm, Germany) and a 60 × objective (Nikon, NA=0.8). The spectra were acquired using a CCD detector (PI-MAX, Princeton Instruments Inc., Trenton, NJ) placed behind a spectrograph (Acton, Princeton Instruments Inc., Trenton, NJ). ScanCtrlSpectroscopyPlus software (version 1.60, Witec) was used for collecting data and the OPUS software (Bruker, Germany) for spectral processing of all Raman data.
The data supporting the findings of this study are available from the authors upon reasonable request.
How to cite this article: Priemel, T. et al. Rapid self-assembly of complex biomolecular architectures during mussel byssus biofabrication. Nat. Commun. 8, 14539 doi: 10.1038/ncomms14539 (2017).
Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Cranford, S. W., de Boer, J., van Blitterswijk, C. & Buehler, M. J. Materiomics: an-omics approach to biomaterials research. Adv. Mater. 25, 802–824 (2013).
Fratzl, P. & Weinkamer, R. Nature's hierarchical materials. Prog. Mater. Sci. 52, 1263–1334 (2007).
Keten, S., Xu, Z., Ihle, B. & Buehler, M. J. Nanoconfinement controls stiffness, strength and mechanical toughness of beta-sheet crystals in silk. Nat. Mater. 9, 359–367 (2010).
Denny, M. W. & Gaylord, B. Marine ecomechanics. Ann. Rev. Mar. Sci. 2, 89–114 (2010).
Tamarin, A., Lewis, P. & Askey, J. Structure and formation of byssus attachment plaque in Mytilus. J. Morphol. 149, 199–221 (1976).
Carrington, E., Waite, J. H., Sara, G. & Sebens, K. P. Mussels as a model system for integrative ecomechanics. Ann. Rev. Mar. Sci. 7, 443–469 (2015).
Degtyar, E., Harrington, M. J., Politi, Y. & Fratzl, P. The mechanical role of metal ions in biogenic protein-based materials. Angew. Chem. Int. Ed. 53, 12026–12044 (2014).
Lee, B. P., Messersmith, P. B., Israelachvili, J. N. & Waite, J. H. Ann. Rev. Mater. Res. 41, 99–132 (2011).
Krauss, S., Metzger, T. H., Fratzl, P. & Harrington, M. J. Self-repair of a biological fiber guided by an ordered elastic framework. Biomacromolecules 14, 1520–1528 (2013).
Waite, J. H., Qin, X. X. & Coyne, K. J. The peculiar collagens of mussel byssus. Matrix Biol. 17, 93–106 (1998).
Gosline, J. et al. Elastic proteins: biological roles and mechanical properties. Philos. Trans. R. Soc. Lond. B Biol. Sci. 357, 121–132 (2002).
Reinecke, A., Bertinetti, L., Fratzl, P. & Harrington, M. J. Cooperative behavior of a sacrificial bond network and elastic framework in providing self-healing capacity in mussel byssal threads. J. Struct. Biol. 196, 329–339 (2016).
Schmitt, C. N. Z., Politi, Y., Reinecke, A. & Harrington, M. J. Role of sacrificial protein-metal bond exchange in mussel byssal thread self-healing. Biomacromolecules 16, 2852–2861 (2015).
Holten-Andersen, N., Fantner, G. E., Hohlbauch, S., Waite, J. H. & Zok, F. W. Protective coatings on extensible biofibres. Nat. Mater. 6, 669–672 (2007).
Harrington, M. J., Masic, A., Holten-Andersen, N., Waite, J. H. & Fratzl, P. Iron-clad fibers: a metal-based biological strategy for hard flexible coatings. Science 328, 216–220 (2010).
Schmitt, C. N. Z. et al. Mechanical homeostasis of a DOPA-enriched biological coating from mussels in response to metal variation. J. R. Soc. Interface 12, 20150466 (2015).
Filippidi, E. et al. The microscopic network structure of mussel (Mytilus) adhesive plaques. J. R. Soc. Interface 12, 20150827 (2015).
Waite, J. H. The formation of mussel byssus: anatomy of a natural manufacturing process. Results Probl. Cell Differ. 19, 27–54 (1992).
Petrone, L. et al. Mussel adhesion is dictated by time-regulated secretion and molecular conformation of mussel adhesive proteins. Nat. Commun. 6, 8737 (2015).
Yu, J. et al. Mussel protein adhesion depends on interprotein thiol-mediated redox modulation. Nat. Chem. Biol. 7, 588–590 (2011).
Brown, C. H. Some structural protein of Mytilus edulis. Q. J. Microsc. Sci. 93, 487–502 (1952).
Pujol, J. P. Formation of byssus in common mussel (Mytilus edulis). Nature 214, 204 -& (1967).
Tamarin, A. & Keller, P. J. Ultrastructural study of byssal thread forming system in Mytilus. J. Ultrastruct. Res. 40, 401–416 (1972).
Vitellaro-Zuccarello, L. The collagen gland of Mytilus galloprovincialis: an ultrastructural and cytochemical study on secretory granules. J. Ultrastruct. Res. 73, 135–147 (1980).
Vitellaro-Zuccarello, L. Ultrastructural and cytochemical study on the enzyme gland of the foot of a mollusk. Tissue Cell 13, 701–713 (1981).
Silverman, H. G. & Roberto, F. F. in Biological Adhesive Systems eds Von Byern J., Grunwald I. 273–283Springer (2010).
Lillie, R. D. Further experiments with the Masson trichrome modification of Mallory's connective tissue stain. Stain Technol. 15, 17–22 (1940).
Junqueira, L. C. U., Bignolas, G. & Brentani, R. R. Picosirius staining plus polarization microscopy, a method for collagen detection in tissue sections. Histochem. J. 11, 447–455 (1979).
Paz, M. A. et al. Specific detection of quinoproteins by redox-cycling staining. J. Biol. Chem. 266, 689–692 (1991).
Benedict, C. V. & Waite, J. H. Location and analysis of byssal structural proteins of Mytilus edulis. J. Morphol. 189, 171–181 (1986).
Smyth, J. D. A technique for the histochemical demonstration of polyphenol oxidase and its application to egg-shell formation in helminths and byssus formation in Mytilus. Q. J. Microsc. Sci. 95, 139–152 (1954).
Harrington, M. J. & Waite, J. H. pH-dependent locking of giant mesogens in fibers drawn from mussel byssal collagens. Biomacromolecules 9, 1480–1486 (2008).
Hassenkam, T., Gutsmann, T., Hansma, P., Sagert, J. & Waite, J. H. Giant bent-core mesogens in the thread forming process of marine mussels. Biomacromolecules 5, 1351–1354 (2004).
Flückiger, R., Paz, M. A. & Gallop, P. M. Redox-cycling detection of dialyzable pyrroloquinoline quinone and quinoproteins. Methods Enzymol. 258, 140–149 (1995).
Rodriguez, N. R. M., Das, S., Kaufman, Y., Israelachvili, J. N. & Waite, J. H. Interfacial pH during mussel adhesive plaque formation. Biofouling 31, 221–227 (2015).
Nicklisch, S. C. T., Spahn, J. E., Zhou, H., Gruian, C. M. & Waite, J. H. Redox capacity of an extracellular matrix protein associated with adhesion in Mytilus californianus. Biochemistry 55, 2022–2030 (2016).
Hwang, D. S. et al. Protein- and metal-dependent interactions of a prominent protein in mussel adhesive plaques. J. Biol. Chem. 285, 25850–25858 (2010).
Lefevre, T., Paquet-Mercier, F., Rioux-Dube, J.-F. & Pezolet, M. Structure of silk by raman spectromicroscopy: from the spinning glands to the fibers. Biopolymers 97, 322–336 (2012).
Monti, P., Freddi, G., Bertoluzza, A., Kasai, N. & Tsukada, M. Raman spectroscopic studies of silk fibroin from Bombyx mori. J. Raman Spectrosc. 29, 297–304 (1998).
Arnold, A. A. et al. Solid-state NMR structure determination of whole anchoring threads from the blue mussel Mytilus edulis. Biomacromolecules 14, 132–141 (2013).
Harrington, M. J., Gupta, H. S., Fratzl, P. & Waite, J. H. Collagen insulated from tensile damage by domains that unfold reversibly: in situ X-ray investigation of mechanical yield and damage repair in the mussel byssus. J. Struct. Biol. 167, 47–54 (2009).
Frushour, B. G. & Koenig, J. L. Raman scattering of collagen, gelatin and elastin. Biopolymers 14, 379–391 (1975).
Wopenka, B., Kent, A., Pasteris, J. D., Yoon, Y. & Thomopoulos, S. The tendon-to-bone transition of the rotator cuff: a preliminary Raman spectroscopic study documenting the gradual mineralization across the insertion in rat tissue samples. Appl. Spectrosc. 62, 1285–1294 (2008).
Hwang, D. S. & Waite, J. H. Three intrinsically unstructured mussel adhesive proteins, mfp-1, mfp-2, and mfp-3: analysis by circular dichroism. Protein Sci. 21, 1689–1695 (2012).
Holten-Andersen, N. et al. pH-induced mussel metal-ligand cross-links yield self-healing polymer networks with near-covalent elastic moduli. Proc. Natl Acad. Sci. USA 108, 2651–2655 (2011).
Fullenkamp, D. E., Barrett, D. G., Miller, D. R., Kurutz, J. W. & Messersmith, P. B. pH-dependent cross-linking of catechols through oxidation via Fe3+ and potential implications for mussel adhesion. RSC Adv. 4, 25127–25134 (2014).
Sagert, J. & Waite, J. H. Hyperunstable matrix proteins in the byssus of Mytilus galloprovincialis. J. Exp. Biol. 212, 2224–2236 (2009).
Heim, M., Keerl, D. & Scheibel, T. Spider silk: from soluble protein to extraordinary fiber. Angew. Chem. Int. Ed. 48, 3584–3596 (2009).
Mouw, J. K., Ou, G. & Weaver, V. M. Extracellular matrix assembly: a multiscale deconstruction. Nat. Rev. Mol. Cell Biol. 15, 771–785 (2014).
Reinecke, A., Brezesinski, G. & Harrington, M. J. pH-responsive self-organization of metal-binding protein motifs from biomolecular junctions in mussel byssus. Adv. Mater. Interfaces 4, 1600416 (2017).
Harrington, M. J. & Waite, J. H. How nature modulates a fiber's mechanical properties: mechanically distinct fibers drawn from natural mesogenic block copolymer variants. Adv. Mater. 21, 440–444 (2009).
Picken, S. J., Sikkema, D. J., Boerstoel, H., Dingemans, T. J. & van der Zwaag, S. Liquid crystal main-chain polymers for high-performance fibre applications. Liq. Cryst. 38, 1591–1605 (2011).
Picken, S. J., van der Zwaag, S. & Northolt, M. G. Molecular and macroscopic orientational order in aramid solution - a model to explain the influence of some spinning parameters on the modulus of aramid yarns. Polymer. (Guildf) 33, 2998–3006 (1992).
Krogsgaard, M., Nue, V. & Birkedal, H. Mussel-inspired materials: self-healing through coordination chemistry. Chem. Eur. J. 22, 844–857 (2016).
Zhao, H. & Waite, J. H. Linking adhesive and structural proteins in the attachment plaque of Mytilus californianus. J. Biol. Chem. 281, 26150–26158 (2006).
Wei, W. et al. A mussel-derived one component adhesive coacervate. Acta Biomater. 10, 1663–1670 (2014).
Bonn, D., Kellay, H., Benamar, M. & Meunier, J. Viscous finger widening with surfactants and polymers. Phys. Rev. Lett. 75, 2132–2135 (1995).
Hernandez, B., Coic, Y.-M., Pflueger, F., Kruglik, S. G. & Ghomi, M. All characteristic Raman markers of tyrosine and tyrosinate originate from phenol ring fundamental vibrations. J. Raman Spectrosc. 47, 210–220 (2016).
Zhao, Q. et al. Underwater contact adhesion and microarchitecture in polyelectrolyte complexes actuated by solvent exchange. Nat. Mater. 15, 407–412 (2016).
Schofield, R. M. S., Nesson, M. H., Richardson, K. A. & Wyeth, P. Zinc is incorporated into cuticular "tools" after ecdysis: the time course of the zinc distribution in "tools" and whole bodies of an ant and a scorpion. J. Insect Physiol. 49, 31–44 (2003).
Drury, J. L. & Mooney, D. J. Hydrogels for tissue engineering: scaffold design variables and applications. Biomaterials 24, 4337–4351 (2003).
Hou, Q. P., De Bank, P. A. & Shakesheff, K. M. Injectable scaffolds for tissue regeneration. J. Mater. Chem. 14, 1915–1923 (2004).
Kretlow, J. D., Klouda, L. & Mikos, A. G. Injectable matrices and scaffolds for drug delivery in tissue engineering. Adv. Drug Deliv. Rev. 59, 263–273 (2007).
Stalling, D., Westerhoff, M. & Hege, H. C. The Visualization Handbook 749–767Elsevier (2005).
Qin, X. X., Coyne, K. J. & Waite, J. H. Tough tendons-mussel byssus has collagen with silk-like domains. J. Biol. Chem. 272, 32623–32627 (1997).
Qin, X.X. & Waite, J. H. A potential mediator of collagenous block copolymer gradients in mussel byssal threads. Proc. Natl Acad. Sci. USA 95, 10517–10522 (1998).
Coyne, K. J., Qin, X.-X. & Waite, J. H. Extensible collagen in mussel byssus: a natural block copolymer. Science 277, 1830–1832 (1997).
Sun, C., Lucas, J. M. & Waite, J. H. Collagen-binding matrix proteins from elastomeric extraorganismic byssal fibers. Biomacromolecules 3, 1240–1248 (2002).
Sun, C. J. & Waite, J. H. Mapping chemical gradients within and along a fibrous structural tissue, mussel byssal threads. J. Biol. Chem. 280, 39332–39336 (2005).
Rzepecki, L. M., Hansen, K. M. & Waite, J. H. Characterization of a cystine-rich polyphenolic protein family for the blue mussel Mytilus edulis. Biol. Bull. 183, 123–137 (1992).
Papov, V. V., Diamond, T. V., Biemann, K. & Waite, J. H. Hydroxyarginine containing polyphenolic proteins in the adhesive plaques of the marine mussel Mytilus edulis. J. Biol. Chem. 270, 20183–20192 (1995).
Zhao, H. & Waite, J. H. Proteins in load-bearing junctions: the histidine-rich metal-binding protein of mussel byssus. Biochemistry 45, 14223–14231 (2006).
Waite, J. H. & Qin, X. X. Polyphosphoprotein from the adhesive pads of Mytilus edulis. Biochemistry 40, 2887–2893 (2001).
We acknowledge support from the Deutsche Forschungsgemeinschaft (DFG) through SPP-1568 (promotion of young researchers) and an Individual DFG Research Grant (HA6369/3-1), as well as from the Max Planck Society. We thank V. Schöppler for assistance with the microCT measurements and J.H. Waite for providing a plaque scanning electron microscopy image.
The authors declare no competing financial interests.
Supplementary Figures (PDF 494 kb)
Byssus formation: Movie presented at 10X speed showing a mussel (Mytilus edulis) forming three byssal threads consecutively. The mussel is attached to a transparent plexiglass plate with fishing line and a rubber band, allowing observation of thread formation from the ventral side of the foot. Each thread is formed in ~3 minutes. Secretion of the plaque proteins can be observed as a white spot near the end of the foot while core and cuticle formation are hidden within the ventral groove; however, the thread is seen to be fully formed once it is released from the groove. During the secretion process and especially immediately prior to the thread being released from the groove, the foot undergoes clear muscular contractions that presumably apply tensile mechanical load to the developing thread, which may contribute to protein alignment in the core. (AVI 19083 kb)
About this article
Cite this article
Priemel, T., Degtyar, E., Dean, M. et al. Rapid self-assembly of complex biomolecular architectures during mussel byssus biofabrication. Nat Commun 8, 14539 (2017). https://doi.org/10.1038/ncomms14539
Advanced Functional Materials (2021)
A platform for functionalization of cellulose, chitin/chitosan, alginate with polydopamine: A review on fundamentals and technical applications
International Journal of Biological Macromolecules (2021)
Nature Reviews Materials (2021)
Demonstration of Environmentally Stable, Broadband Energy Dissipation via Multiple Metal Cross‐Linked Glycerol Gels
Advanced Functional Materials (2021)