Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Electromagnon dispersion probed by inelastic X-ray scattering in LiCrO2

Abstract

Inelastic X-ray scattering with meV energy resolution (IXS) is an ideal tool to measure collective excitations in solids and liquids. In non-resonant scattering condition, the cross-section is strongly dominated by lattice vibrations (phonons). However, it is possible to probe additional degrees of freedom such as magnetic fluctuations that are strongly coupled to the phonons. The IXS spectrum of the coupled system contains not only the phonon dispersion but also the so far undetected magnetic correlation function. Here we report the observation of strong magnon–phonon coupling in LiCrO2 that enables the measurement of magnetic correlations throughout the Brillouin zone via IXS. We find electromagnon excitations and electric dipole active two-magnon excitations in the magnetically ordered phase and heavily damped electromagnons in the paramagnetic phase of LiCrO2. We predict that several (frustrated) magnets with dominant direct exchange and non-collinear magnetism show surprisingly large IXS cross-section for magnons and multi-magnon processes.

Introduction

The coupling between magnetic and lattice degrees of freedom gives rise to many interesting effects. It can induce multiferroic order with ferroelectric polarization coupled to the magnetic structure1,2,3 or it can generate dynamic mixed magnon–phonon excitations. If the magnon is coupled to a polar phonon, the mixed mode, termed electromagnon, can be excited by the electric field of light at the resonant frequency4,5,6. Previous experiments showed that magnetization dynamics of materials can be studied at ultrafast timescales by exciting electromagnons via femtosecond light pulses7. Moreover, optical properties of magnetoelectric materials at the resonant frequency can be controlled via external magnetic field8,9. Measurement of electromagnons is possible via THz spectroscopy. However, this technique is able to probe only the centre of the Brillouin zone. As we shall show, electromagnons can appear at finite momentum, thus inaccessible to THz spectroscopy. Inelastic neutron scattering can also identify the magnetic and phononic component of an electromagnon excitation, however previous studies found only small energy shifts of the magnons due to magnon–phonon coupling10,11, while the transfer of spectral weight between magnons and phonons could not be resolved so far. Here we show that LiCrO2 is an exceptional material, where the magnon–phonon coupling is strong enough to make the transferred spectral weight from phonons to magnons visible for inelastic X-ray scattering and thus enables the direct measurement of the electromagnon dispersion. We also suggest additional systems, where similarly strong effects can be present.

LiCrO2 is an excellent realization of the two-dimensional (2D) S=3/2 Heisenberg triangular lattice antiferromagnet (TLA) model with only minimal corrections due to structure and symmetry. Dzyaloshinskii–Moriya interactions are forbidden on all bonds due to the space group symmetry of . Single-ion anisotropy is expected to be small due to the octahedral coordination of the Cr3+ ion, which have half-filled t2g shells resulting in quenched orbital angular momentum. The interplane interactions are weak due to the large separation of the triangular layers. LiCrO2 develops long-range magnetic order at TN=61.2 K (ref. 12). The magnetic structure is an ac-plane helical order with wavevectors of km=(1/3, 1/3, 0) and km=(−2/3, 1/3, 1/2). The angles between neighbouring spins on the triangular planes are exactly 120° and the chirality is staggered along the c axis as a result of the double-Q structure13. The staggered chirality implies the appearance of a small symmetry breaking term in the spin Hamiltonian below TN. The magnetic interactions in the plane are dominated by direct exchange14. These interactions are sensitive to the modulation of the bond length, similarly to other Cr3+ compounds with short bonds such as ZnCr2O4 (refs 15, 16) and MgCr2O4 (ref. 17). Furthermore, LiCrO2 shows a pronounced anomaly in the dielectric constant at TN but no ferroelectric polarization could be observed18 pointing towards an antiferroelectric ground state induced by the staggered chirality of the triangular layers19,20.

We report the spin and lattice excitation spectrum of LiCrO2 measured via inelastic X-ray scattering with meV energy resolution (IXS) and inelastic neutron scattering (INS), and a direct observation of an electromagnon. The data reveal a surprisingly strong mixing between magnons and phonons. We show that the observed electromagnon is the result of the strong coupling between the phason spin wave mode and the longitudinal acoustic (LA) phonon in the magnetically ordered phase of LiCrO2. We also present a model that describes both the measured quasiparticle dispersion and the cross-sections for IXS and INS at low temperature. This model shows that non-collinear magnetic order and exchange striction (ES) can induce linear coupling between magnons and phonons. Furthermore, we report the observation of two-magnon (2M) excitations in the ordered phase and strongly damped excitations above the Néel temperature from our IXS data.

Results

Temperature-dependent IXS spectrum of LiCrO2

The IXS spectrum of LiCrO2 measured at room temperature at Q=(1.5, 1.5, 0) shows three phonon modes at energies of 30.8(4), 34.6(2) and 59.2(1) meV (Fig. 1 and Supplementary Fig. 1). The measured Q-point is equivalent to the M′-point of the Brillouin zone shifted by (1, 1, 0) (Fig. 2b). The lowest-energy mode has an unusually large intrinsic width of 6.8(5) meV (see Methods for details of the data analysis). On cooling, the phonon spectrum goes through a marked change. The lowest phonon peak loses almost all of its intensity and a new resonance develops gradually below 10 meV. This new mode appears as a broad diffuse scattering signal at 99 K, centred at about 8 meV. With decreasing temperature, the peak becomes more pronounced accompanied with increasing spectral weight and decreasing width. At the lowest measured temperature of 7 K the peak position is at 10.3(2) meV and it has a resolution limited width. To compare directly the integrated intensities at different temperatures we calculated the dynamical susceptibility for the lowest phonon peak and the new resonance, shown in Fig. 3. It is clearly visible that the lowest energy phonon transfers most of its spectral weight to the new mode on cooling while the sum of the two is temperature independent. The measured room-temperature phonon energies are well reproduced by our ab initio calculation (see Methods) shown as vertical purple lines in Fig. 1. The calculated dispersion reveals that the observed phonon with lowest energy is a LA branch while the two peaks at higher energy correspond to optical branches (PH1 and PH2). While the relative spectral weight of the two upper modes is well reproduced by the calculation, the intensity of the LA phonon is strongly underestimated (see red curve in Fig. 1). The calculated energy of the LA phonon is 31.4 meV and its symmetry belongs to the Eu polar representation.

Figure 1: Temperature evolution of the measured IXS spectrum at the M′-point.
figure 1

Green dots denote experimental data normalized to the same monitor. Red, yellow, green and grey filled areas are fitted electromagnon (EM), paraelectromagnon (PEM), LA and optical phonon peaks (PH1 and PH2), respectively. Light grey area shows the full width at half maximum of the elastic line. Red lines are the theoretical spectrum of the coupled model at 7 K and the pure phonon model at 295 K. Vertical purple lines show the calculated quasiparticle energies. Error bars indicate 1 s.d.

Figure 2: Coupled magnon and phonon modes in LiCrO2.
figure 2

(a) A single triangle of Cr3+ spins is shown with the surrounding O6 octahedra. Purple arrows depict the helical magnetic structure (rotated into the ab-plane for better visibility), the phonon and phason amplitude at the M′-point is shown by black and red arrows, respectively. (b) Reciprocal space of the triangular lattice with black and dashed hexagons denoting the magnetic and crystallographic Brillouin zones, respectively. The upper-left and lower-right colour maps show the phason energy and the value, respectively (see text). Green and red dashed lines show the path of the IXS and INS measurement, respectively. (c) Comparison of the measured phonon dispersion at 7 K and the coupled magnon–phonon model along the (h, h, 0) direction. The colour map on the left half shows the calculated IXS cross-section in a.u., while the filled green circles and blue squares denote the measured quasiparticle energies using IXS and INS, respectively. The black dashed and red dashed lines denote the magnon and longitudinal phonon dispersion of the uncoupled model, while the continuous black lines correspond to the coupled dispersion. The empty red circles on the right half denote the eλ·g(k) factor that determines the strength of the magnon–phonon coupling for each λ phonon mode. (d) Model calculation for in-plane direction perpendicular to (h, h, 0). Error bars indicate 1 s.d.

Figure 3: Imaginary part of the dynamical susceptibility at the M′-point.
figure 3

The green and blue dots denote the integrated signal of the electromagnon (EM) and LA phonon after correction for the Bose factor. All values are normalized to the room temperature value of the LA phonon. Error bars indicate 1 s.d.

Electromagnon dispersion in LiCrO2

To unambiguously identify the new low-energy mode of LiCrO2 we measured the excitation spectrum by INS along the (h, 1−2h, 0) reciprocal space direction equivalent to (h, h, 0) in the magnetic Brillouin zone (Supplementary Fig. 2). At the M-point (equivalent to M′) a single spin wave excitation was found in the helical phase at 1.5 K centred at 10.3(1) meV. Since neutrons are sensitive to magnetic fluctuations in the measured momentum range, we can conclude that the low-energy resonance at T<TN has not only polar phononic but also magnetic character, thus it is an electromagnon with a finite momentum. Moreover, at intermediate temperatures above TN the strongly damped low-energy excitation might be a paraelectromagnon due to the lack of both magnetic and electric dipole order. The origin of this excitation can be a phonon coupled to the excitation of the 2D correlated magnetic state, which persists above TN due to the low dimensionality of the system13,21,22.

Two-magnon continuum

To determine the coupling mechanism that drives the observed strong magnon–phonon mixing, we measured IXS spectra at multiple points along the (h, h, 0) reciprocal space direction at 7 K and fitted the phonon energies. The electromagnon spectrum is reported in Fig. 4a–i (also in Supplementary Fig. 3). Remarkably, the energy width of the electromagnon excitation increases substantially around the magnetic Bragg point (K-point). Since the one magnon excitations are sharp at low temperature, the broad IXS peaks can be due to phonons coupled to the 2M continuum that is intrinsically broad for dispersive magnons. The 2M continuum is a purely quantum effect and the corresponding dynamical structure factor is typically much smaller than that of the single magnon. It is related to the longitudinal fluctuations of the ordered spins23. To corroborate our argument, we calculated the non-interacting 2M dynamical structure factor for the TLA (ref. 23) with first- and second-neighbour antiferromagnetic interactions J1=8.17 meV and J2=0.556 meV, shown in Fig. 4j; and a cut at (1.292, 1.292, 0) reciprocal space point is shown in Fig. 4e. The 2M dynamical structure factor is strongest close to the K-point, and the centre of the 2M spectral weight is expected to be close to the one-magnon energy. This can explain why the measured electromagnon spectrum continuously changes from a sharp one magnon–one phonon mode to a phonon mixed with the 2M continuum as its momentum gets closer to the K-point. In the following we model only the single magnon–phonon spectrum.

Figure 4: IXS electromagnon spectrum measured at 7 K and the 2M continuum.
figure 4

(ai) Green dots denote experimental data along (h, h, 0) normalized to the same monitor after the subtraction of the elastic peak. Red, yellow, green and grey filled areas are fitted electromagnon (EM), 2M, LA and optical phonon peaks (PH1 and PH2), respectively. Light grey area shows the full width at half maximum (FWHM) of the elastic line. The plots are scaled individually to enhance the visibility of the weak peaks. The red line in e shows the theoretical 2M spectrum convoluted with the experimental resolution function at Q=(1.292, 1.292, 0). The horizontal purple bar in a shows the FWHM of the instrumental resolution function. (j) The absolute value of the 2M dynamical structure function for the pure magnon model. Green line denotes the dispersion of the phason spin wave mode. Error bars indicate 1 s.d.

Phason spin wave mode as electromagnon

The fitted peak positions of both the INS and IXS data are presented in Fig. 2c,d (Supplementary Tables 1–3) together with the model calculations, which will be explained in the following. In general, helical magnetic structures have three spin wave modes: a phason mode with rotation of all spins in the ordering plane and two canting modes correspond to spins canting away from the ordering plane. Strikingly, our measured electromagnon spectrum contains only one of the three spin wave modes that according to its dispersion corresponds to the phason mode of the helical magnetic structure. Moreover, the two canting modes of the spin spiral are completely decoupled from the phonons. Besides, the phason mode shows a roton-like minimum at M′. Similar minima were previously observed in several TLAs such as CuCrO2 (refs 24, 25), α-CaCr2O4 (ref. 26) and LuMnO3 (ref. 27). This points towards a general sensitivity of the magnon energy at the M-point to perturbations such as quantum fluctuations28,29, further neighbour interactions or magnon–phonon coupling30. The electromagnon in LiCrO2 has large IXS scattering cross-section at both the Γ- and M′-points.

Model of the magnon–phonon coupling

The microscopic mechanism that couples the magnons and phonons in LiCrO2 is the symmetric ES, since the antisymmetric exchange is too weak being a relativistic correction31. In the following we will show that the measured electromagnon dispersion and IXS cross-section can be well described on a single triangular layer assuming strong ES between first-neighbour chromium atoms. We will show that in non-collinear magnets ES gives a linear coupling between magnons and phonons thus can generate a strong mixing (for a detailed description see Supplementary Note 1). For a quantitative description, we propose the following Hamiltonian that couples spins to phonons, taking into account the ideal isotropic nature of the spins in LiCrO2:

where J(r) is the Heisenberg exchange between first-neighbour spins as a function of the bond length r, Sm is the spin vector operator on the mth magnetic atom and is the Hamiltonian of the lattice vibrations. To simplify equation (1), we keep only the constant and linear term from the Taylor expansion of J(r) around the r0 equilibrium bond length. The constant term J1 describes the spin wave dynamics in the absence of phonons, while the linear coefficient Jmp gives the leading magnon–phonon coupling term:

where um is the displacement vector of atom m and is the unit bond vector pointing from atom m to atom n. In the magnetically ordered phase if the order is non-collinear linearly couples the phonon and magnon bosonic operators aλ(k) and b(k). After applying the linear Holstein–Primakoff approximation and using a rotating coordinate system for the spins23,29,32 the equation simplifies to

where λ indexes the phonon modes. The coupling term γλ(k) is given by

where M is the mass of the magnetic atom, ωλ(k) and eλ(k) are the energy and amplitude of the λ phonon on the chromium atom. The g(k) geometrical factor for the Bravais lattice of magnetic atoms reads

where the sum runs through bonds denoted by d (with ES). The linear coupling vanishes for collinear magnetic order, because g(k) is zero for km=0. It is also zero at the k=km reciprocal space point, explaining why no one-magnon excitation is visible on the IXS spectrum close to the K-point. The coupled model can be solved using Bogoliubov transformation, and the corresponding neutron and X-ray scattering cross-sections can be calculated (Supplementary Note 1). The inactivity of the additional two canting spin wave modes of the helical structure in the IXS spectrum can be explained within our model as follows. The exchange interactions in the system can be thought of as effective magnetic fields acting on each magnetic site and being equal to the sum of the neighbouring moments times the exchange constant J1. In the absence of phonons, the field is parallel to the moment direction on every site as illustrated by purple arrows in Fig. 2a. However, when a phonon perturbs the system and modulates the uniform J1 via ES, the effective magnetic field will not be parallel to the moment direction any more but points somewhere within the plane of the spin spiral. This will induce a modulation of the phase of the spins within the spiral as spins reorient themselves to minimize the total energy. This phase modulation is exactly the phason spin wave mode that we see in our data.

Discussion

For a full interpretation of the IXS spectrum of LiCrO2, we start with the pure phonon spectrum in the paramagnetic phase determined from ab initio calculation. The dispersion of the longitudinal phonons are shown in Fig. 2c,d by black dashed lines and the full phonon spectrum in Supplementary Fig. 4. The calculated dispersion relation agrees well with the measured phonon energies showing that the magnon–phonon coupling introduces only minor energy shifts. The introduction of Jmp will mix the phason and phonon amplitudes. The strongest mixing is calculated to be between the LA and transverse acoustic phonon branches of the 2D triangular planes and the phason spin wave mode of the helical magnetic structure in agreement with the experiment. The wavevector-dependent intensity of the IXS electromagnon signal is proportional to , which is largest along the (h, h, 0) in reciprocal space and zero at lattice and magnetic Bragg points (Fig. 2b). It is important to note that although is zero at the M-point, the coupled dispersion is the same as at M′ just both g(k) and e(k) vectors are rotated by 90° thus invisible for IXS. The largest mixing amplitude is expected at Γ and M′ in agreement with our experimental results. Remarkably, the strong coupling causes a roton-like minimum of the spin wave dispersion at M′ downwards renormalizing the phason energy by 42%, when compared with the decoupled model, even though the lowest phonon mode is 20 meV higher in energy.

To determine the parameters of the coupled model, we fitted the experimental electromagnon dispersions using J1 and Jmp as parameters. The best model parameters are J1=6.00(25) meV and Jmp=65(4) meV Å−1. Including an additional second-neighbour exchange interaction in the triangular planes results in zero within error bar. The optimized coupled model describes both the measured dispersion (see black lines in Fig. 2c) and the IXS cross section (see red line in Fig. 1) very well. Some deviation close to the Γ-point is due to the overestimation of the speed of sound from the ab initio calculation. The real-space dynamics of the strong coupling at the M′-point is visualized in Fig. 2a. At this wavevector the LA phonon (black arrows) shortens and lengthens the S1S2 and S2S3 bonds, respectively. The excited phason mode is in phase with the phonon that makes the S1S2 bond stronger (J1+δJ) while the S2S3 bond weaker (J1+δJ). Thus, a ferromagnetic fluctuation on the longer bond and antiferromagnetic fluctuation on the shorter bond is energetically favourable if ES is present. This explains the reduction of the phason energy and the roton-like minimum. The S1S2 bond is inactive at this wavevector since it changes neither length nor relative spin orientation. The largest electromagnon cross-section is predicted close to the Γ-point in agreement with experiment. Although the g(k) coupling term vanishes at Γ, the decreasing energy separation between the LA phonon and the phason mode overcomes this reduction towards the zone centre.

There are potentially many other magnetic correlated systems where the magnon–phonon coupling is present and matrix elements are allowed by symmetry. However, for a measurable hybridization between magnetic and lattice fluctuations a large coupling is necessary that makes only a few of them suitable for studying magnetism via IXS. For example, ZnCr2O4 and MgCr2O4 with pyrochlore structures have ES values comparable to LiCrO2. It is also possible that the observed molecular resonance-like magnetic signal in these systems33,34,35,36 is related to hybridized magnon–phonon modes. Besides, large magnon–phonon coupling is expected for magnetic 5d systems, where the extended d orbitals can support large modulation of the superexchange interaction due to ligand vibrations. For example, in NaOsO3 an upward shift of the optical phonon energy by 5 meV was attributed to the onset of magnetic correlations37. 5d systems are especially promising for IXS studies as the general lack of large single crystals prohibits detailed INS experiments.

In conclusion, we reported inelastic X-ray scattering data on LiCrO2 that revealed a dispersive electromagnon. Our analysis showed that it is the phason mode of the helical spin order coupled to a LA phonon. We identified the exchange striction between first-neighbour chromium ions as the microscopic coupling mechanism. Fitting the model parameters to the measured electromagnon dispersion we could reproduce both the experimental dispersion and the dynamical structure factor for inelastic X-ray scattering. Beside the one-magnon process we also found signature of coupling between the acoustic phonon branches and the 2M continuum around the magnetic Bragg points that can be explained by including higher-order corrections to our linear theory. In the paramagnetic phase we observed a heavily damped electromagnon that might be stabilized by the low-dimensional magnetic correlations of the 2D triangular lattice. By accessing the momentum dependence, our results shed light on a much richer physics of electromagnons that is beyond the reach of THz light experiments. The reported measurement also shows how inelastic X-ray scattering can be used to probe magnetic correlations with high energy and momentum resolution in certain systems with large enough magnon–phonon coupling. This study will open a route towards measuring magnetic correlations at extreme conditions using diamond anvil cells. Indeed, IXS can be performed with samples as thin as 10–20 μm, which allow extending such studies up to Mbar pressure38. It is furthermore possible to work with evanescent wave fields in grazing angle conditions, which allows surface sensitive studies, measurements on thin films and multilayer systems39,40.

Methods

Crystal growth

LiCrO2 single crystals were grown by the Li2O–B2O3 flux or Li2O–PbO–B2O3 flux methods for IXS and INS measurements, respectively. A typical growth was done by a mixture of Li2O, Cr2O3 and B2O3 or with additional PbO. The mixture was heated at 1,300 °C and then slowly cooled down to 800 or 900 °C, respectively.

Inelastic X-ray scattering

IXS was measured on the ID28 beamline at the European Synchrotron Radiation Facility along the reciprocal space direction (h, h, 0) at temperatures 295, 99, 69, 40 and 7 K using incident photon energy of 17.794 keV (λ=0.6968 Å) produced by the (9, 9, 9) Si Bragg reflection and beam size of 50 × 50 μm2. Since the sample was a thin plate perpendicular to (0, 0, 1), we choose the (h, h, l) scattering plane to minimize absorption. The ID28 instrumental energy resolution has a pseudo-Voigt profile with 2.71(2) and 3.3(1) meV full width at half maximum of the Gaussian and Lorentzian components and a mixing parameter of 0.63(2). The momentum resolution of the ID28 spectrometer is close to rectangular with 0.027 and 0.076 Å−1 horizontal and vertical width perpendicular to the momentum transfer, while the longitudinal momentum resolution is at least two orders of magnitude better than the transverse.

Inelastic neutron scattering

INS was measured on the EIGER triple-axis spectrometer at SINQ at the Paul Scherrer Institut using fixed final neutron energy of 14.7 meV, double focusing graphite monochromator and horizontal focusing graphite analyser. To eliminate spurious scattering a pyrolytic graphite filter was applied after the sample. We have used a 50 mg single crystal of LiCrO2 and performed measurements at 1.5 K. Owing to the small sample size, the spin wave signal was only collected close to the magnetic Bragg points along the (h, 1–2h, 0) direction and at (1/2, 1/2, 0) in reciprocal space. The spin wave peak as a function of neutron energy transfer was fitted with a Gaussian function.

Curve fitting

All constant momentum transfer scans were fitted with a line shape that is the instrumental energy resolution convoluted with a Lorentzian to model the finite lifetime of the excitations. In the main text all intrinsic line width are given by the full width at half maximum of the Lorentzian component. All given error are 1 s.d., originating from the statistical error of the detector counts.

Phonon calculation

Lattice dynamics calculations were performed using the finite displacement method within density functional theory (DFT)41. Distorted atomic configurations were generated and the induced forces of a 4 × 4 × 4 supercell were computed by total energy calculations using Projector Augmented Waves method as implemented in VASP42,43,44. A shifted 4 × 4 × 4 momentum grid is used for the ionic relaxations and the calculation of Born Effective charges by perturbation theory45 in the primitive unit cell. While the internal ionic coordinates are relaxed, the lattice constant is kept fixed to the experimental value to reduce the error due to unit cell volume. The valence electrons are treated explicitly by the VASP PAW potentials are 1s22s2sp1 for Li, 3p63d54s1 for Cr and 2s22p4 for O. A plane wave cutoff of 500 eV, which is 25% larger than suggested, is used and tested to provide good convergence. PBEsol exchange correlation functional46,47 is used for all calculations. To account for the underestimation of on-site correlations by generalized gradient approximation (GGA), the DFT+U approximation48 is used with a U of 3 eV, which has previously been shown to faithfully reproduce the spin-phonon properties of Cr oxides in the same implementation49. Dynamical matrices throughout the Brillouin zone were computed using Fourier transformation as implemented in Phonopy50 and non-analytical term corrections due to finite Born charges were applied. A shifted 4 × 4 × 4 momentum grid has been used for sampling the electronic structure of the primitive unit cell.

Model of the magnon–phonon coupling

The spin wave model and the coupled magnon–phonon model was solved numerically using a modified version of SpinW (ref. 32).

Data availability

All relevant data that support the findings of this study are available from the corresponding author on request.

Additional information

How to cite this article: Tóth, S. et al. Electromagnon dispersion probed by inelastic X-ray scattering in LiCrO2. Nat. Commun. 7, 13547 doi: 10.1038/ncomms13547 (2016).

Publisher’s note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

References

  1. Eerenstein, W., Mathur, N. D. & Scott, J. F. Multiferroic and magnetoelectric materials. Nature 442, 759–765 (2006).

    ADS  CAS  Article  Google Scholar 

  2. Tokura, Y. Multiferroics as quantum electromagnets. Science 312, 1481–1482 (2006).

    CAS  Article  Google Scholar 

  3. Cheong, S.-W. & Mostovoy, M. Multiferroics: a magnetic twist for ferroelectricity. Nat. Mater. 6, 13–20 (2007).

    ADS  CAS  Article  Google Scholar 

  4. Pimenov, A. et al. Possible evidence for electromagnons in multiferroic manganites. Nat. Phys. 2, 97–100 (2006).

    CAS  Article  Google Scholar 

  5. Sushkov, A. B., Aguilar, R. V., Park, S., Cheong, S.-W. & Drew, H. D. Electromagnons in multiferroic YMn2O5 and TbMn2O5 . Phys. Rev. Lett. 98, 027202 (2007).

    ADS  CAS  Article  Google Scholar 

  6. Sushkov, A. B., Mostovoy, M., Valdés Aguilar, R., Cheong, S.-W. & Drew, H. D. Electromagnons in multiferroic RMn2O5 compounds and their microscopic origin. J. Phys. Condens. Matter 20, 434210 (2008).

    ADS  Article  Google Scholar 

  7. Sheu, Y. M. et al. Using ultrashort optical pulses to couple ferroelectric and ferromagnetic order in an oxide heterostructure. Nat. Commun. 5, 5832 (2014).

    CAS  Article  Google Scholar 

  8. Takahashi, Y., Shimano, R., Kaneko, Y., Murakawa, H. & Tokura, Y. Magnetoelectric resonance with electromagnons in a perovskite helimagnet. Nat. Phys. 8, 121–125 (2011).

    Article  Google Scholar 

  9. Kézsmárki, I. et al. One-way transparency of four-coloured spin-wave excitations in multiferroic materials. Nat. Commun. 5, 3203 (2014).

    Article  Google Scholar 

  10. Lovesey, S. W. Theory of the magnon and phonon interaction in FeF2 . J. Phys. C Solid State Phys. 5, 2769–2784 (1972).

    ADS  CAS  Article  Google Scholar 

  11. Petit, S. et al. Spin phonon coupling in hexagonal multiferroic YMnO3 . Phys. Rev. Lett. 99, 266604 (2007).

    ADS  CAS  Article  Google Scholar 

  12. Sugiyama, J. et al. μ+SR investigation of local magnetic order in LiCrO2 . Phys. Rev. B 79, 184411 (2009).

    ADS  Article  Google Scholar 

  13. Kadowaki, H., Takei, H. & Motoya, K. Double-Q 120° structure in the Heisenberg antiferromagnet on rhombohedrally stacked triangular lattice LiCrO2 . J. Phys. Condens. Matter 7, 6869–6884 (1995).

    ADS  CAS  Article  Google Scholar 

  14. Mazin, I. Electronic structure and magnetism in the frustrated antiferromagnet LiCrO2: first-principles calculations. Phys. Rev. B 75, 094407 (2007).

    ADS  Article  Google Scholar 

  15. Sushkov, A. B., Tchernyshyov, O., Ratcliff, W. II, Cheong, S.-W. & Drew, H. D. Probing spin correlations with phonons in the strongly frustrated magnet ZnCr2O4 . Phys. Rev. Lett. 94, 137202 (2005).

    ADS  CAS  Article  Google Scholar 

  16. Ji, S. et al. Spin-lattice order in frustrated ZnCr2O4 . Phys. Rev. Lett. 103, 037201 (2009).

    ADS  CAS  Article  Google Scholar 

  17. Oh, J. et al. Magnon Breakdown in a two dimensional triangular lattice Heisenberg antiferromagnet of multiferroic LuMnO3 . Phys. Rev. Lett. 111, 257202 (2013).

    ADS  Article  Google Scholar 

  18. Seki, S., Onose, Y. & Tokura, Y. Spin-driven ferroelectricity in triangular lattice antiferromagnets ACrO2 (A=Cu, Ag, Li, or Na). Phys. Rev. Lett. 101, 067204 (2008).

    ADS  CAS  Article  Google Scholar 

  19. Arima, T.-H. Ferroelectricity induced by proper-screw type magnetic order. J. Phys. Soc. Jpn 76, 073702 (2007).

    ADS  Article  Google Scholar 

  20. Soda, M., Kimura, K., Kimura, T., Matsuura, M. & Hirota, K. Electric control of spin helicity in multiferroic triangular lattice antiferromagnet CuCrO2 with proper-screw order. J. Phys. Soc. Jpn 78, 124703 (2009).

    ADS  Article  Google Scholar 

  21. Moreno, N. et al. Magnetic properties of the frustrated antiferromagnet LiCrO2 . J. Magn. Magn. Mater. 272–276, e1023–e1024 (2004).

    Article  Google Scholar 

  22. Alexander, L. K., Büttgen, N., Nath, R., Mahajan, A. V. & Loidl, A. 7Li NMR studies on the triangular lattice system LiCrO2 . Phys. Rev. B 76, 064429 (2007).

    ADS  Article  Google Scholar 

  23. Coldea, R., Tennant, D. & Tylczynski, Z. Extended scattering continua characteristic of spin fractionalization in the two-dimensional frustrated quantum magnet Cs2CuCl4 observed by neutron scattering. Phys. Rev. B 68, 134424 (2003).

    ADS  Article  Google Scholar 

  24. Poienar, M., Damay, F., Martin, C., Robert, J. & Petit, S. Spin dynamics in the geometrically frustrated multiferroic CuCrO2 . Phys. Rev. B 81, 104411 (2010).

    ADS  Article  Google Scholar 

  25. Frontzek, M. et al. Magnetic excitations in the geometric frustrated multiferroic CuCrO2 . Phys. Rev. B 84, 094448 (2011).

    ADS  Article  Google Scholar 

  26. Toth, S. et al. Magnetic soft modes in the distorted triangular antiferromagnet α-CaCr2O4 . Phys. Rev. Lett. 109, 127203 (2012).

    ADS  CAS  Article  Google Scholar 

  27. Oh, J. et al. Magnon breakdown in a two dimensional triangular lattice Heisenberg antiferromagnet of multiferroic LuMnO3 . Phys. Rev. Lett. 111, 257202 (2013).

    ADS  Article  Google Scholar 

  28. Zheng, W., Fjærestad, J., Singh, R., McKenzie, R. H. & Coldea, R. Anomalous excitation spectra of frustrated quantum antiferromagnets. Phys. Rev. Lett. 96, 057201 (2006).

    ADS  Article  Google Scholar 

  29. Chernyshev, A. & Zhitomirsky, M. E. Spin waves in a triangular lattice antiferromagnet: decays, spectrum renormalization, and singularities. Phys. Rev. B 79, 144416 (2009).

    ADS  Article  Google Scholar 

  30. Kim, J. & Han, J. Coupling of phonons and spin waves in a triangular antiferromagnet. Phys. Rev. B 76, 054431 (2007).

    ADS  Article  Google Scholar 

  31. Moriya, T. Anisotropic superexchange interaction and weak ferromagnetism. Phys. Rev. 120, 91–98 (1960).

    ADS  CAS  Article  Google Scholar 

  32. Toth, S. & Lake, B. Linear spin wave theory for single-Q incommensurate magnetic structures. J. Phys. Condens. Matter 27, 166002 (2015).

    ADS  CAS  Article  Google Scholar 

  33. Lee, S.-H., Broholm, C., Kim, T. H., Ratcliff, W. & Cheong, S.-W. Local spin resonance and spin-peierls-like phase transition in a geometrically frustrated antiferromagnet. Phys. Rev. Lett. 84, 3718–3721 (2000).

    ADS  CAS  Article  Google Scholar 

  34. Lee, S.-H. et al. Emergent excitations in a geometrically frustrated magnet. Nature 418, 856–858 (2002).

    ADS  CAS  Article  Google Scholar 

  35. Tomiyasu, K. et al. Molecular spin resonance in the geometrically frustrated magnet MgCr2O4 by inelastic neutron scattering. Phys. Rev. Lett. 101, 177401 (2008).

    ADS  CAS  Article  Google Scholar 

  36. Tomiyasu, K. et al. Emergence of highly degenerate excited states in the frustrated magnet MgCr2O4 . Phys. Rev. Lett. 110, 077205 (2013).

    ADS  CAS  Article  Google Scholar 

  37. Calder, S. et al. Enhanced spin-phonon-electronic coupling in a 5d oxide. Nat. Commun. 6, 8916 (2015).

    CAS  Article  Google Scholar 

  38. Antonangeli, D. et al. Elasticity of cobalt at high pressure studied by inelastic X-ray scattering. Phys. Rev. Lett. 93, 215505 (2004).

    ADS  CAS  Article  Google Scholar 

  39. Murphy, B. M. et al. Phonon modes at the 2H–NbSe2 surface observed by grazing incidence inelastic X-ray scattering. Phys. Rev. Lett. 95, 256104 (2005).

    ADS  CAS  Article  Google Scholar 

  40. Serrano, J. et al. InN thin film lattice dynamics by grazing incidence inelastic X-ray scattering. Phys. Rev. Lett. 106, 205501 (2011).

    ADS  CAS  Article  Google Scholar 

  41. Parlinski, K., Li, Z. Q. & Kawazoe, Y. First-principles determination of the soft mode in cubic ZrO2 . Phys. Rev. Lett. 78, 4063 (1997).

    ADS  CAS  Article  Google Scholar 

  42. Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953 (1994).

    ADS  Article  Google Scholar 

  43. Kresse, G. & Furthmüller, J. Efficiency of ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996).

    CAS  Article  Google Scholar 

  44. Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169 (1996).

    ADS  CAS  Article  Google Scholar 

  45. Baroni, S., de Gironcoli, S., Dal Corso, A. & Giannozzi, P. Phonons and related crystal properties from density-functional perturbation theory. Rev. Mod. Phys. 73, 515–562 (2001).

    ADS  CAS  Article  Google Scholar 

  46. Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).

    ADS  CAS  Article  Google Scholar 

  47. Perdew, J. P. et al. Restoring the density-gradient expansion for exchange in solids and surfaces. Phys. Rev. Lett. 100, 136406 (2008).

    ADS  Article  Google Scholar 

  48. Liechtenstein, A. I., Anisimov, V. I. & Zaanen, J. Density-functional theory and strong interactions: orbital ordering in Mott-Hubbard insulators. Phys. Rev. B 52, R5467 (1995).

    ADS  CAS  Article  Google Scholar 

  49. Wysocki, A. L. & Birol, T. Magnetically-induced phonon splitting in ACr2O4 spinels from first principles. Phys. Rev. B 93, 134425 (2015).

    ADS  Article  Google Scholar 

  50. Togo, A. & Tanaka, I. First principles phonon calculations in materials science. Scr. Mater. 108, 1–5 (2015).

    CAS  Article  Google Scholar 

Download references

Acknowledgements

We thank Andrea Scaramucci and Michel Kenzelmann for helpful discussions on electromagnons. The IXS measurements were performed on beamline ID28 at the European Synchrotron Radiation Facility, Grenoble, France. We are grateful to Thanh-Tra for providing assistance in using beamline ID28 and Christina Drathen for collecting data on beamline ID22. We also thank Céline Besnard for preliminary X-ray diffraction measurements performed at University of Geneva. Part of this work is based on experiments performed at the Swiss spallation neutron source SINQ, Paul Scherrer Institute, Villigen, Switzerland. The research leading to these results has received funding from the European Community’s Seventh Framework Programme (FP7/2007–2013) under Grant Agreement No. 290605 (COFUND: PSI-FELLOW). K.K. and T.K. were supported by JSPS KAKENHI (grant no. 24244058).

Author information

Authors and Affiliations

Authors

Contributions

S.T. and B.W. carried out inelastic X-ray spectroscopy and analysed data; S.T., K.R. and U.S. carried out INS experiments and analysed data; K.R., H.T., K.K. and T.K. synthesized samples; B.W. and T.B. carried out ab initio calculations; the results were discussed and interpreted by S.T. and C.R.; the manuscript was written by S.T. with input from all the authors.

Corresponding author

Correspondence to Sándor Tóth.

Ethics declarations

Competing interests

The authors declare no competing financial interests.

Supplementary information

Supplementary Information

Supplementary Figures 1-4, Supplementary Table 1-4, Supplementary Note 1 and Supplementary References. (PDF 871 kb)

Peer Review File (PDF 233 kb)

Rights and permissions

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

About this article

Verify currency and authenticity via CrossMark

Cite this article

Tóth, S., Wehinger, B., Rolfs, K. et al. Electromagnon dispersion probed by inelastic X-ray scattering in LiCrO2. Nat Commun 7, 13547 (2016). https://doi.org/10.1038/ncomms13547

Download citation

  • Received:

  • Accepted:

  • Published:

  • DOI: https://doi.org/10.1038/ncomms13547

Further reading

Comments

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Search

Quick links

Nature Briefing

Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.

Get the most important science stories of the day, free in your inbox. Sign up for Nature Briefing